CN102140177A - 一种溶解高分子量壳聚糖的碱性溶剂及其用法 - Google Patents

一种溶解高分子量壳聚糖的碱性溶剂及其用法 Download PDF

Info

Publication number
CN102140177A
CN102140177A CN 201110099176 CN201110099176A CN102140177A CN 102140177 A CN102140177 A CN 102140177A CN 201110099176 CN201110099176 CN 201110099176 CN 201110099176 A CN201110099176 A CN 201110099176A CN 102140177 A CN102140177 A CN 102140177A
Authority
CN
China
Prior art keywords
chitosan
molecular weight
molecular
solution
solvent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201110099176
Other languages
English (en)
Other versions
CN102140177B (zh
Inventor
胡巧玲
李友良
张雨菲
艾锋
邓海琴
张珂
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang University ZJU
Original Assignee
Zhejiang University ZJU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang University ZJU filed Critical Zhejiang University ZJU
Priority to CN2011100991763A priority Critical patent/CN102140177B/zh
Publication of CN102140177A publication Critical patent/CN102140177A/zh
Application granted granted Critical
Publication of CN102140177B publication Critical patent/CN102140177B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开的溶解高分子量壳聚糖的碱性溶剂能溶解分子量100万~600万的壳聚糖，其组分及其重量百分比含量为：氢氧化锂：1.0~5.0%，氢氧化钠：0~4.0%，尿素：4.0~9.0%，丙三醇：0.1~3.0%，其余为水。采用本发明的溶剂可以避免高分子量壳聚糖在酸性溶剂中降解而引起制品强度大幅下降的问题。本发明的溶剂使用方法简单。溶解有高分子量的壳聚糖溶液可用于研究高分子量壳聚糖的溶解行为与分子结构的关系，及应用于高强壳聚糖凝胶、壳聚糖纤维、壳聚糖棒材、壳聚糖支架材料等制品的加工。

Description

一种溶解高分子量壳聚糖的碱性溶剂及其用法
技术领域
本发明涉及一种溶解高分子量壳聚糖的溶剂，尤其是溶解高分子量壳聚糖的碱性溶剂及其用法。
背景技术
壳聚糖具有良好的生物相容性和生物可降解性，可应用于医疗保健及组织工程等领域。而高分子量壳聚糖制品（如透析膜、纤维、支架或凝胶）具有强度大、性能好的优点，随着应用范围的扩大，高分子量壳聚糖的需求必然越来越大。目前国内外常用的溶剂是各种稀酸，而壳聚糖在酸性溶液中是极不稳定的，会造成壳聚糖长链的部分水解及糖苷键断裂，使壳聚糖分子量降低及多分散，从而致使壳聚糖产品性能不足。中国专利CN101215341A公开了可溶解中低分子量壳聚糖的碱性溶剂，但至今还未有可溶解高分子量壳聚糖的碱性溶剂。
发明内容
本发明的目的是要提供一种溶解高分子量壳聚糖的碱性溶剂及其用法，以获得稳定的高分子量壳聚糖溶液，用于制备高分子量壳聚糖制品。
本发明的溶解高分子量壳聚糖的碱性溶剂，它能溶解分子量100万~600万的壳聚糖，其组分及其重量百分比含量为：
氢氧化锂：1.0~5.0 %
氢氧化钠：0~4.0 %
尿素：4.0~9.0 %
丙三醇：0.1~3.0 %
其余为水。
溶解高分子量壳聚糖的碱性溶剂的制备方法，步骤如下：按重量百分比含量取各组分，先将氢氧化锂、氢氧化钠和尿素混合，然后再加水和丙三醇混合；或者先将氢氧化锂和氢氧化钠混合，然后加水溶解，再加尿素和丙三醇混合；或者先将尿素、水和丙三醇混合，然后再加氢氧化锂和氢氧化钠混合。
本发明的溶解高分子量壳聚糖的碱性溶剂的使用方法，步骤如下：
将脱乙酰度50~85 %、分子量100万~600万的壳聚糖粉末分散于上述溶解壳聚糖的碱性溶剂中，静置1-3小时使其充分溶胀，然后将该溶胀液在-60℃~-20℃冷冻备用；使用时，在0℃~60℃下解冻，并在机械搅拌下使其完全溶解，得到透明的高分子量壳聚糖溶液。
本发明的有益效果在于：
采用本发明的溶剂可以溶解高分子量的壳聚糖得到稳定的溶液，避免了高分子量壳聚糖在酸性溶剂中降解而引起制品强度大幅下降的问题。本发明的溶剂使用方法简单。溶解有高分子量的壳聚糖溶液可用于研究高分子量壳聚糖的溶解行为与分子结构的关系，及应用于高强壳聚糖凝胶、壳聚糖纤维、壳聚糖棒材、壳聚糖支架材料等制品的加工。
具体实施方式
以下结合实例进一步说明本发明。
实施例1：
将15.0克氢氧化锂、12.5克氢氧化钠和40.0克尿素混合，然后加入430.0克水和2.5克丙三醇，在磁力搅拌下形成透明碱性溶剂。
将5.0克脱乙酰度60%、分子量300万的壳聚糖粉末分散于上述碱性溶剂中，静置3小时使其充分溶胀，再将该溶胀液在-60℃冷冻，使用时10℃解冻，在机械搅拌下使其完全溶解，得到透明的高分子量壳聚糖溶液。所得溶液用2#砂芯漏斗真空抽滤，溶液可完全过滤，所得溶液澄清透明，表明高分子量壳聚糖在本例制得的碱性溶剂中能够完全溶解。该溶液放置6周，粘度基本不变，表明该壳聚糖碱性溶液比较稳定。
实施例2
将17.5克氢氧化锂和15.0克氢氧化钠混合加入到440.0克水中，再加入22.5克尿素和5.0克丙三醇，在磁力搅拌下形成透明碱性溶剂。
将7.5克脱乙酰度69%、分子量500万的壳聚糖粉末分散于上述碱性溶剂中，静置2小时使其充分溶胀，再将该溶胀液在-40℃冷冻，使用时0℃解冻，在机械搅拌下使其完全溶解，得到透明的高分子量壳聚糖溶液。所得溶液用2#砂芯漏斗真空抽滤，溶液可完全过滤，所得溶液澄清透明，表明高分子量壳聚糖在本例制得的碱性溶剂中能够完全溶解。该溶液放置6周，粘度基本不变，表明该壳聚糖碱性溶液比较稳定。
实施例3
将15.0克氢氧化锂和15.0克氢氧化钠混合加入到420.0克水中，再加入40.0克尿素和10.0.克丙三醇，在磁力搅拌下形成透明碱性溶剂。
将10.0克脱乙酰度78%、分子量400万的壳聚糖粉末分散于上述碱性溶剂中，静置1小时使其充分溶胀，再将该溶胀液在-50℃冷冻，使用时40℃解冻，在机械搅拌下使其完全溶解，进而得到透明的高分子量壳聚糖溶液。所得溶液用2#砂芯漏斗真空抽滤，溶液可完全过滤，所得溶液澄清透明，表明高分子量壳聚糖在本例制得的碱性溶剂中能够完全溶解。该溶液放置6周，粘度基本不变，表明该壳聚糖碱性溶液比较稳定。
实施例4
将45.0克尿素加入到398.0克水中，再加入25.0克氢氧化锂、10.0克氢氧化钠和12.0克丙三醇，在磁力搅拌下形成透明碱性溶剂。
将25.0克脱乙酰度82%、分子量100万的壳聚糖粉末分散于上述碱性溶剂中，静置3小时使其充分溶胀，再将该溶胀液在-20℃冷冻，使用时60℃解冻，在机械搅拌下使其完全溶解，得到透明的高分子量壳聚糖溶液。所得溶液用2#砂芯漏斗真空抽滤，溶液可完全过滤，所得溶液澄清透明，表明高分子量壳聚糖在本例制得的碱性溶剂中能够完全溶解。该溶液放置6周，粘度基本不变，表明该壳聚糖碱性溶液比较稳定。

Claims (2)

1.一种溶解高分子量壳聚糖的碱性溶剂，其特征在于：它能溶解分子量100万~600万的壳聚糖，其组分及其重量百分比含量为：
氢氧化锂：1.0~5.0 %
氢氧化钠：0~4.0 %
尿素：4.0~9.0 %
丙三醇：0.1~3.0 %
其余为水。
2.根据权利要求1所述的溶解高分子量壳聚糖的碱性溶剂的使用方法，其特征在于：将脱乙酰度50~85 %、分子量100万~600万的壳聚糖粉末分散于权利要求1所述的溶解壳聚糖的碱性溶剂中，静置1-3小时使其充分溶胀，然后将该溶胀液在-60℃~-20℃冷冻备用；使用时，在0℃~60℃下解冻，并在机械搅拌下使其完全溶解，得到透明的高分子量壳聚糖溶液。
CN2011100991763A 2011-04-20 2011-04-20 一种溶解高分子量壳聚糖的碱性溶剂及其用法 Expired - Fee Related CN102140177B (zh)