CN102011308A - 一种全棉针织布的环保耐久阻燃整理方法 - Google Patents
一种全棉针织布的环保耐久阻燃整理方法 Download PDFInfo
- Publication number
- CN102011308A CN102011308A CN 201010291408 CN201010291408A CN102011308A CN 102011308 A CN102011308 A CN 102011308A CN 201010291408 CN201010291408 CN 201010291408 CN 201010291408 A CN201010291408 A CN 201010291408A CN 102011308 A CN102011308 A CN 102011308A
- Authority
- CN
- China
- Prior art keywords
- environmental protection
- fire
- retardant
- finishing method
- cotton knitting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种全棉针织布的环保耐久阻燃整理方法,通过浸轧→低温烘干→高温焙烘→水洗→烘干→制软除臭的流程加工,本发明使用Aflammit KWB阻燃剂,在常规的染整设备上加工,由于阻燃剂与棉纤维发生共价键结合使产品不仅具有优异的阻燃性能,而且手感较柔软,更符合环保要求。采用本发明工艺生产的产品手感柔软,阻燃效果50次水洗可达美国CFR1615标准,甲醛含量低于20ppm,符合环保要求,无刺激性气味。
Description
技术领域
本发明公开了一种针织布的阻燃整理方法,具体涉及一种用于全棉针织布的环保耐久阻燃整理方法。
背景技术
近年来,由于纺织品引发的火灾数量和造成的经济损失较其它原因引起的火灾数量要高,并已经成为重大的社会性问题。为了阻止火灾发生,许多国家除加强防火措施外,还使用具有阻燃作用的纺织品。阻燃纺织品可延长人员撤离和采取措施灭火的时间,美、日、欧盟等许多国家相继出台了一系列的纺织品燃烧性技术法规和市场准入制度,阻燃纺织品广泛应用于服装、装饰和工业,阻燃纺织品的开发是大势所趋。
纯棉织物的耐久性阻燃整理大多由于有毒、有害被禁用,目前市场上的耐久阻燃整理主要有两种,一种是以THPC为阻燃剂的英国Proban工艺,另一种是以Huntsman公司的Pyrovatex CP为阻燃剂的工艺。前者的氨熏工艺由于纯粹的自交联反应,手感硬;TP-C键键能低,易分解产生甲醛,游离和释放甲醛含量高;同时由于设备复杂,其应用受到了限制;后者在整理和服用过程中也存在甲醛和刺激性气味等问题。
因而,亟需一种用于全棉针织布的环保耐久阻燃整理方法。
发明内容
针对上述缺陷,本发明目的是提供一种阻燃整理方法,其环保耐久,且所制成的布料手感好。
为达到上述目的,本发明采用的技术方案是:
本发明的一种全棉针织布的环保耐久阻燃整理方法,具体步骤为:
(1)、浸轧:
首先调配阻燃整理液,其中:
AFLAMMIT KWB阻燃剂 450-500g/L
磷酸 20-25g/L
交联剂TMM 18-23g/L
A105渗透剂 1-3g/L
其次,将坯布浸轧在阻燃整理液中,一浸一轧,轧辊压力为0.2-0.25MPa,轧余率为90-100%;
(2)、低温烘干:将温度控制在100-130℃,车速控制在8-10y/min进行烘干,以烘干透为准;
(3)、高温焙烘:在160-170℃下焙烘2-3min;
(4)、水洗:先进行冷水冲洗,再在48-53℃下进行碱洗8-12min,再在68-75下水洗8-12min,进而在38-42下1-2mL/L的双氧水中水洗8-12min,最后进行冷水冲洗;
(5)、烘干:将坯布烘干;
(6)、制软除臭:调配制软除臭液,其中包括3%-5%的硅油、0.5-0.8g/L甲醛捕捉剂、8-12g/L除臭剂。
在本发明的一种优选实施例中,所述整理液中,
AFLAMMIT KWB阻燃剂 480g/L
磷酸 22g/L
交联剂TMM 20g/L
A105渗透剂 2g/L
在本发明的一种优选实施例中,步骤(1)中,调配整理液,先将阻燃剂用冷水稀释溶解,然后加入事先稀释好的其它助剂,最后加水至总量。
在本发明的一种优选实施例中,所述步骤(4)中,碱洗液中添加纯碱量为10g/L。
在本发明的一种优选实施例中,所述甲醛捕捉剂为尿素。
在本发明的一种优选实施例中,所述除臭剂为植物类除臭剂。
在本发明的一种优选实施例中,采用松式热风烘干机进行烘干。
在本发明的一种优选实施例中,采用平幅松式水洗机进行水洗。
本发明与现有技术相比具有以下优点:
1)、选择了高纯度的阻燃剂,与同类阻燃剂相比,Aflammit KWB含量低、杂质少、对纤维有更多的固着率,因此降低织物游离甲醛的含量,水洗液中磷含量下降。
2)、低温烘干时温度控制在130℃以下,可以避免织物过烘而产生手感变硬现象。
3)、低温烘干后及时进行高温焙烘,可以避免放置过久引起织物泛黄,强力下降及色变现象产生。
4)、焙烘后的织物在24小时内进行中和水洗,可以避免影响阻燃效果及对织物产生不利影响。
5)、水洗时控制纯碱用量,确保布面最终PH值在7-8之间,同时碱洗、氧化温度要控制在一定范围内,可以避免影响水洗效果。
6)、使用植物类除臭剂有利于去除织物上的刺激性气味,尿素作为甲醛的捕捉剂,有利于进一步去除甲醛残留。
本发明使用Aflammit KWB阻燃剂能在常规的染整设备上加工,由于阻燃剂与棉纤维发生共价键结合使产品不仅具有优异的阻燃性能,而且手感较柔软,更符合环保要求。采用本发明工艺生产的产品手感柔软,阻燃效果50次水洗可达美国CFR1615标准,甲醛含量低于20ppm,符合环保要求,无刺激性气味。
附图说明
图1为本发明阻燃整理工艺的流程图。
具体实施方式
下面结合附图对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
一种全棉针织布的环保耐久阻燃整理方法,具体步骤为:
(1)、浸轧:
首先调配阻燃整理液,其中:
AFLAMMIT KWB阻燃剂 450-500g/L
磷酸 20-25g/L
交联剂TMM 18-23g/L
A105渗透剂 1-3g/L
其次,将坯布浸轧在阻燃整理液中,一浸一轧,轧辊压力为0.2-0.25MPa,轧余率为90-100%;
(2)、低温烘干:将温度控制在100-130℃,车速控制在8-10y/min进行烘干,以烘干透为准;
(3)、高温焙烘:在160-170℃下焙烘2-3min;
(4)、水洗:先进行冷水冲洗,再在48-53℃下进行碱洗8-12min,再在68-75℃下水洗8-12min,进而在38-42℃下1-2mL/L的双氧水中水洗8-12min,最后进行冷水冲洗;
(5)、烘干:将坯布烘干;
(6)、制软除臭:调配制软除臭液,其中包括3%-5%的硅油、0.5-0.8g/L甲醛捕捉剂、8-12g/L除臭剂。
实施例一:
(1)、浸轧:
首先调配阻燃整理液,其中:
AFLAMMIT KWB阻燃剂 480g/L
磷酸 22g/L
交联剂TMM 20g/L
A105渗透剂 2g/L
其次,将全棉活性印花针织布浸轧在阻燃整理液中,一浸一轧,轧辊压力为0.22MPa,轧余率为100%;
(2)、低温烘干:将温度控制在100-120℃,车速控制在9y/min进行烘干,以烘干透为准;
(3)、高温焙烘:在160℃下焙烘2min;
(4)、水洗:先进行冷水冲洗,再在50℃下进行碱洗10min,再在70℃下水洗10min,进而在40℃下1.5mL/L 27.5%双氧水中水洗10min,最后进行冷水冲洗;
(5)、烘干:将经过整理的布烘干;
(6)、制软除臭:调配制软除臭液,其中包括5%的硅油、0.5g/L尿素、10g/L除臭剂。
本工艺过程需要注意以下几点:
1、本工艺方法通过定型机、平幅水洗机、松式热风烘干机实现,要控制好轧车左、中、右压力一致,控制好轧余率。针织布保持松式加工可防止卷边造成的中边阻燃效果不一致,同时使用平幅松式水洗机可保证充分水洗,这对于一些未反应物质、游离甲醛和异味的去除非常重要。
2、活性印花的染料要严格筛选,不使用整理变色染料。
3、配制整理液时,先将阻燃剂用冷水稀释溶解,然后加入事先稀释好的其它助剂,最后加水至总量。
4、烘干时严格温度控制在130℃以下,以免织物过烘而产生手感变硬现象。
5、烘干后要及时焙烘,避免放置过久引起织物泛黄,强力下降及色变现象产生。
6、焙烘后的织物必须在24小时内中和水洗,以免影响阻燃效果及对织物产生不利影响。
7、水洗时控制纯碱用量,确保布面最终PH值在7-8之间,同时碱洗、氧化温度要控制好,以免影响水洗效果,对布面甲醛的残留及刺激性气味的去除不利。
8、本工艺方法使用植物类除臭剂有利于去除织物上的刺激性气味,尿素可作为甲醛的捕捉剂,有利于进一步去除甲醛残留。
本发明使用Aflammit KWB阻燃剂,能在常规的染整设备上加工,由于阻燃剂与棉纤维发生共价键结合使产品不仅具有优异的阻燃性能,与同类阻燃剂相比,Aflammit KWB杂质少、对纤维有更多的固着率,因此降低织物游离甲醛的含量,水洗液中磷含量下降,所制成的布料手感较柔软,更符合环保要求。采用本发明工艺生产的产品手感柔软,阻燃效果50次水洗可达美国CFR1615标准,甲醛含量低于20ppm,符合环保要求,无刺激性气味。
以上所述,仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本领域的技术人员在本发明所揭露的技术范围内,可不经过创造性劳动想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (8)
1.一种全棉针织布的环保耐久阻燃整理方法,其特征在于,具体步骤为:
(1)、浸轧:
首先调配阻燃整理液,其中:
AFLAMMIT KWB阻燃剂 450-500g/L
磷酸 20-25g/L
交联剂TMM 18-23g/L
A105渗透剂 1-3g/L
其次,将坯布浸轧在阻燃整理液中,一浸一轧,轧辊压力为0.2-0.25MPa,轧余率为90-100%;
(2)、低温烘干:将温度控制在100-130℃,车速控制在8-10y/min进行烘干,以烘干透为准
(3)、高温焙烘:在160-170℃下焙烘2-3min;
(4)、水洗:先进行冷水冲洗,再在48-53℃下进行碱洗8-12min,再在68-75下水洗8-12min,进而在38-42℃下1-2mL/L的双氧水中水洗8-12min,最后进行冷水冲洗;
(5)、烘干:将坯布烘干;
(6)、制软除臭:调配制软除臭液,其中包括3%-5%的硅油、0.5-0.8g/L甲醛捕捉剂、8-12g/L除臭剂。
2.根据权利要求1所述的一种全棉针织布的环保耐久阻燃整理方法,其特征在于,所述整理液中,
AFLAMMIT KWB阻燃剂 480g/L
磷酸 22g/L
交联剂TMM 20g/L
A105渗透剂 2g/L
3.根据权利要求2所述的一种全棉针织布的环保耐久阻燃整理方法,其特征在于,步骤(1)中,调配整理液,先将阻燃剂用冷水稀释溶解,然后加入事先稀释好的其它助剂,最后加水至总量。
4.根据权利要求1所述的一种全棉针织布的环保耐久阻燃整理方法,其特征在于,所述步骤(4)中,碱洗液中添加纯碱量为10g/L。
5.根据权利要求1所述的一种全棉针织布的环保耐久阻燃整理方法,其特征在于,所述甲醛捕捉剂为尿素。
6.根据权利要求5所述的一种全棉针织布的环保耐久阻燃整理方法,其特征在于,所述除臭剂为植物类除臭剂。
7.根据权利要求1所述的一种全棉针织布的环保耐久阻燃整理方法,其特征在于,采用松式热风烘干机进行烘干。
8.根据权利要求7所述的一种全棉针织布的环保耐久阻燃整理方法,其特征在于,采用平幅松式水洗机进行水洗。