IN2015DN00401A - - Google Patents

Info

Publication number
IN2015DN00401A
IN2015DN00401A IN401DEN2015A IN2015DN00401A IN 2015DN00401 A IN2015DN00401 A IN 2015DN00401A IN 401DEN2015 A IN401DEN2015 A IN 401DEN2015A IN 2015DN00401 A IN2015DN00401 A IN 2015DN00401A
Authority
IN
India
Prior art keywords
orientation
strength ratio
random strength
steel sheet
represented
Prior art date
Application number
Inventor
Natsuko Sugiura
Shigeru Yonemura
Naoki Maruyama
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of IN2015DN00401A publication Critical patent/IN2015DN00401A/en

Abstract

A cold rolled steel sheet which contains in mass% 0.0005 to 0.0045% of C 0.80 to 2.50% of Mn 0.002 to 0.150% of Ti and 0.0005 to 0.01% of B fulfills the requirement represented by formula (1) and also contains iron and unavoidable impurities as a remainder wherein the random strength ratio (A) in the [332] <110> orientation is 3 or less and each of the random strength ratio (B) in the [557] <9 16 5> orientation and the random strength ratio (C) in the [111] <112> orientation is 7 or more as measured at a position corresponding to one fourth of the thickness of the steel sheet and the requirements represented by the formulae [(B)/(A) = 5] and [(B) > (C)] are fulfilled.
IN401DEN2015 2012-07-31 2013-07-31 IN2015DN00401A (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012170316 2012-07-31
PCT/JP2013/070745 WO2014021382A1 (en) 2012-07-31 2013-07-31 Cold-rolled steel sheet, electrolytic zinc-coated cold-rolled steel sheet, hot-dip zinc-coated cold-rolled steel sheet, alloyed hot-dip zinc-coated cold-rolled steel sheet, and methods for producing said steel sheets

Publications (1)

Publication Number Publication Date
IN2015DN00401A true IN2015DN00401A (en) 2015-06-19

Family

ID=50028052

Family Applications (1)

Application Number Title Priority Date Filing Date
IN401DEN2015 IN2015DN00401A (en) 2012-07-31 2013-07-31

Country Status (12)

Country Link
US (1) US9879336B2 (en)
EP (1) EP2881483B1 (en)
JP (1) JP5582274B2 (en)
KR (1) KR101649456B1 (en)
CN (1) CN104487603B (en)
BR (1) BR112015001475B1 (en)
ES (1) ES2756328T3 (en)
IN (1) IN2015DN00401A (en)
MX (1) MX365928B (en)
PL (1) PL2881483T3 (en)
TW (1) TWI488979B (en)
WO (1) WO2014021382A1 (en)

Families Citing this family (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6264861B2 (en) * 2013-11-27 2018-01-24 新日鐵住金株式会社 High Young's modulus cold-rolled steel sheet excellent in workability, electrogalvanized cold-rolled steel sheet, hot-dip galvanized cold-rolled steel sheet, alloyed hot-dip galvanized cold-rolled steel sheet, and production methods thereof
JP6248782B2 (en) * 2014-04-22 2017-12-20 新日鐵住金株式会社 High Young's modulus cold-rolled steel sheet, high Young's modulus electrogalvanized cold-rolled steel sheet, high Young's modulus hot-dip galvanized cold-rolled steel sheet, high Young's modulus galvannealed cold-rolled steel sheet, and methods for producing them
JP6032300B2 (en) * 2015-02-03 2016-11-24 Ｊｆｅスチール株式会社 High-strength cold-rolled steel sheet, high-strength galvanized steel sheet, high-strength hot-dip galvanized steel sheet, high-strength galvannealed steel sheet, and methods for producing them
JP6032299B2 (en) * 2015-02-03 2016-11-24 Ｊｆｅスチール株式会社 High-strength cold-rolled steel sheet, high-strength galvanized steel sheet, high-strength hot-dip galvanized steel sheet, high-strength galvannealed steel sheet, and methods for producing them
JP6032298B2 (en) * 2015-02-03 2016-11-24 Ｊｆｅスチール株式会社 High-strength cold-rolled steel sheet, high-strength galvanized steel sheet, high-strength hot-dip galvanized steel sheet, high-strength galvannealed steel sheet, and methods for producing them
JP6443126B2 (en) * 2015-02-26 2018-12-26 新日鐵住金株式会社 Ferritic steel sheet
KR101795918B1 (en) * 2015-07-24 2017-11-10 주식회사 포스코 Hot dip galvanized and galvannealed steel sheet having higher bake hardening and aging properties, and method for the same
KR102058601B1 (en) * 2015-08-24 2019-12-23 닛폰세이테츠 가부시키가이샤 Alloyed hot dip galvanized steel sheet and its manufacturing method
CN108097720B (en) * 2017-11-28 2020-09-25 甘肃酒钢集团宏兴钢铁股份有限公司 Rolling process of pure titanium cold-rolled thin titanium strip with width of 1250mm
US11035022B2 (en) * 2018-04-02 2021-06-15 Nippon Steel Corporation Metal sheet, method of producing metal sheet, method of producing molded product of metal sheet, and molded product of metal sheet
KR102426248B1 (en) * 2020-11-05 2022-07-28 주식회사 포스코 Method for manufacturing hot-dip galvanized high strength steel sheet having excellent distinctness of image after painting
KR102468036B1 (en) * 2020-11-12 2022-11-17 주식회사 포스코 High-strength hot-dip galvanized steel sheet with excellent formability and process for producing same

Family Cites Families (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5324892B2 (en) * 1972-10-19 1978-07-24
US4973367A (en) 1988-12-28 1990-11-27 Kawasaki Steel Corporation Method of manufacturing steel sheet having excellent deep-drawability
JPH0730411B2 (en) * 1988-12-28 1995-04-05 川崎製鉄株式会社 Method for producing hot rolled steel sheet with excellent deep drawability
JPH05255804A (en) 1992-03-11 1993-10-05 Nippon Steel Corp Cold rolled steel sheet excellent in formability and rigidity and its manufacture
JP3450985B2 (en) * 1997-04-10 2003-09-29 新日本製鐵株式会社 High-strength cold-rolled steel sheet having good shape and excellent bendability and manufacturing method thereof
TW476790B (en) * 1998-05-18 2002-02-21 Kawasaki Steel Co Electrical sheet of excellent magnetic characteristics and its manufacturing method
JP2000104144A (en) 1998-07-29 2000-04-11 Kawasaki Steel Corp Silicon steel sheet excellent in magnetic property in l orientation and c orientation and its production
US6368728B1 (en) 1998-11-18 2002-04-09 Kawasaki Steel Corporation Galvannealed steel sheet and manufacturing method
EP1136575A4 (en) * 1999-08-10 2008-04-23 Jfe Steel Corp Method of producing cold rolled steel sheet
US7076983B2 (en) * 2001-03-16 2006-07-18 Nakayama Steel Works, Ltd. Apparatus and method for hot rolling
JP4059050B2 (en) * 2001-10-05 2008-03-12 Ｊｆｅスチール株式会社 Cold rolled steel plate manufacturing base plate, high strength and high ductility cold rolled steel plate and methods for producing them
JPWO2004001084A1 (en) * 2002-06-25 2005-10-20 Ｊｆｅスチール株式会社 High-strength cold-rolled steel sheet and manufacturing method thereof
JP3911226B2 (en) 2002-10-09 2007-05-09 新日本製鐵株式会社 Method for producing cold-rolled steel sheet with excellent shape freezing property
JP4126007B2 (en) 2003-10-20 2008-07-30 新日本製鐵株式会社 Cold-rolled steel sheet excellent in shape freezing property and bake hardenability and method for producing the same
JP4528137B2 (en) 2004-03-19 2010-08-18 新日本製鐵株式会社 Manufacturing method of high strength and high ductility steel sheet with excellent hole expandability
JP4843981B2 (en) 2004-03-31 2011-12-21 Ｊｆｅスチール株式会社 High-rigidity and high-strength steel sheet and manufacturing method thereof
AU2005227564B2 (en) * 2004-03-31 2008-02-21 Jfe Steel Corporation High-rigidity high-strength thin steel sheet and method for producing same
EP2700730A3 (en) * 2004-07-27 2017-08-09 Nippon Steel & Sumitomo Metal Corporation Steel sheet having high Young's modulus, hot-dip galvanized steel sheet using the same, alloyed hot-dip galvanized steel sheet, steel pipe having high Young's modulus, and methods for manufacturing these
JP4622783B2 (en) 2005-09-29 2011-02-02 Ｊｆｅスチール株式会社 High-strength thin steel sheet with excellent rigidity and manufacturing method thereof
EP1932932B1 (en) * 2005-10-05 2016-05-04 Nippon Steel & Sumitomo Metal Corporation Cold-rolled steel sheet excellent in coating curability in baking and cold slow-aging property and process for producing the same
JP5058508B2 (en) * 2005-11-01 2012-10-24 新日本製鐵株式会社 Low yield ratio type high Young's modulus steel plate, hot dip galvanized steel plate, alloyed hot dip galvanized steel plate and steel pipe, and production method thereof
JP5228447B2 (en) * 2006-11-07 2013-07-03 新日鐵住金株式会社 High Young's modulus steel plate and method for producing the same
JP5157215B2 (en) 2007-03-28 2013-03-06 Ｊｆｅスチール株式会社 High rigidity and high strength steel plate with excellent workability
JP5233142B2 (en) 2007-03-28 2013-07-10 Ｊｆｅスチール株式会社 High-stiffness and high-strength steel sheet excellent in hole expansibility and method for producing the same
JP5037415B2 (en) 2007-06-12 2012-09-26 新日本製鐵株式会社 High Young's modulus steel plate excellent in hole expansibility and method for producing the same
JP5088021B2 (en) 2007-07-05 2012-12-05 新日本製鐵株式会社 High-rigidity, high-strength cold-rolled steel sheet and manufacturing method thereof
BRPI0909806B1 (en) * 2008-03-27 2017-07-04 Nippon Steel & Sumitomo Metal Corporation Cold rolled sheet steel, galvanized sheet steel, hot dip galvanized sheet steel, and methods of producing the same
ES2758553T3 (en) 2009-11-30 2020-05-05 Nippon Steel Corp High strength steel sheet with excellent resistance to hydrogen brittleness and a maximum tensile strength of 900 MPa or more, and method for its production
PL2610357T3 (en) * 2010-08-23 2020-05-18 Nippon Steel Corporation Cold-rolled steel sheet and process for production thereof

Also Published As

Publication number Publication date
JPWO2014021382A1 (en) 2016-07-21
PL2881483T3 (en) 2020-02-28
KR20150029741A (en) 2015-03-18
CN104487603A (en) 2015-04-01
EP2881483A1 (en) 2015-06-10
TWI488979B (en) 2015-06-21
MX2015001071A (en) 2015-04-08
JP5582274B2 (en) 2014-09-03
BR112015001475B1 (en) 2020-04-22
US9879336B2 (en) 2018-01-30
EP2881483B1 (en) 2019-09-25
CN104487603B (en) 2017-03-08
ES2756328T3 (en) 2020-04-27
US20150203948A1 (en) 2015-07-23
WO2014021382A1 (en) 2014-02-06
MX365928B (en) 2019-06-20
KR101649456B1 (en) 2016-08-19
EP2881483A4 (en) 2016-04-13
TW201406969A (en) 2014-02-16
BR112015001475A2 (en) 2017-07-04

Similar Documents

Publication Publication Date Title
IN2015DN00401A (en)
BR112015024854A2 (en) hot rolled steel sheet and method for its production
MA32294B1 (en) The process of fabrication of cold rolled steel sheets in double-stage with very high resistance and sheets produced as such
IN2014DN11227A (en)
MX2014003083A (en) Non-grain-oriented magnetic steel sheet.
BR112012018552A2 (en) high strength cold rolled steel sheet and production method thereof
GB201214327D0 (en) High strength steel sheet excellent in seam weldability
MX2017003993A (en) High formability super strength cold-roll steel sheet or steel strip, and manufacturing method therefor.
IN2014CN02603A (en)
IN2014DN00268A (en)
IN2015DN02627A (en)
IN2014DN06146A (en)
IN2014KN01297A (en)
MX2015013941A (en) Cold-rolled steel sheet and manufacturing method therefor.
IN2015DN00283A (en)
MY171985A (en) High strength cold rolled steel sheet having yield strength with low planar anisotropy, and method for manufacturing the same
IN2014KN01254A (en)
MY171981A (en) High-strength, cold rolled steel sheet suitable for chemical conversion treatment, and method for manufacturing the same
MY163017A (en) High strength cold rolled steel sheet having excellent formability, and method for manufacturing the same
MX2016002690A (en) Hot-rolled steel sheet having excellent cold workability and excellent surface properties and hardness after working.
MY169973A (en) Steel sheet having excellent formability and method for producing the same
TH153590A (en)
TH135651B (en) High strength cold rolled steel plate, which has anti-yield strength with anisotropy properties. The low-plane type and the method for the production of such steel sheet.
TH162324B (en) High strength cold rolled steel plate with high yield ratio. And production method For the steel plate.
TH162324A (en) High strength cold rolled steel plate with high yield ratio. And production method For the steel plate.