CN101497532A - 一种自抗裂建筑围护用发泡乳胶水泥节能材料 - Google Patents

一种自抗裂建筑围护用发泡乳胶水泥节能材料 Download PDF

Info

Publication number
CN101497532A
CN101497532A CNA2008100468285A CN200810046828A CN101497532A CN 101497532 A CN101497532 A CN 101497532A CN A2008100468285 A CNA2008100468285 A CN A2008100468285A CN 200810046828 A CN200810046828 A CN 200810046828A CN 101497532 A CN101497532 A CN 101497532A
Authority
CN
China
Prior art keywords
energy
market sale
cracking
building enclosure
whipping agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008100468285A
Other languages
English (en)
Inventor
饶俊明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUHAN WALLPRO TECHNOLOGY Co Ltd
Original Assignee
WUHAN WALLPRO TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUHAN WALLPRO TECHNOLOGY Co Ltd filed Critical WUHAN WALLPRO TECHNOLOGY Co Ltd
Priority to CNA2008100468285A priority Critical patent/CN101497532A/zh
Publication of CN101497532A publication Critical patent/CN101497532A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种建筑材料，尤其是自抗裂建筑围护用发泡乳胶水泥节能材料；本发明提出了的自抗裂建筑围护用发泡乳胶水泥节能材料，该材料将低导热系数的空气(导热系数0.023)有效的封闭在系统中，轻质隔热材料一起，形成节能效果显著建筑材料，同时在系统中用弹性乳胶改善无机胶凝材料的脆性，从而获得吸水率低，安全性高，自抗裂，无须专门的抗裂保护层，施工工艺简单，系统强度高，工期短，综合造价低的新材料，有效的解决了传统建筑节能材料系统需要特别的抗裂保护层施工工艺复杂，吸水率高，系统安全性差，工期长，造价高等弊病。

Description

一种自抗裂建筑围护用发泡乳胶水泥节能材料
技术领域：
本发明涉及一种节能材料，尤其是涉及一种自抗裂建筑围护用发泡乳胶水泥节能材料.
技术背景：
我国建筑能耗占全国能耗30％，而且，随着经济的不断发展，建筑能耗的比重会进一步增加，因此，建筑节能意义重大，国家立法推广.建筑围护节能的产品和技术，国内外有大量的研究，其中EPS、XPX保温系统、胶粉聚苯颗粒保温系统、中空玻化微珠保温系统、闭孔珍珠岩保温系统、发泡水泥保温系统是我国目前的建筑围护节能比较常用的建筑节能体系；上述节能系统节能效果好，但普遍存在制品强度低，稳定性差，施工复杂，需要专门的抗裂加强层，施工周期长，成本高等弊端.如何生产出节能效果好，同时制品安全性高，稳定性好，施工简便，无需专门的抗裂层，施工周期短，成本底的节能系统材料，是建筑节能的一个难题.
发明内容：
针对现有产品和技术中存在的上述问题，本发明的目的是提出一个新的产品方案，以解决现有产品中存在的问题.
本发明的方案是这样实现的：本发明的一种自抗裂建筑围护用发泡乳胶节能材料，是按常规方法制备的，它包括发泡剂、弹性乳胶、无机胶凝材料、混凝土外加剂、骨料、轻质隔热材料、纤维材料组成和水组成，各组分的重量百分比是：
发泡剂          0.1-1％
弹性乳胶        1-20％
无机胶凝材料    20-80％
混凝土外加剂    0.1-1％
骨料            35-60％
轻质隔热材料    2-50％
纤维材料        0.01-0.8％
水              2-30％
采用本发明材料，不仅解决了传统产品高强度高导热系数的矛盾，同时也解决了传统材料需要专门抗裂防护的施工难题，使用本发明产品施工，跟传统墙体抹批水泥砂浆一样方便快捷，大幅度缩短了施工工期和降低了施工成本.
下面通过实施例对本发明做进一步的说明，但本发明不限于这些例子.
本发明所指的发泡剂：阴离子表面活性剂、植物蛋白发泡剂、动物蛋白发泡剂、松香皂类发泡剂；
本发明所指的弹性乳胶：苯丙乳液，纯丙乳液，硅丙乳液，VAE乳液；
本发明所指的无机胶凝材料：普通硅酸盐水泥、复合硅酸盐水泥、膨胀硅酸盐水泥、白色硅酸盐水泥、石膏、CaO、MgO；早强剂、减水剂、防冻剂、微膨胀剂；
本发明所指的混凝土外加剂：
本发明所指的骨料：石英砂，天然石粉，煅烧陶土颗粒，微硅粉，粉煤灰
本发明所指的轻质隔热材料：漂珠、中空玻化微珠、闭孔珍珠岩、膨胀珍珠岩、膨胀蛭石、EPS颗粒、硅酸铝棉、海泡石
本发明所指的纤维材料：聚丙烯纤维、木质纤维、矿物纤维、植物纤维
本发明所指的水是常用的自来水.
本发明所指的发泡剂可以分别使用或相互代用；发明所指的弹性乳胶可以分别使用或相互代用；本发明所指的无机胶凝材料可以分别使用或相互代用；本发明所指的骨料可以分别使用或相互代用；本发明所指的轻质隔热材料可以分别使用或相互代用；本发明所指的纤维材料可以分别使用或相互代用.
本发明所指的发泡剂、弹性乳胶、无机胶凝材料、骨料、轻质隔热材料、纤维材料都是常用的化工原料或建筑材料，并有商品销售.
本发明的生产工艺如下：
1.所需原料准确称量备用；
2.将发泡剂发泡备用；
3.将无机胶凝材料、骨料、轻质隔热材料、纤维材料、弹性乳胶、水在搅拌机中预混合
4.将所发的泡沫倒入搅拌机中混合均匀；
5.将搅拌均匀的浆料均匀的批抹于墙体，干燥后及形成自抗裂建筑围护用发泡乳胶水泥节能材料
实施例一：
动物蛋白发泡剂        2千克
苯丙弹性乳液          10千克
水泥                  100千克
聚羧酸盐减水剂        0.2千克
中砂                  120千克
玻化微珠              50千克
漂珠                  15千克
PP纤维                0.02千克
水                    30千克
实施例二：
动物蛋白发泡剂        3千克
苯丙弹性乳液         15千克
水泥                 150千克
聚羧酸盐减水剂        0.3千克
中砂                 100千克
硅微粉               50千克
微膨胀剂             15千克
漂珠                 150千克
PP纤维               2千克
玄武岩纤维           1千克
水                   80千克
实施例三：
动物蛋白发泡剂       2千克
苯丙弹性乳液         10千克
水泥                 100千克
聚羧酸盐减水剂       0.2千克
中砂                 130千克
微硅粉               15千克
粉煤灰               50千克
玻化微珠             100千克
PP纤维               0.02千克
水                   22千克。

Claims (9)

1.一种自抗裂建筑围护用发泡乳胶节能材料，是按常规方法制备的，它包括发泡剂、弹性乳胶、无机胶凝材料、骨料、轻质隔热材料、纤维材料和水组成.
2 一种建筑围护用发泡保温材料，其特征是所述材料的由以下组成(重量百分比)：
发泡剂               0.1-1％
弹性乳胶             1-20％
无机胶凝材料         20-80％
混凝土外加剂         0.1-1％
骨料                 35-60％
轻质隔热材料         2-50％
纤维材料             0.05-0.8％
水                   2-30％
3.根据权利要求2所述的发泡剂，是市场销售阴离子表面活性剂、植物性发泡剂、动物性发泡剂、松香类发泡剂的一种或几种；
4.根据权利要求2所述的弹性乳胶是市场销售的丙烯酸类高分子聚合物中的一种或几种；
5.根据权利要求2所述的无机胶凝材料是市场销售的普通硅酸盐水泥、复合硅酸盐水泥、膨胀硅酸盐水泥、白色硅酸盐水泥、石膏、CaO、MgO中的一种或者几种；
6.根据权利要求2所述的混凝土外加剂，是市场销售的早强剂、减水剂、防冻剂、微膨胀剂中的一种或几种；
7.根据权利要求2所述的骨料是市场销售的石英砂、河砂、天然石粉、烧结陶土颗粒、微硅粉、粉煤灰中的一种或者几种；
8.根据权利要求2所述的轻质隔热材料是市场销售的漂珠、中空玻化微珠、闭孔珍珠岩、膨胀珍珠岩、膨胀蛭石、EPS颗粒、硅酸铝棉、海泡石中的—种或几种；
9.根据权利要求2所述的纤维材料是市场销售的聚丙烯纤维、木质纤维、矿物纤维、植物纤维中的一种或几种。
CNA2008100468285A 2008-01-30 2008-01-30 一种自抗裂建筑围护用发泡乳胶水泥节能材料 Pending CN101497532A (zh)