BR112017007973A2 - folha de aço galvanizada por imersão a quente - Google Patents

folha de aço galvanizada por imersão a quente

Info

Publication number
BR112017007973A2
BR112017007973A2 BR112017007973A BR112017007973A BR112017007973A2 BR 112017007973 A2 BR112017007973 A2 BR 112017007973A2 BR 112017007973 A BR112017007973 A BR 112017007973A BR 112017007973 A BR112017007973 A BR 112017007973A BR 112017007973 A2 BR112017007973 A2 BR 112017007973A2
Authority
BR
Brazil
Prior art keywords
layer
steel sheet
dip galvanized
base steel
hot dip
Prior art date
Application number
BR112017007973A
Other languages
English (en)
Inventor
Arai Hayato
Kawata Hiroyuki
Ueda Kohei
Maruyama Naoki
KOMAMI Ryosuke
Uchida Satoshi
Yasui Takeshi
Nakamura Toyomitsu
Yamaguchi Yuji
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of BR112017007973A2 publication Critical patent/BR112017007973A2/pt

Abstract

trata-se de uma folha de aço galvanizada por imersão a quente que compreende uma folha de aço de base e uma camada galvanizada por imersão a quente formada em pelo menos uma superfície da folha de aço de base, em que a camada galvanizada por imersão a quente inclui cristais colunares que compreende uma fase ¿ e que tem um teor de fe de mais do que 0% a 5% e um teor de al de mais do que 0% a 1,0% na superfície da folha de aço, sendo que 20% ou mais da interface inteira da camada galvanizada por imersão a quente e da folha de aço de base é adicionalmente revestida pela fase ¿, sendo que uma interface formada pela camada de aço de base e grânulos ¿ em que óxido grosso está presente entre os grânulos de cristal ¿ é 50% ou menos da interface inteira da fase ¿ e a folha de aço de base na camada galvanizada por imersão a quente, em que a camada de aço de base tem uma composição química específica e tem uma camada refinada diretamente adjacente à interface da folha de aço de base e da camada galvanizada por imersão a quente, sendo que a espessura média da camada refinada é 0,1 a 5,0 µm, sendo que o tamanho de grânulo médio de ferrita na camada refinada é 0,1 a 3,0 µm, em que a camada refinada contém um ou mais óxidos de si e mn e sendo que o diâmetro máximo dos óxidos é 0,01 a 0,4 µm.
BR112017007973A 2014-11-05 2015-11-05 folha de aço galvanizada por imersão a quente BR112017007973A2 (pt)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014225398 2014-11-05
PCT/JP2015/081236 WO2016072478A1 (ja) 2014-11-05 2015-11-05 溶融亜鉛めっき鋼板

Publications (1)

Publication Number Publication Date
BR112017007973A2 true BR112017007973A2 (pt) 2017-12-19

Family

ID=55909199

Family Applications (2)

Application Number Title Priority Date Filing Date
BR112017007973A BR112017007973A2 (pt) 2014-11-05 2015-11-05 folha de aço galvanizada por imersão a quente
BR112017008043A BR112017008043A2 (pt) 2014-11-05 2015-11-05 chapa de aço galvanizada por imersão a quente

Family Applications After (1)

Application Number Title Priority Date Filing Date
BR112017008043A BR112017008043A2 (pt) 2014-11-05 2015-11-05 chapa de aço galvanizada por imersão a quente

Country Status (11)

Country Link
US (2) US10822683B2 (pt)
EP (2) EP3216892B1 (pt)
JP (2) JP6365681B2 (pt)
KR (2) KR101918876B1 (pt)
CN (2) CN107148492B (pt)
BR (2) BR112017007973A2 (pt)
ES (2) ES2775480T3 (pt)
MX (2) MX2017005503A (pt)
PL (2) PL3216891T3 (pt)
TW (2) TWI558820B (pt)
WO (2) WO2016072478A1 (pt)

Families Citing this family (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
PL3216891T3 (pl) 2014-11-05 2020-06-29 Nippon Steel Corporation Blacha stalowa cienka cynkowana zanurzeniowo na gorąco
ES2761600T3 (es) 2014-11-05 2020-05-20 Nippon Steel Corp Lámina de acero galvanizada en caliente
JP6358406B2 (ja) * 2016-08-05 2018-07-18 新日鐵住金株式会社 鋼板及びめっき鋼板
JP6892842B2 (ja) * 2017-06-29 2021-06-23 Ｊｆｅスチール株式会社 高強度冷延鋼板用の素材熱延鋼板およびその製造方法
WO2019026106A1 (ja) * 2017-07-31 2019-02-07 新日鐵住金株式会社 溶融亜鉛めっき鋼板
BR112020001163A2 (pt) * 2017-07-31 2020-07-21 Nippon Steel Corporation chapa de aço galvanizada por imersão a quente
BR112020001128A2 (pt) * 2017-07-31 2020-07-21 Nippon Steel Corporation folha de aço galvanizada por imersão a quente
WO2019186997A1 (ja) * 2018-03-30 2019-10-03 日本製鉄株式会社 鋼板およびその製造方法
TWI671410B (zh) * 2018-03-30 2019-09-11 日商日本製鐵股份有限公司 鋼板及其製造方法
JP6638874B1 (ja) * 2018-04-13 2020-01-29 日本製鉄株式会社 Ｎｉ拡散めっき鋼板及びＮｉ拡散めっき鋼板の製造方法
JP7239059B2 (ja) * 2020-03-23 2023-03-14 日本製鉄株式会社 ホットスタンプ成形体
CN113355562B (zh) * 2021-07-05 2022-11-25 华南理工大学 批量热浸锌铝镁合金镀层及其制备方法和应用
CN115558876B (zh) * 2022-09-09 2024-05-10 首钢集团有限公司 一种热镀锌钢板及其制备方法

Family Cites Families (44)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5112575B1 (pt) * 1970-12-30 1976-04-20
JPS533153B2 (pt) 1974-07-19 1978-02-03
JP3198902B2 (ja) * 1995-12-11 2001-08-13 日本鋼管株式会社 薄目付け溶融亜鉛めっき鋼板の製造方法
JP3139353B2 (ja) 1995-12-11 2001-02-26 日本鋼管株式会社 薄目付け溶融亜鉛めっき鋼板の製造方法
JP3126911B2 (ja) 1995-12-27 2001-01-22 川崎製鉄株式会社 めっき密着性の良好な高強度溶融亜鉛めっき鋼板
JPH09241812A (ja) 1996-03-01 1997-09-16 Kobe Steel Ltd 合金化溶融亜鉛めっき鋼板
JP3520741B2 (ja) 1997-11-05 2004-04-19 Ｊｆｅスチール株式会社 めっき密着性に優れた合金化溶融亜鉛めっき鋼板
CN1117884C (zh) 1998-09-29 2003-08-13 川崎制铁株式会社 高强度薄钢板、高强度合金化热镀锌钢板及它们的制造方法
JP3752898B2 (ja) 1999-07-15 2006-03-08 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板の製造方法
JP4552310B2 (ja) 1999-11-08 2010-09-29 Ｊｆｅスチール株式会社 強度−延性バランスとめっき密着性に優れた溶融亜鉛めっき鋼板およびその製造方法
JP3661559B2 (ja) 2000-04-25 2005-06-15 住友金属工業株式会社 加工性とめっき密着性に優れた合金化溶融亜鉛めっき高張力鋼板とその製造方法
JP3536814B2 (ja) * 2000-11-29 2004-06-14 住友金属工業株式会社 美麗な溶融亜鉛めっき鋼板およびその製造方法
JP3898923B2 (ja) 2001-06-06 2007-03-28 新日本製鐵株式会社 高加工時のめっき密着性および延性に優れた高強度溶融Ｚｎめっき鋼板及びその製造方法
JP5087813B2 (ja) 2001-08-31 2012-12-05 Ｊｆｅスチール株式会社 めっき性に優れた高張力溶融亜鉛めっき鋼板およびその製造方法
JP4631241B2 (ja) 2001-09-21 2011-02-16 Ｊｆｅスチール株式会社 強度延性バランス、めっき密着性と耐食性に優れた高張力溶融亜鉛めっき鋼板および高張力合金化溶融亜鉛めっき鋼板
JP2004124187A (ja) 2002-10-03 2004-04-22 Sumitomo Metal Ind Ltd 密着性・溶接性に優れた高強度溶融亜鉛めっき鋼板
JP4119804B2 (ja) 2003-08-19 2008-07-16 新日本製鐵株式会社 密着性の優れた高強度合金化溶融亜鉛めっき鋼板及びその製造方法
JP4192051B2 (ja) 2003-08-19 2008-12-03 新日本製鐵株式会社 高強度合金化溶融亜鉛めっき鋼板の製造方法と製造設備
JP4457673B2 (ja) 2004-01-19 2010-04-28 Ｊｆｅスチール株式会社 耐二次加工脆性およびめっき密着性に優れた高成形性燃料タンク用めっき冷延鋼板およびその製造方法
JP4966485B2 (ja) 2004-08-25 2012-07-04 住友金属工業株式会社 高張力溶融亜鉛めっき鋼板とその製造方法
JP4837464B2 (ja) 2006-07-11 2011-12-14 新日本製鐵株式会社 めっき密着性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
BRPI0621421B8 (pt) 2006-01-30 2019-05-21 Nippon Steel & Sumitomo Metal Corp chapa de aço galvanizada por imersão a quente, chapa de aço galvanizada e recozida e métodos de produção das mesmas
JP4790525B2 (ja) 2006-07-19 2011-10-12 新日本製鐵株式会社 耐チッピング性に優れた高強度合金化溶融めっき鋼板
US8888933B2 (en) 2009-05-27 2014-11-18 Nippon Steel & Sumitomo Metal Corporation High-strength steel sheet, hot-dipped steel sheet, and alloy hot-dipped steel sheet that have excellent fatigue, elongation, and collision characteristics, and manufacturing method for said steel sheets
JP5703608B2 (ja) 2009-07-30 2015-04-22 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5370104B2 (ja) 2009-11-30 2013-12-18 新日鐵住金株式会社 耐水素脆化特性に優れた引張最大強度９００ＭＰａ以上の高強度鋼板および高強度冷延鋼板の製造方法、高強度亜鉛めっき鋼板の製造方法
US10023947B2 (en) * 2009-11-30 2018-07-17 Nippon Steel & Sumitomo Metal Corporation High strength steel plate with ultimate tensile strength of 900 MPa or more excellent in hydrogen embrittlement resistance and method of production of same
JP5434960B2 (ja) 2010-05-31 2014-03-05 Ｊｆｅスチール株式会社 曲げ性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
WO2012004889A1 (ja) * 2010-07-09 2012-01-12 新日本製鐵株式会社 溶融亜鉛系めっき鋼板
KR20120041544A (ko) * 2010-10-21 2012-05-02 주식회사 포스코 도금성, 도금밀착성 및 스폿용접성이 우수한 용융아연도금강판 및 그 제조방법
US20120100391A1 (en) * 2010-10-21 2012-04-26 Posco Hot-dip galvanized steel sheet having excellent plating qualities, plating adhesion and spot weldability and manufacturing method thereof
WO2013018739A1 (ja) 2011-07-29 2013-02-07 新日鐵住金株式会社 曲げ性に優れた高強度亜鉛めっき鋼板およびその製造方法
BR112014007483B1 (pt) * 2011-09-30 2019-12-31 Nippon Steel & Sumitomo Metal Corp chapa de aço galvanizado a quente e processo de fabricação da mesma
WO2013047810A1 (ja) 2011-09-30 2013-04-04 新日鐵住金株式会社 合金化溶融亜鉛めっき鋼板
BR112014007545B1 (pt) 2011-09-30 2019-05-14 Nippon Steel & Sumitomo Metal Corporation Chapa de aço galvanizada por imersão a quente de alta resistência, chapa de aço galvanizada por imersão a quente de alta resistência ligada e método para produção das mesmas.
BR112014007500A2 (pt) 2011-09-30 2017-04-04 Nippon Steel & Sumitomo Metal Corp folha de aço galvanizada por imersão a quente e método de fabricação da mesma
WO2013047821A1 (ja) * 2011-09-30 2013-04-04 新日鐵住金株式会社 焼付硬化性に優れた高強度溶融亜鉛めっき鋼板、高強度合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
WO2013047755A1 (ja) * 2011-09-30 2013-04-04 新日鐵住金株式会社 耐衝撃特性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法、並びに、高強度合金化溶融亜鉛めっき鋼板およびその製造方法
CN103857819B (zh) * 2011-10-04 2016-01-13 杰富意钢铁株式会社 高强度钢板及其制造方法
TWI468534B (zh) * 2012-02-08 2015-01-11 Nippon Steel & Sumitomo Metal Corp 高強度冷軋鋼板及其製造方法
CN102787271A (zh) * 2012-07-17 2012-11-21 马钢(集团)控股有限公司 一种460MPa级高表面质量结构用热镀锌钢板的生产方法及其产品
KR101403076B1 (ko) 2012-09-03 2014-06-02 주식회사 포스코 신장 플랜지성 및 도금밀착성이 우수한 고강도 합금화 용융아연도금강판 및 그 제조방법
ES2761600T3 (es) 2014-11-05 2020-05-20 Nippon Steel Corp Lámina de acero galvanizada en caliente
PL3216891T3 (pl) 2014-11-05 2020-06-29 Nippon Steel Corporation Blacha stalowa cienka cynkowana zanurzeniowo na gorąco

Also Published As

Publication number Publication date
EP3216891B1 (en) 2020-01-15
WO2016072478A1 (ja) 2016-05-12
JPWO2016072475A1 (ja) 2017-09-21
US10822684B2 (en) 2020-11-03
PL3216892T3 (pl) 2019-12-31
KR20170062500A (ko) 2017-06-07
ES2775480T3 (es) 2020-07-27
WO2016072475A1 (ja) 2016-05-12
JP6519028B2 (ja) 2019-05-29
KR101913989B1 (ko) 2018-10-31
JP6365681B2 (ja) 2018-08-01
KR101918876B1 (ko) 2018-11-14
EP3216891A4 (en) 2018-04-18
CN107148492A (zh) 2017-09-08
MX2017005503A (es) 2017-08-16
CN107148491A (zh) 2017-09-08
CN107148492B (zh) 2019-06-18
EP3216892A4 (en) 2018-04-18
US10822683B2 (en) 2020-11-03
US20170314115A1 (en) 2017-11-02
TWI558820B (zh) 2016-11-21
JPWO2016072478A1 (ja) 2017-08-31
US20170305114A1 (en) 2017-10-26
TW201623650A (zh) 2016-07-01
KR20170066552A (ko) 2017-06-14
CN107148491B (zh) 2019-08-16
EP3216891A1 (en) 2017-09-13
MX2017005505A (es) 2017-06-20
EP3216892A1 (en) 2017-09-13
PL3216891T3 (pl) 2020-06-29
TWI601848B (zh) 2017-10-11
ES2748019T3 (es) 2020-03-12
EP3216892B1 (en) 2019-08-14
TW201629245A (zh) 2016-08-16
BR112017008043A2 (pt) 2017-12-19

Similar Documents

Publication Publication Date Title
BR112017007973A2 (pt) folha de aço galvanizada por imersão a quente
BR112017008311A2 (pt) folha de aço galvanizada por mergulho a quente
BR112015001774A2 (pt) chapa de aço galvanizada para conformação a quente
BR112017008460A2 (pt) chapa de aço galvanizada por imersão a quente
BR112018010352A2 (pt) método para marcar um substrato, substrato marcado, produto, e, uso de um substrato marcado.
BR112016029465A2 (pt) chapa de aço elétrica
BR112019000965A2 (pt) material de mancal de deslizamento de alumínio livre de chumbo com superfície funcional
BR112017017291A2 (pt) chapa de aço laminada a quente
WO2014130582A3 (en) Compounds useful as modulators of trpm8
BR112018010665A8 (pt) ?método para fabricação de um material de acondicionamento laminado, material de acondicionamento laminado, e, recipiente de acondicionamento?
BR112017017443A2 (pt) folha de aço laminada a quente
BR112014007483A2 (pt) folha de aço galvanizado a quente de alta resistência que possui excelente resistência à fratura retardada e método de fabricação da mesma
BR112016021766A2 (pt) Elemento chapa de aço conformado a quente de alta resistência
BR112015016797A2 (pt) reator dotado de um refrigerador
BR112017016799A2 (pt) chapa de aço laminada a quente
BR112017004711A2 (pt) chapa de aço laminada a quente
BR112015026523A2 (pt) aço limpo com baixo teor de oxigênio e produto de aço limpo com baixo teor de oxigênio
BR112015026344A2 (pt) camada de proteção contra oxidação baseada em cromo
BR112015030003A2 (pt) chapa de aço laminada a frio, chapa de aço laminada a frio galvanizada e método de produção da mesma
BR112015027819A2 (pt) Método de cisalhamento a quente e refino de grão de camada de superfície e peça de trabalho obtida por cisalhamento a quente e refino de grão de camada de superfície
BR112012030807A2 (pt) esferas flutuantes e sua utilização para formar barreiras de gás em superfícies líquidas
BR112018003267A2 (pt) chapa de aço
BR112019025451A8 (pt) Estrutura de revestimento, produto do tipo folha e seu uso
BR112017019895A2 (pt) tira ou folha de metal, placa, placa bipolar e método para a fabricação de uma tira ou folha de metal
BR112017022937A2 (pt) revestimento isolante para chapa de aço elétrico

Legal Events

Date Code Title Description
B25D Requested change of name of applicant approved

Owner name: NIPPON STEEL CORPORATION (JP)

B06U Preliminary requirement: requests with searches performed by other patent offices: procedure suspended [chapter 6.21 patent gazette]
B07A Application suspended after technical examination (opinion) [chapter 7.1 patent gazette]
B09B Patent application refused [chapter 9.2 patent gazette]
B09B Patent application refused [chapter 9.2 patent gazette]

Free format text: MANTIDO O INDEFERIMENTO UMA VEZ QUE NAO FOI APRESENTADO RECURSO DENTRO DO PRAZO LEGAL