CN107163906A - 服装标签用胶水及其制备方法 - Google Patents

服装标签用胶水及其制备方法 Download PDF

Info

Publication number
CN107163906A
CN107163906A CN201710447179.9A CN201710447179A CN107163906A CN 107163906 A CN107163906 A CN 107163906A CN 201710447179 A CN201710447179 A CN 201710447179A CN 107163906 A CN107163906 A CN 107163906A
Authority
CN
China
Prior art keywords
mass parts
organosilicon
label
curing agent
platinum catalyst
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710447179.9A
Other languages
English (en)
Inventor
翟慎理
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Mei Sheng Intelligent System Co., Ltd.
Original Assignee
Shanghai Maxim Garment Accessories Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Maxim Garment Accessories Co Ltd filed Critical Shanghai Maxim Garment Accessories Co Ltd
Priority to CN201710447179.9A priority Critical patent/CN107163906A/zh
Publication of CN107163906A publication Critical patent/CN107163906A/zh
Pending legal-status Critical Current

Abstract

一种服装标签用胶水，由如下原料制成：铂催化剂0.5‑0.7质量份；有机硅95‑105质量份；UV固化剂2‑4质量份。本发明胶水内聚力高，标签从服装布料上剥离后，不容易留下残胶，并且由于有机硅为惰性材料，制成的胶水耐温性强，布料不容易产生色变。

Description

服装标签用胶水及其制备方法
技术领域
本发明属于标签用胶水技术领域，尤其涉及一种服装标签用胶水及其制备方法。
背景技术
服装标签通常通过胶水粘附于服装上(如尺码贴)。
目前，服装标签常用的丙烯酸压敏胶水内聚力不足，在标签剥离后容易在服装上留下残胶，并且耐温性不强，在高温下容易在服装上产生色变。
发明内容
基于此，针对上述技术问题，提供一种服装标签用胶水及其制备方法。
为解决上述技术问题，本发明采用如下技术方案：
一种服装标签用胶水，由如下原料制成：
铂催化剂 0.5-0.7质量份；
有机硅 95-105质量份；
UV固化剂 2-4质量份。
所述铂催化剂为0.6质量份，所述有机硅为100质量份，所述UV固化剂为2-4质量份。
本方案还涉及一种服装标签用胶水的制备方法，包括：
将铂催化剂以及UV固化剂加入有机硅中，三者配比为：
铂催化剂 0.5-0.7质量份；
有机硅 95-105质量份；
UV固化剂 2-4质量份；
通过搅拌机对加入铂催化剂以及UV固化剂的有机硅进行搅拌，搅拌速度在30秒内从300转/秒提升至3000转/秒，搅拌时间10-20分钟。
所述铂催化剂为0.6质量份，所述有机硅为100质量份，所述UV固化剂为2-4质量份。
本发明胶水内聚力高，标签从服装布料上剥离后，不容易留下残胶，并且由于有机硅为惰性材料，制成的胶水耐温性强，布料不容易产生色变。
具体实施方式
一种服装标签用胶水，由如下原料制成：
铂催化剂 0.5-0.7质量份；
有机硅 95-105质量份；
UV固化剂 2-4质量份。
其制备过程如下：
按上述配比将铂催化剂以及UV固化剂加入有机硅中。
通过搅拌机对加入铂催化剂以及UV固化剂的有机硅进行搅拌，搅拌速度在30秒内从300转/秒提升至3000转/秒，搅拌时间10-20分钟。
本发明胶水粘合性能佳、内聚力高，移除性能优秀，标签从服装布料上剥离后，不会留下残胶，并且由于有机硅为惰性材料，制成的胶水耐温性强，布料不会产生色变。
较佳的，铂催化剂为0.6质量份，有机硅为100质量份，UV固化剂为2-4质量份，制成的胶水内聚力、耐温性更佳。
通过如下实验对上述性能进行验证：
在温度60-80℃、湿度60-80％的环境下，在多种常用服装的布料上通过本发明的胶水贴上标签(如尺码贴)，并用5kg的重物压在标签上7天，7天后将标签从服装布料上剥离，实验结果见表1：
表1
实施例1
本实施例为一种服装标签用胶水，由如下原料制成：
铂催化剂 0.5质量份；
有机硅 105质量份；
UV固化剂 2质量份。
其制备过程如下：
按上述配比将铂催化剂以及UV固化剂加入有机硅中。
通过搅拌机对加入铂催化剂以及UV固化剂的有机硅进行搅拌，搅拌速度在30秒内从300转/秒提升至3000转/秒，搅拌时间10分钟。
实施例2
本实施例为一种服装标签用胶水，由如下原料制成：
铂催化剂 0.7质量份；
有机硅 95质量份；
UV固化剂 4质量份。
其制备过程如下：
按上述配比将铂催化剂以及UV固化剂加入有机硅中。
通过搅拌机对加入铂催化剂以及UV固化剂的有机硅进行搅拌，搅拌速度在30秒内从300转/秒提升至3000转/秒，搅拌时间20分钟。
实施例3
本实施例为一种服装标签用胶水，由如下原料制成：
铂催化剂 0.6质量份；
有机硅 100质量份；
UV固化剂 3质量份。
其制备过程如下：
按上述配比将铂催化剂以及UV固化剂加入有机硅中。
通过搅拌机对加入铂催化剂以及UV固化剂的有机硅进行搅拌，搅拌速度在30秒内从300转/秒提升至3000转/秒，搅拌时间15分钟。
但是，本技术领域中的普通技术人员应当认识到，以上的实施例仅是用来说明本发明，而并非用作为对本发明的限定，只要在本发明的实质精神范围内，对以上所述实施例的变化、变型都将落在本发明的权利要求书范围内。

Claims (4)

1.一种服装标签用胶水，其特征在于，由如下原料制成：
铂催化剂0.5-0.7质量份；
有机硅95-105质量份；
UV固化剂2-4质量份。
2.根据权利要求1所述的一种服装标签用胶水，其特征在于，所述铂催化剂为0.6质量份，所述有机硅为100质量份，所述UV固化剂为2-4质量份。
3.一种服装标签用胶水的制备方法，其特征在于，包括：
将铂催化剂以及UV固化剂加入有机硅中，三者配比为：
铂催化剂0.5-0.7质量份；
有机硅95-105质量份；
UV固化剂2-4质量份；
通过搅拌机对加入铂催化剂以及UV固化剂的有机硅进行搅拌，搅拌速度在30秒内从300转/秒提升至3000转/秒，搅拌时间10-20分钟。
4.根据权利要求3所述的一种服装标签用胶水的制备方法，其特征在于，所述铂催化剂为0.6质量份，所述有机硅为100质量份，所述UV固化剂为2-4质量份。
CN201710447179.9A 2017-06-14 2017-06-14 服装标签用胶水及其制备方法 Pending CN107163906A (zh)