CN100357357C - 水溶性聚合组合物 - Google Patents
水溶性聚合组合物 Download PDFInfo
- Publication number
- CN100357357C CN100357357C CNB988110199A CN98811019A CN100357357C CN 100357357 C CN100357357 C CN 100357357C CN B988110199 A CNB988110199 A CN B988110199A CN 98811019 A CN98811019 A CN 98811019A CN 100357357 C CN100357357 C CN 100357357C
- Authority
- CN
- China
- Prior art keywords
- polymkeric substance
- polymer
- group
- water
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
A聚合物 | %STY/AMA/AA | Mn | Mw | Mz | Fn | Fw | 酸值 | Tg(开始点/中间点) |
1 | 22/45/33 | 1060 | 1607 | 2360 | 5.08 | 7.71 | 267 | 75/81 |
2 | 22/45/33 | 1180 | 1810 | 2700 | 5.72 | 8.78 | 266 | 79/85 |
3 | 13/55/32 | 988 | 1459 | 2124 | 4.74 | 265 | 77/85 | |
4 | 22/45/33 | 1003 | 1512 | 2231 | 4.72 | 7.12 | 264 | 73/83 |
STY-苯乙烯AMS-α-甲基苯乙烯AA-丙烯酸 |
B聚合物 | 组合物 | 摩尔比率 | Mn | Mw | Mz | Tg(开始点/中间点) |
1 | MpDiol/异邻苯二甲酸/CHDA | 10/6/3 | 3023 | 6486 | 10720 | 8/14 |
2 | Esterdiol 204/异邻苯二甲酸 | 4/3 | 1294 | 1975 | 2893 | 1/6 |
3 | CHDA/壬二酸 | 7/6 | 2695 | 5756 | 9556 | -48/-42 |
4 | 新戊基乙二醇/马来酸酐/己二酸 | 13/3/9 | 2432 | 4851 | 8347 | -40/-37 |
5 | Esterdiol 204/CHDM/异邻苯二甲酸 | 5/3/7 | 2332 | 4452 | 7055 | 25/31 |
6 | 同上(5%过量的乙二醇) | 5/3/7 | 2427 | 4442 | 6958 | 24/29 |
CHDA-1,4-环己烷二羧酸CHDM-1,4-环己烷二甲醇MpDiol-2-甲基-1,3-丙二醇,从PA,Newton Square ARCO化学购得Esterdiol 204-从CT,Danbury,联合碳化物购得 |
实例 | A聚合物 | B聚合物 | 摩尔比率B/A | %B | 酸值 | Mn | Mw | Mz | Tg℃开始点/中间点 |
2 | 3 | 2 | 1/2 | 40 | 140 | 1655 | 4261 | 9619 | 40/51 |
3 | 1 | 3 | 1/2 | 48 | 116 | 2618 | 16770 | 62610 | 5/17 |
4 | 1 | 4 | 1/2 | 55 | 116 | 2824 | 95260 | 864200 | -2/8 |
5 | 1 | 5 | 1.2/2 | 58 | 102 | 2345 | 8378 | 20450 | 47/56 |
6 | 1 | 6 | 1.2/2 | 58 | 93 | 2723 | 11550 | 33320 | 48/56 |
7 | 1 | 1 | 1/2 | 59 | 102 | 2715 | 20440 | 91990 | 40/45 |
8 | 1 | 1 | 1.25/2 | 65 | 72 | 3719 | 36310 | 382800 | 22/27 |
9 | 2 | 1 | 1.25/2 | 62 | 83 | 3008 | 23000 | 102900 | 31/40 |
10 | 2 | 1 | 1.4/2 | 65 | 72 | 3845 | 44700 | 234800 | 21/31 |
11 | 2 | 1 | 1.62/2 | 69 | 62 | 4327 | 139300 | 4015000 | 19/28 |
12 | 1 | * | 1/3 | 34 | 148 | 2318 | 207000 | 2327000 | 3/19 |
*Tone 1320 triol-聚己酸内酯多羟基化物从CT,Danbury,联合碳化物购得mp-中间点 |
A聚合物 | 组合物 | 官能团 | AV* | Mn | Mw | Tg | FN |
I | 苯乙烯丙烯酸a | 羧基 | 277 | 923 | 1637 | 45 | 4.56 |
II | 苯乙烯丙烯酸b | 羧基 | 269 | 1116 | 1779 | 67 | 5.35 |
III | STY/AA | 羧基 | 289 | 1000 | 1526 | 65 | 5.15 |
IV | STY/AMS/AA | 羧基 | 264 | 1003 | 1512 | 71 | 4.72 |
V | MMA/AA | 羧基 | 339 | 1121 | 1753 | 36 | 6.77 |
VI | C-1,4α-石蜡MAn | 酐 | 2327 | 7.9 | |||
VII | STY/MMA/GMA | 环氧基 | 2200 | 3.8 | |||
VIII | 丙烯酸C | 羟基 | 1400 | 3.5 | |||
IX | MMA/BA/HEA | 羟基 | 1180 | 5.28 | |||
Joncryl 682从威斯康星州Sturtevant SC.Johnson聚合物购得Morez 300从伊利诺斯州芝加哥,Morton国际购得Joncyl 569从SC.Johnson聚合物购得酸值根据聚合物固体颗粒获得STY-苯乙烯;AA-丙烯酸;AMS-α甲基苯乙烯;MMA-甲基甲基丙烯酸酯;MAn-马来酸酐;GMA-glycidal甲基丙烯酸酯;BA-丁基丙烯酸酯;HEA-羟基乙基丙烯酸酯 |
B聚合物 | 组合物 | 官能团 | Mn | FN |
I | 线性聚酯a | 1羟基 | 1000 | 2 |
II | 枝化聚酯b | 1羟基 | 900 | 3 |
II | 线性聚酯 | 羧基 | 1700 | 2 |
IV | 线性聚氨酯 | 异氰酸根合 | 2500 | 2 |
V | 线性二聚物酸聚酰胺 | 1氨基 | 4028 | 2 |
VI | 线性二聚物酸聚酰胺 | 恶唑啉基 | 3776 | 2 |
VII | 线性己二酸尼龙 | 1氨基 | 1020 | 2 |
VIII | 线性聚丙烯乙二醇c | 2羟基 | 425 | 2 |
IX | 环氧树脂d | 环氧基 | 600 | 2 |
X | 聚醚二胺e | 1氨基 | 600 | 2 |
Rucoflex 1015-120从纽约州Hicksville,RUCO聚合物公司购得Tone 0310从康涅狄格州Danbury联合碳化物公司购得聚乙二醇P425从密歇根州Midland,Dow化学公司购得EPON836从德克萨斯州Houston壳牌化学公司购得Jeffamine ED 600从德克萨斯州Houston Huntsman公司购得 |
实例No. | A聚合物 | B聚合物 | 摩尔比率A∶B | Wt.%B | Mn | Mw | Mz | 开始点Tg | 末端官能团 |
I | I | II | 3∶1 | 23 | 1703 | 9566 | 36210 | 18 | 153AV |
II | I | I | 2∶1 | 29 | 1751 | 7506 | 22840 | -6 | 143AV |
III | I | VI | 2∶1 | 66 | 2087 | 8369 | 22420 | ND | 70AV |
IV | I | V | 2∶1 | 71 | 2982 | 11810 | 22430 | ND | 55AV |
V | VIII | III | 2∶1 | 38 | 2609 | 62120 | 1714000 | ND | ND |
VI | IV | VII | 2∶1 | 34 | ND | ND | ND | 76 | 140AV |
VII | V | VIII | 2∶1 | 16 | 1699 | 5996 | 18760 | 26 | 250AV |
VIII | I | VIII | 2∶1 | 18 | 1292 | 3194 | 6696 | 26 | 176AV |
IX | II | VIII | 2∶1 | 16 | 1534 | 4401 | 11220 | 38 | 173AV |
X | III | IV | 2∶1 | 56 | 1385 | 4228 | 9618 | ND | ND |
XI | VII | III | 2∶1 | 33 | 2288 | 5590 | 10150 | ND | ND |
XII | IX | IV | 2∶1 | 53 | 2646 | 6411 | 17290 | -29 | ND |
XIII | VI | X | 2∶1 | 12 | ND | ND | ND | ND | 300AV |
XIV | IV | IX | 2∶1 | 24 | 1485 | 5609 | ND | ND | 155AV |
ND=未确定;AV=酸值 |
组成 | 研磨树脂(Grind)-C | 研磨树脂(Grind)-1 | 研磨树脂(Grind)-2 |
亚丙基乙二醇 | 21.6 | ||
水 | 45.8 | ||
分散剂 DSP-C | 1.6 | ||
分散剂DSP-4 | 166.7 | ||
分散剂DSP-5 | 142.9 | ||
Triton CF-10 | 2.5 | ||
Proxel GXL | 0.5 | ||
氢氧化铵 | 0.7 | 0.7 | 0.7 |
Dehydran 1620 | 0.6 | 0.6 | 0.6 |
DSX-1550 | 0.5 | ||
R-706 TiO2 | 250 | 250 | 250 |
水 | 5.0 | 10.0 | 8.5 |
丁基溶纤剂 | 7.5 | ||
非挥发物% | 7.2 | 70.1 | 71.4 |
Triton CF-10是分散剂从宾夕法尼亚州费城Rhom&Hass购得Proxel GXL是防腐剂从特拉华州Wilmington ICI购得Dehydran 1620+DSX-1550是增稠剂从宾夕法尼亚州Amber,Henke购得R-706 TiO2是色料从特拉华州Wilmington DuPont de Nemours&公司购得所有数值以克为单位,除非另外指出 |
ADD-CM-1 | ADD-1 | ADD-2 | ADD-CM-2 | ADD-3 | ADD-4 | |
乳胶 | SCX-1520 | SCX-1520 | SCX-1520 | J-77 | J-77 | J-77 |
固体粒子% | 41.5 | 41.5 | 41.5 | 46.0 | 46.0 | 46.0 |
研磨树脂(Grind)I.D. | C | 1 | 2 | C | 1 | 2 |
研磨树脂(Grind)量 | 40.0 | 40 | 40 | 40.0 | 52.0 | 50.0 |
乳胶量 | 115.6 | 115.6 | 115.6 | 113.0 | 113.0 | 113.0 |
搅拌加入Texanol@6% | 4.2 | 4.2 | 4.2 | 4.2 | 4.2 | 4.2 |
5%亚硝酸钠 | 2.2 | 2.2 | 2.2 | 2.2 | 2.2 | 2.2 |
DSX1514 50%水溶液 | 1.0 | 1.0 | 1.0 | 1.0 | 1.0 | 1.0 |
总量 | 172.7 | 172.7 | 172.7 | 160.4 | 172.4 | 170.4 |
调配前固体粒子% | 48.4 | 48.4 | 48.4 | 52.1 | 53.8 | 53.5 |
DSX1514-增稠剂从PA,Amber,Henkel购得Texanol-酯溶剂从TN,Kingsport Eastman化学购得 |
光泽度 | Wspot24h干燥Sw/SftBl/颜色 | MEK/7 | K1 | K7 | DFT | FR | Crp | Blst | ||||
20 | 60 | 20 | 60 | |||||||||
3天 | 7天 | |||||||||||
ADD-CM-1 | 73 | 90 | 72 | 90 | 6/4/10/10 | 13/13 | 26 | 41 | 1-1.4 | 1 | 1/16 | 6D |
ADD-1 | 71 | 88 | 70 | 88 | 10/3/6D/10 | 11/21 | 52 | 54 | “ | 1 | 1/16 | 6D |
ADD-2 | 60 | 85 | 61 | 85 | 8/10/10/10 | 15/29 | 43 | 49 | “ | 1 | 1/16 | 6D |
ADD-CM-2 | 83 | 94 | 80 | 92 | 7/4/10/10 | 10/19 | 14 | 23 | “ | 1 | 1/8 | 6D |
ADD-3 | 16 | 57 | 16 | 56 | 10/4/4MD/10 | 8/25 | 23 | 27 | “ | 1 | 1/8 | 6D |
ADD-4 | 67 | 89 | 67 | 88 | 9/3/2F/10 | 11/22 | 25 | 30 | “ | 1 | 1/8 | 6D |
Wspot=水斑试验;Sw=溶胀;Sft=软化;Bl=起泡MEK=抗甲基乙基酮摩擦试验DFT=干膜厚度FR=表面锈蚀Crp=蠕变Rlst=起泡率 |
24小时汽油 | 24小时去离子水 | |||||||
sw | s | bl | clr | sw | s | bl | clr | |
ADD-CM-1 | 8 | 0 | 10 | 8 | 9 | 9 | 10 | 9 |
ADD-1 | 9 | 0 | 10 | 9 | 9 | 9 | 8VF | 10 |
ADD-2 | 9 | 0 | 10 | 8 | 8 | 8 | 10 | 10 |
ADD-CM-2 | 10 | 1 | 10 | 9 | 9 | 5 | 10 | 5 |
ADD-3 | 10 | 1 | 10 | 9 | 9 | 6 | 10 | 8 |
ADD-4 | 10 | 1 | 10 | 9 | 9 | 6 | 4F | 7 |
Sw=溶胀 VF=很少S=软化 F=少Bl=起泡Clr=颜色 |
24小时5%硫酸 | 24小时盐酸 | |||||||
sw | s | bl | clr | sw | s | bl | clr | |
ADD-CM-1 | 10 | 10 | 10 | 10 | 9 | 4 | 10 | 10 |
ADD-1 | 10 | 10 | 10 | 10 | 9 | 6 | 10 | 10 |
ADD-2 | 10 | 10 | 10 | 10 | 9 | 8 | 10 | 10 |
ADD-CM-2 | 10 | 8 | 10 | 10 | 9 | 1 | 10 | 10 |
ADD-3 | 10 | 9 | 10 | 10 | 10 | 2 | 10 | 8 |
ADD-4 | 10 | 10 | 10 | 10 | 9 | 9 | 10 | 10 |
Sw=溶胀S=软化Bl=起泡Clr=颜色 |
24小时制动液 | 24小时Formula 409 | |||||||
sw | s | bl | clr | sw | s | bl | clr | |
ADD-CM-1 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
ADD-1 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
ADD-2 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
ADD-CM-2 | 0 | 0 | 0 | 0 | 10 | 3 | 10 | 10 |
ADD-3 | 0 | 0 | 0 | 0 | 10 | 7 | 10 | 10 |
ADD-4 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
Sw=溶胀S=软化Bl=起泡Clr=颜色 |
24小时异丙醇 | 24小时氢氧化钠 | |||||||
sw | s | bl | clr | sw | s | bl | clr | |
ADD-CM-1 | 10 | 10 | 10 | 10 | 10 | 10 | 8MD | 10 |
ADD-1 | 10 | 10 | 10 | 10 | 10 | 10 | 8D | 10 |
ADD-2 | 10 | 10 | 10 | 10 | 10 | 10 | 8F | 9 |
ADD-CM-2 | 10 | 7 | 10 | 10 | 9 | 3 | 8D | 8 |
ADD-3 | 10 | 10 | 10 | 10 | 10 | 5 | 10 | 9 |
ADD-4 | 10 | 10 | 10 | 10 | 0 | 0 | 0 | 0 |
Sw=溶胀 D=密集S=软化 F=少Bl=起泡 MD=中等密集Clr=颜色 |
样品ID | WBC-1 | WBC-2 | WBC-3 | WBC-CM-1 |
聚合组合物 | 实例15 | 实例15 | 实例14 | Joncryl 77 |
其他 | 氢氧化铵 | 氢氧化铵 | 氢氧化铵 | |
20%TEA | 10%TEA | |||
乳胶 | (所有树脂溶液-非乳胶) | |||
树脂含量% | 100 | 100 | 100 | |
PH | 9.92 | 9.66 | 9.5 | 8.3 |
粘度-厘泊 | 800 | 100 | 100 | 510 |
非挥发物% | 30 | 30.10 | 30 | 46 |
加水% | 11% | 无 | 12% | 10 |
粘度-厘泊 | 110 | 100 | 110 | 85 |
非挥发物% | 26.7 | 30.1 | 26.4 | 41.8 |
抗化学物质性能 | ||||
用K-涂漆机#1@6在n2a leneta板料上滴涂 | ||||
所有样品干燥2分钟@RT/1分钟@140 F-16小时后测试 | ||||
润湿性 | 4 | 3 | 3.5 | 4 |
流平性 | 3.5 | 3 | 3 | 3.5 |
不下渗性 | 3 | 2.5 | 2.5 | 2.5 |
60光泽度 | ||||
黑 | 71.1 | 71.1 | 69.3 | 71.5 |
白 | 44.4 | 36.5 | 38.2 | 27 |
抗水性 | ||||
1分钟点滴测试 | 5 | 5 | 5 | 5 |
5分钟点滴测试 | 5 | 5 | 5 | 5 |
10分钟点滴测试 | 5 | 5 | 5 | 5 |
30分钟点滴测试 | 5 | 5 | 5 | 5 |
抗5%氢氧化钠 | ||||
1分钟点滴测试 | 4 | 4 | 4 | 3 |
5分钟点滴测试 | 3.5 | 3.5 | 3.5 | 2.5 |
10分钟点滴测试 | 3 | 3 | 2 | 2 |
30分钟点滴测试 | 1 | 1 | 1 | 1.5 |
抗IPA/水(1/1) | ||||
1分钟点滴测试 | 5 | 5 | 5 | 5 |
5分钟点滴测试 | 5 | 5 | 5 | 5.0* |
10分钟点滴测试 | 5 | 5.0* | 5 | 4.0* |
30分钟点滴测试 | 4 | 4.0* | 3.5 | 3.5* |
乙醇/水(1/1) | ||||
1分钟点滴测试 | 5 | 5 | 5 | 5 |
5分钟点滴测试 | 5 | 5 | 5 | 5 |
10分钟点滴测试 | 5 | 5 | 4 | 4 |
30分钟点滴测试 | 5 | 5 | 4 | 3.0* |
409清洁剂 | ||||
1分钟点滴测试 | 3 | 3 | 3 | 3 |
5分钟点滴测试 | 2.5 | 2.5 | 2.5 | 2.5 |
10分钟点滴测试 | 2 | 2 | 2 | 2 |
30分钟点滴测试 | 1.5 | 1.5 | 1.5 | 1.5 |
*膜变白 | ||||
用K-涂漆机#1@10在涂墨10 pt.Tech service板料上滴涂 | ||||
所有样品干燥2分钟@RT/1分钟@140 F-16小时后测试 | ||||
润湿性 | 4 | 4 | 4 | 4 |
流平性 | 3.5 | 3.5 | 3.5-4 | 3.4 |
不下渗性 | 4 | 4 | 4 | 4 |
60光泽度 | ||||
AVE of 5 | 36.6 | 38.8 | 39.2 | 36.6 |
温度/相对湿度 | 70/50% | 70/50% | 70/50% | 70/50% |
静态摩擦角 | ||||
JEM-3.5#SLED | 32.7/32.6 | 30.6/32.1 | 27.8/30.6 | 30.1/32.8 |
表面/表面 | 33.0/32.2 | 31.3/32.2 | 33.2/33.6 | 33.2/33.6 |
1 ST 5读数 | 33.2-32.5 | 31.2=31.5 | 33.1=31.7 | 30.4=32.0 |
AOS偏差涂布 | 0.8 | 1.6 | 5.8 | 3.5 |
Sutherland摩擦表面/表面w/4#SLED | ||||
100个周期 | 1.5 | 1.5 | 1.5 | 1.5 |
200个周期 | 0.5 | 0.5 | 0.5 | 1 |
抗粘连性 | ||||
140 F/125 PSI/16 HRS | ||||
表面/表面-干燥 | 2.5 | 2.5 | 4 | 3 |
水测试-1滴 | ||||
表面/表面-湿表面 | 0 | 0 | 0 | 0.5 |
表面/表面-湿背表面 | 0 | 0 | 0 | 0 |
Joncryll 77-是苯乙烯丙烯酸乳胶从威斯康星州,struevant,S.C.Johnson聚合物购得 |
实例 | WBC-4 | WBC-5 | WBC-6 |
固体粒子(wt%) | 27 | 27 | 25 |
粘度(厘泊) | 42 | 24 | 12.5 |
光泽度(黑) | 76 | 78 | 80 |
(白) | 72 | 75 | 71 |
抗化学物质性能 | |||
水 | 5.0 | 5.0 | 5.0 |
氢氧化钠5%水溶液 | 0.9 | 0.9 | 2.4 |
IPA50%水溶液 | 4.0 | 2.3 | 5.0 |
EtOH 50%水溶液 | 4.0 | 2.0 | 5.0 |
409清洁剂# | 0.8 | 1.0 | 1.5 |
摩擦角 | |||
度 | 42 | 34 | 粘着 |
(涂布) | 4.2 | 1.4 | - |
抗摩擦性能 | |||
100个周期 | 1.5 | 1.0 | 粘着 |
200个周期 | 1.0 | .05 | 粘着 |
抗粘连性能 | |||
干燥 | 1.0 | 4.0 | 粘着 |
润湿(表面) | 0 | 0 | 粘着 |
润湿(背表面) | 0 | 0 | 粘着 |
测试区域变白*409清洁剂是醇基清洁剂从CA,Oakland,Clorox公司购得 |
实例号No. | 对聚丙烯的粘合力(成功/失败) | |
34达因/cm, | 42达因/cm | |
DC1 | 失败 | 成功 |
DC2 | 成功 | 成功 |
DC3 | 成功 | 成功 |
DC4 | 失败 | 成功 |
样品ID | OPV-CM-1 | OPV-1 | OPV-2 | OPV-3 | OPV-4 |
树脂类型 | Joncryl 77 | EP1 | EP2 | EP3 | EP4 |
树脂含量% | 25 | 25 | 20 | 30 | |
PH | 8.3 | 9.04 | 9.45 | 9.36 | 9.52 |
粘度-厘泊 | 510 | 52 | 200 | 210 | 45 |
非挥发物% | 46 | 45.3 | 45.2 | 45 | 42.4 |
加水% | 10 | 无 | 3.50% | 3.00% | 无 |
粘度-厘泊 | 85 | 52 | 110 | 100 | 45 |
非挥发物% | 41.8 | 45.3 | 43.6 | 43.7 | 42.4 |
抗化学物质性能 | |||||
用K涂漆机#1@6滴涂在N2A LENETA板料上 | |||||
样品干燥2分钟@RT/1分钟@140 F-16小时后测试 | |||||
润湿性 | 4 | 4 | 3.5 | 2.5 | 3.5 |
流平性 | 3.5 | 3.5 | 3.5 | 3.5 | 3 |
不下渗性 | 2.5 | 2.5 | 2 | 2.5 | 2.5 |
60光泽度 | |||||
黑 | 71.5(83) | 74.7 | 74.5 | 77.6 | 78.1 |
白 | 27(34) | 28.7 | 23.9 | 31.3 | 30 |
抗水性 | |||||
1分钟点滴试验 | 5 | 5 | 5 | 5 | 5 |
5分钟点滴试验 | 5 | 5 | 5 | 5 | 5 |
10分钟点滴试验 | 5 | 5 | 5 | 5 | 5 |
30分钟点滴试验 | 5 | 5 | 5 | 5 | 5 |
5%氢氧化钠 | |||||
1分钟点滴试验 | 3 | 3.5 | 4 | 4 | 4.5 |
5分钟点滴试验 | 2.5 | 3 | 3.5 | 3.5 | 4 |
10分钟点滴试验 | 2 | 1.5 | 2 | 2 | 2 |
30分钟点滴试验 | 1.5 | 1 | 1 | 1 | 1 |
IPA/水(1/1) | |||||
1分钟点滴试验 | 5 | 5.0* | 5.0* | 5 | 5 |
5分钟点滴试验 | 5.0* | 5.0* | 5.0* | 5.0* | 5.0* |
10分钟点滴试验 | 4.0* | 5.0* | 4.0* | 5.0* | 5.0* |
30分钟点滴试验 | 3.5* | 4.0* | 3.5* | 5.0* | 5.0* |
乙醇/水(1/1) | |||||
1分钟点滴试验 | 5 | 5 | 5 | 3 | 5 |
5分钟点滴试验 | 5 | 5.0* | 5 | 5 | 5 |
10分钟点滴试验 | 4 | 4.0* | 5 | 4 | 4 |
30分钟点滴试验 | 3.0* | 3.5* | 3.5 | 3.5 | 3.5 |
409清洁剂 | |||||
1分钟点滴试验 | 3 | 3 | 3 | 4 | 3.5 |
5分钟点滴试验 | 2.5 | 2.5 | 2.5 | 3 | 3 |
10分钟点滴试验 | 2 | 2 | 2 | 2.5 | 2 |
30分钟点滴试验 | 1.5 | 1.5 | 1.5 | 1.5 | 1.5 |
*膜变白 | |||||
用K涂漆机#1@10滴涂在涂墨10pt.Tech Service板料上 | |||||
样品干燥2分钟@RT/1分钟@140 F-16小时后测试 | |||||
润湿性 | 4 | 4 | 3.5 | 3.5 | 4 |
流平性 | 3.5 | 3 | 3 | 3 | 3 |
不下渗性 | 4 | 4 | 4 | 4 | 4 |
60光泽度 | |||||
AVE OF 5 | 36.6 | 32.8 | 29.6 | 34.2 | 33.8 |
温度/相对湿度 | 70/50% | 70/50% | 70/150% | 70/150% | 70/150% |
静态摩擦角 | |||||
JEM-3.5#SLED | 30.1/32.8 | 33.1/36.1 | 36.1/38.2 | 34.0/31.8 | 38.7/41.4 |
表面/表面 | 33.2/33.6 | 40.9/40.3 | 44.4/38.8 | 34.2/32.2 | 41.6/39.5 |
1 ST 5读数 | 30.4-32.0 | 39.4-38.0 | 44.7-41.4 | 32.9-33.0 | 40.4-40.3 |
AOS偏差涂布 | 3.5 | 7.8 | 8.6 | 2.4 | 2.9 |
Sutherland摩擦 | |||||
表面/表面/w/4#SLED | |||||
100个周期 | 1.5 | 2.5 | 2.5 | 2.5 | 2.5 |
200个周期 | 1 | 1.5 | 1.5 | 1.5 | 1 |
抗粘连性能 | |||||
140F/125PSI/16小时 | |||||
表面/表面-干 | 3 | 1.5 | 2 | 1.5 | 1.5 |
水试验-1滴 | |||||
表面/表面-湿 | 0.5 | 0 | 0 | 0 | 0 |
表面/背表面-湿 | 0 | 0 | 0 | 0 | 0 |
样品ID | OPV-5 | OPV-6 | OPV-7 |
树脂类型 | EP3 | EP5 | EP6 |
树脂含量% | 30 | 30 | 25 |
PH | 9.46 | 9.2 | 9.1 |
粘度-厘泊 | 40 | 140 | 95 |
非挥发物% | 40 | 40.2 | 45.2 |
加水% | 无 | 1.50% | 无 |
粘度-厘泊 | 40 | 110 | 95 |
非挥发物% | 40 | 39.6 | 45.2 |
抗化学物质性能 | |||
用K涂漆机#1@6滴涂在N2A LENETA板料上 | |||
样品干燥2分钟@RT/1分钟@140F-16小时后测试 | |||
润湿性 | 4 | 3 | 3.5 |
流平性 | 3.5 | 3 | 3 |
不下渗性 | 2.5 | 2.5 | 2.5 |
60光泽度 | |||
黑 | 78.2 | 74 | 71.8 |
白 | 36 | 34.3 | 27.8 |
抗水性 | |||
1分钟点滴试验 | 5 | 5 | 5 |
5分钟点滴试验 | 5 | 5 | 5 |
10分钟点滴试验 | 5 | 5 | 5 |
30分钟点滴试验 | 5 | 5 | 5 |
5%氢氧化钠 | |||
1分钟点滴试验 | 4 | 4 | 4.5 |
5分钟点滴试验 | 3.5 | 3.5 | 3.5 |
10分钟点滴试验 | 2.5 | 2.5 | 2.5 |
30分钟点滴试验 | 1.5 | 1 | 1 |
IPA/水(1/1) | |||
1分钟点滴试验 | 5.0* | 5.0* | 5 |
5分钟点滴试验 | 5.0* | 5.0* | 5.0* |
10分钟点滴试验 | 5.0* | 4.0* | 5.0* |
30分钟点滴试验 | 4.0* | 3.5* | 4.0* |
乙醇/水(1/1) | |||
1分钟点滴试验 | 5 | 5 | 5 |
5分钟点滴试验 | 5 | 5.0* | 5.0* |
10分钟点滴试验 | 5 | 5.0* | 5.0* |
30分钟点滴试验 | 4 | 4.0* | 3.5* |
409清洁剂 | |||
1分钟点滴试验 | 3 | 3 | 3 |
5分钟点滴试验 | 2.5 | 2.5 | 2.5 |
10分钟点滴试验 | 2 | 2 | 2 |
30分钟点滴试验 | 1.5 | 1.5 | 1.5 |
*膜变白 | |||
用K涂漆机#1@10滴涂在涂墨10pt.Tech Service板料上 | |||
样品干燥2分钟@RT/1分钟@140 F-16小时后测试 | |||
润湿性 | 3.5 | 4 | 4 |
流平性 | 3 | 3.5 | 3.5 |
不下渗性 | 4 | 4 | 3.5 |
60光泽度 | |||
AVE OF 5 | 34.6 | 35.2 | 29.2 |
温度/相对湿度 | 70/150% | 70/150% | 70/150% |
静态摩擦角 | |||
JEM-3.5#SLED | 37.1/39.4 | 29.3/34.1 | 35.3/38.7 |
表面/表面 | 44.2/44.5 | 34.1/34.1 | 39.5/38.6 |
1 ST 5读数 | 43.3-41.7 | 34.1-33.2 | 38.2-38.0 |
AOS偏差涂布 | 7.4 | 5.2 | 3.9 |
Sutherland摩擦 | |||
表面/表面/w/4#SLED | |||
100个周期 | 2 | 1.5 | 1.5 |
200个周期 | 1.5 | 0.5 | 0.5 |
抗粘连性能 | |||
140 F/125PSI/16小时 | |||
表面/表面-干 | 1.5 | 2 | 2 |
水试验-1滴 | |||
表面/表面-湿 | 0 | 0 | 0 |
表面/背表面-湿 | 0 | 0 | 0 |
色漆 | EM-01 | EM-02 | EM-03 | EM-4 | EM-CM-1 | EM-CM-2 |
固体粒子% | 45 | 40 | 40 | 40 | 41.5 | 46.0 |
Grind量 | 40.0 | 40.0 | 40.0 | 40.0 | 40.0 | 40.0 |
乳胶/聚ID | EX.EP4 | EX.EP3 | EX.EP5 | EX.EP6 | SCX1520 | J-77 |
乳胶量 | 115.6 | 130.0 | 130.0 | 115.6 | 125.3 | 113.0 |
Texanol@8% | 4.2 | 4.2 | 4.2 | 4.2 | 4.2 | 4.2 |
亚硝酸钠5% | 2.2 | 2.2 | 2.2 | 2.2 | 2.2 | 2.2 |
DSX1514,50%水溶液 | 1.0 | 1.0 | 1.0 | 1.0 | 1.0 | 1.0 |
总量 | 162.9 | 177.4 | 177.4 | 162.9 | 172.7 | 160.4 |
调配前固体粒子% | 51.3 | 47.1 | 47.1 | 51.3 | 48.4 | 52.1 |
DSX1514-增稠剂从PA,Amber,Henkel购得Grind用Tamol 1124制备分散剂从PA,费城Rohm&Haas购得Texanol-酯溶剂从CT,Danbury联合碳化物购得以克为单位除另外指出 |
色漆 | EM-05 | EM-06 | EM-07 | EM-08 | EM-09 | EM-CM-3 |
固体粒子% | 45.0 | 45.0 | 45.0 | 45.0 | 45.0 | 41.5 |
Grind量 | 40.0 | 40.0 | 40.0 | 40.0 | 40.0 | 40.0 |
乳胶/聚ID | EX.EP11 | EX.EP10 | EX.EP9 | EX.EP7 | EX.EP8 | SCX-1520 |
乳胶量 | 115.6 | 115.6 | 115.6 | 115.6 | 115.6 | 125.3 |
Texanol@8% | 4.2 | 4.2 | 4.2 | 4.2 | 4.2 | 4.2 |
亚硝酸钠5% | 2.2 | 2.2 | 2.2 | 2.2 | 2.2 | 2.2 |
DSX1514,50%水溶液 | 1.0 | 1.0 | 1.0 | 1.0 | 1.0 | 1.0 |
总量 | 162.9 | 162.9 | 162.9 | 162.9 | 162.9 | 172.7 |
调配前固体粒子% | 51.3 | 51.3 | 51.3 | 51.3 | 51.3 | 48.4 |
DSX1514-增稠剂从PA,Amber,Henkel购得Grind用Tamol 1124制备分散剂从PA,费城Rohm&Haas购得Texanol-酯溶剂从CT,Danbury联合碳化物购得以克为单位除外指出 |
色漆 | 光泽度 | Wspot24hSw/Sft/Bl/颜色 | MEK/7开始/最终 | K1 | K7 | DFT | FR | Crp | Blst | |||
20 | 60 | 20 | 60 | |||||||||
3天 | 7天 | |||||||||||
EM-01 | 78 | 92 | 77 | 92 | 9/6/10/10 | 10/18 | 10 | 15 | 1-1.4 | 9 | 5/32 | 4F |
EM-02 | 76 | 92 | 74 | 91 | 8/6/10/10 | 8/15 | 11 | 18 | 10 | 1/8 | 8D | |
EM-03 | 75 | 93 | 74 | 93 | 8/7/10/10 | 7/17 | 12 | 19 | 8 | 1/16 | 6D | |
EM-4 | 78 | 94 | 77 | 94 | 8/8/10/10 | 10/19 | 8 | 12 | 9 | 1/8 | 8D | |
EM-CM-1 | 73 | 90 | 72 | 90 | 6/4/10/10 | 13/33 | 26 | 41 | 1 | 1/16 | 6D | |
EM-CM-2 | 83 | 94 | 80 | 92 | 7/4/10/10 | 10/19 | 14 | 23 | 1-1.4 | 1 | 1/8 | 6D |
EM-5 | 90 | 96 | 86 | 96 | 8/2/2VF/10 | 5/7 | 9 | 15 | 1 | 1/8 | 6D | |
EM-6 | 88 | 95 | 87 | 94 | 8/5/8M/10 | 6/10 | 6 | 12 | 1 | 1/8 | 6D | |
EM-7 | 83 | 93 | 83 | 94 | 10/7/10/10 | 6/11 | 3 | 6 | 1 | 1/8 | 6D | |
EM-8 | 82 | 93 | 80 | 91 | 9/10/10/10 | 7/13 | 4 | 9 | 1 | 1/8 | 6D | |
EM-9 | 41 | 81 | 42 | 81 | 9/8/10/10 | 7/14 | 3 | 10 | 1 | 1/8 | 6D | |
EM-CM-3 | 72 | 90 | 72 | 90 | 7/6/8M/10 | 13/40 | 26 | 41 | 1 | 1/16 | 6D | |
Wspot=水斑试验;Sw=溶胀;Sft=软化;Bl-起泡MEK=抗甲基乙基酮摩擦测试DET=干膜厚度FR=表面锈蚀;Crp=蠕变;Blst=起泡率 |
色漆 | 24小时汽油 | 24小时去离子水 | ||||||
sw | s | bl | clr | sw | s | bl | clr | |
EM-01 | 10 | 1 | 10 | 9 | 9 | 6 | 10 | 10 |
EM-02 | 10 | 0 | 10 | 9 | 9 | 8 | 10 | 10 |
EM-03 | 10 | 0 | 10 | 9 | 9 | 8 | 10 | 10 |
EM-04 | 9 | 0 | 10 | 9 | 9 | 9 | 10 | 10 |
EM-CM-1 | 8 | 0 | 10 | 8 | 9 | 9 | 10 | 9 |
EM-CM-2 | 10 | 1 | 10 | 9 | 9 | 5 | 10 | 5 |
EM-05 | 0 | 0 | 0 | 0 | 8 | 6 | 8F | 7 |
EM-06 | 0 | 0 | 0 | 0 | 9 | 7 | 4D | 10 |
EM-07 | 0 | 0 | 0 | 0 | 10 | 5 | 8F | 6 |
EM-08 | 0 | 0 | 0 | 0 | 10 | 7 | 6M | 7 |
EM-09 | 0 | 0 | 0 | 0 | 10 | 9 | 10 | 6 |
EM-CM-3 | 9 | 1 | 10 | 8 | 10 | 8 | 10 | 10 |
Sw=溶胀 M=中等S=软化 F=少Bl=起泡 D=密集Clr=颜色 |
色漆 | 24小时5%硫酸 | 24小时盐酸 | ||||||
sw | s | b1 | clr | sw | s | bl | clr | |
EM-01 | 10 | 8 | 10 | 10 | 8 | 2 | 10 | 6 |
EM-02 | 10 | 9 | 10 | 10 | 9 | 2 | 10 | 7 |
EM-03 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 |
EM-04 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 |
EM-CM-1 | 10 | 10 | 10 | 10 | 9 | 4 | 10 | 10 |
EM-CM-2 | 10 | 8 | 10 | 10 | 9 | 1 | 10 | 10 |
EM-05 | 8D | 5 | 8D | 10 | 8 | 2 | 6MD | 10 |
EM-06 | 10 | 9 | 1 | 10 | 0 | 0 | 0 | 0 |
EM-07 | 10 | 2 | 1 | 10 | 0 | 0 | 0 | 0 |
EM-08 | 10 | 2 | 1 | 10 | 0 | 0 | 0 | 0 |
EM-09 | 6D | 1 | 6D | 10 | 0 | 0 | 0 | 0 |
EM-CM-3 | 10 | 9 | 10 | 10 | 8 | 10 | 10 | 10 |
Sw=溶胀 MD=中等密集S=软化 D=密集Bl=起泡Clr=颜色 |
色漆 | 24小时制动液 | 24小时Formula409 | ||||||
sw | s | bl | clr | sw | s | bl | clr | |
EM-0l | 8 | 4 | 10 | 10 | 10 | 3 | 8F | 10 |
EM-02 | 8 | 1 | 10 | 10 | 9 | 1 | 10 | 10 |
EM-03 | 8 | 4 | 10 | 10 | 9 | 3 | 4F | 9 |
EM-04 | 8 | 4 | 10 | 10 | 9 | 2 | 10 | 10 |
EM-CM-1 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
EM-CM-2 | 0 | 0 | 0 | 0 | 10 | 3 | 10 | 10 |
EM-05 | 9 | 9 | 10 | 10 | 10 | 4 | 10 | 10 |
EM-06 | 8 | 8 | 10 | 10 | 9 | 6 | 10 | 8 |
EM-07 | 10 | 10 | 10 | 10 | 10 | 5 | 10 | 10 |
EM-08 | 8 | 8 | 10 | 10 | 10 | 8 | 10 | 9 |
EM-09 | 10 | 10 | 10 | 10 | 10 | 2 | 10 | 10 |
EM-CM-3 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
Sw=溶胀S=软化 F=少Bl=起泡Clr=颜色 |
色漆 | 24小时PAlc | 24小时5%氢氧化钠 | ||||||
sw | s | bl | clr | sw | s | bl | clr | |
EM-01 | 10 | 9 | 10 | 10 | 9 | 9 | 10 | 10 |
EM-02 | 9 | 10 | 10 | 10 | 9 | 10 | 10 | 10 |
EM-03 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 9 |
EM-04 | 10 | 10 | 10 | 10 | 0 | 10 | 0 | 0 |
EM-CM-1 | 10 | 10 | 10 | 10 | 10 | 10 | 8MD | 10 |
EM-CM-2 | 10 | 7 | 10 | 10 | 9 | 3 | 8D | 8 |
EM-05 | 10 | 10 | 10 | 10 | 0 | 1 | 6D | 8 |
EM-06 | 10 | 8 | 10 | 10 | 10 | 2 | 10 | 8 |
EM-07 | 10 | 10 | 10 | 5 | 10 | 2 | 10 | 2 |
EM-08 | 10 | 10 | 10 | 6 | 10 | 2 | 10 | 8 |
EM-09 | 10 | 10 | 10 | 6 | 10 | 1 | 10 | 7 |
EM-CM-3 | 10 | 10 | 10 | 10 | 9 | 3 | 8D | 10 |
Sw=溶胀 D=密集S=软化 MD=中等密集Bl=起泡Clr=颜色 |
Claims (24)