CN100400572C - 聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体及制备方法 - Google Patents

聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体及制备方法 Download PDF

Info

Publication number
CN100400572C
CN100400572C CNB2005100619915A CN200510061991A CN100400572C CN 100400572 C CN100400572 C CN 100400572C CN B2005100619915 A CNB2005100619915 A CN B2005100619915A CN 200510061991 A CN200510061991 A CN 200510061991A CN 100400572 C CN100400572 C CN 100400572C
Authority
CN
China
Prior art keywords
cyanate ester
ester resin
dicyclopentadiene
polyurethane elastomer
resin modifier
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2005100619915A
Other languages
English (en)
Other versions
CN1803890A (zh
Inventor
顾嫒娟
梁国正
王结良
赵雯
张增平
王金合
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang University ZJU
Original Assignee
Zhejiang University ZJU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang University ZJU filed Critical Zhejiang University ZJU
Priority to CNB2005100619915A priority Critical patent/CN100400572C/zh
Publication of CN1803890A publication Critical patent/CN1803890A/zh
Application granted granted Critical
Publication of CN100400572C publication Critical patent/CN100400572C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体及制备方法。按重量计，是2～140份双环戊二烯型氰酸酯树脂和1～40份聚氨酯弹性体经分步熔融共聚。所制得的环氧树脂和热固性氰酸酯树脂共聚体具有高韧、高强、耐高温、优异的介电性能、和耐湿热性能。此外，所采用的分步熔融共聚法具有直接、简单、无污染、适用性广、操作工艺简单的方法。可作为胶粘剂、复合材料树脂基体、涂料、或其他聚合物的改性体。

Description

聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体及制备方法
技术领域
本发明涉及一种聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体及制备方法。
背景技术
氰酸酯树脂具有优异的介电性能、高耐热性、良好的综合力学性能以及极低的吸水率，是二十世纪以来在航空领域中极具潜力的一种功能材料和结构材料。氰酸酯树脂有多种结构，其中双环戊二烯型氰酸酯树脂因其独特的分子结构，使得其具有比常用的双酚A型氰酸酯树脂更为优异的力学、热学和介电性能。但是，与其他类型的氰酸酯树脂一样，双环戊二烯型氰酸酯树脂的固化物较脆，只有增韧改性后才具有重要的实用价值。目前关于氰酸酯的增韧改性集中在双酚A型氰酸酯树脂，所采用的方法主要有：与聚合物共聚/共混、与无机纳米粒子复合等。关于双环戊二烯型氰酸酯树脂的增韧改性研究很少，如果采用现有的增韧体系对双环戊二烯型氰酸酯树脂，可能在增韧的同时，会降低其原有的热性能、介电性能或加工性能。因此，研发一种具有高韧性、强强度、优异的耐热性及良好介电性能的双环戊二烯型氰酸酯改性体，及其一种直接、简单、无污染、适用性广、操作工艺简单的制备方法，具有重要的科学和应用意义。
发明内容
为了克服背景技术存在的问题，本发明的目的在于提供具有高韧性、强强度、优异的耐热性及良好介电性能的氨酯弹性体和双环戊二烯型氰酸酯树脂改性体及制备方法。
为达到上述目的，本发明采用的技术方案为：
一、聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体，按重量计，是2～140份双环戊二烯型氰酸酯树脂和1～40份聚氨酯弹性体经分步熔融共聚；先将1～40份双环戊二烯氰酸酯树脂和1～40份分子量为3000～5000的液体聚醚型或聚酯型聚氨酯弹性体在50～180℃熔融共聚1～3h；然后再加入1～100份双环戊二烯型氰酸酯树脂，混合均匀，即得到聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体。
二、聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体的制备方法，按重量计，先将1～40份双环戊二烯氰酸酯树脂和1～40份分子量为3000～5000的液体聚醚型或聚酯型聚氨酯弹性体在50～180℃熔融共聚1-3h然后再加入1～100份双环戊二烯型氰酸酯树脂，混合均匀，即得到聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体。
本发明与背景技术相比具有的有益效果是：所制得的环氧树脂和热固性氰酸酯树脂共聚体具有高韧、高强、耐高温、优异的介电性能、和耐湿热性能。此外，所采用的分步熔融共聚法具有直接、简单、无污染、适用性广、操作工艺简单的方法。可作为胶粘剂、复合材料树脂基体、涂料、或其他聚合物的改性体。
具体实施方式
实施例1：
按重量计，将10份液体聚醚型和10份双环戊二烯型氰酸酯在120℃熔融共聚3h；然后加入90份双环戊二烯型氰酸酯与之混合均匀，即得到聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体。
实施例2：
按重量计，将40份液体聚醚型和40份双环戊二烯型氰酸酯在50℃熔融共聚3h；然后加入100份双环戊二烯型氰酸酯与之混合均匀，即得到聚氨酯弹性体/双环戊二烯型氰酸酯树脂改性体。
实施例3：
按重量计，将1份液体聚醚型和1份双环戊二烯型氰酸酯在180℃熔融共聚1h；然后再加入1份双环戊二烯型氰酸酯与之混合均匀，即得到聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体。
实施例4：
按重量计，将10份液体聚酯型和20份双环戊二烯型氰酸酯在120℃熔融共聚3h；然后再加入50份双环戊二烯型氰酸酯与之混合均匀，即得到聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体。

Claims (2)

1.聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体，其特征在于：按重量计，是2～140份双环戊二烯型氰酸酯树脂和1～40份聚氨酯弹性体经分步熔融共聚；先将1～40份双环戊二烯氰酸酯树脂和1～40份分子量为3000～5000的液体聚醚型或聚酯型聚氨酯弹性体在50～180℃熔融共聚1～3h然后再加入1～100份双环戊二烯型氰酸酯树脂，混合均匀，即得到聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体。
2.聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体的制备方法，其特征在于：按重量计，先将1～40份双环戊二烯氰酸酯树脂和1～40份分子量为3000～5000的液体聚醚型或聚酯型聚氨酯弹性体在50～180℃熔融共聚1～3h；然后再加入1～100份双环戊二烯型氰酸酯树脂，混合均匀，即得到聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体。
CNB2005100619915A 2005-12-14 2005-12-14 聚氨酯弹性体和双环戊二烯型氰酸酯树脂改性体及制备方法 Expired - Fee Related CN100400572C (zh)