WO2023008452A1 - 酸化物半導体および半導体装置 - Google Patents

酸化物半導体および半導体装置 Download PDF

Info

Publication number
WO2023008452A1
WO2023008452A1 PCT/JP2022/028850 JP2022028850W WO2023008452A1 WO 2023008452 A1 WO2023008452 A1 WO 2023008452A1 JP 2022028850 W JP2022028850 W JP 2022028850W WO 2023008452 A1 WO2023008452 A1 WO 2023008452A1
Authority
WO
WIPO (PCT)
Prior art keywords
oxide semiconductor
layer
oxide
substrate
electrode
Prior art date
Application number
PCT/JP2022/028850
Other languages
English (en)
French (fr)
Inventor
健太郎 金子
倫史 高根
俊実 人羅
Original Assignee
株式会社Flosfia
国立大学法人京都大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社Flosfia, 国立大学法人京都大学 filed Critical 株式会社Flosfia
Priority to CN202280053287.7A priority Critical patent/CN117751435A/zh
Priority to JP2023538574A priority patent/JPWO2023008452A1/ja
Publication of WO2023008452A1 publication Critical patent/WO2023008452A1/ja

Abstract

電気特性に優れたゲルマニウム酸化物含有酸化物半導体を提供する。ドーパント元素を含有する原料溶液を霧化または液滴化し、得られた霧化液滴にキャリアガスを供給し、該キャリアガスでもって前記霧化液滴を前記基体上まで搬送し、ついで、前記基体上で前記霧化液滴を熱反応させることを特徴とする酸化物半導体の形成方法を用いて、ゲルマニウムの酸化物を含有する酸化物半導体膜であって、キャリア密度が１．０×１０１８／ｃｍ３以上であることを特徴とする酸化物半導体を得る。

Description

酸化物半導体および半導体装置
　本発明は、半導体装置に有用な酸化物半導体および該酸化物半導体を用いた半導体装置に関する。
　パワーデバイス等に有用なワイドバンドギャップ半導体として、酸化ゲルマニウムが注目されている。酸化ゲルマニウムはバンドギャップが４．４４ｅＶ～４．６８ｅＶといわれており（非特許文献１）、また、第１原理計算によればホール移動度が２７ｃｍ２／Ｖｓ（ｃ軸と垂直な方向）または２９ｃｍ２／Ｖｓと推定されており（非特許文献２）、ｐｎホモ接合の実現も期待されている。
　上記のような計算による推定ではなく、実際に酸化ゲルマニウムを作製することも検討されており、非特許文献３には、ＭＢＥ法を用いて、Ｒ面サファイア基板上に（Ｓｎ，Ｇｅ）Ｏ２バッファ層を介して酸化ゲルマニウムを成膜することが開示されている。しかしながら、酸化ゲルマニウム膜へのドーピングに成功した例は未だ無く、パワーデバイス等への適用に不可欠な、酸化ゲルマニウム膜へのドーピング技術が待ち望まれていた。
STAPELBROEK, M.; EVANS, B. D. Exciton structure in the uv-absorption edge of tetragonal GeO2. Solid State Communications, 1978, 25.11: 959-962. BUSHICK, Kyle, et al. Electron and hole mobility of rutile GeO2 from first principles: An ultrawide-bandgap semiconductor for power electronics. Applied Physics Letters, 2020, 117.18: 182104. CHAE, Sieun, et al. Epitaxial stabilization of rutile germanium oxide thin film by molecular beam epitaxy. Applied Physics Letters, 2020, 117.7: 072105.
　本発明は、電気特性に優れたゲルマニウムの酸化物を含有する酸化物半導体を提供することを目的とする。
　本発明者らは、上記目的を達成すべく鋭意検討した結果、ミストＣＶＤ法を用いて特定の条件下で酸化ゲルマニウムにドーピングを行うことにより、良好にドーピングされたキャリア密度１．０×１０１８／ｃｍ３以上のゲルマニウム酸化物含有酸化物半導体の創製に世界で初めて成功した。また、このような酸化物半導体が、上記した従来の問題を解決できるものであることを見出した。
　また、本発明者らは、上記知見を得た後、さらに検討を重ねて本発明を完成させるに至った。
　すなわち、本発明は、以下の発明に関する。
［１］　ゲルマニウムの酸化物を含有する酸化物半導体膜であって、キャリア密度が１．０×１０１８／ｃｍ３以上であることを特徴とする酸化物半導体。
［２］　前記酸化物半導体中の金属元素中におけるゲルマニウムの原子比が０．５より大きい前記［１］記載の酸化物半導体。
［３］　ｎ型の導電型を有する前記［１］または［２］に記載の酸化物半導体。
［４］　ドーパントを含有する前記［１］～［３］のいずれかに記載の酸化物半導体。
［５］　前記ドーパントが、周期律表第１５族金属を含む前記［４］記載の酸化物半導体。
［６］　前記ドーパントが、アンチモンである前記［４］または［５］に記載の酸化物半導体。
［７］　比抵抗が１０Ωｃｍ以下である前記［１］～［６］のいずれかに記載の酸化物半導体。
［８］　膜状である前記［１］～［７］のいずれかに記載の酸化物半導体。
［９］　前記［１］～［８］のいずれかに記載の酸化物半導体膜と、電極とを少なくとも備える半導体装置。
［１０］　前記［９］記載の半導体装置を用いた電力変換装置。
［１１］　前記［９］記載の半導体装置を用いた制御システム。
［１２］　基体上にドーピングされたゲルマニウムの酸化物を含有する酸化物半導体を製造する方法であって、ドーパント元素およびゲルマニウムを含有し、前記ドーパント元素よりもゲルマニウムの含有量が多い原料溶液を霧化または液滴化し、得られた霧化液滴にキャリアガスを供給し、該キャリアガスでもって前記霧化液滴を前記基体上まで搬送し、ついで、前記基体上で前記霧化液滴を熱反応させることを特徴とする酸化物半導体の製造方法。
　本発明の酸化物半導体は、電気特性に優れている。
本発明の実施態様で好適に用いられる成膜装置の概略構成図である。 実施例における電気特性の測定結果を示す図である。縦軸が電気抵抗率、横軸がＧｅに対するＳｂの原子比（％）を示す。 ショットキーバリアダイオード（ＳＢＤ）の好適な一例を模式的に示す図である。 ジャンクションバリアショットキーダイオード（ＪＢＳ）の好適な一例を模式的に示す図である。 金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）の好適な一例を模式的に示す図である。 金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）の好適な一例を模式的に示す図である。 絶縁ゲート型バイポーラトランジスタ（ＩＧＢＴ）の好適な一例を模式的に示す図である。 発光素子（ＬＥＤ）の好適な一例を模式的に示す図である。 本発明の実施態様にかかる半導体装置を採用した制御システムの一例を示すブロック構成図である。 本発明の実施態様にかかる半導体装置を採用した制御システムの一例を示す回路図である。 本発明の実施態様にかかる半導体装置を採用した制御システムの一例を示すブロック構成図である。 本発明の実施態様にかかる半導体装置を採用した制御システムの一例を示す回路図である。 高電子移動度トランジスタ（ＨＥＭＴ）の好適な一例を模式的に示す図である。 ガスセンサーの好適な一例を模式的に示す図である。 光電変換素子の好適な一例を模式的に示す図である。 受光素子の好適な一例を模式的に示す図である。 光電極の好適な一例を模式的に示す図である。
　本発明の酸化物半導体は、ゲルマニウムの酸化物を含有する酸化物半導体であって、キャリア密度が１．０×１０１８／ｃｍ３以上であることを特長とする。前記キャリア密度は、ホール効果測定にて測定されるキャリア密度をいう。前記キャリア密度の上限は、特に限定されないが、１．０×１０２３／ｃｍ３以下が好ましく、１．０×１０２２／ｃｍ３以下がより好ましい。また、前記酸化物半導体は、比抵抗（電気抵抗率）が１００Ωｃｍ以下であるのが好ましく、１０Ωｃｍ以下であるのがより好ましい。上記したような好ましい電気特性を有することにより、前記酸化物半導体を半導体装置に適用した場合に、半導体装置により良好な半導体特性を与えることができる。前記酸化物半導体は、結晶性を有していてもよいし、アモルファスであってもよい。前記酸化物半導体が結晶性を有する場合、前記酸化物半導体は、単結晶であってもよいし、多結晶であってもよい。前記酸化物半導体が結晶性を有する場合の結晶構造も、特に限定されない。前記結晶構造としては、六方晶または正方晶等が挙げられる。また、前記酸化物半導体の形状は、本発明の目的を阻害しない限り、特に限定されない。前記酸化物半導体は、膜状であってもよいし、板状であってもよいし、シート状であってもよい。本発明の実施態様においては、前記酸化物半導体が膜状であるのが、半導体装置により好適に適用可能となるので、好ましい。前記酸化物半導体が膜状である場合の膜厚は、特に限定されない。本発明の実施態様においては、前記膜厚が１００ｎｍ以上であるのが好ましい。このような好ましい膜厚とすることにより、前記酸化物半導体を半導体装置に適用した際により優れた耐圧性を前記半導体装置に付与することができる。
　前記酸化物半導体に含有されるゲルマニウムの酸化物は、酸素とゲルマニウムの化合物であれば、特に限定されない。本発明の実施態様においては、前記ゲルマニウムの酸化物を主成分として含むのがより好ましい。なお、ここで「主成分」とは、前記酸化物半導体中におけるゲルマニウムの酸化物（酸化ゲルマニウム）の含有量が、前記酸化物半導体中の組成比で５０％以上であることをいう。本発明の実施態様においては、前記酸化物半導体中のゲルマニウムの酸化物の含有量が、前記酸化物半導体中の組成比で７０％以上であるのが好ましく、９０％以上であるのがより好ましい。また、前記酸化物半導体は、ゲルマニウム以外の他の金属を含んでいてもよい。前記他の金属としては、例えば、ゲルマニウム以外の周期律表第１４族金属（スズまたはケイ素等）が挙げられる。前記酸化物半導体中の金属元素中のゲルマニウムの原子比は、特に限定されない。本発明の実施態様においては、前記酸化物半導体中の金属元素中のゲルマニウムの原子比が、０．５より大きいのが好ましく、０．７以上であるのがより好ましい。ゲルマニウムの原子比をこのような好ましい範囲とすることにより、より高いバンドギャップ（例えば４．０ｅＶ以上）を有する酸化物半導体を実現することができる。
　前記酸化物半導体は、ドーパントを含むのが好ましい。前記ドーパントは、本発明の目的を阻害しない限り、特に限定されない。前記ドーパントは、ｎ型ドーパントであってもよいし、ｐ型ドーパントであってもよい。前記ｎ型ドーパントとしては、例えば、アンチモン（Ｓｂ）、ヒ素（Ａｓ）、ビスマス（Ｂｉ）またはフッ素（Ｆ）等が挙げられる。本発明の実施態様においては、前記ｎ型ドーパントが、アンチモン（Ｓｂ）であるのが好ましい。前記ｐ型ドーパントとしては、例えば、アルミニウム（Ａｌ）、ガリウム（Ｇａ）またはインジウム（Ｉｎ）等が挙げられる。前記酸化物半導体中の前記ドーパントの含有量は、本発明の目的を阻害しない限り、特に限定されない。前記酸化物半導体中の前記ドーパントの含有量は、具体的には、例えば、約１×１０１６／ｃｍ３～１×１０２２／ｃｍ３であってもよいし、本発明によれば、ドーパントを約１×１０２０／ｃｍ３以上の高濃度で含有させてもよい。
　前記酸化物半導体は、例えば次の好適な製造方法により得ることができるが、このような酸化物半導体（以下、「酸化物結晶」または「結晶性酸化物膜」ともいう。）の製造方法も新規且つ有用であり、本発明の１つとして包含される。
　本発明の酸化物半導体の製造方法は、例えば、ドーパント元素およびゲルマニウムを含有し、前記ドーパント元素よりもゲルマニウムの含有量が多い原料溶液を霧化または液滴化し（霧化工程）、得られた霧化液滴にキャリアガスを供給し、該キャリアガスでもって前記霧化液滴を前記基体上まで搬送し（搬送工程）、ついで、前記基体上で前記霧化液滴を熱反応させる（製膜工程）ことを特長とする。
＜基体＞
　前記基体は、前記酸化物半導体を支持できるものであれば、特に限定されない。前記基体の材料も、本発明の目的を阻害しない限り、特に限定されず、公知の基体であってよい。前記基体は、有機化合物からなるものであってもよいし、無機化合物からなるものであってもよい。前記基体の形状も本発明の目的を阻害しない限り、特に限定されない。前記基体の形状としては、例えば、平板や円板等の板状、繊維状、棒状、円柱状、角柱状、筒状、螺旋状、球状、リング状などが挙げられるが、本発明においては、前記基体が基板であるのが好ましく、結晶基板であるのがより好ましい。前記基板の厚さは、特に限定されない。
＜結晶基板＞
　前記結晶基板は、本発明の目的を阻害しない限り特に限定されず、公知の基板であってよい。絶縁体基板であってもよいし、導電性基板であってもよいし、半導体基板であってもよい。単結晶基板であってもよいし、多結晶基板であってもよい。前記結晶基板が、表面に金属膜を有する基板であってもよい。なお、前記結晶基板が導電性基板である場合には、基板を除去することなく縦型デバイスを作製することができる。前記結晶基板の結晶構造も、本発明の目的を阻害しない限り、特に限定されない。前記結晶基板の結晶構造としては、例えば、六方晶構造、正方晶構造等が挙げられる。コランダム構造を有する結晶基板としては、例えばサファイア基板（Ｒ面サファイア基板等）等が挙げられる。正方晶構造を有する結晶基板としては、例えばＳｒＴｉＯ３基板、ＴｉＯ２基板、ＭｇＦ２基板等が挙げられる。本発明の実施態様においては、前記結晶基板が正方晶構造を有するのが好ましく、ルチル型構造を有するのが好ましい。ルチル型構造を有する結晶基板としては、例えば、ルチル型の酸化チタン（ｒ－ＴｉＯ２）基板等が挙げられる。ｒ－ＴｉＯ２基板は、例えばＮｂ等のドーパントを含む導電性基板であるのも好ましい。なお、前記結晶基板はオフ角を有していてもよい。また、本発明の実施態様においては、前記結晶基板としてＧｅ基板を用いるのも好ましい。
（霧化工程）
　霧化工程は、前記原料溶液を霧化する。霧化手段は、前記原料溶液を霧化できさえすれば特に限定されず、公知の手段であってよいが、本発明においては、超音波を用いる霧化手段が好ましい。超音波を用いて得られたミストは、初速度がゼロであり、空中に浮遊するので好ましく、例えば、スプレーのように吹き付けるのではなく、空間に浮遊してガスとして搬送することが可能なミストであるので衝突エネルギーによる損傷がないため、非常に好適である。ミストの液滴のサイズは、特に限定されず、数ｍｍ程度であってもよいが、好ましくは５０μｍ以下であり、より好ましくは１００ｎｍ～１０μｍである。
（原料溶液）
　前記原料溶液は、ドーパント元素およびゲルマニウムを含有し、前記ドーパント元素よりもゲルマニウムの含有量が多いものであれば、特に限定されない。前記原料溶液は無機材料を含んでいてもよいし、有機材料を含んでいてもよい。本発明の実施態様においては、前記原料溶液が、ゲルマニウムを有機ゲルマニウム化合物の形態で含有するのが好ましい。また、本発明の実施態様においては、前記有機ゲルマニウム化合物が、カルボキシ基を有するのが好ましい。前記原料溶液中のゲルマニウム原料（例えば、前記有機ゲルマニウム化合物等）の配合割合は、特に限定されないが、原料溶液全体に対して、０．０００１ｍｏｌ／Ｌ～２０ｍｏｌ／Ｌが好ましく、０．００１ｍｏｌ／Ｌ～１．０ｍｏｌ／Ｌであるのがより好ましい。前記ドーパント元素としては、例えば、アンチモン（Ｓｂ）、ヒ素（Ａｓ）、ビスマス（Ｂｉ）、フッ素（Ｆ）、アルミニウム（Ａｌ）、ガリウム（Ｇａ）またはインジウム（Ｉｎ）等が挙げられる。本発明の実施態様においては、前記ドーパント元素がアンチモン（Ｓｂ）であるのが好ましい。なお、前記ドーパント元素は、無機化合物の形態で前記原料溶液中に含まれていてもよいし、有機化合物の形態で前記原料溶液中にふくまれていてもよい。
　前記原料溶液の溶媒は、特に限定されず、水等の無機溶媒であってもよいし、アルコール等の有機溶媒であってもよいし、無機溶媒と有機溶媒の混合溶液であってもよい。本発明においては、前記溶媒が水を含むのが好ましく、水と酸の混合溶媒であるのも好ましい。前記水としては、より具体的には、例えば、純水、超純水、水道水、井戸水、鉱泉水、鉱水、温泉水、湧水、淡水、海水などが挙げられるが、本発明においては、超純水が好ましい。また、前記酸としては、より具体的には、例えば、酢酸、プロピオン酸、ブタン酸等の有機酸；三フッ化ホウ素、三フッ化ホウ素エーテラート、三塩化ホウ素、三臭化ホウ素、トリフルオロ酢酸、トリフルオロメタンスルホン酸、ｐ－トルエンスルホン酸などが挙げられる。
　また、前記原料溶液には、ハロゲン化水素酸や酸化剤等の添加剤を混合してもよい。前記ハロゲン化水素酸としては、例えば、臭化水素酸、塩酸、ヨウ化水素酸などが挙げられる。前記酸化剤としては、例えば、過酸化水素（Ｈ２Ｏ２）、過酸化ナトリウム（Ｎａ２Ｏ２）、過酸化バリウム（ＢａＯ２）、過酸化ベンゾイル（Ｃ６Ｈ５ＣＯ）２Ｏ２等の過酸化物、次亜塩素酸（ＨＣｌＯ）、過塩素酸、硝酸、オゾン水、過酢酸やニトロベンゼン等の有機過酸化物などが挙げられる。
（搬送工程）
　搬送工程では、前記霧化工程で得られた霧化液滴（以下、単に「ミスト」ともいう。）にキャリアガスを供給し、該キャリアガスによって前記ミストを基体へ搬送する。キャリアガスの種類としては、本発明の目的を阻害しない限り特に限定されず、例えば、酸素、オゾン、窒素やアルゴン等の不活性ガス、または水素ガスやフォーミングガス等の還元ガスなどが挙げられるが、本発明においては、キャリアガスとして酸素を用いるのが好ましい。酸素が用いられているキャリアガスとしては、例えば空気、酸素ガス、オゾンガス等が挙げられるが、とりわけ酸素ガス及び／又はオゾンガスが好ましい。また、キャリアガスの種類は１種類であってよいが、２種類以上であってもよく、キャリアガス濃度を変化させた希釈ガス（例えば１０倍希釈ガス等）などを、第２のキャリアガスとしてさらに用いてもよい。また、キャリアガスの供給箇所も１箇所だけでなく、２箇所以上あってもよい。本発明においては、霧化室、供給管及び製膜室を用いる場合には、前記霧化室及び前記供給管にそれぞれキャリアガスの供給箇所を設けるのが好ましく、前記霧化室にはキャリアガスの供給箇所を設け、前記供給管には希釈ガスの供給箇所を設けるのがより好ましい。また、キャリアガスの流量は、特に限定されないが、０．０１～２０Ｌ／分であるのが好ましく、１～１０Ｌ／分であるのがより好ましい。希釈ガスの場合には、希釈ガスの流量が、０．００１～２Ｌ／分であるのが好ましく、０．１～１Ｌ／分であるのがより好ましい。
（製膜工程）
　製膜工程では、前記霧化液滴を前記基体上で熱反応させて、前記基体表面の一部または全部に製膜する。前記熱反応は、前記ミストから膜が形成される熱反応であれば特に限定されず、熱でもって前記ミストが反応すればそれでよく、反応条件等も本発明の目的を阻害しない限り特に限定されない。本工程においては、前記熱反応を、通常、溶媒の蒸発温度以上の温度で行うが、あまり高すぎない温度以下が好ましい。本発明においては、前記熱反応を、７００℃～８００℃の温度で行うのが好ましい。また、熱反応は、本発明の目的を阻害しない限り、真空下、非酸素雰囲気下、還元ガス雰囲気下および酸化雰囲気下のいずれの雰囲気下で行われてもよく、また、大気圧下、加圧下および減圧下のいずれの条件下で行われてもよいが、本発明においては、酸化雰囲気下で行われるのが好ましく、大気圧下で行われるのも好ましく、酸化雰囲気下でかつ大気圧下で行われるのがより好ましい。なお、「酸化雰囲気」は、前記酸化物半導体が前記熱反応により形成できる雰囲気であれば特に限定されない。例えば、酸素を含むキャリアガスを用いたり、酸化剤を含む原料溶液からなるミストを用いたりして酸化雰囲気とすること等が挙げられる。また、膜厚は、製膜時間を調整することにより、設定することができる。
　本発明の実施態様においては、前記基体上にそのまま製膜してもよいが、前記基体上に、前記酸化物半導体とは異なる層（例えば、ｎ型半導体層、ｎ＋型半導体層、ｎ－型半導体層等）や絶縁体層（半絶縁体層も含む）、バッファ層等の他の層を積層したのち、前記基体上に前記他の層を介して製膜してもよい。特に、前記結晶基板と前記酸化物半導体との格子定数差を緩和するために、バッファ層を好適に用いることができる。前記バッファ層の構成材料としては、例えば、ＳｎＯ２、ＴｉＯ２、ＶＯ２，ＭｎＯ２、ＲｕＯ２、ＣｓＯ２、ＩｒＯ２、ＧｅＯ２、ＣｕＯ２、ＰｂＯ２、ＡｇＯ２、ＣｒＯ２、ＳｉＯ２およびこれらの混晶等が挙げられる。
　上記のようにして得られる前記酸化物半導体は、半導体装置、特にパワーデバイスに有用であり、前記酸化物半導体と電極とを少なくとも備える半導体装置として好適に用いられる。前記酸化物半導体を用いて形成される半導体装置としては、ＭＩＳやＨＥＭＴ等のトランジスタやＴＦＴ、半導体‐金属接合を利用したショットキーバリアダイオード、ＪＢＳ、他のＰ層と組み合わせたＰＮ又はＰＩＮダイオード、受発光素子などが挙げられる。なお、本発明においては、上記した以外にも、前記酸化物半導体を光電変換素子、ガスセンサー、光電極、メモリー等に好適に用いることができる。本発明の実施態様においては、前記酸化物半導体を、所望により前記結晶基板を除去して、前記酸化物半導体として半導体装置に用いてもよいし、前記結晶基板との結晶性積層構造体として半導体装置に用いてもよい。特に前記結晶基板が導電性基板である場合には、前記結晶性積層構造体として好適に半導体装置（縦型デバイス）に適用することができる。
　また、前記半導体装置は、電極が半導体層の片面側に形成された横型の素子（横型デバイス）と、半導体層の表裏両面側にそれぞれ電極を有する縦型の素子（縦型デバイス）のいずれにも好適に用いられるが、本発明の実施態様においては、中でも、縦型デバイスに用いることが好ましい。前記半導体装置の好適な例としては、例えば、ショットキーバリアダイオード（ＳＢＤ）、ジャンクションバリアショットキーダイオード（ＪＢＳ）、金属半導体電界効果トランジスタ（ＭＥＳＦＥＴ）、高電子移動度トランジスタ（ＨＥＭＴ）、金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）、静電誘導トランジスタ（ＳＩＴ）、接合電界効果トランジスタ（ＪＦＥＴ）、絶縁ゲート型バイポーラトランジスタ（ＩＧＢＴ）または発光ダイオード（ＬＥＤ）などが挙げられる。
　以下、本発明の酸化物半導体をｎ型半導体層（ｎ＋型半導体やｎ－半導体層等）に適用した場合の前記半導体装置の好適な例を、図面を用いて説明するが、本発明は、これらの例に限定されるものではない。
（ＳＢＤ）
　図３は、本発明の実施態様に係るショットキーバリアダイオード（ＳＢＤ）の一例を示している。図３のＳＢＤは、ｎ－型半導体層１０１ａ、ｎ＋型半導体層１０１ｂ、ショットキー電極１０５ａおよびオーミック電極１０５ｂを備えている。
　ショットキー電極およびオーミック電極の材料は、公知の電極材料であってもよく、前記電極材料としては、例えば、Ａｌ、Ｍｏ、Ｃｏ、Ｚｒ、Ｓｎ、Ｎｂ、Ｆｅ、Ｃｒ、Ｔａ、Ｔｉ、Ａｕ、Ｐｔ、Ｖ、Ｍｎ、Ｎｉ、Ｃｕ、Ｈｆ、Ｗ、Ｉｒ、Ｚｎ、Ｉｎ、Ｐｄ、ＮｄもしくはＡｇ等の金属またはこれらの合金、酸化錫、酸化亜鉛、酸化レニウム、酸化インジウム、酸化インジウム錫（ＩＴＯ）、酸化亜鉛インジウム（ＩＺＯ）等の金属酸化物導電膜、ポリアニリン、ポリチオフェン又はポリピロ－ルなどの有機導電性化合物、またはこれらの混合物並びに積層体などが挙げられる。
　ショットキー電極およびオーミック電極の形成は、例えば、真空蒸着法またはスパッタリング法などの公知の手段により行うことができる。より具体的に例えば、前記金属のうち２種類の第１の金属と第２の金属とを用いてショットキー電極を形成する場合、第１の金属からなる層と第２の金属からなる層を積層させ、第１の金属からなる層および第２の金属からなる層に対して、フォトリソグラフィの手法を利用したパターニングを施すことにより行うことができる。
　図３のＳＢＤに逆バイアスが印加された場合には、空乏層（図示せず）がｎ型半導体層１０１ａの中に広がるため、高耐圧のＳＢＤとなる。また、順バイアスが印加された場合には、オーミック電極１０５ｂからショットキー電極１０５ａへ電子が流れる。このようにして前記半導体構造を用いたＳＢＤは、高耐圧・大電流用に優れており、スイッチング速度も速く、耐圧性・信頼性にも優れている。
（ＪＢＳ）
　図４は、本発明の好適な実施態様の一つであるジャンクションバリアショットキーダイオード（ＪＢＳ）を示す。図４の半導体装置は、ｎ＋型半導体層４と、前記ｎ型半導体層上積層されたｎ－型半導体層３と、前記ｎ－型半導体層上に設けられておりかつ前記ｉ型半導体層上との間にショットキーバリアを形成可能なショットキー電極２と、ショットキー電極２とｎ－型半導体層３との間に設けられているｐ型半導体層１とを含んでいる。なお、ｐ型半導体層１はｎ－型半導体層３に埋め込まれている。本発明においては、前記ｐ型半導体層が一定間隔ごとに設けられているのが好ましく、前記ショットキー電極の両端と前記ｎ－型半導体層との間に、前記ｐ型半導体層がそれぞれ設けられているのがより好ましい。このような好ましい態様により、熱安定性および密着性により優れ、リーク電流がより軽減され、さらに、より耐圧等の半導体特性に優れるようにＪＢＳが構成されている。なお、図４の半導体装置は、ｎ＋型半導体層４上にオーミック電極５を備えている。
　図４の半導体装置の各層の形成手段は、本発明の目的を阻害しない限り特に限定されず、公知の手段であってよい。例えば、真空蒸着法やＣＶＤ法、スパッタ法、各種コーティング技術等により成膜した後、フォトリソグラフィー法によりパターニングする手段、または印刷技術などを用いて直接パターニングを行う手段などが挙げられる。
（ＭＯＳＦＥＴ）
　本発明の半導体装置がＭＯＳＦＥＴである場合の一例を図５に示す。図５のＭＯＳＦＥＴは、トレンチ型のＭＯＳＦＥＴであり、ｎ－型半導体層１３１ａ、ｎ＋型半導体層１３１ｂ及び１３１ｃ、ゲート絶縁膜１３４、ゲート電極１３５ａ、ソース電極１３５ｂおよびドレイン電極１３５ｃを備えている。
　ドレイン電極１３５ｃ上には、例えば厚さ１００ｎｍ～１００μｍのｎ＋型半導体層１３１ｂが形成されており、前記ｎ＋型半導体層１３１ｂ上には、例えば厚さ１００ｎｍ～１００μｍのｎ－型半導体層１３１ａが形成されている。そして、さらに、前記ｎ－型半導体層１３１ａ上には、ｎ＋型半導体層１３１ｃが形成されており、前記ｎ＋型半導体層１３１ｃ上には、ソース電極１３５ｂが形成されている。
　また、前記ｎ－型半導体層１３１ａ及び前記ｎ＋型半導体層１３１ｃ内には、前記ｎ＋半導体層１３１ｃを貫通し、前記ｎ－型半導体層１３１ａの途中まで達する深さの複数のトレンチ溝が形成されている。前記トレンチ溝内には、例えば、１０ｎｍ～１μｍの厚みのゲート絶縁膜１３４を介してゲート電極１３５ａが埋め込み形成されている。
　図５のＭＯＳＦＥＴのオン状態では、前記ソース電極１３５ｂと前記ドレイン電極１３５ｃとの間に電圧を印可し、前記ゲート電極１３５ａに前記ソース電極１３５ｂに対して正の電圧を与えると、前記ｎ－型半導体層１３１ａの側面にチャネル層が形成され、電子が前記ｎ－型半導体層１３１ａに注入され、ターンオンする。オフ状態は、前記ゲート電極の電圧を０Ｖにすることにより、チャネル層ができなくなり、ｎ－型半導体層１３１ａが空乏層で満たされた状態になり、ターンオフとなる。
（ＨＥＭＴ）
　　図１３は、本発明の実施態様に係る高電子移動度トランジスタ（ＨＥＭＴ）の一例を示している。図１３のＨＥＭＴは、バンドギャップの広いｎ型半導体層１２１ａ、バンドギャップの狭いｎ型半導体層１２１ｂ、ｎ＋型半導体層１２１ｃ、半絶縁体層１２４、緩衝層１２８、ゲート電極１２５ａ、ソース電極１２５ｂおよびドレイン電極１２５ｃを備えている。本発明の実施態様においては、例えば、バンドギャップの広いｎ型半導体層１２１ａに前記酸化物半導体を用い、前記バンドギャップの狭いｎ型半導体層１２１ｂにＧｅを用いるのも好ましい。
　上記例では、ｐ型半導体を使用していない例を示したが、本発明の実施態様においては、これに限定されず、ｐ型半導体を用いてもよい。ｐ型半導体を用いた例を図６～図８および図１４～図１７に示す。これらの半導体装置は、上記例と同様にして製造することができる。なお、ｐ型半導体は、ｎ型半導体と同じ材料であって、ｐ型ドーパントを含むものであるのが好ましい。
（ＭＯＳＦＥＴ）
　図６は、ｎ－型半導体層１３１ａ、第１のｎ＋型半導体層１３１ｂ、第２のｎ＋型半導体層１３１ｃ、ｐ型半導体層１３２、ｐ＋型半導体層１３２ａ、ゲート絶縁膜１３４、ゲート電極１３５ａ、ソース電極１３５ｂおよびドレイン電極１３５ｃを備えている金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）の好適な一例を示す。なお、ｐ＋型半導体層１３２ａは、ｐ型半導体層であってもよく、ｐ型半導体層１３２と同じであってもよい。
（ＩＧＢＴ）
　図７は、ｎ型半導体層１５１、ｎ－型半導体層１５１ａ、ｎ＋型半導体層１５１ｂ、ｐ型半導体層１５２、ゲート絶縁膜１５４、ゲート電極１５５ａ、エミッタ電極１５５ｂおよびコレクタ電極１５５ｃを備えている絶縁ゲート型バイポーラトランジスタ（ＩＧＢＴ）の好適な一例を示す。
（ＬＥＤ）
　本発明の実施態様にかかる半導体装置が発光ダイオード（ＬＥＤ）である場合の一例を図８に示す。図８の半導体発光素子は、第２の電極１６５ｂ上にｎ型半導体層１６１を備えており、ｎ型半導体層１６１上には、発光層１６３が積層されている。そして、発光層１６３上には、ｐ型半導体層１６２が積層されている。ｐ型半導体層１６２上には、発光層１６３が発生する光を透過する透光性電極１６７を備えており、透光性電極１６７上には、第１の電極１６５ａが積層されている。なお、図８の半導体発光素子は、電極部分を除いて保護層で覆われていてもよい。
　透光性電極の材料としては、インジウム（Ｉｎ）またはチタン（Ｔｉ）を含む酸化物の導電性材料などが挙げられる。より具体的には、例えば、Ｉｎ２Ｏ３、ＺｎＯ、ＳｎＯ２、Ｇａ２Ｏ３、ＴｉＯ２、ＣｅＯ２またはこれらの２以上の混晶またはこれらにドーピングされたものなどが挙げられる。これらの材料を、スパッタリング等の公知の手段で設けることによって、透光性電極を形成できる。また、透光性電極を形成した後に、透光性電極の透明化を目的とした熱アニールを施してもよい。
　図８の半導体発光素子によれば、第１の電極１６５ａを正極、第２の電極１６５ｂを負極とし、両者を介してｐ型半導体層１６２、発光層１６３およびｎ型半導体層１６１に電流を流すことで、発光層１６３が発光するようになっている。
　第１の電極１６５ａ及び第２の電極１６５ｂの材料としては、例えば、Ａｌ、Ｍｏ、Ｃｏ、Ｚｒ、Ｓｎ、Ｎｂ、Ｆｅ、Ｃｒ、Ｔａ、Ｔｉ、Ａｕ、Ｐｔ、Ｖ、Ｍｎ、Ｎｉ、Ｃｕ、Ｈｆ、Ｗ、Ｉｒ、Ｚｎ、Ｉｎ、Ｐｄ、ＮｄもしくはＡｇ等の金属またはこれらの合金、酸化錫、酸化亜鉛、酸化インジウム、酸化インジウム錫（ＩＴＯ）、酸化亜鉛インジウム（ＩＺＯ）等の金属酸化物導電膜、ポリアニリン、ポリチオフェン又はポリピロ－ルなどの有機導電性化合物、またはこれらの混合物などが挙げられる。電極の形成法は特に限定されることはなく、印刷方式、スプレー法、コ－ティング方式等の湿式方式、真空蒸着法、スパッタリング法、イオンプレ－ティング法等の物理的方式、ＣＶＤ、プラズマＣＶＤ法等の化学的方式などの中から前記材料との適性を考慮して適宜選択した方法に従って前記基板上に形成することができる。
（ガスセンサー）
　図１４は、本発明の実施態様に係るガスセンサーの一例を示している。図１４のガスセンサーは、第１の層１１、第２の層１２、第１の電極１３および第２の電極１４を備えている。第１の層および第２の層は、ｎ型半導体層であってもよいし、ｐ型半導体層であってもよい。第２の層の仕事関数は、第１の層の仕事関数よりも小さい。前記第２の層と前記第１の電極とは、ショットキー接合を形成しているのが好ましい。前記第１の層と前記第２の電極とは、ショットキー接合しているのが好ましい。前記第１および第２の電極の材料は、特に限定されない。前記第１および第２の電極の材料としては、例えば、金、銀、白金等が挙げられる。前記第１の層および／または前記第２の層に本発明の酸化物半導体を用いることにより、より高感度のガスセンサーを実現することができる。
（光電変換素子）
　図１５は、本発明の実施態様に係る光電変換素子の一例を示している。図１５（ａ）の光電変換素子は、下部電極として機能する導電性膜５１と、電子ブロッキング層５６ａと光電変換層５２と、上部電極として機能する透明導電性膜５５とがこの順に積層された構造を有している。図１５（ｂ）の光電変換素子は、下部電極５１上に、電子ブロッキング層５６ａと、光電変換層５２と、正孔ブロッキング層５６ｂと、上部電極５５とがこの順に積層された構成を有する。図１５（ｂ）中の電子ブロッキング層５６（ａ）、光電変換層５２および正孔ブロッキング層１６ｂの積層順は、用途および特性に応じて適宜変更してもよい。本発明の酸化物半導体は、例えば、光電変換層５２、電子ブロッキング層５６ａまたは正孔ブロッキング層５６ｂ等に用いられてもよい。図１５の光電変換素子では、上部電極５５を介して光電変換層５２に光が入射されることが好ましい。このような光電変換素子は、光センサ用途および撮像素子用途に好適に適用できる。
（受光素子）
　図１６は、本発明の実施態様に係る受光素子の一例を示している。図１６の受光素子は、下部電極４０、高濃度ｎ型層４１、低濃度ｎ型層４２、高濃度ｐ型層４３、ショットキー電極４４、上部電極４５、および特定領域４６を備える。下部電極４０、ショットキー電極４４および上部電極４５の材料は、公知の電極材料（例えば、Ａｕ，Ｎｉ，Ｐｂ、Ｒｈ、Ｃｏ、Ｒｅ、Ｔｅ、Ｉｒ、Ｐｔ、Ｓｅ等）であってよい。また、特定領域４６は、例えば、高濃度ｎ型領域である。本発明の実施態様においては、前記酸化物半導体を、前記高濃度ｎ型層４１、低濃度ｎ型層４２、高濃度ｐ型層４３、および特定領域４６等に好適に用いることができる。図１６の受光素子によれば、上部電極４５の窓部からアイセーフ帯光が入射され、光がショットキー電極４４で自由電子吸収されると、低濃度ｎ型層４２側に電子が放出され、この放出された電子を特定領域４６の先端部近傍の高電界領域で加速することができる。
（光電極）
　図１７は、本発明の実施態様に係る光電極の一例を示している。図１７の光電極は、基板３１と、基板３１上に設けられた導電体層（電子伝導層）３２と、導電体層３２上に設けられた光触媒層（光吸収層）３３とを備える。基板３１としては、例えばガラス基板やサファイア基板等を用いることができる。本発明の実施態様においては、基板３１として、上記した結晶基板等を用いてもよい。前記導電体層３２の厚さは、特に限定されないが、１０ｎｍ～１５０ｎｍがっ好ましい。前記光触媒層３３の厚さは、特に限定されないが、１００ｎｍ以上であるのが好ましい。また、光触媒層３３がｎ型半導体からなる場合は、真空準位と導電体層３２のフェルミ準位とのエネルギー差が、真空準位と光触媒層３３のフェルミ準位とのエネルギー差よりも小さくなるように光触媒層３３と導電体層３２との材料の組合せを決定することが好ましい。また、光触媒層３３がｐ型半導体からなる場合は、真空準位と導電体層３２のフェルミ準位とのエネルギー差が、真空準位と光触媒層３３のフェルミ準位とのエネルギー差よりも大きくなるように、光触媒層３３とで導電体層３２との材料の組合せを決定するのが好ましい。本発明の実施態様においては、前記酸化物半導体を、前記導電体層３２および／または光触媒層３１に好適に用いることができる。図１７の光電極は、例えば、光電気化学セル等に好適に用いられる。
　上述した本発明の結晶性酸化物膜もしくは半導体装置は、上記した機能を発揮させるべく、インバータやコンバータなどの電力変換装置に適用することができる。より具体的には、インバータやコンバータに内蔵されるダイオードや、スイッチング素子であるサイリスタ、パワートランジスタ、ＩＧＢＴ（Ｉｎｓｕｌａｔｅｄ　Ｇａｔｅ　Ｂｉｐｏｌａｒ　Ｔｒａｎｓｉｓｔｏｒ）、ＭＯＳＦＥＴ（Ｍｅｔａｌ－Ｏｘｉｄｅ－Ｓｅｍｉｃｏｎｄｕｃｔｏｒ　Ｆｉｅｌｄ　Ｅｆｆｅｃｔ　Ｔｒａｎｓｉｓｔｏｒ）等として適用することができる。図９は、本発明の実施態様に係る半導体装置を用いた制御システムの一例を示すブロック構成図、図１０は同制御システムの回路図であり、特に電気自動車（Ｅｌｅｃｔｒｉｃ　Ｖｅｈｉｃｌｅ）への搭載に適した制御システムである。
　図９に示すように、制御システム５００はバッテリー（電源）５０１、昇圧コンバータ５０２、降圧コンバータ５０３、インバータ５０４、モータ（駆動対象）５０５、駆動制御部５０６を有し、これらは電気自動車に搭載されてなる。バッテリー５０１は例えばニッケル水素電池やリチウムイオン電池などの蓄電池からなり、給電ステーションでの充電あるいは減速時の回生エネルギーなどにより電力を貯蔵するとともに、電気自動車の走行系や電装系の動作に必要となる直流電圧を出力することができる。昇圧コンバータ５０２は例えばチョッパ回路を搭載した電圧変換装置であり、バッテリー５０１から供給される例えば２００Ｖの直流電圧を、チョッパ回路のスイッチング動作により例えば６５０Ｖに昇圧して、モータなどの走行系に出力することができる。降圧コンバータ５０３も同様にチョッパ回路を搭載した電圧変換装置であるが、バッテリー５０１から供給される例えば２００Ｖの直流電圧を、例えば１２Ｖ程度に降圧することで、パワーウインドーやパワーステアリング、あるいは車載の電気機器などを含む電装系に出力することができる。
　インバータ５０４は、昇圧コンバータ５０２から供給される直流電圧をスイッチング動作により三相の交流電圧に変換してモータ５０５に出力する。モータ５０５は電気自動車の走行系を構成する三相交流モータであり、インバータ５０４から出力される三相の交流電圧によって回転駆動され、その回転駆動力を図示しないトランスミッション等を介して電気自動車の車輪に伝達する。
　一方、図示しない各種センサを用いて、走行中の電気自動車から車輪の回転数やトルク、アクセルペダルの踏み込み量（アクセル量）などの実測値が計測され、これらの計測信号が駆動制御部５０６に入力される。また同時に、インバータ５０４の出力電圧値も駆動制御部５０６に入力される。駆動制御部５０６はＣＰＵ（Ｃｅｎｔｒａｌ　Ｐｒｏｃｅｓｓｉｎｇ　Ｕｎｉｔ）などの演算部やメモリなどのデータ保存部を備えたコントローラの機能を有するもので、入力された計測信号を用いて制御信号を生成してインバータ５０４にフィードバック信号として出力することで、スイッチング素子によるスイッチング動作を制御する。これによって、インバータ５０４がモータ５０５に与える交流電圧が瞬時に補正されることで、電気自動車の運転制御を正確に実行させることができ、電気自動車の安全・快適な動作が実現する。なお、駆動制御部５０６からのフィードバック信号を昇圧コンバータ５０２に与えることで、インバータ５０４への出力電圧を制御することも可能である。
　図１０は、図９における降圧コンバータ５０３を除いた回路構成、すなわちモータ５０５を駆動するための構成のみを示した回路構成である。同図に示されるように、本発明の半導体装置は、例えばショットキーバリアダイオードとして昇圧コンバータ５０２およびインバータ５０４に採用されることでスイッチング制御に供される。昇圧コンバータ５０２においてはチョッパ回路に組み込まれてチョッパ制御を行い、またインバータ５０４においてはＩＧＢＴを含むスイッチング回路に組み込まれてスイッチング制御を行う。なお、バッテリー５０１の出力にインダクタ（コイルなど）を介在させることで電流の安定化を図り、またバッテリー５０１、昇圧コンバータ５０２、インバータ５０４のそれぞれの間にキャパシタ（電解コンデンサなど）を介在させることで電圧の安定化を図っている。
　また、図１０中に点線で示すように、駆動制御部５０６内にはＣＰＵ（Ｃｅｎｔｒａｌ　Ｐｒｏｃｅｓｓｉｎｇ　Ｕｎｉｔ）からなる演算部５０７と不揮発性メモリからなる記憶部５０８が設けられている。駆動制御部５０６に入力された信号は演算部５０７に与えられ、必要な演算を行うことで各半導体素子に対するフィードバック信号を生成する。また記憶部５０８は、演算部５０７による演算結果を一時的に保持したり、駆動制御に必要な物理定数や関数などをテーブルの形で蓄積して演算部５０７に適宜出力する。演算部５０７や記憶部５０８は公知の構成を採用することができ、その処理能力等も任意に選定できる。
　図９や図１０に示されるように、制御システム５００においては、昇圧コンバータ５０２、降圧コンバータ５０３、インバータ５０４のスイッチング動作にはダイオードやスイッチング素子であるサイリスタ、パワートランジスタ、ＩＧＢＴ、ＭＯＳＦＥＴ等が用いられる。さらに、本発明に係る半導体装置等を適用することで、極めて良好なスイッチング特性が期待できるとともに、制御システム５００の一層の小型化やコスト低減が実現可能となる。すなわち、昇圧コンバータ５０２、降圧コンバータ５０３、インバータ５０４のそれぞれが本発明による効果を期待できるものとなり、これらのいずれか一つ、もしくは任意の二つ以上の組合せ、あるいは駆動制御部５０６も含めた形態のいずれにおいても本発明の効果を期待することができる。
　なお、上述の制御システム５００は本発明の半導体装置を電気自動車の制御システムに適用できるだけではなく、直流電源からの電力を昇圧・降圧したり、直流から交流へ電力変換するといったあらゆる用途の制御システムに適用することが可能である。また、バッテリーとして太陽電池などの電源を用いることも可能である。
図１１は、本発明の実施態様に係る半導体装置を採用した制御システムの他の例を示すブロック構成図、図１２は同制御システムの回路図であり、交流電源からの電力で動作するインフラ機器や家電機器等への搭載に適した制御システムである。
　図１１に示すように、制御システム６００は、外部の例えば三相交流電源（電源）６０１から供給される電力を入力するもので、ＡＣ／ＤＣコンバータ６０２、インバータ６０４、モータ（駆動対象）６０５、駆動制御部６０６を有し、これらは様々な機器（後述する）に搭載することができる。三相交流電源６０１は、例えば電力会社の発電施設（火力発電所、水力発電所、地熱発電所、原子力発電所など）であり、その出力は変電所を介して降圧されながら交流電圧として供給される。また、例えば自家発電機等の形態でビル内や近隣施設内に設置されて電力ケーブルで供給される。ＡＣ／ＤＣコンバータ６０２は交流電圧を直流電圧に変換する電圧変換装置であり、三相交流電源６０１から供給される１００Ｖや２００Ｖの交流電圧を所定の直流電圧に変換する。具体的には、電圧変換により３．３Ｖや５Ｖ、あるいは１２Ｖといった、一般的に用いられる所望の直流電圧に変換される。駆動対象がモータである場合には１２Ｖへの変換が行われる。なお、三相交流電源に代えて単相交流電源を採用することも可能であり、その場合にはＡＣ／ＤＣコンバータを単相入力のものとすれば同様のシステム構成とすることができる。
　インバータ６０４は、ＡＣ／ＤＣコンバータ６０２から供給される直流電圧をスイッチング動作により三相の交流電圧に変換してモータ６０５に出力する。モータ６０４は、制御対象によりその形態が異なるが、制御対象が電車の場合には車輪を、工場設備の場合にはポンプや各種動力源を、家電機器の場合にはコンプレッサなどを駆動するための三相交流モータであり、インバータ６０４から出力される三相の交流電圧によって回転駆動され、その回転駆動力を図示しない駆動対象に伝達する。
　なお、例えば家電機器においてはＡＣ／ＤＣコンバータ３０２から出力される直流電圧をそのまま供給することが可能な駆動対象も多く（例えばパソコン、ＬＥＤ照明機器、映像機器、音響機器など）、その場合には制御システム６００にインバータ６０４は不要となり、図１１中に示すように、ＡＣ／ＤＣコンバータ６０２から駆動対象に直流電圧を供給する。この場合、例えばパソコンなどには３．３Ｖの直流電圧が、ＬＥＤ照明機器などには５Ｖの直流電圧が供給される。
　一方、図示しない各種センサを用いて、駆動対象の回転数やトルク、あるいは駆動対象の周辺環境の温度や流量などといった実測値が計測され、これらの計測信号が駆動制御部６０６に入力される。また同時に、インバータ６０４の出力電圧値も駆動制御部６０６に入力される。これらの計測信号をもとに、駆動制御部６０６はインバータ６０４にフィードバック信号を与え、スイッチング素子によるスイッチング動作を制御する。これによって、インバータ６０４がモータ６０５に与える交流電圧が瞬時に補正されることで、駆動対象の運転制御を正確に実行させることができ、駆動対象の安定した動作が実現する。また、上述のように、駆動対象が直流電圧で駆動可能な場合には、インバータへのフィードバックに代えてＡＣ／ＤＣコンバータ６０２をフィードバック制御することも可能である。
　図１２は、図１１の回路構成を示したものである。同図に示されるように、本発明の半導体装置は、例えばショットキーバリアダイオードとしてＡＣ／ＤＣコンバータ６０２およびインバータ６０４に採用されることでスイッチング制御に供される。ＡＣ／ＤＣコンバータ６０２は、例えばショットキーバリアダイオードをブリッジ状に回路構成したものが用いられ、入力電圧の負電圧分を正電圧に変換整流することで直流変換を行う。またインバータ６０４においてはＩＧＢＴにおけるスイッチング回路に組み込まれてスイッチング制御を行う。なお、三相交流電源６０１とＡＣ／ＤＣコンバータ６０２との間にインダクタ（コイルなど）を介在させることで電流の安定化を図り、またＡＣ／ＤＣコンバータ６０２とインバータ６０４の間にキャパシタ（電解コンデンサなど）を介在させることで電圧の安定化を図っている。
　また、図１２中に点線で示すように、駆動制御部６０６内にはＣＰＵからなる演算部６０７と不揮発性メモリからなる記憶部６０８が設けられている。駆動制御部６０６に入力された信号は演算部６０７に与えられ、必要な演算を行うことで各半導体素子に対するフィードバック信号を生成する。また記憶部６０８は、演算部６０７による演算結果を一時的に保持したり、駆動制御に必要な物理定数や関数などをテーブルの形で蓄積して演算部６０７に適宜出力する。演算部６０７や記憶部６０８は公知の構成を採用することができ、その処理能力等も任意に選定できる。
　このような制御システム６００においても、図１１や図１２に示した制御システム５００と同様に、ＡＣ／ＤＣコンバータ６０２やインバータ６０４の整流動作やスイッチング動作にはダイオードやスイッチング素子であるサイリスタ、パワートランジスタ、ＩＧＢＴ、ＭＯＳＦＥＴ等が用いられる。さらに、本発明に係る半導体膜や半導体装置を適用することで、極めて良好なスイッチング特性が期待できるとともに、制御システム６００の一層の小型化やコスト低減が実現可能となる。すなわち、ＡＣ／ＤＣコンバータ６０２、インバータ６０４のそれぞれが本発明による効果を期待できるものとなり、これらのいずれか一つ、もしくは組合せ、あるいは駆動制御部６０６も含めた形態のいずれにおいても本発明の効果を期待することができる。
　なお、図１１および図１２では駆動対象としてモータ６０５を例示したが、駆動対象は必ずしも機械的に動作するものに限られず、交流電圧を必要とする多くの機器を対象とすることができる。制御システム６００においては、交流電源から電力を入力して駆動対象を駆動する限りにおいては適用が可能であり、インフラ機器（例えばビルや工場等の電力設備、通信設備、交通管制機器、上下水処理設備、システム機器、省力機器、電車など）や家電機器（例えば、冷蔵庫、洗濯機、パソコン、ＬＥＤ照明機器、映像機器、音響機器など）といった機器を対象とした駆動制御のために搭載することができる。
（実施例１）
１．成膜装置
　図１を用いて、本実施例で用いたミストＣＶＤ装置を説明する。ミストＣＶＤ装置１９は、基板２０を載置するサセプタ２１と、キャリアガスを供給するキャリアガス供給手段２２ａと、キャリアガス供給手段２２ａから送り出されるキャリアガスの流量を調節するための流量調節弁２３ａと、キャリアガス（希釈）を供給するキャリアガス（希釈）供給手段２２ｂと、キャリアガス（希釈）供給手段２２ｂから送り出されるキャリアガスの流量を調節するための流量調節弁２３ｂと、原料溶液２４ａが収容されるミスト発生源２４と、水２５ａが入れられる容器２５と、容器２５の底面に取り付けられた超音波振動子２６と、内径４０ｍｍの石英管からなる供給管２７と、供給管２７の周辺部に設置されたヒーター２８とを備えている。サセプタ２１は、石英からなり、基板２０を載置する面が水平面から傾斜している。成膜室となる供給管２７とサセプタ２１をどちらも石英で作製することにより、基板２０上に形成される膜内に装置由来の不純物が混入することを抑制している。
２．原料溶液の作製
　ビス［２－カルボキシエチルゲルマニウム（ＩＶ）］セスキオキシド（Ｃ６Ｈ１０Ｇｅ２Ｏ７）を０．００５Ｍの水溶液に、塩酸（ＨＣｌ）を１０体積％を加え、さらに、酢酸アンチモンを、ゲルマニウムに対するアンチモンの原子比が０．０００５となるように混合し、これを原料溶液とした。
３．製膜準備
　上記２．で得られた原料溶液２４ａミスト発生源２４内に収容した。次に、基板２０として、（００１）面ｒ－ＴｉＯ２基板をサセプタ２１上に設置し、ヒーター２８の温度を７５０℃にまで昇温させた。次に、流量調節弁２３ａ、２３ｂを開いて、キャリアガス源であるキャリアガス供給手段２２ａ、２２ｂからキャリアガスを供給管２７内に供給し、供給管２７内の雰囲気をキャリアガスで十分に置換した後、キャリアガスの流量を３．０Ｌ／分に、キャリアガス（希釈）の流量を０．５Ｌ／分にそれぞれ調節した。なお、キャリアガスとして酸素を用いた。
４．成膜
　次に、超音波振動子２６を２．４ＭＨｚで振動させ、その振動を、水２５ａを通じて原料溶液２４ａに伝播させることによって、原料溶液２４ａを霧化させてミスト（霧化液滴）２４ｂを生成させた。このミスト２４ｂが、キャリアガスによって、供給管２７内を通って、成膜室３０内に導入され、大気圧下、７５０℃にて、基板２０上でミストが熱反応して、基板２０上にＧｅＯ２膜を製膜した。
（実施例２）
　原料溶液中のビス［２－カルボキシエチルゲルマニウム（ＩＶ）］セスキオキシド（Ｃ６Ｈ１０Ｇｅ２Ｏ７）の濃度を０．０１Ｍ（ｍｏｌ／Ｌ）としたこと以外は、実施例１と同様にして、ＧｅＯ２膜を製膜した。
（実施例３）
　原料溶液中の酢酸アンチモンの濃度を、ゲルマニウムに対するアンチモンの原子比が１：０．００１となるよう原料溶液を調製したこと以外は、実施例１と同様にして、ＧｅＯ２膜を製膜した。
（実施例４）
　原料溶液中のビス［２－カルボキシエチルゲルマニウム（ＩＶ）］セスキオキシド（Ｃ６Ｈ１０Ｇｅ２Ｏ７）の濃度を０．０１Ｍ（ｍｏｌ／Ｌ）とし、酢酸アンチモンの濃度を、ゲルマニウムに対するアンチモンの原子比が１：０．００１としたこと以外は、実施例１と同様にして、ＧｅＯ２膜を製膜した。
　実施例１～４で得られたＧｅＯ２膜につき、ホール効果測定を行ったところ、キャリアタイプは「ｎ」であった。実施例１～４で得られたＧｅＯ２膜のキャリア密度を表１に示す。表１に示す。表１から明らかなように、本発明の実施態様にかかる酸化物半導体は、良好な電気特性を有することが分かる。また、実施例１～４で得られたＧｅＯ２膜の比抵抗を図２に示す。図２から明らかように、原料溶液中のドーパント濃度を制御することにより、比抵抗を良好に低減できていることが分かる。なお、図２の縦軸が電気抵抗率、横軸がＧｅに対するＳｂの原子比（％）を示す。
Figure JPOXMLDOC01-appb-T000001
　本発明の酸化物半導体は、半導体（例えば化合物半導体電子デバイス等）、電子部品・電気機器部品、光学・電子写真関連装置、工業部材などあらゆる分野に用いることができるが、特に、半導体装置およびその部材等に有用である。
１　　　　　ｐ型半導体層
２　　　　　ショットキー電極
３　　　　　ｎ－型半導体層
４　　　　　ｎ＋型半導体層
５　　　　　オーミック電極
１１　　　　第１の層
１２　　　　第２の層
１３　　　　第１の電極
１４　　　　第２の電極
１９　　　　ミストＣＶＤ装置
２０　　　　基板（結晶基板）
２１　　　　サセプタ
２２ａ　　　キャリアガス供給手段
２２ｂ　　　キャリアガス（希釈）供給手段
２３ａ　　　流量調節弁
２３ｂ　　　流量調節弁
２４　　　　ミスト発生源
２４ａ　　　原料溶液
２５　　　　容器
２５ａ　　　水
２６　　　　超音波振動子
２７　　　　供給管
２８　　　　ヒーター
２９　　　　排気口
３１　　　　基板
３２　　　　導電体層（電子伝導層）
３３　　　　光触媒層（光吸収層）
４０　　　　下部電極
４１　　　　高濃度ｎ型層
４２　　　　低濃度ｎ型層
４３　　　　高濃度ｐ型層
４４　　　　ショットキー電極
４５　　　　上部電極
４６　　　　特定領域
５１　　　　導電性膜
５２　　　　光電変換層
５５　　　　透明導電性膜
５６ａ　　　電子ブロッキング層
５６ｂ　　　正孔ブロッキング層
１０１ａ　　ｎ－型半導体層
１０１ｂ　　ｎ＋型半導体層
１０５ｂ　　オーミック電極
１０５ａ　　ショットキー電極
１２１ａ　　バンドギャップの広いｎ型半導体層
１２１ｂ　　バンドギャップの狭いｎ型半導体層
１２１ｃ　　ｎ＋型半導体層
１２３　　　ｐ型半導体層
１２４　　　半絶縁体層
１２５ａ　　ゲート電極
１２５ｂ　　ソース電極
１２５ｃ　　ドレイン電極
１２８　　　緩衝層
１３１ａ　　ｎ－型半導体層
１３１ｂ　　第１のｎ＋型半導体層
１３１ｃ　　第２のｎ＋型半導体層
１３２　　　ｐ型半導体層
１３２ａ　　ｐ＋型半導体層
１３４　　　ゲート絶縁膜
１３５ａ　　ゲート電極
１３５ｂ　　ソース電極
１３５ｃ　　ドレイン電極
１５１　　　ｎ型半導体層
１５１ａ　　ｎ－型半導体層
１５１ｂ　　ｎ＋型半導体層
１５２　　　ｐ型半導体層
１５４　　　ゲート絶縁膜
１５５ａ　　ゲート電極
１５５ｂ　　エミッタ電極
１５５ｃ　　コレクタ電極
１６１　　　ｎ型半導体層
１６２　　　ｐ型半導体層
１６３　　　発光層
１６５ａ　　第１の電極
１６５ｂ　　第２の電極
１６７　　　透光性電極
５００　　　制御システム
５０１　　　バッテリー（電源）
５０２　　　昇圧コンバータ
５０３　　　降圧コンバータ
５０４　　　インバータ
５０５　　　モータ（駆動対象）
５０６　　　駆動制御部
５０７　　　演算部
５０８　　　記憶部
６００　　　制御システム
６０１　　　三相交流電源（電源）
６０２　　　ＡＣ／ＤＣコンバータ
６０４　　　インバータ
６０５　　　モータ（駆動対象）
６０６　　　駆動制御部
６０７　　　演算部
６０８　　　記憶部

Claims (12)

  1. 　ゲルマニウムの酸化物を含有する酸化物半導体であって、キャリア密度が１．０×１０１８／ｃｍ３以上であることを特徴とする酸化物半導体。
  2. 　前記酸化物半導体中の金属元素中におけるゲルマニウムの原子比が０．５より大きい請求項１記載の酸化物半導体。
  3. 　ｎ型の導電型を有する請求項１または２に記載の酸化物半導体。
  4. 　ドーパントを含有する請求項１～３のいずれかに記載の酸化物半導体。
  5. 　前記ドーパントが、周期律表第１５族金属を含む請求項４記載の酸化物半導体。
  6. 　前記ドーパントが、アンチモンである請求項４または５に記載の酸化物半導体。
  7. 　比抵抗が１０Ωｃｍ以下である請求項１～６のいずれかに記載の酸化物半導体。
  8. 　膜状である請求項１～７のいずれかに記載の酸化物半導体。
  9. 　請求項８記載の酸化物半導体と、電極とを少なくとも備える半導体装置。
  10. 　請求項９記載の半導体装置を用いた電力変換装置。
  11. 　請求項９記載の半導体装置を用いた制御システム。
  12. 　基体上にドーピングされたゲルマニウムの酸化物を含有する酸化物半導体を製造する方法であって、ドーパント元素およびゲルマニウムを含有し、前記ドーパント元素よりもゲルマニウムの含有量が多い原料溶液を霧化または液滴化し、得られた霧化液滴にキャリアガスを供給し、該キャリアガスでもって前記霧化液滴を前記基体上まで搬送し、ついで、前記基体上で前記霧化液滴を熱反応させることを特徴とする酸化物半導体の製造方法。

     
PCT/JP2022/028850 2021-07-30 2022-07-26 酸化物半導体および半導体装置 WO2023008452A1 (ja)