CN101654578B - 水性氟碳仿大理石涂料及其制备方法和仿大理石效果喷涂方法 - Google Patents

水性氟碳仿大理石涂料及其制备方法和仿大理石效果喷涂方法 Download PDF

Info

Publication number
CN101654578B
CN101654578B CN2008101419835A CN200810141983A CN101654578B CN 101654578 B CN101654578 B CN 101654578B CN 2008101419835 A CN2008101419835 A CN 2008101419835A CN 200810141983 A CN200810141983 A CN 200810141983A CN 101654578 B CN101654578 B CN 101654578B
Authority
CN
China
Prior art keywords
parts
paint
water
base fluorocarbon
white
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2008101419835A
Other languages
English (en)
Other versions
CN101654578A (zh
Inventor
陈寿生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Zhanchen Intelligent Property Management Co ltd
Beijing Zhanchen New Material Co ltd
China Zhanchen New Materials Group Co.,Ltd.
Shanghai Zhanchen Paint Co ltd
Zhuhai Zhanchen New Material Co ltd
Original Assignee
Shanghai Fuchen Chemical Co Ltd
Beijing Zhanchen Chemical Co Ltd
Zhanchen Paint Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Fuchen Chemical Co Ltd, Beijing Zhanchen Chemical Co Ltd, Zhanchen Paint Group Co Ltd filed Critical Shanghai Fuchen Chemical Co Ltd
Priority to CN2008101419835A priority Critical patent/CN101654578B/zh
Publication of CN101654578A publication Critical patent/CN101654578A/zh
Application granted granted Critical
Publication of CN101654578B publication Critical patent/CN101654578B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种水性氟碳仿大理石外墙涂料及其制备方法和仿大理石效果喷涂方法，所述涂料包含以下重量份的组份：焦磷酸钠0.05份，纳米硅酸盐2.0份，白漆23.95份，红色漆5份，灰色漆7份，黄色漆2份，自来水60份；所述白漆的组分(以重量份计)包括：水性氟碳乳液12～20份、纤维素0.1～1份、纳米硅酸盐0.1～1份、分散剂0.1～1份、pH调节剂0.1～1份、消泡剂0.1～1份、成膜剂1.0～2.0份、防腐防霉剂1.0～2.5份、1.0～2.0重量份的防冻剂、钛白粉10～12份、碳酸钙20～25份、硫酸钡2.0～5.0份、水35～40。本发明涂料保持了天然大理石相同的装饰效果，同时具有整体色彩一致、节能、环保、施工方便及容易翻新的特点，可完全取代天然大理石在外墙中的应用，节省成本。

Description

水性氟碳仿大理石涂料及其制备方法和仿大理石效果喷涂方法
技术领域
本发明涉及一种外墙涂料的技术领域，尤其涉及一种水性氟碳型外墙涂料及其制备方法。 
背景技术
随着社会经济与技术的飞速发展，特别是近年来我国的建筑发展出现了前所未有的大好局面。旧城改造，新区建设，建筑物外墙装饰向着高环保、高节能、高性能三方面发展，涂料作为建材中的一个非常重要的组成部分而越来越受到人们的欢迎。 
长时间以来，天然大理石在外墙装饰中起到了重要作用，但因天然大理石本身固有的特性也影响其在外墙装饰领域的应用，天然石材的颜色受天然矿石颜色的限制，使得装饰后整体的颜色不会完全一致，而且天然石材具有自重大，对墙体的荷载大、成本高、难以翻新、脱落等缺陷，使得很多地区现在已明令禁止使用，因此，如何找到可以替代天然大理石作为外墙装饰的材料与方法也就成为一项新课题。 
譬如，CN200510060958.0号中国专利“一种高弹性仿大理石施工工艺”就公开了一种高弹性仿大理石施工方法，以厚浆型弹性涂料替代真石漆达到大理石的效果，本发明的工艺步骤如下：(1)清理平整墙面基层；(2)在墙面基层上均匀涂布水性或油性封闭底漆；(3)在墙面封闭底漆层指触干燥后，均匀喷涂厚浆型弹性涂料，所述厚浆型弹性涂料粘度值为50000～300000mpa·s；(4)在墙面弹性涂料层触指干燥后均匀涂布水性或油性罩光面漆，采用厚浆型弹性涂料在颜色的选择调配上更广泛于真石漆的彩砂，其成品颜色效果仿大理的逼真程度要高于真石漆；厚浆型弹性涂料有超优越的抗裂性，其断裂延伸率达到200％以上，但该专利是侧重于提供如何利用厚浆型弹性涂料来替代真石漆达到大理石效果，至于所利用的厚浆型弹性涂料的具体组成成份则没有涉及。 
再如专利号为CN200710132107.1的中国发明专利“新型水性外墙氟碳涂料及其制备方法”公开了一种新型水性外墙氟碳涂料，它是由溶剂(水)、水性氟碳乳液、填料、复合成膜助剂、分散剂、润湿剂、流平剂、增稠剂、杀菌剂研制而成。其中各组分在涂料中的加入量为：溶剂(水)为5.％～15％，水性氟碳乳液为40％-70％，复合成膜助剂为5％-14％，金红石钛白粉10％～25％，滑石粉5％～10％，分散剂为.0.1％～0.5％，润湿剂为.0.001％～0.003％，流平剂为.0.004％～0.01％，杀菌剂为.0.1％～0.4％，增稠剂为.1％～1.8％，消泡剂为0.01％-0.05％。 
综合上述现有技术，我们发现，目前的仿大理石的施工方法以及所涉及的涂料存在如下的缺陷：(1)涂布形成的漆膜表面不够平滑、光亮、纹路不够均匀清晰，从而导致仿大理石的效果不佳；(2)由于采用水、油两相的涂料，从而导致洒点小的不足，而其中的油性涂料使用后还会残余有机溶剂，不利环保。 
发明内容
本发明所解决的技术问题是克服现有技术存在的缺陷，而提出了一种制备用于高档建筑外墙的水性氟碳仿大理石效果涂料，使用该涂料，可达到漆膜表面平滑、光亮，有均匀清晰的纹路，可使喷涂的外墙具备天然大理石的色彩及纹理效果，成本大约为天然大理石的三分之一，有优异的耐候和抗污功能，色泽持久，对环境友好。 
本发明所解决的另一个技术问题是，提供所述的水性氟碳仿大理石效果涂料的制备方法。 
本发明解决的又一个技术问题是，提供利用所述水性氟碳仿大理石外墙涂料进行喷涂以获得预定大理石效果的方法。 
为解决上述技术问题，本发明的技术方案是这样的： 
一种水性氟碳仿大理石外墙涂料，所述涂料包含以下重量份的组份： 
Figure DEST_PATH_GSB00000540124600011
Figure DEST_PATH_GSB00000540124600021
所述白漆包含如下以重量份表示的组分： 
所述灰色漆是用制备好的白漆130克加1.3克芬兰CPS炭黑色浆搅匀而成；所述红色漆是用制备好的白漆160克加9.0克芬兰CPS外墙红浆搅匀而成； 
所述黄色漆是用制备好的白漆190克加14.0克芬兰CPS外墙黄浆搅匀而成。 
所述白漆还包含1.0～2.0重量份的防冻剂。 
所述分散剂选用羧酸胺盐。 
所述钛白粉选用金红石钛白。 
本发明还公开一种水性氟碳仿大理石外墙涂料的制备方法，该方法包括如 下步骤： 
a.在容器中依次加入水、纤维素、纳米硅酸盐、羧酸胺盐分散剂，中速800转/分钟边加边搅，溶解30分钟； 
b.再依次加入PH调节剂、消泡剂、防冻剂、成膜剂、防腐防霉剂，中速800转/分钟搅匀； 
c.再依次加入金红石钛白、碳酸钙、硫酸钡，用高速2000转/分钟，分散达细度45微米，转低速400转/分钟加入水性氟碳乳液搅匀10钟，得到白漆，备用； 
d.用制备好的白漆130克加1.3克芬兰CPS炭黑色浆搅匀制得灰色漆； 
e.用制备好的白漆160克加9.0克芬兰CPS外墙红浆搅匀制得红色漆； 
f.用制备好的白漆190克加14.0克芬兰CPS外墙黄浆搅匀制得黄色漆； 
g.取自来水60份、焦磷酸钠0.05份、纳米硅酸盐2.0份、备用白漆23.95份、备用红色漆5份、备用灰色漆7份和备用黄色漆2份，将水、焦磷酸钠、纳米硅酸盐依次加容器，中速800转/分钟搅匀30分钟，再转低速400转/分钟，依次加入白漆、红色漆、灰色漆、黄色漆，搅拌20分钟，即为仿大理石漆。 
本发明还涉及一种仿大理石效果外墙的喷涂方法，该方法包括：用压力式喷枪均匀喷涂一遍，干后用一水性氟碳罩面漆喷涂一遍，干后则为大理石效果。 
所述喷枪口径2.0毫米、压力1Mpa。 
与现有技术相比，本发明水性氟碳仿大理石外墙涂料的实施可取得如下优越效果：它保持了天然大理石相同的装饰效果，同时又保持整体色彩一致、节能、环保、施工方便及容易翻新的特点，目前可以完全取代天然大理石在外墙中的应用，大约可节省三分之二的成本。 
水性氟碳仿大理石外墙涂料喷涂形成的漆膜表面平滑、光亮，纹路均匀清晰，表面再喷涂水性氟碳罩光清漆作保护，增加光亮度、硬度和质感效果，外观酷似天然石材。同时也区别于传统水油两相的多彩涂料，水油两相的多彩涂料有洒点小和残余有机溶剂等不足，因此水性氟碳仿大理石外墙涂料具有广阔的市场前景。 
下面结合具体实施例，进一步详述本发明的技术方案： 
本发明水性氟碳仿大理石外墙涂料-白漆的组分及其重量份数包括： 
水35～40份 
纤维素0.1～1份 
纳米硅酸盐0.1～1份 
羧酸胺盐分散剂0.1～1份 
PH调节剂0.1～1份 
消泡剂0.1～1份 
防冻剂1.0～2.0份 
成膜剂1.0～2.0份 
防腐防霉剂1.0～2.5份 
金红石钛白10～12份 
碳酸钙20～25份 
具体实施方式：
硫酸钡2.0～5.0份 
水性氟碳乳液12～20份 
其中：所说的水可以采用自来水； 
所说的纤维素可以采用美国亚夸龙H10K； 
所说的纳米硅酸盐可以采用美国洛克伍德RD； 
所说的羧酸胺盐分散剂可采用美国罗门哈斯1124； 
所说的PH调节剂2-氨基-2-甲基丙醇可采用台湾德谦MA-95； 
所说的消泡剂可采用英国布莱克苯245、246； 
所说的防冻剂丙二醇可采用江苏华纶化工； 
所说的成膜剂可采用美国伊士曼Texanol； 
所说的防腐防霉剂可采用美国罗门哈斯Lxe，361； 
所说的金红石钛白可采用美国杜邦化工R706； 
所说的碳酸钙可采用江西永丰CC800； 
所说的硫酸钡可采用广西桂华2500目； 
所说的水性氟碳乳液可采用台湾长兴4311A。 
本发明的制备方法包括如下步骤： 
在容器中依次加入水、纤维素、纳米硅酸盐、羧酸胺盐分散剂，中速800转/分钟边加边搅，溶解30分钟；再依次加入PH调节剂、消泡剂、防冻剂、成膜剂、防腐防霉剂，中速800转/分钟搅匀；再依次加入金红石钛白、碳酸钙、硫酸钡，用高速2000转/分钟，分散达细度45微米，转低速400转/分钟加入水性氟碳乳液搅匀10钟，备用。 
选取一种大理石效果(白底间杂灰、红、黄色)为例： 
色漆准备： 
(1)灰色漆：用制备好的白漆130克加1.3克芬兰CPS炭黑色浆搅匀. 
(2)红色漆：用制备好的白漆160克加9.0克芬兰CPS外墙红浆搅匀. 
(3)黄色漆：用制备好的白漆190克加14.0克芬兰CPS外墙黄浆搅匀. 
大理石效果涂料制备： 
Figure DEST_PATH_GSB00000540124600051
将水、焦磷酸钠、纳米硅酸盐依次加容器，中速800转/分钟搅匀30分钟， 再转低速400转/分钟，依次加入白漆、红色漆、灰色漆、黄色漆，搅拌20分钟，即为仿大理石漆。用压力式喷枪——口径2.0毫米、压力1Mpa，均匀喷涂一遍，干后用一水性氟碳罩面漆喷涂一遍，干后则为大理石效果。 
水性氟碳仿大理石外墙涂料技术性能及实测值(参照GB/T9755-2001)： 
水性氟碳仿大理石外墙涂料安全性能及实测值(参照GB18582-2001)： 
上述结果表明，本发明的水性氟碳仿大理石外墙涂料喷涂技术指标完全优于国家标准，符合环保标准。 

Claims (5)

1.一种水性氟碳仿大理石外墙涂料，所述涂料包含以下重量份的组份：
Figure FSB00000561007400011
所述白漆包含如下以重量份表示的组分：
所述灰色漆是用制备好的白漆130克加1.3克芬兰CPS炭黑色浆搅匀而成；所述红色漆是用制备好的白漆160克加9.0克芬兰CPS外墙红浆搅匀而成；所述黄色漆是用制备好的白漆190克加14.0克芬兰CPS外墙黄浆搅匀而成。
2.按照权利要求1所述的水性氟碳仿大理石外墙涂料，其特征是：所述白漆还包含1.0～2.0重量份的防冻剂。
3.按照权利要求1所述的水性氟碳仿大理石外墙涂料，其特征是：所述分散剂选用羧酸胺盐。
4.按照权利要求1所述的水性氟碳仿大理石外墙涂料，其特征是：所述钛白粉选用金红石钛白。
5.一种如权利要求2所述的水性氟碳仿大理石外墙涂料的制备方法，其特征是：该方法包括如下步骤：
a.在容器中依次加入水、纤维素、纳米硅酸盐、分散剂，中速800转/分钟边加边搅，溶解30分钟；
b.再依次加入PH调节剂、消泡剂、防冻剂、成膜剂、防腐防霉剂，中速800转/分钟搅匀；
c.再依次加入钛白粉、碳酸钙、硫酸钡，用高速2000转/分钟，分散达细度45微米，转低速400转/分钟加入水性氟碳乳液搅匀10钟，得到白漆，备用；
d.用制备好的白漆130克加1.3克芬兰CPS炭黑色浆搅匀制得灰色漆；
e.用制备好的白漆160克加9.0克芬兰CPS外墙红浆搅匀制得红色漆；
f.用制备好的白漆190克加14.0克芬兰CPS外墙黄浆搅匀制得黄色漆；
g.取自来水60份、焦磷酸钠0.05份、纳米硅酸盐2.0份、备用白漆23.95份、备用红色漆5份、备用灰色漆7份和备用黄色漆2份，将水、焦磷酸钠、纳米硅酸盐依次加容器，中速800转/分钟搅匀30分钟，再转低速400转/分钟，依次加入白漆、红色漆、灰色漆、黄色漆，搅拌20分钟，即为水性氟碳仿大理石外墙涂料。
CN2008101419835A 2008-08-22 2008-08-22 水性氟碳仿大理石涂料及其制备方法和仿大理石效果喷涂方法 Active CN101654578B (zh)