CN102702731A - 一种可化学电镀高光泽汽车门把手用玻璃纤维增强尼龙材料 - Google Patents
一种可化学电镀高光泽汽车门把手用玻璃纤维增强尼龙材料 Download PDFInfo
- Publication number
- CN102702731A CN102702731A CN2012101975777A CN201210197577A CN102702731A CN 102702731 A CN102702731 A CN 102702731A CN 2012101975777 A CN2012101975777 A CN 2012101975777A CN 201210197577 A CN201210197577 A CN 201210197577A CN 102702731 A CN102702731 A CN 102702731A
- Authority
- CN
- China
- Prior art keywords
- parts
- door handle
- nylon
- glaze
- glass fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于高分子复合材料领域，公开了一种可化学电镀高光泽汽车门把手用玻璃纤维增强尼龙材料，按照重量份计该材料包括以下组份：基础尼龙树脂60~100份，玻璃纤维20~50份，抗冲击剂3~10份，润滑剂0.3~0.5份，导电改性剂0.1-0.5份；其中所述基础尼龙树脂为非结晶共聚尼龙Novamipx21和PA3460的混合物，二者之间的重量比为1:2~2:3。本发明制备的材料拥有良好的力学性能、防紫外线性能，表面光泽度高，可免喷漆；且该材料可化学电镀铜。使用该材料制备汽车门把手，光泽度好，美观，且能够节省生产工艺和成本。
Description
技术领域
本发明属于高分子复合材料领域，涉及一种可化学电镀高光泽汽车门把手用玻璃纤维增强尼龙材料。
背景技术
塑料零件具有重量轻、加工容易、光洁度高、不会锈蚀、节约金属和降低成本等优点，但也存在着不导电、没有金属光泽等不足之处。塑料经过电镀后就能使表面出现金属光泽，也能够导电、导磁和焊接，从而扩大了塑料零件的应用范围。塑料进行电镀，首先要进行金属化处理，使其表面有一层导电层。目前电镀效果较好的工程塑料为ABS与PC/ABS，ABS塑料电镀后的结合力较好。当浸入粗化液中进行粗化时，ABS塑料中的“B”组份—丁二烯被粗化液溶蚀，生成无数个孔穴(一般达6万个每平方米)，经过敏化、活化、还原、无电解镀、电镀等工序后，金属镀层能牢固地“投锚”在这无数的孔穴内，使镀层与塑料表面紧密地结合在一起。
尼龙是一种半硬质塑料，质地坚韧，有较好的机械性能，特别是耐冲击性能是其他塑料不可比拟的。此外，尼龙还具有优良的耐化学腐蚀性、电性能，成型加工方便等优点。但尼龙作为结构件，由于它蠕变性大，耐热性低，收缩率大，尺寸稳定性差，这就限制了尼龙的使用范围。用玻璃纤维增强后其力学性能、热性能显著提高，特别是拉伸强度和弯曲强度成倍增长，因而应用于国民经济各部门，特别是近年来广泛应用于汽车行业。但是用普通尼龙制备的门把手光泽度非常低，且化学电镀时粗化液与PA塑料表层结合力不强，无法得到良好的表观。后期进行喷漆等处理才能保证门把手的光泽度，并使门把手拥有良好的耐热、耐紫外、耐盐雾等性能。
为了达到良好的化学电镀性能，有很多研究者对PA电镀工艺的进行调整，但效果仍然不明显，本发明专利从材料本身进行开发，达到良好的电镀效果。
发明内容
本发明的目的就是克服现有技术的不足，提供一种可化学电镀高光泽汽车门把手用玻璃纤维增强尼龙材料，采用该材料制备的门把手表面电镀后光泽优异，可免喷漆处理，同时具备良好的阻隔性能。
为实现上述目的，本发明采取的技术方案为：一种可化学电镀高光泽汽车门把手用玻璃纤维增强尼龙材料，按照重量份该材料包括以下组份：
基础尼龙树脂 60~100份
玻璃纤维 20~50份
抗冲击剂 3~10份
润滑剂 0.3~0.5份
导电改性剂 0.1-0.5份
所述基础尼龙树脂为非结晶共聚尼龙Novamipx21 和PA3460的混合物，二者之间的重量
比为1:2~2:3；
所述玻璃纤维直径为10~15μm，经硅烷偶联剂表面处理；
所述抗冲击剂为POE-g-MAH或硅橡胶类材料；
所述润滑剂为硅酮、EBS、硅油中的一种或几种；
所述导电改性剂为导电炭黑或导电玻璃粉中的一种或几种。
本发明制备方法如下：
（1）首先将基础尼龙树脂干燥，再按配方重量份精确称量基础尼龙树脂、抗冲击剂、润滑剂、导电改性剂。
（2）将精确称量的各组分倒入高速混合机中进行搅拌3-5分钟，使各组分充分分散均匀。（3）将混合好的物料加入带9段温控区的双螺杆挤出机，基础尼龙树脂等从主喂料口加
入，玻璃纤维从侧喂料口加入。控制挤出机螺杆转速为230-320r/min，喂料转速控制在15-25r/min，切粒机转速为400-800r/min。其中9段温控区的温度分别为1区150-170℃，2区220-240℃，3至5区250-270℃，6至9区260-275℃，机头温度为265-270℃。
（4）对双螺杆挤出机挤出的物料进行冷却、风干、造粒。
本发明的有益效果：
（1）基础树脂采用Novamipx21 和PA3460的混合物， Novamip X21为非结晶性尼龙树脂，具有较高的玻璃化温度，机械性能稳定，吸水性低，氧阻隔性好；PA3460表面活性强，因此制备的材料拥有良好的力学性能、防紫外性能，且表面光泽度高，可免喷漆，节省了生产工艺和成本。
（2）目前PA类材料无法进行化学电镀，本发明通过选用特殊PA及添加导电改性剂，使得材料可化学电镀铜。
具体实施方式
下面结合实施例对本发明做进一步详细说明。
实施例1
| 组份 | Novamipx21 | PA3460 | 玻璃纤维 | 抗冲击剂 | 润滑剂 | 导电改性剂 |
| 含量（份） | 20 | 40 | 20 | 3 | 0.3 | 0.2 |
实施例2
| 组份 | Novamipx21 | PA3460 | 玻璃纤维 | 抗冲击剂 | 润滑剂 | 导电改性及 |
| 含量（份） | 23 | 42 | 30 | 5 | 0.4 | 0.4 |
实施例3
| 组份 | Novamipx21 | PA3460 | 玻璃纤维 | 抗冲击剂 | 润滑剂 | 导电改性剂 |
| 含量（份） | 23 | 42 | 35 | 6 | 0.4 | 0.3 |
实施例4
| 组份 | Novamipx21 | PA3460 | 玻璃纤维 | 抗冲击剂 | 润滑剂 | 导电改性剂 |
| 含量（份） | 40 | 60 | 50 | 10 | 0.5 | 0.4 |
将上述实施例制备的材料，挤出造粒后的材料干燥后，制作成标准样条进行性能测试，测试结果见下表：
| 组份 | 实施例1 | 实施例2 | 实施例1 | 实施例2 |
| 拉伸强度（MPa） | 166 | 182 | 187 | 183 |
| 弯曲强度（MPa） | 245 | 260 | 263 | 262 |
| 摩擦系数 | 0.14 | 0.12 | 0.10 | 0.11 |
| 电镀后表观性能 | 良好 | 良好 | 良好 | 良好 |
Claims (2)
1.一种可化学电镀高光泽汽车门把手用玻璃纤维增强尼龙材料，其特征在于，按照重量份计该材料包括以下组份：基础尼龙树脂60~100份，玻璃纤维20~50份，抗冲击剂3-10份，润滑剂0.3-0.5份，导电改性剂0.1-0.5份；
所述基础尼龙树脂为非结晶共聚尼龙Novamipx21 和PA3460的混合物，二者之间的重量份比为1:2~2:3。
2.根据权利要求1所述的可化学电镀高光泽汽车门把手用玻璃纤维增强尼龙材料，其特征在于所述玻璃纤维直径为10~15μm，经硅烷偶联剂表面处理。