CN102428112A - 可聚合的聚合物光引发剂和辐射可固化组合物 - Google Patents
可聚合的聚合物光引发剂和辐射可固化组合物 Download PDFInfo
- Publication number
- CN102428112A CN102428112A CN2010800225537A CN201080022553A CN102428112A CN 102428112 A CN102428112 A CN 102428112A CN 2010800225537 A CN2010800225537 A CN 2010800225537A CN 201080022553 A CN201080022553 A CN 201080022553A CN 102428112 A CN102428112 A CN 102428112A
- Authority
- CN
- China
- Prior art keywords
- group
- radiation curable
- light trigger
- polymkeric substance
- ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种式(I)的可聚合的聚合物光引发剂:其中:PL代表n+m+p-官能的聚合物核心;n和m独立代表整数1-30;p代表整数0-10;o是0或1;INI代表选自二苯酮、噻吨酮、咔唑、蒽醌、樟脑醌、α-羟基烷基苯酮、α-氨基烷基苯酮、酰基膦氧化物、二酰基膦氧化物、酰基膦硫化物、乙醛酸苯酯、安息香醚、苄缩酮、α-二烷氧基苯乙酮、咔唑基-O-酰基-肟、α-卤代芳基酮和α-卤代芳基砜的基团;L3和L4代表包含1-14个碳原子的取代或未被取代的二价连接基团;A代表选自丙烯酸酯、甲基丙烯酸酯、苯乙烯、丙烯酰胺、甲基丙烯酰胺、马来酸酯、富马酸酯、衣康酸酯、乙烯基醚、烯丙基醚、烯丙基酯、马来酰亚胺、乙烯腈和乙烯基酯的自由基可聚合的官能团;和R4代表取代或未被取代的烷基。还公开含有可聚合的聚合物光引发剂的辐射可固化组合物和制备可聚合的聚合物光引发剂的方法。
Description
技术领域
本发明涉及尤其适合食品顺应性辐射可固化组合物的一类新的可聚合的聚合物光引发剂,和制备该光引发剂的方法。
背景技术
当暴露于光化辐射时自由基光引发剂通过形成自由基引发单体的聚合。光引发剂经常用于UV可固化组合物,比如UV可固化喷墨油墨。
可区别两种类型的自由基光引发剂。Norrish Type I引发剂是在激发后裂解的引发剂,立即得到引发基团。Norrish Type II引发剂是由光化辐射激活的光引发剂,通过从第二化合物夺取氢形成自由基,第二化合物变为实际引发自由基。这种第二化合物称为共引发剂或聚合协合剂。
光引发剂可以是单官能化合物,但也可以是多官能化合物,即具有一个以上光引发基团。WO 03/033492(COATES BROTHERS)公开多官能噻吨酮光引发剂。
当辐射可固化组合物用于食品包装、玩具和牙科应用时,可提取的残留物量是关键性问题,需要最小化。低分子量化合物通常不完全建入聚合物网络内,很容易提取或扩散出固化组合物外。因此,持续关注设计较不容易提取或迁移出固化组合物外的光引发剂。
使光引发剂的提取最小化的一种方法是使用具有较高分子量的光引发剂。但是,聚合物引发剂容易丧失反应性。因此,对于使用辐射可固化组合物的多种应用比如喷墨印刷,经常需要相当大量的聚合物引发剂以达到理想的固化速度,从而也使粘度增加至不合乎需要的水平。为了克服辐射可固化组合物粘度的不合乎需要的增加,EP1616921 A(AGFA GRAPHICS)和EP 1674499 A(AGFA GRAPHICS)公开包含聚合物光引发剂的辐射可固化组合物,包含树枝状聚合物核心。虽然使用树枝状聚合物核心有利于维持辐射可固化组合物的低粘度,但合乎需要的是进一步改善固化速度,尤其是在没有氮惰性化的情况下。
解决提取问题的另一种方法是设计具有一种或多种烯属不饱和可聚合基团以便它可与辐射可固化组合物的其它单体共聚的光引发剂。很多包含烯属不饱和可聚合基团的光引发剂已公开于文献,用于辐射可固化组合物或作为制备聚合物光引发剂的单体。
JP 2004224993(NIPPON KAYAKY)公开减少其从辐射可固化组合物的固化膜中蒸发或升华的自-光聚合类型光聚合引发剂。其它(甲基)丙烯酸酯化噻吨酮已公开于例如CA 2005283(BASF)和CA1180486(CIBA);
(甲基)丙烯酸酯化二苯酮公开于例如US 2006142408(NATIONAL STARCH)和GB 925117(DU PONT);
(甲基)丙烯酸酯化a-羟基-酮公开于例如WO 2005/108452(ASHLAND)、WO 97/17378(COATES BROTHERS)和EP 538553 A(HUGHES AIRCRAFT)。
(甲基)丙烯酸酯化a-氨基酮公开于例如WO 96/20919(CIBA)和CA 2005283(BASF)。
(甲基)丙烯酸酯化酰基膦氧化物引发剂公开于例如WO2006/056541(CIBA)、WO 2004/103580(CIBA)和AU 2003205731(BASF)。
(甲基)丙烯酸酯化苯偶酰二烷基缩醛公开于JP 2005082679(DAINIPPON INK);
通常,合成靶光引发剂需要使用(甲基)丙烯酰氯。众所周知(甲基)丙烯酰氯为高度反应性的,稳定性有限。经常被环状二聚体污染(见例如JP 2002187868(DAICEL CHEMICAL),因此在使用前需要蒸馏。结合(甲基)丙烯酰氯的高度毒性、有限的市场利用度和高成本,使用(甲基)丙烯酰氯的合成方法不是很适合以工业规模制备(甲基)丙烯酸酯化光引发剂。
WO 2009/068590(AGFA GRAPHICS)公开制备丙烯酸酯化或甲基丙烯酸酯化光引发剂的优化合成方法。虽然避免了高毒性和不稳定的试剂,但仍然需要分离步骤以获得高纯度(甲基)丙烯酸酯化光引发剂,适合食品包装应用,产生额外的生产成本和增加生态学足迹。
因此,仍然需要光引发剂,它被提取或迁移出固化组合物外的趋势明显减小,与广泛多种辐射可固化组合物具有良好相容性并且可通过生态学足迹减少的简单和有成本效益的合成步骤获得。
发明的公开
发明目的
本发明的目的是提供可通过简单和有成本效益的合成步骤获得的一类新的可聚合聚合物光引发剂。
本发明又一个目的是提供包含此类可聚合聚合物光引发剂的辐射可固化组合物。
本发明又一个目的是提供包含此类可聚合光引发剂的辐射可固化油墨和辐射可固化喷墨油墨。
在下文的详细描述中将明白本发明的这些及其它目的。
发明概述
通过使具有至少一个羟基的光引发剂与具体单体在催化剂的存在下反应,不需要分离地制备可聚合光引发剂,发现意想不到地简单的方法可解决上文提到的问题。不需要有机溶剂,从而避免非生态学地除去溶剂。这允许例如辐射可固化喷墨油墨缺乏有机溶剂,结果是通过改善等待时间和更少故障喷嘴在印刷机中表现改善的喷射性能。
通过简单除去催化剂和使用溶于具体单体中的可聚合的聚合物光引发剂,这样用于加入辐射可固化组合物内,还可避免分离的可聚合的聚合物光引发剂在辐射可固化组合物中的溶解度问题。
用权利要求1限定的可聚合的聚合物光引发剂已实现本发明的目的。
从以下描述将明白本发明的其它优点和实施方案。
定义
术语“染料”,如用于公开本发明,指在有关的环境条件下在它应用的介质中溶解度为10mg/L以上的着色剂。
术语“颜料”在通过引用结合到本文中的DIN 55943中限定,是在有关的环境条件下几乎不溶于应用介质因此在其中的溶解度小于10mg/L的着色剂。
术语“C.I.”用于公开本申请是染料索引(Color Index)的缩写。
术语“烷基”指烷基中每种碳原子数可能的所有变体,即对于3个碳原子:正丙基和异丙基;对于4个碳原子:正丁基、异丁基和叔丁基;对于5个碳原子:正戊基、1,1-二甲基-丙基、2,2-二甲基丙基和2-甲基-丁基等。
可聚合的聚合物光引发剂
本发明的可聚合的聚合物光引发剂具有式(I)化学结构:
其中:
PL代表n+m+p-官能的聚合物核心;
n和m独立代表整数1-30;
p代表整数0-10;
o是0或1;
INI代表选自取代或未被取代的二苯酮、取代或未被取代的噻吨酮、取代或未被取代的咔唑、取代或未被取代的蒽醌、樟脑醌、α-羟基烷基苯酮、α-氨基烷基苯酮、酰基膦氧化物、二酰基膦氧化物、酰基膦硫化物、乙醛酸苯酯、安息香醚、苄缩酮、α-二烷氧基苯乙酮、咔唑基-O-酰基-肟、α-卤代芳基酮和α-卤代芳基砜的基团;
L3和L4代表包含1-14个碳原子的取代或未被取代的二价连接基团;
A代表选自丙烯酸酯、甲基丙烯酸酯、苯乙烯、丙烯酰胺、甲基丙烯酰胺、马来酸酯、富马酸酯、衣康酸酯、乙烯基醚、烯丙基醚、烯丙基酯、马来酰亚胺、乙烯腈和乙烯基酯的自由基可聚合的官能团;和
R4代表取代或未被取代的烷基。
在优选实施方案中,PL代表基于聚醚、聚酯或聚酰胺的聚合物核心,更优选基于聚醚或聚酯的聚合物核心,最优选基于聚醚的聚合物核心。
在另一个优选实施方案中,n+m+p代表整数2-50,更优选n+m+p代表整数5-40。
在最优选的实施方案中PL代表星形、支化或树枝状聚合物核心,优选聚醚或聚酯核心,特别优选聚醚。树枝状聚合物核心包括树枝状大分子、树枝化基元(dendron)、支化接枝聚合物(dendrigraft)和超支化聚合物核心。特别优选超支化聚合物核心,因为它们的合成比树枝状大分子和树枝化基元简单。树枝状聚合物核心具有超过相同分子量的线形或支化聚合物核心的优点,即它们增加辐射可固化组合物的粘度没有线形或支化聚合物核心那么多。这种低粘度行为使它们能够应用于低粘性辐射可固化组合物,比如辐射可固化喷墨油墨。
在又一个优选实施方案中,A选自丙烯酸酯和甲基丙烯酸酯。
在另一个优选实施方案中,L4选自取代或未被取代的亚烷基或脂族含醚基团。
在最优选的实施方案中,R4代表甲基。
在优选实施方案中,光引发部分INI是α-羟基烷基苯酮基团。
在优选实施方案中,光引发部分INI是取代的二苯酮基团或未被取代的二苯酮基团。
在优选实施方案中,光引发部分INI是取代的噻吨酮基团或未被取代的噻吨酮基团。
在优选实施方案中,光引发部分INI是膦氧化物基团。
典型的式(I)可聚合的聚合物光引发剂由表1给出,但不限于此。本领域技术人员明白聚合物引发剂具有分子量分布和取代度。为清楚起见,以一种具体分子量和/或一种取代度举例说明聚合物引发剂。
表1
可聚合的聚合物光引发剂的制备方法
为了制备本发明的可聚合的聚合物光引发剂,使用至少一种式(II)单体:
其中
R1、R2和R3独立选自氢、任选取代的烷基和任选取代的芳基,或者R1和R3代表形成5-8元环的必需原子;
L代表包含1-14个碳原子的任选取代的二价连接基团;和
A代表选自丙烯酸酯基、甲基丙烯酸酯基、苯乙烯基、丙烯酰胺基、甲基丙烯酰胺基、马来酸酯基、富马酸酯基、衣康酸酯基、乙烯基醚基、烯丙基醚基、烯丙基酯基、马来酰亚胺基、乙烯腈基和乙烯基酯基的自由基可聚合的基团。
在优选实施方案中,自由基可聚合的基团A选自丙烯酸酯和甲基丙烯酸酯,特别优选丙烯酸酯。
在又一个优选实施方案中,R2和R3都代表氢。
在优选实施方案中R1,代表氢。
在更优选的实施方案中,R1、R2和R3全部代表氢。
在优选实施方案中,二价连接基团L选自任选取代的亚烷基和脂族含醚基团。
优选二价连接基团L是-(-CH2-CH2-O-)n-CH2-CH2-,其中n是等于1、2、3、4、5或6的整数。
优选二价连接基团L是-(-CH2-)n-,其中n是等于1-14的整数,更优选n等于1、2、3、4、5或6。
优选的式(II)单体在表10给出,但不限于此。
表10
最优选的式(II)单体是由表10中化合物醚-1代表的丙烯酸2-(2-乙烯氧基乙氧基)乙基酯。
制备本发明的可聚合光引发剂的方法包括以下步骤:
a)提供包含至少一个羟基的聚合物光引发剂;
b)提供式(II)单体:
其中,
R1、R2和R3独立选自氢、烷基和芳基,或者R1和R3代表形成5-8元环的必需原子;
A代表选自丙烯酸酯基、甲基丙烯酸酯基、苯乙烯基、丙烯酰胺基、甲基丙烯酰胺基、马来酸酯基、富马酸酯基、衣康酸酯基、乙烯基醚基、烯丙基醚基、烯丙基酯基、马来酰亚胺基、乙烯腈基和乙烯基酯基的自由基可聚合的基团;和
L代表包含1-14个碳原子的任选取代的二价连接基团;和
c)用催化剂催化单体与聚合物光引发剂之间的反应以得到式(I)可聚合的聚合物光引发剂。
在可聚合的聚合物光引发剂制备方法的优选实施方案中,催化剂选自三氟乙酸、三氯乙酸、甲苯磺酸吡啶鎓、交联聚(乙烯基吡啶)盐酸盐、聚(乙烯基吡啶鎓)甲苯磺酸盐和磺酸取代的离子交换剂。
在最优选的实施方案中,反应在不存在有机溶剂的情况下进行。优点是不需要除去有机溶剂,这对于生态学原因和在制造辐射可固化喷墨油墨时都有利。在延长的非印刷时间的过程中,这些有机溶剂容易在喷墨印刷头的喷嘴蒸发。当再开印刷机时,一些喷嘴出现堵塞(=故障喷嘴)。等待时间是在故障喷嘴出现之前印刷头可打开盖子并闲置的时间。
因此用于制备可聚合光引发剂的本发明方法的主要优点是不需要有机溶剂而且可用式(II)单体作为反应介质。但是,在本发明制备可聚合的聚合物光引发剂的方法中仍然可以将一种或多种有机溶剂用于合成。
式(II)单体优选不仅用作反应物还用作反应介质。式(II)单体的浓度将比包含至少一个羟基的聚合物光引发剂的浓度高很多。优选式(II)单体与包含至少一个羟基的光引发剂的摩尔比至少为2,更优选至少5,最优选至少10。
还可以将其它单体加入反应介质中,即使是其它的式(II)单体。在后者的情况下,取决于不同式(II)单体的浓度,可获得不同的可聚合的聚合物光引发剂的混合物。
在完成反应后,辐射可固化组合物至少包括式(I)可聚合的聚合物光引发剂、式(II)单体和催化剂。在多数情况下,催化剂可保留在辐射可固化组合物中,条件是它不干扰可固化组合物的应用或固化。但是,最优选除去催化剂。催化剂可以是例如聚合物催化剂,并可引起UV可固化喷墨油墨不可接受的粘度。
包括至少一种能够自由基聚合的式(II)单体和由包含至少一个羟基官能团的光引发剂部分和式(II)单体衍生的可聚合光引发剂的所得组合物,可直接用于辐射可固化组合物的组成,适合食品包装应用。
如果具体应用需要,可将式(I)可聚合的聚合物光引发剂用现有技术中已知的任何技术比如沉淀、结晶和任选层析进行分离和纯化。
催化剂
用于通过将醇加入烯基醚、优选乙烯基醚中制备不对称缩醛的催化剂,包括具有足够低pKa的质子酸,比如盐酸、磷酸、磺酸、硫酸,和被吸电子基团比如氟和氯取代的羧酸。
合适的催化剂包括磺酸的有机盐,比如吡啶盐。磺酸作为催化剂的用途已公开于很多文件(如Munro等,Bioorganic and Medicinalchemistry,16(3),1279-1286(2008);Snowden等Helvetica ChimicaActa,89(12),3071-3086(2006),Lucatelli等,Journal of OrganicChemistry,67(26),9468-9470(2002);Wipf等,Tetrahedron Letters,40(28),5139-5142(1999))。典型实例是对甲苯磺酸、10-樟脑磺酸和甲磺酸。
盐酸的用途已公开于几个文件(如Trofimov等,TetrahedronLetters,49,3104-3107(2008))。磷酸的用途已由Toshiaki等公开(Tetrahedron Letters,47,3251-3255(2006))。
硫酸的用途已由Rappe等描述(Justus Liebigs Annalen der Chemie,601,84-111(1956))。
被吸电子取代基取代的羧酸的用途已公开于多个文件(如Rivillo等,Angewandte Chemie,国际版,46(38),7247-72450(2007);WO2007010483(Firmenich S;A.);Alvarez de Cienfuego等,Tetrahedron:asymmetry,17(2),1863-1866(2006);US2005171062(Allergan Inc.))。典型实例是三氟乙酸和三氯乙酸。
磺酸有机盐的用途已公开于几个文件(Lee等Bulletin of theKorean Chemical Society,28(4),513-514(2007);Hattori等,OrganicLetters,10(5),717-720(2008);Nakamura等,Organic Letters,10(2),309-312(2008);Nicolau等Journal of the American chemical Society,129(48),14850-14851(2007);Nakamura等,Tetrahedron,63(35),8670-8676(2007))。磺酸有机盐的典型实例是甲苯磺酸吡啶鎓。有时,路易斯酸也被报道作为催化剂(Alper.H.,Synthesis 1972,81)。
也已显示几种过渡金属有效地作为催化剂用于从烯基醚和醇合成不对称缩醛(Maity,G;Synth Commun 1993,23,1667;Iqbal,J;SynthCommun 1989,19,901;Kantam,M;Synth Commun 1993,23,2225;Bhuma,V;Synth Commun 1992,22,2941;Ma,S;Tetrahedron Lett 1993,34,5269;Molnar,A;Tetrahedron Lett 1996,37,8597)。
经常报道多相催化(Bongini,A;Synthesis 1979,618;Johnston,R;Synthesis 1988,393;Olah,G;Synthesis 1983,892;Menger,F;J OrgChem 1981,46,5044;Hoyer,S;Synthesis 1986,655;Upadhya,T;SynthCommun 1996,26,4539;Campelo,J;Synth Commun 1994,24,1345;Bandgar,B;Synth Commun 1995,25,2211;Kumar,P;Synthesis 1993,1069;Chavez,F;Synth Commun 1992,22,159;Patney,H;SynthCommun 1991,21,2329;Campelo,J;Synth Commun 1992,22,2335)。
也已报道丙酮基三苯基磷鎓衍生物作为催化剂用于将醇转化为不对称缩醛(Hon等,Tetrahedron,57,5991-6001)。
特别优选催化剂选自被吸电子基团取代的羧酸、磺酸的有机盐和多相催化剂,优选选自含有树脂的交联乙烯基吡啶和含有树脂的交联磺酸的盐。
最优选催化剂选自三氟乙酸、三氯乙酸、甲苯磺酸吡啶鎓、交联聚(乙烯基吡啶)盐酸盐、聚(乙烯基吡啶鎓)甲苯磺酸盐和磺酸取代的离子交换剂。
可用本领域已知的任何技术除去缩醛作用催化剂。优选将催化剂通过过滤、中和,然后过滤、在离子交换剂或碱性树脂上中和以及提取来除去。
辐射可固化组合物
本发明的辐射可固化组合物包括至少式(I)的可聚合光引发剂,最优选还包括至少一种式(II)单体。可聚合聚合物引发剂的优选量是总油墨重量的1-50wt%,更优选总油墨重量的1-25wt%。
辐射可固化组合物优选含有丙烯酸2-(2-乙烯氧基乙氧基)乙基酯作为式(II)单体。
辐射可固化组合物可作为无色液体或作为有色液体使用,在后一种情况下它称为辐射可固化油墨。
在优选实施方案中,本发明的辐射可固化组合物是辐射可固化喷墨组合物,更优选辐射可固化喷墨油墨。
辐射可固化组合物和油墨还可有利地用于胶版印刷、丝网印刷、柔版印刷及其它印刷或涂布技术。
辐射可固化组合物和油墨优选通过UV辐射固化。
在优选实施方案中,本发明的辐射可固化组合物实质上不含有机溶剂。
辐射可固化组合物和油墨优选是非水性液体或油墨。术语“非水性”指不应含水的液体载体。但有时可存在小量、基于组合物或油墨总重量计通常小于5wt%的水。这些水并非特意加入,而是作为污染经由其它组分比如极性有机溶剂进入组合物内。高于5wt%量的水容易使非水性液体和油墨不稳定,优选基于辐射可固化组合物或油墨总重量计含水量小于1wt%,最优选根本不存在水。
辐射可固化组合物和油墨优选不含可蒸发组分比如有机溶剂。但有时掺入小量有机溶剂可能有利于在UV固化后改善对衬底表面的粘附。在这种情况下,加入的溶剂可以是在不导致溶剂抗性和VOC问题范围内的任何量,优选0.1-10.0wt%,特别优选0.1-5.0wt%,各自基于可固化组合物或油墨的总重量计。
辐射可固化组合物和油墨优选是油墨套件(ink set)、更优选喷墨油墨套件的一部分,所述油墨套件包含至少一种含有一种或多种着色剂、优选一种或多种彩色颜料的油墨。可固化油墨套件优选包含至少一种黄色可固化油墨(Y)、至少一种青色可固化油墨(C)和至少一种品红可固化油墨(M),优选还包含至少一种黑色可固化油墨(K)。还可将可固化CMYK-油墨套件用额外的油墨比如红色、绿色、蓝色和/或橙色扩充,以进一步扩大图像的色域。还可将CMYK-油墨套件通过彩色油墨和/或黑色油墨的全密度和低密度油墨的组合扩充,以通过降低颗粒性改善图像质量。
着色的辐射可固化油墨优选含有分散剂,更优选聚合物分散剂,用于分散颜料。着色的可固化油墨可含有分散协合剂以改善分散质量和油墨稳定性。优选至少品红油墨含有分散协合剂。分散协合剂的混合物可用于进一步改善分散稳定性。
可固化液体和油墨的粘度优选在30℃和100s-1剪切速率小于100mPa.s。辐射可固化喷墨油墨和液体的粘度优选在100s-1剪切速率和10-70℃喷射温度小于50mPa.s,更优选低于30mPa.s,最优选2-15mPa.s。
可固化液体和油墨的表面张力优选在25℃为约20mN/m-约70mN/m,更优选在25℃为约22mN/m-约40mN/m。
可固化组合物或油墨还可进一步含有至少一种抑制剂以改善组合物或油墨的热稳定性。
可固化组合物或油墨还可进一步含有至少一种表面活性剂用于获得在衬底上的良好铺展特性。
共引发剂
本发明的辐射可固化组合物可含有一种或多种共引发剂。基于辐射可固化组合物总重量计,优选共引发剂的量是1-30wt%,更优选2-20wt%,最优选5-10wt%。
由于安全原因,特别是对于食品包装应用,本发明的辐射可固化组合物含有至少一种所谓扩散受阻共引发剂。扩散受阻共引发剂是在辐射可固化组合物或油墨固化层中表现比单官能、不可聚合的共引发剂比如苯甲酸二烷基氨基酯低很多的移动性的共引发剂。几种方法可用于降低共引发剂的移动性。一种方法是增加共引发剂的分子量以便减小扩散速度,如多官能共引发剂或聚合物共引发剂。另一种方法是增加它的反应性以便将它建入聚合网络内,如多官能共引发剂和可聚合共引发剂。
扩散受阻共引发剂优选选自非聚合物二或多官能共引发剂、低聚物或聚合物共引发剂和可聚合的共引发剂。非聚合物二或多官能共引发剂通常具有300-900道尔顿(Dalton)的分子量。具有该范围内分子量的多官能共引发剂不是扩散受阻共引发剂。
在本发明辐射可固化组合物的优选实施方案中,至少一种共引发剂是扩散受阻二烷基氨基取代的芳族化合物,选自低聚物或聚合物二烷基氨基取代的芳族化合物、多官能二烷基氨基取代的芳族化合物和包含至少一个可聚合烯属不饱和基团的二烷基氨基取代的芳族化合物。特别优选包含至少一个可聚合烯属不饱和基团的二烷基氨基取代的芳族化合物。
在更优选的实施方案中包含至少一个可聚合烯属不饱和基团的二烷基氨基取代的芳族化合物是式(C-I)的共引发剂:
其中,
R1和R2独立选自烷基、烯基、炔基、芳烷基、烷芳基、芳基和杂芳基;
R3-R6独立选自氢、烷基、烯基、炔基、酰基、硫代烷基、烷氧基、卤素、芳烷基、烷芳基、芳基和杂芳基;
R7选自氢、醛基、酮基、酯基、酰胺基、酰基、硫代烷基、烷氧基、卤素、腈基、磺酸基、磺酰胺基、烷基、烯基、炔基、芳烷基、烷芳基、芳基和杂芳基;
R1和R2、R1和R3、R2和R5、R3和R4、R4和R7、R5和R6以及R6和R7可代表形成5-至8-元环的必需原子;前提是芳族胺具有至少一个α-氢;和
R1-R7中至少一个包含选自丙烯酸酯、取代的丙烯酸酯、甲基丙烯酸酯、苯乙烯、丙烯酰胺、甲基丙烯酰胺、烯丙基酯、烯丙基醚、乙烯基酯、乙烯基醚、富马酸酯、马来酸酯、马来酰亚胺和乙烯腈的可聚合烯属不饱和官能团。在可聚合共引发剂中,优选R7代表选自醛、酮、酯和酰胺的吸电子基团,更优选R3、R4、R5和R6全部代表氢。
用于R1-R7的烷基、烯基、炔基、芳烷基、烷芳基、芳基和杂芳基可以是取代或未被取代的基团,即可使用取代或未被取代的烷基、取代或未被取代的烯基、取代或未被取代的炔基、取代或未被取代的芳烷基、取代或未被取代的烷芳基和取代或未被取代的(杂)芳基。
在优选实施方案中,可聚合的共引发剂对应于式(C-II):
其中,
R1-R6具有关于式(C-I)限定的相同含义;
X选自O、S和NR9;
R8和R9独立选自氢、烷基、烯基、炔基、芳烷基、烷芳基、芳基和杂芳基;
R1和R2、R1和R3、R2和R5、R3和R4、R5和R6、R4和R8、R6和R8以及R8和R9可代表形成5-至8-元环的必需原子;R1-R6和R8中至少一个包含选自丙烯酸酯、取代的丙烯酸酯、甲基丙烯酸酯、苯乙烯、丙烯酰胺、甲基丙烯酰胺、烯丙基酯、烯丙基醚、乙烯基酯、乙烯基醚、富马酸酯、马来酸酯、马来酰亚胺和乙烯腈的可聚合烯属不饱和官能团。在可聚合的共引发剂中,优选R3、R4、R5和R6全部代表氢。
在式(C-II)可聚合共引发剂的一个优选实施方案中,R1代表甲基或乙基,R2包含选自丙烯酸酯、取代的丙烯酸酯、甲基丙烯酸酯、苯乙烯、丙烯酰胺、甲基丙烯酰胺、烯丙基酯、烯丙基醚、乙烯基酯、乙烯基醚、富马酸酯、马来酸酯、马来酰亚胺和乙烯腈的可聚合烯属不饱和官能团;还更优选R3、R4、R5和R6全部代表氢。
在式(C-I)可聚合共引发剂的另一个优选实施方案中,R1和R2独立代表甲基或乙基,R8包含选自丙烯酸酯、取代的丙烯酸酯、甲基丙烯酸酯、苯乙烯、丙烯酰胺、甲基丙烯酰胺、烯丙基酯、烯丙基醚、乙烯基酯、乙烯基醚、富马酸酯、马来酸酯、马来酰亚胺和乙烯腈的可聚合烯属不饱和官能团;还更优选R3、R4、R5和R6全部代表氢。
在更优选的实施方案中,可聚合的共引发剂对应于式(C-III):
其中,
R1和R2独立选自甲基、乙基、丙基和丁基;
L代表包含至少一个碳原子的二价连接基团;和
R10代表氢、甲基、乙基、丙基或丁基。
在式(C-III)可聚合共引发剂的优选实施方案中,二价连接基团L包含1-30个碳原子,更优选2-10个碳原子,最优选3-6个原子。
可聚合的共引发剂可含有两个、三个或更多个独立选自丙烯酸酯、取代的丙烯酸酯、甲基丙烯酸酯、苯乙烯、丙烯酰胺、甲基丙烯酰胺、烯丙基酯、烯丙基醚、乙烯基酯、乙烯基醚、富马酸酯、马来酸酯、马来酰亚胺和乙烯腈的可聚合烯属不饱和官能团。
单体和低聚物
用于辐射可固化组合物和油墨(尤其用于食品包装应用)中的单体和低聚物,优选是没有或几乎没有杂质、更特别是没有毒性或致癌杂质的纯化化合物。杂质通常是在可聚合的化合物合成过程中获得的衍生化合物。但是,有时可故意将无毒量的一些化合物加入纯的可聚合化合物内,例如聚合抑制剂或稳定剂。
能够自由基聚合的任何单体或低聚物都可用作可聚合的化合物。还可使用单体、低聚物和/或预聚物的组合。单体、低聚物和/或预聚物可具备不同的官能度,可使用包括单-、二-、三-和更高官能度单体、低聚物和/或预聚物组合的混合物。可将辐射可固化组合物和油墨的粘度通过改变单体与低聚物之间的比率调节。
特别优选的单体和低聚物在作为具体引用结合到本文中的EP1911814 A(AGFA GRAPHICS)的[0106]-[0115]列出。
优选的单体和低聚物种类是乙烯基醚丙烯酸酯,比如描述于通过引用结合到本文中的US 6310115(AGFA)的那些。特别优选化合物是(甲基)丙烯酸2-(2-乙烯氧基乙氧基)乙基酯,最优选化合物是丙烯酸2-(2-乙烯氧基乙氧基)乙基酯。
抑制剂
辐射可固化组合物和油墨可含有聚合抑制剂。合适的聚合抑制剂包括酚型抗氧化剂、受阻胺光稳定剂、磷型抗氧化剂、常用于(甲基)丙烯酸酯单体中的氢醌单甲基醚,还可使用氢醌、叔丁基邻苯二酚、连苯三酚、2,6-二叔丁基-4-甲基酚。
合适的市售抑制剂是例如由Sumitomo Chemical Co.Ltd.生产的SumilizerTM GA-80、SumilizerTM GM和SumilizerTM GS;Rahn AG的GenoradTM 16、GenoradTM 18和GenoradTM 20;Ciba Specialty Chemicals的IrgastabTM UV10和IrgastabTM UV22、TinuvinTM 460和CGS20;Kromachem Ltd的FloorstabTM UV系列(UV-1、UV-2、UV-5和UV-8),Cytec Surface Specialties的AdditolTM S系列(S100、S110、S120和S130)。
抑制剂优选可聚合的抑制剂。
因为过量加入这些聚合抑制剂可降低固化速度,所以优选在共混之前测定能够预防聚合的量。聚合抑制剂的量优选低于总油墨或液体的5wt%,更优选低于3wt%。
表面活性剂
辐射可固化组合物和油墨可含有表面活性剂。表面活性剂可以是阴离子、阳离子、非离子或两性离子的,且加入的总量基于辐射可固化组合物或油墨总重量计通常小于10wt%,特别是基于辐射可固化组合物或油墨总重量计总计小于5wt%。
合适的表面活性剂包括公开于作为具体引用结合到本文中的WO2008/074548(AGFA GRAPHICS)的[0283]-[0291]段的表面活性剂。
着色剂
用于辐射可固化油墨中的着色剂可以是染料、颜料或其组合。可使用有机和/或无机颜料。着色剂优选颜料或聚合物染料,最优选颜料。
颜料可以是黑色、白色、青色、品红、黄色、红色、橙色、紫色、蓝色、绿色、棕色、其混合物等。该彩色颜料可选自公开于HERBST,Willy,等.Industrial Organic Pigments,Production,Properties,Applications.第三版.Wiley-VCH,2004.ISBN 3527305769的颜料。
合适的颜料公开于WO 2008/074548(AGFA GRAPHICS)的[0128]-[0138]段。
合适的颜料包括上述特定优选颜料的混合晶体。混合晶体也称为固溶体。例如,在一定条件下不同的喹吖啶酮互相混合以形成固溶体,固溶体与化合物的物理混合物和化合物本身二者都完全不同。在固溶体中,组分的分子进入相同晶格内,通常但不总是一种组分的晶格内。所得结晶固体的x-射线衍射图是该固体的特征,并可与相同比例的相同组分的物理混合物的图明显区分。在此类物理混合物中,可区别每种组分的x-射线图,而许多这些线的消失是形成固溶体的标准之一。市售实例是Ciba Specialty Chemicals的CinquasiaTM MagentaRT-355-D。
在辐射可固化油墨中还可使用颜料的混合物。对于一些喷墨应用,优选中性黑色喷墨油墨,并可例如通过将黑色颜料和青色颜料混合入油墨内获得。喷墨应用还可需要一种或多种斑点颜色(spot color),例如用于包装喷墨印刷或织物喷墨印刷。银色和金色经常是喷墨海报印刷和销售点展示的所需颜色。
非有机颜料可用于彩色喷墨油墨中。特定的优选颜料是C.I.Pigment Metal 1、2和3。无机颜料的示例性实例包括红氧化铁(III)、镉红、群青蓝、普鲁士蓝、氧化铬绿、钴绿、琥珀色、钛黑和合成铁黑。
在喷墨油墨中的颜料颗粒应足够小以容许油墨自由流动穿过喷墨印刷装置,尤其在喷射喷嘴处。同样合乎需要的是使用最大色强度的小颗粒以减慢沉降。
数均颜料粒度优选为0.050-1μm,更优选为0.070-0.300μm,特别优选为0.080-0.200μm。最优选,数均颜料粒度不大于0.150μm。平均粒度小于0.050μm由于降低耐光性而不太合乎需要,但主要还是因为非常小的颜料颗粒或其个别颜料分子在食品包装应用中仍然可被提取。基于动态光散射原理用Brookhaven Instruments Particle SizerBI90plus测定颜料颗粒的平均粒度。将油墨用乙酸乙酯稀释至0.002wt%的颜料浓度。BI90plus的测量设置是:在23℃运行5次,90°角,波长635nm和制图法=校正函数。
但是对于白色辐射可固化油墨,白色颜料的数均颗粒直径优选为50-500nm,更优选为150-400nm,最优选为200-350nm。当平均直径小于50nm时不能获得足够的遮盖力,而且当平均直径超过500nm时油墨的贮存能力和喷出适合性容易降低。最好通过光子相关谱在633nm波长用4mW HeNe激光器对着色喷墨油墨的稀释样品测定数均颗粒直径。所用合适的粒度分析仪是购自Goffin-Meyvis的MalvernTM nano-S。样品可以例如通过将一滴油墨加入含有1.5mL乙酸乙酯的试管内并混合直至获得均匀样品制备。测量的粒度是由6次20秒运行组成的3个连续测量的平均值。
合适的白色颜料由WO 2008/074548(AGFA GRAPHICS)的[0116]中表2给出。白色颜料优选折光率大于1.60的颜料。可以单种或组合使用白色颜料。优选二氧化钛用作折光率大于1.60的颜料。合适的二氧化钛颜料公开于WO 2008/074548(AGFA GRAPHICS)的[0117]和[0118]。
存在的颜料是0.01-10%重量,优选0.1-5%重量,各自基于辐射可固化油墨总重量计。对于白色辐射可固化油墨,白色颜料存在的量优选为油墨组合物重量的3%-30%,更优选5%-25%。小于3%重量的量不能实现足够的遮盖力,并通常表现非常差的贮存稳定性和喷射特性。
通常颜料通过分散剂比如聚合物分散剂稳定在分散介质中。但是,可将颜料的表面改性以获得所谓“可自分散的”或“自分散的”颜料,即可以不需要分散剂地分散在分散介质中的颜料。
分散剂
分散剂优选是聚合物分散剂。典型的聚合物分散剂是两种单体但可含有三种、四种、五种或甚至更多种单体的共聚物。聚合物分散剂的特性取决于单体的性质及其在聚合物中的分布。合适的共聚物分散剂具有下列聚合物组成:
·统计学上聚合的单体(如聚合成ABBAABAB的单体A和B);
·交替聚合的单体(如聚合成ABABABAB的单体A和B);
·梯度(锥形)聚合的单体(如聚合成AAABAABBABBB的单体A和B);
·嵌段共聚物(如聚合成AAAAABBBBBB的单体A和B)其中每种嵌段的嵌段长度(2、3、4、5或甚至更多)对于聚合物分散剂的分散能力是重要的;
·接枝共聚物(接枝共聚物由聚合物主链和与主链连接的聚合物侧链组成);和
·这些聚合物的混合形式,如嵌段梯度共聚物。
合适的聚合物分散剂列出于作为具体引用结合到本文中的EP1911814 A(AGFA GRAPHICS)的“分散剂”部分,更具体来讲在[0064]-[0070]和[0074]-[0077]中。
聚合物分散剂优选具有500-30000、更优选1500-10000的数均分子量Mn。
聚合物分散剂优选具有小于100000、更优选小于50000且最优选小于30000的重均分子量Mw。
聚合物分散剂优选具有小于2、更优选小于1.75且最优选小于1.5的多分散性PD。
聚合物分散剂的市售实例如下:
·购自BYK CHEMIE GMBH的DISPERBYKTM分散剂;
·购自NOVEON的SOLSPERSETM分散剂;
·来自DEGUSSA的TEGOTM DISPERSTM分散剂;
·来自LYONDELL的ETHACRYLTM分散剂;
·来自ISP的GANEXTM分散剂;
·来自CIBA SPECIALTY CHEMICALS INC的DISPEXTM和EFKATM分散剂;
·来自DEUCHEM的DISPONERTM分散剂;和
·来自JOHNSON POLYMER的JONCRYLTM分散剂。
特别优选的聚合物分散剂包括NOVEON的SolsperseTM分散剂、CIBA SPECIALTY CHEMICALS INC的EfkaTM分散剂和BYKCHEMIE GMBH的DisperbykTM分散剂。特别优选的分散剂是NOVEON的SolsperseTM 32000、35000和39000分散剂。
基于颜料重量计,优选聚合物分散剂的用量为2-600wt%,更优选5-200wt%。
分散协合剂
分散协合剂通常由阴离子部分和阳离子部分组成。分散协合剂的阴离子部分表现一定的与彩色颜料的分子相似性,而分散协合剂的阳离子部分由一种或多种质子和/或阳离子组成以补偿分散协合剂阴离子部分的电荷。
优选加入小于聚合物分散剂的量的协合剂。聚合物分散剂/分散协合剂的比率取决于颜料,应当用实验测定。通常将比率wt%聚合物分散剂/wt%分散协合剂选择为2∶1-100∶1,优选2∶1-20∶1。
可市售获得的合适的分散协合剂包括NOVEON的SolsperseTM5000和SolsperseTM 22000。
用于品红油墨的特别优选的颜料是二酮吡咯并吡咯颜料或喹吖啶酮颜料。合适的分散协合剂包括公开于EP 1790698 A(AGFAGRAPHICS)、EP 1790696 A(AGFA GRAPHICS)、WO 2007/060255(AGFA GRAPHICS)和EP 1790695 A(AGFA GRAPHICS)的分散协合剂。
在分散C.I.Pigment Blue 15:3时,优选使用磺酸化Cu-酞菁分散协合剂,如NOVEON的SolsperseTM 5000。用于黄色喷墨油墨的合适的分散协合剂包括公开于EP 1790697 A(AGFA GRAPHICS)的分散协合剂。
辐射可固化油墨的制备
平均粒度和分布是喷墨油墨的重要特点。油墨可通过在分散剂的存在下在分散介质中将颜料沉淀或研磨来制备。
混合装置可包括压力捏合机、开放式捏合机、行星式搅拌机、溶解器和Dalton Universal Mixer。合适的研磨和分散装置是球磨、珍珠磨、胶体磨、高速分散器、双滚筒机、砂磨机、涂料调节器和三滚筒机。分散体还可用超声能制备。
许多不同类型的材料可用作研磨介质,比如玻璃、陶瓷、金属和塑料。在优选实施方案中,研磨介质可包含颗粒,优选形状基本上为球形,如基本上由聚合物树脂组成的珠或钇稳定的氧化锆珠。
在混合、研磨和分散过程中,每种过程都伴随冷却进行以预防热的积累,对于辐射可固化油墨则尽可能在其中已基本排除光化辐射的光条件下进行。
油墨可含有多于一种的颜料,油墨可用每种颜料的单独分散体制备,或者备选地,在制备分散体时可将几种颜料混合和共研磨。
分散过程可以连续、分批或半分批模式进行。
磨机磨料成分的优选量和比率将根据具体材料和预期应用而变化很大。研磨混合物的内含物包含磨机磨料和研磨介质。磨机磨料包含颜料、聚合物分散剂和液体载体。对于喷墨油墨,颜料在磨机磨料中存在的量通常为1-50wt%,不包括研磨介质。颜料与聚合物分散剂的重量比是20∶1-1∶2。
研磨时间可变化很大,取决于颜料、选择的机械工具和停留条件、初始和所需的终粒度等。在本发明中可制备平均粒度小于100nm的颜料分散体。
在研磨完成后,将研磨介质从研磨的微粒产物(呈干燥或液体分散体形式)用常规分离技术分离,比如通过过滤、用网筛过筛等。经常将筛建入磨机如砂磨机内。优选将研磨的颜料浓缩物通过过滤与研磨介质分离。
一般来讲,合乎需要的是将油墨制备成浓缩磨机磨料的形式,随后将其稀释至适当浓度用于印刷系统。这种技术使能够用设备制备更大量的着色油墨。通过稀释,将油墨调节至所需的粘度、表面张力、颜色、色度、饱和密度和印刷覆盖区域用于特定应用。
喷墨印刷工具
本发明的可固化组合物和油墨可通过一个或多个印刷头喷射,所述印刷头将油墨小滴以受控方式通过喷嘴喷出在油墨接收表面上,该表面相对于印刷头移动。
喷墨印刷系统的优选印刷头是压电头。压电喷墨印刷是基于当对其施加电压时压电陶瓷换能器的移动。电压的施加改变压电陶瓷换能器在印刷头中的形状产生空隙,然后将其用油墨填充。当再次除去电压时,陶瓷扩大为其原有形状,从印刷头喷出油墨滴。但是本发明的喷墨印刷方法不限于压电喷墨印刷。可使用其它喷墨印刷头,包括各种类型,比如连续型以及热、静电和声学的按需滴落型。
在高印刷速度下,油墨必须很容易从印刷头喷出,这对油墨的物理特性有许多约束,如在可在25℃-110℃变化的喷射温度下低粘度,表面能以便印刷头喷嘴可形成必需的小滴,能够快速转化至干燥印刷区的均匀油墨,…
喷墨印刷头正常在横跨移动的油墨接收表面的方向上来回扫描。在返回途中喷墨印刷头经常不印刷。双向印刷优选用于获得高面积通量。另一种优选印刷方法是通过“单趟印刷法”,可通过使用页宽喷墨印刷头或覆盖油墨接收表面整个宽度的多个交错喷墨印刷头进行。在单趟印刷过程中,喷墨印刷头通常保持静止,在喷墨印刷头下输送油墨接收表面。
固化工具
本发明的可固化组合物和油墨可通过将它们暴露于光化辐射,优选通过紫外线辐射固化。
在喷墨印刷时,固化工具可与喷墨印刷机的印刷头组合排列,随其移动以便可固化组合物在喷射后非常短时间内暴露于固化辐射。
在此类排列中,可能难以提供与印刷头连接并随其移动的足够小的辐射源。因此,可采用静止固定的辐射源,如固化UV-光源,通过柔性辐射传导工具比如光纤束或内反射柔管与辐射源连接。
备选地,可通过包括在辐射头上的镜子的镜子排列将光化辐射从固定来源供应至辐射头。
被安排不随印刷头移动的辐射源,还可以是横跨待固化油墨接收表面延伸并靠近印刷头横向路径的狭长辐射源,以便在该辐射源下方,分步或连续经过印刷头形成的图像的后续各行。
任何紫外线光源,只要发射光的部分可被光引发剂或光引发剂系统吸收,都可用作辐射源,比如高或低压汞灯、冷阴极管、黑光灯、紫外线LED、紫外线激光器和闪光灯。其中,优选来源是表现具有300-400nm主波长的相对长的波长的UV-贡献的来源。具体来讲,优选UV-A光源,因为它的光散射减小导致更有效的内部固化。
UV辐射通常分为如下的UV-A、UV-B和UV-C:
·UV-A:400nm-320nm
·UV-B:320nm-290nm
·UV-C:290nm-100nm。
而且,可以用不同波长或照度的两种光源连续或同时使图像固化。例如,可选择第一种UV-源富含UV-C,特别是在260nm-200nm范围。然后第二种UV-源可富含UV-A,如掺杂镓的灯,或者UV-A和UV-B均高的不同的灯。已发现使用两种UV-源具有优点如固化速度快和固化程度高。
为了有助于固化,喷墨印刷机经常包括一个或多个氧消耗单元。氧消耗单元放置一层氮气或其它相对惰性的气体(如CO2),具有可调节的位置和可调节的惰性气体浓度,以减小固化环境中的氧浓度。残留的氧水平通常维持低至200ppm,但通常在200ppm-1200ppm范围。
实施例
材料
除非另外指定,用于下列实施例的所有材料很容易购自AldrichChemical Co.(Belgium)。
所用水是去离子水。
DPGDA是SARTOMER的二丙烯酸二丙二醇酯。
VEEA是丙烯酸2-(乙烯基乙氧基)乙基酯,购自NIPPONSHOKUBAI,Japan的二官能单体。
VEEM是甲基丙烯酸2-(乙烯氧基乙氧基)乙酯,购自NIPPONSHOKUBAI,Japan的二官能单体。
M600是六丙烯酸二季戊四醇酯,为购自RAHN AG的MiramerTMM600的缩写。
GenopolTM TX是购自Rahn AG的低聚物噻吨酮。
GenopolTM AB是购自Rahn AG的低聚物4-二甲基苯甲酸衍生物。
丙烯酸异癸酯是购自Sartomer的SR395。
LewatitTM M600MB来自BAYER。
S35000是SOLSPERSETM 35000的缩写,来自NOVEON的聚乙烯亚胺-聚酯超分散剂。
HostapermTM Blue P-BFS,购自CLARIANT的青色颜料(C.I.Pigment Blue 15:4)。
BykTM-333是购自BYK CHEMIE GMBH的表面活性剂。
PET100是100μm未涂胶层的PET衬底,背侧是具有抗静电特性的防粘连层,以P100C PLAIN/ABAS购自AGFA-GEVAERT。
GenoradTM 16是RAHN AG的聚合抑制剂。
DCC是二环己基碳二亚胺。
DCU是二环己基脲(dicyclohexylureum)。
COMPINI-1是具有以下结构的二苯酮型抑制剂:
COMPINI-1如下合成:
(4-苯甲酰基苯氧基)-乙酸根据Chen等,MacromolecularChemistry and Physics(2007),208(15),1694-1706制备。使25.6g(0.10mol)(4-苯甲酰基苯氧基)-乙酸溶于100mL甲苯和30mL二甲基乙酰胺中。加入14.8g(0.20mol)仲丁醇和28g(0.15mol)对甲苯磺酸。将反应混合物在共沸除去水的条件下回流。加入250mL乙酸乙酯,用200mL 1N NaOH提取混合物。将有机流分用MgSO4干燥,减压除去溶剂。分离呈白色结晶化合物的COMPINI-1。分离29.8g(95%)COMPINI-1。
Type I是具有以下结构的a-烷氧基-酮Norrish type I引发剂:
该引发剂已根据以下步骤制备:将80g(0.36mol)由Ciba SpecialtyChemicals供应的Darocure 2959加入177.05g(0.95mol)丙烯酸2-(乙烯氧基乙氧基)乙基酯和80mL乙酸乙酯的混合物内。加入1.6g BHT(7.1mmol)和532μL(6.9mmol)三氟乙酸,将混合物加热至70℃。让反应在70℃继续8小时。离子交换剂1的激活:将25g LewatitTM M600MB用75mL 1N氢氧化钠溶液处理并搅拌2小时。将离子交换剂过滤分离,用水洗涤几次并干燥直至恒重。让反应混合物冷却至室温,加入20g活化离子交换剂1。将混合物在室温下搅拌1小时。过滤除去离子交换剂,减压除去乙酸乙酯。通过1H-NMR分析来分析可聚合的Type I引发剂,证明是在丙烯酸2-(乙烯氧基乙氧基)乙基酯中的86w%溶液。将溶液就这样用于辐射可固化组合物中。
COINI-1是具有以下结构的4-二甲基氨基-苯甲酸衍生物:
合成已公开于EP 2033949 A(AGFA GRAPHICS)的实施例1。
COMPINI-2是Lucirin TPO-L,由BASF供应:
Type II是具有以下结构的可聚合的噻吨酮:
引发剂根据以下流程制备:
2-羟基-9H-噻吨-9-酮的制备:
使90.8g(0.59mol)硫代水杨酸溶于840mL浓硫酸中。加入240g(2.54mol)苯酚,温度上升至75℃。让反应继续2小时,同时缓慢冷却至室温。将反应混合物在60℃缓慢加入1300mL水中。让混合物冷却至室温,将粗制2-羟基-9H-噻吨-9-酮过滤分离。使粗制2-羟基-9H-噻吨-9-酮悬浮于150mL冰和200mL水中。用5N KOH将pH调节至13.5。完成溶解后,用乙酸将pH调节至5.4。将2-羟基-9H-噻吨-9-酮过滤分离,并在75℃用200mL水处理30分钟。将2-羟基-9H-噻吨-9-酮过滤分离、洗涤和干燥。分离30g 2-羟基-9H-噻吨-9-酮。
Type II的制备:
使28.2g(0.13mol)2-羟基-9H-噻吨-9-酮悬浮于204.8g(1.1mol)丙烯酸2-(乙烯氧基乙氧基)乙基酯中。加入0.5g BHT。将反应混合物加热至70℃,加入0.37mL(4.8mmol)三氟乙酸。在70℃让反应继续3小时。让反应混合物冷却至室温,加入35g活化离子交换剂1。将混合物在室温下搅拌1小时。过滤除去离子交换剂,丙烯酸2-[2-[1-(9-氧代-9H-噻吨-2-基氧基)-乙氧基]-乙氧基]乙酯在VEEA中的溶液就这样用于辐射可固化组合物中。
测量方法
1.1H-NMR谱的测量
1H-NMR谱如下记录:使100mg每种预制剂的样品溶于0.7mLCDCl3中。加入TMS作为位移参考。将波谱记录在600MHz Varian波谱仪上(谱窗10924Hz(~18ppm),采集时间5s,驰豫延迟10s,脉冲宽度45deg,瞬态数:32)。
2.固化度
在用UV光固化后立即在涂层上测试固化度。用Q-tip工具摩擦固化涂层。当表面不损伤时,涂层完全固化。当可以损伤一些固化涂层时,涂层只是部分固化。当整个固化涂层都损伤时,涂层不固化。
3.固化速度
将在Fusion DRSE-120传送机上的固化速度定义为固化样品需要灯的最大输出的百分数。数字越低固化速度越高。当用Q-tip刮划也没有可见的损伤时将样品视为完全固化。
超过灯的最大输出100%的百分数意味着必须减小传送带的速度以使样品在灯的最大输出完全固化。百分数越高,带必须减慢越多。固化速度160%意味着在灯的最大输出下带速为12.5m/min。150%-200%的百分数视为实际使用的界限。高于200%的百分数视为在实际使用范围之外,不测量更高的百分数。
实施例1
本实施例说明本发明聚合物减小的可提取性。
聚合物噻吨酮的衍生,POLY-7的合成:
用1H-NMR和HPLC分析GenopolTM TX(由Rahn A.G.供应)。发现它是化合物的混合物。在混合物中的主要组分证明具有以下结构:
用1H-NMR测定平均酯化度。在供应的批料中,平均1.5个羟基转化为噻吨酮酯,导致平均剩余1.5个羟基。每种酯化度都显示一种乙氧基化程度的分布,导致低聚物的复杂混合物,既具有羟基也具有噻吨酮端基。
预制剂1的制备:
根据以下步骤,将聚合物引发剂进一步转化为可聚合的聚合物光引发剂,产生聚合物的混合物,具有以下结构作为主要组分:
离子交换剂的预处理:将25g LewatitTM M600MB用75mL 1N氢氧化钠处理,并搅拌2小时。将离子交换剂过滤分离,用水洗涤几次和干燥直至恒重。
使10g GenopolTMTX溶于30g丙烯酸2-(2-乙烯氧基乙氧基)乙基酯中。加入125mg三氟乙酸,让反应在50℃继续16小时。让反应混合物冷却至室温。加入25g预处理的离子交换剂,将混合物在室温下搅拌1小时。过滤除去离子交换剂以得到预制剂1。
用LCMS分析混合物。使1mg预制剂1溶于20mL乙腈中,并用流动注射LCMS(阳性模式,combi ESI-APCI,流速:0.5ml/min,操作温度:40℃,洗脱剂:MeOH,10%乙酸铵,质量范围500-1400)分析。LCMS分析表明羟基的完全转化。预制剂1可直接用于制备辐射可固化组合物。
辐射可固化组合物的制备和评价
制备浓缩颜料分散体Dispersion 1,这是通过用DISPERLUXTMYELLOW075(来自DISPERLUX S.A.R.L.,Luxembourg)将466.7g 30wt%的S35000聚合物分散剂在VEEA中的溶液、86.3g VEEA、7.0g稳定剂GenoradTM16和140.0g HostapermTM Blue P-BFS混合30分钟,接着用0.4mm直径钇稳定的氧化锆珠(来自TOSOH Co.的“高耐磨氧化锆研磨介质”)在Eiger Lab Bead磨(来自EIGER TORRANCE Ltd.)中研磨该混合物。将砂磨机的52%用研磨珠填充,在以4250rpm研磨220分钟过程中用水冷却。在研磨后用滤布将分散体与珠分离。浓缩颜料分散体Dispersion 1具有用MalvernTM nano-S粒度分析仪测量为113nm的平均粒度和在10s-1和25℃为129mPa.s的粘度。
预制剂1直接用于制备本发明的辐射可固化组合物。
将可聚合的聚合物光引发剂POLY-7的可提取性与原料GenopolTM TX在相同组合物中的可提取性相比。比较的辐射可固化组合物COMP-1至COMP-5根据表2制备。本发明的辐射可固化组合物INV-1至INV-5根据表3制备。重量%(wt%)是基于辐射可固化组合物的总重量计。
表2
表3
wt%: | INV-1 | INV-2 | INV-3 | INV-4 | INV-5 |
DPGDA | 14.40 | 13.15 | 10.90 | 14.40 | 13.15 |
M600 | 16.30 | 16.30 | 16.30 | 16.30 | 16.30 |
VEEA | 15.75 | 15.75 | 15.75 | 26.25 | 22.5 |
预制剂1 | 19.00 | 19.00 | 19.00 | 5.00 | 10.00 |
GenopolTM AB | 1.25 | 2.50 | 4.75 | 4.75 | 4.75 |
丙烯酸异癸酯 | 18.30 | 18.30 | 18.30 | 18.30 | 18.30 |
Dispersion 1 | 15.00 | 15.00 | 15.00 | 15.00 | 15.00 |
将30mg BykTM-333加入每一种比较的和本发明的辐射可固化组合物中。
辐射可固化组合物的涂布和固化
用刮条涂布机和10μm铁丝刮条(wired bar)将自由基可固化液体COMP-1至COMP-5和INV-1至INV-5涂在PET100衬底上。每种涂布样品都用配备Fusion VPS/I600灯(D-bulb)的Fusion DRSE-120传送机固化,该机器将样品在UV-灯下在传送带上以10m/min的速度输送2次。样品在氮惰性条件下固化。在将涂布的样品放在传送带上之前,将涂布的样品安装在金属板上,并在板的上方放置具有非UV-吸收石英玻璃窗的1cm高金属架,以便与内部的涂布样品形成气密室。然后,通过将纯氮气引入该室内30秒用氮气代替室内截留空气。发现所有固化的样品都完全固化。
可提取低聚物噻吨酮的量的评价
然后评价每种固化样品COMP-1至COMP-5和INV-1至INV-5的可提取低聚物噻吨酮的量。
将两种COMP-1至5和INV-1至INV-5的7.068cm2样品放入50mL烧杯内,用超声用4.5mL乙腈提取30分钟。将提取物转移至5mL容量瓶内。将样品用小量乙腈漂洗2次,将漂洗溶剂转移至5mL容量瓶内直至将体积调节至5mL。将溶液充分混合,用0.45mm滤器过滤。将10mL各样品注在HPLC上。
与每种比较的和本发明的引发剂的已知浓度的参考样品相比测定浓度,参考样品在与提取样品相同的条件下洗脱。
假定各样品的总涂层重量为10g/m2。
使用由Alltech供应的Alltime C18 5mm柱(150×3.2mm)。在40℃温度使用0.5mL/min流速。用在254nm的DAD检测器检测提取的引发剂。
以下HPLC方法用于所有样品。
洗脱剂A:H2O
洗脱剂B:CH3CN
表4
时间(min) | %洗脱剂A | %洗脱剂B |
0 | 55 | 45 |
6 | 55 | 45 |
11 | 0 | 100 |
30 | 0 | 100 |
31 | 55 | 45 |
38 | 55 | 45 |
结果总结于表4。将结果用食品ppb表示。如上所述测定以μg表示的在14.136cm2中可提取的低聚物噻吨酮的量。将其再计算为600cm2,相当于1升立方体的表面。可提取的低聚物噻吨酮的再计算量相当于可提取入1升食品刺激剂内的最大量,将其定义为食品ppb。
表5
辐射可固化组合物 | 可提取的低聚物噻吨酮(食品ppb) |
COMP-1 | 3133 |
INV-1 | 594 |
COMP-2 | 3127 |
INV-2 | 354 |
COMP-3 | 561 |
INV-3 | 105 |
COMP-4 | 1150 |
INV-4 | 172 |
COMP-5 | 2714 |
INV-5 | 380 |
根据表5显然的是,将羟基官能化低聚物噻吨酮系统地转化为可聚合的低聚物噻吨酮导致可提取的残留物明显减少。
实施例2
本实施例说明可聚合的聚合物光引发剂POLY-8和POLY-11的合成。
合成
聚合物光引发剂POLY-8和POLY-11根据以下反应流程制备:
其中POLY-8中的R=H,POLY-11中的R=Me
中间体二苯酮衍生的聚缩水甘油的制备
使8g平均分子量为2000的超支化聚缩水甘油(根据WO2000/37532(Bayer A.-G.)和Sunder A.等,Macromolecules,32,4240-4246(1999)制备)在40℃溶于200mL二甲基乙酰胺中。加入12.9g(62mmol)DCC,将混合物搅拌30分钟。加入13.3g(52mmol)2-(4-苯甲酰基苯氧基)-乙酸,在60℃使反应继续16小时。过滤除去沉淀的DCU,减压蒸发溶剂。将残留物用150mL二氯甲烷处理,并使混合物冷却至0℃。1小时后,过滤除去沉淀的DCU,并减压蒸发溶剂。将二苯酮取代的超支化聚缩水甘油通过制备大小排阻层析在60×2.5cm柱上纯化,PL-gel 10微米,孔径=500A,Mw范围:500-30000,由Polymer Laboratories供应,使用四氢呋喃、5%乙酸作为洗脱剂,流速为10mL/min,产物载量为每次运行200mg。将汇集的流分减压蒸发。使残留物再溶于1000mL二氯甲烷中,用500mL盐水提取,经MgSO4干燥,减压除去溶剂。分离6.5g二苯酮取代的聚缩水甘油。1H-NMR-分析显示分离的聚合物平均被7个二苯酮部分取代。
POLY-8的合成
在70℃使4.5g二苯酮衍生的超支化聚缩水甘油溶于11.5mL(12g,65mmol)VEEA中。加入18mg由Aldrich供应的25%二乙烯基苯交联的聚乙烯基吡啶甲苯磺酸酯树脂,让反应在70℃继续4小时,在室温再继续16小时。过滤除去催化剂,POLY-8在VEEA中的溶液就这样用于实施例3的辐射可固化组合物中。
POLY-11的合成
在70℃使2g二苯酮衍生的超支化聚缩水甘油溶于5mL(5.15g,26mmol)VEEM中。加入8.1mg由Aldrich供应的25%二乙烯基苯交联的聚乙烯基吡啶甲苯磺酸酯树脂,让反应在70℃继续4小时,在室温再继续16小时。过滤除去催化剂,POLY-11在VEEM中的溶液就这样用于实施例3的辐射可固化组合物中。
实施例3
本实施例说明POLY-8在辐射可固化组合物中的固化速度和可提取性的优点。
辐射可固化组合物的制备和评价
根据表6制备比较的辐射可固化组合物COMP-6和本发明的辐射可固化组合物INV-6。重量%(wt%)是基于辐射可固化组合物的总重量计。将邻苯二甲酸二丁酯加入辐射可固化组合物内作为内标物以使能够分析可提取的残留物。
表6
COMP-6 | INV-6 | |
COMPINI-1 | 7.5 | - |
POLY-8在VEEA中 | - | 50.0 |
Type I | 7.5 | 7.5 |
COINI-1 | 7.5 | 7.5 |
M600 | 15.0 | 15.0 |
VEEA | 60.5 | 18.0 |
邻苯二甲酸二丁酯 | 2.0 | 2.0 |
固化速度
用刮条涂布机和10μm铁丝刮条将自由基可固化液体COMP-6和INV-6涂在PET100衬底上。每种涂布样品都用配备Fusion VPS/I600灯(D-bulb)的Fusion DRSE-120传送机固化,该机器将样品在UV-灯下在传送带上以20m/min的速度输送。测定固化速度,显示于表7。
表7
辐射可固化样品 | 固化速度(最大输出%) |
COMP-6 | >400 |
INV-6 | 85 |
根据表7清楚的是,与具有相同吸收谱的低分子参考引发剂相比,本发明的超支化光引发剂导致明显更高的固化速度。
POLY-8的可提取性
将两种7.068cm2的INV-6样品放入50mL烧杯内,用超声用4.5mL乙腈提取30分钟。将提取物转移至5mL容量瓶内。将样品用小量乙腈漂洗2次,将漂洗溶剂转移至5mL容量瓶内直至将体积调节至5mL。将溶液充分混合,用0.45μm滤器过滤。将100μL各样品注在GPC上。
与引发剂的已知浓度参考样品相比测定浓度,参考样品在与提取样品的相同条件下洗脱。
假定各样品的总涂层重量为10g/m2。
使用3*混合B柱组,用聚苯乙烯标准品校正。THF/5%乙酸用作洗脱剂。使用RI-检测器。流速是1.5ml/min,在40℃洗脱样品。
在GPC示踪中检测不到POLY-8残留物。这说明本发明的超支化光引发剂完全建入网络内。
实施例4
本实施例说明可聚合的聚合物光引发剂POLY-12和POLY-13的合成。
POLY-12和POLY-13的合成
可聚合的聚合物光引发剂POLY-12和POLY-13根据以下流程制备:
苯基(2,4,6-三甲基苯甲酰基)膦氯化物根据DE10206117(BASFA.-G.)制备。
在50℃使6.5g平均分子量为2000的超支化聚缩水甘油(根据WO2000/37532(Bayer A.-G.)和Sunder A.等,Macromolecules,32,4240-4246(1999)制备)溶于160mL二甲基乙酰胺中。加入7.2mL(5.22g,52mmol)三乙胺和14.5g(43mmol)苯基(2,4,6-三甲基苯甲酰基)膦氯化物。让反应在室温下继续16小时。过滤除去沉淀的盐,减压蒸发溶剂。将粗制酰基膦氧化物取代的超支化聚缩水甘油通过制备大小排阻层析在60×2.5cm柱上纯化,PL-凝胶10微米,孔径=Mw范围:500-30000,由Polymer Laboratories供应,用四氢呋喃、5%乙酸作为洗脱剂,流速为10mL/min,产物载量为每次运行200mg。将汇集的流分减压蒸发。使残留物再溶于最小量乙酸乙酯中,用己烷沉淀。将油状聚合物流分分离和减压干燥。
POLY-12的合成
使3.6g酰基膦氧化物取代的超支化聚缩水甘油溶于50mL二氯甲烷中。加入9mL VEEA、0.3g BHT和1g 25%二乙烯基苯交联的聚乙烯基吡啶甲苯磺酸酯树脂(由Aldrich供应),让反应在室温下继续16小时。过滤除去交联的聚乙烯基吡啶甲苯磺酸酯树脂,减压蒸发溶剂。分离11.5g POLY-12在VEEA中的溶液。溶液就这样用于辐射可固化组合物中。
POLY-13的合成
在40℃使3g酰基膦氧化物取代的超支化聚缩水甘油溶于50mL二氯甲烷中。加入7.7mL VEEM、0.3g BHT和1g 25%二乙烯基苯交联的聚乙烯基吡啶甲苯磺酸酯树脂(由Aldrich供应),让反应在室温下继续16小时。过滤除去交联的聚乙烯基吡啶甲苯磺酸酯树脂,减压蒸发溶剂。分离POLY-13在VEEM中的11.2g溶液。溶液就这样用于辐射可固化组合物中。
实施例5
本实施例说明辐射可固化组合物中POLY-12和POLY-13的优点。
辐射可固化组合物的制备和评价
比较的辐射可固化组合物COMP-7和本发明的辐射可固化组合物INV-7和INV-8根据表8制备。重量%(wt%)是基于辐射可固化组合物总重量计。将邻苯二甲酸二丁酯作为内标物加入辐射可固化组合物中使能够分析可提取的残留物。
表8
wt%: | COMP-7 | INV-7 | INV-8 |
COMPINI-2 | 7.5 | - | - |
POLY-12在VEEA中 | - | 40.0 | - |
POLY-13在VEEM中 | - | - | 40.0 |
Type II | 7.5 | 7.5 | 7.5 |
COINI-1 | 7.5 | 7.5 | 7.5 |
M600 | 15.0 | 15.0 | 15.0 |
VEEA | 60.5 | 28 | 28 |
邻苯二甲酸二丁酯 | 2.0 | 2.0 | 2.0 |
固化速度
用刮条涂布机和10μm铁丝刮条将自由基可固化液体COMP-7、INV-7和INV-8涂在PET100衬底上。每种涂布样品都用配备FusionVPS/I600灯(D-bulb)的Fusion DRSE-120传送机固化,该机器将样品在UV-灯下在传送带上以20m/min的速度输送。测定固化速度,显示于表9。
表9
根据表9显然的是,本发明的超支化光引发剂具有良好至优秀的固化速度。
POLY-12和POLY-13的可提取性
将两种7.068cm2的INV-7和INV-8样品放入50mL烧杯内,用超声用4.5mL乙腈提取30分钟。将提取物转移至5mL容量瓶内。将样品用小量乙腈漂洗2次,将漂洗溶剂转移至5mL容量瓶内直至将体积调节至5mL。将溶液充分混合,用0.45μm滤器过滤。将100μL各样品注在GPC上。
与引发剂已知浓度的参考样品相比测定浓度,参考样品在与提取样品的相同条件下洗脱。
假定各样品的总涂层重量为10g/m2。
使用3*混合B柱组,用聚苯乙烯标准品校正。THF/5%乙酸用作洗脱剂。使用RI-检测器。流速是1.5ml/min,在40℃洗脱样品。
在GPC示踪中检测不到POLY-12和POLY-13残留物。这说明本发明的超支化光引发剂完全建入网络内。
Claims (13)
1.一种式(I)的可聚合的聚合物光引发剂:
其中:
PL代表n+m+p-官能的聚合物核心;
n和m独立代表整数1-30;
p代表整数0-10;
o是0或1;
INI代表选自二苯酮、噻吨酮、咔唑、蒽醌、樟脑醌、α-羟基烷基苯酮、α-氨基烷基苯酮、酰基膦氧化物、二酰基膦氧化物、酰基膦硫化物、乙醛酸苯酯、安息香醚、苄缩酮、α-二烷氧基苯乙酮、咔唑基-O-酰基-肟、α-卤代芳基酮和α-卤代芳基砜的基团;
L3和L4代表包含1-14个碳原子的取代或未被取代的二价连接基团;
A代表选自丙烯酸酯、甲基丙烯酸酯、苯乙烯、丙烯酰胺、甲基丙烯酰胺、马来酸酯、富马酸酯、衣康酸酯、乙烯基醚、烯丙基醚、烯丙基酯、马来酰亚胺、乙烯腈和乙烯基酯的自由基可聚合的官能团;和
R4代表烷基。
2.权利要求1的可聚合的聚合物光引发剂,其中PL代表基于聚醚、聚酯或聚酰胺的聚合物核心。
3.权利要求1或2的可聚合的聚合物光引发剂,其中n+m+p代表整数2-50。
4.权利要求1-3中任一项的可聚合的聚合物光引发剂,其中PL代表星形、支化或树枝状聚合物核心。
5.权利要求1-4中任一项的可聚合的聚合物光引发剂,其中L4选自亚烷基或脂族含醚基团。
6.权利要求1-5中任一项的可聚合的聚合物光引发剂,其中R4代表甲基。
7.一种辐射可固化组合物,其包含权利要求1-6中任一项的可聚合的聚合物光引发剂。
8.权利要求7的辐射可固化组合物,其中所述辐射可固化组合物是辐射可固化喷墨油墨。
9.权利要求7或8的辐射可固化组合物,其含有丙烯酸2-(2-乙烯氧基乙氧基)乙基酯。
10.权利要求7-9中任一项的辐射可固化组合物,其实质上不含有机溶剂。
12.权利要求11的方法,其中所述催化剂选自三氟乙酸、三氯乙酸、甲苯磺酸吡啶鎓、交联聚(乙烯基吡啶)盐酸盐、聚(乙烯基吡啶鎓)甲苯磺酸盐和磺酸取代的离子交换剂。
13.权利要求11-12中任一项的方法,其中所述反应在不存在有机溶剂的情况下进行。