CN102409537B - 一种防缩防皱、吸湿快干型衬衫领衬的后整理工艺 - Google Patents

一种防缩防皱、吸湿快干型衬衫领衬的后整理工艺 Download PDF

Info

Publication number
CN102409537B
CN102409537B CN201110356813.0A CN201110356813A CN102409537B CN 102409537 B CN102409537 B CN 102409537B CN 201110356813 A CN201110356813 A CN 201110356813A CN 102409537 B CN102409537 B CN 102409537B
Authority
CN
China
Prior art keywords
drying
finishing
padding
quick
fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201110356813.0A
Other languages
English (en)
Other versions
CN102409537A (zh
Inventor
戴建
张冯兵
左小慧
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong hymo industrial Limited by Share Ltd
Original Assignee
Rugao Wushan Bleach and Dyeing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rugao Wushan Bleach and Dyeing Co Ltd filed Critical Rugao Wushan Bleach and Dyeing Co Ltd
Priority to CN201110356813.0A priority Critical patent/CN102409537B/zh
Publication of CN102409537A publication Critical patent/CN102409537A/zh
Application granted granted Critical
Publication of CN102409537B publication Critical patent/CN102409537B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种防缩防皱、吸湿快干型衬衫领衬的后整理工艺：选取聚乙烯硅氧烷的改性物作为后整理剂的快干吸湿剂30-40g/l，与一定浓度量的树脂、Cat.D催化剂配置成PH值为4.5的浸轧液；再将待整理织物置于浸轧液中，待浸轧率达80%时，进行预烘和焙烘两个步骤。本发明的浸轧整理液内起主要吸湿快干作用的为聚乙烯硅氧烷的改性物，聚乙烯硅氧烷的改性物适用于棉、涤及其混纺交织物吸湿快干整理，并赋予织物极佳的柔软手感。聚乙烯硅氧烷的改性物采用浸扎法可单独使用，也可与防缩防皱整理剂及硬挺树脂等初缩体协同使用，减少纤维孔道的溶胀率并获得更佳的吸湿快干效果。

Description

一种防缩防皱、吸湿快干型衬衫领衬的后整理工艺
技术领域
本发明涉及一种衬衫领衬的后整理工艺，具体是一种采用浸轧的方法实现后整理的工艺。
背景技术
当前，随着社会的文明进步和人们生活水平的不断提高，人们对服饰的需求早已突破其遮体、防寒、保暖的原有基本功能，而是向追求个性化、风格化和功能的多样化方向发展。为适应上述形势的发展变化，纺织印染行业及染料助剂行业均进行了大量的研究和探索，大量采用新材料、新技术、新工艺生产的新型纺织品不断涌现，它们除了满足人们日益提高的日常生活及服用需求外，还渗透到社会生产的各个方面，为纺织品寻求到新的生存发展空间。     这其中，对各类普通纺织品，如棉、麻、涤棉、化纤及其混纺织物、色织物等进行不同类型的功能性后整理，使其在保有原纤维织造特性的基础上，赋予更优的服用性能及更广泛的其他用途功能，使纺织品的功能得以延伸和发展，便是重要的途径之一。     
功能性后整理的主要途径：
机械物理整理法：机械物理法整理工艺一般有机械柔软、拉幅定型、预缩、磨毛、磨绒、光泽整理、轧花等。它们均是利用机械作用力并配合一定的温度、湿度等工艺条件，使织物纤维的表面性状或内部组织产生纯物理性变化，而达到不同的整理效果及服用性能。 
化学助剂整理法：采用各类化学助剂对纺织品进行功能性后整理的工艺方法种类繁多，并且随着人们使用要求的不断发展变化及各种新型后整理助剂的不断涌现，各种新的后整理工艺方法也是层出不穷。目前较为常见的化学助剂法后整理工艺有上浆整理、涂层整理、增白拉幅、柔软整理、树脂整理、免烫防皱整理、拒水，防污，防油整理、易去污整理、阻燃整理、防静电整理、防紫外线整理、防腐防霉整理、抗菌防臭整理，以及风格化整理（如丝鸣整理、碱减量处理、酸减量处理、水洗、砂洗和酶洗处理）等等。它们利用各种天然或化学整理剂（或液、浆）等的不同化学特性，在一定的温度、湿度及时间等工艺条件下，或是化学整理剂（或液、浆）等自身产生变化反应，或是与织物中天然或化学纤维等的分子链产生交联、键合反应，使得各种化学整理剂（或液、浆）等的化学特性被转嫁至纺织品上显现，从而使织物获得不同的整理效果，产生功能各异的风格特性。 
两类整理法的对比分析：
功能风格多样化的纺织品必然要有多样化的功能性后整理工艺与之对应，各类整理方法或各种整理工艺均有其各自的优缺点及一定的适用范围，简单的以某一类整理方法替代另一类整理方法或以某一种整理工艺替代另一种整理工艺而达到相同的整理效果，在目前的情况下尚待研究。
机械物理整理法以其安全、环保、无化学物残留等特征而日益引起人们的关注，并得到越来越广泛的应用。但其使用范围当前仅局限于对织物纤维进行表面性状处理等工艺中，而大部分功能性后整理工艺必须通过化学助剂整理法进行。
化学助剂整理法可实现多种用途的功能性后整理，而不同的功能整理工艺均有其特定的温度、湿度、时间等工艺条件，还需要配置各种不同的功能整理助剂来实现，本专利所要解决的是对织物快干吸湿的新型的工艺及整理助剂的相关研究。
发明内容
本发明的主要任务在于提供一种防缩防皱、吸湿快干型衬衫领衬的后整理工艺，具体是在浸轧后整理工艺上，通过改进浸轧整理液及为配合该整理液对工艺进行改进，实现了一种具有防缩防皱、吸湿快干型功能的衬衫领衬的后整理工艺。
为了解决以上技术问题，本发明的一种防缩防皱、吸湿快干型衬衫领衬的后整理工艺，其特征在于：a、选取聚乙烯硅氧烷的改性物作为后整理剂的快干吸湿剂30-40g/l，与以下组分配置成浸轧液：树脂：60-100g/l，Cat.D催化剂：20%(对树脂重)，上述浸轧液的PH：4.5；b、将待整理织物置于浸轧液中，待浸轧率达80%时，进行预烘和焙烘两个步骤；所述焙烘为在烘房内按150-175℃的温度烘干30s-3min。       
进一步地，所述聚乙烯硅氧烷的改性物的分子式为：
。
进一步地，所述树脂为GFR10树脂或TMDD树脂。
本发明的优点在于：1、本发明的浸轧整理液内起主要吸湿快干作用的为聚乙烯硅氧烷的改性物。聚乙烯硅氧烷的改性物，外观：无色透明液体，离子属性：非离子，比重：约1.05（20℃）， PH值：约6.5（5%水溶液），溶解性功能：能以任意比例溶解于冷水中， 相容性能：能与各种离子型化合物拼混使用。
聚乙烯硅氧烷的改性物适用于棉、涤及其混纺交织物吸湿快干整理，并赋予织物极佳的柔软手感。
特点：1优异的吸湿性能，显著增强纺织物毛效：2赋予织物亲水性能；3耐久的柔软手感；4不泛黄；5高活性高性能。
优点：1增大织物与周围环境之间水分的浓度梯度，加快水分传递速率；2改善织物抗静电性、易去污性等表面性能；3改善织物的弹性、强力、抗起毛起球等物理性能；4特别适用于白色、浅色织物；5低成本。
应用的优点：聚乙烯硅氧烷的改性物采用浸扎法可单独使用，也可与防缩防皱整理剂及硬挺树脂等初缩体协同使用，减少纤维孔道的溶胀率并获得更佳的吸湿快干效果；其主要的工作原理为：
1、通过分子链中链段亲水原理。
2、采用上述吸湿快感型的浸轧整理液按本发明的工艺整理的织物，具有柔软性、吸湿性、速干性效果明显的特征。
具体实施方式
实施例1
    对棉质衬衫领衬进行防缩防皱处理，该实施例的棉为：20s.20s，60.60。
采用的工艺为：浸轧（轧浸率80%），采用三辊轧机，轧浸压力2P；浸轧液：选取聚乙烯硅氧烷的改性物作为后整理剂的快干吸湿剂30-40g/l，与以下组分配置成浸轧液：树脂：60-100g/l，Cat.D催化剂：20%(对树脂重)，上述浸轧液的PH：4.5。本聚乙烯硅氧烷的改性物的分子式为：。
预烘：预烘为在温度80-100℃温度下常规预烘即可，该步骤不累述。
焙烘：采用8节烘房：前两节温度设置为150℃，烘3min，中间2节设170℃，烘30s，后4节设175℃，烘30s。烘焙结束，得成品。
    将上述的织物进行效果监测：效果监测（标准）标准号：GB/T   21655.1-2008。
 吸湿率/% ：100；
吸湿性：滴水扩散时间/S ：5；芯吸高度/mm ：90；
        速干性：蒸发速度/g/h ：0.18；透湿量/g/m2.d ：8000。
缩  率：经向-0.5%，纬向-0.5%。
实施例2
      对棉质衬衫领衬进行防缩防皱处理，该实施例的棉为：20s.20s，50.50。
    工艺配方和工艺流程参见实施例1。制得的成品，经检测，结果如下：
效果监测（标准） 标准号：GB/T   21655.1-2008。
吸湿率/% ：100；
吸湿性：滴水扩散时间/S ：5；芯吸高度/mm ：90；
       速干性：蒸发速度/g/h ：0.18；透湿量/g/m2.d ：8000。
 缩  率：经向-0.5%，纬向-0.5%。

Claims (1)

1.一种防缩防皱、吸湿快干型衬衫领衬的后整理工艺，其特征在于：a、选取 作为后整理剂的快干吸湿剂30-40g/l，与以下组分配置成浸轧液：树脂：60-100g/l，Cat.D催化剂：20%(对树脂重)，上述浸轧液的pH：4.5；b、将待整理织物置于浸轧液中，待浸轧率达80%时，进行预烘和焙烘两个步骤；所述焙烘为在烘房内按150-175℃的温度烘干30s-3min。
CN201110356813.0A 2011-11-11 2011-11-11 一种防缩防皱、吸湿快干型衬衫领衬的后整理工艺 Active CN102409537B (zh)