CN101121841A - 新型水性外墙氟碳涂料及其制备方法 - Google Patents
新型水性外墙氟碳涂料及其制备方法 Download PDFInfo
- Publication number
- CN101121841A CN101121841A CNA2007101321071A CN200710132107A CN101121841A CN 101121841 A CN101121841 A CN 101121841A CN A2007101321071 A CNA2007101321071 A CN A2007101321071A CN 200710132107 A CN200710132107 A CN 200710132107A CN 101121841 A CN101121841 A CN 101121841A
- Authority
- CN
- China
- Prior art keywords
- agent
- water
- percent
- covers
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的新型水性外墙氟碳涂料是由溶剂(水)、水性氟碳乳液、填料、复合成膜助剂、分散剂、润湿剂、流平剂、增稠剂、杀菌剂研制而成。其中各组分在涂料中的加入量为:溶剂(水)为5.%~15%,水性氟碳乳液为40%-70%,复合成膜助剂为5%-14%,金红石钛白粉10%~25%,滑石粉5%~10%,分散剂为.0.1%~0.5%,润湿剂为.0.001%~0.003%,流平剂为.0.004%~0.01%,杀菌剂为.0.1%~0.4%,增稠剂为.1%~1.8%,消泡剂为0.01%-0.05%。本发明采用改变填料和增加复合成膜助剂的用量来成功研制了新型水性外墙氟碳涂料,制备工艺简单,使用后不开裂、不起泡、不泛白,表面光滑,保光保色,柔韧性好,耐候性、耐腐蚀性、耐热耐寒性、耐酸碱性及成膜效果更好,无污染,成本低,施工方便,有着很好的发展前景。
Description
技术领域
本发明涉及建筑外墙涂料领域,特别涉及一种新型水性外墙氟碳涂料,进一步还涉及这种新型水性外墙氟碳涂料的制备方法。
技术背景
水性外墙氟碳涂料是一种以含氟碳树脂乳液为主要成膜物的新型涂料,具有极高的耐候性、耐腐蚀性、耐热耐寒性、耐酸碱性等优点,受到建筑装饰业界的极大关注与青睐,也成为涂料科技工作者研究的热点课题。近年来在中国建筑外墙上的使用取得了相当大的突破。但是在水性氟碳外墙涂料使用中,仍然存在开裂、起泡、泛白等方面的一些不足问题一直以来未能得到解决。
本发明采用改变填料和增加复合成膜助剂的用量来研制水性外墙氟碳涂料,这种方法在中国专利网和现有期刊的检索文献中尚未见报道。
发明内容
技术问题为了解决上述的水性外墙氟碳涂料存在的不足,提高水性外墙氟碳涂料的综合性能,本发明的目的是提供一种新型水性外墙氟碳涂料及制备方法。
技术方案为了达到上述目的,本发明的一种新型水性外墙氟碳涂料,其配方由溶剂(水)、水性氟碳乳液、填料、复合成膜助剂、分散剂、润湿剂、流平剂、增稠剂、杀菌剂研制而成。
其中溶剂(水)在涂料中的加入量为5.%~15%,水性氟碳乳液在涂料中的加入量为40%-70%,复合成膜助剂在涂料中的加入量为5%-14%,金红石钛白粉在涂料中的10%~25%,滑石粉在涂料中的5%~10%,分散剂在涂料中的加入量为.0.1%~0.5%,润湿剂在涂料中的加入量为.0.001%~0.003%,流平剂在涂料中的加入量为.0.004%~0.01%,杀菌剂在涂料中的加入量为.0.1%~0.4%,增稠剂在涂料中的加入量为.1%~1.8%,消泡剂在涂料中的加入量为0.01%-0.05%。
其中,水性氟碳乳液的选择,是决定氟碳涂料性能最关键的因素,水性外墙氟碳涂料具有超常的耐候性、耐水性、耐酸碱性与水性氟碳乳液的含氟量有关,氟含量越高,制备的涂料耐老化性、耐化学稳定性的耐久性越长,当氟含量小于15%时,其涂料性能急剧下降,将国内几种水性氟碳乳液的含氟量及主要性能测试比较见表1。
表1国内几种水性氟碳乳液的含氟量及主要性能比较
品种 | JF-2X | JF-3X | CHSF-30 |
含氟量/%耐碱性(5%Ca(OH)2)耐擦洗性/次耐人工老化(h) | 20.5360h250002500h | 21.0370h300002800 | 23.0480h400003500 |
根据表1对比可知,GHSF-30的性能较好,本发明选择GHSF-30作为涂料的主要成膜物。
为了达到上述目的,本发明的另一方案是提供一种新型水性外墙氟碳涂料的制备方法。
先将溶剂(水)、水性氟碳乳液、填料、复合成膜助剂、分散剂、润湿剂、流平剂、增稠剂、杀菌剂按一定重量比例混合,搅拌分散30-40min,然后加入消泡剂及润湿剂,搅拌分散20min,最后用砂磨机研磨,过滤,装桶包装。
有益效果从下面的表2可以看出,产品在耐水性、耐碱性、耐盐性、耐擦洗刷性、耐人工老化性等方面有超常特殊的性能,主要原因与水性氟碳乳液的含氟量直接相关,无开裂,不起泡,不泛白其主要原因是与填料的品种和复合成膜助剂的用量有关。
表2水性外墙氟碳涂料性能检测结果
项目 | 技术指标 | 检测结果 |
容器中的状态施工性低温稳定性干燥时间/h涂膜外观对比率(白色和浅色)耐水性/h耐碱性/h耐盐雾性/h耐洗刷性/次耐人工老化性/h耐温变性(10次循环) | 搅拌后无硬块,呈均匀状态刷涂二道无障碍不变质≤2正常≥0.9396无异常48无异常1000≥2000600不起泡,不剥落,无裂纹无异常 | 合格合格合格≤1表面光滑,合格≥0.95580无异常580无异常3500≥500004000合格 |
本发明的主要优点是:耐水性、耐碱性、耐人工老化、耐洗刷性均有明显提高,无开裂、不起泡、不泛白等优点,克服了水性氟碳外墙涂料存在开裂、起泡、泛白等方面的一些不足问题。产品性能居国内领先水平。具有一定的社会效益、经济效益和科学价值。在生产过程中无污染,是一项投资少、见效快值得推广的项目,有着很好的发展前景。
具体实施方式
本发明的一种新型水性外墙氟碳涂料的实施例1至实施例6的组分:水(A)、水性氟碳乳液(B)、金红石钛白粉(C)、滑石粉(D)、复合成膜助剂(E)、分散剂(F)、流平剂(G)、增稠剂(H)、润湿剂(I)、杀菌剂(J)、消泡剂(K)、耐人工老化性/h(L)、耐洗刷性/次(M)、耐水性/h(N)、耐碱性/h(O)的配比分别按表3中的配比制备而成。
表3新型水性外墙氟碳涂料研制实例
A% | B% | C% | D% | E% | F% | G% | H% | I% | J% | K% | L | M | |
例1例2例3例4例5例6 | 5.01514117.06.0 | 704050555760 | 132510151722 | 5.06.0108.07.05.0 | 5.012149.0105.0 | 0.50.10.20.30.10.2 | 0.010.0010.010.0040.0030.002 | 1.0371.7881.4681.4641.7861.676 | 0.0030.0010.0020.0020.0010.002 | 0.40.10.30.20.10.1 | 0.050.010.020.030.010.02 | 360031003300350038004000 | 400002800035000400004500050000 |
N、0均为580h。
实施例1至实施例6的制备过程均为:先将溶剂(水)、水性氟碳乳液、填料、复合成膜助剂、分散剂、润湿剂、流平剂、增稠剂、杀菌剂按一定重量比例混合,搅拌分散30-40min,然后加入消泡剂及润湿剂,搅拌分散20min,最后用砂磨机研磨,过滤,装桶包装。
Claims (3)
1.新型水性外墙氟碳涂料,其特征是,该涂料由如下组分和含量(按质量百分比)混合组成:
溶剂(水) 5.%~15%,
水性氟碳乳液 40%-70%,
复合成膜助剂 5%-14%,
金红石钛白粉 10%~25%,
滑石粉 5%~10%,
分散剂 0.1%~0.5%,
润湿剂 0.001%~0.003%,
流平剂 0.004%~0.01%,
杀菌剂 0.1%~0.4%,
增稠剂 1%~1.8%,
消泡剂 0.01%-0.05%。
2.根据权利要求1所述的新型水性外墙氟碳涂料,其特征是,所述的水性氟碳乳液为GHSF-30氟碳乳液;所述的复合成膜助剂为乙二醇、乙二醇醚和醇脂十二;所述的分散剂为4560分散剂;所述的流平剂为2#;所述的增稠剂为PU;所述的润湿剂为PE-100;所述的杀菌剂为LXE; 所述的消泡剂为CF-246。
3.制备权利要求1新型水性外墙氟碳涂料的方法,其方法包括下列步骤:
(1)将水、水性氟碳乳液、填料及混合成膜助剂按比例混合,高速搅拌均匀;
(2)依次加入各种助剂、高速搅拌分散均匀;
(3)用砂磨机研磨,过滤,装桶包装。