CN102086275A - 全钢子午线轮胎零度带束层配方胶料 - Google Patents

全钢子午线轮胎零度带束层配方胶料 Download PDF

Info

Publication number
CN102086275A
CN102086275A CN2009102165756A CN200910216575A CN102086275A CN 102086275 A CN102086275 A CN 102086275A CN 2009102165756 A CN2009102165756 A CN 2009102165756A CN 200910216575 A CN200910216575 A CN 200910216575A CN 102086275 A CN102086275 A CN 102086275A
Authority
CN
China
Prior art keywords
zero degree
degree belt
carbon black
steel radial
rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2009102165756A
Other languages
English (en)
Inventor
杨齐
张勋民
卿勤
曾清
胡录伟
杨利伟
黄晓丽
何洋
杨维建
袁德彬
戴明利
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SICHUAN TYRE RUBBER (GROUP) CO Ltd
Original Assignee
SICHUAN TYRE RUBBER (GROUP) CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SICHUAN TYRE RUBBER (GROUP) CO Ltd filed Critical SICHUAN TYRE RUBBER (GROUP) CO Ltd
Priority to CN2009102165756A priority Critical patent/CN102086275A/zh
Publication of CN102086275A publication Critical patent/CN102086275A/zh
Pending legal-status Critical Current

Abstract

本发明是全钢子午线轮胎零度带束层配方胶料。其要点在于:由多种原料配制而成,配方中原料包括10#天然橡胶、炭黑N375、炭黑N660、水合二氧化硅、氧化锌、改性烷基苯酚-甲醛树脂TKM-M、N-(1,3-二甲基丁基)-N′-苯基对苯二胺、间苯二酚甲醛树脂、硼酰化钴、六甲氧基甲基蜜胺、N-叔丁基-2-苯并噻唑次磺酰胺、不溶性硫黄HD OT20、N-环己基硫代邻苯二甲酰亚胺。本发明用于全钢子午线轮胎生产零度带束层使用的胶料。使用本发明生产的胶料降低了零度带束层的压出温度,提升了压出速度,提高了零度带束层的表面粘性,延长了粘性保持时间,改善了覆胶效果,有效解决了点状露铜、表面粘性差等质量缺陷。

Description

全钢子午线轮胎零度带束层配方胶料
所属技术领域
本发明涉及一种全钢子午线轮胎零度带束层的胶料,该胶料用于全钢子午线轮胎的生产。
背景技术
全钢子午线轮胎的关键部件-零度带束层的生产主要采用压出法。压出法是通过挤出机螺杆塑化胶料,依靠挤出机头产生的机械力将胶料挤压渗透到钢丝帘线中,从而使胶料与钢丝帘线有机的结合在一起成为零度带束层。在实际使用过程中普通胶料压出温度高,压出速度慢,压出的零度带束层表面不光滑、粘性差且有点状露铜现象,这就要求生产零度带束层的胶料应具有较低的门尼粘度,较好的流动性,优异的自粘性和较长的门尼焦烧时间。
发明内容
为了满足全钢子午线轮胎零度带束层压出工艺对胶料的加工性能要求,本发明的目的是提供能够满足生产工艺的零度带束层配方胶料,从而保证工艺的执行,提高零度带束层质量。
本发明所采用的技术方案是:采用调整补强体系、增粘树脂品种,同时优化调整硫化体系和混炼工艺的方式制成全钢子午线轮胎零度带束层配方胶料。其特征在于:由下述原料按重量比配制而成:
天然橡胶(SMR10#)                        100.0
炭黑N375                                30.0-40.0
炭黑N660                                15.0-20.0
氧化锌                                  8.0
水合二氧化硅                            5.0-7.0
改性烷基苯酚-甲醛树脂TKM-M              2.0-4.0
N-(1,3-二甲基丁基)-N′-苯基对苯二胺    2.0
间苯二酚甲醛树脂                        2.0
硼酰化钴                                1.0
六甲基氧基甲基密胺                      5.0
N-叔丁基-2-苯并噻唑次磺酰胺             1.4
不溶性硫黄HD OT20(硫黄含量为80%)       4.0-5.0
N-环己基硫代邻苯二甲酰亚胺              0.3
本发明的技术原理是通过并入部分N660炭黑,降低了胶料生热;用增粘树脂TKM-M代替203树脂,同时减少白炭黑及硫黄用量,提高了胶料的自粘性;在混炼中改用分段加氧化锌、多段加炭黑等改进和优化措施,降低了胶料门尼粘度,提高了炭黑分散度和胶料流动性,延长了胶料焦烧时间。
本发明的有益效果是,使用本实施配方制成的零度带束层胶料能够满足零度带束层压出工艺的加工性能要求,有效解决了过程质量缺陷。
具体实施方式:
零度带束层配方胶料由下述原料按重量比配制而成:
天然橡胶(SMR10#)                        100.0
炭黑N375                                33.0
炭黑N660                                16.0
氧化锌                                  8.0
水合二氧化硅                            5.0
改性烷基苯酚-甲醛树脂TKM-M              3.0
N-(1,3-二甲基丁基)-N′-苯基对苯二胺    2.0
间苯二酚甲醛树脂                        2.0
硼酰化钴                                1.0
六甲氧基甲基蜜胺                        5.0
N-叔丁基-2-苯并噻唑次磺酰胺             1.2
不溶性硫黄HD OT20                       4.4
N-环己基硫代邻苯二甲酰亚胺              0.3
在本实施例中,制造胶料采取以下工艺:
小配合试验胶料在Φ160×320开炼机上进行两段混炼制取。在第二段混炼过程中加入所有硫化体系材料,其它的配合剂均在第一段混炼过程中加入。一段混炼生产结束,制得的胶料停放4小时后方可进行二段混炼生产。
车间大料实验胶料,分为四段混炼生产,均执行自动混炼工艺。一、二、三段混炼均在2#GK270密炼机中进行,一段混炼加入生胶、2/3氧化锌、改性烷基苯酚-甲醛树脂TKM-M、白炭黑、2/3炭黑,排胶温度控制在160±5℃;二段混炼加入1/3氧化锌、1/6炭黑,排胶温度控制在150±5℃;三段混炼加入间苯二酚甲醛树脂、硼酰化钴、1/6炭黑,排胶温度控制在140±5℃;终炼胶在3#GK270密炼机中进行,在三段母炼胶中加入不溶性硫黄HD OT20、六甲氧基甲基蜜胺、N-叔丁基-2-苯并噻唑次磺酰胺、N-环己基硫代邻苯二甲酰亚胺,排胶温度控制在100±5℃。各段胶料须在室温下停放至少4h后方可进入下一步骤。
使用本实施例配方制成的零度带束层胶料性能测试数据如下:
门尼粘度[ML(1+4)100℃]            52.0
碳黑分散度/级                     8.2
300%定伸强度/MPa                 18.0
扯断强度/MPa                      23.9
邵尔A型硬度/度                    77
钢帘线H抽出力/N            1484
使用本实施例配方的胶料在全钢零度带束层压出工序操作中,降低了零度带束层的压出温度,明显提升了压出速度,提高了零度带束层的表面粘性,延长了粘性保持时间,改善了覆胶效果,有效解决了点状露铜、表面粘性差等质量缺陷。

Claims (2)

1.全钢子午线轮胎零度带束层配方胶料,其特征在于:由下述原料按重量比配制而成:
天然橡胶(SMR10#)                            100.0
炭黑N375                                    30.0-40.0
炭黑N660                                    15.0-20.0
氧化锌                                      8.0
水合二氧化硅                                5.0-7.0
改性烷基苯酚-甲醛树脂TKM-M                  2.0-4.0
N-(1,3-二甲基丁基)-N′-苯基对苯二胺        2.0
间苯二酚甲醛树脂                            2.0
硼酰化钴                                    1.0
六甲基氧基甲基密胺                          5.0
N-叔丁基-2-苯并噻唑次磺酰胺                 1.4
不溶性硫黄HD OT20(硫黄含量为80%)           4.0-5.0
N-环己基硫代邻苯二甲酰亚胺                  0.3
2.根据权利要求书1所述的零度带束层胶料,其特征在于:由下述原料按重量比配制而成:
天然橡胶(SMR10#)                            100.0
炭黑N375                                    33.0
炭黑N660                                    16.0
氧化锌                                      8.0
水合二氧化硅                                5.0
改性烷基苯酚-甲醛树脂TKM-M                  3.0
N-(1,3-二甲基丁基)-N′-苯基对苯二胺        2.0
间苯二酚甲醛树脂                            2.0
硼酰化钴                                    1.0
六甲氧基甲基蜜胺                            5.0
N-叔丁基-2-苯并噻唑次磺酰胺                 1.2
不溶性硫黄HD OT20                           4.4
N-环己基硫代邻苯二甲酰亚胺                  0.3
CN2009102165756A 2009-12-07 2009-12-07 全钢子午线轮胎零度带束层配方胶料 Pending CN102086275A (zh)