CN101434716B - 半钢丝子午线轮胎带束层压延胶料 - Google Patents

半钢丝子午线轮胎带束层压延胶料 Download PDF

Info

Publication number
CN101434716B
CN101434716B CN2007100505275A CN200710050527A CN101434716B CN 101434716 B CN101434716 B CN 101434716B CN 2007100505275 A CN2007100505275 A CN 2007100505275A CN 200710050527 A CN200710050527 A CN 200710050527A CN 101434716 B CN101434716 B CN 101434716B
Authority
CN
China
Prior art keywords
carbon black
steel wire
semi
sizing material
calendering
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2007100505275A
Other languages
English (en)
Other versions
CN101434716A (zh
Inventor
杨齐
张勋民
卿勤
董继学
李冬
罗建刚
朱家甫
田小顺
黄玉君
杨利伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SICHUAN TYRE RUBBER (GROUP) CO Ltd
Original Assignee
SICHUAN TYRE RUBBER (GROUP) CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SICHUAN TYRE RUBBER (GROUP) CO Ltd filed Critical SICHUAN TYRE RUBBER (GROUP) CO Ltd
Priority to CN2007100505275A priority Critical patent/CN101434716B/zh
Publication of CN101434716A publication Critical patent/CN101434716A/zh
Application granted granted Critical
Publication of CN101434716B publication Critical patent/CN101434716B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种半钢丝子午线轮胎压延带束层胶料。其要点在于：由多种原料配制而成，配方中原料包括天然橡胶牌号SMR20、炭黑N326、炭黑N660、白炭黑、硅烷偶联剂、氧化锌、防老剂4020、防老剂RD、间苯二酚-80、六甲氧基甲基蜜胺、促进剂DZ、不溶性硫黄IS-7020、防焦剂CTP。

Description

半钢丝子午线轮胎带束层压延胶料
所属技术领域
本发明涉及一种半钢丝子午线轮胎带束层胶料，该胶料用于压延法生产带束层。
背景技术
半钢丝子午线轮胎的关键部件-钢丝带束层，主要采用压延法生产。压延法是通过开炼机热炼胶料使胶料具有一定的流动性，同时压延机辊筒产生强大的机械力将胶料挤压、渗透到钢丝帘线中，从而使胶料与钢丝帘线有机地结合在一起成为坚固的带束层。在实际使用过程中普通胶料容易出现焦烧现象，而且压延帘布不平整。这就要求压延法生产带束层的胶料应具有较高门尼粘度以满足压延帘布的平整性和挺性、同时具有较长的门尼焦烧时间以满足压延工序操作安全性。
发明内容
本发明的目的是提供压延法生产带束层的胶料。
本发明的目的是通过以下技术方案实现的：半钢丝子午线轮胎带束层压延胶料，其特征在于：由下述原料按重量比配制而成：
原材料                                 发明胶料        普通胶料
天然橡胶  牌号SMR20                     100.0            100.0
炭黑N326                                25.0-35.0        55.0
炭黑N660                                15.0-25.0        0
氧化锌                                  5.0-10.0         8.0
水合二氧化硅                            10.0             10.0
[双(三乙氧基甲硅烷基丙基)]四硫化物      2.5              2.5
N-(1，3-二甲基丁基)-N′-苯基对苯二胺    1.5              1
2，2，4-三甲基-1，2-二氢化喹啉聚合体    1.5              1
间苯二酚-80                             1.0-3.0          3.0
六甲氧基甲基密胺                        2.5-5.0          5.0
N，N-二环己基-2-苯并噻唑次磺酰胺        0.5-1.7          1.4
二硫化二吗啉                            0-1.0            1.0
不溶性硫黄IS-7020                       5.0-7.0          5.0
N-环己基硫代邻苯二甲酰亚胺              0.3              0.3
本发明的技术原理是打破传统思维，通过并用N326、N660两种炭黑，提高胶料的门尼粘度；通过调整硫化体系各材料之间的配比关系，提高胶料的门尼焦烧时间。
具体实施方式：
原材料                                            重量比例
天然橡胶 牌号SMR20                                 100.0
炭黑N326                                           35.0
炭黑N660                                           25.0
氧化锌                                             8.0
水合二氧化硅                                       10.0
[双(三乙氧基甲硅烷基丙基)]四硫化物                 3.0
N-(1，3-二甲基丁基)-N′-苯基对苯二胺               1.5
2，2，4-三甲基-1，2-二氢化喹啉聚合体               1.5
间苯二酚-80                                        2.0
六甲氧基甲基蜜胺                                   5.0
N，N-二环己基-2-苯并噻唑次磺酰胺                   1.5
二硫化二吗啉                                       0
不溶性硫黄IS-7020                                  5.5
N-环己基硫代邻苯二甲酰亚胺                         0.3
在本实施例中，制造胶料采取以下工艺：
小配合试验胶料在Φ160×320开炼机上进行两段混炼制取。在第二段混炼过程中加入间苯二酚-80、六甲氧基甲基蜜胺以及所有硫化体系材料，其它的配合剂均在第一段混炼过程中加入。一段混炼生产结束，制得的胶料停放4小时后方可进行二段混炼生产。
车间大料实验胶料，分为三段混炼生产，均执行自动混炼工艺。一、二段混炼胶料在GK400N密炼机内进行生产；三段混炼胶料在GK255N密炼机内进行生产，胶料在压片机上翻炼3个来回后出片。各段胶料停放不少于4个小时后才能进入下一步骤。
使用本实施例配方制成的压延带束层胶料性能测试数据见下表。
项目                        实施配方                    普通配方
门尼焦烧时间(127℃)/min      18.10                        9.72
门尼粘度[ML(1+4)100℃]       75.0                         65.0
硫化仪数据(150℃)
ML/(dN.m)                    1.20                         0.85
MH/(dN.m)                    16.89                        14.23
T10/min                      3.05                         3.10
T90/min                      17.06                        16.97
T90-T10/min                  14.01                        13.87
项目                        实施配方            普通配方
胶料物理机械性能
300％定伸应力/MPa            16.5                15.9
拉伸强度/MPa                 20.7                20.8
拉断伸长率/％                390                 375
拉断永久变形/％              23                  20
邵尔A型硬度/度               74                  71
撕裂力/(kN.m-1)              118                 119
密度/(Mg.m-3)                1.20                1.18
100℃×72h热空气老化后胶料物理机械性能
拉伸强度/MPa                 14.5                14.1
扯断伸长率/％                280                 270
邵尔A型硬度/度               86                  85
撕裂力/(kN.m-1)              92                  88
H抽出力/N1)
老化前                       388                 397
热空气老化(100℃×72h)       348                 333
蒸汽老化(65℃×72h)          335                 345
盐水老化2)(75℃×72h)        314                 305
注：1)H抽出力实验所用钢帘线规格为：2+2×0.25NT
2)为该温度下的重量比为10％盐水
从以上内容可以看出，使用本实施例胶料比普通胶料可明显提高混炼胶料的门尼粘度，改善胶料的门尼焦烧，提高胶料的加工安全性能。
在带束层压延工序操作中，本实施例的原车胶料及其返回胶料均未出现焦烧现象，钢丝压延帘布平整。本实施例制得的胶料经过实际使用，完全满足带束层压延工艺的要求。

Claims (2)

1.一种半钢丝子午线轮胎带束层压延胶料，胶料的特征在于：由下述原料按重量比配制而成：
天然橡胶  牌号SMR20                     100.0
炭黑N326                                25.0-35.0
炭黑N660                                15.0-25.0
氧化锌                                  5.0-10.0
水合二氧化硅                            10.0
[双(三乙氧基甲硅烷基丙基)]四硫化物      2.5
N-(1，3-二甲基丁基)-N′-苯基对苯二胺    1.5
2，2，4-三甲基-1，2-二氢化喹啉聚合体    1.5
间苯二酚-80                             1.0-3.0
六甲氧基甲基密胺                        2.5-5.0
N，N-二环己基-2-苯并噻唑次磺酰胺        0.5-1.7
二硫化二吗啉                            0-1.0
不溶性硫黄IS-7020                       5.0-7.0
N-环己基硫代邻苯二甲酰亚胺              0.3。
2.根据权利要求1所述的带束层压延胶料，其特征在于：由下述原料按重量比配制而成：
天然橡胶  牌号SMR20                     100.0
炭黑N326                                35.0
炭黑N660                                25.0
氧化锌                                  8.0
水合二氧化硅                            10.0
[双(三乙氧基甲硅烷基丙基)]四硫化物      3.0
N-(1，3-二甲基丁基)-N′-苯基对苯二胺    1.5
2，2，4-三甲基-1，2-二氢化喹啉聚合体    1.5
间苯二酚-80                             2.0
六甲氧基甲基蜜胺                        5.0
N，N-二环己基-2-苯并噻唑次磺酰胺        1.5
二硫化二吗啉                            0
不溶性硫黄IS-7020                       5.5
N-环己基硫代邻苯二甲酰亚胺              0.3。
CN2007100505275A 2007-11-16 2007-11-16 半钢丝子午线轮胎带束层压延胶料 Expired - Fee Related CN101434716B (zh)