WO2023286738A1 - Fibres de polyamide pour câble pour pneu et procédé de production de celles-ci - Google Patents

Fibres de polyamide pour câble pour pneu et procédé de production de celles-ci Download PDF

Info

Publication number
WO2023286738A1
WO2023286738A1 PCT/JP2022/027269 JP2022027269W WO2023286738A1 WO 2023286738 A1 WO2023286738 A1 WO 2023286738A1 JP 2022027269 W JP2022027269 W JP 2022027269W WO 2023286738 A1 WO2023286738 A1 WO 2023286738A1
Authority
WO
WIPO (PCT)
Prior art keywords
less
dtex
polyamide fiber
tire
cord
Prior art date
Application number
PCT/JP2022/027269
Other languages
English (en)
Japanese (ja)
Inventor
浩介 井田
Original Assignee
旭化成株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 旭化成株式会社 filed Critical 旭化成株式会社
Priority to JP2023534794A priority Critical patent/JPWO2023286738A1/ja
Priority to CN202280049215.5A priority patent/CN117642531A/zh
Publication of WO2023286738A1 publication Critical patent/WO2023286738A1/fr

Abstract

L'invention concerne : des fibres de polyamide pour un câble pour pneu, avec lesquelles une coupe d'un câble pendant des étapes de production d'un câble pour pneu et d'un tissu câblé pour pneu est supprimée ; un procédé de production de celles-ci ; un câble à fils torsadés utilisant les fibres ; et un tissu câblé utilisant le câble. La présente invention concerne des fibres de polyamide pour un câble pour pneu et un procédé de production de celles-ci, la résistance au nœud aérien des fibres de polyamide dans un environnement à une température de 180 °C étant de 3,5 à 6,0 cN/dtex.
PCT/JP2022/027269 2021-07-16 2022-07-11 Fibres de polyamide pour câble pour pneu et procédé de production de celles-ci WO2023286738A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2023534794A JPWO2023286738A1 (fr) 2021-07-16 2022-07-11
CN202280049215.5A CN117642531A (zh) 2021-07-16 2022-07-11 轮胎帘线用聚酰胺纤维及其制法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2021117985 2021-07-16
JP2021-117985 2021-07-16

Publications (1)

Publication Number Publication Date
WO2023286738A1 true WO2023286738A1 (fr) 2023-01-19

Family

ID=84919388

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2022/027269 WO2023286738A1 (fr) 2021-07-16 2022-07-11 Fibres de polyamide pour câble pour pneu et procédé de production de celles-ci

Country Status (3)

Country Link
JP (1) JPWO2023286738A1 (fr)
CN (1) CN117642531A (fr)
WO (1) WO2023286738A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5541330B2 (fr) * 1977-06-30 1980-10-23
JPS63165513A (ja) * 1986-12-25 1988-07-08 Toray Ind Inc ポリアミド繊維の直接紡糸延伸方法
JP2007062585A (ja) * 2005-08-31 2007-03-15 Yokohama Rubber Co Ltd:The 空気入りタイヤ
JP2009068132A (ja) * 2007-09-12 2009-04-02 Toray Ind Inc 繊維、ゴム補強コード、ならびに補強ゴム

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5541330B2 (fr) * 1977-06-30 1980-10-23
JPS63165513A (ja) * 1986-12-25 1988-07-08 Toray Ind Inc ポリアミド繊維の直接紡糸延伸方法
JP2007062585A (ja) * 2005-08-31 2007-03-15 Yokohama Rubber Co Ltd:The 空気入りタイヤ
JP2009068132A (ja) * 2007-09-12 2009-04-02 Toray Ind Inc 繊維、ゴム補強コード、ならびに補強ゴム

Also Published As

Publication number Publication date
CN117642531A (zh) 2024-03-01
JPWO2023286738A1 (fr) 2023-01-19

Similar Documents

Publication Publication Date Title
JP5251490B2 (ja) ポリフェニレンサルファイド繊維およびその製造方法
JP4584503B2 (ja) すだれ織物
TWI491551B (zh) 聚酯單絲捲裝物
EP2847370B1 (fr) Renfort textile comprenant des fils d'aramide continue
JP2009013511A (ja) ポリアミドマルチフィラメントおよびそれを用いた織物
CN107034534A (zh) 一种锦纶6分纤母丝生产设备及生产方法
US4850186A (en) Thread of carbon fiber
JP6210209B2 (ja) モノフィラメント様高強度ポリエチレン繊維
CN107531442B (zh) 由聚乳酸系单丝形成的圆筒状卷装体
JP2018003190A (ja) 仮撚り用複合ポリアミド繊維
WO2023286738A1 (fr) Fibres de polyamide pour câble pour pneu et procédé de production de celles-ci
JP4983518B2 (ja) 仮撚用ポリアミド繊維および仮撚用ポリアミド繊維の製造方法
JP4677870B2 (ja) ポリアミドフィラメント
JP4749838B2 (ja) 交絡糸およびその製造方法
JP2003027333A (ja) ポリケトン繊維
WO2019208404A1 (fr) Monofilament de polyamide
JP3804771B2 (ja) ポリケトン繊維
JP3595204B2 (ja) ポリエステル繊維の製造方法
TR2023019128T2 (tr) Lastik kord bezi için poliamid elyaflar ve bunların üretimi için yöntem.
JP2022157916A (ja) ポリフェニレンスルフィド繊維の製造方法
JP2009084720A (ja) 熱可塑性合成繊維の製造方法
JP4395977B2 (ja) ポリアミド繊維の製造方法
JP2006265758A (ja) ポリアミドモノフィラメントおよびその製造方法
JPH07216642A (ja) ナイロン６繊維の直接紡糸延伸法
JPH09188930A (ja) 織物用ポリエステル系マルチフィラメント糸及びその製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22842082

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2023534794

Country of ref document: JP

WWE Wipo information: entry into national phase

Ref document number: 2023/019128

Country of ref document: TR

WWE Wipo information: entry into national phase

Ref document number: 202280049215.5

Country of ref document: CN

Ref document number: 2401000210

Country of ref document: TH

NENP Non-entry into the national phase

Ref country code: DE