CN101440141A - 一种用以回收工程塑料的增容扩链剂 - Google Patents

一种用以回收工程塑料的增容扩链剂 Download PDF

Info

Publication number
CN101440141A
CN101440141A CNA2007100315730A CN200710031573A CN101440141A CN 101440141 A CN101440141 A CN 101440141A CN A2007100315730 A CNA2007100315730 A CN A2007100315730A CN 200710031573 A CN200710031573 A CN 200710031573A CN 101440141 A CN101440141 A CN 101440141A
Authority
CN
China
Prior art keywords
grams per
engineering plastics
chain
per liters
grams
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2007100315730A
Other languages
English (en)
Inventor
郑一泉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitac Precision Technology Shunde Ltd
Original Assignee
Mitac Precision Technology Shunde Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitac Precision Technology Shunde Ltd filed Critical Mitac Precision Technology Shunde Ltd
Priority to CNA2007100315730A priority Critical patent/CN101440141A/zh
Publication of CN101440141A publication Critical patent/CN101440141A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种用以回收工程塑料的增容扩链剂，每升溶液中含有苯乙烯1～99克；甲基丙烯酸酯0～60克；甲基丙烯酸缩水甘油酯1～80克；过氧化二异丙苯0.1～5.0克；链转移剂0.1～5.0克。其中，苯乙烯、甲基甲基丙烯酸酯以及甲基丙烯酸缩水甘油酯为共聚物组成，过氧化二异丙苯为引发剂，上述物质在150℃的温度下进行自由基共聚反应，得到共聚产物，该共聚产物有效提升废旧工程塑料的分子量，以达到重新回收工程塑料的目的。

Description

一种用以回收工程塑料的增容扩链剂
技术领域
本发明涉及一种扩链剂，尤其涉及一种用于回收废旧工程塑料的增容扩链剂。
背景技术
现今，由于工程塑料广泛用于汽车工业，家用电器，通讯设备如移动电话等，随着石油价格的飞涨，工程塑料的价格也随之飞涨，而价格的飞涨极大的增加了消费厂商的成本。
目前，业界对工程塑料废料(如PC/ABS废料)的处理方法主要包括以下几种：(1)采用焚烧或填埋的方式处理，但此种方式不仅不经济而且会带来环境污染，如焚烧会产生二氧化硫等有害气体，此是形成酸雨的主要原因。而采用填埋方式PC/ABS不易降解从而也对环境造成很大的危害。(2)对PC/ABS废料进行简单的回收抽粒而不进行任何改性，降级为普通塑料使用，其虽比第一种方式较好，但依然未能充分利用PC/ABS的价值。
发明内容
鉴于上述问题，本发明提供了一种用以回收工程塑料的增容扩链剂。
为了达到上述目的，本发明采用了如下的技术方案：一种用以回收工程塑料的增容扩链剂，其特征在于，每升溶液中含有：
苯乙烯                         1～99克；
甲基丙烯酸酯                   0～60克；
甲基丙烯酸缩水甘油酯           1～80克；
过氧化二异丙苯                 0.1～5.0克。
较佳的，本发明所述之用以回收工程塑料的增容扩链剂还可包括链转移剂0.1～5.0克/升。
较佳的，本发明所述之用以回收工程塑料的增容扩链剂的优化配方为：
苯乙烯                           42克/升；
甲基丙烯酸酯                     33克/升；
甲基丙烯酸缩水甘油酯             25克/升；
过氧化二异丙苯                   1克/升；
链转移剂                         1克/升。
较佳的，本发明所述之用以回收工程塑料的增容扩链剂的最佳配方为：
苯乙烯                      33克/升；
甲基丙烯酸酯                2克/升；
甲基丙烯酸缩水甘油酯        65克/升；
过氧化二异丙苯              2克/升。
较佳的，本发明所述之用以回收工程塑料的增容扩链剂的最优配方为：
苯乙烯                       66克/升；
甲基丙烯酸酯                 1克/升；
甲基丙烯酸缩水甘油酯         33克/升；
过氧化二异丙苯               1克/升。
相较于先前技术，本发明所述之用以回收工程塑料的增容扩链剂，利用新型链转移剂，有效提升了废旧工程塑料的分子量，重新回收了废旧工程塑料。
具体实施方式
众所周知，塑料容易氧化降解，工程塑料如PC/ABS也不例外，PC/ABS在回收过程中易于吸水降解，导致分子量降低，性能变差。
本发明提供了一种用以回收工程塑料的增容扩链剂，其利用新型链转移剂，有效提升了废旧工程塑料的分子量，所述增容扩链剂反应温度约为150℃，其三组实施例如下所示。
实施例1：
苯乙烯                         42克/升；
甲基丙烯酸酯                   33克/升；
甲基丙烯酸缩水甘油酯           25克/升；
过氧化二异丙苯                 1克/升；
链转移剂                       1克/升。
其中，苯乙烯、甲基甲基丙烯酸酯以及甲基丙烯酸缩水甘油酯为共聚物组成，过氧化二异丙苯为引发剂，上述物质在150℃的温度下进行自由基共聚反应，得到共聚产物，该共聚产物有效提升废旧工程塑料的分子量，以达到重新回收工程塑料的目的。
实施例2：
苯乙烯                          33克/升；
甲基丙烯酸酯                    2克/升；
甲基丙烯酸缩水甘油酯            65克/升；
过氧化二异丙苯                  2克/升。
其中，苯乙烯、甲基甲基丙烯酸酯以及甲基丙烯酸缩水甘油酯为共聚物组成，过氧化二异丙苯为引发剂，上述物质在150℃的温度下进行自由基共聚反应，得到共聚产物，该共聚产物有效提升废旧工程塑料的分子量，以达到重新回收工程塑料的目的。
实施例3：
苯乙烯                    66克/升；
甲基丙烯酸酯              1克/升；
甲基丙烯酸缩水甘油酯      33克/升；
过氧化二异丙苯            1克/升。
其中，苯乙烯、甲基甲基丙烯酸酯以及甲基丙烯酸缩水甘油酯为共聚物组成，过氧化二异丙苯为引发剂，上述物质在150℃的温度下进行自由基共聚反应，得到共聚产物，该共聚产物有效提升废旧工程塑料的分子量，以达到重新回收工程塑料的目的。

Claims (5)

1.一种用以回收工程塑料的增容扩链剂，其特征在于，每升溶液中含有：
苯乙烯                    1～99克；
甲基丙烯酸酯              0～60克；
甲基丙烯酸缩水甘油酯      1～80克；
过氧化二异丙苯            0.1～5.0克。
2.根据权利要求1所述的用以回收工程塑料的增容扩链剂，其特征在于，每升溶液中还含有：
链转移剂                 0.1～5.0克。
3.根据权利要求2所述的用以回收工程塑料的增容扩链剂，其特征在于，该增容扩链剂的优化配方为：
苯乙烯                        42克/升；
甲基丙烯酸酯                  33克/升；
甲基丙烯酸缩水甘油酯          25克/升；
过氧化二异丙苯                1克/升；
链转移剂                      1克/升。
4.根据权利要求1所述的用以回收工程塑料的增容扩链剂，其特征在于，该增容扩链剂的最佳配方为：
苯乙烯                       33克/升；
甲基丙烯酸酯                 2克/升；
甲基丙烯酸缩水甘油酯         65克/升；
过氧化二异丙苯               2克/升。
5.根据权利要求1所述的用以回收工程塑料的增容扩链剂，其特征在于，该增容扩链剂的最优配方为：
苯乙烯                     66克/升；
甲基丙烯酸酯               1克/升；
甲基丙烯酸缩水甘油酯       33克/升；
过氧化二异丙苯             1克/升。
CNA2007100315730A 2007-11-23 2007-11-23 一种用以回收工程塑料的增容扩链剂 Pending CN101440141A (zh)