CN1020335C - 金属液表面覆盖剂 - Google Patents

金属液表面覆盖剂 Download PDF

Info

Publication number
CN1020335C
CN1020335C CN 90107645 CN90107645A CN1020335C CN 1020335 C CN1020335 C CN 1020335C CN 90107645 CN90107645 CN 90107645 CN 90107645 A CN90107645 A CN 90107645A CN 1020335 C CN1020335 C CN 1020335C
Authority
CN
China
Prior art keywords
present
powder
steel
molten
graphite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 90107645
Other languages
English (en)
Other versions
CN1059679A (zh
Inventor
李新合
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 90107645 priority Critical patent/CN1020335C/zh
Publication of CN1059679A publication Critical patent/CN1059679A/zh
Application granted granted Critical
Publication of CN1020335C publication Critical patent/CN1020335C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种金属液(铁水、钢水)表面覆盖剂，适用于各种条件的熔炼炉、高炉的大罐、中间包铁水和钢水的表面保温，其特征在于它由矿物-石墨粉，白灰粉，漂珠，珍珠砂，黄土粉，酸化石墨组合而成，其保温性能优于炭化稻壳，价格和用量低于炭化稻壳，比重大于炭化稻壳。使用该覆盖剂时不粘包，不挂渣，提高钢包、铁包的使用次数，解决罐坎，提前了脱硫时间，降低了脱硫剂用量，能多吃废钢，减少了扣罐坎，改善环境污染，便于运输、库存。

Description

随着我国工业的迅速发展，对钢铁成本质量有了新的要求，目前全国炼铁行业采用鱼雷罐传递铁水为数不多，大多数还是和钢包一样敞开大罐，由于铁水罐和钢水罐的传递时间较长（70分钟以上），这样在传递过程中铁水和钢水的温度损失非常严重。铁水温度的高低，对炼钢生产技术经济指标及后续工程都有着重要的影响，提高铁水、钢水温度，不仅有利于炼钢多吃废钢，降低能耗，而且也是后续连铸工程的要求。近年来，为提高铁水、钢水温度，许多厂家都作了一些有益的工作，或直接提高铁水、钢水温度，或铁罐加盖，或在铁水罐、钢水罐里加炭化稻壳，草木灰，蛭石，焦粉等保温材料，这些工作都取得了一定的效果。
但是提高铁水、钢水出炉温度不但耗能多，而且时间长影响设备寿命，有些铁水（比如高钛型钒钛磁铁矿）限制炉温，铁罐加盖设备大，不如使用保温材料，而草木灰，蛭石，焦粉虽然成本较低但保温效果差，温度损失仍然很大，炭化稻壳的保温效果虽然较好，但价格贵（900元/吨），用量大（0.1%），此外，它在铁水表面的铺展性不好，影响了保温效果，比重又小，运输、保管时占空间太大，使用时漫天飞扬，污染严重，并且受资源限制（做混合饲料和提炼白炭黑用）货源难以保证。
本发明的目的在于克服现有保温材料的不足，提供一种金属液（铁水、钢水）表面覆盖剂，它在铁水、钢水表面的铺展性和保温性好，价格低谦，用量少，且环境污染小，便于运输和库存;不受资源限制，能满足大生产需要。
本发明的金属液覆盖剂是一种粉末状（或颗粒状）的矿物组合物，其中成份有石墨粉，白灰粉、漂珠，珍珠砂，黄土粉，酸化石墨，各种成份的重量配比如下（总合不等于100）
石墨粉    35-50
白灰粉    30-10
漂珠    15-25
珍珠砂    30-15
黄土粉    5-15
酸化石墨    0.5-1
石墨粉起着骨架和保温隔热作用。石墨粉是酸性物质，用量低于下限时保温性差，用量高于上限时酸性大，有挂包现象;
白灰粉和黄土粉起着调整酸碱度的作用。白灰粉用量低于下限时碱性小，用量高于上限时碱性大;黄土粉含氧化硅，用量低于下限时酸性小，用量高于上限时酸性大;
漂珠起着覆盖、发热、保温作用。漂珠是酸性物质，用量低于下限时保温性差，用量高于上限时酸性大;
珍珠砂起着膨胀、绝热作用。用量低于下限时绝热性差，用量高于上限时熔点低;
酸化石墨是调整扩散性的。用量低于下限时铺展性差，用量高于上限时污染性大。
金属液覆盖剂的物化性能如下：
物理性能（见后表）
本发明的实施例如下：
一    二    三
石墨粉    35    42    50
白灰粉    30    20    10
漂珠    15    20    25
珍珠砂    30    22    15
黄土粉    5    10    15
酸化石墨    0.5    0.7    1
实施例一的覆盖剂碱度大，渣子稀，耗剂量大，保温差;实施例三的覆盖剂碱度小，粘度大可能出现挂渣现象，成本高;实施例二的覆盖剂酸碱度适当，熔点、熔速合适，保温性较好。
金属液表面覆盖剂按以下工艺流程制备如图
本产品适合各种条件的熔炼炉、高炉的大罐、中间包铁水和钢水的表面覆盖保温，如果钢水和铁水的表面液渣少可以多加覆盖剂，液渣厚可以少加 覆盖剂，一般用量为金属液的0.05%-0.1%，每分钟温降0.4-1.2度，降温速率可降低20-40%，提高温度20-40℃。该覆盖剂价格低廉（500元/吨），用量少（0.05%-0.1%），使用时金属液覆盖剂不粘包，不挂渣，不粘包，不浸包衬，不结壳，提高钢包、铁包的使用次数，提前了脱硫时间，降低了脱硫剂用量，解决了罐坎，提高铁水、钢水利用率，能多吃废钢，提高连铸机生产率;又由于其比重较大，不会漫天飞扬污染环境，既改善了工人的工作条件，又延长除尘风机使用寿命，减少库房占用，节约铁路运输车皮。
物理性能
熔点℃ 熔速T（1350度） 堆角（度） 容重g/cm2水份% 粒度（目）
1320±80    140±60    ≥90    ≤0.9    ≤1.5    ≤5
化学成分
SiO2CaO Al2O3Fe2O3MgO C S+P
34-50    8-30    8-15    1-5    1-5    7-27    微量

Claims (1)

  1. 一种金属液(铁水、钢水)表面覆盖剂，其特征在于它由石墨粉，白灰粉、漂珠，珍珠砂，黄土粉，酸化石墨组成，其重量配比如下(总合不等于100)
    石墨粉    35-50
    白灰粉    30-10
    漂珠      15-25
    珍珠砂    30-15
    黄土粉    5-15
    酸化石墨  0.5-1
CN 90107645 1990-09-10 1990-09-10 金属液表面覆盖剂 Expired - Fee Related CN1020335C (zh)