CN102115978B - 一种涤纶高速纺油剂 - Google Patents
一种涤纶高速纺油剂 Download PDFInfo
- Publication number
- CN102115978B CN102115978B CN201110001633.0A CN201110001633A CN102115978B CN 102115978 B CN102115978 B CN 102115978B CN 201110001633 A CN201110001633 A CN 201110001633A CN 102115978 B CN102115978 B CN 102115978B
- Authority
- CN
- China
- Prior art keywords
- oil
- constituent
- weight part
- part ratio
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种涤纶高速纺油剂,其组成成分及其重量份比为:平滑剂66–74,乳化剂10–14,抗静电剂4–8,集束剂6–10,添加剂3–5,所述平滑剂包括植物油、动物油、矿物油以及合成油脂中任意一种或多种的混合物、磷酸酯与聚丙烯酸酯,所述乳化剂包括烷基醚型表面活性剂、蓖麻油聚氧乙烯醚与月桂酸聚氧乙烯醚,所述抗静电剂包括铵盐的阳离子表面活性剂与十八醇磷酸酯钾盐,所述集束剂包括聚乙二醇月桂酸双酯、丙二醇与橡胶裂解油,所述添加剂包括滑石粉、脂肪醇、脂肪酸与丙烯酸。本设计不仅摩擦系数较稳定,而且油膜强度与油剂闪点均较高。
Description
技术领域
本发明涉及一种涤纶油剂,尤其涉及一种涤纶高速纺油剂,具体适用于稳定性强、油膜强度高、闪点温度高的涤纶高速纺油剂。
背景技术
化纤油剂是化纤在防治过程中,为了消除因摩擦而产生的静电、降低摩擦系数、使纤维具有较好的集束性、平滑性和分纤性,从而使其具有良好的可纺性和后加工性,而必须加入的一种油剂。现有的合成纤维用油剂,由于其构成组份的差异,在纺织应用过程中,易出现毛丝、断头等现象,导致卷绕成型差、优品率低、腐蚀现象严重,难以适应涤纶高速纺织的使用要求。
中国专利专利号为ZL99124724.8的发明专利公开了一种涤纶高速纺FDY油剂及其制造方法,各组份的重量百分比为平滑剂55—65%,乳化剂17—27%,集束剂5—15%,抗静电剂2—8%,添加剂1—5%,其制造方法为:先将计量准确的乳化剂、集束剂、抗静电剂抽入反应釜中,加热至40—80℃搅拌均匀,再将平滑剂抽入反应釜中,搅拌30—50min后,加入添加剂,搅拌均匀后冷却,过滤,包装即得。虽然该发明能有效提高涤纶纺丝质量,但其摩擦系数不稳定,易造成纤维缠绕、断头,而且,油膜强度较低,不仅易发生起毛现象,而且增加了后续加工的难度,此外,油剂闪点较低,易造成失火现象。
发明内容
本发明的目的是克服现有技术中存在的摩擦系数不稳定、油膜强度较低、油剂闪点较低的缺陷与问题,提供一种摩擦系数较稳定、油膜强度较高、油剂闪点较高的涤纶高速纺油剂。
为实现以上目的,本发明的技术解决方案是:一种涤纶高速纺油剂,其组成成分包括平滑剂、乳化剂、抗静电剂、集束剂和添加剂;所述涤纶高速纺油剂的组成成分及其重量份比为:平滑剂66–74,乳化剂10–14,抗静电剂4–8,集束剂6–10,添加剂3–5。
所述涤纶高速纺油剂的组成成分及其重量份比为:平滑剂70,乳化剂12,抗静电剂6,集束剂8,添加剂4。
所述平滑剂的组成成分及其重量份比为:植物油、动物油、矿物油以及合成油脂中任意一种或多种的混合物50–70,磷酸酯20–30,聚丙烯酸酯10–20;所述乳化剂的组成成分及其重量份比为:烷基醚型表面活性剂30–60,蓖麻油聚氧乙烯醚20–50,月桂酸聚氧乙烯醚10–30;所述抗静电剂的组成成分及其重量份比为:铵盐的阳离子表面活性剂50–70,十八醇磷酸酯钾盐30–50;所述集束剂的组成成分及其重量份比为:聚乙二醇月桂酸双酯20–50,丙二醇20–40,橡胶裂解油30–40;所述添加剂的组成成分及其重量份比为:滑石粉20–40,脂肪醇30–40,脂肪酸10–20,丙烯酸10–30。
所述平滑剂的组成成分及其重量份比为:植物油、动物油、矿物油以及合成油脂中任意一种或多种的混合物60,磷酸酯25,聚丙烯酸酯15;所述乳化剂的组成成分及其重量份比为:烷基醚型表面活性剂45,蓖麻油聚氧乙烯醚35,月桂酸聚氧乙烯醚20;所述抗静电剂的组成成分及其重量份比为:铵盐的阳离子表面活性剂60,十八醇磷酸酯钾盐40;所述集束剂的组成成分及其重量份比为:聚乙二醇月桂酸双酯35,丙二醇30,橡胶裂解油35;所述添加剂的组成成分及其重量份比为:滑石粉30,脂肪醇35,脂肪酸15,丙烯酸20。
与现有技术相比,本发明的有益效果为:
1、由于本发明一种涤纶高速纺油剂中平滑剂的重量份比为66–74,平滑剂的组成成分及其重量份比为:植物油、动物油、矿物油以及合成油脂中任意一种或多种的混合物50–70,磷酸酯20–30,聚丙烯酸酯10–20,尤其是磷酸酯与聚丙烯酸酯的加入增强了平滑剂的润滑性,从而使本发明能够确保金属与纤维之间具有稳定的摩擦系数,且保持在1.364左右,不仅使丝条所受的牵拉力稳定,纺丝张力波动极小,而且无丝线晃动及拉伸点移动,拉伸均匀,进而确保纤维不易发生缠绕、断头现象。因此本发明的摩擦系数较稳定。
2、由于本发明一种涤纶高速纺油剂中抗静电剂的重量份比为4–8,且抗静电剂的组成成分及其重量份比为:铵盐的阳离子表面活性剂50–70,十八醇磷酸酯钾盐30–50,尤其是铵盐的阳离子表面活性剂的加入,能够提高油膜强度,使其达到750N,不仅能够减少牵伸过程中的起毛现象,而且有利于适应后加工整经编织、喷水织机高速经纬纺织所需的油膜高强度。因此本发明的油膜强度较高。
3、由于本发明一种涤纶高速纺油剂中添加剂的重量份比为3–5,且添加剂的组成成分及其重量份比为:滑石粉20–40,脂肪醇30–40,脂肪酸10–20,丙烯酸10–30,尤其是脂肪酸与丙烯酸的加入能够提高本发明中各组成成分的结合程度,稳定各组成成分的物理和化学性质,从而提升本发明的闪点,使其可达205℃以上。因此本发明的油剂闪点较高。
具体实施方式
以下结合具体实施方式对本发明作进一步详细的说明
一种涤纶高速纺油剂,其组成成分包括平滑剂、乳化剂、抗静电剂、集束剂和添加剂;所述涤纶高速纺油剂的组成成分及其重量份比为:平滑剂66–74,乳化剂10–14,抗静电剂4–8,集束剂6–10,添加剂3–5。
优选涤纶高速纺油剂的组成成分及其重量份比为:平滑剂70,乳化剂12,抗静电剂6,集束剂8,添加剂4。
进一步优选平滑剂的组成成分及其重量份比为:植物油、动物油、矿物油以及合成油脂中任意一种或多种的混合物50–70,磷酸酯20–30,聚丙烯酸酯10–20;乳化剂的组成成分及其重量份比为:烷基醚型表面活性剂30–60,蓖麻油聚氧乙烯醚20–50,月桂酸聚氧乙烯醚10–30;抗静电剂的组成成分及其重量份比为:铵盐的阳离子表面活性剂50–70,十八醇磷酸酯钾盐30–50;集束剂的组成成分及其重量份比为:聚乙二醇月桂酸双酯20–50,丙二醇20–40,橡胶裂解油30–40;添加剂的组成成分及其重量份比为:滑石粉20–40,脂肪醇30–40,脂肪酸10–20,丙烯酸10–30。
再次优选平滑剂的组成成分及其重量份比为:植物油、动物油、矿物油以及合成油脂中任意一种或多种的混合物60,磷酸酯25,聚丙烯酸酯15;乳化剂的组成成分及其重量份比为:烷基醚型表面活性剂45,蓖麻油聚氧乙烯醚35,月桂酸聚氧乙烯醚20;抗静电剂的组成成分及其重量份比为:铵盐的阳离子表面活性剂60,十八醇磷酸酯钾盐40;集束剂的组成成分及其重量份比为:聚乙二醇月桂酸双酯35,丙二醇30,橡胶裂解油35;添加剂的组成成分及其重量份比为:滑石粉30,脂肪醇35,脂肪酸15,丙烯酸20。
实施例1:
一种涤纶高速纺油剂,其组成成分及其重量份比为:平滑剂66,乳化剂14,抗静电剂4,集束剂6,添加剂5。
平滑剂的组成成分及其重量份比为:植物油、动物油、矿物油以及合成油脂中任意一种或多种的混合物50,磷酸酯20,聚丙烯酸酯20;乳化剂的组成成分及其重量份比为:烷基醚型表面活性剂30,蓖麻油聚氧乙烯醚50,月桂酸聚氧乙烯醚30;抗静电剂的组成成分及其重量份比为:铵盐的阳离子表面活性剂50,十八醇磷酸酯钾盐50;集束剂的组成成分及其重量份比为:聚乙二醇月桂酸双酯20,丙二醇40,橡胶裂解油40;添加剂的组成成分及其重量份比为:滑石粉20,脂肪醇40,脂肪酸20,丙烯酸10。
实施例2:
一种涤纶高速纺油剂,其组成成分及其重量份比为:平滑剂74,乳化剂10,抗静电剂4,集束剂6,添加剂3。
平滑剂的组成成分及其重量份比为:植物油、动物油、矿物油以及合成油脂中任意一种或多种的混合物70,磷酸酯20,聚丙烯酸酯10;乳化剂的组成成分及其重量份比为:烷基醚型表面活性剂60,蓖麻油聚氧乙烯醚20,月桂酸聚氧乙烯醚10;抗静电剂的组成成分及其重量份比为:铵盐的阳离子表面活性剂70,十八醇磷酸酯钾盐30;集束剂的组成成分及其重量份比为:聚乙二醇月桂酸双酯50,丙二醇20,橡胶裂解油30;添加剂的组成成分及其重量份比为:滑石粉40,脂肪醇30,脂肪酸10,丙烯酸30。
实施例3:
一种涤纶高速纺油剂,其组成成分及其重量份比为:平滑剂70,乳化剂12,抗静电剂6,集束剂8,添加剂4。
平滑剂的组成成分及其重量份比为:植物油、动物油、矿物油以及合成油脂中任意一种或多种的混合物60,磷酸酯25,聚丙烯酸酯15;乳化剂的组成成分及其重量份比为:烷基醚型表面活性剂45,蓖麻油聚氧乙烯醚35,月桂酸聚氧乙烯醚20;抗静电剂的组成成分及其重量份比为:铵盐的阳离子表面活性剂60,十八醇磷酸酯钾盐40;集束剂的组成成分及其重量份比为:聚乙二醇月桂酸双酯35,丙二醇30,橡胶裂解油35;添加剂的组成成分及其重量份比为:滑石粉30,脂肪醇35,脂肪酸15,丙烯酸20。
由上可见,本发明不仅摩擦系数较稳定,而且油膜强度与油剂闪点均较高。
以上所述仅为本发明的较佳实施方式,本发明的保护范围并不以上述实施方式为限,但凡本领域普通技术人员根据本发明所揭示内容所作的等效修饰或变化,皆应纳入权利要求书中记载的保护范围内。
Claims (3)
1.一种涤纶高速纺油剂,其组成成分包括平滑剂、乳化剂、抗静电剂、集束剂和添加剂,其特征在于所述涤纶高速纺油剂的组成成分及其重量份比为:平滑剂66–74,乳化剂10–14,抗静电剂4–8,集束剂6–10,添加剂3–5;所述平滑剂的组成成分及其重量份比为:植物油、动物油、矿物油以及合成油脂中任意一种或多种的混合物50–70,磷酸酯20–30,聚丙烯酸酯10–20;所述乳化剂的组成成分及其重量份比为:烷基醚型表面活性剂30–60,蓖麻油聚氧乙烯醚20–50,月桂酸聚氧乙烯醚10–30;所述抗静电剂的组成成分及其重量份比为:铵盐的阳离子表面活性剂50–70,十八醇磷酸酯钾盐30–50;所述集束剂的组成成分及其重量份比为:聚乙二醇月桂酸双酯20–50,丙二醇20–40,橡胶裂解油30–40;所述添加剂的组成成分及其重量份比为:滑石粉20–40,脂肪醇30–40,脂肪酸10–20,丙烯酸10–30。
2.根据权利要求1所述的一种涤纶高速纺油剂,其特征在于所述涤纶高速纺油剂的组成成分及其重量份比为:平滑剂70,乳化剂12,抗静电剂6,集束剂8,添加剂4。
3.根据权利要求2所述的一种涤纶高速纺油剂,其特征在于:所述乳化剂的组成成分及其重量份比为:烷基醚型表面活性剂45,蓖麻油聚氧乙烯醚35,月桂酸聚氧乙烯醚20;
所述平滑剂的组成成分及其重量份比为:植物油、动物油、矿物油以及合成油脂中任意一种或多种的混合物60,磷酸酯25,聚丙烯酸酯15;
所述抗静电剂的组成成分及其重量份比为:铵盐的阳离子表面活性剂60,十八醇磷酸酯钾盐40;
所述集束剂的组成成分及其重量份比为:聚乙二醇月桂酸双酯35,丙二醇30,橡胶裂解油35;
所述添加剂的组成成分及其重量份比为:滑石粉30,脂肪醇35,脂肪酸15,丙烯酸20。