CN101134595A - 氟化钙的生产方法 - Google Patents

氟化钙的生产方法 Download PDF

Info

Publication number
CN101134595A
CN101134595A CNA2006101069692A CN200610106969A CN101134595A CN 101134595 A CN101134595 A CN 101134595A CN A2006101069692 A CNA2006101069692 A CN A2006101069692A CN 200610106969 A CN200610106969 A CN 200610106969A CN 101134595 A CN101134595 A CN 101134595A
Authority
CN
China
Prior art keywords
calcium
fluorspan
solid
fluoride
silicon tetrafluoride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2006101069692A
Other languages
English (en)
Inventor
李世江
侯红军
杨华春
皇甫根利
于贺华
闫春生
张梅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Duo Fluoride Chemicals Co Ltd
Original Assignee
Duo Fluoride Chemicals Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Duo Fluoride Chemicals Co Ltd filed Critical Duo Fluoride Chemicals Co Ltd
Priority to CNA2006101069692A priority Critical patent/CN101134595A/zh
Publication of CN101134595A publication Critical patent/CN101134595A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种氟化钙的生产方法，以氟硅酸和氧化钙为原料，包括以下步骤：(1)将氟硅酸溶液和氧化钙反应10～60分钟，反应结束后，过滤得到氟硅酸钙固体；(2)将氟硅酸钙在200～600℃的温度下分解1～5小时，生成氟化钙固体产品和四氟化硅气体；(3)将四氟化硅气体用水吸收并水解，过滤得到的氟硅酸溶液返回去制氟硅酸钙，二氧化硅固体经洗涤、干燥得到白炭黑。本发明的方法是以磷肥副产氟硅酸为原料代替了传统方法中的以萤石矿产为原料生产氟化钙，节约了萤石资源，大大降低了生产成本。氟硅酸是磷肥生产过程的副产有害废物，用途很少，并且对周围环境造成了严重影响，氟硅酸的开发处理急需解决。本发明以氟硅酸为主要原料，变废为宝，大大缓解了由于氟硅酸的积压而对周围环境造成的污染。本发明工艺简单，降低了氟化钙的生产成本，具有很好的经济价值和社会价值，易于推广应用。

Description

氟化钙的生产方法
技术领域
本发明涉及一种氟化钙的生产方法，尤其涉及一种以氟硅酸与氧化钙为原料生产氟化钙的方法。
背景技术
氟化钙，主要用于氢氟酸的生产原料及冶金熔剂。氟化钙的传统生产方法为天然萤石矿物浮选，其生产工艺过程复杂，且生产成本高。
发明内容
本发明目的在于提供一种氟化钙的生产方法，以大大降低其生产成本。
为实现上述目的，本发明的技术方案在于采用了一种氟化钙的生产方法，以氟硅酸和氧化钙为原料，包括以下步骤：
(1)将氟硅酸溶液和氧化钙反应10～60分钟，反应结束后，过滤得到氟硅酸钙固体；
(2)将氟硅酸钙在200～600℃的温度下分解1～5小时，生成氟化钙固体产品和四氟化硅气体；
(3)将四氟化硅气体用水吸收并水解，过滤得到的氟硅酸溶液返回去制氟硅酸钙，二氧化硅固体经洗涤、干燥得到白炭黑。
所述的氟硅酸溶液的浓度为10～40％。
所述的氧化钙为固体或浓度为10～30％的料浆。
本发明反应式为：
H2SiF6+CaO+H2O→CaSiF6·2H2O
CaSiF6·2H2O→CaF2+SiF4↑+2H2O↑
3SiF4+2H2O→2H2SiF6+SiO2↓
本发明的方法是以磷肥副产氟硅酸为原料代替了传统方法中的以萤石矿产为原料生产氟化钙，节约了萤石资源，大大降低了生产成本。氟硅酸是磷肥生产过程的副产有害废物，用途很少，并且对周围环境造成了严重影响，氟硅酸的开发处理急需解决。本发明以氟硅酸为主要原料，变废为宝，大大缓解了由于氟硅酸的积压而对周围环境造成的污染。另外，本发明方法所得的产品氟硅酸溶液可以返回去制氟硅酸钙，在一定程度上节约了成本。本发明工艺简单，大大降低了氟化钙的生产成本，具有很好的经济价值和社会价值，易于推广应用。
氟化钙产品质量
具体实施方式
实施例1
本实施例的氟化钙的生产方法，以氟硅酸和氧化钙为原料，包括以下步骤：
(1)将浓度为15％的氟硅酸溶液和氧化钙固体反应40分钟，反应结束后，过滤得到氟硅酸钙固体；
(2)将氟硅酸钙在300℃的温度下分解4小时，生成氟化钙固体产品和四氟化硅气体；
(3)将四氟化硅气体用水吸收并水解，过滤得到的氟硅酸溶液返回去制氟硅酸钙，二氧化硅固体洗涤、干燥得到白炭黑。
实施例2
本实施例的氟化钙的生产方法，以氟硅酸和氧化钙为原料，包括以下步骤：
(1)将浓度为25％的氟硅酸溶液与浓度为30％的氧化钙料浆反应30分钟，反应结束后，过滤得到氟硅酸钙固体；
(2)将氟硅酸钙在400℃的温度下分解3小时，生成氟化钙固体产品和四氟化硅气体；
(3)将四氟化硅气体用水吸收并水解，过滤得到的浓度为25％的氟硅酸溶液返回去制氟硅酸钙，二氧化硅固体洗涤、干燥得到白炭黑。
实施例3
本实施例的氟化钙的生产方法，以氟硅酸和氧化钙为原料，包括以下步骤：
(1)将浓度为35％的氟硅酸溶液与浓度为20％的氧化钙料浆反应20分钟，反应结束后，过滤得到氟硅酸钙固体；
(2)将氟硅酸钙在500℃的温度下分解2小时，生成氟化钙固体产品和四氟化硅气体；
(3)将四氟化硅气体用水吸收并水解，过滤得到的浓度为35％的氟硅酸溶液返回去制氟硅酸钙，二氧化硅固体洗涤、干燥得到白炭黑。
最后所应说明的是：以上实施例仅用以说明而非限制本发明的技术方案，尽管参照上述实施例对本发明进行了详细说明，本领域的普通技术人员应当理解：依然可以对本发明进行修改或者等同替换，而不脱离本发明的精神和范围的任何修改或局部替换，其均应涵盖在本发明的权利要求范围当中。

Claims (3)

1.一种氟化钙的生产方法，以氟硅酸和氧化钙为原料，包括以下步骤：
(1)将氟硅酸溶液和氧化钙反应10～60分钟，反应结束后，过滤得到氟硅酸钙固体；
(2)将氟硅酸钙在200～600℃的温度下分解1～5小时，生成氟化钙固体产品和四氟化硅气体；
(3)将四氟化硅气体用水吸收并水解，过滤得到的氟硅酸溶液返回去制氟硅酸钙，二氧化硅固体经洗涤、干燥得到白炭黑。
2.根据权利要求1所述的氟化钙的生产方法，其特征在于：所述的氟硅酸溶液的浓度为10～40％。
3.根据权利要求1所述的氟化钙的生产方法，其特征在于：所述的氧化钙为固体或浓度为10～30％的料浆。
CNA2006101069692A 2006-09-01 2006-09-01 氟化钙的生产方法 Pending CN101134595A (zh)