CN102432937A - 一种核电站用1e级k1类无卤阻燃热缩管及其制备方法 - Google Patents

一种核电站用1e级k1类无卤阻燃热缩管及其制备方法 Download PDF

Info

Publication number
CN102432937A
CN102432937A CN2011102376627A CN201110237662A CN102432937A CN 102432937 A CN102432937 A CN 102432937A CN 2011102376627 A CN2011102376627 A CN 2011102376627A CN 201110237662 A CN201110237662 A CN 201110237662A CN 102432937 A CN102432937 A CN 102432937A
Authority
CN
China
Prior art keywords
parts
nuclear power
level
ethylene
halogen
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011102376627A
Other languages
English (en)
Other versions
CN102432937B (zh
Inventor
赵成刚
尹沾松
曾志安
王进
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changyuan electronic (Group) Co., Ltd.
Changyuan Electronics (Dongguan) Co., Ltd.
Original Assignee
CHANGYUAN GROUP Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=45981298&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=CN102432937(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by CHANGYUAN GROUP Ltd filed Critical CHANGYUAN GROUP Ltd
Priority to CN2011102376627A priority Critical patent/CN102432937B/zh
Publication of CN102432937A publication Critical patent/CN102432937A/zh
Application granted granted Critical
Publication of CN102432937B publication Critical patent/CN102432937B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种核电站用 1E 级 K1 类无卤阻燃热缩管，由下列按照重量计的组分组成：乙烯基聚合物 100 份；微胶囊红磷 5 － 15 份；氢氧化铝 20 － 60 份；光稳定剂 0.5 － 3 份；紫外线吸收剂 0.5 － 2 份；抗氧剂 4 － 12 份；润滑剂 2 － 5 份；所述光稳定剂为聚丁二酸 (4- 羟基 -2,2,6,6- 四甲基 -1- 哌啶乙醇 ) 酯；所述的紫外线吸收剂为 2- （ 2'- 羟基 -3',5'- 二特戊基苯基）苯并三唑；所述抗氧剂为四 ( β -(3,5- 二叔丁基 -4- 羟基苯基 ) 丙酸 ) 季戊四醇酯与 4,4'- 硫代双 (6- 叔丁基 -3- 甲基苯酚 ) 按照 1 ： 1 混配而成。本发明核电站用 1E 级 K1 类无卤阻燃热缩管，不含有卤素，阻燃性能好，能够通过 VW-1 燃烧试验，能够在 90 ℃温度条件下使用 60 年。

Description

一种核电站用1E级K1类无卤阻燃热缩管及其制备方法
技术领域
本发明涉及一种热缩管及其制备方法，尤其涉及可供核电站使用的热缩管及其制备方法。
背景技术
核电属于清洁能源，是我国优先发展的产业。截至2008年底，我国已建成浙江秦山、广东大亚湾和江苏田湾三个核电基地，现役核电机组11台、装机容量910万千瓦。按照2007年《核电中长期发展规划》确定的我国核电发展目标，到2020年我国要建设4000万千瓦的核电，核电的比例要从2％提高到4％。
类热缩管安装在安全壳内，能够在正常环境条件下、地震荷载下以及在事故环境下和事故后能完成其规定功能。
我国已建成的浙江秦山、广东大亚湾和江苏田湾三个核电基地，使用寿命为40年，核电站用1E级K1类热缩管只要达到90℃温度下使用40年，就能满足要求，可是从现在开始核电站的使用寿命提高到60年，相应的核电站用1E级K1类热缩管也要能在90℃温度下使用60年。
核电站用1E级K1类热缩管在90℃温度条件下使用60年，要求达到如下性能：
阻燃性：通过VW-1，拉伸强度最小值：9Mpa，断裂伸长率最小值：250%；
175℃、230小时的热老化以后，拉伸强度最小值：7Mpa，断裂伸长率最小值：100%；
175℃、230小时热老化，辐射剂量750KGy以后，拉伸强度最小值：5.5Mpa，断裂伸长率最小值：50%；
175℃、230小时热老化，辐射剂量2400KGy以后，置于300mm的水下24小时，其绝缘电阻要大于2.5MΩ，耐电压3150V/mm，5min不击穿。
目前，核电站用1E级K1类热缩管都是有卤阻燃，就连美国泰科提供的1E级K1类热缩管也含有卤素，可是核电站用1E级K1类电缆能够做到无卤阻燃，核电站用1E级K1类无卤电缆已经大量应用在核电站建设中，因此核电站用1E级K1类无卤阻燃热缩管是一种发展趋势，它必将取代核电站用1E级K1类有卤阻燃热缩管而广泛应用在核电站建设中。
发明内容
本发明要解决的技术问题在于：克服现有的热缩管无法达到核电站1E级K1类热缩管的技术要求的问题，提供一种核电站用1E级K1类无卤阻燃热缩管及其制备方法。
为了解决上述技术问题，本发明提出下列第一个技术方案：一种核电站用1E级K1类无卤阻燃热缩管，由下列按照重量计的组分组成：乙烯基聚合物 100份；微胶囊红磷 5－15份；氢氧化铝  20－60份；光稳定剂  0.5－3份；紫外线吸收剂    0.5－2份；抗氧剂   4－12份；润滑剂   2－5份；
所述乙烯基聚合物为下述物质中的一种或多种：低密度聚乙烯；中密度聚乙烯；乙烯-甲基丙烯酸甲酯共聚物；乙烯-丙烯酸甲酯共聚物；乙烯-丙烯酸乙酯共聚物；乙烯-丙烯酸丁酯共聚物；乙烯-醋酸已烯共聚物；乙烯-辛烯共聚物；乙丙橡胶；
所述光稳定剂为聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯；
所述的紫外线吸收剂为2-（2'-羟基-3',5'-二特戊基苯基）苯并三唑；
所述抗氧剂为四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯与 4,4'-硫代双(6-叔丁基-3-甲基苯酚)按照1：1混配而成。
对上述第一个技术方案的进一步限定在于，所述润滑剂为下述物质中的一种或多种：聚乙烯蜡；硬脂酸锌；硬脂酸钙；硬脂酸。
为了解决上述技术问题，本发明还提出下列第二个技术方案：一种制备所述核电站用1E级K1类无卤阻燃热缩管的制备方法，按重量取乙烯基聚合物  100份，微胶囊红磷  5--15份，氢氧化铝20--60份，光稳定剂0.5-3份，紫外线吸收剂0.5—2份，抗氧剂    4-12份，润滑剂    2-5份，经过密炼混炼造粒或者平行双螺杆挤出机混炼造粒，然后用单螺杆挤出机挤出成管材，所述管材经过钴60或者电子加速器50-180KGy辐射交联，辐射交联后的管材在90-150℃温度下扩张2-6倍。
对上述第二个技术方案的进一步限定在于，所述润滑剂为下述物质中的一种或多种：聚乙烯蜡；硬脂酸锌；硬脂酸钙；硬脂酸。
本发明具有以下有益效果：
1、光稳定剂、紫外线吸收剂与抗氧剂共用，具有抗热老化的协同效应，能显著提高材料的抗热老化性能，满足核电站对核电站用1E级K1类热缩管90℃温度下使用60年的要求；
2、光稳定剂、紫外线吸收剂与抗氧剂共用，具有抗辐射老化的协同效应，能显著提高材料的耐辐射性能，满足核电站对核电站用1E级K1类热缩管的辐射耐辐射性能要求，即剂量2400KGy以后，置于300mm的水下24小时，其绝缘电阻要大于2.5MΩ，耐电压3150V/mm，5min不击穿；
3、本发明核电站用1E级K1类无卤阻燃热缩管，不含有卤素，阻燃性能好，能够通过VW-1燃烧试验，能够在90℃温度条件下使用60年，安装在安全壳内，能够在正常环境条件下、地震荷载下以及在事故环境下和事故后能完成其规定功能，具有加热收缩功能，安装在电线电缆的接续部位，起到绝缘和密封作用；
4、在乙烯基聚合物中同时加入光稳定剂、紫外线吸收剂和抗氧剂，材料的耐热老化性能优良、抗强辐射性能以及耐受高温高压水蒸汽性能优异，具体表现为：175℃、240小时的热老化以后，拉伸强度大于9Mpa，断裂伸长率大于200%； 175℃、240小时热老化以后，连续承受2400KGy的辐射剂量和经过长达1个月的最高温度218℃、最高压力达到0.85MPa，以6.1 L/min/m2的速度喷淋包含0.28 mol /L H3BO3 、0.064 mol/L Na2S2O3与NaOH混合溶液，试验结束后，将其置于300mm的水下24小时，其绝缘电阻大于2.5MΩ,耐电压3150V/mm，5min不击穿。
具体实施方式
本发明提出一种核电站用1E级K1类无卤阻燃热缩管，由下列按照重量计的组分组成：乙烯基聚合物    100份；微胶囊红磷    5－15份；氢氧化铝    20－60份；光稳定剂   0.5－3份；紫外线吸收剂   0.5－2份；抗氧剂  4－12份；润滑剂  2－5份。
所述乙烯基聚合物为下述物质中的一种或多种：低密度聚乙烯；中密度聚乙烯；乙烯-甲基丙烯酸甲酯共聚物；乙烯-丙烯酸甲酯共聚物；乙烯-丙烯酸乙酯共聚物；乙烯-丙烯酸丁酯共聚物；乙烯-醋酸已烯共聚物；乙烯-辛烯共聚物；乙丙橡胶。
所述光稳定剂为聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯。
所述的紫外线吸收剂为2-（2'-羟基-3',5'-二特戊基苯基）苯并三唑。
所述抗氧剂为四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯与 4,4'-硫代双(6-叔丁基-3-甲基苯酚)按照1：1混配而成。
所述润滑剂为下述物质中的一种或多种：聚乙烯蜡；硬脂酸锌；硬脂酸钙；硬脂酸。
制备所述的核电站用1E级K1类无卤阻燃热缩管的制备方法是：按重量取乙烯基聚合物   100份，微胶囊红磷  5－15份，氢氧化铝20－60份，光稳定剂0.5－3份，紫外线吸收剂0.5－2份，抗氧剂   4－12份，润滑剂 2－5份，经过密炼混炼造粒或者平行双螺杆挤出机混炼造粒，然后用单螺杆挤出机挤出成管材，所述管材经过钴60或者电子加速器50-180KGy辐射交联，辐射交联后的管材在90-150℃温度下扩张2-6倍。
制备实施例1
按重量取乙烯-丙烯酸乙酯共聚物50份，乙丙橡胶50份，微胶囊红磷  10份，氢氧化铝40份，聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯1.8份，2-（2'-羟基-3',5'-二特戊基苯基）苯并三唑1.2份，四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯4份，4,4'-硫代双(6-叔丁基-3-甲基苯酚) 4份，硬脂酸锌3.5份。以上材料经过密炼混炼造粒，然后用单螺杆挤出机挤出成管材，所述管材经过钴60或者电子加速器100KGy辐射交联，辐射交联后的管材在120℃温度下扩张4倍，得到核电站用1E级K1类热缩管，其性能如下：
阻燃性：通过VW-1，拉伸强度：13.2Mpa，断裂伸长率：460%；
175℃、230小时的热老化以后，拉伸强度：10.5Mpa，断裂伸长率：380%；
175℃、230小时热老化，辐射剂量750KGy以后，拉伸强度：10.6Mpa，断裂伸长率：290%；
175℃、230小时热老化，辐射剂量2400KGy和LOCA试验以后，置于300mm的水下24小时，其绝缘电阻11.5MΩ,耐电压3150V/mm，5min不击穿。
不含有卤素。
制备实施例2
按重量取低密度聚乙烯50份，乙丙橡胶50份，微胶囊红磷  5份，氢氧化铝60份，聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯0.5份，2-（2'-羟基-3',5'-二特戊基苯基）苯并三唑0.5份，四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯2份， 4,4'-硫代双(6-叔丁基-3-甲基苯酚)2份，聚乙烯腊1份，硬脂酸锌1份。以上材料经过密炼混炼造粒，然后用单螺杆挤出机挤出成管材，所述管材经过钴60或者电子加速器100KGy辐射交联，辐射交联后的管材在120℃温度下扩张4倍，得到核电站用1E级K1类热缩管，其性能如下：
阻燃性：通过VW-1，拉伸强度：12.9Mpa，断裂伸长率：420%；
175℃、230小时的热老化以后，拉伸强度：10Mpa，断裂伸长率：320%；
175℃、230小时热老化，辐射剂量750KGy以后，拉伸强度：9.8Mpa，断裂伸长率：260%；
175℃、230小时热老化，辐射剂量2400KGy和LOCA试验以后，置于300mm的水下24小时，其绝缘电阻12MΩ,耐电压3150V/mm，5min不击穿。
不含有卤素。
制备实施例3
按重量取乙烯-甲基丙烯酸甲酯共聚物50份，乙烯-辛烯共聚物50份，微胶囊红磷      15份，氢氧化铝20份，聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯3份，2-（2'-羟基-3',5'-二特戊基苯基）苯并三唑2份，四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯6份， 4,4'-硫代双(6-叔丁基-3-甲基苯酚)6份，硬脂酸锌2.5份，硬脂酸2.5份。以上材料经过密炼混炼造粒，然后用单螺杆挤出机挤出成管材，所述管材经过钴60或者电子加速器100KGy辐射交联，辐射交联后的管材在120℃温度下扩张4倍，得到核电站用1E级K1类热缩管，其性能如下：
阻燃性：通过VW-1，拉伸强度：13.6Mpa，断裂伸长率：510%；
175℃、230小时的热老化以后，拉伸强度：12Mpa，断裂伸长率：405%；
175℃、230小时热老化，辐射剂量750KGy以后，拉伸强度：11Mpa，断裂伸长率：360%；
175℃、230小时热老化，辐射剂量2400KGy和LOCA试验以后，置于300mm的水下24小时，其绝缘电阻10MΩ,耐电压3150V/mm，5min不击穿。
不含有卤素。 

Claims (4)

1.一种核电站用1E级K1类无卤阻燃热缩管，由下列按照重量计的组分组成：乙烯基聚合物          100份；微胶囊红磷           5－15份；氢氧化铝           20－60份；光稳定剂      0.5－3份；紫外线吸收剂      0.5－2份；抗氧剂     4－12份；润滑剂         2－5份；
所述乙烯基聚合物为下述物质中的一种或多种：低密度聚乙烯；中密度聚乙烯；乙烯-甲基丙烯酸甲酯共聚物；乙烯-丙烯酸甲酯共聚物；乙烯-丙烯酸乙酯共聚物；乙烯-丙烯酸丁酯共聚物；乙烯-醋酸已烯共聚物；乙烯-辛烯共聚物；乙丙橡胶；
所述光稳定剂为聚丁二酸(4-羟基-2,2,6,6-四甲基-1-哌啶乙醇)酯；
所述的紫外线吸收剂为2-（2'-羟基-3',5'-二特戊基苯基）苯并三唑；
所述抗氧剂为四(β-(3,5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯与 4,4'-硫代双(6-叔丁基-3-甲基苯酚)按照1：1混配而成。
2.根据权利要求1所述的核电站用1E级K1类无卤阻燃热缩管，其特征在于：所述润滑剂为下述物质中的一种或多种：聚乙烯蜡；硬脂酸锌；硬脂酸钙；硬脂酸。
3.一种制备如权利要求1所述的核电站用1E级K1类无卤阻燃热缩管的制备方法，其特征在于：按重量取乙烯基聚合物       100份，微胶囊红磷       5－15份，氢氧化铝20－60份，光稳定剂0.5－3份，紫外线吸收剂0.5－2份，抗氧剂      4－12份，润滑剂      2－5份，经过密炼混炼造粒或者平行双螺杆挤出机混炼造粒，然后用单螺杆挤出机挤出成管材，所述管材经过钴60或者电子加速器50-180KGy辐射交联，辐射交联后的管材在90-150℃温度下扩张2-6倍。
4.根据权利要求3所述的核电站用1E级K1类无卤阻燃热缩管的制备方法，其特征在于，所述润滑剂为下述物质中的一种或多种：聚乙烯蜡；硬脂酸锌；硬脂酸钙；硬脂酸。
CN2011102376627A 2011-08-18 2011-08-18 一种核电站用1e级k1类无卤阻燃热缩管及其制备方法 Active CN102432937B (zh)