CN101130318A - 喷墨记录材料 - Google Patents
喷墨记录材料 Download PDFInfo
- Publication number
- CN101130318A CN101130318A CNA2007101424078A CN200710142407A CN101130318A CN 101130318 A CN101130318 A CN 101130318A CN A2007101424078 A CNA2007101424078 A CN A2007101424078A CN 200710142407 A CN200710142407 A CN 200710142407A CN 101130318 A CN101130318 A CN 101130318A
- Authority
- CN
- China
- Prior art keywords
- jet recording
- ink jet
- recording materials
- substrate
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种当以染料墨或颜料墨印刷时没有吸墨、印刷密度优良并且允许清楚地印刷高清晰度图像的喷墨记录材料。所述喷墨记录材料包含其至少一个表面用墨固定剂处理的基底，所述墨固定剂为由以下通式表示的阳离子表面活性剂，其中R为含有8至18个碳原子的烷基。
Description
技术领域
本发明涉及一种当用染料墨或颜料墨印刷时没有吸墨、印刷密度优良并且能够清楚地印刷高清晰度图像的喷墨记录材料。
背景技术
随着用于在高速下制造硬拷贝的喷墨打印机的近来技术的进展，获得清晰的图像和高的印刷质量已经成为可能。因此，为了进一步改善印刷质量，目前存在着对更好质量的记录材料的需求。为了满足此需求，已经开发出了各种的记录材料。
用于喷墨打印机的水性墨被分类为使用染料的染料墨以及使用颜料的颜料墨。前者主要是从清晰的观点来使用。然而最近，所讨论的水性墨也已经逐渐用于印刷户外展览用的大尺寸海报。在此情况下，当使用染料墨的海报在户外展览一段长的时期时，其被紫外光和臭氧氧化，导致使用染料墨形成的该图像变得褪色和难看，从而产生了没有获得满意的印刷耐光性的缺点。
另一方面，颜料墨的特征在于使用颜料墨的印刷部分在储存稳定性方面优良。然而，与染料墨中使用的染料的尺寸相比，颜料墨中的颜料粒子非常大，从而产生了用于染料墨的常规喷墨记录材料不能提供清晰的印刷图像的问题。
最近，喷墨打印机的应用已经从印刷文件等扩展至宽的广告例如海报的应用。对于印刷广告等，通常采用的是能够在宽的印刷材料上有效印刷的喷墨打印机，该喷墨打印机被称为例如喷墨绘图机。通过使用这样的喷墨绘图机获得的印刷品在许多情形中是在户外展览的，因此主要使用在印刷部分的储存稳定性方面优良的颜料墨。此外，它们的用途是用于广告，即使从远距离图像也必需是清晰可见的。因此，存在吐出的墨量逐年变得更大的趋势。
由于染料墨和颜料墨在特征上不同，例如与染料墨的染料尺寸相比，颜料墨的颜料粒子非常大，因此已经将专有地用于染料墨和颜料墨的喷墨记录材料分别提供作为记录介质。例如，在使用颜料墨印刷染料墨用的常规喷墨记录材料的情况下，在实际应用中出现的问题是，例如，颜料墨不被记录材料吸收；在印刷部分中导致不均匀性；或墨粒子的固定差，并且当用手指等接触时，墨从印刷部分脱落。
在此情形下，存在着的强烈需求是开发这样一种喷墨记录材料，不论使用染料墨和颜料墨中的哪一种，该喷墨记录材料都没有吸墨，并且具有优异的印刷适性。
为了满足这样的需求，作为不论使用染料墨和颜料墨中的哪一种都表现优异的印刷适性的喷墨记录材料，已经提出了：使用部分水解的聚乙烯醇和丙烯酸酯聚合物作为墨接收层中的乳化树脂的记录材料(例如见，JP2000-309160A)；在墨接收层中含有选自丙烯酸类聚合物、乙烯-乙酸乙烯酯聚合物和乙酸乙烯酯聚合物中的至少一种的乳液型粘合剂的记录材料(例如见，JP2005-280338A)；在墨接收层中含有水溶性金属盐的记录材料(例如见，JP2002-274022A)；以及使用含有作为主要组分的木浆和填料的原纸的喷墨记录片材，该原纸经由含有阳离子树脂和水溶性多价金属盐的施胶溶液(size press solution)进行表面处理，该阳离子树脂为三种组分的缩聚物，该三种组分是二甲胺、表氯醇和胺(例如见，JP 2005-271522A)。
然而，它们没有一种被认为完全满足在染料墨和颜料墨的使用时的印刷适性。因而，目前仍然存在着的强烈需求是开发这样一种喷墨记录材料，不论使用染料墨和颜料墨的中的哪一种，该喷墨记录材料都表现优异的印刷适性。
发明内容
本发明的一个目的是提供一种这样的喷墨记录材料，不论在印刷该记录材料中使用染料墨和颜料墨中的哪一种，该喷墨记录材料都表现优异的印刷适性。
本发明人已经进行了认真的研究以解决上述问题，已经发现，所述问题可以通过采用以下设计来解决。
根据本发明，首先是提供一种包含基底的喷墨记录材料，所述基底的一个或两个表面具有含墨固定剂(ink fixing agent)的涂层，该喷墨记录材料的特征在于所述墨固定剂是由以下通式表示的阳离子表面活性剂：
其中R为含有8至18个碳原子的烷基。
根据本发明，其次是提供一种包含基底的喷墨记录材料，所述基底的一个或两个表面具有涂层，所述涂层包含颜料、粘合剂和墨固定剂，该喷墨记录材料的特征在于所述墨固定剂是由以下通式表示的阳离子表面活性剂：
其中R为含有8至18个碳原子的烷基。
根据本发明，第三是提供上述第二的喷墨记录材料，其中基于100质量份的颜料，所述涂层包含1至30质量份的阳离子表面活性剂和20至70质量份的粘合剂。
根据本发明，第四是提供上述第二或第三的喷墨记录材料，其中所述粘合剂包含非离子丙烯酸酯(共)聚合物和阳离子丙烯酸酯(共)聚合物。
根据本发明，第五是提供上述第四的喷墨记录材料，其中所述非离子丙烯酸酯(共)聚物涂布有水溶性聚合物保护胶体。
根据本发明，第六是提供一种喷墨记录材料，其中水溶性聚合物保护胶体为聚乙烯醇。
根据本发明，第七是提供上述第四的喷墨记录材料，其中所述基底为透气性的基底。
根据本发明，第八是提供一种喷墨记录材料，其中基底为非透气性基底。
发明效果
根据本发明可以提供这样一种喷墨记录材料，不论在印刷该记录材料中使用染料墨和颜料墨中的哪一种，所述喷墨记录材料都表现优异的无吸墨的印刷适性、优良的墨密度。
发明详述
以下将详细描述本发明。
关于本发明的喷墨记录材料，通过短语“基底的一个或两个表面具有含墨固定剂的涂层”，表示的是进行一种处理以使以下通式的阳离子表面活性剂存在于喷墨记录材料的基底的至少一个表面上。对层的构造以及涂层形成方法没有具体的限制。例如，可以将含有阳离子表面活性剂的涂布溶液涂敷到基底表面的一个或两个表面上。被涂敷到基底上的涂布溶液可以是具有其它物质的混合物。可以用涂布溶液浸渍基底。另外，在形成基底例如纸的时候，可以将阳离子表面活性剂加入到其中。根据使用的基底的类型和性质，可以通过适宜的方式将阳离子表面活性剂涂敷至基底。
其中R为含有8至18个碳原子的烷基。
(层的构造)
本发明在于一种包含基底的喷墨记录材料，该基底的至少一个表面在其上具有含墨固定剂的涂层，该喷墨记录材料的特征在于，所述墨固定剂为由上述通式表示的阳离子表面活性剂。
可以在基底的不仅一个表面，而且两个表面上都涂敷这样的涂层。在基底的两个表面上同时具有涂层的情况下，在喷墨记录材料的两个表面上实现清晰印刷就变得可能。
每个表面上的涂层可以包含多个层。可以在基底和所述涂层之间安置下涂层。另外，在所述涂层上可以安置上涂层，以使记录材料具有光泽，或增强它的储存稳定性，条件是涂层的印刷适性不被削弱。
(基底)
基底可以是透气性基底或非透气性基底。可以根据应用以及应用的目的来选择性地使用两者。优选的是透气性基底，以尽快地分离颜料墨中的颜料和溶剂，并且增强颜料固定性质和印刷密度。
(透气性基底)
透气性基底的合适实例为不含木浆的纸、美术纸、机上涂布纸(on-machine coated paper)、抛光涂料纸、牛皮纸、钡地纸、浸渍用纸、敷金属纸和水溶性纸。
透气性基底主要由木浆以及必要时的填料组成。可使用的木浆的实例包括各种化学浆、机械浆和再生浆。对于这些浆，可以通过打浆机调节打浆程度(游离度)，以调节纸的挺度和造纸适应性。对使用的浆的打浆程度(游离度)没有具体的限制，但是通常在250至550ml(CSF：JIS P8121)的范围内。为了改善平滑性，需要提高打浆程度。对于由墨中所含的湿气对纸上的印刷所导致的纸的不均匀性和记录图像的模糊，为了获得良好的结果，在许多情况下最好不提高打浆程度。因此，优选的是约300至500ml(CSF：JIS P8 121)的游离度。
填料是用于使基底具有不透明性，或调节墨的可吸收性的目的的组分。作为填料，可以使用例如碳酸钙、煅烧高岭土、二氧化硅或氧化钛。尤其地，碳酸钙的使用是优选的，因为它提供了具有高白度的基底，结果是提高了喷墨记录材料的光泽感。填料在纸基底中的含量(灰分含量)优选为1至20质量％。如果填料含量过高，则存在着会恶化纸的挺度的顾虑。如果填料的含量过低，则将会恶化纸基底的气体渗透性。优选的填料含量为7至20质量％。只要填料含量落入此范围之内，平滑性、气体渗透性和纸的挺度就是平衡的，从而变得更容易获得光滑感优良的喷墨记录材料。
例如，可以将胶料、固定剂、纸挺度增强剂、收率改善剂、染料和荧光增白剂作为助剂加入到透气性基底。另外，在造纸机中的施胶压榨过程中，可以将例如淀粉、聚乙烯醇和阳离子树脂涂敷到或浸渍进入基底中，以调节表面强度和施胶程度。Stockigt施胶程度(按100g/m2的纸计)优选为1至200秒。如果施胶程度高，就有可能使颜料墨和溶剂迅速彼此分离，并且会恶化墨的可吸收性和印刷密度。施胶程度的更优选范围为5至120秒。基底的重量没有特别的限制，但是通常是在20至400g/m2的范围内，优选为50至250g/m2，更优选为60至200g/m2。
(非透气性基底)
可使用的非透气性基底的实例为：聚合物膜(包括被称作合成纸的聚合物膜)，例如聚乙烯膜、聚丙烯膜、软的聚氯乙烯膜、刚性聚氯乙烯膜和聚酯膜，金属膜，包含纸或无纺织物以及层压在其上的热塑性树脂的树脂涂布纸；纸，例如为不含木浆的纸、美术纸、机上涂布纸、抛光涂料纸、金属箔纸、牛皮纸、浸渍用纸、涂敷金属纸和水溶性纸；以及包含纸或无纺织物以及层压在其上的膜的层压片材。作为基底的优选实例，提及的有所谓的合成纸，该合成纸通过拉伸聚丙烯，并且对该拉伸的聚丙烯进行特别处理来制备，其代表是YUPO(商品名，YUPO Corp.的产品)；以及包含纸基底和层压在其上的聚烯烃(优选聚乙烯树脂)的树脂涂布纸。在非透气性基底的情况下，墨中的染料、颜料-溶剂分离速度低，但是墨溶剂并不渗透到基底中，因此非透气性基底的使用在其中起皱外观造成问题的应用中是有影响的。
合成纸通常是通过挤出包含无机颜料例如碳酸钙的聚丙烯树脂，并且双轴拉伸该挤出的树脂，以在它的内部中形成空隙来制备的。优选层压片材包含多个层。特别地，优选的是采用在其上形成有记录层并且在其表面上具有没有不均匀性表皮层的合成纸。为了改善可涂布性或改善抗静电性，可以在合成纸的表面上形成各种层，例如固定层(anchor layer)、底漆层和抗静电层。
作为树脂涂布纸，通过将其中捏合有氧化钛的聚乙烯树脂涂布到纸的表面上所制备的基底是特别优选的，因为它的成品外观几乎与照相印刷纸的成品外观相等。聚乙烯树脂层的厚度优选为3至50μm，更优选5至30μm。如果聚乙烯树脂层的厚度小于3μm，则聚乙烯树脂中的缺陷例如孔在树脂涂布的时候趋向于增加，并且在许多情况中难以控制厚度。还难以获得平滑性。相反地，如果聚乙烯树脂厚度超过50μm，则尽管增加了成本，但所产生的效果没有如此显著，这是不经济的。
在树脂涂布纸中使用的纸基底是使用木浆作为主要组分制备的。作为木浆，可以使用各种化学浆、机械浆和再生浆中的任何一种。关于这些浆，可以通过打浆机来调节打浆程度(游离度)，以调节纸的挺度、平滑性和造纸适应性。对打浆程度(游离度)没有特别限制，但是优选是在250至550ml(CSF：JIS P8121)的范围内。无氯浆例如ECF和TCF也是优选可使用的。在需要之处，可以加入颜料。作为颜料的优选实例，此处提及的有滑石、碳酸钙、粘土、高岭土、煅烧高岭土、二氧化硅和沸石。通过颜料的加入，就有可能增强不透明性和平滑性。如果颜料添加过量，则会恶化纸的挺度。基于使用的木浆的量，加入的颜料的量优选在1至20质量％的范围内。
为了改善基底和涂层之间的粘合的目的，预先可以对基底的涂层形成表面进行粘合或粘接改善处理。具体地，在使用树脂涂布纸作为基底的情况下，优选对树脂涂层的表面应用电晕电放处理，或通过采用明胶或聚乙烯醇在树脂涂层的表面上形成下涂层。
(墨固定剂)
在根据本发明的喷墨记录材料中，采用由以下通式表示的阳离子表面活性剂作为墨固定剂。关于允许以下通式的阳离子表面活性剂有助于使记录材料具有优异的印刷适性的机理的细节，其依赖于未来的研究。然而，据推测，由于阳离子表面活性剂与墨着色剂的反应速率高，因此可以将墨着色剂固定在表面，而没有进入层中，因此获得的优异的印刷适性。
其中R为含有8至18个碳原子的烷基，该烷基可以是直链的烷基或支链的烷基。
作为在本发明的喷墨记录材料中使用的阳离子表面活性剂的实例，提及的有氯化癸基二甲基苄基铵、氯化十二烷基二甲基苄基铵、氯化十四烷基二甲基苄基铵、氯化十六烷基二甲基苄基铵、氯化十八烷基二甲基苄基铵和氯化异辛基二甲基苄基铵，其中就印刷适性而言，氯化十二烷基二甲基苄基铵和氯化十四烷基二甲基苄基铵是最优选的。
基于100质量份的包含墨固定剂的涂层，墨固定剂的量优选为5至90质量份，更优选10至80质量份。如果墨固定剂的量小于5质量份，则存在吸墨会变得显著的顾虑，而如果它超过90质量份，则存在会恶化涂布溶液的发泡性的顾虑。在使用颜料的情况下，基于100质量份的颜料，墨固定剂的量优选为1至30质量份，更优选3至20质量份。如果墨固定剂的量小于1质量份，则存在吸墨会变得显著并且会恶化印刷密度的顾虑，而如果它超过30质量份，则存在的顾虑是，会恶化涂布溶液的发泡性，结果是产生了因气泡所致的在涂布表面上的白色部分以及印刷密度的恶化。
除了前述通式的墨固定剂，此处还可以使用已知的墨固定剂，只要本发明中阐述的墨固定剂的功能和效果不受削弱即可。作为已知的墨固定剂的实例，此处提及的是以下可商购的墨固定剂：1)聚亚烷基胺，例如聚亚乙基胺和聚亚丙基胺或它们的衍生物；2)具有叔或季铵基团的丙烯酸类树脂；4)由双氰胺-甲醛缩聚物为代表的双氰-基阳离子树脂；5)由双氰胺-二亚乙基三胺缩聚物为代表的多胺-基阳离子树脂；6)二甲胺-表氯醇的加聚物；7)氯化二烯丙基二甲基铵-SO2的共聚物；8)二烯丙基胺盐-SO2的共聚物；9)氯化二甲基二烯丙基铵聚合物；10)烯丙基胺盐聚合物；11)乙烯基苄基三烯丙基铵盐的均聚物或共聚物；12)(甲基)丙烯酸二烷基氨基乙酯的季盐的共聚物；13)丙烯酰胺-二烯丙基胺盐的共聚物；14)铝盐，例如聚氯化铝和聚乙酸铝。这些化合物可以各自单独使用，或可以将它们中的几种组合使用。
(涂层中的颜料)
在使用颜料的情况下，可以使用任何的颜料，只要迄今它已经被用在喷墨记录材料的墨接收层中即可。可使用的颜料的实例为：无机颜料，例如轻质碳酸钙、重质碳酸钙、高岭土、滑石、硫酸钙、二氧化钛、氧化锌、硫化锌、碳酸锌、缎光白、硅酸铝、硅藻土、硅酸钙、硅酸镁、氢氧化铝、氧化铝、假勃姆石、锌钡白、沸石、水合埃洛石、碳酸镁和氢氧化镁；以及由以下这样的树脂组成的有机颜料，例如：丙烯酸或甲基丙烯酸树脂、聚氯乙烯树脂、聚乙酸乙烯酯树脂、聚酯树脂、苯乙烯-丙烯酰基树脂、苯乙烯-丁二烯树脂、苯乙烯-异戊二烯树脂、聚碳酸酯树脂、有机硅树脂、尿素树脂、蜜胺树脂、环氧树脂、酚醛树脂和邻苯二甲酸二烯丙酯树脂。这些颜料各自都可以为真正的球形或无定形的。同样地，它们可以是多孔或非多孔的。它们各自可以单独使用，或以它们中的两种或更多种组合使用。无定形二氧化硅是更优选的。对于怎样制备二氧化硅没有特别限制。在本发明中可以使用通过电弧法、干法和湿法(沉淀或胶凝方法)中的任何一种制备的二氧化硅。
二氧化硅的次级粒子的平均粒径优选为2至12μm，更优选4至8μm。如果平均粒径小于2μm，那么当将这样的二氧化硅用于染料墨用的喷墨记录片材中时，用于染料墨的片材的可吸收性将会恶化，并且涂层强度也将会恶化。另一方面，如果二氧化硅的次级粒子的平均粒径超过12μm，则用于染料墨的喷墨记录片材和用于颜料墨的喷墨记录片材都会遇到在印刷中倾向于发生不均匀性的问题。二氧化硅的平均粒径是通过Coulter颗粒计数器方法测量的。根据此方法，将二氧化硅在蒸馏水中超声分散30秒，并且将如此分散的二氧化硅用作用于测量的样品。它表示体积平均粒径。
在使用颜料的情况，基于100质量份的包含墨固定剂和颜料的涂层，颜料的量为50至85质量份，优选为60至70质量份。如果颜料的量小于50质量份，则存在着会恶化印刷密度的顾虑，而如果它大于85质量份，则存在着会恶化涂层强度的顾虑。
(涂层中的粘合剂)
对在涂层中使用的粘合剂没有特别限制，但是可以使用通常用于喷墨记录材料的常规已知粘合剂。实例为：蛋白质，例如酪蛋白、大豆蛋白和合成蛋白；各种淀粉，例如淀粉和氧化淀粉；聚乙烯醇及其衍生物；纤维素衍生物，例如羟甲基纤维素和甲基纤维素；共轭二烯类树脂，例如苯乙烯-丁二烯树脂和甲基丙烯酸甲酯-丁二烯共聚物；丙烯酸类树脂，例如丙烯酸、甲基丙烯酸、丙烯酸酯和甲基丙烯酸酯的聚合物或共聚物；以及乙烯基类树脂，例如乙烯-乙酸乙烯酯共聚物。这些可以各自单独使用，或以它们的两种或更多种的组合使用。
特别优选的是丙烯酸酯(共)聚合物，该丙烯酸酯(共)聚合物各自包含非离子丙烯酸酯(共)聚合物和阳离子丙烯酸酯(共)聚合物，所述非离子丙烯酸酯(共)聚合物涂布有水溶性聚合物保护胶体，所述水溶性聚合物为聚乙烯醇。
作为粘合剂，通常为已知的水溶性粘合剂和乳液型粘合剂，但是已经明确的是，通过使用水溶性聚合物保护胶体型丙烯酸酯共聚物，不论使用染料墨和颜料墨中的哪一种，都获得了优异的印刷适性。它与阳离子丙烯酸酯(共)聚合物的组合使用是特别优选的。至于作为粘合剂的所述水溶性的保护胶体型丙烯酸酯(共)聚合物是通过何种机理有助于优异的印刷适性，它的详情没有确定。然而，据推测，由于丙烯酸酯(共)聚合物涂布有水溶性聚合物，因此墨着色剂粘合或固定到作为保护性胶体的水溶性聚合物的表面，并且染料墨和颜料墨的墨粒子或着色剂存在于该丙烯酸酯(共)聚合物之中，而没有被隐藏，致使获得了优异的颜色可显影性。
基于100质量份的包含墨固定剂的涂层，粘合剂的比例优选为10至95质量份，更优选20至90质量份。如果粘合剂的量小于10质量份，则难以增加涂布溶液的量，而如果它大于90质量份，则存在着墨溢流和吸墨变得更显著的顾虑。在使用颜料的情况下，基于100质量份的颜料，粘合剂的比例为20至70质量份，更优选40至60质量份。如果粘合剂的量超过70质量份，存在着墨溢流和发生吸墨的顾虑，而如果粘合剂的量小于20质量份，则涂层的强度趋于变得更低。
可以适当地向涂层加入各种例如在制造涂布纸中使用的助剂，例如增稠剂、消泡剂、润湿剂、表面活性剂、着色剂、抗静电剂、耐光助剂、紫外吸收剂、抗氧化剂和防腐剂。
对涂敷含有墨固定剂的涂层的涂布溶液的量没有特别限制，但是优选为0.1至30g/m2，更优选为0.5至20g/m2。如果所涂敷的涂布溶液的量小于0.1g/m2，则可吸墨性和图像清晰性则倾向于恶化，而如果涂敷的涂布溶液的量超过30g/m2，则涂层强度和图像清晰性则趋向于恶化。涂层可以是多个涂层的层压体。在此情况下，涂层可以具有不同的组成。
涂层可以使用各种已知涂布机的任何一种来形成，这些已知的涂布机包括刮刀涂布机、气刀涂布机、辊涂布机、棒涂布机、照相凹板涂布机、棒式刮刀涂布机、刀刃涂布机(lip coater)、幕涂布机、模涂布机、逆转辊涂布机、辊舐涂布机、浇铸涂布机、champlex涂布机、刷涂布机、闸辊式涂布机、哈密顿涂布机(hamilton coater)、KCM涂布机、施胶压榨涂布机、计量施胶机、计量薄膜转移辊涂布机和滑珠涂布机(slide bead coater)。
用于涂层的干燥条件是例如通过调节涂布溶液的浓度来调节的。在此关系中，吸收速率的行为也取决于干燥条件而变化。优选在尽可能强的干燥条件下干燥涂布溶液。然而，过度干燥趋向于导致颜色可显影性恶化。
可以使用砑光机例如机械砑光机、高度砑光机或软砑光机在涂布操作以后进行修整工序。然而，同样关于这样的修整工序，有必要的是使调整处于不削弱印刷适性的范围内。
将通过本发明的操作实施例来具体地描述本发明，但是不言而喻的是本发明并不受以下实施例限制。除非另外提及，实施例中的份和％是不包含水在内的固体，并且分别表示质量份和质量％。
实施例1：
[制备用于涂层的涂布溶液]
将100份的作为颜料的湿法二氧化硅(商品名：Fine Seal X-60，Tokuyama Corp.的产品)、10份的作为墨固定剂的氯化十四烷基二甲基苄基铵(商品名：M2-100R，NOF CORP.的产品)、20份的甲硅烷基改性的聚乙烯醇(PVA)(商品名：R-1130，Kuraray Co.，Ltd.的产品)、15份的水溶性聚合物保护胶体型非离子丙烯酸酯共聚物(商品名：VINYBLAN 2680，Nisshin Chemical Co.，Ltd.的产品)，以及10份的作为粘合剂的阳离子丙烯酸酯共聚物(商品名：VINYBLAN 2647，Nisshin Chemical Co.，Ltd.的产品)混合并且分散，以制备固含量为20％的涂布溶液。
[制备喷墨记录材料]
以10g/m2的量将涂布溶液涂敷到重量为170g/m2的不含木浆的纸的一个表面上，然后干燥以制备喷墨记录材料。
实施例2：
除用氯化十二烷基二甲基苄基铵60％/氯化十四烷基苄基铵40％(商品名：F2-50R，NOF CORP.的产品)代替包含于在实施例1中制备的涂布溶液中的墨固定剂氯化十四烷基二甲基苄基铵(商品名：M2-100R，NOFCORP.的产品)以外，以与实施例1中相同的方式制备喷墨记录材料。
实施例3：
除用25份的聚乙烯醇(商品名：PVA-117，Kuraray Co.，Ltd.的产品)代替在实施例1中制备涂布溶液所用的15份水溶性聚合物保护胶体型非离子丙烯酸酯共聚物(商品名：VINYBLAN 2680，Nisshin Chemical Co.，Ltd.的产品)和10份阳离子丙烯酸酯共聚物(商品名：VINYBLAN 2647，NisshinChemical Co.，Ltd.的产品)以外，以与实施例1中相同的方式制备喷墨记录材料。
实施例4：
除用100份的轻质碳酸钙(商品名：ED-111，Yonesho Lime Industry Co.，Ltd.的产品)代替用于在实施例1中制备涂布溶液的100份的湿法二氧化硅(商品名：Fine Seal X-60，Tokuyama Corp.的产品)以外，以与实施例1中相同的方式制备喷墨记录材料。
实施例5：
通过双辊施胶压榨的方式，将由20份的作为墨固定剂的氯化十二烷基二甲基苄基铵60％/氯化十四烷基二甲基苄基铵40％(商品名：F2-50R，NOF CORP.的产品)和30份的氧化淀粉(商品名：Ace A，Ohji Corn Starch的产品)组成的混合涂布溶液，以5g/m2的量涂敷在重量为170g/m2的不含木浆的纸的一个表面上，然后干燥以提供喷墨记录材料。
比较例1：
除用聚氯化二烯丙基二甲基铵(商品名：UNISENCE CP-91，SENKACORP.的产品)代替包含于在实施例1中制备的涂布溶液中的墨固定剂氯化十四烷基二甲基苄基铵(商品名：M2-100R，NOF CORP.的产品)以外，以与实施例1中相同的方式制备喷墨记录材料。
比较例2：
除用双氰胺-聚烯丙基胺的共聚物(商品名：Neofix E-117，NiccaChemical的产品)代替包含于在实施例1中制备的涂布溶液中的墨固定剂氯化十四烷基二甲基苄基铵(商品名：M2-100R，NOF CORP.的产品)以外，以与实施例1中相同的方式制备喷墨记录材料。
比较例3：
除用聚氯化二烯丙基二甲基铵(商品名：UNISENCE CP-91，SENKACORP.的产品)代替在实施例5中使用的20份的墨固定剂氯化十二烷基二甲基苄基铵60％/氯化十四烷基二甲基苄基铵40％(商品名：F2-50R，NOFCORP.的产品)以外，以与实施例5中相同的方式制备喷墨记录材料。
通过以下方法评价在以上实施例和比较例中制备的喷墨记录材料的印刷密度、吸墨和印刷耐水性。
在进行评价中，对喷墨记录材料的印刷是使用商购颜料喷墨打印机(商品名：Image PROGRAF W6200，CANON INC.的产品，印刷模式：厚涂布纸/清晰)和商购染料喷墨打印机(商品名：PIXUS ip8600，CANON INC.的产品，印刷模式：无光像片纸/清晰)进行的。
[印刷密度]
在两种型号的打印机即ImagePROGRAF W6200(使用颜料墨)和PIXUS ip8600(使用染料墨)上印刷由财团法人日本标准协会(JapaneseStandards Association)出版的图像(“高清晰度颜色数字标准图像XYZ-JIS-SCID”，识别标记：S6，图像名：Color Chart)，并且使用RD-914(Guretag Macbeth Co.的产品)对黑色的最高色调部分测量印刷密度。
[吸墨]
在视觉上评价来自在两个打印机即Image PROGRAF W6200和PIXUSip8600上的印刷边界部分的印刷吸墨。
◎：优异的水平，没有可辨认的印刷吸墨。
○：印刷有点吸墨，但是在实际使用中不产生问题。
△：印刷有点吸墨，并且在实际使用中略微产生问题。
×：显著的印刷吸墨，在实际使用中造成严重问题。
表1
| W6200(颜料墨) | ip8600(染料墨) | |||
| 黑色印刷密度 | 吸墨 | 黑色印刷密度 | 吸墨 | |
| 实施例1 | 1.56 | ○ | 1.74 | ◎ |
| 实施例2 | 1.60 | ◎ | 1.78 | ◎ |
| 实施例3 | 1.53 | ○ | 1.70 | ○ |
| 实施例4 | 1.49 | ○ | 1.68 | ○ |
| 实施例5 | 1.48 | ○ | 1.66 | ○ |
| 比较例1 | 1.41 | × | 1.59 | △ |
| 比较例2 | 1.40 | △ | 1.55 | × |
| 比较例3 | 1.32 | × | 1.45 | × |
由表1明显的是，关于使用染料墨和颜料墨印刷的图像，根据本发明的喷墨记录材料表现出很少的吸墨，并且印刷密度优良。
工业可适用性
根据本发明，如上所述，可以提供一种当用染料墨或颜料墨印刷时没有吸墨且印刷密度优良、而且允许清楚地印刷高清晰度图像的喷墨记录材料。因而，本发明的喷墨记录材料在实际应用中是非常有用的。
Claims (8)
1.一种含有基底的喷墨记录材料，所述基底的一个或两个表面具有含墨固定剂的涂层，所述喷墨记录材料的特征在于所述墨固定剂为由以下通式表示的阳离子表面活性剂：
其中R为含有8至18个碳原子的烷基。
2.一种含有基底的喷墨记录材料，所述基底的一个或两个表面具有涂层，所述涂层包含颜料、粘合剂和墨固定剂，所述喷墨记录材料的特征在于所述墨固定剂为由以下通式表示的阳离子表面活性剂：
其中R为含有8至18个碳原子的烷基。
3.根据权利要求2所述的喷墨记录材料，其中基于100质量份的所述颜料，所述涂层包含1至30质量份的所述阳离子表面活性剂和20至70质量份的所述粘合剂。
4.根据权利要求2或权利要求3所述的喷墨记录材料，其中所述粘合剂包含非离子丙烯酸酯聚合物和阳离子丙烯酸酯聚合物。
5.根据权利要求4所述的喷墨记录材料，其中所述非离子丙烯酸酯聚合物涂布有水溶性聚合物保护胶体。
6.根据权利要求5所述的喷墨记录材料，其中所述水溶性聚合物保护胶体为聚乙烯醇。
7.根据权利要求1至6中任一项所述的喷墨记录材料，其中所述基底为透气性基底。
8.根据权利要求1至6中任一项所述的喷墨记录材料，其中所述基底为非透气性基底。