CN105330215A - 一种保温砂浆的制备方法 - Google Patents

一种保温砂浆的制备方法 Download PDF

Info

Publication number
CN105330215A
CN105330215A CN201510694405.4A CN201510694405A CN105330215A CN 105330215 A CN105330215 A CN 105330215A CN 201510694405 A CN201510694405 A CN 201510694405A CN 105330215 A CN105330215 A CN 105330215A
Authority
CN
China
Prior art keywords
parts
thermal insulation
cement
mortar
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510694405.4A
Other languages
English (en)
Inventor
刘元正
陈雪梅
钟华
李涛
王海军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WEIFANG DELIN BUILDING MATERIAL Co Ltd
Original Assignee
WEIFANG DELIN BUILDING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WEIFANG DELIN BUILDING MATERIAL Co Ltd filed Critical WEIFANG DELIN BUILDING MATERIAL Co Ltd
Priority to CN201510694405.4A priority Critical patent/CN105330215A/zh
Publication of CN105330215A publication Critical patent/CN105330215A/zh
Pending legal-status Critical Current

Abstract

一种保温砂浆的制备方法，其特征和组成的重量配比包括：水泥:500~1000份，矿粉：0~200份，粉煤灰：0~150份，滑石粉0~100份，重钙粉0~100份，硅灰：0~50份，膨胀剂：0~100份，早强剂：0~1份，PP纤维：0~2份，木质纤维0~2份，乳胶粉：0~30份，纤维素醚：0.5~8份，憎水剂：0~3份，引气剂：0.001~0.2份，减水剂：1~4份，淀粉醚0~2份，缓凝剂：0~2份，轻质颗粒：2~500份，水：400~1000份。保温砂浆具有良好的流动性及流动性保持，包裹性好，耐久性好，强度高，本发明的产品可作为干混砂浆生产，也可使用湿拌砂浆生产线、混凝土搅拌站生产湿拌砂浆，利用罐车运输至工地使用，符合现阶段节能减排、防止粉尘的环保要求；并且可塑性好，可用于外墙保温、室内隔墙、屋顶等，适用范围广，成本低廉。

Description

一种保温砂浆的制备方法
技术领域
[0001] 本发明涉及一种大流动性保温砂浆的制备方法，属于建筑材料设计领域。
背景技术
[0002] 随着全球性的的能源危机，世界各国对保护环境和节约能源的要求日渐提高。1979年，在维也纳联合国召开的科学技术促进发展的研讨会上，将能源问题和人口问题、粮食问题、环境问题一同列为目前人类所面临的四大主要问题。与此同时，世界各国也相继提出了要控制矿物质能源的用量，开发新能源与利用可再生能源，提高用能效率，从而使环境得到保护、能源能够得到有效利用。
[0003] 建筑作为一种高能耗的行业，则备受瞩目，它已成为近年来世界各国建筑行业发展的一个基本趋势。由于建筑能耗的比重不断增大，则需要我们提倡一种对人类健康生活有利、有效降低能耗并能提高用能率的建筑节能，由此形成一种降低建筑业能耗的大形势。
[0004] 墙体保温分为墙体外保温、墙体内保温、墙体自保温三种，墙体内保温由于难以施工，并且占用室内使用面积，现在使用很少；墙体外保温通常使用保温砂浆、保温板、保温装饰一体板等，其保温隔热性能受保温层厚度的限制，不可能做到太高；墙体自保温现阶段使用还不是很成熟，使用自保温砌块在砌块之间会有冷桥热桥存在，并且从预制砌块到砌成墙体，其可塑性较差；现阶段使用很有限，但其保温性能较好，比较容易达到65%的节能要求。因此，制备一种大流动性可浇筑的墙体自保温材料，克服现有自保温系统施工较慢、具有冷热桥、可塑性差的缺点，具有很高的工程应用价值。
发明内容
[0005] 本发明的目的旨在克服现有技术中的不足，提出一种保温砂浆的制备方法。制备的保温砂浆具有流动性及流动性保持好的特点，栗送浇筑施工效率高，浇筑的墙体具有自保温的功能，无传统自保温砌块接缝的冷热桥现象。
[0006] 本发明的内容是:一种保温砂浆的制备方法，其特征和组成的重量配比包括:水泥:500-1000份，矿粉:0~200份，粉煤灰:0~150份，滑石粉0-100份，重钙粉0-100份，硅灰:0~50份，膨胀剂:0~100份，早强剂:0~1份，PP纤维:0~2份，木质纤维0-2份，乳胶粉:0-30份，纤维素醚:0.5-8份，憎水剂:0~3份，引气剂:0.001-0.2份，减水剂:1-4份，淀粉醚0~2份，缓凝剂:0~2份，轻质颗粒:2~500份，水:400~1000份。
[0007] 本发明的内容中:所述的水泥为硅酸盐水泥，普通硅酸盐水泥，矿渣水泥、火山灰水泥中的一种；所述的矿粉为S95、S105级矿粉，比表面积大于400m2/Kg ;所述的粉煤灰为I级粉煤灰。
[0008] 本发明的内容中:所述的滑石粉细度为600~1000目；所述的重钙粉细度为600-1500目；所述的硅灰比表面积为15~27m2/g;所述的膨胀剂为钙矾石类、方镁石类、II
型硬石膏类、复合膨胀剂中的一种。
[0009] 本发明的内容中:所述的早强剂为碳酸锂、甲酸钙、硝酸钠等非硫酸盐、氯盐早强剂中的一种；所述的PP纤维为直径彡0.02mm，长度彡5mm的PP纤维；所述的可再分散乳胶粉为醋酸乙烯酯一乙烯共聚乳胶粉，固含多98%，细度0.5〜8 μπι;所述的纤维素醚为羟乙基一甲基纤维素醚(HEMC)或羟丙基一甲基纤维素醚(HPMC)。
[0010] 本发明的内容中:所述憎水剂为有机硅憎水剂、硬酯酸钙憎水剂、改性硬脂酸钙憎水剂中的一种；所述的引气剂为十二烷基苯磺酸钠或松香引气剂；所述的减水剂为萘系减水剂、氨基磺酸盐减水剂、脂肪族减水剂、聚羧酸减水剂中的一种，减水率15%~35% ;所述的淀粉醚为羟烷基淀粉、羧甲基淀粉、阳离子淀粉中的一种；所述的缓凝剂为葡萄糖酸钠、柠檬酸钠、酒石酸、糖、糖蜜中的一种。
[0011] 本发明的内容中:所述的轻质颗粒为聚苯颗粒、玻化微珠、膨胀珍珠岩中的一种。
[0012] 本发明所测试的流动性参照GB/T50448-2008《水泥基灌浆材料应用技术规范》测定。
[0013] 与现有技术相比，本发明具有下列特点和有益效果:
1、保温砂浆具有良好的流动性及流动性保持，流动性为200~320mm，能够使用砂浆栗、混凝土栗进行输送，浇筑后能够良好的填充墙体，可操作时间长，施工方便，效率高。
[0014] 2、保温砂浆的导热系数可根据需要加入适量的轻质颗粒进行调整，容重在200Kg/m3~1000Kg/m3之间，很容易达到65%及以上的节能要求。
[0015] 3、保温砂浆的包裹性好，对不同比例的轻质骨料均能表现出良好的包裹性及流动性，在栗送和运输过程中不容易发生轻质颗粒上浮的现象，浇筑后为匀质的砂浆。
[0016] 4、保温砂浆使用的水泥基材料本身强度高、耐久性好，浆体包裹轻质颗粒后形成的闭孔结构阻止有害组分侵入，添加憎水剂后表面的憎水性提高了防水性能，浇筑的墙体与建筑物同寿命。
[0017] 5、适用范围广，成本低廉；本发明的产品可作为干混砂浆生产，也可使用湿拌砂浆生产线、混凝土搅拌站生产湿拌砂浆，利用罐车运输至工地使用，符合现阶段节能减排、防止粉尘的环保要求；并且可塑性好，可用于外墙保温、室内隔墙、屋顶等。
具体实施方式
[0018] 下面给出的实施例拟以对本发明作进一步说明，但不能理解为是对本发明保护范围的限制，该领域的技术人员根据上述本发明的内容对本发明作出的一些非本质的改进和调整，仍属于本发明的保护范围。
[0019] 实施例1
保温砂浆，其组成为:水泥:800份，矿粉:100份，粉煤灰:100份，重钙粉50份，膨胀剂:50份，早强剂:0.5份，纤维素醚'2份，憎水剂:1份，引气剂:0.005份，减水剂:1份，聚苯颗粒:6份，水:600份。
[0020] 将上述原材料中浆体(除去轻质颗粒)搅拌均匀，然后添加轻质颗粒拌合均匀即可制备保温砂浆。
[0021 ] 所制得的保温砂浆流动度为220mm，容重为540Kg/m3，抗压强度为4.0MPa。
[0022] 实施例2
保温砂浆，其组成为:水泥:550份，矿粉:200份，粉煤灰:100份，滑石粉50份，重钙粉50份，膨胀剂:60份，早强剂:1份，纤维素醚:0.5份，憎水剂:1份，引气剂:0.05份，减水剂:2份，缓凝剂:0.5份，聚苯颗粒:4份，水:500份。
[0023] 将上述原材料中浆体(除去轻质颗粒)搅拌均匀，然后添加轻质颗粒拌合均匀即可制备保温砂浆。
[0024] 所制得的保温砂浆流动度为280mm，容重为720Kg/m3，抗压强度为7.9MPa。
[0025] 实施例3
保温砂浆，其组成为:水泥:900份，滑石粉100份，重钙粉50份，硅灰:50份，膨胀剂:80份，早强剂:1份，纤维素醚:1份，憎水剂'2份，减水剂'2份，缓凝剂:0.5份，聚苯颗粒:4份，水:450份。
[0026] 将上述原材料中浆体(除去轻质颗粒)搅拌均匀，然后添加轻质颗粒拌合均匀即可制备保温砂浆。
[0027] 所制得的保温砂浆流动度为210mm，容重为780Kg/m3，抗压强度为10.5MPa。
[0028] 实施例4
保温砂浆，其组成为:水泥:600份，矿粉:200份，粉煤灰:100份，重钙粉50份，膨胀剂:60份，早强剂:1份，木质纤维1份，纤维素醚:1份，引气剂:0.05份，减水剂'2份，缓凝剂:1份，膨胀珍珠岩:200份，水:650份。
[0029] 将上述原材料中浆体(除去轻质颗粒)搅拌均匀，然后添加轻质颗粒拌合均匀即可制备保温砂浆。
[0030] 所制得的保温砂浆流动度为300mm，容重为480Kg/m3，抗压强度为3.2MPa。
[0031] 实施例5
保温砂浆，其组成为:水泥:800份，矿粉:100份，粉煤灰:滑石粉50份，重钙粉100份，膨胀剂:60份，早强剂:1份，PP纤维:0.5份，乳胶粉:10份，纤维素醚:1份，憎水剂'2份，引气剂:0.005份，减水剂:3份，淀粉醚0.5份，缓凝剂:1份，玻化微珠:300份，水:450份。
[0032] 将上述原材料中浆体(除去轻质颗粒)搅拌均匀，然后添加轻质颗粒拌合均匀即可制备保温砂浆。
[0033] 所制得的保温砂浆流动度为300mm，容重为810Kg/m3，抗压强度为12.0MPa。
[0034] 实施例6
保温砂浆，其组成为:水泥:700份，矿粉:200份，粉煤灰:100份，重钙粉50份，膨胀剂:50份，早强剂:1份，乳胶粉:20份，纤维素醚'2份，憎水剂:2份，引气剂:0.1份，减水剂:3份，淀粉醚1份，缓凝剂:0.5份，聚苯颗粒:10份，水:800份。
[0035] 将上述原材料中浆体(除去轻质颗粒)搅拌均匀，然后添加轻质颗粒拌合均匀即可制备保温砂浆。
[0036] 所制得的保温砂浆流动度为220mm，容重为270Kg/m3，抗压强度为0.5MPa。
[0037] 实施例7
保温砂浆，其组成为:水泥:700份，矿粉:200份，粉煤灰:100份，重钙粉50份，膨胀剂:50份，早强剂:1份，乳胶粉:20份，纤维素醚'2份，憎水剂:2份，引气剂:0.1份，减水剂:3份，淀粉醚1份，缓凝剂:0.5份，聚苯颗粒:12份，水:800份
将上述原材料中浆体(除去轻质颗粒)搅拌均匀，然后添加轻质颗粒拌合均匀即可制备保温砂浆。
[0038] 所制得的保温砂浆流动度为200mm，容重为210Kg/m3，抗压强度为0.3MPa。
[0039] 实施例8
保温砂浆，其组成为:水泥:650份，矿粉:200份，粉煤灰:100份，滑石粉50份，重钙粉100份，石圭灰:50份，膨胀剂:60份，早强剂:1份，乳胶粉:0~30份，纤维素醚:0.5份，憎水剂:2份，引气剂:0.05份，减水剂:3份，缓凝剂:0~2份，玻化微珠:200份，水:400份。
[0040] 将上述原材料中浆体(除去轻质颗粒)搅拌均匀，然后添加轻质颗粒拌合均匀即可制备保温砂浆。
[0041] 所制得的保温砂浆流动度为310mm，容重为930Kg/m3，抗压强度为15.5MPa。
[0042] 上述实施例中:所述的水泥为娃酸盐水泥，普通娃酸盐水泥，矿渣水泥、火山灰水泥中的一种；所述的矿粉为S95、S105级矿粉，比表面积大于400m2/Kg ;所述的粉煤灰为I级粉煤灰。
[0043] 上述实施例中:所述的滑石粉细度为600~1000目；所述的重钙粉细度为600~1500目；所述的硅灰比表面积为15~27m2/g ;所述的膨胀剂为钙矾石类、方镁石类、II型硬石膏类、复合膨胀剂中的一种。
[0044] 上述实施例中:所述的早强剂为碳酸锂、甲酸钙、硝酸钠等非硫酸盐、氯盐早强剂中的一种；所述的PP纤维为直径彡0.02mm,长度彡5mm的PP纤维；所述的可再分散乳胶粉为醋酸乙烯酯一乙烯共聚乳胶粉，固含多98%，细度0.5〜8 μπι;所述的纤维素醚为羟乙基一甲基纤维素醚(HEMC)或羟丙基一甲基纤维素醚(HPMC)。
[0045] 上述实施例中:所述憎水剂为有机硅憎水剂、硬酯酸钙憎水剂、改性硬脂酸钙憎水剂中的一种；所述的引气剂为十二烷基苯磺酸钠或松香引气剂；所述的减水剂为萘系减水剂、氨基磺酸盐减水剂、脂肪族减水剂、聚羧酸减水剂中的一种，减水率15%~35% ;所述的淀粉醚为羟烷基淀粉、羧甲基淀粉、阳离子淀粉中的一种；所述的缓凝剂为葡萄糖酸钠、柠檬酸钠、酒石酸、糖、糖蜜中的一种。
[0046] 上述实施例中:所述的轻质颗粒为聚苯颗粒、玻化微珠、膨胀珍珠岩中的一种。
[0047] 本发明所测试的流动性参照GB/T50448-2008《水泥基灌浆材料应用技术规范》测定。
[0048] 本发明不限于上述实施例，本发明内容所述均可实施并具有所述良好效果。

Claims (6)

1.一种保温砂浆的制备方法，其特征和组成的重量配比包括••水泥:500~1000份，矿粉:0~200份，粉煤灰:0~150份，滑石粉0~100份，重钙粉0~100份，硅灰:0~50份，膨胀剂:0-100份，早强剂:0~1份，PP纤维:0~2份，木质纤维0-2份，乳胶粉:0~30份，纤维素醚:0.5-8份，憎水剂:0~3份，引气剂:0.001-0.2份，减水剂:1~4份，淀粉醚0~2份，缓凝剂:0-2份，轻质颗粒:2~500份，水:400~1000份。
2.按权利要求1所述的一种保温砂浆的制备方法，其特征是:所述的水泥为:水泥为硅酸盐水泥，普通硅酸盐水泥，矿渣水泥、火山灰水泥中的一种；所述的矿粉为S95、S105级矿粉，比表面积大于400m2/Kg ;所述的粉煤灰为I级粉煤灰。
3.按权利要求1所述的一种保温砂浆的制备方法，其特征是:所述的滑石粉细度为600-1000目；所述的重钙粉细度为600~1500目；所述的硅灰比表面积为15~27m2/g ;所述的膨胀剂为钙矾石类、方镁石类、II型硬石膏类、复合膨胀剂中的一种。
4.按权利要求1所述的一种保温砂浆的制备方法，其特征是:所述的早强剂为碳酸锂、甲酸钙、硝酸钠等非硫酸盐、氯盐早强剂中的一种；所述的PP纤维为直径< 0.02mm，长度(5mm的PP纤维；所述的可再分散乳胶粉为醋酸乙烯酯一乙烯共聚乳胶粉，固含多98%，细度0.5〜8 μ m ;所述的纤维素醚为羟乙基一甲基纤维素醚(HEMC)或羟丙基一甲基纤维素醚(HPMC)0
5.按权利要求1所述的一种保温砂浆的制备方法，其特征是:所述憎水剂为有机硅憎水剂、硬酯酸钙憎水剂、改性硬脂酸钙憎水剂中的一种；所述的引气剂为十二烷基苯磺酸钠或松香引气剂；所述的减水剂为萘系减水剂、氨基磺酸盐减水剂、脂肪族减水剂、聚羧酸减水剂中的一种，减水率15°/『35% ;所述的淀粉醚为羟烷基淀粉、羧甲基淀粉、阳离子淀粉中的一种；所述的缓凝剂为葡萄糖酸钠、柠檬酸钠、酒石酸、糖、糖蜜中的一种。
6.按权利要求1所述的一种保温砂浆的制备方法，其特征是:所述的轻质颗粒为聚苯颗粒、玻化微珠、膨胀珍珠岩中的一种。
CN201510694405.4A 2015-10-23 2015-10-23 一种保温砂浆的制备方法 Pending CN105330215A (zh)