CN101974819A - 一种花椒纤维梭织面料的前处理、染色和整理工艺 - Google Patents
一种花椒纤维梭织面料的前处理、染色和整理工艺 Download PDFInfo
- Publication number
- CN101974819A CN101974819A CN2010105049694A CN201010504969A CN101974819A CN 101974819 A CN101974819 A CN 101974819A CN 2010105049694 A CN2010105049694 A CN 2010105049694A CN 201010504969 A CN201010504969 A CN 201010504969A CN 101974819 A CN101974819 A CN 101974819A
- Authority
- CN
- China
- Prior art keywords
- dyeing
- woven fabric
- chinese prickly
- prickly ash
- working solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种花椒纤维梭织面料的前处理、染色和整理工艺,工艺流程为:花椒纤维梭织面料坯布、复合生物酶退浆煮炼、氧漂、纤维素酶处理、气流机染色、拉幅预缩,最后得到成品花椒纤维梭织面料。经本发明生产的花椒纤维梭织面料除具有纯天然、可降解、柔软等特性,同时还具有药用和保健的功效,还可起到防治湿疹、骚痒,延缓衰老等辅助作用,另外,还有驱避蚊子的效果。是一种上乘高档的服装面料,适合高档时装、晚装等服装面料的选材。
Description
技术领域
本发明涉及纺织制造业的染整技术领域,尤其是涉及一种花椒纤维梭织面料的前处理、染色和整理工艺。
背景技术
纺织服装是人类赖以生存的最基本需求之一,随着人口数量的增长和生活质量的提高,对纺织梭织面料的要求也越来越高。人们希望纺织面料在具有传统的御寒、美观等普通功能的同时,又具有特殊的辅助功能。如防水、防油、阻燃、易去污、药用保健功能等。花椒纤维梭织面料除具有纯天然、可降解、柔软等优点外,还赋予纺织品药用和保健的功能,在抑菌驱螨、微生物等方面具有显著功效,同时可以起到防治湿疹、骚痒,延缓衰老等辅助作用,另外,还有驱避蚊子的效果。花椒纤维梭织面料是一种具有优良药用保健功能的高档服装面料。
纺织企业发展的关键在于新产品的开发。目前,纺织技术复合化是国际纺织技术发展的主要趋势,保健药品与纺织品相互结合,以获得新的服用性和功能性。采用新工艺、新设备、新技术开发具有多用途、高性能、高附加值的产品已成为纺织品新的发展趋势。市场调研发现具有保健功能的纺织服装产品是长期深受大众期望和喜爱的。花椒纤维梭织面料是本发明人根据大量市场调研立项开发的一种高档纺织服装面料。
纺织工业“十一五”发展纲要对印染行业提出:要推行生物技术等高技术手段、提高印染布产品质量。由于花椒纤维梭织面料组织成份的特殊性,制定其染整处理方法需要格外注意的主要有3点。
第一:保证花椒纤维梭织面料的保健功能。
第二、保证花椒纤维梭织面料产品良好的服用性能。
第三:整个生产过程达到节能减排、绿色生产的目的。
有鉴于此,本工艺方法在经过一系列的研究和试验的基础上,总结和完善出一套花椒纤维梭织面料的前处理、染色和整理工艺,本案由此产生。
发明内容
本发明的目的在于提供一种花椒纤维梭织面料的前处理、染色和整理工艺方法,以使织物经染整处理后白度、毛效、布面等达到较好的效果,又不对花椒纤维梭织面料的保健功能有太大的损伤。
为了实现上述目的,本发明的解决方案如下:
一种花椒纤维梭织面料的前处理、染色和整理工艺,工艺流程为:花椒纤维梭织面料坯布、复合生物酶退浆煮炼、氧漂、气流机染色、拉幅预缩,最后得到成品。
所述花椒纤维梭织面料中花椒含量按重量百分比计为(6-8)%。
所述复合生物酶退浆煮练工艺流程为:热水洗、浸轧工作液、堆置、水洗、烘干;复合生物酶由淀粉酶2000L、301精炼酶和果胶酶CR复配;浸轧工作液的处方:
淀粉酶2000L 2.5g/L
301精炼酶 3.2g/L
果胶酶CR 1.0g/L
渗透剂 2g/L
螯合剂 0.5g/L
退浆煮练工艺条件:热水洗温度95℃,浸轧工作液温度60℃,轧余率110-130%,汽蒸堆置:温度60℃,时间60min,pH值6.5-7。
所述氧漂的工艺流程为:热水洗、浸轧工作液、汽蒸、热水洗、冷水洗、烘干;浸轧工作液处方:过氧化氢5-6g/L,硅酸钠4-6g/L,高效精炼剂DMA-1(厦门德美化工有限公司生产)5-7g/L,螯合剂DME-101(厦门德美化工有限公司生产)3-4g/L;氧漂工艺条件:常温浸轧工作液,堆置汽蒸温度95-100℃,反应时间45-50min,热水洗温度95-100℃。
所述气流机染色工艺流程为:下布、升温、染色、加入纯碱固色、清洗、皂化、清洗;气流机染色工艺条件:升温75℃/10min,染色75℃,(30-40)min,染色时间根据染色深度不同而异,颜色浅相对染色时间短,颜色深染色时间长,一般在(30-40)min。加入元明粉、碳酸钠固色60℃,30min,皂洗95℃,20min。
工作液处方为:
活性染料0.1%-8%(布重量的百分比,即o.w.f),烷基萘磺酸钠2-4g/L,硫酸钠(即元明粉)20-80g/L,碳酸钠5-20g/L,浴中柔软剂(浴中宝DXB-626,厦门德美化工有限公司生产)4-6g/L,匀染剂DS(酯肪胺聚氧乙烯醚的复配物)1g/L;pH稳定剂(AB-55)0.8g/L;上述活性染料为S-B红、S-3R黄、S-G藏青(亨斯迈纺织染化(中国)有限公司生产)中任意一种或几种混合。所述百分比%为各组分占布的重量百分比;g/L为每升工作液中加入各组分的克数。
浴中柔软剂和pH稳定剂AB-55为市售产品。柔软剂可以由厦门德美化工有限公司生产,AB-55可以由亨斯迈纺织染化(中国)有限公司生产。
以上助剂的用途为:
浴中柔软剂:有利于防止织物在染色运转过程中造成的擦伤问题。
匀染剂DS:增加织物染色的匀染性防止色花现象产生。
pH稳定剂AB-55:各种染料在不同的pH值(酸碱度)下上染率不同造成上色深浅和色光不一,该pH稳定剂有利于稳定染浴中的酸碱度以保证上染率及染物色光稳定。
气流机染色与传统工艺相比,要达到进一步的节能减排,气流机染色浴比可望降低到1∶3-4。但在超低浴比的条件下,染料易于团聚和聚集,染料团聚后,大大影响染料的上染性能。烷基萘磺酸钠系列表面活性剂对染料具有良好增溶作用,染料分子可以在表面活性剂胶束中增溶,同时对高浓度染料具有良好的解聚作用。
采用本发明工艺的有益效果表述如下:
在绿色环保方面,由于纺织品染整行业是污染大户,绿色环保是国家大力提倡的一项国策。针对花椒纤维梭织面料,需要探寻一种处理条件温和又高效合理的处理工艺,复合生物酶前处理为我们提供了良好的选择。本工艺采用的生物酶前处理由于其高效性、专一性、处理的生物温和性以及节能、环保等特性,具有其独特的优点。本工艺将生物酶复配技术在花椒纤维梭织面料前处理、染色、整理工艺中进行应用,使半制品及成品皆达到了生产和市场的要求。
在工艺改进方面,本方法还采用了汽流染色新工艺、新技术、新设备应用于花椒纤维梭织面料。
气流机染色是织物在封闭容器中依靠循环风机产生的高速空气流来带动,染液经过特殊的喷嘴,形成颗粒非常小的液状喷洒在织物表面,染液与织物充分接触,交换后回流到槽体底部,染液反复循环喷洒织物以达到染色目的。生产过程超小浴比、节能环保。
烷基萘磺酸钠系表面活性剂对染料具有良好增溶作用,染料分子可以在表面活性剂胶束中增溶,同时对高浓度染料具有良好的解聚作用,实现了超小浴比染色的顺利实施。
在提高产品质量方面,本发明提供的的一种花椒纤维梭织面料的前处理、染色、整理新工艺技术方法,所生产的花椒纤维梭织面料除具有纯天然、可降解、柔软等优点,同时还具有药用和保健的功能,在抑菌驱螨、微生物等方面具有显著功效,同时可以起到防治湿疹、骚痒,延缓衰老等辅助作用,另外,还有驱避蚊子的效果。适合高档休闲装、晚装、内衣等服装梭织面料的选材。
在应用前景方面,目前国内生产花椒纤维梭织面料的生产厂家基本没有。本工艺开发的花椒纤维梭织面料的染色、整理工艺方法为花椒纤维梭织面料新产品的开发提供了保证。高档花椒纤维梭织面料梭织面料的成功开发,成为全国纺织品市场的新热点。
具体实施方式
实施例1:
花椒纤维梭织面料坯布:组织结构:15tex/15tex,523根/10cm×283根/10cm;花椒含量(按重量百分比计):6%。
复合酶退浆煮练工艺流程:热水洗、浸轧工作液、堆置、水洗、烘干;浸轧工作液的处方(g/L表示每升工作液加入组分的克数):
淀粉酶2000L 2.5g/L
301精炼酶 3.2g/L
果胶酶CR 1.0g/L
渗透剂 2g/L
螯合剂 0.5g/L
注:以上淀粉酶2000L,301精炼酶,果胶酶CR复配为复合酶。渗透剂可选用JFC(脂肪醇聚氧乙烯醚)。螯合剂可选用DME-101,厦门德美化工有限公司生产。
退浆煮练工艺条件:热水洗温度95℃,浸轧工作液温度60℃,轧余率110-130%,汽蒸堆置时间60min,温度60℃,pH值6.5-7。
氧漂工艺流程:热水洗2格——浸轧工作液——堆置——热水洗——冷水洗——烘干。
1)工作液处方:双氧水5-6g/L,硅酸钠5g/L,高效精炼剂6g/L,金属螯合剂4g/L。
2)氧漂工艺条件:常温浸轧工作液,汽蒸堆置温度100℃,时间45min,热水洗温度95℃。
气流机染色工艺流程:下布——升温——染色——加入碳酸钠固色——清洗——皂化——清洗。
气流机染色工艺条件:
1)气流机染色处方(%)
组织规格:15tex/15tex,523根/10cm×283根/10cm,(花椒含量按重量百分比计:6%)
S-B红 0.31%(占布重)
S-3R黄 0.32%(占布重)
S-藏青 1.12%(占布重)
烷基萘磺酸钠 4g/L
元明粉 60g/L
碳酸钠 15g/L
浴中宝DXB-626 5g/L
匀染剂DS 1g/L
pH稳定剂AB-55 0.8g/L。
以上各百分比%为各组分占布重的重量百分比;g/L为每升工作液中加入各组分的克数。
2)气流机染色工艺:升温75℃/10min,染色75℃,30min,加入纯碱固色60℃,30min,皂洗95℃,20min。
前处理工艺采用了生物酶复配技术,利用生物降解改善织物物理性能及染色性能。染色采用超小浴比气流机染色方法,利用气流喷射带动织物循环完成染色过程。染液中加入烷基萘磺酸钠系列表面活性剂对染料具有良好增溶作用,染料分子可以在表面活性剂胶束中增溶,同时对高浓度染料具有良好的解聚作用,实现了超小浴比染色的顺利实施。
采用本发明制造的花椒纤维梭织面料除具有纯天然、可降解、柔软等优点,同时还具有药用和保健的功能,在抑菌驱螨、微生物等方面具有显著功效,同时可以起到防治湿疹、骚痒,延缓衰老等辅助作用,另外,还有驱避蚊子的效果。适合高档休闲装、晚装、内衣等服装梭织面料的选材。
以上仅为本发明的较佳实施例,并非对本发明的保护范围的限定,凡依本案的设计思路所做的等同变化,均落入本案的保护范围。
Claims (6)
1.一种花椒纤维梭织面料的前处理、染色和整理工艺,其特征在于其工艺流程为:花椒纤维梭织面料坯布、复合生物酶退浆煮炼、氧漂、气流机染色、拉幅预缩,最后得到成品。
2.如权利要求1所述的一种花椒纤维梭织面料的前处理、染色和整理工艺,其特征在于:所述花椒纤维梭织面料花椒含量重量比计为(6-8)%。
3.如权利要求1所述的一种花椒纤维梭织面料的前处理、染色和整理工艺,其特征在于:所述复合生物酶退浆煮练工艺流程为:热水洗、浸轧工作液、堆置、水洗、烘干;复合生物酶由淀粉酶2000L,301精炼酶和果胶酶CR复配;
浸轧工作液的处方:
淀粉酶2000L 2.5g/L
301精炼酶 3.2g/L
果胶酶CR 1.0g/L
渗透剂JFC 2g/L
螯合剂 0.5g/L
退浆煮练工艺条件:热水洗温度95℃,浸轧工作液温度60℃,轧余率110-130%,汽蒸堆置:温度60℃,时间60min,pH值6.5-7。
4.如权利要求1所述的一种花椒纤维梭织面料的前处理、染色和整理工艺,其特征在于:
所述氧漂的工艺流程为:热水洗、浸轧工作液、汽蒸、热水洗、冷水洗、烘干;浸轧工作液处方:过氧化氢5-6g/L,硅酸钠4-6g/L,高效精炼剂5-7g/L,螯合剂3-4g/L;氧漂工艺条件:常温浸轧工作液,堆置汽蒸温度95-100℃,反应时间45-50min,热水洗温度95-100℃。
5.如权利要求1所述的一种花椒纤维梭织面料的前处理、染色和整理工艺,其特征在于:
所述气流机染色工艺流程为:下布、升温、染色、加入纯碱固色、清洗、皂洗、清洗;工作液处方为:活性染料0.1-8%,烷基萘磺酸钠2-4g/L,硫酸钠20-80g/L,碳酸钠5-20g/L,浴中柔软剂4-6g/L,匀染剂1g/L;pH稳定剂0.8g/L;所述百分比%为各组分占布的重量百分比;g/L为每升工作液中加入各组分的克数;气流机染色工艺条件:升温75℃/10min,染色75℃,(30-40)min,加入硫酸钠、碳酸钠固色60℃,30min,皂洗95℃,20min。
6.如权利要求5所述的一种花椒纤维梭织面料的前处理、染色和整理工艺,其特征在于:所述活性染料为S-B红、S-3R黄、S-G藏青中任意一种或几种混合。