BR112015001475A2 - chapa de aço laminada a frio, chapa de aço laminada a frio eletrogalvanizada, chapa de aço laminada a frio galvanizada por imersão a quente, chapa de aço laminada a frio galvanizada por imersão a quente em liga, e métodos de fabricação das mesmas - Google Patents

chapa de aço laminada a frio, chapa de aço laminada a frio eletrogalvanizada, chapa de aço laminada a frio galvanizada por imersão a quente, chapa de aço laminada a frio galvanizada por imersão a quente em liga, e métodos de fabricação das mesmas

Info

Publication number
BR112015001475A2
BR112015001475A2 BR112015001475A BR112015001475A BR112015001475A2 BR 112015001475 A2 BR112015001475 A2 BR 112015001475A2 BR 112015001475 A BR112015001475 A BR 112015001475A BR 112015001475 A BR112015001475 A BR 112015001475A BR 112015001475 A2 BR112015001475 A2 BR 112015001475A2
Authority
BR
Brazil
Prior art keywords
steel sheet
rolled steel
cold
hot
dip galvanized
Prior art date
Application number
BR112015001475A
Other languages
English (en)
Other versions
BR112015001475B1 (pt
Inventor
Maruyama Naoki
Sugiura Natsuko
Yonemura Shigeru
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of BR112015001475A2 publication Critical patent/BR112015001475A2/pt
Publication of BR112015001475B1 publication Critical patent/BR112015001475B1/pt

Abstract

resumo patente de invenção: "chapa de aço laminada a frio, chapa de aço laminada a frio eletrolítica revestida com zinco, chapa de aço laminada a frio revestida com zinco por imersão a quente, chapa de aço laminada a frio revestida com zinco por imersão a quente em liga, e métodos de fabricação das mesmas". trata-se de uma chapa de aço laminada a frio que contém, em % em massa, 0,0005 a 0,0045% de c, 0,80 a 2,50% de mn, 0,002 a 0,150% de ti e 0,0005 a 0,01% de b, que satisfaz a exigência representada pela fórmula (1), e também contém ferro e impurezas inevitáveis como resíduo, em que a razão de intensidade aleatória (a) na orientação {332}<110> é igual a 3 ou menos, e cada uma dentre a razão de intensidade aleatória (b) na orientação {557}<9 16 5> e a razão de intensidade aleatória (c) na orientação {111}<112> é igual a 7 ou mais conforme medido em uma posição correspondente a um quarto da espessura da chapa de aço e as exigências representadas pelas fórmulas {(b)/(a) = 5} e {(b) > (c)} são satisfeitas.
BR112015001475A 2012-07-31 2013-07-31 Chapade aço laminada a frio e método de fabricação damesma BR112015001475B1 (pt)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012170316 2012-07-31
PCT/JP2013/070745 WO2014021382A1 (ja) 2012-07-31 2013-07-31 冷延鋼鈑、電気亜鉛系めっき冷延鋼板、溶融亜鉛めっき冷延鋼板、合金化溶融亜鉛めっき冷延鋼板、及び、それらの製造方法

Publications (2)

Publication Number Publication Date
BR112015001475A2 true BR112015001475A2 (pt) 2017-07-04
BR112015001475B1 BR112015001475B1 (pt) 2020-04-22

Family

ID=50028052

Family Applications (1)

Application Number Title Priority Date Filing Date
BR112015001475A BR112015001475B1 (pt) 2012-07-31 2013-07-31 Chapade aço laminada a frio e método de fabricação damesma

Country Status (12)

Country Link
US (1) US9879336B2 (pt)
EP (1) EP2881483B1 (pt)
JP (1) JP5582274B2 (pt)
KR (1) KR101649456B1 (pt)
CN (1) CN104487603B (pt)
BR (1) BR112015001475B1 (pt)
ES (1) ES2756328T3 (pt)
IN (1) IN2015DN00401A (pt)
MX (1) MX365928B (pt)
PL (1) PL2881483T3 (pt)
TW (1) TWI488979B (pt)
WO (1) WO2014021382A1 (pt)

Families Citing this family (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6264861B2 (ja) * 2013-11-27 2018-01-24 新日鐵住金株式会社 加工性に優れた高ヤング率冷延鋼鈑、電気亜鉛系めっき冷延鋼板、溶融亜鉛めっき冷延鋼板、合金化溶融亜鉛めっき冷延鋼板、及び、それらの製造方法
JP6248782B2 (ja) * 2014-04-22 2017-12-20 新日鐵住金株式会社 高ヤング率冷延鋼鈑、高ヤング率電気亜鉛系めっき冷延鋼板、高ヤング率溶融亜鉛めっき冷延鋼板、高ヤング率合金化溶融亜鉛めっき冷延鋼板、及び、それらの製造方法
JP6032300B2 (ja) * 2015-02-03 2016-11-24 Ｊｆｅスチール株式会社 高強度冷延鋼板、高強度めっき鋼板、高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
JP6032299B2 (ja) * 2015-02-03 2016-11-24 Ｊｆｅスチール株式会社 高強度冷延鋼板、高強度めっき鋼板、高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
JP6032298B2 (ja) 2015-02-03 2016-11-24 Ｊｆｅスチール株式会社 高強度冷延鋼板、高強度めっき鋼板、高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
JP6443126B2 (ja) * 2015-02-26 2018-12-26 新日鐵住金株式会社 フェライト系薄鋼板
KR101795918B1 (ko) * 2015-07-24 2017-11-10 주식회사 포스코 내시효성 및 소부경화성이 우수한 용융아연도금강판, 합금화 용융아연도금강판 및 그 제조방법
CN107923017A (zh) * 2015-08-24 2018-04-17 新日铁住金株式会社 合金化热浸镀锌钢板及其制造方法
CN108097720B (zh) * 2017-11-28 2020-09-25 甘肃酒钢集团宏兴钢铁股份有限公司 一种宽度1250mm纯钛冷轧薄钛带的轧制工艺
MX2020010273A (es) * 2018-04-02 2021-12-10 Nippon Steel Corp Lamina de metal, metodo de produccion de lamina de metal, metodo de produccion de producto moldeado de lamina de metal y producto moldeado de lamina de metal.
KR102426248B1 (ko) * 2020-11-05 2022-07-28 주식회사 포스코 선영성이 우수한 고강도 아연계 도금강판 및 그 제조방법
KR102468036B1 (ko) * 2020-11-12 2022-11-17 주식회사 포스코 성형성이 우수한 고강도 아연계 도금강판 및 그 제조방법

Family Cites Families (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5324892B2 (pt) * 1972-10-19 1978-07-24
JPH0730411B2 (ja) * 1988-12-28 1995-04-05 川崎製鉄株式会社 深絞り性に優れた熱延鋼板の製造方法
US4973367A (en) 1988-12-28 1990-11-27 Kawasaki Steel Corporation Method of manufacturing steel sheet having excellent deep-drawability
JPH05255804A (ja) 1992-03-11 1993-10-05 Nippon Steel Corp 成形性および剛性の優れた冷延鋼板およびその製造方法
JP3450985B2 (ja) * 1997-04-10 2003-09-29 新日本製鐵株式会社 形状が良好で曲げ性に優れた高強度冷延鋼板とその製造方法
TW476790B (en) 1998-05-18 2002-02-21 Kawasaki Steel Co Electrical sheet of excellent magnetic characteristics and its manufacturing method
JP2000104144A (ja) 1998-07-29 2000-04-11 Kawasaki Steel Corp Ｌ方向及びｃ方向の磁気特性に優れた電磁鋼板及びその製造方法
US6368728B1 (en) 1998-11-18 2002-04-09 Kawasaki Steel Corporation Galvannealed steel sheet and manufacturing method
EP1136575A4 (en) * 1999-08-10 2008-04-23 Jfe Steel Corp PROCESS FOR PRODUCING COLD LAMINATED STEEL STRIPS
US7076983B2 (en) * 2001-03-16 2006-07-18 Nakayama Steel Works, Ltd. Apparatus and method for hot rolling
JP4059050B2 (ja) * 2001-10-05 2008-03-12 Ｊｆｅスチール株式会社 冷延鋼板製造用母板、高強度高延性冷延鋼板およびそれらの製造方法
EP1516937B1 (en) * 2002-06-25 2008-03-05 JFE Steel Corporation High-strength cold rolled steel sheet and process for producing the same
JP3911226B2 (ja) * 2002-10-09 2007-05-09 新日本製鐵株式会社 形状凍結性に優れた冷延鋼板の製造方法
JP4126007B2 (ja) * 2003-10-20 2008-07-30 新日本製鐵株式会社 形状凍結性と焼付硬化性に優れた冷延鋼板及びその製造方法
WO2006011503A1 (ja) * 2004-07-27 2006-02-02 Nippon Steel Corporation 高ヤング率鋼板、それを用いた溶融亜鉛めっき鋼板、合金化溶融亜鉛めっき鋼板、および高ヤング率鋼管、並びにそれらの製造方法
JP4528137B2 (ja) * 2004-03-19 2010-08-18 新日本製鐵株式会社 穴拡げ性に優れた高強度高延性薄鋼板の製造方法
CA2546009A1 (en) * 2004-03-31 2005-10-13 Jfe Steel Corporation High-rigidity high-strength thin steel sheet and method for producing same
JP4843981B2 (ja) 2004-03-31 2011-12-21 Ｊｆｅスチール株式会社 高剛性高強度薄鋼板およびその製造方法
JP4622783B2 (ja) 2005-09-29 2011-02-02 Ｊｆｅスチール株式会社 剛性に優れた高強度薄鋼板およびその製造方法
BRPI0520600B1 (pt) * 2005-10-05 2014-11-11 Nippon Steel & Sumitomo Metal Corp "método de produção de uma chapa de aço laminada a frio, bem como chapa de aço laminada a frio produzido pelo método".
JP5058508B2 (ja) * 2005-11-01 2012-10-24 新日本製鐵株式会社 低降伏比型高ヤング率鋼板、溶融亜鉛めっき鋼板、合金化溶融亜鉛めっき鋼板及び鋼管、並びにそれらの製造方法
JP5228447B2 (ja) * 2006-11-07 2013-07-03 新日鐵住金株式会社 高ヤング率鋼板及びその製造方法
JP5233142B2 (ja) 2007-03-28 2013-07-10 Ｊｆｅスチール株式会社 穴拡げ性に優れた高剛性高強度鋼板およびその製造方法
JP5157215B2 (ja) 2007-03-28 2013-03-06 Ｊｆｅスチール株式会社 加工性に優れた高剛性高強度鋼板およびその製造方法
JP5037415B2 (ja) 2007-06-12 2012-09-26 新日本製鐵株式会社 穴広げ性に優れた高ヤング率鋼板及びその製造方法
JP5088021B2 (ja) 2007-07-05 2012-12-05 新日本製鐵株式会社 高剛性高強度冷延鋼板及びその製造方法
ES2578952T3 (es) * 2008-03-27 2016-08-03 Nippon Steel & Sumitomo Metal Corporation Chapa de acero laminada en frío, chapa de acero galvanizado de alta resistencia y chapa de acero galvanizado por inmersión en caliente aleada de alta resistencia que tiene excelente conformabilidad y soldabilidad, y métodos para fabricar las mismas
ES2758553T3 (es) 2009-11-30 2020-05-05 Nippon Steel Corp Lámina de acero de alta resistencia con excelente resistencia a la fragilidad por hidrógeno y una resistencia a tensión máxima de 900 MPa o más, y método para su producción
CN103180468B (zh) * 2010-08-23 2015-07-01 新日铁住金株式会社 冷轧钢板及其制造方法

Also Published As

Publication number Publication date
TWI488979B (zh) 2015-06-21
JP5582274B2 (ja) 2014-09-03
IN2015DN00401A (pt) 2015-06-19
CN104487603B (zh) 2017-03-08
MX365928B (es) 2019-06-20
US20150203948A1 (en) 2015-07-23
EP2881483B1 (en) 2019-09-25
KR20150029741A (ko) 2015-03-18
US9879336B2 (en) 2018-01-30
ES2756328T3 (es) 2020-04-27
PL2881483T3 (pl) 2020-02-28
EP2881483A4 (en) 2016-04-13
TW201406969A (zh) 2014-02-16
WO2014021382A1 (ja) 2014-02-06
CN104487603A (zh) 2015-04-01
KR101649456B1 (ko) 2016-08-19
EP2881483A1 (en) 2015-06-10
JPWO2014021382A1 (ja) 2016-07-21
BR112015001475B1 (pt) 2020-04-22
MX2015001071A (es) 2015-04-08

Similar Documents

Publication Publication Date Title
BR112015001475A2 (pt) chapa de aço laminada a frio, chapa de aço laminada a frio eletrogalvanizada, chapa de aço laminada a frio galvanizada por imersão a quente, chapa de aço laminada a frio galvanizada por imersão a quente em liga, e métodos de fabricação das mesmas
BR112014002198A2 (pt) chapa de aço de alta resistência e chapa de aço galvanizada de alta resistência excelentes em capacidade de conformação e métodos de produção das mesmas
BR112014007498A2 (pt) chapa de aço galvanizado a quente de alta resistência, chapa de aço galvanizada a quente com liga de alta resistência excelente em temperabilidade, e método de produção das mesmas
BR112013026079A2 (pt) chapa de aço laminada a frio de alta resistência tendo excelente deformabilidade local, e método de produção da mesma
BR112014002026A2 (pt) chapa de aço de alta resistência e chapa de aço galvanizado de alta resistência excelente em fixabilidade de forma, e método de produção das mesmas
BR112013005453A2 (pt) ligas de alumínio 7xxx aperfeiçoadas, e processos para produção das mesmas
BR112013001864A2 (pt) chapa de aço laminada a quente, chapa de aço laminada a frio, chapa de aço galvanizada e método de produção da mesma
BR112014026678A2 (pt) chapa de aço galvanizado na cor negra
BR112013001367A2 (pt) processamento de ligas de titânio alfa/beta
BR112013023792A2 (pt) chapa de aço para elemento gravado a quente e método de produção da mesma
BR112016029379A2 (pt) chapa de aço laminada a quente
BR112015021149A2 (pt) chapa de aço laminada a quente e seu método de produção
BR112015002312A2 (pt) chapa de aço laminada a frio e método para produção da mesma, e elememento conformado por estampagem a quente
IN2014KN01673A (pt)
WO2014104428A8 (ko) 아연도금강판용 표면처리 조성물, 아연도금강판의 표면처리 방법 및 아연도금강판
BR112012018552A2 (pt) chapa de aço laminada a frio de alta resistência e método de produção da mesma
BR112012033494A2 (pt) método para fosfatagem seletiva de uma construção metálica compósita
BR112016030919A2 (pt) Chapa de aço laminada a quente
BR112015028001A2 (pt) chapa de aço galvanizada e recozida e método para sua produção
BR112014019497A8 (pt) Chapa de aço laminada a frio, chapa de aço revestida, e métodos para produção das mesmas
BR112017023814A2 (pt) tira de aço de alta resistência galvanizada por imersão a quente
BR112017004293A2 (pt) chapa de aço galvanizada contendo quasicristais e método para produzir chapa de aço galvanizada contendo quasicristais
BR112014026671A2 (pt) liga de alumínio tendo uma combinação excelente de força, extrudabilidade e resistência à corrosão
EP2527484A4 (en) HIGH-FIXED FIRE-GRAINED STEEL PLATE WITH EXCELLENT PROCESSABILITY AND POINT WELDABILITY, AND METHOD FOR THE PRODUCTION THEREOF
EP2995698A4 (en) HOT-DIP ZINC-COATED STEEL SHEET OR ALLOYED HOT-DIP ZINC-COATED STEEL SHEET HAVING SUPERIOR STRENGTH-BENDABILITY BALANCE WITH TENSILE STRENGTH OF 1180 MPa OR MORE

Legal Events

Date Code Title Description
B06F Objections, documents and/or translations needed after an examination request according [chapter 6.6 patent gazette]
B06A Patent application procedure suspended [chapter 6.1 patent gazette]
B25D Requested change of name of applicant approved

Owner name: NIPPON STEEL CORPORATION (JP)

B09A Decision: intention to grant [chapter 9.1 patent gazette]
B16A Patent or certificate of addition of invention granted [chapter 16.1 patent gazette]

Free format text: PRAZO DE VALIDADE: 20 (VINTE) ANOS CONTADOS A PARTIR DE 31/07/2013, OBSERVADAS AS CONDICOES LEGAIS.

B21F Lapse acc. art. 78, item iv - on non-payment of the annual fees in time

Free format text: REFERENTE A 9A ANUIDADE.

B24J Lapse because of non-payment of annual fees (definitively: art 78 iv lpi, resolution 113/2013 art. 12)

Free format text: EM VIRTUDE DA EXTINCAO PUBLICADA NA RPI 2681 DE 24-05-2022 E CONSIDERANDO AUSENCIA DE MANIFESTACAO DENTRO DOS PRAZOS LEGAIS, INFORMO QUE CABE SER MANTIDA A EXTINCAO DA PATENTE E SEUS CERTIFICADOS, CONFORME O DISPOSTO NO ARTIGO 12, DA RESOLUCAO 113/2013.