PL3783116T3 - Wstępnie powlekane blachy do wytwarzania powlekanych i utwardzanych ciśnieniowo części stalowych - Google Patents

Wstępnie powlekane blachy do wytwarzania powlekanych i utwardzanych ciśnieniowo części stalowych

Info

Publication number
PL3783116T3
PL3783116T3 PL20156836.7T PL20156836T PL3783116T3 PL 3783116 T3 PL3783116 T3 PL 3783116T3 PL 20156836 T PL20156836 T PL 20156836T PL 3783116 T3 PL3783116 T3 PL 3783116T3
Authority
PL
Poland
Prior art keywords
coated
hardened
press
production
steel parts
Prior art date
Application number
PL20156836.7T
Other languages
English (en)
Inventor
Juan David PUERTA VELASQUEZ
Jonas STAUDTE
Pascal Drillet
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of PL3783116T3 publication Critical patent/PL3783116T3/pl

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/012—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/34—Methods of heating
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/34—Methods of heating
    • C21D1/52—Methods of heating with flames
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/62—Quenching devices
    • C21D1/673—Quenching devices for die quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/74—Methods of treatment in inert gas, controlled atmosphere, vacuum or pulverulent material
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/74—Methods of treatment in inert gas, controlled atmosphere, vacuum or pulverulent material
    • C21D1/76—Adjusting the composition of the atmosphere
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D3/00—Diffusion processes for extraction of non-metals; Furnaces therefor
    • C21D3/02—Extraction of non-metals
    • C21D3/04—Decarburising
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/002—Heat treatment of ferrous alloys containing Cr
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0257—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment with diffusion of elements, e.g. decarburising, nitriding
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
    • C21D8/0457—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment with diffusion of elements, e.g. decarburising, nitriding
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/003—Apparatus
    • C23C2/0038—Apparatus characterised by the pre-treatment chambers located immediately upstream of the bath or occurring locally before the dipping process
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/12—Aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Articles (AREA)
  • Solid-Phase Diffusion Into Metallic Material Surfaces (AREA)
  • Coating With Molten Metal (AREA)
  • Heat Treatment Of Strip Materials And Filament Materials (AREA)
  • Laminated Bodies (AREA)
  • Heat Treatments In General, Especially Conveying And Cooling (AREA)
  • Architecture (AREA)
  • Structural Engineering (AREA)
  • Combustion & Propulsion (AREA)
  • Transportation (AREA)
  • Mounting, Exchange, And Manufacturing Of Dies (AREA)
  • Forging (AREA)
  • Reduction Rolling/Reduction Stand/Operation Of Reduction Machine (AREA)
PL20156836.7T 2012-09-06 2013-09-06 Wstępnie powlekane blachy do wytwarzania powlekanych i utwardzanych ciśnieniowo części stalowych PL3783116T3 (pl)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/FR2012/000350 WO2014037627A1 (fr) 2012-09-06 2012-09-06 Procede de fabrication de pieces d'acier revêtues et durcies a la presse, et tôles prerevêtues permettant la fabrication de ces pieces

Publications (1)

Publication Number Publication Date
PL3783116T3 true PL3783116T3 (pl) 2023-07-10

Family

ID=46982626

Family Applications (3)

Application Number Title Priority Date Filing Date
PL13803200T PL2893047T3 (pl) 2012-09-06 2013-09-06 Sposób wytwarzania powlekanych i utwardzanych części stalowych oraz wstępnie powlekane blachy do wytwarzania takich części
PL20156836.7T PL3783116T3 (pl) 2012-09-06 2013-09-06 Wstępnie powlekane blachy do wytwarzania powlekanych i utwardzanych ciśnieniowo części stalowych
PL20157000.9T PL3783118T3 (pl) 2012-09-06 2013-09-06 Sposób wytwarzania powlekanych i utwardzanych ciśnieniowo części stalowych

Family Applications Before (1)

Application Number Title Priority Date Filing Date
PL13803200T PL2893047T3 (pl) 2012-09-06 2013-09-06 Sposób wytwarzania powlekanych i utwardzanych części stalowych oraz wstępnie powlekane blachy do wytwarzania takich części

Family Applications After (1)

Application Number Title Priority Date Filing Date
PL20157000.9T PL3783118T3 (pl) 2012-09-06 2013-09-06 Sposób wytwarzania powlekanych i utwardzanych ciśnieniowo części stalowych

Country Status (18)

Country Link
US (2) US9909194B2 (pl)
EP (4) EP3783118B1 (pl)
JP (2) JP6166787B2 (pl)
KR (1) KR101643513B1 (pl)
CN (1) CN104769138B (pl)
BR (2) BR122019008477B1 (pl)
CA (1) CA2895944C (pl)
ES (3) ES2945840T3 (pl)
FI (2) FI3783118T3 (pl)
HU (3) HUE061920T2 (pl)
IN (1) IN2015DN01908A (pl)
MA (1) MA37932B1 (pl)
MX (2) MX366129B (pl)
PL (3) PL2893047T3 (pl)
RU (1) RU2610995C2 (pl)
UA (1) UA115791C2 (pl)
WO (2) WO2014037627A1 (pl)
ZA (1) ZA201501534B (pl)

Families Citing this family (58)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014166630A1 (en) * 2013-04-10 2014-10-16 Tata Steel Ijmuiden Bv Product formed by hot forming of metallic coated steel sheet, method to form the product, and steel strip
JP5852690B2 (ja) * 2013-04-26 2016-02-03 株式会社神戸製鋼所 ホットスタンプ用合金化溶融亜鉛めっき鋼板
KR20160085830A (ko) * 2013-12-10 2016-07-18 아르셀러미탈 강판의 어닐링 방법
WO2016079565A1 (en) * 2014-11-18 2016-05-26 Arcelormittal Method for manufacturing a high strength steel product and steel product thereby obtained
WO2016132165A1 (fr) * 2015-02-19 2016-08-25 Arcelormittal Procede de fabrication d'une piece phosphatable a partir d'une tole revetue d'un revetement a base d'aluminium et d'un revetement de zinc
WO2017006144A1 (en) 2015-07-09 2017-01-12 Arcelormittal Steel for press hardening and press hardened part manufactured from such steel
JP2017066508A (ja) * 2015-10-02 2017-04-06 株式会社神戸製鋼所 熱間プレス用亜鉛めっき鋼板および熱間プレス成形品の製造方法
WO2017098304A1 (en) * 2015-12-09 2017-06-15 Arcelormittal Method for producing an automotive structural part comprising a lowerside sill and a lower front pillar
DE102015016656A1 (de) * 2015-12-19 2017-06-22 GM Global Technology Operations LLC (n. d. Ges. d. Staates Delaware) Verfahren zur Herstellung eines beschichteten, durch Warmumformung gehärteten Körpers sowie ein nach dem Verfahren hergestellter Körper
KR101696121B1 (ko) 2015-12-23 2017-01-13 주식회사 포스코 내수소지연파괴특성, 내박리성 및 용접성이 우수한 열간성형용 알루미늄-철 합금 도금강판 및 이를 이용한 열간성형 부재
DE102016100648B4 (de) 2015-12-23 2018-04-12 Benteler Automobiltechnik Gmbh Wärmebehandlungsofen sowie Verfahren zur Wärmebehandlung einer vorbeschichteten Stahlblechplatine und Verfahren zur Herstellung eines Kraftfahrzeugbauteils
DE102016102504A1 (de) * 2016-02-08 2017-08-10 Salzgitter Flachstahl Gmbh Aluminiumbasierte Beschichtung für Stahlbleche oder Stahlbänder und Verfahren zur Herstellung hierzu
EP3378965B1 (en) * 2016-02-25 2020-08-12 Nippon Steel Corporation High-strength hot-dip galvanized steel sheet excellent in impact peeling resistance and worked portion corrosion resistance
JP6237937B2 (ja) * 2016-03-11 2017-11-29 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
WO2017182833A1 (en) 2016-04-19 2017-10-26 Arcelormittal Method for producing a metallic coated steel sheet
DE102016117474A1 (de) * 2016-09-16 2018-03-22 Benteler Automobiltechnik Gmbh Karosseriebauteil mit reduzierter Rissneigung und Verfahren zur Herstellung
GB2555104B (en) * 2016-10-14 2022-06-01 Liberty Performance Steels Ltd Manufacture of a stress relieved length of steel having an oxidised surface layer
CN106334875A (zh) * 2016-10-27 2017-01-18 宝山钢铁股份有限公司 一种带铝或者铝合金镀层的钢制焊接部件及其制造方法
WO2018096387A1 (en) * 2016-11-24 2018-05-31 Arcelormittal Hot-rolled and coated steel sheet for hot-stamping, hot-stamped coated steel part and methods for manufacturing the same
WO2018115914A1 (en) 2016-12-19 2018-06-28 Arcelormittal A manufacturing process of hot press formed aluminized steel parts
KR101858868B1 (ko) 2016-12-23 2018-05-16 주식회사 포스코 충격특성이 우수한 열간성형용 도금강판, 열간성형 부재 및 그들의 제조방법
US20180237877A1 (en) * 2017-02-17 2018-08-23 GM Global Technology Operations LLC Mitigating liquid metal embrittlement in zinc-coated press hardened steels
CN110214197A (zh) * 2017-02-20 2019-09-06 日本制铁株式会社 热冲压成形体
WO2018179839A1 (ja) * 2017-03-30 2018-10-04 Ｊｆｅスチール株式会社 ホットプレス部材およびその製造方法
DE102017112164A1 (de) * 2017-06-01 2018-12-06 Benteler Automobiltechnik Gmbh Blechumformbauteil sowie Verfahren zur Herstellung des Blechumformbauteils
WO2018220412A1 (fr) 2017-06-01 2018-12-06 Arcelormittal Procede de fabrication de pieces d'acier a haute resistance mecanique et ductilite amelioree, et pieces obtenues par ce procede
WO2018220430A1 (en) 2017-06-02 2018-12-06 Arcelormittal Steel sheet for manufacturing press hardened parts, press hardened part having a combination of high strength and crash ductility, and manufacturing methods thereof
WO2018234839A1 (en) * 2017-06-20 2018-12-27 Arcelormittal ZINC COATED STEEL SHEET HAVING HIGH STRENGTH POINTS WELDABILITY
US10329639B2 (en) * 2017-08-04 2019-06-25 Gm Global Technology Operations Llc. Multilayer steel and method of reducing liquid metal embrittlement
WO2019043422A1 (en) 2017-08-30 2019-03-07 Arcelormittal COATED METALLIC SUBSTRATE
JP7167428B2 (ja) * 2017-11-10 2022-11-09 昭和電工マテリアルズ株式会社 鉄基焼結合金材及びその製造方法
EP3715493A4 (en) 2017-12-27 2020-11-25 JFE Steel Corporation HIGH STRENGTH STEEL SHEET AND METHOD OF MANUFACTURING ITEM
JP6916129B2 (ja) * 2018-03-02 2021-08-11 株式会社神戸製鋼所 ホットスタンプ用亜鉛めっき鋼板およびその製造方法
US11613789B2 (en) 2018-05-24 2023-03-28 GM Global Technology Operations LLC Method for improving both strength and ductility of a press-hardening steel
CN112534078A (zh) 2018-06-19 2021-03-19 通用汽车环球科技运作有限责任公司 具有增强的机械性质的低密度压制硬化钢
CN109433960A (zh) * 2018-09-30 2019-03-08 苏州普热斯勒先进成型技术有限公司 热冲压高强钢汽车车身覆盖件及其制造方法、制造系统
WO2020070545A1 (en) 2018-10-04 2020-04-09 Arcelormittal A press hardening method
JP2020082102A (ja) * 2018-11-19 2020-06-04 株式会社神戸製鋼所 接合構造体及び接合構造体の製造方法
UA127773C2 (uk) 2018-12-18 2023-12-27 Арселорміттал Зміцнена під пресом деталь із високою стійкістю до уповільненого руйнування та спосіб її виготовлення
KR102165223B1 (ko) 2018-12-19 2020-10-13 주식회사 포스코 열간성형 후 충격특성이 우수한 열간성형용 도금강판, 열간성형 부재 및 이들의 제조방법
MX2021007922A (es) * 2019-03-29 2021-08-11 Nippon Steel Corp Miembro de acero revestido, lamina de acero revestida, y metodos para producir los mismos.
US11149327B2 (en) * 2019-05-24 2021-10-19 voestalpine Automotive Components Cartersville Inc. Method and device for heating a steel blank for hardening purposes
US11530469B2 (en) 2019-07-02 2022-12-20 GM Global Technology Operations LLC Press hardened steel with surface layered homogenous oxide after hot forming
WO2021084303A1 (en) * 2019-10-30 2021-05-06 Arcelormittal A press hardening method
WO2021084304A1 (en) * 2019-10-30 2021-05-06 Arcelormittal A press hardening method
WO2021084305A1 (en) * 2019-10-30 2021-05-06 Arcelormittal A press hardening method
WO2021084302A1 (en) * 2019-10-30 2021-05-06 Arcelormittal A press hardening method
WO2021230150A1 (ja) * 2020-05-13 2021-11-18 日本製鉄株式会社 ホットスタンプ用鋼板およびホットスタンプ成形体
CN115151669B (zh) * 2020-05-13 2023-12-26 日本制铁株式会社 热冲压成形体
CN111778467B (zh) * 2020-09-04 2020-11-24 育材堂（苏州）材料科技有限公司 带铝或铝合金预镀层的预镀层钢板、制造方法及热冲压成形构件
WO2022129989A1 (en) * 2020-12-15 2022-06-23 Arcelormittal Annealing method
WO2022129994A1 (en) * 2020-12-16 2022-06-23 Arcelormittal Coated steel sheet and high strength press hardened steel part and method of manufacturing the same
WO2022129995A1 (en) * 2020-12-16 2022-06-23 Arcelormittal Coated steel sheet and high strength press hardened steel part and method of manufacturing the same
US20240060163A1 (en) * 2020-12-23 2024-02-22 Voestalpine Stahl Gmbh A zinc or zinc-alloy coated strip or steel with improved zinc adhesion
CN112877632A (zh) * 2021-01-12 2021-06-01 鞍钢股份有限公司 高塑性热冲压成型用铝硅镀层钢板及其热冲压方法
DE102021201845A1 (de) 2021-02-26 2022-09-01 Volkswagen Aktiengesellschaft Verfahren zur Herstellung eines warmumgeformten und pressgehärteten Stahlblechbauteils
WO2024122120A1 (ja) * 2022-12-09 2024-06-13 日本製鉄株式会社 めっき鋼板
WO2024122119A1 (ja) * 2022-12-09 2024-06-13 日本製鉄株式会社 ホットスタンプ成形体

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE1294402B (de) * 1965-08-06 1969-05-08 Armco Steel Corp Verfahren zur Herstellung eines mit einem Metallueberzug versehenen Eisenmetalls mit stark verbesserter Ziehbarkeit
JPH04276057A (ja) * 1991-03-05 1992-10-01 Nippon Steel Corp めっき密着性の良好な高Ｓｉ含有高張力合金化溶融亜鉛めっき鋼板の製造方法
JPH10130782A (ja) 1996-11-01 1998-05-19 Nippon Steel Corp 超高強度冷延鋼板およびその製造方法
FR2780984B1 (fr) 1998-07-09 2001-06-22 Lorraine Laminage Tole d'acier laminee a chaud et a froid revetue et comportant une tres haute resistance apres traitement thermique
JP4582850B2 (ja) 2000-02-24 2010-11-17 日新製鋼株式会社 曲げ加工性に優れた高強度ステンレス鋼板
FR2807447B1 (fr) * 2000-04-07 2002-10-11 Usinor Procede de realisation d'une piece a tres hautes caracteristiques mecaniques, mise en forme par emboutissage, a partir d'une bande de tole d'acier laminee et notamment laminee a chaud et revetue
CA2520814C (en) * 2003-03-31 2009-09-15 Nippon Steel Corporation Alloyed molten zinc plated steel sheet and process of production of same
BRPI0409569B1 (pt) * 2003-04-10 2013-06-11 processo de produÇço de uma chapa de aÇo revestida de zinco fundido de alta resistÊncia.
JP2006051543A (ja) 2004-07-15 2006-02-23 Nippon Steel Corp 冷延、熱延鋼板もしくはＡｌ系、Ｚｎ系めっき鋼板を使用した高強度自動車部材の熱間プレス方法および熱間プレス部品
JP2006104546A (ja) * 2004-10-08 2006-04-20 Nippon Steel Corp 高強度自動車部材および熱間プレス方法
RU2418094C2 (ru) * 2006-01-30 2011-05-10 Ниппон Стил Корпорейшн Высокопрочный горячеоцинкованный погружением стальной лист и высокопрочный отожженный после цинкования стальной лист с превосходными формуемостью и способностью к нанесению гальванопокрытия и способы изготовления и устройства для изготовления таких листов
KR100760152B1 (ko) 2006-06-07 2007-09-18 현대하이스코 주식회사 핫스탬핑을 이용하여 아연도금강판으로 고강도 자동차용부품을 제조하는 방법
KR101504370B1 (ko) * 2007-02-23 2015-03-19 타타 스틸 이즈무이덴 베.뷔. 초고강도를 갖는 최종 제품을 열가공 정형하는 방법 및 이에 의해 제조된 제품
EP2009129A1 (en) * 2007-06-29 2008-12-31 ArcelorMittal France Process for manufacturing a galvannealed steel sheet by DFF regulation
DE102007061489A1 (de) 2007-12-20 2009-06-25 Voestalpine Stahl Gmbh Verfahren zum Herstellen von gehärteten Bauteilen aus härtbarem Stahl und härtbares Stahlband hierfür
EP2123786A1 (fr) * 2008-05-21 2009-11-25 ArcelorMittal France Procédé de fabrication de tôles d'aciers dual phase laminées à froid à trés haute résistance et tôles ainsi produites
JP5131844B2 (ja) * 2008-08-12 2013-01-30 新日鐵住金株式会社 熱間プレス用熱延鋼板およびその製造方法ならびに熱間プレス鋼板部材の製造方法
DE102008044693B4 (de) * 2008-08-28 2011-02-24 Benteler Automobiltechnik Gmbh Verfahren zur Herstellung gehärteter Bauteile mit mehrfachem Erwärmen
DE102009044861B3 (de) * 2009-12-10 2011-06-22 ThyssenKrupp Steel Europe AG, 47166 Verfahren zum Herstellen eines gut umformbaren Stahlflachprodukts, Stahlflachprodukt und Verfahren zur Herstellung eines Bauteils aus einem solchen Stahlflachprodukt

Also Published As

Publication number Publication date
BR122019008477B1 (pt) 2020-02-18
US20170260599A1 (en) 2017-09-14
PL3783118T3 (pl) 2023-07-10
ES2785071T3 (es) 2020-10-05
RU2015112317A (ru) 2016-10-27
EP3783117A1 (fr) 2021-02-24
EP3783116A1 (fr) 2021-02-24
EP3783118A1 (fr) 2021-02-24
PL2893047T3 (pl) 2020-10-19
JP6359155B2 (ja) 2018-07-18
EP3783118B1 (fr) 2023-04-12
CN104769138A (zh) 2015-07-08
EP2893047A1 (fr) 2015-07-15
IN2015DN01908A (pl) 2015-08-07
ES2945840T3 (es) 2023-07-07
JP2016504488A (ja) 2016-02-12
FI3783116T3 (fi) 2023-06-14
CN104769138B (zh) 2017-03-08
JP2018012884A (ja) 2018-01-25
ZA201501534B (en) 2016-01-27
MX2019002069A (es) 2019-06-03
ES2946442T3 (es) 2023-07-18
CA2895944A1 (fr) 2015-03-12
WO2014037627A1 (fr) 2014-03-13
BR112015005090B8 (pt) 2019-09-03
MX2015002972A (es) 2015-11-11
US9909194B2 (en) 2018-03-06
MX366129B (es) 2019-06-28
BR112015005090B1 (pt) 2019-08-06
KR20150047627A (ko) 2015-05-04
WO2015033177A8 (fr) 2015-04-30
JP6166787B2 (ja) 2017-07-19
BR112015005090A2 (pt) 2017-07-04
HUE049636T2 (hu) 2020-09-28
EP2893047B1 (fr) 2020-04-01
EP3783116B1 (fr) 2023-04-26
RU2610995C2 (ru) 2017-02-17
HUE061920T2 (hu) 2023-08-28
UA115791C2 (uk) 2017-12-26
HUE062051T2 (hu) 2023-09-28
US9957582B2 (en) 2018-05-01
FI3783118T3 (fi) 2023-06-15
CA2895944C (fr) 2018-02-13
MA37932B1 (fr) 2016-06-30
BR112015005090A8 (pt) 2019-06-25
KR101643513B1 (ko) 2016-07-27
WO2015033177A1 (fr) 2015-03-12
US20160017452A1 (en) 2016-01-21
MA20150410A1 (fr) 2015-11-30

Similar Documents

Publication Publication Date Title
PL3783116T3 (pl) Wstępnie powlekane blachy do wytwarzania powlekanych i utwardzanych ciśnieniowo części stalowych
ZA201401304B (en) High-strength steel sheet and high-strength galvanised steel sheet excellent inshapeability and methods of production of same
EP2813595A4 (en) HIGHLESS COLD-ROLLED STEEL PLATE AND METHOD FOR THE PRODUCTION THEREOF
EP2857544A4 (en) BLACK PLATED STEEL PLATE
EP2824210A4 (en) HIGH STRENGTH COLD LAMINATED STEEL SHEET AND METHOD FOR MANUFACTURING THE SAME
EP2987884A4 (en) HOT-ROLLED STEEL PLATE
PL2692895T3 (pl) Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
ZA201500132B (en) Steel material
EP2960353A4 (en) HIGH-FIXED COLD-ROLLED STEEL PLATE WITH EXCELLENT BENDING CAPACITY
PL2891727T3 (pl) Blacha stalowa cienka
PL2818569T3 (pl) Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
ZA201207927B (en) High-strength cold-rolled steel sheet and method for manufacturing the same
EP2933346A4 (en) COLD-ROLLED STEEL PLATE AND MANUFACTURING METHOD THEREFOR
SG11201502932TA (en) Compounds and methods for the production of suckerin and uses thereof
EP2881443A4 (en) PAINT, AND COATED STEEL MATERIAL
EP2826881A4 (en) HIGH STRENGTH STEEL PLATE AND METHOD FOR THE PRODUCTION THEREOF
EP2730672A4 (en) COLD LAMINATED STEEL SHEET
PL2864213T3 (pl) Dwuczęściowa puszka z blachy stalowej ocynowanej częściowo powlekana
EP2801019A4 (en) MAINTENANCE OF CLOSED APPLICATIONS IN HISTORIC STACK
EP2808414A4 (en) ELECTROMAGNETIC STEEL PLATE
ZA201409300B (en) Steel material
EP2933348A4 (en) ORIENTED ELECTROMAGNETIC STEEL PLATE
EP2918694A4 (en) STEEL ELEMENT AND PROCESS FOR PRODUCING THE SAME
ZA201209143B (en) High strength steel sheet.
HK1206403A1 (en) Combined steel wall