WO2023117492A2 - Compositions de matériau d'électrode pour électrodes d'accumulateurs d'énergie présentant des capacités de charge et de décharge rapides - Google Patents

Compositions de matériau d'électrode pour électrodes d'accumulateurs d'énergie présentant des capacités de charge et de décharge rapides Download PDF

Info

Publication number
WO2023117492A2
WO2023117492A2 PCT/EP2022/085176 EP2022085176W WO2023117492A2 WO 2023117492 A2 WO2023117492 A2 WO 2023117492A2 EP 2022085176 W EP2022085176 W EP 2022085176W WO 2023117492 A2 WO2023117492 A2 WO 2023117492A2
Authority
WO
WIPO (PCT)
Prior art keywords
particles
electrode
active material
composition according
optionally
Prior art date
Application number
PCT/EP2022/085176
Other languages
English (en)
Other versions
WO2023117492A3 (fr
Original Assignee
Skeleton Technologies GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from DE102022100864.9A external-priority patent/DE102022100864A1/de
Application filed by Skeleton Technologies GmbH filed Critical Skeleton Technologies GmbH
Publication of WO2023117492A2 publication Critical patent/WO2023117492A2/fr
Publication of WO2023117492A3 publication Critical patent/WO2023117492A3/fr

Abstract

Une composition de matériau actif négatif pour une électrode négative (22) d'un accumulateur d'énergie (1) est constituée de 70 % en poids à 99 % en poids de matériau actif négatif ; de 1 % en poids à 10 % en poids d'au moins un liant ; éventuellement jusqu'à 10 % en poids au total d'au moins un additif conducteur ; et éventuellement moins de 10 % en poids au total d'autres constituants ou impuretés, le matériau actif négatif étant constitué de particules de Nb2O5 et de particules de carbone microporeux (MC). Une composition de matériau actif positif pour une électrode positive (32) d'un accumulateur d'énergie (1) est constituée de 0,5 % en poids à 10 % en poids de noir de carbone (CB) ; de 1 % en poids à 20 % en poids d'au moins un liant ; de 56 % en poids à 98,5 % en poids de matériau actif positif qui comprend, pour la plus grande partie, ou est constitué pour la plus grande partie, de particules de LiMn2O4 (LMO) ; d'éventuellement 0,1 % en poids à 2 % en poids de nanotubes de carbone (CNT) ; d'éventuellement 0,1 % en poids à 2 % en poids de graphène ; et d'éventuellement moins de 10 % en poids d'autres constituants ou impuretés.
PCT/EP2022/085176 2021-12-23 2022-12-09 Compositions de matériau d'électrode pour électrodes d'accumulateurs d'énergie présentant des capacités de charge et de décharge rapides WO2023117492A2 (fr)

Applications Claiming Priority (10)

Application Number Priority Date Filing Date Title
DE102021134642 2021-12-23
DE102021134640.1 2021-12-23
DE102021134643 2021-12-23
DE102021134640 2021-12-23
DE102021134642.8 2021-12-23
DE102021134643.6 2021-12-23
DE102021215133.7 2021-12-31
DE102021215133 2021-12-31
DE102022100864.9 2022-01-14
DE102022100864.9A DE102022100864A1 (de) 2021-12-23 2022-01-14 Elektrodenmaterialzusammensetzungen für Elektroden von Energiespeicherzellen mit schneller Lade- und Entladefähigkeit

Publications (2)

Publication Number Publication Date
WO2023117492A2 true WO2023117492A2 (fr) 2023-06-29
WO2023117492A3 WO2023117492A3 (fr) 2023-08-17

Family

ID=84767161

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2022/085176 WO2023117492A2 (fr) 2021-12-23 2022-12-09 Compositions de matériau d'électrode pour électrodes d'accumulateurs d'énergie présentant des capacités de charge et de décharge rapides

Country Status (1)

Country Link
WO (1) WO2023117492A2 (fr)

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5258245A (en) 1991-06-28 1993-11-02 Matsushita Electric Industrial Co., Ltd. Lithium rechargeable battery and method of making the same
JP2005158719A (ja) 2003-10-30 2005-06-16 Yuasa Corp リチウムイオン二次電池
JP2011150954A (ja) 2010-01-25 2011-08-04 Panasonic Corp コイン形有機電解液二次電池
DE102015121585A1 (de) 2014-12-12 2016-06-16 Ningbo Csr New Energy Technology Co., Ltd. Verfahren zur Herstellung einer Kathodenpaste für einen hybriden Kondensator
DE102018202929A1 (de) 2018-02-27 2019-08-29 Robert Bosch Gmbh Hybridsuperkondensator und Verfahren zur Herstellung eines Hybridsuperkondensators
US20210110979A1 (en) 2019-10-15 2021-04-15 GM Global Technology Operations LLC Ultra-high power hybrid cell design with uniform thermal distribution
US20210110980A1 (en) 2019-10-15 2021-04-15 GM Global Technology Operations LLC Voltage-modified hybrid electrochemical cell design
US20210218048A1 (en) 2020-01-15 2021-07-15 GM Global Technology Operations LLC Electrode overlaying configuration for batteries comprising bipolar components
WO2021193500A1 (fr) 2020-03-24 2021-09-30 株式会社Ｇｓユアサ Électrode positive pour élément de stockage d'énergie et élément de stockage d'énergie

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005222851A (ja) * 2004-02-06 2005-08-18 Sii Micro Parts Ltd 電極活物質及びこれを用いた電気化学セル
JPWO2016163282A1 (ja) * 2015-04-07 2018-03-22 日立化成株式会社 リチウムイオン二次電池
DE102016215070A1 (de) * 2016-08-12 2018-02-15 Bayerische Motoren Werke Aktiengesellschaft Elektrode für Festkörperzelle mit eingebettetem Leitfähigkeitszusatz
DE102016221172A1 (de) * 2016-10-27 2018-05-03 Robert Bosch Gmbh Optimierter Hybridsuperkondensator
US11037738B2 (en) * 2018-02-13 2021-06-15 Nanotek Instruments Group, Llc Hybrid supercapacitor containing a niobium composite metal oxide as an anode active material
CN110400920A (zh) * 2019-07-05 2019-11-01 联动天翼新能源有限公司 一种高能量密度长寿命电池及其制作方法
CN113036125A (zh) * 2019-12-24 2021-06-25 广州汽车集团股份有限公司 正极浆料、正极极片、锂离子电芯、锂离子电池包及应用

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5258245A (en) 1991-06-28 1993-11-02 Matsushita Electric Industrial Co., Ltd. Lithium rechargeable battery and method of making the same
JP2005158719A (ja) 2003-10-30 2005-06-16 Yuasa Corp リチウムイオン二次電池
JP2011150954A (ja) 2010-01-25 2011-08-04 Panasonic Corp コイン形有機電解液二次電池
DE102015121585A1 (de) 2014-12-12 2016-06-16 Ningbo Csr New Energy Technology Co., Ltd. Verfahren zur Herstellung einer Kathodenpaste für einen hybriden Kondensator
DE102018202929A1 (de) 2018-02-27 2019-08-29 Robert Bosch Gmbh Hybridsuperkondensator und Verfahren zur Herstellung eines Hybridsuperkondensators
US20210110979A1 (en) 2019-10-15 2021-04-15 GM Global Technology Operations LLC Ultra-high power hybrid cell design with uniform thermal distribution
US20210110980A1 (en) 2019-10-15 2021-04-15 GM Global Technology Operations LLC Voltage-modified hybrid electrochemical cell design
US20210218048A1 (en) 2020-01-15 2021-07-15 GM Global Technology Operations LLC Electrode overlaying configuration for batteries comprising bipolar components
WO2021193500A1 (fr) 2020-03-24 2021-09-30 株式会社Ｇｓユアサ Électrode positive pour élément de stockage d'énergie et élément de stockage d'énergie

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
THOMMES ET AL., PURE APPL. CHEM., vol. 87, no. 9-10, 2015, pages 1051 - 1069

Also Published As

Publication number Publication date
WO2023117492A3 (fr) 2023-08-17

Similar Documents

Publication Publication Date Title
EP2797142B1 (fr) Anode destinée à une batterie secondaire au lithium et batterie secondaire au lithium incluant ladite anode
JP4731967B2 (ja) リチウムイオンキャパシタ
JP4857073B2 (ja) リチウムイオンキャパシタ
JP4971729B2 (ja) リチウムイオンキャパシタ
Shi et al. Effect of the capacity design of activated carbon cathode on the electrochemical performance of lithium-ion capacitors
JP5228531B2 (ja) 蓄電デバイス
JPWO2006118120A1 (ja) 蓄電デバイス用負極活物質
US20110043968A1 (en) Hybrid super capacitor
KR101528121B1 (ko) 실리콘산화물-탄소 복합체, 이의 제조방법 및 이를 함유하는 에너지 저장소자
US20210028438A1 (en) Negative electrode active material for lithium secondary battery and lithium secondary battery comprising the same
WO2013152814A1 (fr) Batterie secondaire au sodium-ion, et matériau d'anode de batterie au sodium-ion
KR102530678B1 (ko) 리튬 이차전지용 음극활물질, 이를 포함하는 음극 및 리튬 이차전지
KR102647045B1 (ko) 리튬 이차 전지용 음극 활물질 및 이를 포함하는 이차전지
Ionica-Bousquet et al. Polyfluorinated boron cluster based salts: A new electrolyte for application in nonaqueous asymmetric AC/Li4Ti5O12 supercapacitors
JPH04162357A (ja) 非水系二次電池
JP4731974B2 (ja) リチウムイオンキャパシタ
KR101138481B1 (ko) 리튬이온 커패시터 및 리튬이온 커패시터 제조방법
JP2001345122A (ja) 二次電源及び二次電源の製造方法
JP4705404B2 (ja) リチウムイオンキャパシタ
WO2023117492A2 (fr) Compositions de matériau d'électrode pour électrodes d'accumulateurs d'énergie présentant des capacités de charge et de décharge rapides
EP4173068A1 (fr) Électrolyte amélioré pour cellule électrochimique
WO2023117488A1 (fr) Compositions d'électrolyte pour cellules de stockage d'énergie à capacités de charge et de décharge rapides
WO2023117491A1 (fr) Éléments de stockage d'énergie à capacités de charge et de décharge rapides
JP2011204828A (ja) リチウムイオンキャパシタ用非水電解液及びそれを備えたリチウムイオンキャパシタ
WO2023117490A1 (fr) Compositions de matériau d'électrode pour électrodes de piles d'accumulation d'énergie présentant des capacités de charge et de décharge rapides

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22834981

Country of ref document: EP

Kind code of ref document: A2