CN102382612A - 具有疏水性能的单组份聚氨酯粘接密封胶及其制备方法 - Google Patents

具有疏水性能的单组份聚氨酯粘接密封胶及其制备方法 Download PDF

Info

Publication number
CN102382612A
CN102382612A CN2011101857899A CN201110185789A CN102382612A CN 102382612 A CN102382612 A CN 102382612A CN 2011101857899 A CN2011101857899 A CN 2011101857899A CN 201110185789 A CN201110185789 A CN 201110185789A CN 102382612 A CN102382612 A CN 102382612A
Authority
CN
China
Prior art keywords
polyurethane adhesive
component polyurethane
hydrophobic performance
single component
seal gum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011101857899A
Other languages
English (en)
Other versions
CN102382612B (zh
Inventor
陈福泰
白渝平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zibo hitecmen new Mstar Technology Ltd
Original Assignee
ZIBO HITECMEN CHEMICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZIBO HITECMEN CHEMICAL CO Ltd filed Critical ZIBO HITECMEN CHEMICAL CO Ltd
Priority to CN 201110185789 priority Critical patent/CN102382612B/zh
Publication of CN102382612A publication Critical patent/CN102382612A/zh
Application granted granted Critical
Publication of CN102382612B publication Critical patent/CN102382612B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于密封胶技术领域，具体涉及一种具有疏水性能的单组份聚氨酯粘接密封胶及其制备方法，具有疏水性能的单组份聚氨酯粘接密封胶，由如下质量份数的原料制成：端羟基聚醚10～35份；端羟基聚二甲基硅氧烷5～15份；异氰酸酯5～15份；增塑剂29.6～35.89份；无机填料5～30份；有机填料5～15份；催化剂0.01～0.3份；抗氧剂0.01～0.2份，其制备方法简单易行。本发明所述的具有疏水性能的单组份聚氨酯粘接密封胶表面具有疏水性能。

Description

具有疏水性能的单组份聚氨酯粘接密封胶及其制备方法
技术领域
本发明属于密封胶技术领域，具体涉及一种具有疏水性能的单组份聚氨酯粘接密封胶及其制备方法。
背景技术
密封胶是以不定形态现场嵌填接缝、粘接界面并承受接缝位移变形的密封材料。它一般是膏状材料，固化后将基材连接成一个整体。早期的密封胶由沥青、焦油、天然(或合成)树脂、天然(或合成)橡胶等干性(或非干性)的粘稠物为基料，配合一定的助剂组成。目前高性能密封胶有3种：类聚硫、硅酮和聚氨酯。
聚氨酯(PU)密封胶是分子链中含有氨酯基(-NHCOO-)和/或异氰酸酯基(-NCO)类的密封胶，一般分为单组分和双组分两种基本类型，单组分为湿气固化型，双组分为反应固化型。聚氨酯粘密封胶具有弹性好，伸长率大，强度高，耐磨性突出，耐酸性、耐碱性、耐低温性、然而聚氨酯密封胶易在高温、高湿环境下吸潮而水解。
发明内容
本发明所要解决的问题是提供了一种具有疏水性能的单组份聚氨酯粘接密封胶，该密封胶表面具有疏水性能，稳定性好、强度高，具备延缓密封胶水解老化的功能和作用；本发明同时提供了其制备方法。
本发明所述的具有疏水性能的单组份聚氨酯粘接密封胶，由如下质量份数的原料制成：
Figure BDA0000073617250000011
所述的端羟基聚醚为平均分子量为4500～6000的端羟基三元聚氧化丙稀醚。
所述的端羟基聚二甲基硅氧烷的平均分子量为2000～4000。
所述的异氰酸酯为甲苯二异氰酸酯。
所述的增塑剂为邻苯二甲酸二丁酯。
所述的无机填料为乙炔炭黑。
所述的有机填料为PVC糊树脂。
所述的催化剂为辛酸亚锡。
所述的抗氧剂为2，6-二叔丁基对甲酚。
所述的具有疏水性能的单组份聚氨酯粘接密封胶的制备方法，其特征在于包括如下步骤：
(1)按配方量称取各原料；
(2)将端羟基聚醚与端羟基聚二甲基硅氧烷加入到反应釜中，缓慢升温至80～100℃，真空脱气1～2小时；
(3)加入有机填料和异氰酸酯，缓慢升温至80～100℃，在氮气保护下反应2～3小时；
(4)加入增塑剂、无机填料、催化剂和抗氧剂，在80～100℃下真空搅拌1～2小时；充氮气解除真空，然后冷却至40℃制成。
真空度脱气和真空搅拌的真空度保持0.1MPa±0.02Mpa。
本发明的有益效果如下：
本发明所述的密封胶表面具有疏水性能，水接触角大于90度，稳定性好、强度高，具备延缓密封胶水解老化的功能和作用，其制备方法简单易行。
具体实施方式
以下结合实施例对本发明做进一步描述。
实施例1～5
实施例1～5具体配方见表1。
表1实施例1～5配方表(单位Kg)
Figure BDA0000073617250000021
实施例1～5的制备方法，包括如下步骤：
(1)按配方量称取各原料；
(2)将端羟基聚醚与端羟基聚二甲基硅氧烷加入到反应釜中，缓慢升温至80～100℃，真空脱气1～2小时；
(3)加入有机填料和异氰酸酯，缓慢升温至80～100℃，在氮气保护下反应2～3小时；
(4)加入增塑剂、无机填料、催化剂和抗氧剂，在80～100℃下真空搅拌1～2小时；充氮气解除真空，然后冷却至40℃制成。
实施例1～5的具体工艺参数见表2。
表2实施例1～5工艺参数与产品性能表
Figure BDA0000073617250000031

Claims (10)

1.一种具有疏水性能的单组份聚氨酯粘接密封胶，其特征在于由如下质量份数的原料制成：
Figure FDA0000073617240000011
2.根据权利要求1所述的具有疏水性能的单组份聚氨酯粘接密封胶，其特征在于所述的端羟基聚醚为平均分子量为4500～6000的端羟基三元聚氧化丙稀醚。
3.根据权利要求1所述的具有疏水性能的单组份聚氨酯粘接密封胶，其特征在于所述的端羟基聚二甲基硅氧烷的平均分子量为2000～4000。
4.根据权利要求1所述的具有疏水性能的单组份聚氨酯粘接密封胶，其特征在于所述的异氰酸酯为甲苯二异氰酸酯。
5.根据权利要求1所述的具有疏水性能的单组份聚氨酯粘接密封胶，其特征在于所述的增塑剂为邻苯二甲酸二丁酯。
6.根据权利要求1所述的具有疏水性能的单组份聚氨酯粘接密封胶，其特征在于所述的无机填料为乙炔炭黑。
7.根据权利要求1所述的具有疏水性能的单组份聚氨酯粘接密封胶，其特征在于所述的有机填料为PVC糊树脂。
8.根据权利要求1所述的具有疏水性能的单组份聚氨酯粘接密封胶，其特征在于所述的催化剂为辛酸亚锡。
9.根据权利要求1所述的具有疏水性能的单组份聚氨酯粘接密封胶，其特征在于所述的抗氧剂为2，6-二叔丁基对甲酚。
10.一种权利要求1所述的具有疏水性能的单组份聚氨酯粘接密封胶的制备方法，其特征在于包括如下步骤：
(1)按配方量称取各原料；
(2)将端羟基聚醚与端羟基聚二甲基硅氧烷加入到反应釜中，缓慢升温至80～100℃，真空脱气1～2小时；
(3)加入有机填料和异氰酸酯，缓慢升温至80～100℃，在氮气保护下反应2～3小时；
(4)加入增塑剂、无机填料、催化剂和抗氧剂，在80～100℃下真空搅拌1～2小时；充氮气解除真空，然后冷却至40℃制成。
CN 201110185789 2011-07-04 2011-07-04 具有疏水性能的单组份聚氨酯粘接密封胶及其制备方法 Expired - Fee Related CN102382612B (zh)