CA2879710C - Ultra-high molecular weight polyethylene fiber and method to produce - Google Patents

Ultra-high molecular weight polyethylene fiber and method to produce Download PDF

Info

Publication number
CA2879710C
CA2879710C CA2879710A CA2879710A CA2879710C CA 2879710 C CA2879710 C CA 2879710C CA 2879710 A CA2879710 A CA 2879710A CA 2879710 A CA2879710 A CA 2879710A CA 2879710 C CA2879710 C CA 2879710C
Authority
CA
Canada
Prior art keywords
fiber
fibers
protective coating
treated
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CA2879710A
Other languages
English (en)
French (fr)
Other versions
CA2879710A1 (en
Inventor
Ralf Klein
Henry Gerard Ardiff
John Armstrong Young
Thomas Tam
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Honeywell International Inc
Original Assignee
Honeywell International Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Honeywell International Inc filed Critical Honeywell International Inc
Publication of CA2879710A1 publication Critical patent/CA2879710A1/en
Application granted granted Critical
Publication of CA2879710C publication Critical patent/CA2879710C/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01D—MECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
    • D01D10/00—Physical treatment of artificial filaments or the like during manufacture, i.e. during a continuous production process before the filaments have been collected
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06L—DRY-CLEANING, WASHING OR BLEACHING FIBRES, FILAMENTS, THREADS, YARNS, FABRICS, FEATHERS OR MADE-UP FIBROUS GOODS; BLEACHING LEATHER OR FURS
    • D06L1/00—Dry-cleaning or washing fibres, filaments, threads, yarns, fabrics, feathers or made-up fibrous goods
    • D06L1/12—Dry-cleaning or washing fibres, filaments, threads, yarns, fabrics, feathers or made-up fibrous goods using aqueous solvents
    • D—TEXTILES; PAPER
    • D02—YARNS; MECHANICAL FINISHING OF YARNS OR ROPES; WARPING OR BEAMING
    • D02G—CRIMPING OR CURLING FIBRES, FILAMENTS, THREADS, OR YARNS; YARNS OR THREADS
    • D02G3/00—Yarns or threads, e.g. fancy yarns; Processes or apparatus for the production thereof, not otherwise provided for
    • D02G3/22—Yarns or threads characterised by constructional features, e.g. blending, filament/fibre
    • D02G3/36—Cored or coated yarns or threads
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H3/00—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length
    • D04H3/005—Synthetic yarns or filaments
    • D04H3/007—Addition polymers
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06B—TREATING TEXTILE MATERIALS USING LIQUIDS, GASES OR VAPOURS
    • D06B1/00—Applying liquids, gases or vapours onto textile materials to effect treatment, e.g. washing, dyeing, bleaching, sizing or impregnating
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M10/00—Physical treatment of fibres, threads, yarns, fabrics or fibrous goods made from such materials, e.g. by ultrasonic waves, corona discharge, irradiation, electric currents or magnetic fields; Physical treatment combined with treatment with chemical compounds or elements
    • D06M10/02—Sonic or ultrasonic waves; Corona discharge
    • D06M10/025—Corona discharge or low temperature plasma
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M15/00—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M15/00—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment
    • D06M15/19—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment with synthetic macromolecular compounds
    • D06M15/37—Macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
    • D06M15/564—Polyureas, polyurethanes or other polymers having ureide or urethane links; Precondensation products forming them
    • D06M15/572—Reaction products of isocyanates with polyesters or polyesteramides
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M15/00—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment
    • D06M15/693—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment with natural or synthetic rubber, or derivatives thereof
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M15/00—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment
    • D06M15/70—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment combined with mechanical treatment
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F26—DRYING
    • F26B—DRYING SOLID MATERIALS OR OBJECTS BY REMOVING LIQUID THEREFROM
    • F26B13/00—Machines and apparatus for drying fabrics, fibres, yarns, or other materials in long lengths, with progressive movement
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M2101/00—Chemical constitution of the fibres, threads, yarns, fabrics or fibrous goods made from such materials, to be treated
    • D06M2101/16—Synthetic fibres, other than mineral fibres
    • D06M2101/18—Synthetic fibres consisting of macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D06M2101/20—Polyalkenes, polymers or copolymers of compounds with alkenyl groups bonded to aromatic groups
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]
    • Y10T442/603—Including strand or fiber material precoated with other than free metal or alloy
    • Y10T442/607—Strand or fiber material is synthetic polymer

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Plasma & Fusion (AREA)
  • General Engineering & Computer Science (AREA)
  • Chemical Or Physical Treatment Of Fibers (AREA)
  • Treatments For Attaching Organic Compounds To Fibrous Goods (AREA)
  • Chemical Treatment Of Fibers During Manufacturing Processes (AREA)
  • Yarns And Mechanical Finishing Of Yarns Or Ropes (AREA)
CA2879710A 2012-07-27 2013-07-16 Ultra-high molecular weight polyethylene fiber and method to produce Active CA2879710C (en)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
US201261676409P 2012-07-27 2012-07-27
US61/676,409 2012-07-27
US13/795,278 2013-03-12
US13/795,278 US10132006B2 (en) 2012-07-27 2013-03-12 UHMWPE fiber and method to produce
PCT/US2013/050590 WO2014058497A2 (en) 2012-07-27 2013-07-16 Novel uhmwpe fiber and method to produce

Publications (2)

Publication Number Publication Date
CA2879710A1 CA2879710A1 (en) 2014-04-17
CA2879710C true CA2879710C (en) 2021-07-06

Family

ID=50188173

Family Applications (1)

Application Number Title Priority Date Filing Date
CA2879710A Active CA2879710C (en) 2012-07-27 2013-07-16 Ultra-high molecular weight polyethylene fiber and method to produce

Country Status (13)

Country Link
US (1) US10132006B2 (cg-RX-API-DMAC10.html)
EP (1) EP2877624B1 (cg-RX-API-DMAC10.html)
JP (1) JP6239618B2 (cg-RX-API-DMAC10.html)
KR (1) KR102084617B1 (cg-RX-API-DMAC10.html)
CN (1) CN104662221A (cg-RX-API-DMAC10.html)
BR (1) BR112015001823B1 (cg-RX-API-DMAC10.html)
CA (1) CA2879710C (cg-RX-API-DMAC10.html)
ES (1) ES2750474T3 (cg-RX-API-DMAC10.html)
IL (1) IL236875B (cg-RX-API-DMAC10.html)
IN (1) IN2015DN00573A (cg-RX-API-DMAC10.html)
MX (1) MX367336B (cg-RX-API-DMAC10.html)
TW (1) TWI618824B (cg-RX-API-DMAC10.html)
WO (1) WO2014058497A2 (cg-RX-API-DMAC10.html)

Families Citing this family (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA2807466C (fr) * 2010-08-03 2017-08-01 Soletanche Freyssinet Toron, cable de structure et procede de fabrication du toron
BR122020002315B1 (pt) * 2013-10-29 2021-06-15 Braskem S.A. Método e sistema de pré-recuperação mecânica de pelo menos um líquido em pelo menos um fio polimérico
US9909240B2 (en) 2014-11-04 2018-03-06 Honeywell International Inc. UHMWPE fiber and method to produce
CN104848655B (zh) * 2015-06-02 2017-03-01 天华化工机械及自动化研究设计院有限公司 一种用于超高分子量聚乙烯氮气密闭循环流化床干燥方法
US10272640B2 (en) * 2015-09-17 2019-04-30 Honeywell International Inc. Low porosity high strength UHMWPE fabrics
WO2017090270A1 (ja) * 2015-11-24 2017-06-01 株式会社サンライン 糸およびその製造方法
US10605573B2 (en) 2016-04-15 2020-03-31 Honeywell International Inc. High buoyancy composite materials
CN110418864A (zh) * 2017-03-06 2019-11-05 浙江全米特新材料科技有限公司 一种超高分子量聚乙烯纤维的表面处理方法和处理后纤维的应用
CN108532286A (zh) * 2017-03-06 2018-09-14 浙江全米特新材料科技有限公司 一种超高分子量聚乙烯纤维的表面处理方法和处理后纤维的应用
US20190169793A1 (en) * 2017-12-04 2019-06-06 Torsten D. Quinlan Anti-fray formulation for aramid yarns
DE102017129897A1 (de) * 2017-12-14 2019-06-19 Kiekert Ag Stellantrieb für kraftfahrzeugtechnische Anwendungen
CN108796741A (zh) * 2018-06-27 2018-11-13 南通新帝克单丝科技股份有限公司 超高分子量聚乙烯纤维的表面处理及eva树脂涂层方法
CN109183463A (zh) * 2018-07-24 2019-01-11 江苏工程职业技术学院 一种防切割面料的染色方法
CN110485149A (zh) * 2019-08-23 2019-11-22 沈阳航空航天大学 在线连续改善超高分子量聚乙烯纤维浸润性能的方法、装置及应用
CN112877802B (zh) * 2019-11-29 2025-12-05 霍尼韦尔安全产品美国股份有限公司 抗菌纤维
CN118127801A (zh) * 2024-03-18 2024-06-04 康赛妮集团有限公司 一种羊绒纺线电晕处理方法及设备
US12546035B1 (en) * 2024-12-31 2026-02-10 Advance Denim Co., Ltd. Elastic yarn and elastic fabric

Family Cites Families (63)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
HU167183B (cg-RX-API-DMAC10.html) 1974-04-19 1975-08-28
US4091855A (en) 1976-10-26 1978-05-30 Allied Chemical Corporation Process for improving the ammonolytic stability of polyester textile yarn
US4413110A (en) 1981-04-30 1983-11-01 Allied Corporation High tenacity, high modulus polyethylene and polypropylene fibers and intermediates therefore
EP0091547B2 (en) * 1982-03-19 1993-02-24 Allied Corporation Coated extended chain polyolefin fiber
US4563392A (en) * 1982-03-19 1986-01-07 Allied Corporation Coated extended chain polyolefin fiber
NL8501128A (nl) 1985-04-18 1986-11-17 Stamicarbon Werkwijze voor het bereiden van polyolefinevoorwerpen met grote hechtkracht voor polymere matrices, alsmede voor het bereiden van versterkte matrixmaterialen.
US5032338A (en) 1985-08-19 1991-07-16 Allied-Signal Inc. Method to prepare high strength ultrahigh molecular weight polyolefin articles by dissolving particles and shaping the solution
JPS62161841A (ja) 1986-01-11 1987-07-17 Hiraoka & Co Ltd コロナ放電処理された加工基材の処理効果保持方法
JP2541567B2 (ja) * 1987-07-21 1996-10-09 三井石油化学工業株式会社 補強用繊維材料
US5183701A (en) 1987-10-02 1993-02-02 Dyneema V.O.F. Articles of highly oriented polyolefins of ultrahigh molecular weight, process for their manufacture, and their use
EP0311197A3 (en) 1987-10-02 1990-03-28 Dyneema V.O.F. Articles of highly oriented polyolefins of ultrahigh molecular weight, process for their manufacture, and their use
JPH01260060A (ja) 1988-04-06 1989-10-17 Mitsui Petrochem Ind Ltd 超高分子量ポリオレフィン繊維およびその製造方法
US5075904A (en) 1989-08-05 1991-12-31 Toyo Boseki Kabushiki Kaisha Helmet with reinforcement
DE3929376C1 (cg-RX-API-DMAC10.html) 1989-09-05 1991-04-18 E.I. Du Pont De Nemours And Co., Wilmington, Del., Us
KR930006933B1 (ko) 1990-06-23 1993-07-24 한국과학기술연구원 폴리에틸렌 섬유/에폭시 수지 복합재의 접착력 증진 방법
US5108780A (en) * 1991-01-28 1992-04-28 Brigham Young University Enhanced thermoplastic adhesion to fibers by using plasma discharge
WO1993000389A1 (en) 1991-06-26 1993-01-07 E.I. Du Pont De Nemours And Company Ballistic composite
WO1993012282A1 (en) * 1991-12-17 1993-06-24 Weyerhaeuser Company Hopper blender system and method for coating fibers
US6268301B1 (en) * 1992-03-25 2001-07-31 Toyobo Co., Ltd. Ballistic-resistant article and process for making the same
JPH06158568A (ja) 1992-11-10 1994-06-07 Mitsui Petrochem Ind Ltd 合成樹脂で被覆した高強度ポリエチレン繊維製のロー プ、紐またはネット
US5421378A (en) * 1994-03-30 1995-06-06 Milliken Research Corporation Airbag weaving on a water-jet loom using yarns
US5702657A (en) 1994-12-27 1997-12-30 Nippon Oil Co., Ltd. Method for the continuous production of a polyethylene material having high strength and high modulus of elasticity
JP2915391B2 (ja) * 1997-09-01 1999-07-05 花王株式会社 繊維用精練剤組成物
US6291594B1 (en) * 1998-03-24 2001-09-18 National Starch And Chemical Investment Holding Corporation Textile sizes containing anhydride based graft copolymers
EP1079448B1 (en) 1999-02-08 2004-05-19 Japan Vilene Company, Ltd. Separator for alkaline battery and production method therefor
JP4315311B2 (ja) 2000-03-15 2009-08-19 学校法人金沢工業大学 接着性に優れた超高分子量ポリエチレン繊維及びその製造方法
US6448359B1 (en) 2000-03-27 2002-09-10 Honeywell International Inc. High tenacity, high modulus filament
DE10027636A1 (de) 2000-06-06 2001-12-13 Basf Ag Verwendung von kationisch modifizierten, teilchenförmigen, hydrophoben Polymeren als Zusatz zu Spül-, Pflege-, Wasch- und Reinigungsmitteln
ITMI20011619A1 (it) 2001-07-26 2003-01-26 Montefibre Spa Procedimento per la preparazione di materiali in fibra acrilica idrorepellenti
DE60307435T3 (de) 2002-02-08 2010-09-02 Teijin Twaron Gmbh Stichgeschütztes und antiballistisches material und verfahren zu dessen herstellung
US6846758B2 (en) * 2002-04-19 2005-01-25 Honeywell International Inc. Ballistic fabric laminates
US7364678B2 (en) 2002-12-10 2008-04-29 Dsm Ip Assets B.V. Process for making and process for converting polyolefin fibres
US7344668B2 (en) 2003-10-31 2008-03-18 Honeywell International Inc. Process for drawing gel-spun polyethylene yarns
JP3981835B2 (ja) 2003-12-22 2007-09-26 岩尾株式会社 繊維構造物の洗浄方法
EP1647615A1 (en) 2004-10-14 2006-04-19 DSM IP Assets B.V. Process for making a monofilament-like product
US7074483B2 (en) 2004-11-05 2006-07-11 Innegrity, Llc Melt-spun multifilament polyolefin yarn formation processes and yarns formed therefrom
US7776401B2 (en) 2005-06-21 2010-08-17 E.I. Du Pont De Nemours And Company Method for treating fabric with viscous liquid polymers
FR2893037B1 (fr) 2005-11-10 2012-11-09 Saint Gobain Vetrotex Procede de fonctionnalisation d'une portion de surface d'une fibre polymerique
JP5249510B2 (ja) 2006-02-10 2013-07-31 株式会社Ａｉｋｉリオテック 圧縮流体処理ノズル
JP2007239161A (ja) * 2006-03-13 2007-09-20 Teijin Techno Products Ltd 改質繊維の製造方法
US7846363B2 (en) * 2006-08-23 2010-12-07 Honeywell International Inc. Process for the preparation of UHMW multi-filament poly(alpha-olefin) yarns
EP1938907A1 (en) 2006-12-28 2008-07-02 Nederlandse Organisatie voor toegepast- natuurwetenschappelijk onderzoek TNO Deposition of particles on a substrate
US8969221B2 (en) 2007-03-19 2015-03-03 Honeywell International Inc Inhibition of water penetration into ballistic materials
US9365953B2 (en) 2007-06-08 2016-06-14 Honeywell International Inc. Ultra-high strength UHMWPE fibers and products
US8747715B2 (en) 2007-06-08 2014-06-10 Honeywell International Inc Ultra-high strength UHMW PE fibers and products
US7638191B2 (en) * 2007-06-08 2009-12-29 Honeywell International Inc. High tenacity polyethylene yarn
US8889049B2 (en) 2010-04-30 2014-11-18 Honeywell International Inc Process and product of high strength UHMW PE fibers
KR100903198B1 (ko) 2007-10-05 2009-06-18 코오롱글로텍주식회사 폴리올레핀 섬유 및 그 제조 방법
US7858540B2 (en) 2007-12-21 2010-12-28 Honeywell International Inc. Environmentally resistant ballistic composite based on a nitrile rubber binder
US7994075B1 (en) * 2008-02-26 2011-08-09 Honeywell International, Inc. Low weight and high durability soft body armor composite using topical wax coatings
CN101230501B (zh) * 2008-02-26 2010-06-02 山东爱地高分子材料有限公司 一种采用超高分子量聚乙烯与低密度聚乙烯共混熔融制备高强聚乙烯纤维的方法
US7665149B2 (en) 2008-05-14 2010-02-23 E.I. Du Pont De Nemours And Company Ballistic resistant body armor articles
KR101741124B1 (ko) * 2008-10-31 2017-05-29 루브리졸 어드밴스드 머티어리얼스, 인코포레이티드 올레핀-아크릴릭 공중합에 의한 하이브리드 폴리우레탄의 분산
CN101532239B (zh) 2008-12-19 2012-05-09 东华大学 等离子体处理纳米溶胶超高分子量聚乙烯纤维改性的方法
US7935283B2 (en) 2009-01-09 2011-05-03 Honeywell International Inc. Melt spinning blends of UHMWPE and HDPE and fibers made therefrom
TW201104026A (en) 2009-07-28 2011-02-01 Jen-Taut Yeh Ultra-high molecular weight polyethylene (UHMWPE)/inorganic nanocomposite material and manufacturing method of its high performance fiber
US7964518B1 (en) * 2010-04-19 2011-06-21 Honeywell International Inc. Enhanced ballistic performance of polymer fibers
US8080486B1 (en) 2010-07-28 2011-12-20 Honeywell International Inc. Ballistic shield composites with enhanced fragment resistance
US9023451B2 (en) 2011-09-06 2015-05-05 Honeywell International Inc. Rigid structure UHMWPE UD and composite and the process of making
US9163335B2 (en) 2011-09-06 2015-10-20 Honeywell International Inc. High performance ballistic composites and method of making
US9023450B2 (en) 2011-09-06 2015-05-05 Honeywell International Inc. High lap shear strength, low back face signature UD composite and the process of making
US9023452B2 (en) 2011-09-06 2015-05-05 Honeywell International Inc. Rigid structural and low back face signature ballistic UD/articles and method of making
US9168719B2 (en) 2011-09-06 2015-10-27 Honeywell International Inc. Surface treated yarn and fabric with enhanced physical and adhesion properties and the process of making

Also Published As

Publication number Publication date
IL236875B (en) 2019-01-31
TWI618824B (zh) 2018-03-21
CA2879710A1 (en) 2014-04-17
MX367336B (es) 2019-08-15
WO2014058497A2 (en) 2014-04-17
WO2014058497A3 (en) 2014-07-17
JP6239618B2 (ja) 2017-11-29
EP2877624A4 (en) 2016-03-16
EP2877624B1 (en) 2019-09-04
EP2877624A2 (en) 2015-06-03
BR112015001823A2 (pt) 2017-07-04
US20140065913A1 (en) 2014-03-06
KR102084617B1 (ko) 2020-03-04
BR112015001823B1 (pt) 2022-05-31
JP2015528860A (ja) 2015-10-01
TW201408830A (zh) 2014-03-01
ES2750474T3 (es) 2020-03-25
US10132006B2 (en) 2018-11-20
IN2015DN00573A (cg-RX-API-DMAC10.html) 2015-06-26
KR20150034800A (ko) 2015-04-03
MX2015000945A (es) 2015-04-16
CN104662221A (zh) 2015-05-27

Similar Documents

Publication Publication Date Title
EP2877624B1 (en) Process for treating and coating partially oriented fibres
US10132010B2 (en) UHMW PE fiber and method to produce
US9168719B2 (en) Surface treated yarn and fabric with enhanced physical and adhesion properties and the process of making
US9163335B2 (en) High performance ballistic composites and method of making
US11066765B2 (en) UHMWPE fiber and method to produce

Legal Events

Date Code Title Description
EEER Examination request

Effective date: 20180709

MPN Maintenance fee for patent paid

Free format text: FEE DESCRIPTION TEXT: MF (PATENT, 11TH ANNIV.) - STANDARD

Year of fee payment: 11

MPN Maintenance fee for patent paid

Free format text: FEE DESCRIPTION TEXT: MF (PATENT, 12TH ANNIV.) - STANDARD

Year of fee payment: 12

U00 Fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U00-U101 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE REQUEST RECEIVED

Effective date: 20250708

U11 Full renewal or maintenance fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U11-U102 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE FEE PAYMENT PAID IN FULL

Effective date: 20250708

R11 Change to the name of applicant or owner or transfer of ownership requested

Free format text: ST27 STATUS EVENT CODE: A-4-4-R10-R11-R127 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: TRANSFER RECORDAL REQUEST OR RESPONSE

Effective date: 20260319

W00 Other event occurred

Free format text: ST27 STATUS EVENT CODE: A-4-4-W10-W00-W111 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: CORRESPONDENT DETERMINED COMPLIANT

Effective date: 20260319

R14 Transfer of ownership recorded

Free format text: ST27 STATUS EVENT CODE: A-4-4-R10-R14-R129 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: TRANSFER REQUIREMENTS DETERMINED COMPLIANT

Effective date: 20260505

MPN Maintenance fee for patent paid

Free format text: FEE DESCRIPTION TEXT: MF (PATENT, 13TH ANNIV.) - STANDARD

Year of fee payment: 13

U00 Fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U00-U101 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE REQUEST RECEIVED

Effective date: 20260623

U11 Full renewal or maintenance fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U11-U102 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE FEE PAYMENT PAID IN FULL

Effective date: 20260623

W00 Other event occurred

Free format text: ST27 STATUS EVENT CODE: A-4-4-W10-W00-W100 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: LETTER SENT

Effective date: 20260729