WO2024019013A1 - 鋼材 - Google Patents

鋼材 Download PDF

Info

Publication number
WO2024019013A1
WO2024019013A1 PCT/JP2023/026060 JP2023026060W WO2024019013A1 WO 2024019013 A1 WO2024019013 A1 WO 2024019013A1 JP 2023026060 W JP2023026060 W JP 2023026060W WO 2024019013 A1 WO2024019013 A1 WO 2024019013A1
Authority
WO
WIPO (PCT)
Prior art keywords
particles
steel material
content
steel
number density
Prior art date
Application number
PCT/JP2023/026060
Other languages
English (en)
French (fr)
Inventor
利治 間曽
慶 宮西
Original Assignee
日本製鉄株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本製鉄株式会社 filed Critical 日本製鉄株式会社
Publication of WO2024019013A1 publication Critical patent/WO2024019013A1/ja

Abstract

優れた耐溶融割れ性、優れた耐熱間加工割れ性、及び、優れた被削性を有し、機械構造用部品とした場合に高い疲労強度を得ることができる鋼材を提供する。本開示による鋼材は、明細書に記載の化学組成を有し、式（１）で定義されるＦｎが０．４５～１．０５であり、鋼材の表面から０．０８Ｒ深さ位置において（Ｒは半径）、円相当径が０．１～１．０μｍのＢｉ粒子である微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２以上であり、円相当径が１０．０μｍ以上のＢｉ粒子である粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２以下であり、鋼材の表面から０．６５Ｒ深さ位置において、微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２未満であり、粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２超である。

Description

鋼材
　本開示は鋼材に関し、さらに詳しくは、機械構造用部品の素材となる鋼材に関する。
　機械構造用部品は、自動車及び建設車両のクランクシャフト等に代表される自動車部品に利用される。機械構造用部品には、高い疲労強度が求められる。
　機械構造用部品の疲労強度を向上させる技術は、例えば、特開２００８－１６９４１１号公報（特許文献１）に開示されている。
　特許文献１に開示された、機械構造用部品の素材となる鋼材は、質量％で、Ｃ：０．１５～０．５５％、Ｓｉ：０．０１～２．０％、Ｍｎ：０．０１～２．５％、Ｃｕ：０．０１～２．０％、Ｎｉ：０．０１～２．０％、Ｃｒ：０．０１～２．５％、Ｍｏ：０．０１～３．０％、及び、Ｖ及びＷからなる群から選ばれる少なくとも１種の総量：０．０１～１．０％を含有し、残部がＦｅ及び不可避的不純物からなる。この鋼材は、１０１０℃～１０５０℃で均熱した後、２００℃／分以上の冷却速度で５００℃～５５０℃まで冷却し、引き続き、１００℃／分以上の冷却速度で１５０℃以下まで冷却し、次いで、５５０℃～７００℃の温度域で加熱した後の、室温におけるＨＲＣ硬さの最大値を与えるＬＭＰが１７．６６以上である。この文献では、上記条件で熱処理を行った後の室温におけるＨＲＣ硬さの最大値を与えるＬＭＰを１７．６６以上とし、軟化抵抗を高めることにより、疲労特性を高めている。
特開２００８－１６９４１１号公報
　ところで、機械構造用部品の疲労強度の向上のために、機械構造用部品に対して表面硬化処理が施される場合がある。
　種々の表面硬化処理の一つに、高周波焼入れがある。高周波焼入れは、必要な部位のみ硬化させることができる。高周波焼入れは、高温で加熱した後に冷却して、鋼材の表層に硬化層を形成する。高周波焼入れでは、軟窒化等の他の表面硬化処理と比較して、大きい硬化層深さ及び高い疲労強度が得られる。
　機械構造用部品がクランクシャフトである場合を一例として、機械構造用部品に施される高周波焼入れ処理について説明する。機械構造用部品であるクランクシャフトが図１に示す形状である場合、クランクシャフトの疲労強度を高めるために、例えば、クランクシャフトのフィレットＲ部１に高周波焼入れが施される。この場合、フィレットＲ部１の表層に硬化層が形成される。
　硬化層深さを大きくするためには、高周波焼入れにおいて、高周波電力の出力を増加して加熱温度を高めればよい。しかしながら、高温で高周波焼入れを実施する場合、機械構造用部品のエッジ部で、加熱温度が過剰に高くなりやすい。例えば、機械構造用部品が図１に示すクランクシャフトである場合、エッジ部２で加熱温度が過剰に高くなる。特に、高周波焼入れ時の昇温速度が速い場合、加熱温度が過剰に高くなりやすい。
　例えば、高周波焼入れでの加熱温度が過剰に高くなり、１３５０℃以上となる場合、鋼材の一部が溶融して割れが発生する場合がある。以下、このような割れを、本明細書では、「溶融割れ」という。このような溶融割れの発生は抑制できる方が好ましい。つまり、鋼材には、優れた耐溶融割れ性が求められる。
　また、機械構造用部品の素材となる鋼材では、機械構造用部品の製造工程中、又は、鋼材の製造工程中において、熱間加工が施される。そのため、鋼材において、熱間加工による割れ（熱間加工割れ）の発生の抑制が求められる。つまり、鋼材には、優れた耐熱間加工割れ性が求められる。
　さらに、機械構造用部品の素材となる鋼材は、機械構造用部品の製造工程中において、切削加工を施される。鋼材の特に内部において、優れた被削性が求められる場合がある。例えば機械構造用部品がクランクシャフトの場合、両端面の中心部分に穴あけなどの加工が実施される。そのため、鋼材には、鋼材内部における優れた被削性が求められる。
　上述の特許文献１では、鋼材の耐溶融割れ性、耐熱間加工割れ性、及び、被削性について検討されていない。
　本開示の目的は、優れた耐溶融割れ性、優れた耐熱間加工割れ性、及び、優れた被削性を有し、機械構造用部品の素材として利用された場合に、機械構造用部品が高い疲労強度を得ることができる鋼材を提供することである。
　本開示による鋼材は、軸方向に垂直な断面が円形状の鋼材であって、
　化学組成が、質量％で、
　Ｃ：０．３０超～０．６０％、
　Ｓｉ：０．０１～０．９０％、
　Ｍｎ：０．５０～１．７０％、
　Ｐ：０．０３０％以下、
　Ｓ：０．２００％以下、
　Ｂｉ：０．００５１～０．２５００％、
　Ａｌ：０．００１～０．１００％、
　Ｎ：０．０２５０％以下、
　Ｏ：０．００５０％以下、
　Ｃｒ：０～１．３０％、
　Ｖ：０～０．２００％、
　Ｓｎ：０～０．１０００％、
　Ｓｂ：０～０．０５００％、
　Ａｓ：０～０．０５００％、
　Ｐｂ：０～０．０９％、
　Ｍｇ：０～０．０１００％、
　Ｔｉ：０～０．０４００％、
　Ｎｂ：０～０．０５００％、
　Ｗ：０～０．４０００％、
　Ｚｒ：０～０．２０００％、
　Ｃａ：０～０．０１００％、
　Ｔｅ：０～０．０１００％、
　Ｂ：０～０．００５０％、
　希土類元素：０～０．０１００％、
　Ｃｏ：０～０．０１００％、
　Ｓｅ：０～０．０１００％、
　Ｉｎ：０～０．０１００％、
　Ｍｏ：０～０．３０％、
　Ｃｕ：０～０．５０％、
　Ｎｉ：０～０．５０％、及び、
　残部はＦｅ及び不純物からなり、
　式（１）で定義されるＦｎが０．４５～１．０５であり、
　前記鋼材の半径をＲと定義したとき、前記鋼材の表面から０．０８Ｒ深さ位置において、
　円相当径が０．１～１．０μｍのＢｉ粒子である微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２以上であり、
　円相当径が１０．０μｍ以上のＢｉ粒子である粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２以下であり、
　前記鋼材の表面から０．６５Ｒ深さ位置において、
　前記微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２未満であり、
　前記粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２超である。
　Ｆｎ＝Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ　（１）
　ここで、式（１）中の各元素記号には、対応する元素の質量％での含有量が代入され、元素が含有されていない場合、対応する元素記号には「０」が代入される。
　本開示の鋼材は、優れた耐溶融割れ性、優れた耐熱間加工割れ性、及び、優れた被削性を有し、機械構造用部品の素材として利用された場合に、機械構造用部品が高い疲労強度を得ることができる。
図１は、機械構造用部品の一例であるクランクシャフトの一部の正面図である。 図２は、本実施形態の鋼材の軸方向に垂直な断面図である。 図３は、実施例中の溶融割れ評価試験でのミクロ組織の模式図である。 図４は、実施例中の溶融割れ評価試験での図３と異なるミクロ組織の模式図である。 図５は、実施例の疲労強度評価試験に用いられる疲労試験片の側面図である。
　本発明者らは、初めに、機械構造用部品の素材として利用した場合に機械構造用部品の疲労強度が高まる鋼材の化学組成について検討を行った。その結果、本発明者らは、質量％で、Ｃ：０．３０超～０．６０％、Ｓｉ：０．０１～０．９０％、Ｍｎ：０．５０～１．７０％、Ｐ：０．０３０％以下、Ｓ：０．２００％以下、Ａｌ：０．００１～０．１００％、Ｎ：０．０２５０％以下、Ｏ：０．００５０％以下、Ｃｒ：０～１．３０％、Ｖ：０～０．２００％、Ｓｎ：０～０．１０００％、Ｓｂ：０～０．０５００％、Ａｓ：０～０．０５００％、Ｐｂ：０～０．０９％、Ｍｇ：０～０．０１００％、Ｔｉ：０～０．０４００％、Ｎｂ：０～０．０５００％、Ｗ：０～０．４０００％、Ｚｒ：０～０．２０００％、Ｃａ：０～０．０１００％、Ｔｅ：０～０．０１００％、Ｂ：０～０．００５０％、希土類元素：０～０．０１００％、Ｃｏ：０～０．０１００％、Ｓｅ：０～０．０１００％、Ｉｎ：０～０．０１００％、Ｍｏ：０～０．３０％、Ｃｕ：０～０．５０％、Ｎｉ：０～０．５０％、及び、残部はＦｅ及び不純物からなる化学組成を有する鋼材であれば、この鋼材を素材として機械構造用部品を製造した場合に、機械構造用部品が優れた疲労強度を有する可能性があると考えた。
　続いて、本発明者らは、化学組成中の各元素含有量が上述の範囲内である鋼材において、被削性を高める手段を検討した。その結果、本発明者らは、式（１）で定義されるＦｎを０．４５～１．０５とすることにより、機械構造用部品において優れた疲労強度が得られ、かつ、機械構造用部品の素材である鋼材の被削性が高まることを見出した。
　Ｆｎ＝Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ　（１）
　本発明者らはさらに、高周波焼入れ時における鋼材の耐溶融割れ性を高める手段を検討した。
　高周波焼入れ時の鋼材に発生する溶融割れには、Ｃ含有量が影響する。具体的には、粒界に偏析するＣにより粒界での融点が下がる。その結果、溶融割れが発生しやすくなる。そこで、上述の化学組成にさらに、Ｂｉを０．００５１～０．２５００％含有する。Ｂｉを上述の範囲で含有すれば、鋼材中にＢｉ粒子（介在物）が生成する。微細なＢｉ粒子は、ピン止め効果により、高周波焼入れ時の鋼材中の結晶粒（オーステナイト粒）の粗大化を抑制する。高周波焼入れ時において、結晶粒を微細に維持できれば、粒界面積の低減を抑制できる。粒界面積の低減を抑制でき、ある程度の粒界面積を確保できれば、単位面積当たりの粒界に偏析するＣ濃度が減少する。その結果、溶融割れの発生が抑制される。
　しかしながら、鋼材に上述の範囲のＢｉを含有した場合、微細なＢｉ粒子だけでなく、粗大なＢｉ粒子も生成し得る。粗大なＢｉ粒子は、熱間加工割れの起点となる。そのため、粗大なＢｉ粒子が過剰に存在すれば、鋼材の耐熱間加工割れ性が低下する。
　一方で、粗大なＢｉ粒子は、鋼材の被削性を高める。以上を考慮すれば、上述の化学組成を有する鋼材において、上述の範囲のＢｉを含有することにより、優れた耐溶融割れ性と、優れた耐熱間加工割れ性と、優れた被削性とを同時に得ることは困難であるように思われる。
　しかしながら本発明者らは、鋼材の領域に応じて微細Ｂｉ粒子の個数密度と粗大Ｂｉ粒子の個数密度とを変えることにより、優れた耐溶融割れ性と、優れた耐熱間加工割れ性と、優れた被削性とを同時に得ることができると考えた。具体的には、鋼材のうち、溶融割れや熱間加工割れが発生しやすいのは、鋼材の表層領域である。したがって、鋼材の表層領域では、優れた耐溶融割れ性及び優れた耐熱間加工割れ性が得られるようにすればよい。一方、鋼材の内部領域では、溶融割れや熱間加工割れが発生しにくい。そこで、鋼材の内部領域では、高い被削性が得られるようにすればよい。
　以上の技術思想に基づいて、鋼材の表層領域及び内部領域における微細Ｂｉ粒子の個数密度及び粗大Ｂｉ粒子の個数密度と、鋼材の耐溶融割れ性、耐熱間加工割れ性及び被削性との関係について調査及び検討を行った。その結果、上述の化学組成を満たし、Ｆｎが０．４５～１．０５となる鋼材において、表層領域での微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２以上、粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２以下であり、内部領域での微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２未満、粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２超であれば、優れた耐溶融割れ性、優れた耐熱間加工割れ性、及び、優れた被削性を同時に満たすことができ、さらに、機械構造用部品の素材として利用された場合に、機械構造用部品において優れた疲労強度が得られることを本発明者らは見出した。
　以上の技術思想に基づいて完成した本実施形態による鋼材は、次の構成を有する。
　［１］
　軸方向に垂直な断面が円形状の鋼材であって、
　化学組成が、質量％で、
　Ｃ：０．３０超～０．６０％、
　Ｓｉ：０．０１～０．９０％、
　Ｍｎ：０．５０～１．７０％、
　Ｐ：０．０３０％以下、
　Ｓ：０．２００％以下、
　Ｂｉ：０．００５１～０．２５００％、
　Ａｌ：０．００１～０．１００％、
　Ｎ：０．０２５０％以下、
　Ｏ：０．００５０％以下、
　Ｃｒ：０～１．３０％、
　Ｖ：０～０．２００％、
　Ｓｎ：０～０．１０００％、
　Ｓｂ：０～０．０５００％、
　Ａｓ：０～０．０５００％、
　Ｐｂ：０～０．０９％、
　Ｍｇ：０～０．０１００％、
　Ｔｉ：０～０．０４００％、
　Ｎｂ：０～０．０５００％、
　Ｗ：０～０．４０００％、
　Ｚｒ：０～０．２０００％、
　Ｃａ：０～０．０１００％、
　Ｔｅ：０～０．０１００％、
　Ｂ：０～０．００５０％、
　希土類元素：０～０．０１００％、
　Ｃｏ：０～０．０１００％、
　Ｓｅ：０～０．０１００％、
　Ｉｎ：０～０．０１００％、
　Ｍｏ：０～０．３０％、
　Ｃｕ：０～０．５０％、
　Ｎｉ：０～０．５０％、及び、
　残部はＦｅ及び不純物からなり、
　式（１）で定義されるＦｎが０．４５～１．０５であり、
　前記鋼材の半径をＲと定義したとき、前記鋼材の表面から０．０８Ｒ深さ位置において、
　円相当径が０．１～１．０μｍのＢｉ粒子である微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２以上であり、
　円相当径が１０．０μｍ以上のＢｉ粒子である粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２以下であり、
　前記鋼材の表面から０．６５Ｒ深さ位置において、
　前記微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２未満であり、
　前記粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２超である、
　鋼材。
　Ｆｎ＝Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ　（１）
　ここで、式（１）中の各元素記号には、対応する元素の質量％での含有量が代入され、元素が含有されていない場合、対応する元素記号には「０」が代入される。
　［２］
　［１］に記載の鋼材であって、
　前記化学組成は、
　Ｃｒ：０．０１～１．３０％、
　Ｖ：０．００１～０．２００％、
　Ｓｎ：０．０００１～０．１０００％、
　Ｓｂ：０．０００１～０．０５００％、
　Ａｓ：０．０００１～０．０５００％、
　Ｐｂ：０．０１～０．０９％、
　Ｍｇ：０．０００１～０．０１００％、
　Ｔｉ：０．０００１～０．０４００％、
　Ｎｂ：０．０００１～０．０５００％、
　Ｗ：０．０００１～０．４０００％、
　Ｚｒ：０．０００１～０．２０００％、
　Ｃａ：０．０００１～０．０１００％、
　Ｔｅ：０．０００１～０．０１００％、
　Ｂ：０．０００１～０．００５０％、
　希土類元素：０．０００１～０．０１００％、
　Ｃｏ：０．０００１～０．０１００％、
　Ｓｅ：０．０００１～０．０１００％、
　Ｉｎ：０．０００１～０．０１００％、
　Ｍｏ：０．０１～０．３０％、
　Ｃｕ：０．０１～０．５０％、
　Ｎｉ：０．０１～０．５０％、
　からなる群から選択される１種以上を含有する、
　鋼材。
　以下、本実施形態の鋼材について詳述する。元素に関する「％」は、特に断りがない限り、質量％を意味する。
　［本実施形態の鋼材の特徴］
　本実施形態の鋼材は次の特徴１～特徴４を満たす。
　（特徴１）
　化学組成が、質量％で、Ｃ：０．３０超～０．６０％、Ｓｉ：０．０１～０．９０％、Ｍｎ：０．５０～１．７０％、Ｐ：０．０３０％以下、Ｓ：０．２００％以下、Ｂｉ：０．００５１～０．２５００％、Ａｌ：０．００１～０．１００％、Ｎ：０．０２５０％以下、Ｏ：０．００５０％以下、Ｃｒ：０～１．３０％、Ｖ：０～０．２００％、Ｓｎ：０～０．１０００％、Ｓｂ：０～０．０５００％、Ａｓ：０～０．０５００％、Ｐｂ：０～０．０９％、Ｍｇ：０～０．０１００％、Ｔｉ：０～０．０４００％、Ｎｂ：０～０．０５００％、Ｗ：０～０．４０００％、Ｚｒ：０～０．２０００％、Ｃａ：０～０．０１００％、Ｔｅ：０～０．０１００％、Ｂ：０～０．００５０％、希土類元素：０～０．０１００％、Ｃｏ：０～０．０１００％、Ｓｅ：０～０．０１００％、Ｉｎ：０～０．０１００％、Ｍｏ：０～０．３０％、Ｃｕ：０～０．５０％、Ｎｉ：０～０．５０％、及び、残部はＦｅ及び不純物からなる。
　（特徴２）
　式（１）で定義されるＦｎが０．４５～１．０５である。
　（特徴３）
　鋼材の半径をＲと定義したとき、鋼材の表面から０．０８Ｒ深さ位置において、円相当径が０．１～１．０μｍのＢｉ粒子である微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２以上であり、円相当径が１０．０μｍ以上のＢｉ粒子である粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２以下である。
　（特徴４）
　鋼材の表面から０．６５Ｒ深さ位置において、微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２未満であり、粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２超である。
　以下、特徴１～特徴４について説明する。
　［（特徴１）化学組成について］
　本実施形態の鋼材の化学組成は、次の元素を含有する。
　Ｃ：０．３０超～０．６０％
　炭素（Ｃ）は、鋼材を素材として製造された機械構造用部品の硬さを高め、機械構造用部品の疲労強度を高める。Ｃ含有量が０．３０％以下であれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が十分に得られない。
　一方、Ｃは鋼材の融点を低下させる。そのため、Ｃ含有量が０．６０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材を素材とした機械構造用部品の製造工程において鋼材に対して高周波焼入れを実施したとき、鋼材に溶融割れが発生しやすくなる。
　したがって、Ｃ含有量は０．３０超～０．６０％である。
　Ｃ含有量の好ましい下限は０．３１％であり、さらに好ましくは０．３５％であり、さらに好ましくは０．３７％であり、さらに好ましくは０．３８％である。
　Ｃ含有量の好ましい上限は０．５５％であり、さらに好ましくは０．５０％であり、さらに好ましくは０．４５％である。
　Ｓｉ：０．０１～０．９０％
　シリコン（Ｓｉ）は、製鋼工程において鋼を脱酸する。Ｓｉはさらに、鋼材を素材として製造された機械構造用部品の硬さを高め、機械構造用部品の疲労強度を高める。Ｓｉ含有量が０．０１％未満であれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が十分に得られない。
　一方、ＳｉはＣとの親和力が弱い。そのため、Ｓｉ含有量が０．９０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、加熱時において、Ｃは、Ｓｉが固溶している粒内よりも、粒界に偏析しやすくなる。その結果、鋼材を素材とした機械構造用部品の製造工程において鋼材に対して高周波焼入れを実施したとき、鋼材に溶融割れが発生しやすくなる。
　したがって、Ｓｉ含有量は０．０１～０．９０％である。
　Ｓｉ含有量の好ましい下限は０．０２％であり、さらに好ましくは０．０５％であり、さらに好ましくは０．０８％であり、さらに好ましくは０．１０％である。
　Ｓｉ含有量の好ましい上限は０．７０％であり、さらに好ましくは０．６５％であり、さらに好ましくは０．５５％であり、さらに好ましくは０．５０％である。
　Ｍｎ：０．５０～１．７０％
　マンガン（Ｍｎ）は、製鋼工程において鋼を脱酸する。Ｍｎはさらに、鋼材の焼入れ性を高める。そのため、鋼材を素材として製造された機械構造用部品の硬さが高まり、機械構造用部品の疲労強度が高まる。さらに、ＭｎはＣとの親和力が強い。そのため、加熱時において、ＣはＭｎが固溶している粒内に留まる。そのため、Ｃの粒界への偏析が抑制される。その結果、鋼材を素材とした機械構造用部品の製造工程において鋼材に対して高周波焼入れを実施したとき、溶融割れの発生が抑制される。さらに、Ｍｎは、Ｓと結合してＭｎ硫化物を形成する。そのため、Ｍｎは、粗大なＦｅＳの形成を抑制することができる。その結果、熱間加工時の鋼材の熱間加工性が向上し、耐熱間加工割れ性が高まる。Ｍｎ含有量が０．５０％未満であれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が十分に得られない。
　一方、Ｍｎは鋼材の融点を低下させる。そのため、Ｍｎ含有量が１．７０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材を素材とした機械構造用部品の製造工程において鋼材に対して高周波焼入れを実施したとき、耐溶融割れ性が低下する。さらに、Ｍｎ含有量が１．７０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の硬さが過剰に高まる。この場合、鋼材の被削性が十分に得られない。
　したがって、Ｍｎ含有量は０．５０～１．７０％である。
　Ｍｎ含有量の好ましい下限は０．７０％であり、さらに好ましくは０．８０％であり、さらに好ましくは０．８５％であり、さらに好ましくは０．９０％である。
　Ｍｎ含有量の好ましい上限は１．６５％であり、さらに好ましくは１．６０％であり、さらに好ましくは１．５５％であり、さらに好ましくは１．５０％であり、さらに好ましくは１．４８％であり、さらに好ましくは１．４５％であり、さらに好ましくは１．４３％であり、さらに好ましくは１．４０％である。
　Ｐ：０．０３０％以下
　りん（Ｐ）は不純物である。Ｐは粒界に偏析して鋼材の融点を低下させる。そのため、鋼材を素材とした機械構造用部品の製造工程において鋼材に対して高周波焼入れを実施したとき、鋼材に溶融割れが発生しやすくなる。
　したがって、Ｐ含有量は０．０３０％以下である。
　Ｐ含有量はなるべく低い方が好ましい。しかしながら、Ｐ含有量の過度な低減は、製造コストが高くなる。したがって、通常の工業生産を考慮すれば、Ｐ含有量の好ましい下限は０％超であり、さらに好ましくは０．００１％であり、さらに好ましくは０．００２％である。
　Ｐ含有量の好ましい上限は０．０２８％であり、さらに好ましくは０．０２６％であり、さらに好ましくは０．０２３％であり、さらに好ましくは０．０２０％である。
　Ｓ：０．２００％以下
　硫黄（Ｓ）は硫化物を生成し、鋼材の被削性を高める。Ｓが少しでも含有されれば、他の元素含有量が本実施形態の範囲内であっても、上記効果がある程度得られる。
　しかしながら、Ｓは鋼材の融点を低下させる。そのため、Ｓ含有量が０．２００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材を素材とした機械構造用部品の製造工程において鋼材に対して高周波焼入れを実施したとき、鋼材に溶融割れが発生しやすくなる。
　したがって、Ｓ含有量は０．２００％以下である。
　Ｓ含有量の好ましい下限は０％超であり、さらに好ましくは０．００１％であり、さらに好ましくは０．００５％であり、さらに好ましくは０．０１０％であり、さらに好ましくは０．０１５％であり、さらに好ましくは０．０２０％である。
　Ｓ含有量の好ましい上限は０．１５０％であり、さらに好ましくは０．１２０％であり、さらに好ましくは０．０９５％であり、さらに好ましくは０．０８０％であり、さらに好ましくは０．０７５％であり、さらに好ましくは０．０５５％であり、さらに好ましくは０．０３５％である。
　Ｂｉ：０．００５１～０．２５００％
　ビスマス（Ｂｉ）は、鋼材中に粒子を形成し、ピン止め効果により、高周波焼入れの加熱時において、鋼材中の結晶粒（オーステナイト粒）の粗大化を抑制する。結晶粒を微細に維持できれば、粒界面積の低減を抑制できる。そのため、単位粒界面積当たりのＣ濃度が低減し、高周波焼入れ時の溶融割れが抑制される。Ｂｉはさらに、鋼材の被削性を高める。Ｂｉ含有量が０．００５１％未満であれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が十分に得られない。
　一方、Ｂｉ含有量が０．２５００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の表層領域に粗大なＢｉ粒子が過剰に生成する。表層領域の粗大なＢｉ粒子は、鋼材の製造工程中の熱間加工時、又は、機械構造用部品の製造工程中の熱間加工時において、割れの起点となりやすい。そのため、鋼材の耐熱間加工割れ性が低下する。
　したがって、Ｂｉ含有量は０．００５１～０．２５００％である。
　Ｂｉ含有量の好ましい下限は０．００６０％であり、さらに好ましくは０．００７０％であり、さらに好ましくは０．０１００％であり、さらに好ましくは０．０１５０％であり、さらに好ましくは０．０２００％である。
　Ｂｉ含有量の好ましい上限は０．２０００％であり、さらに好ましくは０．１５００％であり、さらに好ましくは０．１２５０％であり、さらに好ましくは０．１０００％であり、さらに好ましくは０．０９００％であり、さらに好ましくは０．０７５０％であり、さらに好ましくは０．０６００％である。
　Ａｌ：０．００１～０．１００％
　アルミニウム（Ａｌ）は鋼を脱酸する。Ａｌ含有量が０．００１％未満であれば、他の元素含有量が本実施形態の範囲内であっても、上記効果が十分に得られない。
　一方、Ａｌ含有量が０．１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、Ａｌは粗大な酸化物を形成する。粗大な酸化物は、鋼材を素材として製造された機械構造用部品の疲労強度を低下する。
　したがって、Ａｌ含有量は０．００１～０．１００％である。
　Ａｌ含有量の好ましい下限は０．００２％であり、さらに好ましくは０．００３％であり、さらに好ましくは０．００５％であり、さらに好ましくは０．０１０％である。
　Ａｌ含有量の好ましい上限は０．０６０％であり、さらに好ましくは０．０５０％であり、さらに好ましくは０．０４０％であり、さらに好ましくは０．０３０％であり、さらに好ましくは０．０２５％である。
　Ｎ：０．０２５０％以下
　窒素（Ｎ）は鋼材を素材とした機械構造用部品の製造工程中において、窒化物及び／又は炭窒化物を形成して鋼材を析出強化する。その結果、鋼材を素材として製造された機械構造用部品の疲労強度が高まる。Ｎが少しでも含有されれば、他の元素含有量が本実施形態の範囲内であっても、上記効果がある程度得られる。
　一方、Ｎ含有量が０．０２５０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の熱間加工性が低下する。
　したがって、Ｎ含有量は０．０２５０％以下である。
　Ｎ含有量の好ましい下限は０％超であり、さらに好ましくは０．０００１％であり、さらに好ましくは０．０００５％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００２０％であり、さらに好ましくは０．００３０％であり、さらに好ましくは０．００４０％である。
　Ｎ含有量の好ましい上限は０．０２００％であり、さらに好ましくは０．０１９０％であり、さらに好ましくは０．０１７０％であり、さらに好ましくは０．０１５０％であり、さらに好ましくは０．０１３０％であり、さらに好ましくは０．０１００％である。
　Ｏ：０．００５０％以下
　酸素（Ｏ）は不純物である。Ｏは鋼中で酸化物を形成し、鋼材を素材として製造された機械構造用部品の疲労強度を低下する。
　したがって、Ｏ含有量は０．００５０％以下である。
　Ｏ含有量はなるべく低い方が好ましい。しかしながら、Ｏ含有量の過度な低減は、製造コストが高くなる。したがって、通常の工業生産を考慮すれば、Ｏ含有量の好ましい下限は０％超であり、さらに好ましくは０．０００１％であり、さらに好ましくは０．０００２％である。
　Ｏ含有量の好ましい上限は０．００３０％であり、さらに好ましくは０．００２５％であり、さらに好ましくは０．００２０％であり、さらに好ましくは０．００１５％であり、さらに好ましくは０．００１２％である。
　本実施の形態による鋼材の化学組成の残部は、Ｆｅ及び不純物からなる。ここで、不純物とは、鋼材を工業的に製造する際に、原料としての鉱石、スクラップ、又は、製造環境などから混入されるものであって、意図的に含有されるものではなく、本実施形態による鋼材に悪影響を与えない範囲で許容されるものを意味する。
　［任意元素（Ｏｐｔｉｏｎａｌ　Ｅｌｅｍｅｎｔｓ）］
　本実施形態の鋼材の化学組成はさらに、Ｆｅの一部に代えて、
　Ｃｒ：０～１．３０％、
　Ｖ：０～０．２００％、
　Ｓｎ：０～０．１０００％、
　Ｓｂ：０～０．０５００％、
　Ａｓ：０～０．０５００％、
　Ｐｂ：０～０．０９％、
　Ｍｇ：０～０．０１００％、
　Ｔｉ：０～０．０４００％、
　Ｎｂ：０～０．０５００％、
　Ｗ：０～０．４０００％、
　Ｚｒ：０～０．２０００％、
　Ｃａ：０～０．０１００％、
　Ｔｅ：０～０．０１００％、
　Ｂ：０～０．００５０％、
　希土類元素：０～０．０１００％、
　Ｃｏ：０～０．０１００％、
　Ｓｅ：０～０．０１００％、
　Ｉｎ：０～０．０１００％、
　Ｍｏ：０～０．３０％、
　Ｃｕ：０～０．５０％、
　Ｎｉ：０～０．５０％、
　からなる群から選択される１種以上を含有してもよい。
　以下、これらの任意元素について説明する。
　［第１群：Ｃｒ及びＶについて］
　本実施形態の鋼材の化学組成はさらに、Ｆｅの一部に代えて、以下の第１群を含有してもよい。これらの元素は任意元素であり、いずれも、機械構造用部品の疲労強度を高める。
　［第１群］
　Ｃｒ：０～１．３０％、及び、
　Ｖ：０～０．２００％、からなる群から選択される１種以上
　Ｃｒ：０～１．３０％
　クロム（Ｃｒ）は、任意元素であり、含有されなくてもよい。つまり、Ｃｒ含有量は０％であってもよい。
　含有される場合、つまり、Ｃｒ含有量が０％超である場合、Ｃｒは、鋼材の焼入れ性を高める。そのため、鋼材を素材として製造された機械構造用部品の硬さが高まり、機械構造用部品の疲労強度が高まる。Ｃｒが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｃｒ含有量が１．３０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材において、十分な被削性が得られない。
　したがって、Ｃｒ含有量は０～１．３０％であり、含有される場合、Ｃｒ含有量は１．３０％以下である。
　Ｃｒ含有量の好ましい下限は０．０１％であり、さらに好ましくは０．０５％であり、さらに好ましくは０．１０％であり、さらに好ましくは０．１２％であり、さらに好ましくは０．１４％であり、さらに好ましくは０．１６％であり、さらに好ましくは０．１８％である。
　Ｃｒ含有量の好ましい上限は１．２５％であり、さらに好ましくは１．２０％であり、さらに好ましくは１．１０％であり、さらに好ましくは１．００％であり、さらに好ましくは０．９０％である。
　Ｖ：０～０．２００％
　バナジウム（Ｖ）は、任意元素であり、含有されなくてもよい。つまり、Ｖ含有量は０％であってもよい。
　含有される場合、つまり、Ｖ含有量が０％超である場合、Ｖは、鋼材を素材とした機械構造用部品の製造工程中で、Ｖ析出物として鋼材中のフェライト中に析出する。これにより、鋼材中のフェライトの硬さが高まる。その結果、機械構造用部品の疲労強度が高まる。Ｖが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｖ含有量が０．２００％を超えれば、上記効果が飽和し、さらに、製造コストが高くなる。
　したがって、Ｖ含有量は、０～０．２００％であり、含有される場合、Ｖ含有量は０．２００％以下である。
　Ｖ含有量の好ましい下限は０．００１％であり、さらに好ましくは０．００３％であり、さらに好ましくは０．００５％であり、さらに好ましくは０．００７％であり、さらに好ましくは０．０１０％であり、さらに好ましくは０．０１５％であり、さらに好ましくは０．０２０％である。
　Ｖ含有量の好ましい上限は０．１８０％であり、さらに好ましくは０．１６０％であり、さらに好ましくは０．１４０％であり、さらに好ましくは０．１２０％であり、さらに好ましくは０．１００％であり、さらに好ましくは０．０８０％であり、さらに好ましくは０．０５０％であり、さらに好ましくは０．０４９％である。
　［第２群：Ｓｎ、Ｓｂ、Ａｓ及びＰｂについて］
　本実施形態の鋼材の化学組成はさらに、Ｆｅの一部に代えて、以下の第２群を含有してもよい。これらの元素はいずれも任意元素であり、いずれも、鋼材の被削性を高める。
　［第２群］
　Ｓｎ：０～０．１０００％、
　Ｓｂ：０～０．０５００％、
　Ａｓ：０～０．０５００％、及び、
　Ｐｂ：０～０．０９％、からなる群から選択される１種以上
　Ｓｎ：０～０．１０００％
　スズ（Ｓｎ）は、任意元素であり、含有されなくてもよい。つまり、Ｓｎ含有量は０％であってもよい。
　含有される場合、つまり、Ｓｎ含有量が０％超である場合、Ｓｎは、母相と介在物との界面に偏析し、鋼材を脆化する。そのため、鋼材の被削性が高まる。Ｓｎが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｓｎ含有量が０．１０００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、Ｓｎが過剰に偏析する。この場合、鋼材の熱間加工性が低下する。
　したがって、Ｓｎ含有量は０～０．１０００％であり、含有される場合、Ｓｎ含有量は０．１０００％以下である。
　Ｓｎ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００２０％である。
　Ｓｎ含有量の好ましい上限は０．０５００％であり、さらに好ましくは０．０１００％であり、さらに好ましくは０．００９０％であり、さらに好ましくは０．００８０％であり、さらに好ましくは０．００７０％であり、さらに好ましくは０．００６０％であり、さらに好ましくは０．００５０％であり、さらに好ましくは０．００４０％である。
　Ｓｂ：０～０．０５００％
　アンチモン（Ｓｂ）は、任意元素であり、含有されなくてもよい。つまり、Ｓｂ含有量は０％であってもよい。
　含有される場合、つまり、Ｓｂ含有量が０％超である場合、Ｓｂは、母相と介在物との界面に偏析し、鋼材を脆化する。そのため、鋼材の被削性が高まる。Ｓｂが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｓｂ含有量が０．０５００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、Ｓｂが過剰に偏析する。この場合、鋼材の熱間加工性が低下する。
　したがって、Ｓｂ含有量は０～０．０５００％であり、含有される場合、Ｓｂ含有量は０．０５００％以下である。
　Ｓｂ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００２０％である。
　Ｓｂ含有量の好ましい上限は０．０４００％であり、さらに好ましくは０．０３００％であり、さらに好ましくは０．０２００％であり、さらに好ましくは０．０１００％であり、さらに好ましくは０．００８０％であり、さらに好ましくは０．００６０％である。
　Ａｓ：０～０．０５００％
　ヒ素（Ａｓ）は、任意元素であり、含有されなくてもよい。つまり、Ａｓ含有量は０％であってもよい。
　含有される場合、つまり、Ａｓ含有量が０％超である場合、Ａｓは、母相と介在物との界面に偏析し、鋼材を脆化する。そのため、鋼材の被削性が高まる。Ａｓが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ａｓ含有量が０．０５００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、Ａｓが過剰に偏析する。この場合、鋼材の熱間加工性が低下する。
　したがって、Ａｓ含有量は０～０．０５００％であり、含有される場合、Ａｓ含有量は０．０５００％以下である。
　Ａｓ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００２０％である。
　Ａｓ含有量の好ましい上限は０．０１００％であり、さらに好ましくは０．００７０％であり、さらに好ましくは０．００６０％であり、さらに好ましくは０．００５０％であり、さらに好ましくは０．００４０％である。
　Ｐｂ：０～０．０９％
　鉛（Ｐｂ）は、任意元素であり、含有されなくてもよい。つまり、Ｐｂ含有量は０％であってもよい。
　含有される場合、つまり、Ｐｂ含有量が０％超である場合、Ｐｂは、母相中にＰｂ粒子を生成し、鋼材を脆化する。そのため、鋼材の被削性が高まる。Ｐｂが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｐｂ含有量が０．０９％を超えれば、他の元素含有量が本実施形態の範囲内であっても、Ｐｂ粒子が過剰に生成する。この場合、鋼材の熱間加工性が低下する。
　したがって、Ｐｂ含有量は０～０．０９％であり、含有される場合、Ｐｂ含有量は０．０９％以下である。
　Ｐｂ含有量の好ましい下限は０．０１％であり、さらに好ましくは０．０２％であり、さらに好ましくは０．０３％である。
　Ｐｂ含有量の好ましい上限は０．０８％であり、さらに好ましくは０．０７％であり、さらに好ましくは０．０６％であり、さらに好ましくは０．０５％である。
　［第３群：Ｍｇについて］
　本実施形態の鋼材の化学組成はさらに、Ｆｅの一部に代えて、以下の第３群を含有してもよい。
　［第３群］
　Ｍｇ：０～０．０１００％
　マグネシウム（Ｍｇ）は任意元素であり、含有されなくてもよい。つまり、Ｍｇ含有量は０％であってもよい。
　含有される場合、つまり、Ｍｇ含有量が０％超である場合、Ｍｇは鋼を脱酸する。Ｍｇが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｍｇ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、Ｍｇは粗大な酸化物を形成する。粗大な酸化物は、鋼材を素材として製造された機械構造用部品の疲労強度を低下する。
　したがって、Ｍｇ含有量は０～０．０１００％であり、含有される場合、０．０１００％以下である。
　Ｍｇ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００３％であり、さらに好ましくは０．０００５％である。
　Ｍｇ含有量の好ましい上限は０．００５０％であり、さらに好ましくは０．００４５％であり、さらに好ましくは０．００４０％である。
　［第４群：Ｔｉ、Ｎｂ、Ｗ及びＺｒ］
　本実施形態の鋼材の化学組成はさらに、Ｆｅの一部に代えて、以下の第４群を含有してもよい。これらの元素は任意元素であり、いずれも、析出物を形成して、ピン止め効果により鋼材中の結晶粒を微細化して、鋼材を素材として製造された機械構造用部品の靱性を高める。
　［第４群］
　Ｔｉ：０～０．０４００％、
　Ｎｂ：０～０．０５００％、
　Ｗ：０～０．４０００％、及び、
　Ｚｒ：０～０．２０００％、からなる群から選択される１種以上
　Ｔｉ：０～０．０４００％
　チタン（Ｔｉ）は任意元素であり、含有されなくてもよい。つまり、Ｔｉ含有量は０％であってもよい。
　含有される場合、つまり、Ｔｉ含有量が０％超である場合、Ｔｉは、析出物（炭化物及び／又は炭窒化物）を形成する。これらの析出物は、ピン止め効果により、鋼材の結晶粒を微細化する。これにより、機械構造用部品の靱性が高まる。Ｔｉが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｔｉ含有量が０．０４００％を超えれば、上記効果が飽和して、製造コストが高くなる。
　したがって、Ｔｉ含有量は０～０．０４００％であり、含有される場合、０．０４００％以下である。
　Ｔｉ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００５０％であり、さらに好ましくは０．００８０％である。
　Ｔｉ含有量の好ましい上限は０．０３００％であり、さらに好ましくは０．０２００％であり、さらに好ましくは０．０１７５％であり、さらに好ましくは０．０１５０％である。
　Ｎｂ：０～０．０５００％
　ニオブ（Ｎｂ）は任意元素であり、含有されなくてもよい。つまり、Ｎｂ含有量は０％であってもよい。
　含有される場合、つまり、Ｎｂ含有量が０％超である場合、Ｎｂは、Ｔｉと同様に析出物を形成して鋼材の結晶粒を微細化し、機械構造用部品の靱性を高める。Ｎｂが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｎｂ含有量が０．０５００％を超えれば、上記効果が飽和して、製造コストが高くなる。
　したがって、Ｎｂ含有量は０～０．０５００％であり、含有される場合、０．０５００％以下である。
　Ｎｂ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００５０％であり、さらに好ましくは０．００８０％である。
　Ｎｂ含有量の好ましい上限は０．０２００％であり、さらに好ましくは０．０１７５％であり、さらに好ましくは０．０１５０％である。
　Ｗ：０～０．４０００％
　タングステン（Ｗ）は任意元素であり、含有されなくてもよい。つまり、Ｗ含有量は０％であってもよい。
　含有される場合、つまり、Ｗ含有量が０％超である場合、Ｗは、Ｔｉと同様に析出物を形成して鋼材の結晶粒を微細化し、機械構造用部品の靱性を高める。Ｗが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｗ含有量が０．４０００％を超えれば、上記効果が飽和して、製造コストが高くなる。
　したがって、Ｗ含有量は０～０．４０００％であり、含有される場合、０．４０００％以下である。
　Ｗ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．００５０％であり、さらに好ましくは０．０５００％である。
　Ｗ含有量の好ましい上限は０．３５００％であり、さらに好ましくは０．３０００％であり、さらに好ましくは０．２０００％である。
　Ｚｒ：０～０．２０００％
　ジルコニウム（Ｚｒ）は任意元素であり、含有されなくてもよい。つまり、Ｚｒ含有量は０％であってもよい。
　含有される場合、つまり、Ｚｒ含有量が０％超である場合、Ｚｒは、Ｔｉと同様に、析出物を形成して鋼材の結晶粒を微細化し、機械構造用部品の靱性を高める。Ｚｒが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｚｒ含有量が０．２０００％を超えれば、上記効果が飽和して、製造コストが高くなる。
　したがって、Ｚｒ含有量は０～０．２０００％であり、含有される場合、０．２０００％以下である。
　Ｚｒ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００２０％であり、さらに好ましくは０．００５０％である。
　Ｚｒ含有量の好ましい上限は０．１５００％であり、さらに好ましくは０．１０００％であり、さらに好ましくは０．０５００％であり、さらに好ましくは０．０１００％である。
　［第５群：Ｃａ、Ｔｅ、Ｂ、及び、希土類元素（ＲＥＭ）］
　本実施形態の鋼材の化学組成はさらに、Ｆｅの一部に代えて、以下の第５群を含有してもよい。これらの元素は任意元素であり、いずれも、鋼材の被削性を高める。
　［第５群］
　Ｃａ：０～０．０１００％、
　Ｔｅ：０～０．０１００％、
　Ｂ：０～０．００５０％、及び、
　希土類元素：０～０．０１００％、からなる群から選択される１種以上
　Ｃａ：０～０．０１００％
　カルシウム（Ｃａ）は、任意元素であり、含有されなくてもよい。つまり、Ｃａ含有量は０％であってもよい。
　含有される場合、つまり、Ｃａ含有量が０％超である場合、Ｃａは鋼材の被削性を高める。Ｃａが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｃａ含有量が０．０１００％を超えれば、他の元素含有量が本実施の範囲内であっても、粗大酸化物を形成する。粗大酸化物は、鋼材を素材として製造された機械構造用部品の疲労強度を低下する。
　したがって、Ｃａ含有量は０～０．０１００％であり、含有される場合、０．０１００％以下である。
　Ｃａ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００５％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００１５％である。
　Ｃａ含有量の好ましい上限は０．００８５％であり、さらに好ましくは０．００７０％であり、さらに好ましくは０．００５０％であり、さらに好ましくは０．００３０％である。
　Ｔｅ：０～０．０１００％
　テルル（Ｔｅ）は、任意元素であり、含有されなくてもよい。つまり、Ｔｅ含有量は０％であってもよい。
　含有される場合、つまり、Ｔｅ含有量が０％超である場合、Ｔｅは鋼材の被削性を高める。Ｔｅが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｔｅ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の熱間加工性が低下する。
　したがって、Ｔｅ含有量は０～０．０１００％であり、含有される場合、０．０１００％以下である。
　Ｔｅ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００３％であり、さらに好ましくは０．００１０％である。
　Ｔｅ含有量の好ましい上限は０．００９０％であり、さらに好ましくは０．００８５％であり、さらに好ましくは０．００８０％であり、さらに好ましくは０．００４０％である。
　Ｂ：０～０．００５０％
　ボロン（Ｂ）は、任意元素であり、含有されなくてもよい。つまり、Ｂ含有量は０％であってもよい。
　含有される場合、つまり、Ｂ含有量が０％超である場合、ＢはＮと結合してＢＮを形成し、鋼材の被削性を高める。Ｂはさらに、粒界に偏析して粒界強化に寄与し、鋼材を素材として製造された機械構造用部品の疲労強度を高める。Ｂが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｂ含有量が０．００５０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の熱間加工性が低下する。
　したがって、Ｂ含有量は０～０．００５０％であり、含有される場合、０．００５０％以下である。
　Ｂ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００５％であり、さらに好ましくは０．００１０％である。
　Ｂ含有量の好ましい上限は０．００４０％であり、さらに好ましくは０．００３５％であり、さらに好ましくは０．００３０％である。
　希土類元素（ＲＥＭ）：０～０．０１００％
　希土類元素（ＲＥＭ）は、任意元素であり、含有されなくてもよい。つまり、ＲＥＭ含有量は０％であってもよい。
　ＲＥＭが含有される場合、つまり、ＲＥＭ含有量が０％超である場合、ＲＥＭは、鋼材の被削性を高める。ＲＥＭが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、ＲＥＭ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の熱間加工性が低下する。
　したがって、ＲＥＭ含有量は０～０．０１００％であり、含有される場合、０．０１００％以下である。
　ＲＥＭ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００５％であり、さらに好ましくは０．００１０％である。
　ＲＥＭ含有量の好ましい上限は０．００９０％であり、さらに好ましくは０．００８０％であり、さらに好ましくは０．００７０％であり、さらに好ましくは０．００４０％である。
　本明細書におけるＲＥＭとは、原子番号２１番のスカンジウム（Ｓｃ）、原子番号３９番のイットリウム（Ｙ）、及び、ランタノイドである原子番号５７番のランタン（Ｌａ）～原子番号７１番のルテチウム（Ｌｕ）からなる群から選択される１種以上の元素である。本明細書におけるＲＥＭ含有量とは、これらの元素の合計含有量である。
　［第６群：Ｃｏ、Ｓｅ、及び、Ｉｎ］
　本実施形態の鋼材の化学組成はさらに、Ｆｅの一部に代えて、以下の第６群を含有してもよい。これらの元素は任意元素であり、いずれも鋼材の脱炭を抑制する。
　［第６群］
　Ｃｏ：０～０．０１００％、
　Ｓｅ：０～０．０１００％、及び、
　Ｉｎ：０～０．０１００％、からなる群から選択される１種以上
　Ｃｏ：０～０．０１００％
　コバルト（Ｃｏ）は、任意元素であり、含有されなくてもよい。つまり、Ｃｏ含有量は０％であってもよい。
　含有される場合、つまり、Ｃｏが０％超である場合、Ｃｏは、製造工程時に鋼材の脱炭を抑制する。Ｃｏが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｃｏ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の熱間加工性が低下する。
　したがって、Ｃｏ含有量は０～０．０１００％であり、含有される場合、０．０１００％以下である。
　Ｃｏ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００５％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００３０％である。
　Ｃｏ含有量の好ましい上限は０．００９０％であり、さらに好ましくは０．００８０％であり、さらに好ましくは０．００７０％である。
　Ｓｅ：０～０．０１００％
　セレン（Ｓｅ）は、任意元素であり、含有されなくてもよい。つまり、Ｓｅ含有量は０％であってもよい。
　含有される場合、つまり、Ｓｅが０％超である場合、Ｓｅは、製造工程時に鋼材の脱炭を抑制する。Ｓｅが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｓｅ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、熱間加工割れを発生させる。
　したがって、Ｓｅ含有量は０～０．０１００％であり、含有される場合、０．０１００％以下である。
　Ｓｅ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．００１０％であり、さらに好ましくは０．００２０％である。
　Ｓｅ含有量の好ましい上限は０．００９０％であり、さらに好ましくは０．００８０％であり、さらに好ましくは０．００７０％である。
　Ｉｎ：０～０．０１００％
　インジウム（Ｉｎ）は、任意元素であり、含有されなくてもよい。つまり、Ｉｎ含有量は０％であってもよい。
　含有される場合、つまり、Ｉｎが０％超である場合、Ｉｎは、製造工程時に鋼材の脱炭を抑制する。Ｉｎが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｉｎ含有量が０．０１００％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の熱間加工性を低下する。
　したがって、Ｉｎ含有量は０～０．０１００％であり、含有される場合、０．０１００％以下である。
　Ｉｎ含有量の好ましい下限は０．０００１％であり、さらに好ましくは０．０００５％であり、さらに好ましくは０．００１０％である。
　Ｉｎ含有量の好ましい上限は０．００９０％であり、さらに好ましくは０．００８０％であり、さらに好ましくは０．００７０％である。
　［第７群：Ｍｏ、Ｃｕ、及び、Ｎｉ］
　本実施形態の鋼材の化学組成はさらに、Ｆｅの一部に代えて、以下の第７群を含有してもよい。これらの元素は任意元素であり、いずれも鋼材を素材として製造された機械構造用部品の疲労強度を高める。
　［第７群］
　Ｍｏ：０～０．３０％、
　Ｃｕ：０～０．５０％、及び、
　Ｎｉ：０～０．５０％、からなる群から選択される１種以上
　Ｍｏ：０～０．３０％
　モリブデン（Ｍｏ）は任意元素であり、含有されなくてもよい。つまり、Ｍｏ含有量は０％であってもよい。
　含有される場合、つまり、Ｍｏ含有量が０％超である場合、Ｍｏは、鋼材を素材として製造された機械構造用部品の疲労強度を高める。Ｍｏが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｍｏ含有量が０．３０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、鋼材の硬さが過剰に高くなり、鋼材の熱間加工性が低下する。
　したがって、Ｍｏ含有量は０～０．３０％であり、含有される場合、０．３０％以下である。
　Ｍｏ含有量の好ましい下限は０．０１％であり、さらに好ましくは０．０５％であり、さらに好ましくは０．１０％である。
　Ｍｏ含有量の好ましい上限は０．２０％であり、さらに好ましくは０．１７％であり、さらに好ましくは０．１５％である。
　Ｃｕ：０～０．５０％
　銅（Ｃｕ）は任意元素であり、含有されなくてもよい。つまり、Ｃｕ含有量は０％であってもよい。
　含有される場合、つまり、Ｃｕ含有量が０％超である場合、Ｃｕは、鋼材を素材として製造された機械構造用部品の疲労強度を高める。Ｃｕが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｃｕ含有量が０．５０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、高周波焼入れ時に溶融割れが発生しやすくなる。
　したがって、Ｃｕ含有量は０～０．５０％であり、含有される場合、０．５０％以下である。
　Ｃｕ含有量の好ましい下限は０．０１％であり、さらに好ましくは０．０２％である。
　Ｃｕ含有量の好ましい上限は０．２０％であり、さらに好ましくは０．１０％であり、さらに好ましくは０．０５％である。
　Ｎｉ：０～０．５０％
　ニッケル（Ｎｉ）は任意元素であり、含有されなくてもよい。つまり、Ｎｉ含有量は０％であってもよい。
　含有される場合、つまり、Ｎｉ含有量が０％超である場合、Ｎｉは、鋼材を素材として製造された機械構造用部品の疲労強度を高める。Ｎｉが少しでも含有されれば、上記効果がある程度得られる。
　しかしながら、Ｎｉ含有量が０．５０％を超えれば、他の元素含有量が本実施形態の範囲内であっても、高周波焼入れ時に溶融割れが発生しやすくなる。
　したがって、Ｎｉ含有量は０～０．５０％であり、含有される場合、０．５０％以下である。
　Ｎｉ含有量の好ましい下限は０．０１％であり、さらに好ましくは０．０２％である。
　Ｎｉ含有量の好ましい上限は０．２０％であり、さらに好ましくは０．１０％であり、さらに好ましくは０．０５％である。
　［（特徴２）Ｆｎについて］
　本実施形態の鋼材ではさらに、式（１）で定義されるＦｎが０．４５～１．０５である。
　Ｆｎ＝Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ　（１）
　ここで、式（１）中の各元素記号には、対応する元素の質量％での含有量が代入される。元素が含有されていない場合、対応する元素記号には「０」が代入される。
　Ｆｎは鋼材を素材として製造された機械構造用部品の疲労強度と、鋼材の被削性との指標である。Ｆｎが０．４５未満であれば、鋼材が特徴１、特徴３及び特徴４を満たしていても、鋼材を素材として製造された機械構造用部品において、十分な疲労強度が得られない。一方、Ｆｎが１．０５を超えれば、鋼材が特徴１、特徴３及び特徴４を満たしていても、鋼材の被削性が低下する。
　したがって、Ｆｎは０．４５～１．０５である。
　Ｆｎの好ましい下限は０．５０であり、さらに好ましくは０．５５であり、さらに好ましくは０．６０である。
　Ｆｎの好ましい上限は１．００であり、さらに好ましくは０．９５であり、さらに好ましくは０．９０である。
　［（特徴３）０．０８Ｒ深さ位置Ｄ０．０８ＲでのＢｉ粒子の個数密度］
　図２は、本実施形態の鋼材の軸方向に垂直な断面図である。図２に示すとおり、鋼材の軸方向に垂直な断面１０は、円形状である。断面１０の半径をＲと定義する。鋼材の表面Ｄ０．００Ｒを起点とした０．０８Ｒ深さの位置を「０．０８Ｒ深さ位置Ｄ０．０８Ｒ」と定義する。
　本実施形態の鋼材では、０．０８Ｒ深さ位置Ｄ０．０８Ｒにおいて、円相当径が０．１～１．０μｍのＢｉ粒子である微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２以上であり、円相当径が１０．０μｍ以上のＢｉ粒子である粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２以下である。
　図２に示すとおり、鋼材の表面Ｄ０．００Ｒから０．０８Ｒ深さ位置Ｄ０．０８Ｒまでの範囲の領域を、表層領域ＳＡと定義する。鋼材の表層領域ＳＡは、鋼材の製造工程中の熱間加工工程、又は、鋼材を素材とした機械構造用部品の製造工程中の熱間加工工程において、金型又はロールといった加工工具と接触する鋼材表面近傍の領域である。そのため、表層領域ＳＡでは、十分な耐熱間加工割れ性が求められる。表層領域ＳＡはさらに、鋼材を素材とした機械構造用部品の製造工程で高周波焼入れを実施するとき、高周波誘導加熱により温度が高くなる領域である。そのため、表層領域ＳＡでは、十分な耐溶融割れ性が求められる。したがって、鋼材の表層領域ＳＡでは、十分な耐熱間加工割れ性及び十分な耐溶融割れ性が求められる。
　上述のとおり、高周波焼入れでの加熱時において、円相当径が０．１～１．０μｍのＢｉ粒子である微細Ｂｉ粒子は、ピン止め効果により、表層領域ＳＡでの結晶粒の粗大化を抑制する。表層領域ＳＡでの微細Ｂｉ粒子の個数密度を高くすれば、ピン止め効果により結晶粒を微細な状態で維持できる。そのため、粒界面積の低減が抑制され、溶融割れの発生が抑制される。表層領域ＳＡ内の０．０８Ｒ深さ位置Ｄ０．０８Ｒにおいて、微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２以上であれば、高周波焼入れでの加熱時において、結晶粒を微細に維持することができる。その結果、鋼材において、十分な耐溶融割れ性が得られる。
　また、表層領域ＳＡでは、熱間加工時に熱間加工工具からの外力を大きく受ける。熱間加工時において、鋼材のうち受ける外力が大きい表層領域ＳＡでは、円相当径が１０．０μｍ以上のＢｉ粒子である粗大Ｂｉ粒子は、熱間加工割れの起点となる。したがって、鋼材の表層領域ＳＡでは、粗大Ｂｉ粒子の個数密度はなるべく低い方が好ましい。表層領域ＳＡ内の０．０８Ｒ深さ位置Ｄ０．０８Ｒにおいて、粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２以下であれば、表層領域ＳＡにおいて、粗大Ｂｉ粒子の個数密度が十分に低い。そのため、鋼材において、十分な耐熱間加工割れ性が得られる。
　したがって、０．０８Ｒ深さ位置Ｄ０．０８Ｒでの微細Ｂｉ粒子の個数密度は１５．００個／ｍｍ２以上であり、粗大Ｂｉ粒子の個数密度は０．２５個／ｍｍ２以下である。
　０．０８Ｒ深さ位置Ｄ０．０８Ｒでの微細Ｂｉ粒子の個数密度の好ましい下限は２０．００個／ｍｍ２であり、さらに好ましくは２５．００個／ｍｍ２であり、さらに好ましくは３０．００個／ｍｍ２である。
　０．０８Ｒ深さ位置Ｄ０．０８Ｒでの微細Ｂｉ粒子の個数密度の上限は特に限定されない。鋼材が特徴１及び特徴２を満たす場合、０．０８Ｒ深さ位置Ｄ０．０８Ｒでの微細Ｂｉ粒子の個数密度の上限は例えば１０００．００個／ｍｍ２である。
　０．０８Ｒ深さ位置Ｄ０．０８Ｒでの粗大Ｂｉ粒子の個数密度の好ましい上限は０．２０個／ｍｍ２であり、さらに好ましくは０．１６個／ｍｍ２であり、さらに好ましくは０．１２個／ｍｍ２であり、さらに好ましくは０．０８個／ｍｍ２である。
　０．０８Ｒ深さ位置Ｄ０．０８Ｒでの粗大Ｂｉ粒子の個数密度は低い方が好ましい。０．０８Ｒ深さ位置Ｄ０．０８Ｒでの粗大Ｂｉ粒子の個数密度の好ましい下限は０．０３個／ｍｍ２であり、さらに好ましくは０．００個／ｍｍ２である。
　なお、表層領域ＳＡ中には、上述の微細Ｂｉ粒子及び粗大Ｂｉ粒子だけではなく、円相当径が１．０超～１０．０μｍ未満のＢｉ粒子も存在する。しかしながら、表層領域ＳＡにおいて、微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度の方が、円相当径が１．０超～１０．０μｍ未満のＢｉ粒子の個数密度よりも、熱間加工割れ及び高周波焼入れ時の溶融割れと強く相関する。したがって、本実施形態では、表層領域ＳＡ内の０．０８Ｒ深さ位置Ｄ０．０８Ｒにおける微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度を、鋼材の熱間加工割れ及び高周波焼入れ時の溶融割れの指標とする。
　［（特徴４）０．６５Ｒ深さ位置Ｄ０．６５ＲでのＢｉ粒子の個数密度］
　図２を参照して、鋼材の表面Ｄ０．００Ｒを起点とした０．６５Ｒ深さの位置を「０．６５Ｒ深さ位置Ｄ０．６５Ｒ」と定義する。鋼材の表面Ｄ０．００Ｒを起点とした１．００Ｒ深さの位置を「１．００Ｒ深さ位置Ｄ１．００Ｒ」と定義する。
　本実施形態の鋼材では、０．６５Ｒ深さ位置Ｄ０．６５Ｒにおいて、円相当径が０．１～１．０μｍのＢｉ粒子である微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２未満であり、円相当径が１０．０μｍ以上のＢｉ粒子である粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２超である。
　図２に示すとおり、０．６５Ｒ深さ位置Ｄ０．６５Ｒから１．００Ｒ深さ位置Ｄ１．００Ｒまでの範囲である領域を、内部領域ＣＡと定義する。鋼材の内部領域ＣＡは、表層領域ＳＡと比較して、熱間加工時の外力や、高周波焼入れ時の熱量を受けにくい。そのため、内部領域ＣＡでは、表層領域ＳＡと比較して、耐熱間加工割れ性や耐溶融割れ性は求められない。一方、内部領域ＣＡは、鋼材を素材とした機械構造用部品の製造工程において、切削加工が施される場合がある。この場合、内部領域ＣＡでは、十分な被削性が求められる。
　切削加工時において、粗大Ｂｉ粒子は切り屑を鋼材本体から剥離する起点となる。そのため、粗大Ｂｉ粒子は鋼の被削性を高める。したがって、内部領域ＣＡでの粗大Ｂｉ粒子の個数密度は高い方が好ましい。内部領域ＣＡ内の０．６５Ｒ深さ位置Ｄ０．６５Ｒにおいて、粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２超であれば、鋼材において十分な被削性が得られる。
　一方、微細Ｂｉ粒子の鋼の被削性への影響は低い。さらに、微細Ｂｉ粒子の個数密度が高ければ、その分、粗大Ｂｉ粒子の個数密度は低くなる。したがって、内部領域ＣＡにおいて、微細Ｂｉ粒子の個数密度は低い方が好ましい。内部領域ＣＡ内の０．６５Ｒ深さ位置Ｄ０．６５Ｒにおいて、微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２未満であれば、内部領域ＣＡにおいて粗大Ｂｉ粒子が生成しやすい。その結果、鋼材において十分な被削性が得られる。
　したがって、０．６５Ｒ深さ位置Ｄ０．６５Ｒでの微細Ｂｉ粒子の個数密度は１５．００個／ｍｍ２未満であり、粗大Ｂｉ粒子の個数密度は０．２５個／ｍｍ２超である。
　０．６５Ｒ深さ位置Ｄ０．６５Ｒでの微細Ｂｉ粒子の個数密度の好ましい上限は１４．００個／ｍｍ２であり、さらに好ましくは１０．００個／ｍｍ２であり、さらに好ましくは７．５０個／ｍｍ２である。
　０．６５Ｒ深さ位置Ｄ０．６５Ｒでの微細Ｂｉ粒子の個数密度は低い方が好ましい。０．６５Ｒ深さ位置Ｄ０．６５Ｒでの微細Ｂｉ粒子の個数密度の好ましい下限は５．００個／ｍｍ２であり、さらに好ましくは３．００個／ｍｍ２であり、さらに好ましくは１．５０個／ｍｍ２であり、さらに好ましくは０．００個／ｍｍ２である。
　０．６５Ｒ深さ位置Ｄ０．６５Ｒでの粗大Ｂｉ粒子の個数密度の好ましい下限は０．２６個／ｍｍ２であり、さらに好ましくは０．３０個／ｍｍ２であり、さらに好ましくは０．４０個／ｍｍ２であり、さらに好ましくは０．５０個／ｍｍ２である。
　０．６５Ｒ深さ位置Ｄ０．６５Ｒでの粗大Ｂｉ粒子の個数密度の上限は特に限定されない。しかしながら、鋼材が特徴１及び特徴２を満たす場合、０．６５Ｒ深さ位置Ｄ０．６５Ｒでの粗大Ｂｉ粒子の個数密度の上限は例えば１０．００個／ｍｍ２であり、さらに好ましくは７．００個／ｍｍ２である。
　なお、内部領域ＣＡ中には、上述の微細Ｂｉ粒子及び粗大Ｂｉ粒子だけではなく、円相当径が１．０超～１０．０μｍ未満のＢｉ粒子も存在する。しかしながら、内部領域ＣＡにおいて、粗大Ｂｉ粒子の個数密度の方が、円相当径が１．０超～１０．０μｍ未満のＢｉ粒子の個数密度よりも、被削性と強く相関する。したがって、本実施形態では、内部領域ＣＡ内の０．６５Ｒ深さ位置Ｄ０．６５Ｒにおいて、粗大Ｂｉ粒子の個数密度を、鋼材の被削性の指標とする。
　［０．０８Ｒ深さ位置Ｄ０．０８Ｒでの微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度の測定方法について］
　０．０８Ｒ深さ位置Ｄ０．０８Ｒでの微細Ｂｉ粒子の個数密度及び粗大Ｂｉ粒子の個数密度は、次の方法で測定できる。
　鋼材の軸方向に平行であって、鋼材の中心軸を含む断面において、０．０８Ｒ深さ位置Ｄ０．０８Ｒを含む試験片を採取する。採取した試験片のうち、上記鋼材の軸方向に平行であって、鋼材の中心軸を含む断面を、観察面とする。
　観察面を鏡面研磨する。走査型電子顕微鏡（Ｓｃａｎｎｉｎｇ　Ｅｌｅｃｔｒｏｎ　Ｍｉｃｒｏｓｃｏｐｅ：ＳＥＭ）を用いて、１０００倍の倍率で、鏡面研磨後の観察面のうち、０．０８Ｒ深さ位置Ｄ０．０８Ｒを含む矩形の観察領域を選定する。観察領域の面積を２５．６ｍｍ２とする。観察領域の中心位置に０．０８Ｒ深さ位置Ｄ０．０８Ｒが配置されるように、観察領域を選定する。さらに、観察領域を２０２．５μｍ×２０２．５μｍの矩形の視野に６２４分割（２６×２４分割）する。
　ＳＥＭ観察により得られた各視野の反射電子像に基づいて、周知の画像解析の粒子解析方法を用いて、粗大Ｂｉ粒子及び微細Ｂｉ粒子の個数密度を調べる。具体的には、鋼材の母相と粒子との界面に基づいて、鋼材中の粒子を特定する。ここでいう粒子は、介在物又は析出物である。画像解析を行い、特定された粒子の円相当径を求める。具体的には、特定された各粒子の面積を求める。求めた面積と同じ面積の円での直径を、当該粒子の円相当径（μｍ）とする。
　上記ＳＥＭ観察により得られた反射電子像中で観察される粒子のうち、円相当径が０．１～１．０μｍの粒子であって、かつ、ＳＥＭに備えられたエネルギー分散型Ｘ線分析装置（ＥＤＸ：Ｅｎｅｒｇｙ　Ｄｉｓｐｅｒｓｉｖｅ　Ｘ－ｒａｙ　ｓｐｅｃｔｒｏｓｃｏｐｙ）を用いて粒子の組成を点分析した結果、Ｂｉ含有量が質量％で５０％以上である粒子を、微細Ｂｉ粒子と特定する。また、ＳＥＭ観察により得られた反射電子像で観察される粒子のうち、円相当径が１０．０μｍ以上の粒子であって、かつ、ＥＤＸを用いて粒子の組成を点分析した結果、Ｂｉ含有量が質量％で５０％以上である粒子を、粗大Ｂｉ粒子と特定する。ＥＤＸ分析の加速電圧は２０ｋＶとする。なお、Ｂｉは重元素であるため、反射電子像において高輝度で観察される。そのため、輝度に基づいてＢｉ粒子を特定してもよい。
　各視野で認定された微細Ｂｉ粒子の総個数と、上記観察領域を構成する複数の視野の総面積（２５．６ｍｍ２）とに基づいて、０．０８Ｒ深さ位置Ｄ０．０８Ｒでの微細Ｂｉ粒子の個数密度（個／ｍｍ２）を求める。同様に、各視野で認定された粗大Ｂｉ粒子の総個数と、上記複数の視野の総面積（２５．６ｍｍ２）とに基づいて、０．０８Ｒ深さ位置Ｄ０．０８Ｒでの粗大Ｂｉ粒子の個数密度（個／ｍｍ２）を求める。
　［０．６５Ｒ深さ位置Ｄ０．６５Ｒでの微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度の測定方法について］
　０．６５Ｒ深さ位置Ｄ０．６５Ｒでの微細Ｂｉ粒子の個数密度及び粗大Ｂｉ粒子の個数密度は、次の方法で測定できる。
　鋼材の軸方向に平行であって、鋼材の中心軸を含む断面において、０．６５Ｒ深さ位置Ｄ０．６５Ｒを含む試験片を採取する。採取した試験片のうち、上記鋼材の軸方向に平行であって、鋼材の中心軸を含む断面を、観察面とする。
　観察面を鏡面研磨する。ＳＥＭを用いて、１０００倍の倍率で、鏡面研磨後の観察面のうち、０．６５Ｒ深さ位置Ｄ０．６５Ｒを含む矩形の観察領域を選定する。観察領域の面積を２５．６ｍｍ２とする。観察領域の中心位置に０．６５Ｒ深さ位置Ｄ０．６５Ｒが配置されるように、観察領域を選定する。さらに、観察領域を２０２．５μｍ×２０２．５μｍの矩形の視野に６２４分割（２６×２４分割）する。
　ＳＥＭ観察により得られた各視野の反射電子像に基づいて、周知の画像解析の粒子解析方法を用いて、粗大Ｂｉ粒子及び微細Ｂｉ粒子の個数密度を調べる。具体的には、鋼材の母相と粒子との界面に基づいて、鋼材中の粒子を特定する。ここでいう粒子は、介在物又は析出物である。画像解析を行い、特定された粒子の円相当径を求める。具体的には、特定された各粒子の面積を求める。求めた面積と同じ面積の円での直径を、当該粒子の円相当径（μｍ）とする。
　上記ＳＥＭ観察により得られた反射電子像中で観察される粒子のうち、円相当径が０．１～１．０μｍの粒子であって、かつ、ＥＤＸを用いて粒子の組成を点分析した結果、Ｂｉ含有量が質量％で５０％以上である粒子を、微細Ｂｉ粒子と特定する。また、ＳＥＭ観察により得られた反射電子像で観察される粒子のうち、円相当径が１０．０μｍ以上の粒子であって、かつ、ＥＤＸを用いて粒子の組成を点分析した結果、Ｂｉ含有量が質量％で５０％以上である粒子を、粗大Ｂｉ粒子と特定する。ＥＤＸ分析の加速電圧は２０ｋＶとする。なお、Ｂｉは重元素であるため、反射電子像において高輝度で観察される。そのため、輝度に基づいてＢｉ粒子を特定してもよい。
　各視野で認定された微細Ｂｉ粒子の総個数と、上記観察領域を構成する複数の視野の総面積（２５．６ｍｍ２）とに基づいて、０．６５Ｒ深さ位置Ｄ０．６５Ｒでの微細Ｂｉ粒子の個数密度（個／ｍｍ２）を求める。同様に、各視野で認定された粗大Ｂｉ粒子の総個数と、上記複数の視野の総面積（２５．６ｍｍ２）とに基づいて、０．６５Ｒ深さ位置Ｄ０．６５Ｒでの粗大Ｂｉ粒子の個数密度（個／ｍｍ２）を求める。
　［本実施形態の鋼材の効果］
　以上のとおり、本実施形態の鋼材は、特徴１～特徴４を満たす。そのため、鋼材において、優れた耐溶融割れ性、優れた耐熱間加工割れ性、及び、優れた被削性が同時に得られる。さらに、鋼材を素材として製造された機械構造用部品において、高い疲労強度が得られる。
　［本実施形態の鋼材の好ましい用途及び形状］
　本実施形態の鋼材は、例えば、機械構造用部品の素材として広く適用可能である。本実施形態の鋼材は特に、機械構造用部品の製造工程において、熱間鍛造等の熱間加工、高周波焼入れ及び切削加工を実施する場合に好適である。ただし、熱間加工、高周波焼入れ及び切削加工の１工程以上を実施しない場合であっても、本実施形態の鋼材は、機械構造用部品の素材として適用可能である。
　なお、鋼材の軸方向に垂直な断面は円形状である。鋼材の軸方向に垂直な断面での直径は特に限定されないが、例えば、１０～２００ｍｍである。
　［製造方法］
　本実施形態による鋼材の製造方法の一例を説明する。特徴１～特徴４を満たす鋼材は、以降に説明する製造方法以外の他の製造方法により製造されてもよい。しかしながら、以降に説明する製造方法は、本実施形態による鋼材の製造方法の好ましい一例である。
　本実施形態の鋼材の製造方法の一例は、次の工程を含む。なお、工程３は任意の工程であり、実施しなくてもよい。
　（工程１）精錬工程
　（工程２）鋳造工程
　（工程３）熱間加工工程
　以下、各工程について説明する。
　［（工程１）精錬工程］
　精錬工程では、上述の特徴１及び特徴２を満たす化学組成を有する溶鋼を製造する。精錬工程は、一次精錬工程と二次精錬工程とを含む。
　一次精錬工程では、周知の方法で製造された溶銑に対して、転炉での精錬を実施して溶鋼を製造する。二次精錬工程では、溶鋼に対して合金元素を添加して、溶鋼の化学組成が、特徴１及び特徴２を満たすように調整する。具体的には、二次精錬工程では、周知の精錬方法で溶鋼を攪拌しながら、Ｂｉ以外の溶鋼の成分調整を実施する。その後、ワイヤーにより溶鋼にＢｉを添加した後に溶鋼を攪拌し、Ｂｉの成分調整を行う。二次精錬工程では、次の条件を満たす。
　（条件１）
　溶鋼にＢｉを添加した後、二次精錬工程での攪拌終了までの時間ｔ０を１５分超～６０分未満とする。
　（条件２）
　溶鋼にＢｉを添加した後の溶鋼の撹拌動力密度εを１０～１００Ｗ／ｔとする。ここで、撹拌動力密度ε（Ｗ／ｔ）は次の式（Ａ）で定義される。
　ε＝０．０２８５×Ｑ×Ｔ／Ｗ×ｌｏｇ（１＋５１３．５×Ｚ／Ｖ１）　（Ａ）
　ここで、式（Ａ）中のＱには、溶鋼を収納した取鍋への吹き込みガス流量（ＮＬ／ｍｉｎ）が代入される。Ｔには、溶鋼温度（Ｋ）が代入される。Ｗには、溶鋼質量（ｔ）が代入される。Ｚには取鍋中の溶鋼深さ（ｍ）が代入される。Ｖ１には、撹拌中の溶鋼を含む雰囲気での真空度（ｔｏｒｒ）が代入される。
　以下、条件１及び条件２について説明する。
　［条件１：時間ｔ０について］
　二次精錬工程において、Ｂｉを添加した後、二次精錬工程での攪拌終了までの時間ｔ０は、１５分超～６０分未満である。
　Ｂｉを添加した後、二次精錬工程での撹拌終了までの時間ｔ０が１５分以下の場合、溶鋼中でＢｉが十分に拡散しない。この場合、製造された鋼材中において、粗大Ｂｉ粒子が過剰に生成する。そのため、０．０８Ｒ深さ位置Ｄ０．０８Ｒでの粗大Ｂｉ粒子の個数密度が過剰に高くなる。
　一方、Ｂｉを添加した後、二次精錬工程での撹拌終了までの時間ｔ０が６０分以上の場合、溶鋼中のＢｉが凝集しやすくなる。この場合、製造された鋼材中において、微細Ｂｉ粒子の個数密度が減少する。そのため、０．０８Ｒ深さ位置Ｄ０．０８Ｒでの微細Ｂｉ粒子の個数密度が過剰に低くなる。
　二次精錬工程で、Ｂｉを添加した後、二次精錬工程での撹拌終了までの時間ｔ０が１５分超～６０分未満であれば、溶鋼中でＢｉが十分に拡散する。そのため、条件２及び後述の条件３及び条件４を満たすことを前提として、鋼材中の０．０８Ｒ深さ位置Ｄ０．０８Ｒ及び０．６５Ｒ深さ位置Ｄ０．６５Ｒでの微細Ｂｉ粒子の個数密度及び粗大Ｂｉ粒子の個数密度が適切な範囲となる。
　なお、Ｂｉを添加した後、二次精錬工程での撹拌終了までの溶鋼の温度は１５１０～１６３０℃である。
　［条件２：撹拌動力密度εについて］
　溶鋼にＢｉを添加した後の溶鋼の撹拌動力密度εは、１０～１００Ｗ／ｔである。
　溶鋼にＢｉを添加した後の溶鋼の撹拌動力密度εが１０Ｗ／ｔ未満であれば、溶鋼中でＢｉが十分に拡散しない。この場合、製造された鋼材中において、粗大Ｂｉ粒子が過剰に生成する。そのため、０．０８Ｒ深さ位置Ｄ０．０８Ｒでの粗大Ｂｉ粒子の個数密度が過剰に高くなる。
　一方、溶鋼にＢｉを添加した後の溶鋼の撹拌動力密度εが１００Ｗ／ｔを超えれば、溶鋼中のＢｉが凝集しやすくなる。この場合、製造された鋼材中において、微細Ｂｉ粒子の個数密度が減少する。そのため、０．０８Ｒ深さ位置Ｄ０．０８Ｒでの微細Ｂｉ粒子の個数密度が過剰に低くなる。
　溶鋼にＢｉを添加した後の溶鋼の撹拌動力密度εが１０～１００Ｗ／ｔであれば、溶鋼中でＢｉが十分に拡散する。そのため、条件２及び後述の条件３及び条件４を満たすことを前提として、鋼材中の０．０８Ｒ深さ位置Ｄ０．０８Ｒ及び０．６５Ｒ深さ位置Ｄ０．６５Ｒでの微細Ｂｉ粒子の個数密度及び粗大Ｂｉ粒子の個数密度が適切な範囲となる。
　［（工程２）鋳造工程］
　鋳造工程では、溶鋼を用いて、周知の連続鋳造法により鋳片を製造する。鋳造工程は、次の条件で実施する。
　（条件３）
　鋳片の長手方向に垂直な断面において、表面から１５ｍｍ深さ位置での凝固冷却速度を表層凝固冷却速度と定義したとき、表層凝固冷却速度を５５０℃／分以上とする。
　（条件４）
　鋳片の長手方向に垂直な断面において、断面形状が矩形の場合は、当該矩形断面の長辺の幅中央の線上における、鋳片表面と鋳片中心との中間点での凝固冷却速度を内部凝固冷却速度と定義し、断面形状が円形の場合は、半径Ｒの中間点（つまり、Ｒ／２深さ位置）での凝固冷却速度を内部凝固冷却速度と定義したとき、内部凝固冷却速度を１００℃／分以下とする。
　以下、条件３及び条件４について説明する。
　［条件３：表層凝固冷却速度について］
　Ｂｉ粒子は凝固時に生成する。つまり、Ｂｉ粒子は晶出により生成する。したがって、鋼材が特徴３を満たすためには、鋳片の表層部分の凝固冷却速度を速くして、Ｂｉ粒子が粗大化する前に鋼を凝固させる方が好ましい。そこで、鋳造工程において、製造された鋳片の表面から１５ｍｍ深さ位置での凝固冷却速度が５５０℃／分以上となるように、連続鋳造装置でのモールドでの鋳片の冷却速度を調整する。
　ここで、鋳造工程における鋼の温度域のうち、液相線温度から固相線温度までの冷却速度を凝固冷却速度（℃／分）と定義する。そして、上述のとおり、鋳片の表面から１５ｍｍ深さ位置での凝固冷却速度を「表層凝固冷却速度」と定義する。表層凝固冷却速度は次の方法で決定する。
　連続鋳造法で製造された鋳片の長手方向に垂直な断面のうち、鋳片の表面から１５ｍｍ深さ位置を含む試験片を採取する。例えば、鋳片の長手方向に垂直な断面が矩形である場合、鋳片の表面の幅中央位置（断面が長方形である場合は長辺に相当する表面の幅中央位置）から１５ｍｍ深さ位置を含む試験片を採取する。試験片のうち、鋳片の長手方向に垂直な断面に相当する面を観察面とする。観察面のうち、鋳片の表面から１５ｍｍ深さ位置を中心とする５ｍｍ×５ｍｍの領域を、観察領域とする。観察領域において、１０カ所のデンドライト二次アーム間隔を測定し、その算術平均値をλ２（μｍ）とする。測定されたデンドライド二次アーム間隔λ２（μｍ）を用いて、表層凝固冷却速度Ｖ（℃／分）を求める。
　Ｖ＝（λ２／７７０）－１／０．４１
　鋳片の表面から１５ｍｍ深さ位置の領域は、連続鋳造装置の鋳型（モールド）を通過中に凝固する。そのため、表層凝固冷却速度は、鋳型での冷却機構により調整される。表層凝固冷却速度の上限は特に限定されない。表面凝固冷却速度の好ましい下限は６００℃／分以上、さらに好ましい下限は７００℃／分以上である。なお、５５０℃／分以上の表層凝固冷却速度を得るための好ましい鋳造速度として、０．６ｍ／分以下を例示できる。
　［条件４：内部凝固冷却速度について］
　上述のとおり、Ｂｉ粒子は凝固時に生成する。したがって、鋼材が特徴４を満たすためには、鋳片の内部の凝固冷却速度を遅くして、Ｂｉ粒子を粗大化させた後に鋼を凝固させる方が好ましい。そこで、鋳造工程において、内部凝固冷却速度が１００℃／分以下となるように、鋳片の冷却速度を調整する。
　ここで、上述の定義に基づく内部凝固冷却速度を、次の方法で決定する。
　連続鋳造法で製造された鋳片の長手方向に垂直な断面のうち、断面形状が矩形の場合は、当該矩形断面の長辺の幅中央の線上における鋳片表面と鋳片中心との中間点を含む試験片を採取し、断面形状が円形の場合は、半径Ｒの中間点（Ｒ／２深さ位置）を含む試験片を採取する。試験片のうち、鋳片の長手方向に垂直な断面に相当する面を観察面とする。観察面のうち、上記中間点を中心とする５ｍｍ×５ｍｍの領域を、観察領域とする。観察領域において、１０カ所のデンドライト二次アーム間隔を測定し、その算術平均値をλ２（μｍ）とする。測定されたデンドライド二次アーム間隔λ２（μｍ）を用いて、内部凝固冷却速度Ｖ（℃／分）を求める。
　Ｖ＝（λ２／７７０）－１／０．４１
　内部凝固冷却速度は、例えば、鋳型（モールド）のサイズを変更することにより調整できる。具体的には、鋳型の横断面の面積を調整することにより、内部凝固冷却速度を調整できる。さらに、連続鋳造機の鋳型下流に配列されたロール群において、ロール間に、鋳片を冷却するための流体ノズルが複数配置されている。そのため、これらの複数の流体ノズルから噴射する流体（水に代表される冷却液、空気、又は冷却液及び空気の混合流体）の流量を調整することにより、内部凝固冷却速度を調整できる。内部凝固冷却速度の下限は特に限定されないが、好ましい下限は１０℃／分以上である。好ましい上限は５０℃／分以下、さらに好ましい上限は２５℃／分以下である。
　［（工程３）熱間加工工程］
　熱間加工工程は、任意の工程である。つまり、熱間加工工程は実施してもよいし、実施しなくてもよい。熱間加工工程を実施する場合、熱間加工工程では、上記鋳造工程で製造された鋳片に対して、熱間加工を実施して、鋼材を製造する。
　熱間加工工程は例えば、周知の粗圧延工程のみであってもよいし、周知の粗圧延工程と、粗圧延工程後に実施される周知の仕上げ圧延工程とを含んでもよい。粗圧延工程では例えば、分塊圧延、又は、分塊圧延及び分塊圧延後の連続圧延機による熱間圧延により、加熱された鋳片又は鋼塊からビレットを製造する。仕上げ圧延工程では例えば、加熱されたビレットに対して、周知の連続圧延機を用いた仕上げ圧延を実施して鋼材（棒鋼）を製造する。粗圧延工程での加熱温度は例えば、１０００～１３００℃である。仕上げ圧延工程での加熱温度は例えば、１０００～１３００℃である。
　上述の熱間加工工程では、熱間圧延により鋼材を製造する。しかしながら、熱間圧延以外の他の熱間加工により、鋼材を製造してもよい。例えば、熱間圧延に代えて、熱間鍛造により鋼材を製造してもよい。また、熱間圧延と熱間鍛造とを実施して鋼材を製造してもよい。熱間加工工程において熱間鍛造を実施する場合においても、加熱温度は例えば、１０００～１３００℃である。
　以上の製造工程により、本実施形態の鋼材が製造される。なお、上述のとおり、熱間加工工程を省略してもよい。つまり、本実施形態の鋼材は、鋳造品（鋳片）であってもよい。
　［機械構造用部品の製造方法］
　本実施形態の鋼材は、上述のとおり、機械構造用部品の素材として用いられる。機械構造用部品の製造方法は周知であり、例えば、次のとおりである。
　本実施形態の鋼材を熱間加工して、機械構造用部品（例えばクランクシャフト）の粗形状の中間品を製造する。熱間加工は例えば、熱間鍛造である。製造された中間品を大気中で放冷する。
　放冷後の中間品に対して切削加工を実施して、中間品を所定の形状に切削する。切削加工後の中間品に対して、周知の高周波焼入れ（焼戻しは省略）、又は、周知の高周波焼入れ及び周知の焼戻しを実施する。以上の工程により、機械構造用部品が製造される。
　実施例により本実施形態の鋼材の効果をさらに具体的に説明する。以下の実施例での条件は、本実施形態の鋼材の実施可能性及び効果を確認するために採用した一条件例である。したがって、本実施形態の鋼材はこの一条件例に限定されない。
　表１－１～表１－３の化学組成を有する鋼材を製造した。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
Figure JPOXMLDOC01-appb-T000003
　具体的には、７０トン転炉を用いて、精錬工程（一次精錬工程、及び、二次精錬工程）を実施した。一次精錬工程では、周知の方法で製造された溶銑に対して転炉での精錬を同じ条件で実施した。
　一次精錬工程後、二次精錬工程を実施した。具体的には、ＬＦ（Ｌａｄｌｅ　Ｆｕｒｎａｃｅ）を用いた精錬処理を実施し、その後、ＲＨ真空脱ガス処理を実施した。これらの工程を通じて、Ｂｉ以外の元素の成分の調整を実施した。その後さらに、ワイヤーにてＢｉを溶鋼に添加した後に溶鋼を撹拌し、Ｂｉの成分調整を行った。
　Ｂｉを溶鋼に添加した後、二次精錬工程での攪拌終了までの時間ｔ０（分）は、表２に示すとおりであった。さらに、撹拌時の撹拌動力密度ε（Ｗ／ｔ）は、表２に示すとおりであった。なお、Ｂｉを溶鋼に添加した後、二次精錬工程での攪拌終了までの溶鋼温度は、１５１０～１６３０℃であった。以上の工程により、溶鋼を製造した。
Figure JPOXMLDOC01-appb-T000004
　溶鋼を用いて、連続鋳造法により、鋳片（ブルーム）を製造した。鋳造時に凝固冷却速度（℃／分）を調整した。表層凝固冷却速度と内部凝固冷却速度は表２に示すとおりであった。なお、表層凝固冷却速度及び内部凝固冷却速度は、上述の［条件３：表層凝固冷却速度について］及び［条件４：内部凝固冷却速度について］に記載の方法により求めた。
　製造されたブルームに対して熱間加工を実施した。具体的には、ブルームに対して粗圧延加工を実施して、横断面が１８０ｍｍ×１８０ｍｍのビレットを製造した。なお、粗圧延加工時のブルームの加熱温度は１２５０℃であった。
　さらに、ビレットに対して仕上げ圧延に相当する熱間鍛造を実施して、直径９７ｍｍの鋼材（棒鋼）を製造した。なお、熱間鍛造時のビレットの加熱温度は１２５０℃であった。鍛造は株式会社大谷機械製作所製のエアーハンマー（型式６００ＨＰ）を用いて実施した。ビレットを１２５０℃で１時間加熱した後、横断面が１２０ｍｍ×１２０ｍｍに鍛造した。その後、再び１２５０℃で１時間加熱した後、横断面が直径９７ｍｍの円に外接する八角形になるように鍛造した。その後、再び１２５０℃で１時間加熱した後、直径９７ｍｍの断面が円形状の棒鋼（丸鋼）に鍛造した。以上の製造工程により、鋼材を製造した。
　［評価試験］
　各試験番号の鋼材に対して、次の評価試験を実施した。
　（試験１）０．０８Ｒ深さ位置Ｄ０．０８Ｒでの微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度測定試験
　（試験２）０．６５Ｒ深さ位置Ｄ０．６５Ｒでの微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度測定試験
　（試験３）熱間加工割れ評価試験
　（試験４）溶融割れ評価試験
　（試験５）被削性評価試験（ドリル寿命試験）
　（試験６）疲労強度評価試験（回転曲げ疲労試験）
　以下、各評価試験について説明する。
　［（試験１）０．０８Ｒ深さ位置Ｄ０．０８Ｒでの微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度測定試験］
　各試験番号の鋼材に対して、上述の［０．０８Ｒ深さ位置Ｄ０．０８Ｒでの微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度の測定方法について］に記載の方法により、０．０８Ｒ深さ位置Ｄ０．０８Ｒでの微細Ｂｉ粒子の個数密度（個／ｍｍ２）及び０．０８Ｒ深さ位置Ｄ０．０８Ｒでの粗大Ｂｉ粒子の個数密度（個／ｍｍ２）を求めた。結果を表２に示す。
　［（試験２）０．６５Ｒ深さ位置Ｄ０．６５Ｒでの微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度測定試験］
　各試験番号の鋼材に対して、上述の［０．６５Ｒ深さ位置Ｄ０．６５Ｒでの微細Ｂｉ粒子及び粗大Ｂｉ粒子の個数密度の測定方法について］に記載の方法により、０．６５Ｒ深さ位置Ｄ０．６５Ｒでの微細Ｂｉ粒子の個数密度（個／ｍｍ２）及び０．６５Ｒ深さ位置Ｄ０．６５Ｒでの粗大Ｂｉ粒子の個数密度（個／ｍｍ２）を求めた。結果を表２に示す。
　［（試験３）熱間加工割れ評価試験］
　製造された各試験番号の鋼材の表面を観察した。観察の結果、鋼材の表面において、鋼材の長手方向１ｍ当たり２箇所以上の明確な割れが観察される場合、熱間加工割れが発生したと判断した。一方、観察の結果、鋼材の表面において鋼材の長手方向１ｍ当たり２箇所以上の明確な割れが観察されない場合、熱間加工割れが抑制されたと判断した。ここで明確な割れとは、肉眼で、または簡単な拡大鏡を用いて観察された長さ３ｍｍ以上の割れのことをいう。
　熱間加工割れの評価結果を表２の「熱間加工割れ」欄に示す。熱間加工割れが発生した場合を「ＮＧ」で示し、熱間加工割れが抑制された場合を「ＯＫ」で示す。
　［（試験４～試験６）溶融割れ評価試験、被削性評価試験及び疲労強度評価試験について］
　［模擬機械構造用部品の中間品の製造］
　各試験番号の鋼材を素材とした機械構造用部品の製造工程中の熱間鍛造を模擬した熱処理を実施した。具体的には、鋼材を加熱して、鋼材を１１００℃で３０分保持した。その後、鋼材を大気中で放冷した。以上の熱処理を施された鋼材を、以降では、「機械構造用部品の模擬中間品（又は、単に模擬中間品）」という。機械構造用部品の模擬中間品は、直径９７ｍｍの棒鋼（丸鋼）であった。
　［（試験４）溶融割れ評価試験］
　機械構造用部品の模擬中間品の表層領域ＳＡを含む領域から、幅１０ｍｍ、厚さ３ｍｍ、長さ１００ｍｍの試験片を機械加工により作製した。試験片の長手方向は、模擬中間品の長手方向と平行であった。また、試験片の長手方向に平行な中心軸が、０．０８Ｒ深さ位置と一致した。
　富士電波工機株式会社製の熱サイクル試験装置を用いて、試験片に対して、高周波焼入れを模擬した焼入れ試験を実施した。具体的には、試験片を１００℃／秒の昇温速度で１４００℃まで加熱した。そして、試験片を１４００℃で１５秒間保持した。その後、試験片を水冷した。
　水冷後の試験片を、試験片の長手方向での中央位置で、長手方向に垂直な方向に切断した。そして、切断面を観察面とした。観察面を機械研磨した。機械研磨後の観察面をピクラール試薬にて腐食した。腐食された観察面の中心位置を４００倍の光学顕微鏡で観察し、溶融割れの有無を目視で確認した。観察視野を２５０μｍ×４００μｍとした。
　観察面において、粒界で長さが５μｍ以上の明瞭に腐食されている領域（腐食領域）が観察された場合、溶融割れが発生したと判断した。粒界において幅が５μｍ以上の明瞭に腐食されている領域とは、例えば、図３中の符号１５で示す領域を意味する。一方、図４のように、粒界に腐食領域が観察されない場合、溶融割れが抑制されたと判断した。溶融割れの評価結果を表２の「溶融割れ」欄に示す。溶融割れが発生した場合、「ＮＧ」を示す。溶融割れが抑制された場合、「ＯＫ」を示す。
　［（試験５）被削性評価試験（ドリル寿命試験）］
　機械構造用部品の模擬中間品から被削性評価試験用の試験片を切り出した。具体的には、直径９７ｍｍの模擬中間品の長手方向に対して垂直な断面の内部領域ＣＡに相当する領域の任意の位置を、ドリルを用いて穿孔した。工具として、株式会社不二越製の型番ＳＤ３．０のドリルを使用した。穿孔条件として、１回転当たりの送り量を０．２５ｍｍ／ｒｅｖ、１穴の穿孔深さを９ｍｍとした。潤滑剤は水溶性の切削油であった。
　上述の穿孔条件でドリル穿孔を実施して、鋼材の被削性を評価した。評価指標として、最大切削速度ＶＬ１０００（ｍ／分）を用いた。最大切削速度ＶＬ１０００とは、累積穴深さで１０００ｍｍ長の穴あけが可能なドリルの切削速度の最大値である。
　最大切削速度ＶＬ１０００に基づいて、被削性を次のとおり評価した。
　ＶＬ１０００が２０ｍ／分以上：被削性に優れる　（「ＯＫ」）
　ＶＬ１０００が２０ｍ／分未満：被削性が低い　　（「ＮＧ」）
　表２の「被削性」欄に、「ＯＫ」、「ＮＧ」の評価結果を示す。
　［（試験６）疲労強度評価試験（回転曲げ疲労試験）］
　次の試験方法により、鋼材を素材として製造された機械構造用部品を想定した疲労試験片を用いて、疲労強度を評価した。
　機械構造用部品の模擬中間品から、図５に示す疲労試験片を作製した。疲労試験片は丸棒試験片であり、平行部の直径Ｄ１が８ｍｍであり、掴み部の直径が１２ｍｍであった。機械構造用部品の模擬中間品の長手方向に対して垂直な断面のＲ／２位置（つまり、半径の中央位置）から、疲労試験片を機械加工により作製した。疲労試験片の長手方向は、模擬中間品の長手方向と平行であった。なお、高周波焼入れ前の試験片での回転曲げ疲労強度が十分に高ければ、高周波焼入れ後の試験片においても、回転曲げ疲労強度が十分に高いことは、当業者に周知の技術常識である。
　疲労試験片の平行部には仕上げ研磨を実施し、表面粗さを調整した。具体的には、ＪＩＳ　Ｂ　０６０１：２００１に準拠した、表面の中心線平均粗さ（Ｒａ）を３．０μｍ以内とし、最大高さ（Ｒｍａｘ）を９．０μｍ以内にした。
　疲労試験片を用いて、室温（２３℃）、大気雰囲気にて、回転数３６００ｒｐｍの両振りの条件で小野式回転曲げ疲労試験を行った。複数の試験片に対して加える応力を変えて疲労試験を実施し、１０７サイクル後に破断しなかった最も高い応力を、疲労強度（ＭＰａ）とした。
　得られた疲労強度が３００ＭＰａ以上であれば、十分な疲労強度が得られたと判断した。疲労強度評価の結果を表２の「疲労強度」欄に示す。疲労強度が３００ＭＰａ以上の場合を「ＯＫ」とし、疲労強度が３００ＭＰａ未満の場合を「ＮＧ」とした。
　［試験結果］
　表１－１～表１－３及び表２に試験結果を示す。
　表１－１～表１－３及び表２を参照して、試験番号１～３８の鋼材は、化学組成が適切であり、かつ、式（１）を満たした。さらに製造条件も適切であった。そのため、各試験番号の鋼材は、特徴１～特徴４を満たした。その結果、熱間加工割れ及び溶融割れが確認されず、優れた耐熱間加工割れ性及び優れた耐溶融割れ性が得られた。さらに、鋼材の最大切削速度ＶＬ１０００は２０ｍ／分以上であり、優れた被削性が得られた。さらに、鋼材の疲労強度は３００ＭＰａ以上であり、鋼材を素材として製造された機械構造用部品の疲労強度は高かった。
　一方、試験番号３９及び４０では、Ｆｎが０．４５未満であった。そのため、鋼材を素材として製造された機械構造用部品の疲労強度が低かった。
　試験番号４１及び４２では、Ｆｎが１．０５超であった。そのため、鋼材の被削性が低かった。
　試験番号４３及び４４では、Ｂｉ添加後から攪拌終了までの時間ｔ０が１５分以下であった。そのため、０．０８Ｒ深さ位置Ｄ０．０８Ｒの粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２超であった。その結果、熱間加工割れが発生した。
　試験番号４５及び４６では、Ｂｉ添加後から攪拌終了までの時間ｔ０が６０分以上であった。そのため、０．０８Ｒ深さ位置Ｄ０．０８Ｒの微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２未満となった。その結果、溶融割れが発生した。
　試験番号４７及び４８では、Ｂｉ添加後の溶鋼の撹拌動力密度εが１０Ｗ／ｔ未満であった。そのため、０．０８Ｒ深さ位置Ｄ０．０８Ｒの粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２超であった。その結果、熱間加工割れが発生した。
　試験番号４９及び５０では、Ｂｉ添加後の溶鋼の撹拌動力密度εが１００Ｗ／ｔ超であった。そのため、０．０８Ｒ深さ位置Ｄ０．０８Ｒの微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２未満となった。その結果、溶融割れが発生した。
　試験番号５１及び５２では、鋳造時の表層凝固冷却速度が５５０℃／分未満であった。そのため、０．０８Ｒ深さ位置Ｄ０．０８Ｒの微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２未満であり、０．０８Ｒ深さ位置Ｄ０．０８Ｒの粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２超となった。その結果、熱間加工割れと溶融割れが発生した。
　試験番号５３及び５４では、鋳造時の内部凝固冷却速度が１００℃／分超であった。そのため、０．６５Ｒ深さ位置Ｄ０．６５Ｒの微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２以上であり、０．６５Ｒ深さ位置Ｄ０．６５Ｒの粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２以下となった。その結果、鋼材の被削性が低かった。
　試験番号５５では、Ｂｉ含有量が低すぎた。そのため、０．０８Ｒ深さ位置Ｄ０．０８Ｒの微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２未満であり、０．６５Ｒ深さ位置Ｄ０．６５Ｒの粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２以下となった。その結果、溶融割れが発生し、さらに鋼材の被削性が低かった。
　試験番号５６では、Ｂｉ含有量が高すぎた。そのため、０．０８Ｒ深さ位置Ｄ０．０８Ｒの粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２超となった。その結果、熱間加工割れが発生した。
　以上、本発明の実施の形態を説明した。しかしながら、上述した実施の形態は本発明を実施するための例示に過ぎない。したがって、本発明は上述した実施の形態に限定されることなく、その趣旨を逸脱しない範囲内で上述した実施の形態を適宜変更して実施することができる。
１　フィレットＲ部
２　クランクシャフトのエッジ部
１５　溶融割れ

Claims (2)

  1. 　軸方向に垂直な断面が円形状の鋼材であって、
    　化学組成が、質量％で、
    　Ｃ：０．３０超～０．６０％、
    　Ｓｉ：０．０１～０．９０％、
    　Ｍｎ：０．５０～１．７０％、
    　Ｐ：０．０３０％以下、
    　Ｓ：０．２００％以下、
    　Ｂｉ：０．００５１～０．２５００％、
    　Ａｌ：０．００１～０．１００％、
    　Ｎ：０．０２５０％以下、
    　Ｏ：０．００５０％以下、
    　Ｃｒ：０～１．３０％、
    　Ｖ：０～０．２００％、
    　Ｓｎ：０～０．１０００％、
    　Ｓｂ：０～０．０５００％、
    　Ａｓ：０～０．０５００％、
    　Ｐｂ：０～０．０９％、
    　Ｍｇ：０～０．０１００％、
    　Ｔｉ：０～０．０４００％、
    　Ｎｂ：０～０．０５００％、
    　Ｗ：０～０．４０００％、
    　Ｚｒ：０～０．２０００％、
    　Ｃａ：０～０．０１００％、
    　Ｔｅ：０～０．０１００％、
    　Ｂ：０～０．００５０％、
    　希土類元素：０～０．０１００％、
    　Ｃｏ：０～０．０１００％、
    　Ｓｅ：０～０．０１００％、
    　Ｉｎ：０～０．０１００％、
    　Ｍｏ：０～０．３０％、
    　Ｃｕ：０～０．５０％、
    　Ｎｉ：０～０．５０％、及び、
    　残部はＦｅ及び不純物からなり、
    　式（１）で定義されるＦｎが０．４５～１．０５であり、
    　前記鋼材の半径をＲと定義したとき、前記鋼材の表面から０．０８Ｒ深さ位置において、
    　円相当径が０．１～１．０μｍのＢｉ粒子である微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２以上であり、
    　円相当径が１０．０μｍ以上のＢｉ粒子である粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２以下であり、
    　前記鋼材の表面から０．６５Ｒ深さ位置において、
    　前記微細Ｂｉ粒子の個数密度が１５．００個／ｍｍ２未満であり、
    　前記粗大Ｂｉ粒子の個数密度が０．２５個／ｍｍ２超である、
    　鋼材。
    　Ｆｎ＝Ｃ＋（Ｓｉ／１０）＋（Ｍｎ／５）－（５Ｓ／７）＋（５Ｃｒ／２２）＋１．６５Ｖ　（１）
    　ここで、式（１）中の各元素記号には、対応する元素の質量％での含有量が代入され、元素が含有されていない場合、対応する元素記号には「０」が代入される。
  2. 　請求項１に記載の鋼材であって、
    　前記化学組成は、
    　Ｃｒ：０．０１～１．３０％、
    　Ｖ：０．００１～０．２００％、
    　Ｓｎ：０．０００１～０．１０００％、
    　Ｓｂ：０．０００１～０．０５００％、
    　Ａｓ：０．０００１～０．０５００％、
    　Ｐｂ：０．０１～０．０９％、
    　Ｍｇ：０．０００１～０．０１００％、
    　Ｔｉ：０．０００１～０．０４００％、
    　Ｎｂ：０．０００１～０．０５００％、
    　Ｗ：０．０００１～０．４０００％、
    　Ｚｒ：０．０００１～０．２０００％、
    　Ｃａ：０．０００１～０．０１００％、
    　Ｔｅ：０．０００１～０．０１００％、
    　Ｂ：０．０００１～０．００５０％、
    　希土類元素：０．０００１～０．０１００％、
    　Ｃｏ：０．０００１～０．０１００％、
    　Ｓｅ：０．０００１～０．０１００％、
    　Ｉｎ：０．０００１～０．０１００％、
    　Ｍｏ：０．０１～０．３０％、
    　Ｃｕ：０．０１～０．５０％、
    　Ｎｉ：０．０１～０．５０％、
    　からなる群から選択される１種以上を含有する、
    　鋼材。
PCT/JP2023/026060 2022-07-20 2023-07-14 鋼材 WO2024019013A1 (ja)