CN102399389A - 高性能阻燃抗静电聚丙烯塑料的制备方法 - Google Patents

高性能阻燃抗静电聚丙烯塑料的制备方法 Download PDF

Info

Publication number
CN102399389A
CN102399389A CN201010274567XA CN201010274567A CN102399389A CN 102399389 A CN102399389 A CN 102399389A CN 201010274567X A CN201010274567X A CN 201010274567XA CN 201010274567 A CN201010274567 A CN 201010274567A CN 102399389 A CN102399389 A CN 102399389A
Authority
CN
China
Prior art keywords
preparation
antistatic polypropylene
vestolen
antistatic
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201010274567XA
Other languages
English (en)
Inventor
李天辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201010274567XA priority Critical patent/CN102399389A/zh
Publication of CN102399389A publication Critical patent/CN102399389A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种高性能的阻燃抗静电聚丙烯塑料，是在聚丙烯中加入一定量聚氯乙烯，三氧化二锑，硬脂酸，硬脂酸钙，芥酸酰胺，超导石墨，受阻酚类抗氧化剂1010，混合，经过螺杆挤出机熔融挤出即得；试验证明，本发明制备的阻燃抗静电聚丙烯塑料的性能：氧指数达到29，表面电阻达到103～108Ω，抗拉强度50MPa；成本远低于市场销售的双抗网。

Description

高性能阻燃抗静电聚丙烯塑料的制备方法
技术领域
本发明属于塑料领域，涉及一种用于阻燃和抗静电的塑料，尤其涉及一种高性能阻燃抗静电聚丙烯塑料的制备方法。
背景技术
聚丙烯(PP)是一种性能优良的热塑性合成树脂，具有密度小、无毒、易加工、冲击强度高、抗挠曲性以及电绝缘性好等优点，因此在电器、航空、石油化工、煤矿交通等领域得到广泛应用。自1957年在意大利首次实现工业化生产以来，其发展速度一直居各种通用塑料之首。但是，聚丙烯容易燃烧、静电积累严重(表面电阻高达1018Ω)，因此在生产、运输、使用时，因摩擦而产生静电容易引起火灾。特别是聚丙烯防护网代替金属网用于煤矿深层开采的假顶的防护材料有着严格的安全要求,表面电阻必须小于109Ω,氧指数大于27,以防意外事故发生。所以聚丙烯用于煤矿井下防护材料必须进行阻燃、抗静电性能的改性。聚丙烯塑料的阻燃和抗静电的改性方法很多，主要是向聚丙烯中添加阻燃剂和抗静电剂。添加型阻燃剂有：卤素系阻燃剂，如十溴二苯醚 (DBDPO) 、氯蜡系列等；磷系阻燃剂包括无机磷类和有机磷酸酯类；氮系阻燃剂有三聚氰胺，多聚磷酸铵等；无机系阻燃剂主要是Al2(OH)3、Mg(OH)2；助阻燃剂Sb2O3等。添加型抗静电剂有：表面活性剂型，永久型抗静电高分子，导电炭黑型。表面活性剂型抗静电剂包括阳离子型、阴离子型和非离子型。阳离子型抗静电剂主要是季铵盐类化合物，抗静电效果较好，相容性强，但热稳定性差，不适合混炼。阴离子型抗静电剂主要有烷基磺酸盐、磷酸盐、碳酸盐类化合物，抗静电效果好，相容性差，热稳定性强。非离子型抗静电剂主要是胺类化合物，抗静电效果差，相容性强，热稳定性强。永久型抗静电高分子包括导电高分子和亲水高分子。导电炭黑型抗静电剂主要有导电炭黑和石墨。阻燃抗静电聚丙烯发明已经有很多，但是这些专利存在的问题是：生产的产品中添加剂量较大，成本较高；许多产品不能同时达到较好的阻燃和抗静电效果。为解决存在的问题。本发明用聚氯乙烯代替传统阻燃剂，用阴离子硬脂酸钙、非离子表面活性剂芥酸酰胺和超导石墨作复合抗静电剂，在达到较好阻燃和抗静电效果的同时，大幅降低塑料生产成本，具有很强的实用性。
发明内容
本发明的目的是为了克服现有技术中聚丙烯阻燃和抗静电性能不强的缺点，提供一种廉价的高性能的阻燃和抗静电聚丙烯塑料。本发明的另一目的是提供一种高性能阻燃抗静电聚丙烯塑料的制备方法。是在100份聚丙烯中加入1.0~10.0份聚氯乙烯，0.1~1.0份三氧化二锑，0.01~0.1份硬脂酸，0.05~0.5份硬脂酸钙，0.05~0.5份芥酸酰胺，0.1~1.0份超导石墨，0.1~1.0份受阻酚类抗氧化剂1010，搅拌混合均匀后，送入螺杆挤出机熔融挤出。
具体实施方式
［实施例1］按质量份数，在100份聚丙烯中加入1.0份聚氯乙烯，0.1份三氧化二锑，0.01份硬脂酸，0.05份硬脂酸钙，0.05份芥酸酰胺，0.1份超导石墨，0.1份受阻酚类抗氧化剂1010，搅拌混合均匀后，送入螺杆挤出机熔融挤出。［实施例2］按质量份数，在100份聚丙烯中加入10.0份聚氯乙烯，1.0份三氧化二锑，0.1份硬脂酸，0.5份硬脂酸钙，0.5份芥酸酰胺，1.0份超导石墨，1.0份受阻酚类抗氧化剂1010，搅拌混合均匀后，送入螺杆挤出机熔融挤出。
性能表征
力学性能按  GB1040-79测定;阻燃性能按  GB2406-80测定;表面电阻按GB1410-78测定。                                                                                 
性能 参数 实例1 实例2
氧指数 ≥27 28 30
表面电阻(Ω) ＜109 1·108 6·103
抗拉强度(MPa) ≥10 50 50
由表可以得出：产品的氧指数较高说明阻燃能力较强，表面电阻较小说明抗静电能力较强，并且力学性能较好。
优点
经过上述试验可以得出：高性能阻燃抗静电聚丙烯塑料的阻燃和抗静电性能都较好。用聚氯乙烯和三氧化二锑作为复合阻燃剂，取代传统的阻燃剂，提高了塑料的产率和阻燃性能，并且大大降低了产品中阻燃剂的成本。用阴离子表面活性剂硬脂酸钙、非离子表面活性剂芥酸酰胺、超导石墨作为三元复合抗静电剂，添加量是传统抗静电剂的几十分之一，能达到同样抗静电效果，大幅降低了产品中抗静电剂的成本。本发明的最大优点是提高塑料阻燃抗静电性能，并且生产成本较大降低，具有很强的实用性。

Claims (9)

1.一种高性能阻燃抗静电聚丙烯塑料的制备方法，是在100份聚丙烯中加入1.0～10.0份聚氯乙烯，0.1～1.0份三氧化二锑，0.01～0.1份硬脂酸，0.05～0.5份硬脂酸钙，0.05～0.5份芥酸酰胺，0.1～1.0份超导石墨，0.1～1.0份受阻酚类抗氧化剂1010，搅拌混合均匀后，送入螺杆挤出机熔融挤出即得。
2.如权利要求1所述高性能阻燃抗静电聚丙烯塑料的制备方法，其特征在于：所述聚氯乙烯可以用聚氯丙烯代替。
3.如权利要求1所述高性能阻燃抗静电聚丙烯塑料的制备方法，其特征在于：所述聚氯乙烯加入量是聚丙烯质量的1.0～10.0%。
4.如权利要求1所述高性能阻燃抗静电聚丙烯塑料的制备方法，其特征在于：所述三氧化二锑加入量是聚丙烯质量的0.1～1.0%。
5.如权利要求1所述高性能阻燃抗静电聚丙烯塑料的制备方法，其特征在于：所述硬脂酸加入量是聚丙烯质量的0.01～0.1%。
6.如权利要求1所述高性能阻燃抗静电聚丙烯塑料的制备方法，其特征在于：所述硬脂酸钙加入量是聚丙烯质量的0.05～0.5%。
7.如权利要求1所述高性能阻燃抗静电聚丙烯塑料的制备方法，其特征在于：所述芥酸酰胺加入量是聚丙烯质量的0.05～0.5%。
8.如权利要求1所述高性能阻燃抗静电聚丙烯塑料的制备方法，其特征在于：所述超导石墨加入量是聚丙烯质量的0.1～1.0%。
9.如权利要求1所述高性能阻燃抗静电聚丙烯塑料的制备方法，其特征在于：所述受阻酚类抗氧化剂1010加入量是聚丙烯质量的0.1～1.0%。
CN201010274567XA 2010-09-07 2010-09-07 高性能阻燃抗静电聚丙烯塑料的制备方法 Pending CN102399389A (zh)