CN101962479A - 加成型液体硅橡胶 - Google Patents
加成型液体硅橡胶 Download PDFInfo
- Publication number
- CN101962479A CN101962479A CN2009100413094A CN200910041309A CN101962479A CN 101962479 A CN101962479 A CN 101962479A CN 2009100413094 A CN2009100413094 A CN 2009100413094A CN 200910041309 A CN200910041309 A CN 200910041309A CN 101962479 A CN101962479 A CN 101962479A
- Authority
- CN
- China
- Prior art keywords
- silicon rubber
- platinum
- add
- type liquid
- liquid silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种加成型液体硅橡胶，该硅橡胶包含的原料有：有机硅聚硅氧烷，白碳黑填料，甲基氢聚硅氧烷交联剂，催化剂与抑制剂。原料的重量份数组成如下：有机硅聚硅氧烷，100重量份；经处理的白碳黑填料，5-45重量份；甲基氢聚硅氧烷交联剂0.5-15重量份；铂金催化剂0.1-0.5重量份；铂金催化延迟剂0.01-0.1重量份。本发明的优点在于：提供一种抗毒能力强、粘接性能强、硫化速度快的加成型液体硅橡胶，本发明制备的产品可广泛应用于服装商标的制作。
Description
技术领域
本发明涉及一种硅橡胶产品，更具体的说，是涉及一种加成型液体硅橡胶。
背景技术
目前，许多服装标牌都采用PVC材料，由于PVC材料被证明对人体有害，在许多场合下是被禁止使用的。而硅橡胶具有无毒无害、耐候性好、防化学腐蚀、抗污染等特性，常被用来替代PVC材料制作服装商标。
但在制作精细图案的服装商标时，普通的硅橡胶很难满足要求，而加成型液体硅橡胶具有良好的流动性，能制作精细图案，而且能低温硫化，硫化速度快，非常适合用于制作服装商标。
由于服装标牌的辅料错综复杂，经常引起加成型液体硅橡胶中毒不硫化或附着力不好，严重影响了加成型液体硅橡胶的推广使用。为了解决这些问题，对于这种辅料常用底涂处理以增加附着力，但底涂工艺复杂，增加了制作成本，且底涂剂中含有机物挥发份大，对操作工人的身体有害。也有人在使用时采用补加偶联剂的方法，虽然粘接有所改善，但严重影响了操作性能。
发明内容
本发明提供一种抗毒能力强、粘接性能强的加成型液体硅橡胶及其制备方法。
本发明的另一目的是提供一种快速硫化、低成本的加成型液体硅橡胶。
本发明采用的技术方案是：一种粘接性能强、快速硫化的加成型液体硅橡胶，包含：
(A)100重量份的具有以下通式的有机硅聚硅氧烷：
Vi(CH3)2Si[OSi(CH3)2]m[OSi CH3Vi]nO Si(CH3)2Vi
其中，m为整数m＝200-1500；n为整数n＝0-50。
具有不同通式的有机硅聚硅氧烷为具有不同规格的硅油。
(B)0.5-15重量份的具有以下通式的甲基氢聚硅氧烷：
(R1O)2R2Si[OSi(CH3)2]x[OSi HCH3]yO Si R2(RiO)2
其中，R1为-CH3或-C2H5；R2为-H或-CH3；x为整数x＝0-200；y为整数y＝3-200。
(C)5-45重量份的白碳黑填料，白炭黑为硅氮烷处理过的比表面积为200m2/g的白炭黑。
(D)0.1-0.5重量份的铂金催化剂。铂金催化剂为铂的含炔醇基团氨基配合物，其中铂金含量在1000-6000ppm之间。
(E)0.01-0.1重量份的铂金催化延迟剂，铂金催化延迟剂为炔醇化合物，具体为甲基戊炔醇。
具体实施方式
实施例1.选用100重量份结构通式为Vi(CH3)2Si[OSi(CH3)2]500OSi(CH3)2 Vi的硅油为基础料，添加20重量份的硅氮烷处理过的比表面积为200m2/g白碳黑，加入5重量份的粘度为1000mpa.S(25℃)，结构通式为(C2H5O)2(CH3)2Si [OSi(CH3)2]50[OSiHCH3]150OSi(CH3)2(C2H5O)2的甲基氢聚硅氧烷，0.05重量份甲基戊炔醇，搅拌均匀之后，再加入0.5重量份的铂金催化剂，此催化剂为铂的含炔醇基团氨基配合物(2500ppm，以铂计)，再一次搅拌均匀，在真空中除尽气泡，注入点胶瓶，通过点胶机将上述混合物点入标牌模具中，附上制作服装标签用的尼龙布，在120℃条件下模压30S，两模之间压力0.6Mpa，将模压好的标签冷却待测。
实施例2.选用100重量份结构通式为Vi(CH3)2Si[OSi(CH3)2]500O Si(CH3)2Vi的硅油为基础料，添加20重量份的硅氮烷处理过的比表面积为200m2/g白碳黑，加入5重量份的粘度为1000mpa.S(25℃)不限定x值和y值的甲基氢聚硅氧烷，0.05重量份甲基戊炔醇，搅拌均匀之后，再加入0.5重量份的铂金催化剂，此催化剂为铂的含炔醇基团氨基配合物(2500ppm，以铂计)，再一次搅拌均匀，在真空中除尽气泡，注入点胶瓶，通过点胶机将上述混合物点入标牌模具中，附上制作服装标签用的尼龙布，在120℃条件下模压30S，两模之间压力0.6Mpa，将模压好的标签冷却待测。
测试结果如下表：
| 产品 | 拉拔力测试 | 硬度 |
| 实例1产品 | 15公斤拉力 | 40(邵氏) |
| 对比实例2产品 | 6公斤拉力 | 42(邵氏) |
实施例3.选用100重量份结构通式为Vi(CH3)2Si[OSi(CH3)2]500OSi(CH3)2Vi的硅油为基础料，添加20重量份的硅氮烷处理过的比表面积为200m2/g白碳黑，加入5重量份的粘度为1000mpa.S(25℃)的甲基氢聚硅氧烷，0.05重量份甲基戊炔醇，搅拌均匀之后，再加入0.5重量份的铂金催化剂，此催化剂为铂的含炔醇基团氨基配合物(2500ppm，以铂计)，再一次搅拌均匀，在真空中除尽气泡，注入点胶瓶，通过点胶机将上述混合物点入标牌模具中，附上条状尼龙布，此尼龙布表面用磷酸三乙酯处理过后，在120℃条件下模压30S，两模之间压力0.6Mpa，将模压好的标签冷却待测。
实施例4.对比实验，选用100重量份结构通式为Vi(CH3)2Si[OSi(CH3)2]500O Si(CH3)2 Vi的硅油为基础料，添加20重量份的硅氮烷处理过的比表面积为200m2/g白碳黑，加入5重量份的粘度为1000mpa.S(25℃)的不限定x值和y值的甲基氢聚硅氧烷，0.05重量份甲基戊炔醇，搅拌均匀之后，再加入0.5重量份的铂金催化剂，此铂金催化剂为karstedt催化剂(2500ppm，以铂计)，再一次搅拌均匀，在真空中除尽气泡，注入点胶瓶，通过点胶机将上述混合物点入标牌模具中，附上条状尼龙布，此尼龙布表面用磷酸三乙酯处理过后，在120℃条件下模压30S，两模之间压力0.6Mpa，将模压好的标签冷却待测。
测试结果如下：
| 产品 | 标签表面干爽度 | 硬度 |
| 实例3产品 | 干爽，硅橡胶硫化完全 | 38(邵氏) |
| 对比实例4产品 | 不干爽，硅橡胶硫化不完全 | 5(邵氏) |
通过以上例子可以得知，采用本发明用于制作标签，具有快速硫化、抗毒能力强和与底材粘接性能强的特点。
以上内容仅为本发明的较佳实施例，对于本领域的普通技术人员，依据本发明的思想，在具体实施方式及应用范围上均会有改变之处，本说明书内容不应理解为对本发明的限制。
Claims (7)
1.一种加成型液体硅橡胶，其特征在于：包含：
(A)100重量份的具有以下通式的有机硅聚硅氧烷：
Vi(CH3)2Si[OSi(CH3)2]m[OSi CH3Vi]nO Si(CH3)2Vi
其中，m为整数m＝200-1500；n为整数n＝0-50；
(B)0.5-15重量份的具有以下通式的甲基氢聚硅氧烷：
(R1O)2R2Si[OSi(CH3)2]x[OSi HCH3]yO Si R2(R1O)2
其中，R1为-CH3或-C2H5；R2为-H或-CH3；x为整数x＝0-200；y为整数y＝3-200；
(C)5-45重量份的白碳黑填料；
(D)0.1-0.5重量份的铂金催化剂；
(E)0.01-0.1重量份的铂金催化延迟剂。
2.根据权利要求1所述的加成型液体硅橡胶，其特征在于：(A)通式中的m取值范围为500-1000，n取值范围为3-10。
3.根据权利要求1所述的加成型液体硅橡胶，其特征在于：(B)通式中的x取值范围为50-100，y取值范围为50-100。
4.根据权利要求1所述的加成型液体硅橡胶，其特征在于：(C)中白炭黑填料为硅氮烷处理过的比表面积为200m2/g的白炭黑。
5.根据权利要求1所述的加成型液体硅橡胶，其特征在于：(D)铂金催化剂为铂的含炔醇基团氨基配合物，铂金含量在1000-6000ppm之间。
6.根据权利要求1所述的加成型液体硅橡胶，其特征在于：(E)铂金催化延迟剂为炔醇化合物。
7.根据权利要求6所述的加成型液体硅橡胶，其特征在于：铂金催化延迟剂为甲基戊炔醇。