ATE287974T1 - VERFAHREN FÜR EIN FEUERVERZINKUNGS- UND ßGALVANNEALINGß-PROZESS IN EINEM ALUMINIUM- HALTIGEN ZINKBAD - Google Patents
VERFAHREN FÜR EIN FEUERVERZINKUNGS- UND ßGALVANNEALINGß-PROZESS IN EINEM ALUMINIUM- HALTIGEN ZINKBADInfo
- Publication number
- ATE287974T1 ATE287974T1 AT99958743T AT99958743T ATE287974T1 AT E287974 T1 ATE287974 T1 AT E287974T1 AT 99958743 T AT99958743 T AT 99958743T AT 99958743 T AT99958743 T AT 99958743T AT E287974 T1 ATE287974 T1 AT E287974T1
- Authority
- AT
- Austria
- Prior art keywords
- dip galvanizing
- bath
- galvanealing
- containing aluminum
- hot dip
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/003—Apparatus
- C23C2/0034—Details related to elements immersed in bath
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/003—Apparatus
- C23C2/0034—Details related to elements immersed in bath
- C23C2/00342—Moving elements, e.g. pumps or mixers
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/003—Apparatus
- C23C2/0034—Details related to elements immersed in bath
- C23C2/00342—Moving elements, e.g. pumps or mixers
- C23C2/00344—Means for moving substrates, e.g. immersed rollers or immersed bearings
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/003—Apparatus
- C23C2/0036—Crucibles
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/003—Apparatus
- C23C2/0038—Apparatus characterised by the pre-treatment chambers located immediately upstream of the bath or occurring locally before the dipping process
- C23C2/004—Snouts
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/325—Processes or devices for cleaning the bath
Landscapes
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Coating With Molten Metal (AREA)
- Coating By Spraying Or Casting (AREA)
- Electroplating And Plating Baths Therefor (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US09/197,708 US6177140B1 (en) | 1998-01-29 | 1998-11-23 | Method for galvanizing and galvannealing employing a bath of zinc and aluminum |
PCT/US1999/025768 WO2000031311A1 (en) | 1998-11-23 | 1999-11-05 | Method for galvanizing and galvannealing employing a bath of zinc and aluminum |
Publications (1)
Publication Number | Publication Date |
---|---|
ATE287974T1 true ATE287974T1 (de) | 2005-02-15 |
Family
ID=22730439
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
AT99958743T ATE287974T1 (de) | 1998-11-23 | 1999-11-05 | VERFAHREN FÜR EIN FEUERVERZINKUNGS- UND ßGALVANNEALINGß-PROZESS IN EINEM ALUMINIUM- HALTIGEN ZINKBAD |
Country Status (15)
Country | Link |
---|---|
US (1) | US6177140B1 (de) |
EP (1) | EP1141435B1 (de) |
JP (1) | JP4667603B2 (de) |
KR (1) | KR100643085B1 (de) |
CN (1) | CN1212421C (de) |
AT (1) | ATE287974T1 (de) |
AU (1) | AU758268B2 (de) |
BR (1) | BR9915624B1 (de) |
CA (1) | CA2351337C (de) |
DE (1) | DE69923477T2 (de) |
ES (1) | ES2237182T3 (de) |
MX (1) | MXPA01005183A (de) |
PT (1) | PT1141435E (de) |
RU (1) | RU2241063C2 (de) |
WO (1) | WO2000031311A1 (de) |
Families Citing this family (28)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6461364B1 (en) | 2000-01-05 | 2002-10-08 | Integrated Vascular Systems, Inc. | Vascular sheath with bioabsorbable puncture site closure apparatus and methods of use |
EP1404253B1 (de) * | 2001-07-06 | 2008-12-03 | Angiomed GmbH & Co. Medizintechnik KG | Abgabesystem mit einer schieberanordnung für einen selbstexpandierenden stent und eine schnellwechselkonfiguration |
GB0123633D0 (en) * | 2001-10-02 | 2001-11-21 | Angiomed Ag | Stent delivery system |
JP2004124144A (ja) * | 2002-10-01 | 2004-04-22 | Chugai Ro Co Ltd | 連続溶融金属めっき設備 |
CA2513082C (en) * | 2003-01-15 | 2010-11-02 | Angiomed Gmbh & Co. Medizintechnik Kg | Trans-luminal surgical device |
GB0327306D0 (en) * | 2003-11-24 | 2003-12-24 | Angiomed Gmbh & Co | Catheter device |
AT412418B (de) * | 2003-01-20 | 2005-02-25 | Voest Alpine Ind Anlagen | Tauchrolle |
FR2876711B1 (fr) * | 2004-10-20 | 2006-12-08 | Usinor Sa | Procede de revetement au trempe a chaud dans un bain de zinc des bandes en acier fer-carbone-manganese |
US7914851B2 (en) * | 2004-12-28 | 2011-03-29 | Posco | Method of manufacturing hot-dipped galvanized steel sheet |
WO2007048883A1 (fr) | 2005-10-27 | 2007-05-03 | Usinor | Procede de fabrication d'une piece a tres hautes caracteristiques mecaniques a partir d'une tole laminee et revetue |
US20100055344A1 (en) * | 2006-05-15 | 2010-03-04 | Thyssenkrupp Steel Ag | Process for Producing a Sheet Steel Product Coated with an Anticorrosion System |
EP1857566B1 (de) * | 2006-05-15 | 2017-05-03 | ThyssenKrupp Steel Europe AG | Mit einem Korrosionsschutzüberzug versehenes Stahlflachprodukt und Verfahren zu seiner Herstellung |
US20080085071A1 (en) * | 2006-10-05 | 2008-04-10 | Wayne-Dalton Corporation | Pressurized bearing assembly |
CN101842509A (zh) * | 2007-09-10 | 2010-09-22 | 帕蒂·J·西珀拉 | 用于改进具有高抗拉强度的镀锌钢的成形性的方法及设备 |
KR101502198B1 (ko) * | 2008-02-08 | 2015-03-12 | 지멘스 바이 메탈스 테크놀로지 에스에이에스 | 강철 스트립의 경화 아연도금을 위한 방법 |
CN100591794C (zh) * | 2008-07-31 | 2010-02-24 | 攀钢集团研究院有限公司 | 热镀锌钢板的镀锌方法 |
US20110256420A1 (en) * | 2008-07-30 | 2011-10-20 | Pangang Group Steel Vanadium & Titanium Co., Ltd. | Hot-dip galvanized steel plate and production method thereof |
CN100596311C (zh) * | 2008-07-31 | 2010-03-31 | 攀钢集团研究院有限公司 | 热镀锌钢板的制法 |
DE102011118197B3 (de) | 2011-11-11 | 2013-05-08 | Thyssenkrupp Steel Europe Ag | Verfahren und Vorrichtung zum Schmelztauchbeschichten eines Metallbands mit einem metallischen Überzug |
DE102011118199B3 (de) | 2011-11-11 | 2013-05-08 | Thyssenkrupp Steel Europe Ag | Verfahren und Vorrichtung zum Schmelztauchbeschichten eines Metallbands mit einem metallischen Überzug |
RU2485205C1 (ru) * | 2011-11-23 | 2013-06-20 | Российская Федерация, от имени которой выступает Министерство промышленности и торговли Российской Федерации (Минпромторг России) | Состав расплава на основе цинка для нанесения защитных покрытий на стальную полосу горячим погружением |
CN102621941B (zh) * | 2012-01-19 | 2014-08-20 | 东北大学 | 一种冷轧电镀锌机组钢卷排序方法及系统 |
CN108541274B (zh) | 2015-12-23 | 2021-01-15 | 巴斯夫欧洲公司 | 用于加热气体的热交换器以及该热交换器的用途 |
US11208711B2 (en) | 2018-11-15 | 2021-12-28 | Psitec Oy | Method and an arrangement for manufacturing a hot dip galvanized rolled high strength steel product |
WO2020157198A1 (en) * | 2019-02-01 | 2020-08-06 | Primetals Technologies France SAS | Method of coating a part to be submerged into a galvanizing bath and parts thereof |
CN109881134A (zh) * | 2019-04-16 | 2019-06-14 | 中冶赛迪工程技术股份有限公司 | 钢带连续热浸镀锌的锌锅智能加锌方法、设备及存储介质 |
KR102148459B1 (ko) * | 2019-05-03 | 2020-08-26 | (주)스텝이엔지 | 강판 용융아연도금 공정에서의 탕면 이물질제거장치 |
US11384419B2 (en) * | 2019-08-30 | 2022-07-12 | Micromaierials Llc | Apparatus and methods for depositing molten metal onto a foil substrate |
Family Cites Families (25)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3323940A (en) * | 1964-01-20 | 1967-06-06 | Inland Steel Co | Method for producing smooth galvanized sheet |
US3977842A (en) * | 1968-08-27 | 1976-08-31 | National Steel Corporation | Product and process |
US3619247A (en) * | 1968-08-29 | 1971-11-09 | Bethlehem Steel Corp | Method of producing thin, bright unspangled galvanized coatings on ferrous metal strips |
LU77032A1 (de) * | 1976-04-01 | 1977-07-22 | ||
JPS54149334A (en) * | 1978-05-17 | 1979-11-22 | Nisshin Steel Co Ltd | One side lead*other side zinc plated steel plate and production thereof |
JPS55128569A (en) * | 1979-03-26 | 1980-10-04 | Nippon Kokan Kk <Nkk> | Method and apparatus for hot galvanization |
US4361448A (en) | 1981-05-27 | 1982-11-30 | Ra-Shipping Ltd. Oy | Method for producing dual-phase and zinc-aluminum coated steels from plain low carbon steels |
JPS6237360A (ja) * | 1985-08-09 | 1987-02-18 | Sumitomo Metal Ind Ltd | 連続式溶融亜鉛めつき鋼板製造方法 |
JPS6240353A (ja) * | 1985-08-14 | 1987-02-21 | Sumitomo Metal Ind Ltd | 合金化亜鉛めつき鋼板の製造方法 |
US4759807A (en) | 1986-12-29 | 1988-07-26 | Rasmet Ky | Method for producing non-aging hot-dip galvanized steel strip |
US4971842A (en) * | 1987-02-27 | 1990-11-20 | Rasmet Ky | Method for controlling the thickness of an intermetallic layer on a continuous steel product in a continuous hot-dip galvanizing process |
US4752508A (en) * | 1987-02-27 | 1988-06-21 | Rasmet Ky | Method for controlling the thickness of an intermetallic (Fe-Zn phase) layer on a steel strip in a continuous hot-dip galvanizing process |
JPS63297544A (ja) * | 1987-05-29 | 1988-12-05 | Nisshin Steel Co Ltd | 合金化溶融亜鉛めっき鋼板の製造方法 |
JPH01263255A (ja) * | 1988-04-14 | 1989-10-19 | Nippon Aen Kogyo Kk | 高付着溶融アルミニウム−亜鉛合金めっき方法 |
JP2575468B2 (ja) * | 1988-06-29 | 1997-01-22 | 川崎製鉄株式会社 | 連続溶融亜鉛めっき装置 |
US4913746A (en) * | 1988-08-29 | 1990-04-03 | Lehigh University | Method of producing a Zn-Fe galvanneal on a steel substrate |
EP0406619A1 (de) | 1989-06-21 | 1991-01-09 | Nippon Steel Corporation | Verfahren zur Herstellung von kaltgewalzten verzinkten nichtalternden Stahlblechen mit guter Formbarkeit in einer Durchlaufverzinkungslinie |
JPH04232239A (ja) | 1990-12-28 | 1992-08-20 | Nkk Corp | 耐パウダリング性の優れた合金化溶融亜鉛めっき鋼板の製造方法 |
JP2658580B2 (ja) | 1990-12-29 | 1997-09-30 | 日本鋼管株式会社 | プレス成形性および耐パウダリング性の優れた合金化溶融亜鉛めっき鋼板の製造方法 |
JP2560662B2 (ja) * | 1991-07-09 | 1996-12-04 | 住友金属工業株式会社 | 表面欠陥の少ない溶融亜鉛めっき鋼板の製造装置 |
JPH05171385A (ja) * | 1991-12-26 | 1993-07-09 | Kawasaki Steel Corp | 鋼帯の連続溶融亜鉛めっき方法および装置 |
KR100260225B1 (ko) | 1993-06-25 | 2000-07-01 | 에모토 간지 | 도금 결함이 적은 고장력강판의 용융아연도금방법 |
BE1007793A6 (fr) | 1993-12-24 | 1995-10-24 | Centre Rech Metallurgique | Procede et installation de traitement continu d'une bande d'acier galvanisee. |
JPH0860327A (ja) | 1994-08-16 | 1996-03-05 | Nippon Steel Corp | 合金化亜鉛めっき鋼板の製造方法 |
JP3375546B2 (ja) * | 1998-07-03 | 2003-02-10 | 川崎製鉄株式会社 | 合金化溶融亜鉛めっき鋼板 |
-
1998
- 1998-11-23 US US09/197,708 patent/US6177140B1/en not_active Expired - Lifetime
-
1999
- 1999-11-05 WO PCT/US1999/025768 patent/WO2000031311A1/en active IP Right Grant
- 1999-11-05 RU RU2001117509/02A patent/RU2241063C2/ru active
- 1999-11-05 DE DE69923477T patent/DE69923477T2/de not_active Expired - Lifetime
- 1999-11-05 KR KR1020017006420A patent/KR100643085B1/ko active IP Right Grant
- 1999-11-05 BR BRPI9915624-5A patent/BR9915624B1/pt not_active IP Right Cessation
- 1999-11-05 PT PT99958743T patent/PT1141435E/pt unknown
- 1999-11-05 AT AT99958743T patent/ATE287974T1/de active
- 1999-11-05 EP EP99958743A patent/EP1141435B1/de not_active Expired - Lifetime
- 1999-11-05 MX MXPA01005183A patent/MXPA01005183A/es active IP Right Grant
- 1999-11-05 AU AU16040/00A patent/AU758268B2/en not_active Expired
- 1999-11-05 ES ES99958743T patent/ES2237182T3/es not_active Expired - Lifetime
- 1999-11-05 CA CA002351337A patent/CA2351337C/en not_active Expired - Lifetime
- 1999-11-05 JP JP2000584118A patent/JP4667603B2/ja not_active Expired - Lifetime
- 1999-11-05 CN CNB998158089A patent/CN1212421C/zh not_active Expired - Lifetime
Also Published As
Publication number | Publication date |
---|---|
DE69923477D1 (de) | 2005-03-03 |
KR100643085B1 (ko) | 2006-11-10 |
MXPA01005183A (es) | 2003-06-06 |
WO2000031311A9 (en) | 2002-04-11 |
RU2241063C2 (ru) | 2004-11-27 |
JP4667603B2 (ja) | 2011-04-13 |
CN1333841A (zh) | 2002-01-30 |
CA2351337A1 (en) | 2000-06-02 |
BR9915624B1 (pt) | 2010-01-26 |
ES2237182T3 (es) | 2005-07-16 |
US6177140B1 (en) | 2001-01-23 |
DE69923477T2 (de) | 2005-12-29 |
CA2351337C (en) | 2009-01-20 |
EP1141435A1 (de) | 2001-10-10 |
JP2002530535A (ja) | 2002-09-17 |
AU1604000A (en) | 2000-06-13 |
AU758268B2 (en) | 2003-03-20 |
WO2000031311A1 (en) | 2000-06-02 |
KR20010093105A (ko) | 2001-10-27 |
CN1212421C (zh) | 2005-07-27 |
BR9915624A (pt) | 2001-08-14 |
PT1141435E (pt) | 2005-04-29 |
EP1141435B1 (de) | 2005-01-26 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
ATE287974T1 (de) | VERFAHREN FÜR EIN FEUERVERZINKUNGS- UND ßGALVANNEALINGß-PROZESS IN EINEM ALUMINIUM- HALTIGEN ZINKBAD | |
GB2204594A (en) | Continuous electrodeposition of chromium metal and chromium oxide on metal surfaces | |
DE68923674D1 (de) | Mit zink-aluminium-legierung beschichtetes feuerverzinktes stahlblech für vorgestrichenes stahlblech und verfahren zu seiner herstellung. | |
ATE71987T1 (de) | Verfahren zum kontrollieren der dicke einer intermetallischen schicht auf einem kontistahlerzeugnis innerhalb eines feuerverzinkprozesses. | |
JPS61201767A (ja) | 二段めつき方法 | |
BR8502567A (pt) | Processo de fabricacao de uma cinta de chapa de aco galvanizado a quente isenta de revestimento de zinco puro ou a base de zinco em pelo menos uma face e dispositivo de escovar para aplicacao do processo | |
BR9908146A (pt) | Processo produtivo de folha de aço zincada em banho quente isenta de defeitos de absorção de borra durante recobrimento e aparelho associado | |
ATE134221T1 (de) | Verfahren zum mehrlagigen beschichten von strangförmigem gut | |
ATE124092T1 (de) | Verfahren zum heissmetallisieren von bandstahl. | |
ATE262049T1 (de) | Verfahren und anlage zum feuerverzinken von warmgewalztem stahlband | |
US3089780A (en) | Method and composition for shielding steel from molten coating metal | |
KR950018604A (ko) | 용융아연_합금_도금방법 | |
ATE203062T1 (de) | Verfahren zum wärmebehandeln von znal- schmelztauchbeschichtetem feinblech | |
JPS648705B2 (de) | ||
DE50107196D1 (de) | Verfahren zum herstellen eines mit einer zinkbeschichtung versehenen stahlbandes | |
Singh et al. | A Method to Evaluate Zinc Spelter Cleanliness for Hot-Dip Galvanizing | |
AU9704598A (en) | A method of hot-galvanizing ferrous materials | |
ES2162725B2 (es) | "procedimiento de galvanizacion de chapas de acero". | |
DE69506473D1 (de) | Verfahren zur Herstellung eines feuerverzinkten Stahlbandes | |
JPH07258814A (ja) | 耐食性に優れた合金化溶融亜鉛めっき鋼板 | |
RU95112581A (ru) | Непрерывный способ нанесения гальванопокрытия | |
Ferrier et al. | Relations Between Surface State and Behaviour of Steel for Hot Dip Galvanizing | |
Pugazhenthy | Hot Dip Galvanizing: The Ultimate Answer to Corrosion Protection | |
Bell et al. | A new and improved corrosion protection for band steel | |
JPS59173254A (ja) | 高耐食性亜鉛めつき材の製造法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
UEP | Publication of translation of european patent specification |
Ref document number: 1141435 Country of ref document: EP |
|
EEIH | Change in the person of patent owner |