BR112015005090B8 - chapa laminada a frio e recozida - Google Patents

chapa laminada a frio e recozida Download PDF

Info

Publication number
BR112015005090B8
BR112015005090B8 BR112015005090A BR112015005090A BR112015005090B8 BR 112015005090 B8 BR112015005090 B8 BR 112015005090B8 BR 112015005090 A BR112015005090 A BR 112015005090A BR 112015005090 A BR112015005090 A BR 112015005090A BR 112015005090 B8 BR112015005090 B8 BR 112015005090B8
Authority
BR
Brazil
Prior art keywords
cold rolled
sheet
content
substrate
depth
Prior art date
Application number
BR112015005090A
Other languages
English (en)
Other versions
BR112015005090A8 (pt
BR112015005090B1 (pt
BR112015005090A2 (pt
Inventor
Staudte Jonas
David Puerta Velasquez Juan
Drillet Pascal
Original Assignee
Arcelormittal Investigacion Y Desarrollo Sl
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal Investigacion Y Desarrollo Sl filed Critical Arcelormittal Investigacion Y Desarrollo Sl
Priority to BR122019008477-7A priority Critical patent/BR122019008477B1/pt
Publication of BR112015005090A2 publication Critical patent/BR112015005090A2/pt
Publication of BR112015005090A8 publication Critical patent/BR112015005090A8/pt
Publication of BR112015005090B1 publication Critical patent/BR112015005090B1/pt
Publication of BR112015005090B8 publication Critical patent/BR112015005090B8/pt

Abstract

chapa laminada a frio e recozida e processo de fabricação de uma peça de aço trata-se de uma chapa laminada a frio que é recozida e prérevestida para a fabricação de peças enrijecidas a prensa, composta de um substrato de aço para tratamento térmico com um teor de carbono c0 entre 0,07% e 0,5%, por meio de que esse teor é expresso em peso e um prérevestimento de metal em pelo menos duas faces principais do substrato de aço, caracterizado pelo fato de que o substrato compreende uma área descarburizada na superfície de cada uma das duas faces principais, por meio de que a profundidade p50% da área descarburizada é entre 6 e 30 micrômetros, por meio de que p50% é a profundidade na qual o teor de carbono é igual a 50% do teor c0 e em que a chapa não contém uma camada de óxidode ferro entre o substrato e o pré-revestimento de metal.
BR112015005090A 2012-09-06 2013-09-06 chapa laminada a frio e recozida BR112015005090B8 (pt)

Priority Applications (1)

Application Number Priority Date Filing Date Title
BR122019008477-7A BR122019008477B1 (pt) 2012-09-06 2013-09-06 Processo de fabricação de uma peça de aço

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
PCT/FR2012/000350 WO2014037627A1 (fr) 2012-09-06 2012-09-06 Procede de fabrication de pieces d'acier revêtues et durcies a la presse, et tôles prerevêtues permettant la fabrication de ces pieces
FRPCT/FR2012/000350 2012-09-06
PCT/IB2013/001914 WO2015033177A1 (fr) 2012-09-06 2013-09-06 Procédé de fabrication de pièces d'acier revêtues et durcies a la presse, et tôles prérevêtues permettant la fabrication de ces pièces

Publications (4)

Publication Number Publication Date
BR112015005090A2 BR112015005090A2 (pt) 2017-07-04
BR112015005090A8 BR112015005090A8 (pt) 2019-06-25
BR112015005090B1 BR112015005090B1 (pt) 2019-08-06
BR112015005090B8 true BR112015005090B8 (pt) 2019-09-03

Family

ID=46982626

Family Applications (2)

Application Number Title Priority Date Filing Date
BR122019008477-7A BR122019008477B1 (pt) 2012-09-06 2013-09-06 Processo de fabricação de uma peça de aço
BR112015005090A BR112015005090B8 (pt) 2012-09-06 2013-09-06 chapa laminada a frio e recozida

Family Applications Before (1)

Application Number Title Priority Date Filing Date
BR122019008477-7A BR122019008477B1 (pt) 2012-09-06 2013-09-06 Processo de fabricação de uma peça de aço

Country Status (18)

Country Link
US (2) US9909194B2 (pt)
EP (4) EP3783117A1 (pt)
JP (2) JP6166787B2 (pt)
KR (1) KR101643513B1 (pt)
CN (1) CN104769138B (pt)
BR (2) BR122019008477B1 (pt)
CA (1) CA2895944C (pt)
ES (3) ES2946442T3 (pt)
FI (2) FI3783116T3 (pt)
HU (3) HUE062051T2 (pt)
IN (1) IN2015DN01908A (pt)
MA (1) MA37932B1 (pt)
MX (2) MX366129B (pt)
PL (3) PL2893047T3 (pt)
RU (1) RU2610995C2 (pt)
UA (1) UA115791C2 (pt)
WO (2) WO2014037627A1 (pt)
ZA (1) ZA201501534B (pt)

Families Citing this family (56)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2984198B1 (en) 2013-04-10 2021-06-23 Tata Steel IJmuiden B.V. Product formed by hot forming of metallic coated steel sheet, method to form the product, and steel strip
JP5852690B2 (ja) * 2013-04-26 2016-02-03 株式会社神戸製鋼所 ホットスタンプ用合金化溶融亜鉛めっき鋼板
WO2015088501A1 (en) * 2013-12-10 2015-06-18 Arcelormittal Investigacion Y Desarrollo A method of annealing steel sheets
WO2016079565A1 (en) * 2014-11-18 2016-05-26 Arcelormittal Method for manufacturing a high strength steel product and steel product thereby obtained
WO2016132165A1 (fr) * 2015-02-19 2016-08-25 Arcelormittal Procede de fabrication d'une piece phosphatable a partir d'une tole revetue d'un revetement a base d'aluminium et d'un revetement de zinc
WO2017006144A1 (en) 2015-07-09 2017-01-12 Arcelormittal Steel for press hardening and press hardened part manufactured from such steel
JP2017066508A (ja) * 2015-10-02 2017-04-06 株式会社神戸製鋼所 熱間プレス用亜鉛めっき鋼板および熱間プレス成形品の製造方法
WO2017098304A1 (en) * 2015-12-09 2017-06-15 Arcelormittal Method for producing an automotive structural part comprising a lowerside sill and a lower front pillar
DE102015016656A1 (de) * 2015-12-19 2017-06-22 GM Global Technology Operations LLC (n. d. Ges. d. Staates Delaware) Verfahren zur Herstellung eines beschichteten, durch Warmumformung gehärteten Körpers sowie ein nach dem Verfahren hergestellter Körper
KR101696121B1 (ko) 2015-12-23 2017-01-13 주식회사 포스코 내수소지연파괴특성, 내박리성 및 용접성이 우수한 열간성형용 알루미늄-철 합금 도금강판 및 이를 이용한 열간성형 부재
DE102016100648B4 (de) 2015-12-23 2018-04-12 Benteler Automobiltechnik Gmbh Wärmebehandlungsofen sowie Verfahren zur Wärmebehandlung einer vorbeschichteten Stahlblechplatine und Verfahren zur Herstellung eines Kraftfahrzeugbauteils
DE102016102504A1 (de) * 2016-02-08 2017-08-10 Salzgitter Flachstahl Gmbh Aluminiumbasierte Beschichtung für Stahlbleche oder Stahlbänder und Verfahren zur Herstellung hierzu
ES2820311T3 (es) * 2016-02-25 2021-04-20 Nippon Steel Corp Lámina de acero galvanizado por inmersión en caliente de alta resistencia con excelente resistencia al desprendimiento por impacto y resistencia a la corrosión de la porción mecanizada
JP6237937B2 (ja) * 2016-03-11 2017-11-29 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
WO2017182833A1 (en) 2016-04-19 2017-10-26 Arcelormittal Method for producing a metallic coated steel sheet
DE102016117474A1 (de) * 2016-09-16 2018-03-22 Benteler Automobiltechnik Gmbh Karosseriebauteil mit reduzierter Rissneigung und Verfahren zur Herstellung
GB2555104B (en) * 2016-10-14 2022-06-01 Liberty Performance Steels Ltd Manufacture of a stress relieved length of steel having an oxidised surface layer
CN106334875A (zh) * 2016-10-27 2017-01-18 宝山钢铁股份有限公司 一种带铝或者铝合金镀层的钢制焊接部件及其制造方法
WO2018096387A1 (en) * 2016-11-24 2018-05-31 Arcelormittal Hot-rolled and coated steel sheet for hot-stamping, hot-stamped coated steel part and methods for manufacturing the same
WO2018115914A1 (en) * 2016-12-19 2018-06-28 Arcelormittal A manufacturing process of hot press formed aluminized steel parts
KR101858868B1 (ko) 2016-12-23 2018-05-16 주식회사 포스코 충격특성이 우수한 열간성형용 도금강판, 열간성형 부재 및 그들의 제조방법
US20180237877A1 (en) * 2017-02-17 2018-08-23 GM Global Technology Operations LLC Mitigating liquid metal embrittlement in zinc-coated press hardened steels
JP6617836B2 (ja) * 2017-02-20 2019-12-11 日本製鉄株式会社 ホットスタンプ成形体
WO2018179839A1 (ja) * 2017-03-30 2018-10-04 Ｊｆｅスチール株式会社 ホットプレス部材およびその製造方法
WO2018220412A1 (fr) 2017-06-01 2018-12-06 Arcelormittal Procede de fabrication de pieces d'acier a haute resistance mecanique et ductilite amelioree, et pieces obtenues par ce procede
DE102017112164A1 (de) * 2017-06-01 2018-12-06 Benteler Automobiltechnik Gmbh Blechumformbauteil sowie Verfahren zur Herstellung des Blechumformbauteils
WO2018220430A1 (en) 2017-06-02 2018-12-06 Arcelormittal Steel sheet for manufacturing press hardened parts, press hardened part having a combination of high strength and crash ductility, and manufacturing methods thereof
WO2018234839A1 (en) * 2017-06-20 2018-12-27 Arcelormittal ZINC COATED STEEL SHEET HAVING HIGH STRENGTH POINTS WELDABILITY
US10329639B2 (en) * 2017-08-04 2019-06-25 Gm Global Technology Operations Llc. Multilayer steel and method of reducing liquid metal embrittlement
WO2019043422A1 (en) 2017-08-30 2019-03-07 Arcelormittal COATED METALLIC SUBSTRATE
JP7167428B2 (ja) * 2017-11-10 2022-11-09 昭和電工マテリアルズ株式会社 鉄基焼結合金材及びその製造方法
EP3715493A4 (en) * 2017-12-27 2020-11-25 JFE Steel Corporation HIGH STRENGTH STEEL SHEET AND METHOD OF MANUFACTURING ITEM
JP6916129B2 (ja) * 2018-03-02 2021-08-11 株式会社神戸製鋼所 ホットスタンプ用亜鉛めっき鋼板およびその製造方法
WO2019222950A1 (en) 2018-05-24 2019-11-28 GM Global Technology Operations LLC A method for improving both strength and ductility of a press-hardening steel
US11612926B2 (en) 2018-06-19 2023-03-28 GM Global Technology Operations LLC Low density press-hardening steel having enhanced mechanical properties
CN109433960A (zh) * 2018-09-30 2019-03-08 苏州普热斯勒先进成型技术有限公司 热冲压高强钢汽车车身覆盖件及其制造方法、制造系统
WO2020070545A1 (en) 2018-10-04 2020-04-09 Arcelormittal A press hardening method
JP2020082102A (ja) * 2018-11-19 2020-06-04 株式会社神戸製鋼所 接合構造体及び接合構造体の製造方法
BR112021006244B1 (pt) 2018-12-18 2023-04-04 Arcelormittal Peça de aço revestida endurecida por prensagem, processo para fabricar uma peça de aço revestida endurecida por prensagem e uso de uma peça endurecida por prensagem
KR102165223B1 (ko) 2018-12-19 2020-10-13 주식회사 포스코 열간성형 후 충격특성이 우수한 열간성형용 도금강판, 열간성형 부재 및 이들의 제조방법
JP7111252B2 (ja) * 2019-03-29 2022-08-02 日本製鉄株式会社 被覆鋼部材、被覆鋼板およびそれらの製造方法
US11149327B2 (en) * 2019-05-24 2021-10-19 voestalpine Automotive Components Cartersville Inc. Method and device for heating a steel blank for hardening purposes
US11530469B2 (en) 2019-07-02 2022-12-20 GM Global Technology Operations LLC Press hardened steel with surface layered homogenous oxide after hot forming
WO2021084303A1 (en) * 2019-10-30 2021-05-06 Arcelormittal A press hardening method
WO2021084304A1 (en) * 2019-10-30 2021-05-06 Arcelormittal A press hardening method
WO2021084305A1 (en) * 2019-10-30 2021-05-06 Arcelormittal A press hardening method
WO2021084302A1 (en) * 2019-10-30 2021-05-06 Arcelormittal A press hardening method
KR20220129061A (ko) * 2020-05-13 2022-09-22 닛폰세이테츠 가부시키가이샤 핫 스탬프 성형체
US20230081832A1 (en) * 2020-05-13 2023-03-16 Nippon Steel Corporation Steel sheet for hot stamping and hot-stamping formed body
CN111778467B (zh) * 2020-09-04 2020-11-24 育材堂（苏州）材料科技有限公司 带铝或铝合金预镀层的预镀层钢板、制造方法及热冲压成形构件
WO2022129989A1 (en) * 2020-12-15 2022-06-23 Arcelormittal Annealing method
WO2022129995A1 (en) * 2020-12-16 2022-06-23 Arcelormittal Coated steel sheet and high strength press hardened steel part and method of manufacturing the same
WO2022129994A1 (en) * 2020-12-16 2022-06-23 Arcelormittal Coated steel sheet and high strength press hardened steel part and method of manufacturing the same
US20240060163A1 (en) * 2020-12-23 2024-02-22 Voestalpine Stahl Gmbh A zinc or zinc-alloy coated strip or steel with improved zinc adhesion
CN112877632A (zh) * 2021-01-12 2021-06-01 鞍钢股份有限公司 高塑性热冲压成型用铝硅镀层钢板及其热冲压方法
DE102021201845A1 (de) 2021-02-26 2022-09-01 Volkswagen Aktiengesellschaft Verfahren zur Herstellung eines warmumgeformten und pressgehärteten Stahlblechbauteils

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE1294402B (de) * 1965-08-06 1969-05-08 Armco Steel Corp Verfahren zur Herstellung eines mit einem Metallueberzug versehenen Eisenmetalls mit stark verbesserter Ziehbarkeit
JPH04276057A (ja) * 1991-03-05 1992-10-01 Nippon Steel Corp めっき密着性の良好な高Ｓｉ含有高張力合金化溶融亜鉛めっき鋼板の製造方法
JPH10130782A (ja) 1996-11-01 1998-05-19 Nippon Steel Corp 超高強度冷延鋼板およびその製造方法
FR2780984B1 (fr) 1998-07-09 2001-06-22 Lorraine Laminage Tole d'acier laminee a chaud et a froid revetue et comportant une tres haute resistance apres traitement thermique
JP4582850B2 (ja) * 2000-02-24 2010-11-17 日新製鋼株式会社 曲げ加工性に優れた高強度ステンレス鋼板
FR2807447B1 (fr) * 2000-04-07 2002-10-11 Usinor Procede de realisation d'une piece a tres hautes caracteristiques mecaniques, mise en forme par emboutissage, a partir d'une bande de tole d'acier laminee et notamment laminee a chaud et revetue
PL1634975T3 (pl) * 2003-03-31 2010-11-30 Nippon Steel Corp Stopowana blacha stalowa powlekana zanurzeniowo na gorąco cynkiem oraz sposób jej wytwarzania
KR100979786B1 (ko) * 2003-04-10 2010-09-03 신닛뽄세이테쯔 카부시키카이샤 고강도 용융 아연 도금 강판 및 그 제조 방법
JP2006051543A (ja) 2004-07-15 2006-02-23 Nippon Steel Corp 冷延、熱延鋼板もしくはＡｌ系、Ｚｎ系めっき鋼板を使用した高強度自動車部材の熱間プレス方法および熱間プレス部品
JP2006104546A (ja) * 2004-10-08 2006-04-20 Nippon Steel Corp 高強度自動車部材および熱間プレス方法
RU2418094C2 (ru) * 2006-01-30 2011-05-10 Ниппон Стил Корпорейшн Высокопрочный горячеоцинкованный погружением стальной лист и высокопрочный отожженный после цинкования стальной лист с превосходными формуемостью и способностью к нанесению гальванопокрытия и способы изготовления и устройства для изготовления таких листов
KR100760152B1 (ko) * 2006-06-07 2007-09-18 현대하이스코 주식회사 핫스탬핑을 이용하여 아연도금강판으로 고강도 자동차용부품을 제조하는 방법
WO2008102012A1 (en) * 2007-02-23 2008-08-28 Corus Staal Bv Method of thermomechanical shaping a final product with very high strength and a product produced thereby
EP2009129A1 (en) * 2007-06-29 2008-12-31 ArcelorMittal France Process for manufacturing a galvannealed steel sheet by DFF regulation
DE102007061489A1 (de) 2007-12-20 2009-06-25 Voestalpine Stahl Gmbh Verfahren zum Herstellen von gehärteten Bauteilen aus härtbarem Stahl und härtbares Stahlband hierfür
EP2123786A1 (fr) * 2008-05-21 2009-11-25 ArcelorMittal France Procédé de fabrication de tôles d'aciers dual phase laminées à froid à trés haute résistance et tôles ainsi produites
JP5131844B2 (ja) * 2008-08-12 2013-01-30 新日鐵住金株式会社 熱間プレス用熱延鋼板およびその製造方法ならびに熱間プレス鋼板部材の製造方法
DE102008044693B4 (de) * 2008-08-28 2011-02-24 Benteler Automobiltechnik Gmbh Verfahren zur Herstellung gehärteter Bauteile mit mehrfachem Erwärmen
DE102009044861B3 (de) * 2009-12-10 2011-06-22 ThyssenKrupp Steel Europe AG, 47166 Verfahren zum Herstellen eines gut umformbaren Stahlflachprodukts, Stahlflachprodukt und Verfahren zur Herstellung eines Bauteils aus einem solchen Stahlflachprodukt

Also Published As

Publication number Publication date
ES2945840T3 (es) 2023-07-07
HUE061920T2 (hu) 2023-08-28
KR101643513B1 (ko) 2016-07-27
WO2015033177A1 (fr) 2015-03-12
BR122019008477B1 (pt) 2020-02-18
EP3783116B1 (fr) 2023-04-26
WO2014037627A1 (fr) 2014-03-13
JP6359155B2 (ja) 2018-07-18
JP6166787B2 (ja) 2017-07-19
RU2015112317A (ru) 2016-10-27
EP2893047B1 (fr) 2020-04-01
KR20150047627A (ko) 2015-05-04
BR112015005090A8 (pt) 2019-06-25
US20170260599A1 (en) 2017-09-14
US9957582B2 (en) 2018-05-01
CN104769138B (zh) 2017-03-08
JP2018012884A (ja) 2018-01-25
MA20150410A1 (fr) 2015-11-30
HUE062051T2 (hu) 2023-09-28
BR112015005090B1 (pt) 2019-08-06
ZA201501534B (en) 2016-01-27
EP3783118A1 (fr) 2021-02-24
WO2015033177A8 (fr) 2015-04-30
MA37932B1 (fr) 2016-06-30
ES2946442T3 (es) 2023-07-18
PL3783118T3 (pl) 2023-07-10
EP3783118B1 (fr) 2023-04-12
EP2893047A1 (fr) 2015-07-15
ES2785071T3 (es) 2020-10-05
MX2019002069A (es) 2019-06-03
CA2895944C (fr) 2018-02-13
BR112015005090A2 (pt) 2017-07-04
HUE049636T2 (hu) 2020-09-28
EP3783117A1 (fr) 2021-02-24
PL3783116T3 (pl) 2023-07-10
CA2895944A1 (fr) 2015-03-12
US9909194B2 (en) 2018-03-06
MX2015002972A (es) 2015-11-11
FI3783116T3 (fi) 2023-06-14
IN2015DN01908A (pt) 2015-08-07
PL2893047T3 (pl) 2020-10-19
FI3783118T3 (fi) 2023-06-15
JP2016504488A (ja) 2016-02-12
RU2610995C2 (ru) 2017-02-17
UA115791C2 (uk) 2017-12-26
US20160017452A1 (en) 2016-01-21
MX366129B (es) 2019-06-28
CN104769138A (zh) 2015-07-08
EP3783116A1 (fr) 2021-02-24

Similar Documents

Publication Publication Date Title
BR112015005090B8 (pt) chapa laminada a frio e recozida
BR112015024854A2 (pt) chapa de aço laminada a quente e método para sua produção
IN2014DN07785A (pt)
MX2021003967A (es) Metodo para producir partes de acero recubiertas y conformadas en prensa a una tasa alta de productividad.
BR112016013130A2 (pt) Folha de aço e método para fabricar uma folha de aço
BR112018000234A2 (pt) chapa de aço elétrico de grão orientado e método para produção da mesma
MX2020004769A (es) Hoja de acero laminada en frio y un metodo para la fabricacion de la misma.
BR112013023633A2 (pt) chapa de aço laminada a quente com excelente capacidade de conformação por prensagem e seu método de produção
BR112013001864A2 (pt) chapa de aço laminada a quente, chapa de aço laminada a frio, chapa de aço galvanizada e método de produção da mesma
BR112013023792A2 (pt) chapa de aço para elemento gravado a quente e método de produção da mesma
BR112012029698A2 (pt) método de produção de uma chapa de aço de alta resistência para uma estrutura soldada
BR112015020187A2 (pt) método de produção de chapas de aço elétrico de grão orientado
MX2017009931A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma.
MX2016005086A (es) Lamina de acero laminada en caliente que tiene excelente dureza de superficie despues de tratamiento termico carburizante y excelente capacidad de estiramiento.
BR112013002583A2 (pt) método de fabricação de chapa de aço elétrica não orientada
MX2019014336A (es) Lamina de acero electrico de grano no orientado y metodo para la fabricacion de la misma.
IN2015DN01537A (pt)
BR112015004191A2 (pt) chapa de aço
BR112015030003A2 (pt) chapa de aço laminada a frio, chapa de aço laminada a frio galvanizada e método de produção da mesma
MX2016003390A (es) Soldadura por proyeccion de laminas metalicas.
IN2015DN01536A (pt)
MX2017009930A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma.
BR112015021826A2 (pt) arame de aço para mola e método para fabricação do mesmo
PH12018500105A1 (en) High formability dual phase steel
QU et al. Fiber laser remelting technology of 45 steel

Legal Events

Date Code Title Description
B06F Objections, documents and/or translations needed after an examination request according [chapter 6.6 patent gazette]
B07A Application suspended after technical examination (opinion) [chapter 7.1 patent gazette]
B09A Decision: intention to grant [chapter 9.1 patent gazette]
B16A Patent or certificate of addition of invention granted [chapter 16.1 patent gazette]

Free format text: PRAZO DE VALIDADE: 20 (VINTE) ANOS CONTADOS A PARTIR DE 06/09/2013, OBSERVADAS AS CONDICOES LEGAIS. (CO) 20 (VINTE) ANOS CONTADOS A PARTIR DE 06/09/2013, OBSERVADAS AS CONDICOES LEGAIS

B16C Correction of notification of the grant [chapter 16.3 patent gazette]

Free format text: PRAZO DE VALIDADE: 20 (VINTE) ANOS CONTADOS A PARTIR DE 06/09/2013, OBSERVADAS AS CONDICOES LEGAIS. (CO) REF. RPI 2535 DE 06/08/2019 QUANTO AO ENDERECO.