WO2023190246A1 - 回路基板及びその製造方法、並びにパワーモジュール - Google Patents

回路基板及びその製造方法、並びにパワーモジュール Download PDF

Info

Publication number
WO2023190246A1
WO2023190246A1 PCT/JP2023/011999 JP2023011999W WO2023190246A1 WO 2023190246 A1 WO2023190246 A1 WO 2023190246A1 JP 2023011999 W JP2023011999 W JP 2023011999W WO 2023190246 A1 WO2023190246 A1 WO 2023190246A1
Authority
WO
WIPO (PCT)
Prior art keywords
main surface
circuit board
metal
plate
metal plate
Prior art date
Application number
PCT/JP2023/011999
Other languages
English (en)
French (fr)
Inventor
知広 ▲濱▼岡
聖治 小橋
厚樹 五十嵐
晃正 湯浅
貴裕 中村
善幸 江嶋
Original Assignee
デンカ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by デンカ株式会社 filed Critical デンカ株式会社
Priority to JP2024512409A priority Critical patent/JPWO2023190246A1/ja
Publication of WO2023190246A1 publication Critical patent/WO2023190246A1/ja

Abstract

セラミック板と、金属板と、セラミック板の主面と金属板の主面とを接合するろう材層と、を備える回路基板であって、金属板の主面の外縁の少なくとも一部に沿って金属板に凹部が形成されている、回路基板を提供する。この回路基板と、当該回路基板の金属板に電気的に接続される半導体素子と、を備えるパワーモジュールを提供する。

Description

回路基板及びその製造方法、並びにパワーモジュール
　本開示は、回路基板及びその製造方法、並びにパワーモジュールに関する。
　ロボット及びモーター等の産業機器の高性能化に伴い、大電流及び高電圧を制御するパワーモジュールが使用されている。このようなパワーモジュールに備えられる回路基板は、セラミック基板と銅板と備えており、これらは活性金属を含有するろう材を介して接合される。このような回路基板を形成する際に、ろう材が銅板の表面に染み出して銅板の側面を伝って這い上がる現象が生じる。このような現象が生じると、外観を損なうだけではなく、例えば半導体素子を接合する際に用いるはんだ材のぬれ製の悪化につながることも懸念される。
　特許文献１では、ろう材の這い上がりを抑制するため、金属板の側面に表面粗さの大きい粗部を設けることが提案されている。特許文献２では、這い上がり現象によるシミの発生を抑制するため、半導体素子が搭載される搭載予定面を囲むように回路層にリブを設ける技術が提案されている。特許文献３では、金属板のうち、バリが生じている側の表面をセラミック板の一方の面に重ねるようにして積層してろう付けすることが提案されている。このような技術によって、ろう材の這い上がりによって生じるシミの問題を解決することが試みられている。
国際公開第２０１９／１６３９４１号 特開２０２０－１５５４４４号公報 特開２０１６－３９１６３号公報
　多数個取りの回路基板の製造方法としては、エッチング法が知られている。エッチング法では、金属板を所定のサイズに加工するためにレジスト印刷及びエッチングの工程が必要となる。一方、予め所定のサイズに加工された金属板を接合する搭載法であれば、このような工程が不要となり、生産効率を向上することができる。このような搭載法の場合、金属板の端部とセラミック板との接合信頼性を確保するために、ろう材の塗布量を十分に確保する必要がある。ところが、ろう材の塗布量が多くなると、ろう材の這い上がりが生じることが懸念される。そこで、本開示は、ろう材の這い上がりを抑制することが可能な回路基板及びその製造方法を提供する。また、本開示は、そのような回路基板を備えるパワーモジュールを提供する。
　本開示の一側面に係る回路基板は、セラミック板と、金属板と、セラミック板の主面と金属板の主面とを接合するろう材層と、を備える回路基板であって、金属板の主面の外縁の少なくとも一部に沿って凹部が形成されている。
　上記回路基板では、金属板の主面の外縁の少なくとも一部に沿って金属板に凹部が形成されているため、ろう材が、金属板を這い上がり、金属板のセラミック板側とは反対側の主面にろう材が到達することを十分に抑制できる。このようにろう材の這い上がりが抑制された回路基板は、外観及び半導体素子等の外部回路との接続信頼性に優れる。
　上記金属板における凹部は、金属板の主面の外縁の全周にわたって形成されていてよい。これによって、ろう材層から金属板のセラミック板側とは反対側の主面にろう材が這い上がることを一層抑制することができる。
　上記凹部を構成する金属板の壁面は、セラミック板の主面と対向する対向面を含んでよい。凹部を構成する金属板の壁面がこのような対向面を有することによって、ろう材の這い上がりを一層抑制することができる。
　上記回路基板を、金属板の側面における凹部の端縁に直交し、金属板の厚さ方向に沿う断面で見たときに、凹部の幅Ｘは０．０５ｍｍ以上であってよく、凹部の高さＺは０．０５ｍｍ以上であってよい。凹部がこのようなサイズを有することによって、ろう材の這い上がりを一層抑制することができる。
　上記回路基板を、金属板の側面における凹部の端縁に直交し、金属板の厚さ方向に沿う断面で見たときに、ろう材層は、凹部内においてセラミック板の主面に近づくにつれて拡がる傾斜部を有してよい。ろう材層がこのような傾斜部を有することによって、ろう材の這い上がりを一層抑制することができる。また、ろう材層とセラミック板の主面との接合面積を大きくして、接合信頼性を向上することができる。
　上記回路基板は、セラミック板と、複数の金属板と、セラミック板の上記主面と複数の金属板の主面のそれぞれとを接合する複数のろう材層と、を備え、複数の金属板が、凹部が形成されている上記金属板を含んでよい。
　上記回路基板では、少なくとも一つの金属板の主面の外縁に沿って金属板に凹部が形成されているため、ろう材が、当該金属板の側面を這い上がり、金属板のセラミック板側とは反対側の主面にろう材が到達することを十分に抑制できる。このようにろう材の這い上がりが抑制された回路基板は、外観及び半導体素子との接続信頼性に優れる。なお、複数の金属板のそれぞれは、セラミック板の主面における区画線で画定される区画領域毎に独立して設けられてよい。このような回路基板は、多数個取り回路基板であってよい。このような多数個取り回路基板を分割すれば、複数の個片化基板（分割基板）を纏めて製造することができる。このような回路基板は、生産効率に優れる。
　本開示の一側面に係る回路基板の製造方法は、一方の主面の外縁の少なくとも一部に沿って凹部が形成されている一つ又は複数の金属板を準備する準備工程と、セラミック板の主面にろう材を塗布及び乾燥して一つ又は複数の塗布層を設ける塗布乾燥工程と、一つ又は複数の塗布層を挟むようにしてセラミック板と一つ又は複数の金属板とを積層して積層体を作製する積層工程と、積層体を加熱してセラミック板と一つ又は複数の金属板とが一つ又は複数のろう材層で接合された接合体を得る接合工程と、を有し、積層工程において、一つ又は複数の金属板の一方の主面とセラミック板の主面とが対向するようにセラミック板と一つ又は複数の金属板とを積層する。
　上記製造方法では、積層工程で、一つ又は複数の金属板の主面のうち凹部が形成されている方の主面と金属板とが対向するようにセラミック板と一つ又は複数の金属板とを積層している。このようにして得られる積層体を用いて接合工程を行っているため、ろう材が金属板の側面を這い上がり、金属板のセラミック板側とは反対側の主面にろう材が到達することを十分に抑制できる。このようにろう材の這い上がりが抑制された回路基板は、外観及び半導体素子等の外部回路との接続信頼性に優れる。
　上記製造方法の準備工程では凹部が形成されている複数の金属板を準備し、積層工程では、複数の金属板のそれぞれが、セラミック板の主面における区画線で画定される区画領域毎に独立するように複数の金属板を積層して積層体を作製し、接合工程の後に、接合体におけるセラミック板を区画線に沿って分割する分割工程を有してよい。
　このような接合工程で得られる接合体は、多数個取り回路基板ということもできる。分割工程において、このような多数個取り回路基板を分割すれば、複数の個片化基板（分割基板）を纏めて製造することができる。このような製造方法は、高い生産効率で回路基板（個片化基板）を製造することができる。
　本開示の一側面に係るパワーモジュールは、上述のいずれかの回路基板と、当該回路基板の金属板に電気的に接続される半導体素子と、を備える。このようなパワーモジュールは、上述のいずれかの回路基板を備えることから信頼性に優れる。
　ろう材の這い上がりを抑制することが可能な回路基板及びその製造方法を提供することができる。また、そのような回路基板を備えるパワーモジュールを提供することができる。
図１は、一実施形態に係る回路基板の斜視図である。 図２は、一実施形態に係る回路基板の平面図である。 図３は、図２の回路基板のＩＩＩ－ＩＩＩ線断面図である。 図４は、図３の断面の一部を拡大して示す断面図である。 図５は、回路基板の厚さ方向に沿う断面の一例を示す走査型電子顕微鏡（ＳＥＭ）の写真である。 図６は、パワーモジュールの断面図である。 図７は、比較例１の回路基板の厚さ方向に沿う断面を示す走査型電子顕微鏡（ＳＥＭ）の写真である。
　以下、場合により図面を参照して、本開示の実施形態を説明する。ただし、以下の実施形態は、本開示を説明するための例示であり、本開示を以下の内容に限定する趣旨ではない。説明において、同一要素又は同一機能を有する要素には同一符号を用い、場合により重複する説明は省略する。また、上下左右等の位置関係は、特に断らない限り、図面に示す位置関係に基づくものとする。更に、各要素の寸法比率は図示の比率に限られるものではない。なお、「～」の記号で示される数値範囲は、下限値及び上限値を含む。すなわち、「ｘ～ｙ」で示される数値範囲は、ｘ以上且つｙ以下を意味する。各実施形態における各数値範囲の上限又は下限をいずれかの実施例の数値で置き換えた数値範囲も本開示に含まれる。
　一実施形態に係る回路基板は、セラミック板と、金属板と、セラミック板の主面と金属板の主面とを接合するろう材層と、を備える。一枚のセラミック板の一方の主面に接合される金属板は、一つであってもよいし、複数であってもよい。セラミック板の材質は特に制限されず、例えば、窒化物焼結体、炭化物焼結体、又は酸化物焼結体で構成されていてよい。具体的には、窒化ケイ素焼結体、窒化アルミニウム焼結体、酸化アルミニウム焼結体、及び炭化ケイ素焼結体等が挙げられる。セラミック板の板状であれば特に制限されない。セラミック板の厚みは、例えば０．２～２ｍｍであってよく、０．３２～１．１ｍｍであってもよい。
　金属板は、例えば銅板であってよい。金属板の形状は、セラミック板の主面に対向する主面の外縁の少なくとも一部に沿って凹部が形成されていれば特に制限されない。金属板の厚み（主面間の距離）は、例えば０．１～１．２ｍｍであってよく、０．２～１．０ｍｍであってもよい。金属板は表面にめっき膜を有していてもよい。凹部は屈曲した壁面によって構成されていてよい。すなわち、金属板は、凹部に入隅部を有してよい。この入隅部は、金属板の側面における凹部の端縁と平行に延びていてよい。金属板がこのような凹部を備えることによって、ろう材が金属板のセラミック板側とは反対側の主面に這い上がることを十分に抑制することができる。
　ろう材層は、銀及び銅を含んでよく、さらに、錫、及び活性金属からなる群より選ばれる一種又は二種以上の金属を含有してよい。二種以上の金属は合金となっていてもよい。活性金属は、チタン、ハフニウム、ジルコニウム、及びニオブからなる群より選ばれる一種又は二種以上を含んでいてよい。ろう材層に含まれる銀及び銅は、例えばＡｇ－Ｃｕ共晶合金等の合金としてろう材層に含まれていてもよい。ろう材層における銀の含有量は、Ａｇ換算で４５～９５質量％であってよく、５０～９５質量％であってもよい。ろう材層における銀及び銅の合計含有量は、それぞれＡｇ及びＣｕに換算して６５～１００質量％であってよく、７０～９９質量％であってよく、９０～９８質量％であってもよい。これによって、ろう材層における残留応力を十分に低減しつつ、ろう材層の緻密性を向上することができる。
　ろう材層における活性金属の含有量は、Ａｇ及びＣｕの合計１００質量部に対して、０．５～８質量部であってよい。活性金属の含有量を０．５質量部以上とすることで、セラミック板とろう材層との接合性を向上することができる。一方、活性金属の含有量を８質量部以下とすることで、接合界面に脆弱な合金層が形成されることを抑制できる。
　ろう材層に含有される上記金属は、窒化物、酸化物、炭化物又は水素化物として含まれていてもよい。一例として、ろう材層は、窒化チタン及び／又は水素化チタン（ＴｉＨ２）を含んでいてよい。これによって、セラミック板と金属板との接合強度を十分に高くすることができる。ＡｇとＣｕの合計１００質量部に対するＴｉＨ２の含有量は例えば１～８質量部であってよい。
　図１は、本実施形態に係る回路基板の一例を示す斜視図である。図２は、図１の回路基板の平面図であり、図３は、図２のＩＩＩ－ＩＩＩ線断面図である。図１、図２及び図３に示すように、回路基板１００は、セラミック板１０と、セラミック板１０の主面１０Ａ及び主面１０Ｂ上に複数の金属板２０と、を備える。
　セラミック板１０は、平板形状を有する。セラミック板１０は主面１０Ａにおける区画線によって複数に区画されている。主面１０Ａには、区画線として、第１の方向に沿って延在し且つ等間隔で並ぶ複数の区画線Ｌ１と、第１の方向に直交する第２の方向に沿って延在し且つ等間隔で並ぶ複数の区画線Ｌ２と、が設けられている。区画線Ｌ１と区画線Ｌ２とは互いに直交している。
　区画線Ｌ１，Ｌ２は、例えば、複数の凹みが直線状に並んで構成されていてもよいし、線状に溝が形成されていてもよい。具体的には、レーザー光で形成されるスクライブラインであってよい。レーザー源としては、例えば、炭酸ガスレーザー及びＹＡＧレーザー等が挙げられる。このようなレーザー源からレーザー光を間欠的に照射することによってスクライブラインを形成することができる。なお、区画線Ｌ１，Ｌ２は、等間隔で並んでいなくてもよく、また、直交するものに限定されない。また、区画線Ｌ１，Ｌ２は、直線状ではなく、曲線状であってもよいし、折れ曲がっていてもよい。
　セラミック板１０は、区画線Ｌ１及び区画線Ｌ２によって画定される複数の区画領域５０を有する。複数の区画領域５０のそれぞれに、金属板２０が設けられている。複数の金属板２０は、それぞれ互いに独立している。回路基板１００は、集合基板とも称されるものであり、区画線Ｌ１，Ｌ２に沿って分割することができる。分割することによって複数の回路基板（個片化基板）を得ることができる。このように分割して得られる個片化基板も、本実施形態の回路基板の一例である。
　金属板２０の一方の主面２０Ａは外部に露出している。金属板２０の他方の主面２０Ｂとセラミック板１０の主面１０Ａ（主面１０Ｂ）は、ろう材層３０によって接合されている。金属板２０の主面２０Ｂ（ろう材層３０との接合面）の外縁に沿って、金属板２０には凹部２２が形成されている。このような凹部２２が形成された金属板２０は、主面２０Ｂの外側が階段状になるように切り欠かれたものであってよい。図２に示されるように、凹部２２は、金属板２０の主面２０Ｂにおける外縁の全周にわたって形成されている。すなわち、主面２０Ｂの外縁は凹部２２で形成されている。ただし、凹部２２を主面２０Ｂの外縁の全周にわたって設けることは必須ではない。変形例では、金属板２０の上に半導体素子が搭載される際に半田付けがなされる部分の近傍のみに、凹部２２を設けてもよい。また、複数の金属板２０の一部のみに凹部２２を設けてもよい。例えば、パワーモジュールの放熱板となる金属板２０には凹部２２を設けなくてもよい。
　図４は、図３に示す回路基板１００の断面の一部を拡大して示している。図３及び図４は、ともに、金属板２０の側面２０Ｃにおける凹部２２の端縁２７に直交し、金属板２０の厚さ方向に沿う断面を示している。このような断面で見たときに、凹部２２の幅Ｘは０．０５ｍｍ以上であってよく、０．２ｍｍ以上であってよく、０．４ｍｍ以上であってもよい。このように、幅Ｘが大きくなると、ろう材層３０から金属板２０の側面２０Ｃまでの距離が長くなる。したがって、主面２０Ａへのろう材の這い上がりを一層抑制することができる。
　一方、幅Ｘが大きくなり過ぎると、金属板２０とセラミック板１０との接合部が小さくなる傾向にある。また、回路基板１００を用いてパワーモジュールを作製したときに、凹部２２に樹脂が充填され難くなる傾向にある。このため、幅Ｘは、１０ｍｍ以下であってよく、５ｍｍ以下であってよく、３ｍｍ以下であってよく、１．３ｍｍ以下であってよく、１ｍｍ以下であってもよい。幅Ｘと同じ方向に沿って測定される金属板２０の主面２０Ａの長さに対する幅Ｘの比は、０．０００５～０．５であってよく、０．００１～０．３であってよく、０．００５～０．３であってもよい。主面２０Ａの上記長さは、例えば、５～１００ｍｍであってよく、１５～５０ｍｍであってもよい。金属板２０の外周全体にわたって凹部２２が形成されている場合、いずれの部分においても上記の比の範囲を満たすことが好ましい。
　上記断面で見たときに、凹部２２の高さＺは、０．０５ｍｍ以上であってよく、０．２ｍｍ以上であってよく、０．３ｍｍ以上であってもよい。このように、高さＺが大きくなると、ろう材層３０から金属板２０の側面２０Ｃまでの距離が長くなる。したがって、金属板２０の主面２０Ａへのろう材の這い上がりを一層抑制することができる。
　一方、高さＺが大きくなり過ぎると、回路基板１００を用いてパワーモジュールを作製したときに、凹部２２に樹脂が十分に充填されなくなる場合がある。このため、高さＺは、１．１ｍｍ以下であってよく、０．６ｍｍ以下であってよく、０．５ｍｍ以下であってもよい。金属板２０の厚みに対する高さＺの比は、０．０４～１．０であってよく、０．１～０．６であってもよい。
　ろう材の這い上がりの抑制しつつ、樹脂の充填を円滑にする観点から、幅Ｘに対する高さＺの比は、０．００１～２２であってよく、０．１～４であってよく、０．１５～３であってもよい。なお、幅Ｘは、図３及び図４に示す断面において、セラミック板１０の主面１０Ａ，主面１０Ｂに対して平行な方向に沿って測定される。高さＺは、図３及び図４に示す断面において、セラミック板１０の主面１０Ａ，主面１０Ｂに対して垂直な方向に沿って測定される。
　凹部２２を構成する金属板２０の壁面は、セラミック板１０の主面１０Ａ，主面１０Ｂと対向する対向面２４と、主面１０Ａ，主面１０Ｂに直交する立設面２３と、を含む。対向面２４と立設面２３との境界には、凹部２２の端縁２７と平行に入隅部２５が延在している。金属板２０は、凹部２２に対向面２４及び入隅部２５を有することによって、ろう材層３０からのろう材の這い上がりを一層抑制することができる。本例では、立設面２３が主面１０Ａ，主面１０Ｂに直交しているが、これに限定されない。例えば、対向面２４及び／又は立設面２３は、主面１０Ａ，主面１０Ｂに対して傾斜していてもよい。
　図４に示すような断面において凹部２２が矩形である場合の幅Ｘ及び高さＺは図４に示すとおりである。一方、凹部２２を構成する壁面が傾斜していたり、湾曲したりしている場合、幅Ｘ及び高さＺは、凹部２２の最も凹んだ部分に基づいて測定される。また、側面２０Ｃが曲がっている場合、幅Ｘは側面２０Ｃの最も外方に突出した部分を基準に測定される。すなわち、幅Ｘは、図４に示すような断面において、主面２０Ａと平行方向に測定される、側面２０Ｃと凹部を構成する壁面との距離の最大値として求めることができる。また、高さＺは、図４に示すような断面において、主面２０Ａと直交する方向に測定される、主面１０Ａ（主面１０Ｂ）と凹部２２を形成する壁面（対向面２４）との距離の最大値として求めることができる。
　図５は、回路基板の厚さ方向に沿う断面の一例を示すＳＥＭ写真である。図５は、図４と同様に、金属板２０の側面２０Ｃにおける凹部２２の端縁２７に直交し、金属板２０の厚さ方向に沿う断面の一部を拡大して示している。この例では、ろう材層３０の端部に這い上がり部３２が形成されている。這い上がり部３２は、入隅部２５の下方において略三角形状を呈している。這い上がり部３２は、凹部２２の内部において、セラミック板１０の主面１０Ａに近づくにつれて拡がる傾斜部３２Ａを有する。このような傾斜部３２Ａを有することによって、金属板２０の主面２０Ａへのろう材の這い上がりを一層抑制することができる。また、ろう材層３０による金属板２０とセラミック板１０との接合面積を大きくして、接合強度を高くすることができる。傾斜部３２Ａのサイズは、ろう材の組成、接合時の加熱温度及び加熱時間等を変えることによって調整することができる。
　回路基板１００は、必要に応じて分割して個片化された後、例えば、パワーモジュールに搭載されてもよい。金属板２０は、電気信号を伝達する機能を有する回路板、又は熱を伝達する機能を有する放熱板として機能してよい。また、金属板２０は、熱を伝達する機能と、電気信号を伝達する機能を兼ね備えていてもよい。回路基板１００及びこれを分割して得られる個片化基板（回路基板）は、金属板２０のセラミック板側とは反対側の主面２０Ａにおけるろう材の這い上がりが抑制されている。このため、外観及び半導体素子等の外部回路との接続信頼性に優れる。したがって、高い信頼性が求められるパワーモジュールに搭載される部品として好適である。
　一実施形態に係るパワーモジュールは、回路基板と、回路基板の金属板に電気的に接続される半導体素子と、を備える。回路基板は、上述の回路基板１００又はその変形例であってよいし、別の回路基板であってもよい。回路基板１００及びその変形例に関する説明内容は、本実施形態のパワーモジュールに適用される。このようなパワーモジュールは、信頼性に優れる。回路基板及び半導体素子は、樹脂によって封止されていてもよい。
　図６は、本実施形態に係るパワーモジュールの一例を示す断面図である。パワーモジュール３００は、ベース板７０と、ハンダ６２を介してベース板７０の一方面と接合される回路基板１０１とを備える。回路基板１０１の一方面側における金属板２１がハンダ６２を介してベース板７０と接合している。
　回路基板１０１の他方面側における金属板２０の少なくとも一つには、ハンダ６１を介して半導体素子６０が取り付けられている。半導体素子６０は、アルミワイヤ（アルミ線）等の金属ワイヤ６４で金属板２０の所定箇所に接続されている。このようにして、半導体素子６０と金属板２０とは電気的に接続されている。筐体６６の外部と金属板２０とを電気的に接続するため、金属板２０の一つである金属板２０ａは、ハンダ６５を介して筐体６６を貫通して設けられる電極６３に接続されている。
　ベース板７０の一方の主面上には、当該主面と一体になって回路基板１０１を収容する筐体６６が配置されている。ベース板７０の一方の主面と筐体６６とで形成される収容空間には樹脂８０が充填されている。樹脂８０は、回路基板１０１及び半導体素子６０を封止している。樹脂は、例えば、熱硬化型樹脂であってよく、光硬化型樹脂であってもよい。
　ベース板７０の他方の主面には、グリース７４を介して放熱部をなす冷却フィン７２が接合されている。ベース板７０の端部には冷却フィン７２をベース板７０に固定するネジ７３が取り付けられている。ベース板７０及び冷却フィン７２はアルミニウムで構成されていてもよい。ベース板７０及び冷却フィン７２は、高い熱伝導率を有することによって放熱部として良好に機能する。
　セラミック板１０によって、金属板２０と金属板２１は電気的に絶縁される。金属板２０（２０ａ）は電気回路を形成していてよい。金属板２０及び金属板２１は、ろう材層（不図示）によってセラミック板１０の主面１０Ａ及び主面１０Ｂにそれぞれ接合されている。金属板２０には、図１～図５に示すような凹部が形成されている。この凹部は、凹部２２と同様のサイズを有し、凹部を形成する金属板２０の壁面の少なくとも一部はろう材層で覆われていてよい。これによって、半導体素子６０が搭載される金属板２０の主面におけるろう材の這い上がりが十分に抑制されている。また、凹部に樹脂８０が十分に充填されている。したがって、パワーモジュール３００は、半導体素子６０と金属板２０との電気的な接続の信頼性に優れる。金属板２１にも、金属板２０と同様に凹部２２が形成されていてよい。
　一実施形態に係る回路基板の製造方法は、一方の主面の外縁に沿って凹部が形成されている一つ又は複数の金属板を準備する準備工程と、セラミック板の主面にろう材を塗布及び乾燥して一つ又は複数の塗布層を設ける塗布乾燥工程と、一つ又は複数の塗布層を挟むようにしてセラミック板と一つ又は複数の金属板とを積層して積層体を作製する積層工程と、積層体を加熱してセラミック板と一つ又は複数の金属板とが一つ又は複数のろう材層で接合された接合体を得る接合工程と、を有する。
　各工程の詳細について説明する。まず、一方の主面の外縁に沿って凹部が形成されている一つ又は複数の金属板を準備する。金属板は例えば銅板であってよい。凹部は、例えば、マシニングセンタを用いた機械加工で形成することができる。凹部のサイズ、すなわち幅Ｘ及び高さＺは上述したとおりであってよい。凹部は、金属板の主面の外縁の一部に形成してもよいし、金属板の主面の外縁を全周にわたって切削して形成してもよい。
　塗布乾燥工程で用いるセラミック板は、例えば以下の手順で作製できる。まず、無機化合物の粉末、バインダ樹脂、焼結助剤、可塑剤、分散剤、及び溶媒等を含むスラリーを成形してグリーンシートを作製する。無機化合物の例としては、窒化アルミニウム（ＡｌＮ）、窒化ケイ素（Ｓｉ３Ｎ４）、炭化ケイ素、及び酸化アルミニウム等が挙げられる。焼結助剤としては、希土類金属、アルカリ土類金属、金属酸化物、フッ化物、塩化物、硝酸塩、及び硫酸塩等が挙げられる。これらは一種のみ用いてもよいし二種以上を併用してもよい。焼結助剤を用いることにより、無機化合物粉末の焼結を促進させることができる。バインダ樹脂の例としては、メチルセルロース、エチルセルロース、ポリビニルアルコール、ポリビニルブチラール、及び（メタ）アクリル系樹脂等が挙げられる。
　可塑剤の例としては、精製グリセリン、グリセリントリオレート、ジエチレングリコール、ジ－ｎ－ブチルフタレート等のフタル酸系可塑剤、セバシン酸ジ－２－エチルヘキシル等の二塩基酸系可塑剤等が挙げられる。分散剤の例としては、ポリ（メタ）アクリル酸塩、及び（メタ）アクリル酸－マレイン酸塩コポリマーが挙げられる。溶媒の例としては、エタノール及びトルエン等の有機溶媒が挙げられる。
　グリーンシートの形成方法の例としては、ドクターブレード法及び押出成形法が挙げられる。次に、スラリーを成形して得られたグリーンシートを脱脂して焼結する。脱脂は、例えば、４００～８００℃で、０．５～２０時間加熱して行ってよい。これによって、無機化合物の酸化及び劣化を抑制しつつ、有機物（炭素）の残留量を低減することができる。焼結は、例えば窒素、アルゴン、アンモニア又は水素等の非酸化性ガス雰囲気下、１７００～１９００℃に加熱して行う。これによって、例えばセラミック板１０を得ることができる。必要に応じてセラミック板のレーザー加工を行い、端部を切断したり、スクライブラインを設けたりしてもよい。
　上述の脱脂及び焼結は、例えばグリーンシートを複数積層した状態で行ってもよい。積層して脱脂及び焼結を行う場合、焼結後の基材の分離を円滑にするため、グリーンシート間に離型剤による離型層を設けてよい。離型剤としては、例えば、窒化ホウ素（ＢＮ）を用いることができる。離型層は、例えば、窒化ホウ素の粉末のスラリーを、スプレー、ブラシ、ロールコート、又はスクリーン印刷等の方法により塗布して形成してよい。積層するグリーンシートの枚数は、セラミック板の量産を効率的に行いつつ、脱脂を十分に進行させる観点から、例えば８～１００枚であってよく、３０～７０枚であってもよい。
　セラミック板の一方の主面に複数の金属板を接合する場合、当該一方の主面に区画線を形成してもよい。例えば、セラミック板の主面にレーザー光を照射して、区画線としてスクライブラインを設けてもよい。セラミックの主面に照射するレーザー光としては、例えば、炭酸ガスレーザー及びＹＡＧレーザー等が挙げられる。このようなレーザー源からレーザー光を間欠的に照射することによって、図１及び図２に示すような区画線Ｌ１，Ｌ２となるスクライブラインを形成する。このような区画線Ｌ１，Ｌ２は、後工程において、回路基板を分割する際の切断線として利用することができる。
　セラミック板の主面に塗布するろう材は、例えば、銀、銅、錫、活性金属、及びこれらを構成元素とする金属化合物、有機溶媒、並びにバインダ等を含有する。ろう材の粘度は、例えば５～２０Ｐａ・ｓであってよい。ろう材における有機溶媒の含有量は、例えば、５～２５質量％、バインダ量の含有量は、例えば、２～１５質量％であってよい。
　ろう材は、金属単体又は金属化合物（合金）の形態で、銀を含んでよく、銀に加えて、銅、錫、及び活性金属からなる群より選ばれる一種又は二種以上の金属を含有してよい。二種以上の金属は合金となっていてもよい。活性金属は、チタン、ハフニウム、ジルコニウム、及びニオブからなる群より選ばれる一種又は二種以上を含んでいてよい。ろう材における銀の含有量は、Ａｇ換算で４５～９５質量％であってよく、５０～９５質量％であってもよい。ろう材における銀及び銅の合計含有量は、それぞれＡｇ及びＣｕに換算して６５～１００質量％であってよく、７０～９９質量％であってよく、９０～９８質量％であってもよい。これによって、後工程で形成されるろう材層における残留応力を十分に低減しつつ、ろう材層の緻密性を向上することができる。
　ろう材における活性金属の含有量は、Ａｇ及びＣｕの合計１００質量部に対して、０．５～８質量部であってよい。活性金属の含有量を０．５質量部以上とすることで、セラミック板とろう材との接合性を向上することができる。一方、活性金属の含有量を８質量部以下とすることで、接合界面に脆弱な合金層が形成されることを抑制できる。
　ろう材に含有される上記金属は、窒化物、酸化物、炭化物又は水素化物として含まれていてもよい。一例として、ろう材は、窒化チタン及び／又は水素化チタン（ＴｉＨ２）を含んでいてよい。これによって、セラミック板と金属板との接合強度を十分に高くすることができる。ＡｇとＣｕの合計１００質量部に対するＴｉＨ２の含有量は例えば１～８質量部であってよい。
　ろう材における錫の含有量は、Ａｇ及びＣｕの合計１００質量部に対して、０．５～５質量部であってよい。錫の含有量を０．５質量部以上とすることで、セラミック板とろう材との接合性を向上することができる。一方、錫の含有量を５質量部以下とすることで、接合界面に脆弱な合金層が形成されることを抑制できる。
　セラミック板の主面に、ロールコーター法、スクリーン印刷法、又は転写法等の方法によってろう材を塗布及び乾燥して一つ又は複数の塗布層を設ける。塗布層は、金属板が接合される位置に設ければよい。したがって、塗布層の数は、セラミック板に接合される金属板の数と同じであってよい。
　塗布層を形成したら、塗布層を挟むようにしてセラミック板と金属板とを積層して積層体を作製する。このとき、金属板の２つの主面のうち、凹部が形成されている方の主面とセラミック板の主面とが対向するようにして積層する。積層体を作製する際に、金属板をセラミック板に向かう方向に押圧してもよい。押圧に伴って、塗布層が拡がって、塗布層でセラミック板と金属板とが良好に接着された積層体が得られる。
　図１～図３に示すような回路基板１００を製造する場合、複数の金属板２０のそれぞれがセラミック板１０の主面１０Ａにおける区画線Ｌ１，Ｌ２で画定される区画領域５０毎に独立するように、複数の金属板２０を積層して積層体を作製する。
　得られた積層体を、加熱炉で加熱してセラミック板と金属板とがろう材層で接合された接合体を得る。加熱温度は例えば７００～９００℃であってよい。炉内の雰囲気は窒素等の不活性ガスであってよく、大気圧未満の減圧下で行ってもよいし、真空下で行ってもよい。加熱炉は、複数の接合体を連続的に製造する連続式のものであってもよいし、一つ又は複数の接合体をバッチ式で製造するものであってもよい。加熱は、接合体を上記積層体の積層方向に押圧しながら行ってもよい。
　積層体を加熱すると、塗布層に含まれるろう材は流動しつつ金属板と反応し、ろう材層が形成される。すなわち、ろう材層は、ろう材と金属板に含まれる金属成分との反応生成物を含んでよい。このとき、ろう材の一部が凹部を構成する金属板の壁面を這い上がって、図５に示すような這い上がり部３２が形成されてもよい。その後、金属板にめっき膜を形成する等の表面処理を行う。このとき、ろう材層の形状を整える切削加工等を行ってもよい。このようにして、回路基板を製造することができる。
　接合体が、図１～図３に示すようにセラミック板の一方の主面に複数の金属板を備える集合基板である場合、集合基板を分割して個片化する分割工程を行ってもよい。分割工程では、区画線Ｌ１，Ｌ２に沿って集合基板を分割し、複数の回路基板を得ることができる。
　上述の製造方法は、予め所定のサイズに加工された複数の金属板を接合して接合体を得ることができる。このような製造方法によれば、レジスト印刷工程及び金属板のエッチング工程を行うことなく、這い上がりが抑制された回路基板を効率よく製造することができる。このような製造方法で得られる回路基板は、製造コストが低減できるうえに、外観及び半導体素子等の外部回路との接続信頼性に優れる。ただし、上述の回路基板１００，１０１及びこれらの変形例の製造方法は、上述の製造方法に限定されない。
　このようにして得られた回路基板を用いて、パワーモジュールを製造してもよい。パワーモジュールは、回路基板に、ハンダとワイヤボンディング等を用いて半導体素子を搭載し、回路基板及び半導体素子を筐体の収容空間内に収容したうえで樹脂封止を行って製造することができる。
　以上、本開示の実施形態を説明したが、本開示は上記実施形態に何ら限定されるものではない。例えば、図１～図３の例では、セラミック板の一対の主面のそれぞれに複数の金属板を備えていたが、これに限定されない。例えば、一つ又は複数の金属板がセラミック板の一方の主面にのみ設けられていてもよい。セラミック板の一対の主面のそれぞれに設けられるろう材層及び金属板の構造及び形状は、互いに異なっていてもよい。また、セラミック板の一対の主面のそれぞれに一つの金属板が設けられていてもよい。また、凹部は、主面を取り囲むように設けられていなくてもよい。
　本開示は以下の実施形態を含む。
［１］セラミック板と、金属板と、前記セラミック板の主面と前記金属板の主面とを接合するろう材層と、を備える回路基板であって、
　前記金属板の前記主面の外縁の少なくとも一部に沿って前記金属板に凹部が形成されている、回路基板。
［２］前記金属板における前記凹部は、前記金属板の前記主面の外縁の全周にわたって形成されている、［１］に記載の回路基板。
［３］前記凹部を構成する前記金属板の壁面は、前記セラミック板の前記主面と対向する対向面を含む、［１］又は［２］に記載の回路基板。
［４］前記金属板の側面における前記凹部の端縁に直交し、前記金属板の厚さ方向に沿う断面で見たときに、
　前記凹部の幅Ｘが０．０５ｍｍ以上であり、前記凹部の高さＺが０．０５ｍｍ以上である、［１］～［３］のいずれか一つに記載の回路基板。
［５］前記金属板の側面における前記凹部の端縁に直交し、前記金属板の厚さ方向に沿う断面で見たときに、
　前記ろう材層は、前記凹部内において前記セラミック板の前記主面に近づくにつれて拡がる傾斜部を有する、［１］～［４］のいずれか一つに記載の回路基板。
［６］前記セラミック板と、複数の金属板と、前記セラミック板の前記主面と前記複数の金属板の主面のそれぞれとを接合する複数のろう材層と、を備え、
　前記複数の金属板が、前記凹部が形成されている前記金属板を含む、［１］～［５］のいずれか一つに記載の回路基板。
［７］一方の主面の外縁の少なくとも一部に沿って凹部が形成されている一つ又は複数の金属板を準備する準備工程と、
　セラミック板の主面にろう材を塗布及び乾燥して一つ又は複数の塗布層を設ける塗布乾燥工程と、
　前記一つ又は複数の塗布層を挟むようにして前記セラミック板と前記一つ又は複数の金属板とを積層して積層体を作製する積層工程と、
　前記積層体を加熱して前記セラミック板と前記一つ又は複数の金属板とが一つ又は複数のろう材層で接合された接合体を得る接合工程と、を有し、
　前記積層工程において、一つ又は複数の金属板の前記一方の主面と前記セラミック板の前記主面とが対向するように前記セラミック板と前記一つ又は複数の金属板とを積層する、回路基板の製造方法。
［８］前記準備工程では前記凹部が形成されている複数の金属板を準備し、
　前記積層工程では、前記複数の金属板のそれぞれが前記セラミック板の前記主面における区画線で画定される区画領域毎に独立するように前記複数の金属板を積層して前記積層体を作製し、
　前記接合工程の後に、前記接合体における前記セラミック板を前記区画線に沿って分割する分割工程を有する、［７］に記載の回路基板の製造方法。
［９］上記［１］～［６］のいずれか一項に記載の回路基板、又は上記［７］又は［８］に記載の製造方法で得られる回路基板と、当該回路基板の前記金属板に電気的に接続される半導体素子と、を備えるパワーモジュール。
　実施例及び比較例を参照して本開示の内容をより詳細に説明するが、本開示は下記の実施例に限定されるものではない。
（実施例１）
［回路基板の作製］
　窒化ケイ素製のセラミック板（厚さ：０．３２ｍｍ）、２４枚の銅板（材質：無酸素銅、サイズ：縦×横×厚さ＝１７ｍｍ×３８ｍｍ×０．８ｍｍ）及びろう材を準備した。機械加工によって、各金属板の一方の主面（主面２０Ｂ）の外縁部を全周にわたって切削して凹部を形成した。これによって、図１～図４に示す金属板２０と同様の形状を有する銅板を得た。
　Ａｇ、Ｃｕ、Ｓｎ、及びＴｉＨ２を含むろう材を準備した。ろう材におけるＡｇとＣｕの質量比は９：１であった。このろう材は、ＡｇとＣｕの合計１００質量に対し、Ｓｎを３質量部、及びＴｉＨ２を３．５質量部含んでいた。
　セラミック板の主面をスクライブラインによって２４個の区画領域に区画した。各区画に、スクリーン印刷でろう材を塗布して塗布層を形成した。塗布層の塗布面積は、セラミック板と接合される銅板の主面の面積と同じとした。塗布層を形成した後、セラミック板の上に、塗布層と銅板の当該主面とが接するようにして銅板を積層した。このようにして、セラミック板の一方の主面に、区画部毎に独立するように合計で２４個の銅板を積層した。
　セラミック板の主面上の銅板をセラミック板に向けて０．０１５ＭＰａでプレスして積層体を得た。その後、積層体を、真空中（１.０×１０－３Ｐａ）、７９０℃で１時間加熱した。このようにしてセラミック板の主面にろう材層を介して銅板が接合された接合体を得た。その後、Ｎｉ－Ｐめっき液（リン濃度：８～１２質量％）を用いて無電解メッキ処理を行い、銅板上にめっき膜を有する多数個取り回路基板を形成した。スクライブラインに沿って多数個取り回路基板を分割し、２４個の回路基板を得た。一つの回路基板のセラミック板のサイズは、縦×横×厚さ＝２０ｍｍ×４１ｍｍ×０．３２ｍｍであった。
［回路基板の評価］
＜這い上がりの評価＞
　回路基板における銅板の表面（セラミック板側の主面とは反対側の主面）を、ルーペ（倍率１０倍）を使用して目視観察を行い、ろう材の這い上がりの有無を判定した。銅板の主面に這い上がりが検知されなかったものを合格、銅板の主面に這い上がりが検知されたものを不合格と判定した。２４個の回路基板のうち、合格品の個数とその割合は表１に示すとおりであった。
＜凹部のサイズの測定＞
　金属板の側面における凹部の端縁に直交し、且つ銅板の厚さ方向に沿うように回路基板を切断し、図４に示すような断面を得た。この断面のＳＥＭ観察を行って、凹部の幅Ｘ及び高さＺを測定した。図５は実施例１の回路基板の断面のＳＥＭ写真である。測定結果は表１に示すとおりであった。測定は、１個の回路基板についてのみ行った。なお、２４個の銅板は、いずれも、同じ機械加工の条件で加工した。このため、凹部の幅Ｘ及び高さＺの値は同一とみなすことができる。
＜凹部への樹脂の充填性の評価＞
　エポキシ樹脂の主剤（日本メタロ株式会社、商品名：アカ・レジン）３０．８ｇと、エポキシ樹脂の硬化剤（日本メタロ株式会社、商品名：アカ・キュア）８．４ｇを予備混合した。これらを、セラミック回路が入っているφ：５０ｍｍのモールドカップに入れ、常温及び減圧（－１００ｋＰａ）の条件下、１分間真空脱気した。これによって、銅板の凹部にエポキシ樹脂を充填させた。常温及び大気圧下で４８時間静置した後に、セラミック回路基板を金属板の側面における凹部の端縁に直交し、銅板の厚さ方向に沿うように切断した。得られた切断面を、マイクロスコープ（倍率：２５０倍）で確認して、銅板の凹部への樹脂充填性を評価した。凹部の全体に樹脂が充填されていた場合を「Ａ」、凹部の一部のみに樹脂が充填されていたものを「Ｂ」とした。
（実施例２～８）
　機械加工による銅板の一方の主面における外縁部の切削量を変更して、銅板における凹部の幅Ｘ及び高さＺを表１に示すとおりに変更したこと以外は、実施例１と同様にして回路基板を作製した。そして、実施例１と同様にして回路基板の評価を行った。評価結果は表１に示すとおりであった。
（比較例１）
　銅板の機械加工を行わず、凹部を有しない銅板をセラミック板上に積層したこと以外は、実施例１と同様にして回路基板を作製した。そして、実施例１と同様にして回路基板の評価を行った。評価結果は表１に示すとおりであった。図７は比較例１の回路基板の断面のＳＥＭ写真である。図７に示されるように、ろう材層１３０を介して銅板１２０とセラミック板１１０が接合されていた。そして、セラミック板１１０側とは反対側の主面にまでろう材が到達していた。
Figure JPOXMLDOC01-appb-T000001
　表１に示すとおり、凹部を有する銅板を備える回路基板では、ろう材の這い上がりを十分に抑制できることが確認された。
　本開示によれば、ろう材の這い上がり現象を十分に抑制することが可能な回路基板及びその製造方法を提供することができる。また、信頼性に優れるパワーモジュールを提供することができる。
　１０，１１０…セラミック板、１０Ａ，１０Ｂ…主面、２０，２０ａ…金属板、２０Ａ…主面、２０Ｂ…主面、２０Ｃ…側面、２２…凹部、２３…立設面、２４…対向面、２５…入隅部、２７…端縁、３０，１３０…ろう材層、３２…這い上がり部、３２Ａ…傾斜部、５０…区画領域、６０…半導体素子、６１，６２，６５…ハンダ、６３…電極、６４…金属ワイヤ、６６…筐体、７０…ベース板、７２…冷却フィン、７３…ネジ、７４…グリース、８０…樹脂、１００，１０１…回路基板、１１０…セラミック板、１２０…銅板、３００…パワーモジュール、Ｌ１，Ｌ２…区画線。

 

Claims (9)

  1. 　セラミック板と、金属板と、前記セラミック板の主面と前記金属板の主面とを接合するろう材層と、を備える回路基板であって、
    　前記金属板の前記主面の外縁の少なくとも一部に沿って前記金属板に凹部が形成されている、回路基板。
  2. 　前記金属板における前記凹部は、前記金属板の前記主面の外縁の全周にわたって形成されている、請求項１に記載の回路基板。
  3. 　前記凹部を構成する前記金属板の壁面は、前記セラミック板の前記主面と対向する対向面を含む、請求項１に記載の回路基板。
  4. 　前記金属板の側面における前記凹部の端縁に直交し、前記金属板の厚さ方向に沿う断面で見たときに、
    　前記凹部の幅Ｘが０．０５ｍｍ以上であり、前記凹部の高さＺが０．０５ｍｍ以上である、請求項１に記載の回路基板。
  5. 　前記金属板の側面における前記凹部の端縁に直交し、前記金属板の厚さ方向に沿う断面で見たときに、
    　前記ろう材層は、前記凹部内において前記セラミック板の前記主面に近づくにつれて拡がる傾斜部を有する、請求項１に記載の回路基板。
  6. 　前記セラミック板と、複数の金属板と、前記セラミック板の前記主面と前記複数の金属板の主面のそれぞれとを接合する複数のろう材層と、を備え、
    　前記複数の金属板が、前記凹部が形成されている前記金属板を含む、請求項１に記載の回路基板。
  7. 　一方の主面の外縁の少なくとも一部に沿って凹部が形成されている一つ又は複数の金属板を準備する準備工程と、
    　セラミック板の主面にろう材を塗布及び乾燥して一つ又は複数の塗布層を設ける塗布乾燥工程と、
    　前記一つ又は複数の塗布層を挟むようにして前記セラミック板と前記一つ又は複数の金属板とを積層して積層体を作製する積層工程と、
    　前記積層体を加熱して前記セラミック板と前記一つ又は複数の金属板とが一つ又は複数のろう材層で接合された接合体を得る接合工程と、を有し、
    　前記積層工程において、一つ又は複数の金属板の前記一方の主面と前記セラミック板の前記主面とが対向するように前記セラミック板と前記一つ又は複数の金属板とを積層する、回路基板の製造方法。
  8. 　前記準備工程では前記凹部が形成されている複数の金属板を準備し、
    　前記積層工程では、前記複数の金属板のそれぞれが前記セラミック板の前記主面における区画線で画定される区画領域毎に独立するように前記複数の金属板を積層して前記積層体を作製し、
    　前記接合工程の後に、前記接合体における前記セラミック板を前記区画線に沿って分割する分割工程を有する、請求項７に記載の回路基板の製造方法。
  9. 　請求項１～６のいずれか一項に記載の回路基板と、当該回路基板の前記金属板に電気的に接続される半導体素子と、を備えるパワーモジュール。

     
PCT/JP2023/011999 2022-03-31 2023-03-24 回路基板及びその製造方法、並びにパワーモジュール WO2023190246A1 (ja)