BR112012024275A2 - Folha de aço galvanizado mergulhado no quente de alta resistência e de excelente moldabilidade e método de produção da mesma - Google Patents

Folha de aço galvanizado mergulhado no quente de alta resistência e de excelente moldabilidade e método de produção da mesma

Info

Publication number
BR112012024275A2
BR112012024275A2 BR112012024275A BR112012024275A BR112012024275A2 BR 112012024275 A2 BR112012024275 A2 BR 112012024275A2 BR 112012024275 A BR112012024275 A BR 112012024275A BR 112012024275 A BR112012024275 A BR 112012024275A BR 112012024275 A2 BR112012024275 A2 BR 112012024275A2
Authority
BR
Brazil
Prior art keywords
temperature
steel sheet
galvanized steel
excellent moldability
low
Prior art date
Application number
BR112012024275A
Other languages
English (en)
Inventor
Haruhiko Eguchi
Jun Hirowatari
Kazuhisa Kusumi
Kengo Takeda
Shintarou Fujii
Original Assignee
Nippon Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp filed Critical Nippon Steel Corp
Publication of BR112012024275A2 publication Critical patent/BR112012024275A2/pt

Abstract

folha de aço galvanizado mergulhado no quente de alta resistência e de excelente moldabilidade e método de produção da mesma. a presente invenção refere-se a uma folha de aço galvanizado mergulhado no quente de alta resistência com pouca flutuação em termos de qualidade de material no momento de produção e de excelente moldabilidade. controlando a quantidade de adição de ti no lugar da adição de nb ou b, é possível obter o efeito de retardar a recristalização e o crescimento de grãos mesmo que com recozimento por um processo de recozimento contínuo em uma faixa de temperatura que vai da temperatura de recozimento geral de 720°c até uma temperatura inferior a 800°c ou até a temperatura ac3 (região de temperatura de recozimento fácil). além disso, controlando as condições de laminação e do tratamento térmico, é possível controlar a taxa da fase ferrítica, o tamanho dos grãos das fases transformadas em baixa temperatura, a relação dos valores médios da nanodureza da fase ferrítica e das fases transformadas em baixa temperatura, e as flutuações de dureza das fases transformadas em baixa temperatura em um aço de estrutura compósita de ferrita e fases transformadas em baixas temperatura e obter uma folha de aço galvanizado mergulhado no quente de alta resistência que tem pouca flutuação em termos de qualidade de material e é de excelente moldabilidade.
BR112012024275A 2010-03-31 2011-03-31 Folha de aço galvanizado mergulhado no quente de alta resistência e de excelente moldabilidade e método de produção da mesma BR112012024275A2 (pt)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2010083390 2010-03-31
PCT/JP2011/058749 WO2011126064A1 (ja) 2010-03-31 2011-03-31 成形性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法

Publications (1)

Publication Number Publication Date
BR112012024275A2 true BR112012024275A2 (pt) 2023-12-05

Family

ID=44762999

Family Applications (1)

Application Number Title Priority Date Filing Date
BR112012024275A BR112012024275A2 (pt) 2010-03-31 2011-03-31 Folha de aço galvanizado mergulhado no quente de alta resistência e de excelente moldabilidade e método de produção da mesma

Country Status (7)

Country Link
US (2) US9228244B2 (pt)
JP (1) JP5114760B2 (pt)
KR (1) KR101410435B1 (pt)
CN (1) CN102639738B (pt)
BR (1) BR112012024275A2 (pt)
MX (1) MX2012011280A (pt)
WO (1) WO2011126064A1 (pt)

Families Citing this family (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5545414B2 (ja) 2012-01-13 2014-07-09 新日鐵住金株式会社 冷延鋼板及び冷延鋼板の製造方法
CN104040011B (zh) 2012-01-13 2016-06-22 新日铁住金株式会社 热冲压成型体以及热冲压成型体的制造方法
TWI468530B (zh) 2012-02-13 2015-01-11 新日鐵住金股份有限公司 冷軋鋼板、鍍敷鋼板、及其等之製造方法
MX2014012776A (es) * 2012-04-25 2014-11-21 Nippon Steel & Sumitomo Metal Corp Junta de soldadura por puntos.
WO2014021452A1 (ja) * 2012-08-03 2014-02-06 新日鐵住金株式会社 溶融亜鉛めっき鋼板及びその製造方法
KR101510505B1 (ko) * 2012-12-21 2015-04-08 주식회사 포스코 우수한 도금성과 초고강도를 갖는 고망간 용융아연도금강판의 제조방법 및 이에 의해 제조된 고망간 용융아연도금강판
ES2714097T3 (es) * 2013-07-01 2019-05-27 Nippon Steel & Sumitomo Metal Corp Chapa de acero laminada en frío, chapa de acero laminada en frío galvanizada y método para fabricar la misma
JP5800098B2 (ja) 2013-08-02 2015-10-28 Ｊｆｅスチール株式会社 高強度高ヤング率鋼板およびその製造方法
JP5737485B1 (ja) * 2013-08-02 2015-06-17 Ｊｆｅスチール株式会社 高強度高ヤング率鋼板およびその製造方法
US20180230570A1 (en) * 2015-07-01 2018-08-16 Tata Steel Ijmuiden B.V. High strength hot dip galvanised steel strip
CN108367539B (zh) 2015-12-15 2021-06-11 塔塔钢铁艾默伊登有限责任公司 高强度热浸镀锌钢带材
JP6380781B1 (ja) * 2017-02-13 2018-08-29 Ｊｆｅスチール株式会社 冷延鋼板とその製造方法
CN110541120B (zh) * 2019-10-18 2021-03-16 山东钢铁集团日照有限公司 汽车板用无屈服平台的热镀锌低合金高强钢的生产方法
CN115161443A (zh) * 2022-07-28 2022-10-11 江苏联峰实业有限公司 一种耐热钢退火工艺

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2704350B2 (ja) 1992-11-02 1998-01-26 新日本製鐵株式会社 プレス成形性の良好な高強度鋼板の製造方法
JP3370875B2 (ja) 1996-11-18 2003-01-27 株式会社神戸製鋼所 耐衝撃性に優れた高強度鋼板及びその製造方法
JPH11279693A (ja) * 1998-03-27 1999-10-12 Nippon Steel Corp 焼付硬化性に優れた良加工性高強度熱延鋼板とその製造方法
JP3990550B2 (ja) 2001-06-08 2007-10-17 新日本製鐵株式会社 形状凍結性に優れた低降伏比型高強度鋼板とその製造方法
CA2422753C (en) * 2000-09-21 2007-11-27 Nippon Steel Corporation Steel plate excellent in shape freezing property and method for production thereof
JP2002363685A (ja) 2001-06-07 2002-12-18 Nkk Corp 低降伏比高強度冷延鋼板
JP4523937B2 (ja) * 2003-01-15 2010-08-11 新日本製鐵株式会社 高強度溶融亜鉛系めっき鋼板及びその製造方法
JP5035268B2 (ja) * 2003-04-16 2012-09-26 Ｊｆｅスチール株式会社 高張力冷延鋼板
WO2005019487A1 (ja) * 2003-08-26 2005-03-03 Jfe Steel Corporation 高張力冷延鋼板およびその製造方法
JP4510488B2 (ja) * 2004-03-11 2010-07-21 新日本製鐵株式会社 成形性および穴拡げ性に優れた溶融亜鉛めっき複合高強度鋼板およびその製造方法
JP4730056B2 (ja) 2005-05-31 2011-07-20 Ｊｆｅスチール株式会社 伸びフランジ成形性に優れた高強度冷延鋼板の製造方法
JP4957185B2 (ja) * 2006-10-31 2012-06-20 Ｊｆｅスチール株式会社 塗装後降伏比の低い高靱性電縫鋼管用熱延鋼板およびその製造方法
JP5141232B2 (ja) 2007-12-18 2013-02-13 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5564754B2 (ja) 2008-01-16 2014-08-06 新日鐵住金株式会社 曲げ性に優れた高強度冷延鋼板の製造方法
JP5359296B2 (ja) 2008-01-17 2013-12-04 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5272412B2 (ja) 2008-01-17 2013-08-28 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
US8128762B2 (en) 2008-08-12 2012-03-06 Kobe Steel, Ltd. High-strength steel sheet superior in formability
JP5709151B2 (ja) * 2009-03-10 2015-04-30 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP4883216B2 (ja) * 2010-01-22 2012-02-22 Ｊｆｅスチール株式会社 加工性とスポット溶接性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法

Also Published As

Publication number Publication date
US9228244B2 (en) 2016-01-05
JP5114760B2 (ja) 2013-01-09
CN102639738A (zh) 2012-08-15
US20160002756A1 (en) 2016-01-07
KR20120068990A (ko) 2012-06-27
WO2011126064A1 (ja) 2011-10-13
US10113220B2 (en) 2018-10-30
MX2012011280A (es) 2012-11-06
JPWO2011126064A1 (ja) 2013-07-11
CN102639738B (zh) 2014-04-23
US20130000796A1 (en) 2013-01-03
KR101410435B1 (ko) 2014-06-20

Similar Documents

Publication Publication Date Title
BR112012024275A2 (pt) Folha de aço galvanizado mergulhado no quente de alta resistência e de excelente moldabilidade e método de produção da mesma
MX2018007646A (es) Metodo para producir una hoja de acero de alta fuerza que tiene ductilidad y formabilidad mejoradas y hoja de acero obtenida.
MX2018007649A (es) Metodo para producir una lamina de acero recubierta de alta resistencia que tenga ductilidad y conformabilidad mejorada, y lamina de acero recubierta obtenida.
CN106460115B (zh) 热处理钢材及其制造方法
MX2017009200A (es) Lamina de acero galvanizada de alta resistencia y metodo para producir la misma.
KR102455942B1 (ko) 향상된 강도, 연성 및 성형성을 갖는 고강도 피복 강 시트의 제조 방법
BR112012024625A2 (pt) folha de aço inoxidável ferrítico excelente em brilho de superfície e resistência a corrosão e processo para produção da mesma
EP3164521A1 (en) Method for manufacturing a high strength steel sheet and sheet obtained
BR112017002189A2 (pt) método para produzir uma folha de aço, folha de aço e uso de uma folha de aço
GB201315448D0 (en) High-strength steel sheet exerting excellent deep drawability at room temperature and warm temperatures and method for warm working same
BR112014002875A2 (pt) chapa de aço laminada a quente de alta razão de rendimento que tem excelente absorção de energia de impacto à baixa temperatura e resistência de amolecimento da haz, e método de produção da mesma
CN106929771B (zh) 1000MPa级双相高强镀锌带钢和钢板及制备方法
IN2014DN07404A (pt)
RU2016151388A (ru) Способ получения высокопрочного стального листа с покрытием, имеющего улучшенную прочность и пластичность, и полученный лист
MX2013005011A (es) Hoja de acero laminado de frio de alta resistencia que tiene capacidad de embuticion profunda y capacidad de temple en horno excelentes y metodo para su fabricacion.
MY157318A (en) Cold-rolled steel sheet with excellent aging property and bake hardening and method for manufacturing the same
BR112014005641A2 (pt) tira de aço galvanizada por imersão a quente de alta resistência
MX2019013150A (es) Metodo para producir una lamina de acero de alta resistencia que tiene alta ductilidad, formabilidad y soldadura y lamina de acero obtenida.
ES2899448T3 (es) Procedimiento de producción de una lámina de acero que tiene una resistencia, ductilidad y conformabilidad mejoradas
EP2997168A2 (en) High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath
MX2015013941A (es) Lamina de acero laminada en frio y metodo para la fabricacion de la misma.
WO2016001897A3 (en) Method for producing a high strength coated steel sheet having improved strength, formability and obtained sheet
CN103421941A (zh) 提高抗海洋大气腐蚀结构用钢板耐腐蚀性能的热处理方法
WO2015110585A1 (en) Hot-rolled ultrahigh strength steel strip product
CN104561793B (zh) 一种超高强度热轧基板镀锌板及其制造方法

Legal Events

Date Code Title Description
B08F Application dismissed because of non-payment of annual fees [chapter 8.6 patent gazette]

Free format text: REFERENTE AS 11A E 12A ANUIDADES.

B25D Requested change of name of applicant approved

Owner name: NIPPON STEEL AND SUMITOMO METAL CORPORATION (JP)

B25D Requested change of name of applicant approved

Owner name: NIPPON STEEL CORPORATION (JP)

B08K Patent lapsed as no evidence of payment of the annual fee has been furnished to inpi [chapter 8.11 patent gazette]

Free format text: EM VIRTUDE DO ARQUIVAMENTO PUBLICADO NA RPI 2762 DE 12-12-2023 E CONSIDERANDO AUSENCIA DE MANIFESTACAO DENTRO DOS PRAZOS LEGAIS, INFORMO QUE CABE SER MANTIDO O ARQUIVAMENTO DO PEDIDO DE PATENTE, CONFORME O DISPOSTO NO ARTIGO 12, DA RESOLUCAO 113/2013.