CN103668995B - 一种用于尼纶或尼纶/氨纶织物的吸湿排汗、快干整理剂的制备方法及其应用 - Google Patents
一种用于尼纶或尼纶/氨纶织物的吸湿排汗、快干整理剂的制备方法及其应用 Download PDFInfo
- Publication number
- CN103668995B CN103668995B CN201310654920.0A CN201310654920A CN103668995B CN 103668995 B CN103668995 B CN 103668995B CN 201310654920 A CN201310654920 A CN 201310654920A CN 103668995 B CN103668995 B CN 103668995B
- Authority
- CN
- China
- Prior art keywords
- nylon
- fabric
- finishing agent
- preparation
- quick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种用于尼纶或尼纶/氨纶织物的吸湿排汗、快干整理剂的制备方法及其应用，该方法以二元异氰酸酯，EO/PO嵌段聚醚二元醇，封端剂酮肟为原料制得无色透明的封端型热反应性聚氨酯预聚体，再复配硬脂酸聚氧乙烯醚或亲水性硅油，添加二甘醇单丁醚作溶剂和水制得。本发明开发的整理剂使整理后的尼纶或尼纶/氨纶织物具有柔软、丰满、平滑、悬垂性好的手感，赋予整理织物优异的亲水和吸湿性能，整理的面料适合作为休闲运动面料、女人内衣面料等，能提高产品的附加值。本发明开发的用于尼纶或尼纶/氨纶织物吸湿排汗、快干整理剂使用时，不需要外加交联剂，整理在织物上就具有很好的耐洗性能。
Description
【技术领域】
本发明涉及一种吸湿排汗、快干整理剂的制备方法及其应用，尤其涉及一种用于尼纶或尼纶/氨纶织物的吸湿排汗、快干整理剂的制备方法及其应用，属于纺织化工技术领域。
【背景技术】
尼纶，尼纶/氨纶面料常作为运动休闲面料和女人内衣面料，具有手感柔软，穿着舒适，透气和弹性好等，但随着人们运动休闲面料和内衣面料要求越来越高，这些面料的本身性能不能人们对服饰的更高需求，尼纶，尼纶/氨纶运动休闲和内衣面料不但要求手感柔软、丰满富有弹性而且要求有很好的亲水性能，这些服用性能的改善，都需要通过后整理的方法，添加一些后整理剂来实现的。
在现有技术中有见类似整理剂的使用，但现有类似的整理剂整理在尼纶、尼纶/氨纶针织物上的亲水性能和手感仍达不到高端产品的要求，而且类似的整理剂在织物上的耐洗性不好，需要通过另外加交联剂才能提高整理剂在织物上的耐洗性，本发明所涉及的相关技术未见有的公开报道。
【发明内容】
本发明的目的是克服现有技术的不足，提供一种使织物具有舒适的手感，优异的洗水性和耐水性，卓越的弹性回复，赋予整理织物超级爽弹手感和亲水性能的用于尼纶或尼纶/氨纶织物的吸湿排汗、快干整理剂的制备方法。
本发明的另一目的是提供一种上述制备方法制备的整理剂的应用。
一种用于尼纶或尼纶/氨纶织物的吸湿排汗、快干整理剂的制备方法，其特征在于以二元异氰酸酯，EO/PO嵌段聚醚二元醇，封端剂酮肟为原料制得无色透明的封端型热反应性聚氨酯预聚体，再复配硬脂酸聚氧乙烯醚（9EO）或亲水性硅油，添加二甘醇单丁醚作溶剂和水制得。
本发明制备方法包括以下具体步骤：
a、合成封端型热反应性聚氨酯预聚体
反应釜干燥除水，注入定量的EO/PO嵌段聚醚二元醇，密封后慢慢升温到120℃减压除水2小时，降温到30～40℃，缓慢加入定量的二元异氰酸酯，升温到80℃反应2小时后，缓慢加入定量的封端剂酮肟，80～85℃反应4小时，降温得到无色透明的封端型热反应性聚氨酯预聚体；
b、复配
将步骤a制得的封端型热反应性聚氨酯预聚体与以下各组分按以下重量百分比复配搅拌均匀即可：
本发明中的EO/PO嵌段聚醚二元醇的分子量为1000～8000之间，其中EO的质量百分含量范围为40～80％。
本发明中的二元异氰酸酯优选为异佛尔酮二异氰酸酯（IPDI），二苯基甲烷二异氰酸酯（MDI），1,6-己二异氰酸酯（HDI）和甲苯二异氰酸酯（TDI）中的一种或几种。
本发明中的封端剂酮肟优选为甲基异丁基酮肟，甲乙酮肟，环己基酮肟和二甲基酮肟中的一种或几种。
本发明中合成封端型热反应性聚氨酯预聚体的具体反应路线如下：
封端型热反应性聚氨酯对尼纶、尼纶/氨纶织物的多项性能如手感、弹性修复、抗皱等性能都有不同程度的提高，封端型热反应性聚氨酯引入EO/PO嵌段聚醚二元醇，能够提高尼纶、尼纶/氨纶织物的亲水性和吸湿性能。用酮肟对活性基团的-NCO基团进行封端，整理在织物上，在高温焙烘下，封端型热反应性聚氨酯会解封，重新释放出反应性基团-NCO，与织物上的活性基团、复配的聚醚亲水性硅油和硬脂酸聚氧乙烯醚SG-9上的活性基团发生交联反应，提高整理剂在织物上的耐洗性，不需要外加交联剂就有很好的耐洗性。通过复配聚醚亲水硅油或硬脂酸聚氧乙烯醚SG-9，主要作用进一步改善织物的手感，极少程度降低整理织物的亲水性。
一种上述制备方法制备的整理剂应用于尼纶、尼纶/氨纶针织物的功能性后整理，其应用工艺为：一浸一轧→烘干→热定型；
其中整理液浓度：50-100g/L；
其中一浸一轧的带液率为80～100％，烘干温度为100～120℃，热定型的条件为170～190℃定型120～160s。
本发明相对于现有技术，有以下优点：
本发明开发的用于尼纶或尼纶/氨纶织物吸湿排汗、快干整理剂在后整理工艺中，不但可以渗透到织物和纱线内部，而且在一定的温度下，可以解封释放反应性基团-NCO与尼纶或尼纶/氨纶织物、聚醚亲水硅油、硬脂酸聚氧乙烯醚SG-9上活性基团发生交联反应，同时整理剂本身分子间也会发生反应，以化学键发生交联反应，形成立体网状结构，使整理后的尼纶或尼纶/氨纶织物具有柔软、丰满、平滑、悬垂性好的手感，赋予整理织物优异的亲水和吸湿性能，整理的面料适合作为休闲运动面料、女人内衣面料等，能提高产品的附加值。
本发明开发的用于尼纶或尼纶/氨纶织物吸湿排汗、快干整理剂使用时，不需要外加交联剂，整理在织物上就具有很好的耐洗性能。
【具体实施方式】
下面结合具体实施例对本发明作进一步描述：
实施例1：
反应釜干燥除水，注入300KgEO/PO嵌段聚醚二元醇（分子量1950），慢慢升温到120℃减压除水2h，降温到30～40℃，缓慢加入41Kg二元异氰酸酯IPDI，升温到80℃反应2h后，缓慢加入7.1Kg封端剂甲基异丁基酮肟，于80～85℃反应4h，降温得到无色透明的封端型热反应性聚氨酯预聚体，降温至40℃时加入200Kg二甘醇单丁醚，硬脂酸聚氧乙烯醚（9EO）150Kg，去离子水301.9Kg，搅拌均匀即得。
实施例2：
反应釜干燥除水，注入300KgEO/PO嵌段聚醚二元醇（分子量1950），慢慢升温到120℃减压除水1h，降温到30～40℃，缓慢加入46.2Kg的二苯基甲烷二异氰酸酯MDI，升温到80℃反应2h后，缓慢加入2.7Kg封端剂甲乙酮肟，于80～85℃反应4h，降温得到无色透明的封端型热反应性聚氨酯预聚体，降温至40℃时加入200Kg二甘醇单丁醚，聚醚亲水硅油100Kg，去离子水351.1Kg，搅拌均匀即得。
实施例3：
反应釜干燥除水，注入300KgEO/PO嵌段聚醚二元醇（分子量1950），慢慢升温到120℃减压除水2h，降温到30～40℃，缓慢加入31Kg二元异氰酸酯HDI，升温到80℃反应2h后，缓慢加入7.0Kg封端剂环己酮肟，于85℃反应4h，降温得到无色透明的封端型热反应性聚氨酯预聚体，降温至40℃时加入200Kg二甘醇单丁醚，硬脂酸聚氧乙烯醚（9EO）150Kg，去离子水312Kg，搅拌均匀即得。
实施例4：
反应釜干燥除水，注入300KgEO/PO嵌段聚醚二元醇（分子量1950），慢慢升温到120℃减压除水2h，降温到30～40℃，缓慢加入32Kg二元异氰酸酯TDI，升温到80℃反应2h后，缓慢加入4.48Kg封端剂二甲基酮肟，于85℃反应4h，降温得到无色透明的封端型热反应性聚氨酯预聚体，降温至40℃时加入200Kg二甘醇单丁醚，聚醚亲水硅油100Kg，去离子水363.52Kg，搅拌均匀即得。
应用实验：
分别用实施例1、实施例2、实施例3和实施例4制得整理剂对尼纶、尼纶/氨纶针织面料进行后整理，采用下面整理工艺：
工艺：一浸一轧→烘干（100-120℃）→170×120s定型。
整理液浓度：50g/L
经过整理后的织物置于温度为(20±2）℃，相对湿度为(65±2)%的恒温恒室平衡至少4h，然后测试他的亲水性能和手感。
亲水性测试方法：滴一滴蒸馏水在织物上，观测水滴完全渗透所需时间，时间越短，亲水性能越好。
手感测试方法：5-10组成一组，对整理织物进行触摸，进行评级，以未整理的空白织物为参照物。
测试结果如表1和表2所示：
表1：
表2：
从表1和表2可知，尼纶、尼纶/氨纶织物经过实施例1和实施例2的整理剂整理，吸水性明显提高。整理织物具有柔软、丰满的手感、悬垂性好，经过20次洗水整理织物仍具有很好吸水性能和手感。本发明制备的整理剂在后整时不但可以渗透到织物内部，而且还可以释放活性基团与尼纶或尼纶/氨纶上的氨基及其他整理剂发生交联反应，同时产品内部分子之间也会进行反应，从而以化学键的形式交联，形成立体网状结构，能使整理后的尼纶或尼纶/氨纶织物具有柔软、丰满、平滑、丝滑的超值手感。
本发明整理剂在对尼纶、尼纶/氨纶针织物进行后整理时，在应用浓度50-100g/L（整理液浓度）范围内，浓度越大，整理效果越好，吸湿排汗，快干性能及手感越优异。
Claims (6)
1.一种用于尼纶或尼纶/氨纶织物的吸湿排汗、快干整理剂的制备方法，其特征在于所述的制备方法包括以下具体步骤：
a、合成封端型热反应性聚氨酯预聚体
反应釜干燥除水，注入定量的EO/PO嵌段聚醚二元醇，密封后慢慢升温到120℃减压除水1～2小时，降温到30～40℃，缓慢加入定量的二元异氰酸酯，升温到75～80℃反应2小时后，缓慢加入定量的封端剂酮肟，80～85℃反应4小时，降温得到无色透明的封端型热反应性聚氨酯预聚体；
b、复配
将步骤a制得的封端型热反应性聚氨酯预聚体与以下各组分按以下重量百分比复配搅拌均匀即可：
2.根据权利要求1所述的一种用于尼纶或尼纶/氨纶织物的吸湿排汗、快干整理剂的制备方法，其特征在于所述的EO/PO嵌段聚醚二元醇的分子量为1000～8000之间，其中EO的质量百分含量范围为40～80％。
3.根据权利要求1所述的一种用于尼纶或尼纶/氨纶织物的吸湿排汗、快干整理剂的制备方法，其特征在于所述的二元异氰酸酯为异佛尔酮二异氰酸酯，二苯基甲烷二异氰酸酯，1,6-己二异氰酸酯和甲苯二异氰酸酯中的一种或几种。
4.根据权利要求1所述的一种用于尼纶或尼纶/氨纶织物的吸湿排汗、快干整理剂的制备方法，其特征在于所述的封端剂酮肟为甲基异丁基酮肟，甲乙酮肟，环己基酮肟，丁酮肟和二甲基酮肟中的一种或几种。
5.一种权利要求1所述的制备方法制备的整理剂应用于尼纶、尼纶/氨纶针织物的功能性后整理。
6.根据权利要求5所述的整理剂的应用，其特征在于其应用工艺如下：
工艺：一浸一轧→烘干→热定型；
其中整理液浓度为：50-100g/L；
其中一浸一轧的轧余率为80～100％，烘干温度为100～120℃，热定型的条件为170～190℃定型120～160s。