CA2895944C - Procede de fabrication de pieces d'acier revetues et durcies a la presse, et toles prerevetues permettant la fabrication de ces pieces - Google Patents

Procede de fabrication de pieces d'acier revetues et durcies a la presse, et toles prerevetues permettant la fabrication de ces pieces Download PDF

Info

Publication number
CA2895944C
CA2895944C CA2895944A CA2895944A CA2895944C CA 2895944 C CA2895944 C CA 2895944C CA 2895944 A CA2895944 A CA 2895944A CA 2895944 A CA2895944 A CA 2895944A CA 2895944 C CA2895944 C CA 2895944C
Authority
CA
Canada
Prior art keywords
temperature
sheet
coating
steel
atmosphere
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CA2895944A
Other languages
English (en)
French (fr)
Other versions
CA2895944A1 (fr
Inventor
Juan David PUERTA VELASQUEZ
Jonas STAUDTE
Pascal Drillet
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ArcelorMittal Investigacion y Desarrollo SL
Original Assignee
ArcelorMittal Investigacion y Desarrollo SL
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=46982626&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=CA2895944(C) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by ArcelorMittal Investigacion y Desarrollo SL filed Critical ArcelorMittal Investigacion y Desarrollo SL
Publication of CA2895944A1 publication Critical patent/CA2895944A1/fr
Application granted granted Critical
Publication of CA2895944C publication Critical patent/CA2895944C/fr
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment 
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/012—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/34—Methods of heating
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/34—Methods of heating
    • C21D1/52—Methods of heating with flames
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/62—Quenching devices
    • C21D1/673—Quenching devices for die quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/74—Methods of treatment in inert gas, controlled atmosphere, vacuum or pulverulent material
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/74—Methods of treatment in inert gas, controlled atmosphere, vacuum or pulverulent material
    • C21D1/76—Adjusting the composition of the atmosphere
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D3/00—Diffusion processes for extraction of non-metals; Furnaces therefor
    • C21D3/02—Extraction of non-metals
    • C21D3/04—Decarburising
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/002—Heat treatment of ferrous alloys containing Cr
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0257—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment with diffusion of elements, e.g. decarburising, nitriding
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0447—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the heat treatment
    • C21D8/0457—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the heat treatment with diffusion of elements, e.g. decarburising, nitriding
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/003—Apparatus
    • C23C2/0038—Apparatus characterised by the pre-treatment chambers located immediately upstream of the bath or occurring locally before the dipping process
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/12—Aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Metallurgy (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Articles (AREA)
  • Heat Treatment Of Strip Materials And Filament Materials (AREA)
  • Solid-Phase Diffusion Into Metallic Material Surfaces (AREA)
  • Coating With Molten Metal (AREA)
  • Laminated Bodies (AREA)
  • Heat Treatments In General, Especially Conveying And Cooling (AREA)
  • Mounting, Exchange, And Manufacturing Of Dies (AREA)
  • Reduction Rolling/Reduction Stand/Operation Of Reduction Machine (AREA)
  • Architecture (AREA)
  • Structural Engineering (AREA)
  • Combustion & Propulsion (AREA)
  • Transportation (AREA)
  • Forging (AREA)
CA2895944A 2012-09-06 2013-09-06 Procede de fabrication de pieces d'acier revetues et durcies a la presse, et toles prerevetues permettant la fabrication de ces pieces Active CA2895944C (fr)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
FRPCT/FR2012/000350 2012-09-06
PCT/FR2012/000350 WO2014037627A1 (fr) 2012-09-06 2012-09-06 Procede de fabrication de pieces d'acier revêtues et durcies a la presse, et tôles prerevêtues permettant la fabrication de ces pieces
PCT/IB2013/001914 WO2015033177A1 (fr) 2012-09-06 2013-09-06 Procédé de fabrication de pièces d'acier revêtues et durcies a la presse, et tôles prérevêtues permettant la fabrication de ces pièces

Publications (2)

Publication Number Publication Date
CA2895944A1 CA2895944A1 (fr) 2015-03-12
CA2895944C true CA2895944C (fr) 2018-02-13

Family

ID=46982626

Family Applications (1)

Application Number Title Priority Date Filing Date
CA2895944A Active CA2895944C (fr) 2012-09-06 2013-09-06 Procede de fabrication de pieces d'acier revetues et durcies a la presse, et toles prerevetues permettant la fabrication de ces pieces

Country Status (18)

Country Link
US (2) US9909194B2 (Direct)
EP (5) EP4464815A3 (Direct)
JP (2) JP6166787B2 (Direct)
KR (1) KR101643513B1 (Direct)
CN (1) CN104769138B (Direct)
BR (2) BR112015005090B8 (Direct)
CA (1) CA2895944C (Direct)
ES (4) ES2785071T3 (Direct)
FI (3) FI3783118T3 (Direct)
HU (4) HUE062051T2 (Direct)
IN (1) IN2015DN01908A (Direct)
MA (1) MA37932B1 (Direct)
MX (2) MX366129B (Direct)
PL (4) PL2893047T3 (Direct)
RU (1) RU2610995C2 (Direct)
UA (1) UA115791C2 (Direct)
WO (2) WO2014037627A1 (Direct)
ZA (1) ZA201501534B (Direct)

Families Citing this family (71)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014166630A1 (en) * 2013-04-10 2014-10-16 Tata Steel Ijmuiden Bv Product formed by hot forming of metallic coated steel sheet, method to form the product, and steel strip
JP5852690B2 (ja) * 2013-04-26 2016-02-03 株式会社神戸製鋼所 ホットスタンプ用合金化溶融亜鉛めっき鋼板
EP4215628A1 (en) * 2013-12-10 2023-07-26 Arcelormittal S.A. A method of annealing steel sheets
WO2016079565A1 (en) 2014-11-18 2016-05-26 Arcelormittal Method for manufacturing a high strength steel product and steel product thereby obtained
WO2016132165A1 (fr) 2015-02-19 2016-08-25 Arcelormittal Procede de fabrication d'une piece phosphatable a partir d'une tole revetue d'un revetement a base d'aluminium et d'un revetement de zinc
WO2017006144A1 (en) 2015-07-09 2017-01-12 Arcelormittal Steel for press hardening and press hardened part manufactured from such steel
JP2017066508A (ja) * 2015-10-02 2017-04-06 株式会社神戸製鋼所 熱間プレス用亜鉛めっき鋼板および熱間プレス成形品の製造方法
WO2017098304A1 (en) * 2015-12-09 2017-06-15 Arcelormittal Method for producing an automotive structural part comprising a lowerside sill and a lower front pillar
DE102015016656A1 (de) * 2015-12-19 2017-06-22 GM Global Technology Operations LLC (n. d. Ges. d. Staates Delaware) Verfahren zur Herstellung eines beschichteten, durch Warmumformung gehärteten Körpers sowie ein nach dem Verfahren hergestellter Körper
DE102016100648B4 (de) * 2015-12-23 2018-04-12 Benteler Automobiltechnik Gmbh Wärmebehandlungsofen sowie Verfahren zur Wärmebehandlung einer vorbeschichteten Stahlblechplatine und Verfahren zur Herstellung eines Kraftfahrzeugbauteils
KR101696121B1 (ko) 2015-12-23 2017-01-13 주식회사 포스코 내수소지연파괴특성, 내박리성 및 용접성이 우수한 열간성형용 알루미늄-철 합금 도금강판 및 이를 이용한 열간성형 부재
DE102016102504A1 (de) 2016-02-08 2017-08-10 Salzgitter Flachstahl Gmbh Aluminiumbasierte Beschichtung für Stahlbleche oder Stahlbänder und Verfahren zur Herstellung hierzu
BR112018012606A2 (pt) * 2016-02-25 2018-12-04 Nippon Steel & Sumitomo Metal Corporation chapa de aço galvanizada por imersão a quente de alta resistência com excelente resistência ao destacamento por impacto e resistência à corrosão em seção trabalhada
JP6237937B2 (ja) * 2016-03-11 2017-11-29 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
WO2017182833A1 (en) 2016-04-19 2017-10-26 Arcelormittal Method for producing a metallic coated steel sheet
DE102016117474A1 (de) * 2016-09-16 2018-03-22 Benteler Automobiltechnik Gmbh Karosseriebauteil mit reduzierter Rissneigung und Verfahren zur Herstellung
GB2555104B (en) * 2016-10-14 2022-06-01 Liberty Performance Steels Ltd Manufacture of a stress relieved length of steel having an oxidised surface layer
CN106334875A (zh) * 2016-10-27 2017-01-18 宝山钢铁股份有限公司 一种带铝或者铝合金镀层的钢制焊接部件及其制造方法
WO2018096387A1 (en) * 2016-11-24 2018-05-31 Arcelormittal Hot-rolled and coated steel sheet for hot-stamping, hot-stamped coated steel part and methods for manufacturing the same
WO2018115914A1 (en) * 2016-12-19 2018-06-28 Arcelormittal A manufacturing process of hot press formed aluminized steel parts
KR101858868B1 (ko) 2016-12-23 2018-05-16 주식회사 포스코 충격특성이 우수한 열간성형용 도금강판, 열간성형 부재 및 그들의 제조방법
US20180237877A1 (en) * 2017-02-17 2018-08-23 GM Global Technology Operations LLC Mitigating liquid metal embrittlement in zinc-coated press hardened steels
CA3053661A1 (en) * 2017-02-20 2018-08-23 Nippon Steel Corporation Hot stamped body
US10995385B2 (en) 2017-03-30 2021-05-04 Jfe Steel Corporation Hot pressed part and method of manufacturing same
WO2018220412A1 (fr) 2017-06-01 2018-12-06 Arcelormittal Procede de fabrication de pieces d'acier a haute resistance mecanique et ductilite amelioree, et pieces obtenues par ce procede
DE102017112164A1 (de) * 2017-06-01 2018-12-06 Benteler Automobiltechnik Gmbh Blechumformbauteil sowie Verfahren zur Herstellung des Blechumformbauteils
WO2018220430A1 (en) 2017-06-02 2018-12-06 Arcelormittal Steel sheet for manufacturing press hardened parts, press hardened part having a combination of high strength and crash ductility, and manufacturing methods thereof
WO2018234839A1 (en) * 2017-06-20 2018-12-27 Arcelormittal ZINC COATED STEEL SHEET HAVING HIGH STRENGTH POINTS WELDABILITY
US10329639B2 (en) * 2017-08-04 2019-06-25 Gm Global Technology Operations Llc. Multilayer steel and method of reducing liquid metal embrittlement
WO2019043424A1 (en) 2017-08-30 2019-03-07 Arcelormittal COATED METALLIC SUBSTRATE
WO2019043422A1 (en) * 2017-08-30 2019-03-07 Arcelormittal COATED METALLIC SUBSTRATE
JP7167428B2 (ja) * 2017-11-10 2022-11-09 昭和電工マテリアルズ株式会社 鉄基焼結合金材及びその製造方法
WO2019130713A1 (ja) 2017-12-27 2019-07-04 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP6916129B2 (ja) * 2018-03-02 2021-08-11 株式会社神戸製鋼所 ホットスタンプ用亜鉛めっき鋼板およびその製造方法
US11613789B2 (en) 2018-05-24 2023-03-28 GM Global Technology Operations LLC Method for improving both strength and ductility of a press-hardening steel
CN112534078A (zh) 2018-06-19 2021-03-19 通用汽车环球科技运作有限责任公司 具有增强的机械性质的低密度压制硬化钢
CN109433960A (zh) * 2018-09-30 2019-03-08 苏州普热斯勒先进成型技术有限公司 热冲压高强钢汽车车身覆盖件及其制造方法、制造系统
WO2020070545A1 (en) 2018-10-04 2020-04-09 Arcelormittal A press hardening method
JP2020082102A (ja) * 2018-11-19 2020-06-04 株式会社神戸製鋼所 接合構造体及び接合構造体の製造方法
WO2020128571A1 (en) * 2018-12-18 2020-06-25 Arcelormittal A press hardened part with high resistance to delayed fracture and a manufacturing process thereof
KR102165223B1 (ko) * 2018-12-19 2020-10-13 주식회사 포스코 열간성형 후 충격특성이 우수한 열간성형용 도금강판, 열간성형 부재 및 이들의 제조방법
KR102802089B1 (ko) * 2019-02-08 2025-05-02 오를리콘 서피스 솔루션스 아크티엔게젤샤프트, 페피콘 붕화물-함유 확산 장벽 층을 포함하는 코팅을 구비하는 코팅 공구
JP7111252B2 (ja) * 2019-03-29 2022-08-02 日本製鉄株式会社 被覆鋼部材、被覆鋼板およびそれらの製造方法
US11149327B2 (en) * 2019-05-24 2021-10-19 voestalpine Automotive Components Cartersville Inc. Method and device for heating a steel blank for hardening purposes
US11530469B2 (en) 2019-07-02 2022-12-20 GM Global Technology Operations LLC Press hardened steel with surface layered homogenous oxide after hot forming
WO2021084302A1 (en) 2019-10-30 2021-05-06 Arcelormittal A press hardening method
WO2021084303A1 (en) 2019-10-30 2021-05-06 Arcelormittal A press hardening method
WO2021084304A1 (en) * 2019-10-30 2021-05-06 Arcelormittal A press hardening method
WO2021084305A1 (en) * 2019-10-30 2021-05-06 Arcelormittal A press hardening method
EP4151758A4 (en) * 2020-05-13 2023-10-18 Nippon Steel Corporation HOT STAMPED STEEL SHEET AND HOT STAMPED MOLDING
CN115151669B (zh) * 2020-05-13 2023-12-26 日本制铁株式会社 热冲压成形体
CN111778467B (zh) * 2020-09-04 2020-11-24 育材堂（苏州）材料科技有限公司 带铝或铝合金预镀层的预镀层钢板、制造方法及热冲压成形构件
US20230373038A1 (en) * 2020-10-21 2023-11-23 Verdicio Solutions A.I.E. A method for the manufacture of a welded joint by Narrow Gap Welding
WO2022129989A1 (en) 2020-12-15 2022-06-23 Arcelormittal Annealing method
WO2022129995A1 (en) * 2020-12-16 2022-06-23 Arcelormittal Coated steel sheet and high strength press hardened steel part and method of manufacturing the same
WO2022129994A1 (en) * 2020-12-16 2022-06-23 Arcelormittal Coated steel sheet and high strength press hardened steel part and method of manufacturing the same
WO2022136689A1 (en) * 2020-12-23 2022-06-30 Voestalpine Stahl Gmbh A zinc or zinc-alloy coated strip or steel with improved zinc adhesion
CN112877632A (zh) * 2021-01-12 2021-06-01 鞍钢股份有限公司 高塑性热冲压成型用铝硅镀层钢板及其热冲压方法
DE102021201845A1 (de) 2021-02-26 2022-09-01 Volkswagen Aktiengesellschaft Verfahren zur Herstellung eines warmumgeformten und pressgehärteten Stahlblechbauteils
KR102920268B1 (ko) * 2021-03-17 2026-02-03 닛폰세이테츠 가부시키가이샤 강판, 강 부재 및 피복 강 부재
WO2022234320A1 (en) * 2021-05-04 2022-11-10 Arcelormittal Steel sheet and high strength press hardened steel part and method of manufacturing the same
KR20240155912A (ko) 2022-03-31 2024-10-29 제이에프이 스틸 가부시키가이샤 강판, 부재 및 그들의 제조 방법
CN115652218B (zh) 2022-11-17 2023-06-06 育材堂（苏州）材料科技有限公司 一种低碳的高韧性热冲压成形构件及钢板
JP7727251B2 (ja) * 2022-12-09 2025-08-21 日本製鉄株式会社 ホットスタンプ成形体
KR20250103730A (ko) * 2022-12-09 2025-07-07 닛폰세이테츠 가부시키가이샤 도금 강판
CN116174558A (zh) 2023-02-09 2023-05-30 香港大学 一种铝硅镀层热冲压成形构件及其制备方法和应用
WO2024182196A1 (en) * 2023-03-01 2024-09-06 Cleveland-Cliffs Steel Properties Inc. Furnace humidification system, a method for annealing steel, a continuous annealing line
WO2024203606A1 (ja) * 2023-03-30 2024-10-03 株式会社神戸製鋼所 鋼板および鋼板の製造方法
EP4667606A1 (en) * 2023-03-30 2025-12-24 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Plated steel sheet and method for manufacturing same
WO2025003736A1 (en) * 2023-06-30 2025-01-02 Arcelormittal Steel sheet and high strength press hardened steel part having excellent bending anisotropy and method of manufacturing the same
CN122029295A (zh) * 2023-10-16 2026-05-12 杰富意钢铁株式会社 高强度热镀锌钢板及其制造方法

Family Cites Families (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE1294402B (de) * 1965-08-06 1969-05-08 Armco Steel Corp Verfahren zur Herstellung eines mit einem Metallueberzug versehenen Eisenmetalls mit stark verbesserter Ziehbarkeit
JPH04276057A (ja) * 1991-03-05 1992-10-01 Nippon Steel Corp めっき密着性の良好な高Ｓｉ含有高張力合金化溶融亜鉛めっき鋼板の製造方法
JPH10130782A (ja) 1996-11-01 1998-05-19 Nippon Steel Corp 超高強度冷延鋼板およびその製造方法
FR2780984B1 (fr) 1998-07-09 2001-06-22 Lorraine Laminage Tole d'acier laminee a chaud et a froid revetue et comportant une tres haute resistance apres traitement thermique
JP4582850B2 (ja) * 2000-02-24 2010-11-17 日新製鋼株式会社 曲げ加工性に優れた高強度ステンレス鋼板
FR2807447B1 (fr) * 2000-04-07 2002-10-11 Usinor Procede de realisation d'une piece a tres hautes caracteristiques mecaniques, mise en forme par emboutissage, a partir d'une bande de tole d'acier laminee et notamment laminee a chaud et revetue
KR100748736B1 (ko) * 2003-03-31 2007-08-13 신닛뽄세이테쯔 카부시키카이샤 합금화 용융 아연 도금 강판 및 그 제조 방법
EP1612288B9 (en) 2003-04-10 2010-10-27 Nippon Steel Corporation A method for producing a hot-dip zinc coated steel sheet having high strength
JP2006051543A (ja) 2004-07-15 2006-02-23 Nippon Steel Corp 冷延、熱延鋼板もしくはＡｌ系、Ｚｎ系めっき鋼板を使用した高強度自動車部材の熱間プレス方法および熱間プレス部品
JP2006104546A (ja) * 2004-10-08 2006-04-20 Nippon Steel Corp 高強度自動車部材および熱間プレス方法
RU2418094C2 (ru) * 2006-01-30 2011-05-10 Ниппон Стил Корпорейшн Высокопрочный горячеоцинкованный погружением стальной лист и высокопрочный отожженный после цинкования стальной лист с превосходными формуемостью и способностью к нанесению гальванопокрытия и способы изготовления и устройства для изготовления таких листов
KR100760152B1 (ko) 2006-06-07 2007-09-18 현대하이스코 주식회사 핫스탬핑을 이용하여 아연도금강판으로 고강도 자동차용부품을 제조하는 방법
HUE036195T2 (hu) * 2006-10-30 2018-06-28 Arcelormittal Bevonatolt acélszalagok, eljárások azok elõállítására, eljárások azok alkalmazására, azokból készített nyersdarabok, azokból készített sajtolt termékek, továbbá ilyen sajtolt terméket tartalmazó késztermékek
MX2009008557A (es) * 2007-02-23 2009-08-21 Corus Staal Bv Metodo para conformacion termomecanica de un producto final con una tenacidad muy alta y producto elaborado por el mismo.
EP2009129A1 (en) * 2007-06-29 2008-12-31 ArcelorMittal France Process for manufacturing a galvannealed steel sheet by DFF regulation
DE102007061489A1 (de) 2007-12-20 2009-06-25 Voestalpine Stahl Gmbh Verfahren zum Herstellen von gehärteten Bauteilen aus härtbarem Stahl und härtbares Stahlband hierfür
EP2123786A1 (fr) 2008-05-21 2009-11-25 ArcelorMittal France Procédé de fabrication de tôles d'aciers dual phase laminées à froid à trés haute résistance et tôles ainsi produites
JP5131844B2 (ja) * 2008-08-12 2013-01-30 新日鐵住金株式会社 熱間プレス用熱延鋼板およびその製造方法ならびに熱間プレス鋼板部材の製造方法
DE102008044693B4 (de) * 2008-08-28 2011-02-24 Benteler Automobiltechnik Gmbh Verfahren zur Herstellung gehärteter Bauteile mit mehrfachem Erwärmen
DE102009056443A1 (de) * 2009-12-02 2011-06-09 Benteler Automobiltechnik Gmbh Crashbox und Verfahren zu deren Herstellung
DE102009044861B3 (de) * 2009-12-10 2011-06-22 ThyssenKrupp Steel Europe AG, 47166 Verfahren zum Herstellen eines gut umformbaren Stahlflachprodukts, Stahlflachprodukt und Verfahren zur Herstellung eines Bauteils aus einem solchen Stahlflachprodukt

Also Published As

Publication number Publication date
CA2895944A1 (fr) 2015-03-12
MX2015002972A (es) 2015-11-11
US20160017452A1 (en) 2016-01-21
MX2019002069A (es) 2019-06-03
UA115791C2 (uk) 2017-12-26
FI3783116T3 (fi) 2023-06-14
EP2893047A1 (fr) 2015-07-15
EP3783117A1 (fr) 2021-02-24
PL3783118T3 (pl) 2023-07-10
EP2893047B1 (fr) 2020-04-01
HUE069713T2 (hu) 2025-04-28
US20170260599A1 (en) 2017-09-14
ES2945840T3 (es) 2023-07-07
CN104769138A (zh) 2015-07-08
KR20150047627A (ko) 2015-05-04
RU2610995C2 (ru) 2017-02-17
PL2893047T3 (pl) 2020-10-19
JP2018012884A (ja) 2018-01-25
BR112015005090B8 (pt) 2019-09-03
EP3783116A1 (fr) 2021-02-24
BR112015005090A8 (pt) 2019-06-25
ES2785071T3 (es) 2020-10-05
EP4464815A3 (fr) 2025-01-15
BR112015005090B1 (pt) 2019-08-06
US9909194B2 (en) 2018-03-06
KR101643513B1 (ko) 2016-07-27
IN2015DN01908A (Direct) 2015-08-07
EP3783118A1 (fr) 2021-02-24
ZA201501534B (en) 2016-01-27
WO2015033177A1 (fr) 2015-03-12
EP3783116B1 (fr) 2023-04-26
HUE061920T2 (hu) 2023-08-28
EP3783118B1 (fr) 2023-04-12
PL3783116T3 (pl) 2023-07-10
JP2016504488A (ja) 2016-02-12
ES2946442T3 (es) 2023-07-18
PL3783117T3 (pl) 2025-03-03
MA37932B1 (fr) 2016-06-30
WO2014037627A1 (fr) 2014-03-13
MA20150410A1 (fr) 2015-11-30
HUE062051T2 (hu) 2023-09-28
MX366129B (es) 2019-06-28
WO2015033177A8 (fr) 2015-04-30
ES3014218T3 (en) 2025-04-21
BR122019008477B1 (pt) 2020-02-18
RU2015112317A (ru) 2016-10-27
HUE049636T2 (hu) 2020-09-28
JP6166787B2 (ja) 2017-07-19
FI3783118T3 (fi) 2023-06-15
BR112015005090A2 (pt) 2017-07-04
JP6359155B2 (ja) 2018-07-18
US9957582B2 (en) 2018-05-01
EP3783117B1 (fr) 2024-12-11
FI3783117T3 (fi) 2025-01-30
EP4464815A2 (fr) 2024-11-20
CN104769138B (zh) 2017-03-08

Similar Documents

Publication Publication Date Title
EP2893047B1 (fr) Procede de fabrication de pieces d'acier revêtues et durcies a la presse, et tôles prerevêtues permettant la fabrication de ces pieces
CA2680623C (fr) Acier pour formage a chaud ou trempe sous outil, a ductilite amelioree
CA3071152C (fr) Procede de fabrication de toles d'acier pour durcissement sous presse, et pieces obtenues par ce procede
EP3126459B1 (fr) Procédé de fabrication à haute productivité de pièces d'acier revêtues et durcies à la presse
CA2668393C (fr) Bandes d'acier revetues, procedes de fabrication de celles-ci, procedes d'utilisation de celles-ci, ebauches d'emboutissage preparees a partir de celles-ci, produits emboutis prepares a partir de celles-ci, et articles manufactures contenant un produit embouti de ce type
CA2838665C (fr) Tole d'acier laminee a froid et revetue de zinc ou d'alliage de zinc, procede de fabrication et utilisation d'une telle tole
EP2171112B1 (fr) Procede de fabrication de tôles d'acier a hautes caracteristiques de resistance et de ductilite, et tôles ainsi produites
CA3065036C (fr) Procede de fabrication de pieces d'acier a haute resistance mecanique et ductilite amelioree, et pieces obtenues par ce procede
CA2627394C (fr) Procede de fabrication d'une piece a tres hautes caracteristiques mecaniques a partir d'une tole laminee et revetue
EP3307921A2 (fr) Acier à haute résistance et procédé de fabrication
EP2707513A1 (fr) Procede de fabrication d'acier martensitique a tres haute resistance et tôle ou piece ainsi obtenue
WO2012153013A1 (fr) Procede de fabrication d'acier martensitique a tres haute limite elastique tole ou piece ainsi obtenue.
WO2011104443A1 (fr) Procédé de fabrication d'une pièce a partir d'une tôle revêtue d'aluminium ou d'alliage d'aluminium

Legal Events

Date Code Title Description
MPN Maintenance fee for patent paid

Free format text: FEE DESCRIPTION TEXT: MF (PATENT, 11TH ANNIV.) - STANDARD

Year of fee payment: 11

U00 Fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U00-U101 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE REQUEST RECEIVED

Effective date: 20240826

U11 Full renewal or maintenance fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U11-U102 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE FEE PAYMENT DETERMINED COMPLIANT

Effective date: 20240826

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U11-U102 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE FEE PAYMENT PAID IN FULL

Effective date: 20240826

MPN Maintenance fee for patent paid

Free format text: FEE DESCRIPTION TEXT: MF (PATENT, 12TH ANNIV.) - STANDARD

Year of fee payment: 12

U00 Fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U00-U101 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE REQUEST RECEIVED

Effective date: 20250820

U11 Full renewal or maintenance fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U11-U102 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE FEE PAYMENT PAID IN FULL

Effective date: 20250820

R11 Change to the name of applicant or owner or transfer of ownership requested

Free format text: ST27 STATUS EVENT CODE: A-4-4-R10-R11-R127 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: TRANSFER RECORDAL REQUEST OR RESPONSE

Effective date: 20260216

W00 Other event occurred

Free format text: ST27 STATUS EVENT CODE: A-4-4-W10-W00-W111 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: CORRESPONDENT DETERMINED COMPLIANT

Effective date: 20260217

R14 Transfer of ownership recorded

Free format text: ST27 STATUS EVENT CODE: A-4-4-R10-R14-R129 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: TRANSFER REQUIREMENTS DETERMINED COMPLIANT

Effective date: 20260223