CN103936374A - 一种保险箱用防火材料 - Google Patents

一种保险箱用防火材料 Download PDF

Info

Publication number
CN103936374A
CN103936374A CN201310017438.6A CN201310017438A CN103936374A CN 103936374 A CN103936374 A CN 103936374A CN 201310017438 A CN201310017438 A CN 201310017438A CN 103936374 A CN103936374 A CN 103936374A
Authority
CN
China
Prior art keywords
parts
fire
retardant material
mixture
aes
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310017438.6A
Other languages
English (en)
Other versions
CN103936374B (zh
Inventor
朱小兵
王以丹
贾颂今
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Kangyuan Chemical Co., Ltd.
Original Assignee
Shanghai Waysmos Fine Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Waysmos Fine Chemical Co Ltd filed Critical Shanghai Waysmos Fine Chemical Co Ltd
Priority to CN201310017438.6A priority Critical patent/CN103936374B/zh
Publication of CN103936374A publication Critical patent/CN103936374A/zh
Application granted granted Critical
Publication of CN103936374B publication Critical patent/CN103936374B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种保险箱用防火材料，其特征在于：由以下重量份的组分混合凝固而成：轻烧氧化镁20-25份、中空玻璃微珠7-10份、硅酸锆粉7-10份、海泡石7-10份、高铝水泥7-10份、碳纤维1-4份、石棉纤维素3-5份、闭孔珍珠岩3-5份、发泡剂1-3份，AES活性剂1-3份。该种材料防火隔热性能好、成本低、密度小，可用于制备保险箱防火夹层等。

Description

一种保险箱用防火材料
技术领域
本发明涉及一种隔热防火材料以及该防火材料的制造方法，该材料可用于制备保险箱夹层。
背景技术
现有的保险箱用的防火材料均存在比重大，保温抗热能力较差，因而为了有效的起到防火作用，必然需要采用较厚的防火材料层，这导致采用这些防火材料的防火保险箱重量大，不利于携带或搬移。目前已有比重比较小的防火材料面市，但是其隔热性能仍有待进一步提高。
与此同时，降低耐火材料成本与隔热性能的提高也是企业所考虑的重要问题。虽然市面上现有一些防火享用防火材料，成本较低，但是它们的隔热性能差，耐火时间短，不能满足国家标准要求。而保险箱在高温下的内部温度保温时间在实际应用中具有重要意义，火灾发生后，保温时间越长，获得抢救的机会越大，因此，如何延长材料在火灾中火势蔓延时保温的时间也是本发明所考虑的重要点之一。
发明内容
本发明的目的就在于提供一种隔热性能好、成本低、密度低的防火材料，以及该材料的制造方法；该防火材料可用于制成保险箱的夹层。
为达到上述目的，本发明的技术方案为：
一种保险箱用防火材料，其特征在于：由以下重量份的组分混合凝固而成：轻烧氧化镁20-25份、中空玻璃微珠7-10份、硅酸锆粉7-10份、海泡石7-10份、高铝水泥7-10份、碳纤维1-4份、石棉纤维素3-5份、闭孔珍珠岩3-5份、发泡剂1-3份，AES活性剂1-3份。
上述防火材料使用水进行凝固，所述水的量满足能使各原料的混合物形成粘稠状。
所述硅酸锆粉粒度为100目-200目，中空玻璃微珠的粒径为微米级。
一种制备上述防火材料的方法，按上述组分的重量份由以下步骤完成：(A)、在搅拌机中加入轻烧氧化镁、中空玻璃微珠、硅酸锆粉、海泡石搅拌，再加入高铝水泥和碳纤维、石棉纤维素、闭孔珍珠岩、AES活性剂搅拌混合均匀，然后加水搅拌至混合物呈粘稠状，(B)利用发泡机将发泡剂的水溶液制成泡沫浆；然后将该泡沫浆加入步骤(A)的混合物中，搅拌混合均匀并凝固得到防火材料。
其中，中空玻璃微珠等混合后产生化学反应迅速发泡膨胀，具备保温隔热防火阻燃功能。隔热保温材料首先要有良好的阻燃性，我们用明火直接对试验件燃烧，经20分钟后试验件仍完好无损，既未熔化也未变软，仅出现碳化点。
而加入发泡剂可以将制品密度降低到0.35g/cm3以下，使制品达到180kg/cm3-260kg/cm3，从而使制品降低导热系数，其导热系数达到0.048w/m.k-0.08w/m.k.并有较高的强度以满足成型和施工需要。
掺和碳纤维提高制品的抗折和抗压强度，防止收缩裂缝，同时制品密度没有明显变化，提高强度。而且加入碳纤维可以降低材料重量、增强材料的强度。
石棉纤维素不与其他材料产生化学反应，完全是通过物理作用改善制品的工作性能和力学性能，对制品的稳定性能起到很好作用。
活性剂采用AES活性剂，可去除气味，增加流动效果。闭孔珍珠岩可去除气味，减轻比重，并增强耐火效果。
本发明的保温防火材料可用于灌注入防火箱的夹层中作为防火材料层，按上述的配方混合均匀后所得的浆料流动性极佳，易于灌注，凝固快，而且硬度好，受热后不会裂开、破碎；同时，浆料凝固后比重低，保温吸热性能更强，延长火灾中火势蔓延的时间，有效保存贮藏的物件。
具体实施方式
实施例1
在搅拌机中加入轻烧氧化镁20份、中空玻璃微珠10份、硅酸锆粉10份、海泡石10份，搅拌，再加入高铝水泥7份、碳纤维4份、石棉纤维素5份、闭孔珍珠岩3份、AES活性剂1份搅拌混合均匀，然后加水搅拌至混合物呈粘稠状，(B)利用发泡机将发泡剂3份的水溶液制成泡沫浆；然后将该泡沫浆加入步骤(A)的混合物中，搅拌混合均匀得到防火材料浆料。
实施例2
在搅拌机中加入轻烧氧化镁25份、中空玻璃微珠7份、硅酸锆粉7份、海泡石7份，搅拌，再加入高铝水泥10份、碳纤维1份、石棉纤维素3份、闭孔珍珠岩5份、AES活性剂3份搅拌混合均匀，然后加水搅拌至混合物呈粘稠状，(B)利用发泡机将发泡剂1份的水溶液制成泡沫浆；然后将该泡沫浆加入步骤(A)的混合物中，搅拌混合均匀得到防火材料浆料。
实施例3
在搅拌机中加入轻烧氧化镁20份、中空玻璃微珠8份、硅酸锆粉8份、海泡石9份，搅拌，再加入高铝水泥7份、碳纤维3份、石棉纤维素4份、闭孔珍珠岩3份、AES活性剂1份搅拌混合均匀，然后加水搅拌至混合物呈粘稠状，(B)利用发泡机将发泡剂3份的水溶液制成泡沫浆；然后将该泡沫浆加入步骤(A)的混合物中，搅拌混合均匀得到防火材料浆料。
实施例4
在搅拌机中加入轻烧氧化镁24份、中空玻璃微珠9份、硅酸锆粉7份、海泡石8份，搅拌，再加入高铝水泥8份、碳纤维2份、石棉纤维素3份、闭孔珍珠岩4份、AES活性剂3份搅拌混合均匀，然后加水搅拌至混合物呈粘稠状，(B)利用发泡机将发泡剂1份的水溶液制成泡沫浆；然后将该泡沫浆加入步骤(A)的混合物中，搅拌混合均匀得到防火材料浆料。
实施例5
在搅拌机中加入轻烧氧化镁25份、中空玻璃微珠7份、硅酸锆粉8份、海泡石7份，搅拌，再加入高铝水泥9份、碳纤维2份、石棉纤维素3份、闭孔珍珠岩5份、AES活性剂1份搅拌混合均匀，然后加水搅拌至混合物呈粘稠状，(B)利用发泡机将发泡剂3份的水溶液制成泡沫浆；然后将该泡沫浆加入步骤(A)的混合物中，搅拌混合均匀得到防火材料浆料。
将上述各组分搅拌混合均匀所得到的浆料即可用于关注防火保险箱的夹层，浆料凝固后形成保温抗热层，其比重约637千克/立方米，比现有防火材料的比重大大降低了约33％，令制得的防火保险箱更为轻便。防火材料的隔热性能是指阻隔组件遭受火势的侵害时，限制阻隔组件其非受火面温度(背温)上升值低于特定限值之能力，即防止热量自阻隔组件的受火面传至非受火面所具备的防火性能。采用本发明的新型保温防火材料灌注的塑料夹层箱，当防火材料厚度达到39mm，保险箱按UL72标准实验1小时，箱外温度升至930℃，保险箱内温度仍低于170℃，该保温时间在实际应用中具有重要意义，火灾发生后，保温时间越长，获得抢救的机会越大，因此，本发明的防火材料相对现有其他防火材料来说，可延长火灾中火势蔓延的时间，有利抢救，减少损失。

Claims (5)

1.一种保险箱用防火材料，其特征在于：由以下重量份的组分混合凝固而成：轻烧氧化镁20-25份、中空玻璃微珠7-10份、硅酸锆粉7-10份、海泡石7-10份、高铝水泥7-10份、碳纤维1-4份、石棉纤维素3-5份、闭孔珍珠岩3-5份、发泡剂1-3份，AES活性剂1-3份。
2.根据权利要求1所述防火材料，其特征在于：使用水进行凝固，所述水的量满足能使各原料的混合物形成粘稠状。
3.根据权利要求1所述防火材料，其特征在于：所述硅酸锆粉粒度为100目-200目。
4.一种制备权利1-3任一项所述防火材料的方法，按权利要求1-3中任一项所述组分的重量份由以下步骤完成：(A)、在搅拌机中加入轻烧氧化镁、中空玻璃微珠、硅酸锆粉、海泡石搅拌，再加入高铝水泥和碳纤维、石棉纤维素、闭孔珍珠岩、AES活性剂搅拌混合均匀，然后加水搅拌至混合物呈粘稠状，(B)利用发泡机将发泡剂的水溶液制成泡沫浆；然后将该泡沫浆加入步骤(A)的混合物中，搅拌混合均匀并凝固得到防火材料。
5.一种权利要求1-3任一项所述防火材料的用途，其特征在于其用于制备保险箱的夹层材料。
CN201310017438.6A 2013-01-17 2013-01-17 一种保险箱用防火材料 Active CN103936374B (zh)