WO2022230831A1 - 半導体装置 - Google Patents

半導体装置 Download PDF

Info

Publication number
WO2022230831A1
WO2022230831A1 PCT/JP2022/018787 JP2022018787W WO2022230831A1 WO 2022230831 A1 WO2022230831 A1 WO 2022230831A1 JP 2022018787 W JP2022018787 W JP 2022018787W WO 2022230831 A1 WO2022230831 A1 WO 2022230831A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
crystalline oxide
semiconductor device
semiconductor layer
semiconductor
Prior art date
Application number
PCT/JP2022/018787
Other languages
English (en)
French (fr)
Inventor
雅裕 杉本
慎平 松田
安史 樋口
和良 則松
Original Assignee
株式会社Flosfia
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社Flosfia filed Critical 株式会社Flosfia
Priority to EP22795744.6A priority Critical patent/EP4333075A1/en
Priority to JP2023517524A priority patent/JPWO2022230831A1/ja
Priority to CN202280031264.6A priority patent/CN117441234A/zh
Publication of WO2022230831A1 publication Critical patent/WO2022230831A1/ja
Priority to US18/384,031 priority patent/US20240055471A1/en

Abstract

特にパワーデバイスに有用な、耐圧性に優れた半導体装置を提供する。チャネル層およびドリフト層を含む結晶性酸化物半導体層と、該チャネル層上にゲート絶縁膜を介して配置されているゲート電極とを少なくとも備え、前記チャネル層と前記ドリフト層との間に電流遮断層を有する半導体装置であって、前記ドリフト層が第１の結晶性酸化物を主成分として含み、前記電流遮断層が、第２の結晶性酸化物を主成分として含み、前記第１の結晶性酸化物と前記第２の結晶性酸化物とが異なる組成を有することを特徴とする半導体装置。

Description

半導体装置
　本発明は、パワーデバイス等として有用な半導体装置に関する。
　酸化ガリウム（Ｇａ２Ｏ３）は、室温において４．８－５．３ｅＶという広いバンドギャップを持ち、可視光及び紫外光をほとんど吸収しない透明半導体である。そのため、特に、深紫外光線領域で動作する光・電子デバイスや透明エレクトロニクスにおいて使用するための有望な材料であり、近年においては、酸化ガリウム（Ｇａ２Ｏ３）を基にした、光検知器、発光ダイオード（ＬＥＤ）及びトランジスタの開発が行われている（非特許文献１参照）。当該酸化ガリウムは特許文献４によると、インジウムやアルミニウムをそれぞれ、あるいは組み合わせて混晶とすることによりバンドギャップ制御することが可能であり、ＩｎＡｌＧａＯ系半導体として極めて魅力的な材料系統を構成している。ここでＩｎＡｌＧａＯ系半導体とはＩｎＸＡｌＹＧａＺＯ３（０≦Ｘ≦２、０≦Ｙ≦２、０≦Ｚ≦２、Ｘ＋Ｙ＋Ｚ＝１．５～２．５）を示し、酸化ガリウムを内包する同一材料系統として俯瞰することができる。
　また、酸化ガリウム（Ｇａ２Ｏ３）には、α、β、γ、σ、εの５つの結晶構造が存在し、一般的に最も安定な構造は、β－Ｇａ２Ｏ３である。しかしながら、β－Ｇａ２Ｏ３はβガリア構造であるので、一般に電子材料等で利用する結晶系とは異なり、半導体装置への利用は必ずしも好適ではない。また、β－Ｇａ２Ｏ３薄膜の成長は高い基板温度や高い真空度を必要とするので、製造コストも増大するといった問題もある。また、非特許文献２にも記載されているように、β－Ｇａ２Ｏ３では、高濃度（例えば１×１０１９／ｃｍ３以上）のドーパント（Ｓｉ）でさえも、イオン注入後、８００℃～１１００℃の高温にてアニール処理を施さなければドナーとして使えなかった。
　一方、α－Ｇａ２Ｏ３は、既に汎用されているサファイア基板と同じ結晶構造を有するため、光・電子デバイスへの利用には好適であり、さらに、β－Ｇａ２Ｏ３よりも広いバンドギャップをもつため、パワーデバイスに特に有用であり、そのため、α－Ｇａ２Ｏ３を半導体として用いた半導体装置が待ち望まれている状況である。
　特許文献１には、ドナーを含むＧａ２Ｏ３系結晶層と、前記Ｇａ２Ｏ３系結晶層の少なくとも一部に形成されたＮ添加領域とを有し、前記Ｎ添加領域が、チャネル領域を含む又は電流経路となる開口領域を有する電流遮断領域である縦型ＭＯＳＦＥＴが開示されている。しかしながら、実際に縦型ＭＯＳＦＥＴとして動作することは確認されておらず、また、耐圧等の信頼性においても十分に満足できるようなものではなかった。
特開２０１８－１８６２４６号公報
　本発明は、耐圧に優れた半導体装置を提供することを目的とする。
　本発明者らは、上記目的を達成すべく鋭意検討した結果、チャネル層およびドリフト層を含む結晶性酸化物半導体層と、該チャネル層上にゲート絶縁膜を介して配置されているゲート電極とを少なくとも備え、前記チャネル層と前記ドリフト層との間に電流遮断層を有する半導体装置であって、前記ドリフト層が第１の結晶性酸化物を主成分として含み、前記電流遮断層が、第２の結晶性酸化物を主成分として含み、前記第１の結晶性酸化物と前記第２の結晶性酸化物とが異なる組成を有する半導体装置が、該結晶欠陥領域を有しない構造と比較して耐圧性が向上されたものとなることを見出し、このようにして得られた半導体装置が、上記した従来の問題を解決できるものであることを見出した。
　また、本発明者らは、上記知見を得た後、さらに検討を重ねて本発明を完成させるに至った。
　すなわち、本発明は、以下の発明に関する。
［１］　チャネル層およびドリフト層を含む結晶性酸化物半導体層と、該チャネル層上にゲート絶縁膜を介して配置されているゲート電極とを少なくとも備え、前記チャネル層と前記ドリフト層との間に電流遮断層を有する半導体装置であって、前記ドリフト層が第１の結晶性酸化物を主成分として含み、前記電流遮断領域が、第２の結晶性酸化物半導体を主成分として含み、前記第１の結晶性酸化物と前記第２の結晶性酸化物とが異なる組成を有することを特徴とする半導体装置。
［２］　前記第１の結晶性酸化物が、アルミニウム、インジウムおよびガリウムから選ばれる少なくとも１種の金属を含有する前記［１］記載の半導体装置。
［３］　前記第１の結晶性酸化物が、コランダム構造を有する前記［１］または［２］に記載の半導体装置。
［４］　前記第２の結晶性酸化物が、周期律表第６族～第１０族から選ばれる少なくとも１種の金属を含有する前記［１］～［３］のいずれかに記載の半導体装置。
［５］　前記第２の結晶性酸化物が、周期律表第６族～第１０族から選ばれる少なくとも１種の金属と、周期律表第１３族金属とを少なくとも含む混晶である前記［１］～［４］のいずれかに記載の半導体装置。
［６］　前記第２の結晶性酸化物が、周期律表第９族金属と周期律表第１３族金属とを少なくとも含む混晶である前記［１］～［５］のいずれかに記載の半導体装置。
［７］　前記第２の結晶性酸化物のバンドギャップが、３・０ｅＶ以上である前記［１］～［６］のいずれかに記載の半導体装置。
［８］　前記電流遮断層が、ｐ型の導電型を有する前記［１］～［７］のいずれかに記載の半導体装置。
［９］　前記チャネル層の少なくとも一部にソース領域を有しており、前記ソース領域上にソース電極を備えている前記［１］～［８］のいずれかに記載の半導体装置。
［１０］　前記ソース電極が、前記電流遮断層と直接コンタクトしている前記［１］～［９］のいずれかに記載の半導体装置。
［１１］　前記結晶性酸化物半導体層が、少なくともチャネル層を貫通するトレンチを有しており、該トレンチ内に前記ゲート電極の少なくとも一部が前記ゲート絶縁膜を介して埋め込まれている前記［１］～［１０］のいずれかに記載の半導体装置。
［１２］　トランジスタである前記［１］～［１１］のいずれかに記載の半導体装置。
［１３］　第１の半導体層としてのドリフト層、チャネル層およびソース層がこの順に積層された積層体を含む結晶酸化物半導体層と、前記ソース層およびチャネル層を貫通し前記第１の半導体層に達するトレンチと、該トレンチ内にゲート絶縁膜を介して設けられているゲート電極とを少なくとも備える半導体装置であって、前記ゲート絶縁膜と前記トレンチ側壁の前記チャネル層に接した部分の少なくとも一部との間に、第２の半導体層が設けられており、前記第１の半導体層が第１の結晶性酸化物半導体を主成分として含み、前記第２の半導体層が、第２の結晶性酸化物半導体を主成分として含むことを特徴とする半導体装置。
［１４］　前記［１］～［１３］のいずれかに記載の半導体装置を用いた電力変換装置。
［１５］　前記［１］～［１３］のいずれかに記載の半導体装置を用いた制御システム。
　本発明によれば、耐圧性に優れた半導体装置を提供することができる。
本発明の実施態様にかかる金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）を模式的に示す図である。 本発明の実施態様にかかる金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）の好適な製造工程を模式的に示す図である。 本発明の実施態様にかかる金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）の好適な製造工程を模式的に示す図である。 本発明の実施態様にかかる金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）を模式的に示す図である。 本発明の実施態様にかかる金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）を模式的に示す図である。 実施例におけるサンプル構造を模式的に示す図である。 実施例におけるＩ－Ｖ測定の結果を示す図である。 本発明の実施態様において用いられるミストＣＶＤ装置の構成図である。 本発明の実施態様にかかる半導体装置を採用した制御システムの一例を示すブロック構成図である。 本発明の実施態様にかかる半導体装置を採用した制御システムの一例を示す回路図である。 本発明の実施態様にかかる半導体装置を採用した制御システムの一例を示すブロック構成図である。 本発明の実施態様にかかる半導体装置を採用した制御システムの一例を示す回路図である。 本発明の実施態様にかかる金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）を模式的に示す図である。 本発明の実施態様にかかる金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）を模式的に示す図である。
　本発明の実施態様にかかる半導体装置は、チャネル層およびドリフト層を含む結晶性酸化物半導体層と、該チャネル層上にゲート絶縁膜を介して配置されているゲート電極とを少なくとも備え、前記チャネル層と前記ドリフト層との間に電流遮断層を有する半導体装置であって、前記ドリフト層が第１の結晶性酸化物を主成分として含み、前記電流遮断層が、第２の結晶性酸化物を主成分として含み、前記第１の結晶性酸化物と前記第２の結晶性酸化物とが異なる組成を有することを特長とする。
　前記結晶性酸化物半導体層は、本発明の目的を阻害しない限り、特に限定されない。本発明の実施態様においては、前記結晶性酸化物半導体層が、結晶性酸化物半導体を主成分として含むのが好ましい。前記結晶性酸化物半導体としては、例えば、アルミニウム、ガリウム、インジウム、鉄、クロム、バナジウム、チタン、ロジウム、ニッケル、コバルトおよびイリジウムから選ばれる１種または２種以上の金属を含む金属酸化物などがあげられる。本発明の実施態様においては、前記結晶性酸化物半導体層が、アルミニウム、インジウムおよびガリウムから選ばれる少なくとも１種の金属を含有するのが好ましく、少なくともガリウムを含むのがより好ましく、α－Ｇａ２Ｏ３またはその混晶であるのが最も好ましい。本発明の実施態様によれば、例えば酸化ガリウムまたはその混晶等のバンドギャップの大きい半導体を含む半導体装置であっても、絶縁耐圧を向上させることができる。前記結晶性酸化物半導体層の結晶構造も、本発明の目的を阻害しない限り、特に限定されない。前記結晶性酸化物半導体層の結晶構造としては、例えば、コランダム構造、β－ガリア構造、六方晶構造（例えば、ε型構造等）、直方晶構造（例えばκ型構造等）、立方晶構造、または正方晶構造等が挙げられる。本発明の実施態様においては、前記結晶性酸化物半導体層が、コランダム構造、β－ガリア構造または六方晶構造（例えば、ε型構造等）を有するのが好ましく、コランダム構造を有するのがより好ましい。なお、「主成分」とは、前記結晶性酸化物半導体が、原子比で、前記結晶性酸化物半導体層の全成分に対し、好ましくは５０％以上、より好ましくは７０％以上、さらにより好ましくは９０％以上含まれることを意味し、１００％であってもよいことを意味する。例えば、前記結晶性酸化物半導体が酸化ガリウムである場合、前記結晶性酸化物半導体層中に含まれる全ての金属元素中のガリウムの原子比が０．５以上の割合で前記結晶性酸化物半導体層中に結晶性酸化物半導体としての酸化ガリウムが含まれていればそれでよい。前記結晶性酸化物半導体層中に含まれる全ての金属元素中のガリウムの原子比は、０．７以上であるのが好ましく、０．９以上であるのがより好ましい。また、前記結晶性酸化物半導体層の厚さは、特に限定されず、１μｍ以下であってもよいし、１μｍ以上であってもよいが、本発明の実施態様においては、５μｍ以上であるのが好ましく、１０μｍ以上であるのがより好ましい。前記半導体膜の（平面視における）表面積は特に限定されないが、１ｍｍ２以上であってもよいし、１ｍｍ２以下であってもよいが、１０ｍｍ２～３００ｍｍ２であるのが好ましく、１０ｍｍ２～１００ｍｍ２であるのがより好ましい。また、前記結晶性酸化物半導体層は、通常、単結晶であるが、多結晶であってもよい。また、前記結晶性酸化物半導体層は、通常、２以上の半導体層を含んでいる。前記結晶性酸化物半導体層は、例えば、ｎ＋型半導体層、ドリフト層（ｎ－型半導体層）、チャネル層、およびソース領域（ｎ＋型半導体層）を少なくとも含む。また、前記結晶性酸化物半導体層のキャリア密度は、ドーピング量を調節することにより、適宜設定することができる。
　前記結晶性酸化物半導体層は、ドーパントを含むのが好ましい。前記ドーパントは、特に限定されず、公知のものであってよい。本発明の実施形態においては、特に、前記半導体層がガリウムを含む結晶性酸化物を主成分とする場合、前記ドーパントの好適な例としては、例えば、スズ、ゲルマニウム、ケイ素、チタン、ジルコニウム、バナジウムまたはニオブ等のｎ型ドーパント、またはＭｇ、Ｈ、Ｌｉ、Ｎａ、Ｋ、Ｒｂ、Ｃｓ、Ｆｒ、Ｂｅ、Ｃａ、Ｓｒ、Ｂａ、Ｒａ、Ｍｎ、Ｆｅ、Ｃｏ、Ｎｉ、Ｐｄ、Ｃｕ、Ａｇ、Ａｕ、Ｚｎ、Ｃｄ、Ｈｇ、Ｔｉ、Ｐｂ、Ｎ、もしくはＰ等のｐ型ドーパントなどが挙げられる。本発明の実施態様においては、前記ｎ型ドーパントが、Ｓｎ、ＧｅおよびＳｉから選ばれる少なくとも１種であるのが好ましい。ドーパントの含有量は、前記半導体層の組成中、０．００００１原子％以上であるのが好ましく、０．００００１原子％～２０原子％であるのがより好ましく、０．００００１原子％～１０原子％であるのが最も好ましい。より具体的には、ドーパントの濃度は、通常、約１×１０１６／ｃｍ３～１×１０２２／ｃｍ３であってもよいし、また、ドーパントの濃度を例えば約１×１０１７／ｃｍ３以下の低濃度にしてもよい。また、さらに、本発明によれば、ドーパントを約１×１０２０／ｃｍ３以上の高濃度で含有させてもよい。
　本発明の実施態様においては、前記結晶性酸化物半導体層は、チャネル層を含み、該チャネル層上に前記ゲート絶縁膜を介してゲート電極が配置されている。前記チャネル層の構成材料は、上記した前記結晶性酸化物半導体層の構成材料と同様であってよい。また、前記チャネル層の導電型も、特に限定されず、ｎ型であってもよいし、ｐ型であってもよい。前記チャネル層の導電型がｎ型である場合、前記チャネル層の構成材料としては、好適には、例えば、α－Ｇａ２Ｏ３またはその混晶等が挙げられる。また、前記チャネル層の導電型がｐ型である場合、前記チャネル層の構成材料としては、好適には、例えば、ｐ型ドーパントを含むα－Ｇａ２Ｏ３またはその混晶、周期律表第６族から選ばれる少なくとも１種の金属を含む金属酸化物（例えば、α－Ｃｒ２Ｏ３等）、周期律表第９族から選ばれる少なくとも１種の金属を含む金属酸化物（例えば、α－Ｉｒ２Ｏ３、α－Ｃｒ２Ｏ３、α－Ｒｈ２Ｏ３）等が挙げられる。なお、周期律表第６族から選ばれる少なくとも１種の金属を含む金属酸化物または周期律表第９族から選ばれる少なくとも１種の金属を含む金属酸化物は、他の金属酸化物（例えばＧａ２Ｏ３）との混晶であってもよい。
　前記ゲート絶縁膜（層間絶縁膜）の構成材料は、特に限定されず、公知の材料であってよい。前記ゲート絶縁膜の材料としては、例えば、ＳｉＯ２膜、リン添加ＳｉＯ２膜（ＰＳＧ膜）、ボロン添加ＳｉＯ２膜、リンーボロン添加ＳｉＯ２膜（ＢＰＳＧ膜）等が挙げられる。前記ゲート絶縁膜の形成方法としては、例えば、ＣＶＤ法、大気圧ＣＶＤ法、プラズマＣＶＤ法、ミストＣＶＤ法等が挙げられる。本発明の実施態様においては、前記ゲート絶縁膜の形成方法が、ミストＣＶＤ法または大気圧ＣＶＤ法であるのが好ましい。また、前記ゲート電極の構成材料は、特に限定されず、公知の電極材料であってよい。前記ゲート電極の構成材料としては、例えば、上記した前記ソース電極の構成材料等が挙げられる。前記ゲート電極の形成方法は、特に限定されない。前記ゲート電極の形成方法としては、具体的には例えば、ドライ法やウェット法などが挙げられる。ドライ法としては、例えば、スパッタ、真空蒸着、ＣＶＤ等が挙げられる。ウェット法としては、例えば、スクリーン印刷やダイコート等が挙げられる。
　前記ドリフト層は、第１の結晶性酸化物を主成分として含むものであれば、特に限定されない。前記第１の結晶性酸化物としては、例えば、上記した前記結晶性酸化物半導体層の構成材料が挙げられる。本発明の実施態様においては、また、前記第１の結晶性酸化物は、アルミニウム、インジウムおよびガリウムから選ばれる少なくとも１種の金属を含有するのが好ましく、少なくともガリウムを含むのがより好ましく、α－Ｇａ２Ｏ３またはその混晶であるのが最も好ましい。また、本発明の実施態様においては、前記ドリフト層の導電型はｎ型であるのが好ましい。ここで、「主成分」とは、例えば前記第１の結晶性酸化物がＧａ２Ｏ３である場合、前記ドリフト層中の全ての金属元素中のガリウムの原子比が５０％以上の割合で第１の結晶性酸化物としてのＧａ２Ｏ３が前記ドリフト層中に含まれていればそれでよい。本発明の実施態様においては、前記ドリフト層中の全ての金属元素中のガリウムの原子比が７０％以上の割合で第１の結晶性酸化物としてのＧａ２Ｏ３が前記ドリフト層中に含まれているのが好ましく、９０％以上の割合で含まれているのがより好ましい。前記第１の結晶性酸化物の結晶構造も、本発明の目的を阻害しない限り、特に限定されない。前記第１の結晶性酸化物の結晶構造としては、例えば、コランダム構造、β－ガリア構造、六方晶構造（例えば、ε型構造等）、直方晶構造（例えばκ型構造等）、立方晶構造、または正方晶構造等が挙げられる。本発明の実施態様においては、前記第１の結晶性酸化物が、コランダム構造、β－ガリア構造または六方晶構造（例えば、ε型構造等）を有するのが好ましく、コランダム構造を有するのがより好ましい。前記ドリフト層の構成材料としては、例えば、上記した前記結晶性酸化物半導体層の構成材料が挙げられる。本発明の実施態様においては、本発明の実施態様においては、上述した好ましい電流遮断層を用いるので、酸化ガリウムまたはその混晶等のバンドギャップの大きい酸化物半導体をドリフト層に用いた場合であっても、本来の機能を半導体装置（ＭＯＳＦＥＴ等）において好適に発揮させることができる。
　前記電流遮断層は、前記半導体装置内において、前記チャネル層と前記ドリフト層との間に設けられており、第２の結晶性酸化物を主成分として含むものであれば、特に限定されない。本発明の実施態様においては、前記電流遮断層が、前記ドリフト層内に設けられていてもよいし、前記ドリフト層上に設けられていてもよい。前記第２の結晶性酸化物は、前記第１の結晶性酸化物と組成が異なるものであれば、本発明の目的を阻害しない限り、特に限定されない。前記第２の結晶性酸化物としては、例えば、周期律表第６族～第１０族から選ばれる少なくとも１種の金属を含む金属酸化物等が挙げられる。周期律表第６族金属としては、例えば、クロム（Ｃｒ）、モリブデン（Ｍｏ）、およびタングステン（Ｗ）から選ばれる１種または２種以上の金属が挙げられる。周期律表第７族金属としては、例えば、マンガン（Ｍｎ）、テクネチウム（Ｔｃ）およびレニウム（Ｒｅ）から選ばれる１種または２種以上の金属等が挙げられる。周期律表第８族金属としては、例えば、鉄（Ｆｅ）、ルテニウム（Ｒｕ）およびオスミウム（Ｏｓ）から選ばれる１種または２種以上の金属等が挙げられる。周期律表第９族金属としては、例えば、コバルト（Ｃｏ）、ロジウム（Ｒｈ）およびイリジウムから選ばれる１種または２種以上の金属等が挙げられる。本発明の実施態様においては、第２の結晶性酸化物が、周期律表第７族～第１０族から選ばれる少なくとも１種の金属と、周期律表第１３族金属とを少なくとも含む混晶であるのが好ましい。このような好ましい第２の結晶性酸化物を前記電流遮断層に用いることにより、特に酸化ガリウム等のバンドギャップの大きい酸化物半導体を用いた半導体装置（ＭＯＳＦＥＴ）における耐圧性をより向上させることができる。上述のように酸化ガリウム等のバンドギャップの大きい酸化物半導体との組合せで動作特性をＭＯＳＦＥＴに与えることができるので、前記第２の結晶性酸化物のバンドギャップは３．０ｅＶ以上であるのが好ましく、３．５ｅＶ以上であるのがより好ましい。また、本発明の実施態様においては、前記第２の結晶性酸化物が、周期律表第９族金属と周期律表第１３族金属とを少なくとも含む混晶であるのが好ましく、イリジウムとガリウムとを含む混晶であるのがより好ましい。なお、前記電流遮断層の導電型は、特に限定されない。本発明の実施態様においては、前記電流遮断層の導電型がｐ型であるのが好ましい。このような好ましい構成とすることにより、アバランシェ耐量をより向上させることができる。
　前記ソース領域は、ｎ＋型半導体層を含むものであれば、特にされない。本発明の実施態様においては、前記ソース領域が、ｎ＋型半導体層、および該ｎ＋型半導体層上に配置されており該ｎ＋型半導体層よりもキャリア密度が大きいｎ＋＋型半導体層を少なくとも含むのが好ましい。なお、キャリア密度は、公知の方法を用いて求めることができる。前記キャリア密度を求める方法としては、例えば、ＳＩＭＳ（二次イオン質量分析法）、ＳＣＭ（走査型静電容量顕微鏡法）、ＳＭＭ（走査型マイクロ波顕微鏡法）、およびＳＲＡ（広がり抵抗測定法）等が挙げられる。前記ｎ＋型半導体層の主成分と、前記ｎ＋＋型半導体層の主成分とは同じであってもよいし、異なっていてもよい。本発明の実施態様においては、前記ｎ＋型半導体層の主成分と前記ｎ＋＋型半導体層の主成分とが同じであるのが好ましい。また、本発明の実施態様においては、前記ｎ＋型半導体層と前記ｎ＋＋型半導体層とが同じ結晶構造を有しているのが好ましく、前記ｎ＋型半導体層と前記ｎ＋＋型半導体層とがコランダム構造を有しているのがより好ましい。なお、ここで、「主成分」とは、例えば、前記ｎ＋型半導体層の主成分が酸化ガリウムである場合、前記ｎ＋型半導体層中の全ての金属元素中におけるガリウムの原子比が５０％以上の割合で含まれていればそれでよい。本発明の実施態様においては、前記ｎ＋型半導体層中の全ての金属元素中におけるガリウムの原子比が好ましくは７０％以上、更に好ましくは９０％以上含まれ、１００％であってもよい。本発明の実施態様においては、前記ｎ＋＋型半導体層が、エピタキシャル層であるのが好ましく、前記ｎ＋＋型半導体層がエピタキシャルドーピングされているのがより好ましい。上記したような好ましい前記ｎ＋＋型半導体層を用いることにより、コンタクト抵抗をより良好に低減することができる。ここで、エピタキシャルドーピングとは、例えば、イオン注入等によるドーピングではなく、エピタキシャル成長によってドーピングされていることをいう。前記ｎ＋型半導体層および／または前記ｎ＋＋型半導体層中に含まれるｎ型ドーパントとしては、例えば、スズ、ゲルマニウム、ケイ素、チタン、ジルコニウム、バナジウムおよびニオブから選ばれる少なくとも１種のｎ型ドーパント等が挙げられる。本発明の実施態様においては、前記ｎ型ドーパントが、Ｓｎ、ＧｅおよびＳｉから選ばれる少なくとも１種であるのが好ましい。前記ｎ＋＋型半導体層のキャリア密度は、前記ｎ＋型半導体層のキャリア密度よりも大きければ、特に限定されない。本発明の実施態様においては、前記ｎ＋＋型半導体層のキャリア密度が、１．０×１０１９／ｃｍ３以上であるのが好ましく、６．０×１０１９／ｃｍ３以上であるのがより好ましい。前記ｎ＋＋型半導体層のキャリア密度をこのような好ましい値とすることにより、コンタクト抵抗をより良好に低減することができる。また、前記ｎ＋型半導体層のキャリア密度も、特に限定されない。本発明の実施態様においては、前記ｎ＋型半導体層のキャリア密度が、１．０×１０１７／ｃｍ３以上１．０×１０１９／ｃｍ３未満の範囲内であるのが好ましい。前記ｎ＋型半導体層のキャリア密度を上記のような好ましい範囲とすることにより、ソース抵抗をより良好に低減することができる。なお、本発明の実施態様においては、前記ｎ＋型半導体層へのドーピング方法は、特に限定されず、拡散またはイオン注入であってもよいし、エピタキシャル成長法であってもよい。本発明の実施態様においては、前記ｎ＋型半導体層の移動度が前記ｎ＋＋型半導体層の移動度よりも大きいのが好ましい。前記ｎ＋＋型半導体層の厚みは、本発明の目的を阻害しない限り、特に限定されない。本発明の実施態様においては、前記ｎ＋＋型半導体層の厚みが、１ｎｍ～１μｍの範囲内であるのが好ましく、１０ｎｍ～１００ｎｍの範囲内であるのがより好ましい。本発明の実施態様においては、前記ｎ＋型半導体層の厚みが、前記ｎ＋＋型半導体層の厚みよりも大きいのが好ましい。前記ｎ＋型半導体層および前記ｎ＋＋型半導体層を上記した好ましい組合せとすることにより、前記半導体装置におけるソースコンタクト抵抗およびソース抵抗をより良好に低減することができるので、より素子抵抗が低減された前記半導体装置を実現することができる。
　前記結晶性酸化物半導体層（以下、「酸化物半導体層」、「半導体膜」または「半導体層」ともいう。）は、公知の手段を用いて形成されてよい。前記結晶性酸化物半導体層の形成手段としては、例えば、ＣＶＤ法、ＭＯＣＶＤ法、ＭＯＶＰＥ法、ミストＣＶＤ法、ミスト・エピタキシー法、ＭＢＥ法、ＨＶＰＥ法、パルス成長法またはＡＬＤ法などが挙げられる。本発明の実施態様においては、前記半導体層の形成手段が、ＭＯＣＶＤ法、ミストＣＶＤ法、ミスト・エピタキシー法またはＨＶＰＥ法であるのが好ましく、ミストＣＶＤ法またはミスト・エピタキシー法であるのが好ましい。前記のミストＣＶＤ法またはミスト・エピタキシー法では、例えば図８に示すミストＣＶＤ装置を用いて、原料溶液を霧化し（霧化工程）、液滴を浮遊させ、霧化後、得られた霧化液滴をキャリアガスでもって基体上まで搬送し（搬送工程）、ついで、前記基体近傍で前記霧化液滴を熱反応させることによって、基体上に結晶性酸化物半導体を主成分として含む半導体膜を積層する（成膜工程）ことにより前記半導体層を形成する。
（霧化工程）
　霧化工程は、前記原料溶液を霧化する。前記原料溶液の霧化手段は、前記原料溶液を霧化できさえすれば特に限定されず、公知の手段であってよいが、本発明の実施態様においては、超音波を用いる霧化手段が好ましい。超音波を用いて得られた霧化液滴は、初速度がゼロであり、空中に浮遊するので好ましく、例えば、スプレーのように吹き付けるのではなく、空間に浮遊してガスとして搬送することが可能なミストであるので衝突エネルギーによる損傷がないため、非常に好適である。液滴サイズは、特に限定されず、数ｍｍ程度の液滴であってもよいが、好ましくは５０μｍ以下であり、より好ましくは１００ｎｍ～１０μｍである。
（原料溶液）
　前記原料溶液は、霧化または液滴化が可能であり、半導体膜を形成可能な原料を含んでいれば特に限定されず、無機材料であっても、有機材料であってもよい。本発明の実施態様においては、前記原料が、金属または金属化合物であるのが好ましく、アルミニウム、ガリウム、インジウム、鉄、クロム、バナジウム、チタン、ロジウム、ニッケル、コバルトおよびイリジウムから選ばれる１種または２種以上の金属を含むのがより好ましい。
　本発明の実施態様においては、前記原料溶液として、前記金属を錯体または塩の形態で有機溶媒または水に溶解または分散させたものを好適に用いることができる。錯体の形態としては、例えば、アセチルアセトナート錯体、カルボニル錯体、アンミン錯体、ヒドリド錯体などが挙げられる。塩の形態としては、例えば、有機金属塩（例えば金属酢酸塩、金属シュウ酸塩、金属クエン酸塩等）、硫化金属塩、硝化金属塩、リン酸化金属塩、ハロゲン化金属塩（例えば塩化金属塩、臭化金属塩、ヨウ化金属塩等）などが挙げられる。
　また、前記原料溶液には、ハロゲン化水素酸や酸化剤等の添加剤を混合するのが好ましい。前記ハロゲン化水素酸としては、例えば、臭化水素酸、塩酸、ヨウ化水素酸などが挙げられるが、中でも、異常粒の発生をより効率的に抑制できるとの理由から、臭化水素酸またはヨウ化水素酸が好ましい。前記酸化剤としては、例えば、過酸化水素（Ｈ２Ｏ２）、過酸化ナトリウム（Ｎａ２Ｏ２）、過酸化バリウム（ＢａＯ２）、過酸化ベンゾイル（Ｃ６Ｈ５ＣＯ）２Ｏ２等の過酸化物、次亜塩素酸（ＨＣｌＯ）、過塩素酸、硝酸、オゾン水、過酢酸やニトロベンゼン等の有機過酸化物などが挙げられる。
　前記原料溶液には、ドーパントが含まれていてもよい。原料溶液にドーパントを含ませることで、ドーピングを良好に行うことができる。前記ドーパントは、本発明の目的を阻害しない限り、特に限定されない。前記ドーパントとしては、例えば、スズ、ゲルマニウム、ケイ素、チタン、ジルコニウム、バナジウムまたはニオブ等のｎ型ドーパント、またはＭｇ、Ｈ、Ｌｉ、Ｎａ、Ｋ、Ｒｂ、Ｃｓ、Ｆｒ、Ｂｅ、Ｃａ、Ｓｒ、Ｂａ、Ｒａ、Ｍｎ、Ｆｅ、Ｃｏ、Ｎｉ、Ｐｄ、Ｃｕ、Ａｇ、Ａｕ、Ｚｎ、Ｃｄ、Ｈｇ、Ｔｉ、Ｐｂ、Ｎ、もしくはＰ等のｐ型ドーパントなどが挙げられる。前記ドーパントの含有量は、所望のキャリア密度に対するドーパントの原料中の濃度の関係を示す検量線を用いることにより適宜設定される。
　原料溶液の溶媒は、特に限定されず、水等の無機溶媒であってもよいし、アルコール等の有機溶媒であってもよいし、無機溶媒と有機溶媒との混合溶媒であってもよい。本発明の実施態様においては、前記溶媒が水を含むのが好ましく、水または水とアルコールとの混合溶媒であるのがより好ましい。
（搬送工程）
　搬送工程では、キャリアガスでもって前記霧化液滴を成膜室内に搬送する。前記キャリアガスとしては、本発明の目的を阻害しない限り特に限定されず、例えば、酸素、オゾン、窒素やアルゴン等の不活性ガス、または水素ガスやフォーミングガス等の還元ガスなどが好適な例として挙げられる。また、キャリアガスの種類は１種類であってよいが、２種類以上であってもよく、流量を下げた希釈ガス（例えば１０倍希釈ガス等）などを、第２のキャリアガスとしてさらに用いてもよい。また、キャリアガスの供給箇所も１箇所だけでなく、２箇所以上あってもよい。キャリアガスの流量は、特に限定されないが、０．０１～２０Ｌ／分であるのが好ましく、１～１０Ｌ／分であるのがより好ましい。希釈ガスの場合には、希釈ガスの流量が、０．００１～２Ｌ／分であるのが好ましく、０．１～１Ｌ／分であるのがより好ましい。
（成膜工程）
　成膜工程では、前記基体近傍で前記霧化液滴を熱反応させることによって、基体上に、前記半導体膜を成膜する。熱反応は、熱でもって前記霧化液滴が反応すればそれでよく、反応条件等も本発明の目的を阻害しない限り特に限定されない。本工程においては、前記熱反応を、通常、溶媒の蒸発温度以上の温度で行うが、高すぎない温度（例えば１０００℃）以下が好ましく、６５０℃以下がより好ましく、３００℃～６５０℃が最も好ましい。また、熱反応は、本発明の目的を阻害しない限り、真空下、非酸素雰囲気下（例えば、不活性ガス雰囲気下等）、還元ガス雰囲気下および酸素雰囲気下のいずれの雰囲気下で行われてもよいが、不活性ガス雰囲気下または酸素雰囲気下で行われるのが好ましい。また、大気圧下、加圧下および減圧下のいずれの条件下で行われてもよいが、本発明の実施態様においては、大気圧下で行われるのが好ましい。なお、膜厚は、成膜時間を調整することにより、設定することができる。
（基体）
　前記基体は、前記半導体膜を支持できるものであれば特に限定されない。前記基体の材料も、本発明の目的を阻害しない限り特に限定されず、公知の基体であってよく、有機化合物であってもよいし、無機化合物であってもよい。前記基体の形状としては、どのような形状のものであってもよく、あらゆる形状に対して有効であり、例えば、平板や円板等の板状、繊維状、棒状、円柱状、角柱状、筒状、螺旋状、球状、リング状などが挙げられるが、本発明の実施態様においては、基板が好ましい。基板の厚さは、本発明の実施態様においては特に限定されない。
　前記基板は、板状であって、前記半導体膜の支持体となるものであれば特に限定されない。絶縁体基板であってもよいし、半導体基板であってもよいし、金属基板や導電性基板であってもよいが、前記基板が、絶縁体基板であるのが好ましく、また、表面に金属膜を有する基板であるのも好ましい。前記基板としては、例えば、コランダム構造を有する基板材料を主成分として含む下地基板、またはβ－ガリア構造を有する基板材料を主成分として含む下地基板、六方晶構造を有する基板材料を主成分として含む下地基板などが挙げられる。ここで、「主成分」とは、前記特定の結晶構造を有する基板材料が、原子比で、基板材料の全成分に対し、好ましくは５０％以上、より好ましくは７０％以上、更に好ましくは９０％以上含まれることを意味し、１００％であってもよい。
　基板材料は、本発明の目的を阻害しない限り、特に限定されず、公知のものであってよい。前記のコランダム構造を有する基板材料としては、例えば、α－Ａｌ２Ｏ３（サファイア基板）またはα－Ｇａ２Ｏ３が好適に挙げられ、ａ面サファイア基板、ｍ面サファイア基板、ｒ面サファイア基板、ｃ面サファイア基板や、α型酸化ガリウム基板（ａ面、ｍ面またはｒ面）などがより好適な例として挙げられる。β－ガリア構造を有する基板材料を主成分とする下地基板としては、例えばβ－Ｇａ２Ｏ３基板、又はＧａ２Ｏ３とＡｌ２Ｏ３とを含みＡｌ２Ｏ３が０ｗｔ％より多くかつ６０ｗｔ％以下である混晶体基板などが挙げられる。また、六方晶構造を有する基板材料を主成分とする下地基板としては、例えば、ＳｉＣ基板、ＺｎＯ基板、ＧａＮ基板などが挙げられる。
　本発明の実施態様においては、前記成膜工程の後、アニール処理を行ってもよい。アニールの処理温度は、本発明の目的を阻害しない限り特に限定されず、通常、３００℃～６５０℃であり、好ましくは３５０℃～５５０℃である。また、アニールの処理時間は、通常、１分間～４８時間であり、好ましくは１０分間～２４時間であり、より好ましくは３０分間～１２時間である。なお、アニール処理は、本発明の目的を阻害しない限り、どのような雰囲気下で行われてもよい。非酸素雰囲気下であってもよいし、酸素雰囲気下であってもよい。非酸素雰囲気下としては、例えば、不活性ガス雰囲気下（例えば、窒素雰囲気下）または還元ガス雰囲気下等が挙げられるが、本発明の実施態様においては、不活性ガス雰囲気下が好ましく、窒素雰囲気下であるのがより好ましい。
　また、本発明の実施態様においては、前記基体上に、直接、前記半導体膜を設けてもよいし、応力緩和層（例えば、バッファ層、ＥＬＯ層等）、剥離犠牲層等の他の層を介して前記半導体膜を設けてもよい。各層の形成手段は、特に限定されず、公知の手段であってよいが、本発明の実施態様においては、ミストＣＶＤ法が好ましい。
　本発明の実施態様においては、前記半導体膜を、前記基体等から剥離する等の公知の手段を用いた後に、前記半導体層として半導体装置に用いてもよいし、そのまま前記半導体層として半導体装置に用いてもよい。
　前記ソース電極は、導電性を有するものであれば、本発明の目的を阻害しない限り、特に限定されない。前記ソース電極の構成材料は、導電性無機材料であってもよいし、導電性有機材料であってもよい。本発明の実施態様においては、前記ソース電極の材料が、金属であるのが好ましい。前記金属としては、好適には、例えば、周期律表第４族～第１０族から選ばれる少なくとも１種の金属等が挙げられる。周期律表第４族の金属としては、例えば、チタン（Ｔｉ）、ジルコニウム（Ｚｒ）、ハフニウム（Ｈｆ）などが挙げられる。周期律表第５族の金属としては、例えば、バナジウム（Ｖ）、ニオブ（Ｎｂ）、タンタル（Ｔａ）などが挙げられる。周期律表第６族の金属としては、例えば、クロム（Ｃｒ）、モリブデン（Ｍｏ）およびタングステン（Ｗ）などが挙げられる。周期律表第７族の金属としては、例えば、マンガン（Ｍｎ）、テクネチウム（Ｔｃ）、レニウム（Ｒｅ）などが挙げられる。周期律表第８族の金属としては、例えば、鉄（Ｆｅ）、ルテニウム（Ｒｕ）、オスミウム（Ｏｓ）などが挙げられる。周期律表第９族の金属としては、例えば、コバルト（Ｃｏ）、ロジウム（Ｒｈ）、イリジウム（Ｉｒ）などが挙げられる。周期律表第１０族の金属としては、例えば、ニッケル（Ｎｉ）、パラジウム（Ｐｄ）、白金（Ｐｔ）などが挙げられる。本発明の実施態様においては、前記ソース電極が、チタン（Ｔｉ）、タンタル（Ｔａ）およびタングステン（Ｗ）から選ばれる少なくとも１種の金属を含むのが好ましい。また、本発明の実施態様においては、前記ソース電極が導電性金属酸化物を含んでいてもよい。前記ソース電極に含まれる導電性金属酸化物としては、例えば、酸化錫、酸化亜鉛、酸化インジウム、酸化インジウム錫（ＩＴＯ）、酸化亜鉛インジウム（ＩＺＯ）等の金属酸化物導電膜が挙げられる。前記ソース電極は、単層で構成されていてもよいし、複数の金属層を含むものであってもよい。前記ソース電極が複数の金属層を含む場合、例えば、第１の層および第３の層に周期律表第４族金属を用いて、第１層の層と第３の層との間に位置する第２の層に周期律表第１３族金属（例えば、Ａｌ等）を用いるのが好ましい。このような好ましい構成のソース電極を用いることにより、ソース電極・ソース領域間のオーミック特性の信頼性をより向上させることができる。前記ソース電極の形成方法は、特に限定されない。前記ソース電極の形成方法としては、具体的には例えば、ドライ法やウェット法などが挙げられる。ドライ法としては、例えば、スパッタ、真空蒸着、ＣＶＤ等が挙げられる。ウェット法としては、例えば、スクリーン印刷やダイコート等が挙げられる。
　本発明の実施態様においては、前記ソース電極が、前記電流遮断層とコンタクトを形成しているのが好ましく、前記ソース電極が、前記電流遮断層と直接コンタクトを形成しているのがより好ましい。このような好ましい構成とすることにより、前記半導体装置の応答性をより向上することができる。
　本発明の半導体装置は、様々な半導体素子に有用であり、とりわけ、パワーデバイスに有用である。また、半導体素子は、電極が半導体層の片面側に形成され、半導体層の膜厚方向と垂直方向に電流が流れる横型の素子（横型デバイス）と、半導体層の表裏両面側にそれぞれ電極を有し、半導体層の膜厚方向に電流が流れる縦型の素子（縦型デバイス）に分類することができ、本発明の実施態様においては、前記半導体素子を横型デバイスにも縦型デバイスにも好適に用いることができるが、中でも縦型デバイスに用いることが好ましい。前記半導体素子としては、例えば、金属半導体電界効果トランジスタ（ＭＥＳＦＥＴ）、高電子移動度トランジスタ（ＨＥＭＴ）、金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）、静電誘導トランジスタ（ＳＩＴ）、接合電界効果トランジスタ（ＪＦＥＴ）または絶縁ゲート型バイポーラトランジスタ（ＩＧＢＴ）などが挙げられる。本発明の実施態様においては、前記半導体装置が、ＭＯＳＦＥＴ、ＳＩＴ、ＪＦＥＴまたはＩＧＢＴであるのが好ましく、ＭＯＳＦＥＴまたはＩＧＢＴであるのがより好ましい。
　以下、前記半導体装置の好適な例を、図面を用いて説明するが、本発明はこれら実施の態様に限定されるものではない。なお、以下に例示する半導体装置において、本発明の目的を阻害しない限り、さらに他の層（例えば絶縁体層、半絶縁体層、導体層、半導体層、緩衝層またはその他中間層等）などが含まれていてもよいし、また、緩衝層（バッファ層）なども適宜省いてもよい。
　図１は、本発明の好適な実施態様の一つである金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）の主要部を示す。図１のＭＯＳＦＥＴは、ドレイン電極５ｃ、ｎ＋型半導体層３、ドリフト層としてのｎ－型半導体層７、電流遮断層（電流遮断領域）２、チャネル層６、ソース領域（ｎ＋型半導体層）１、ゲート絶縁膜４ａ、層間絶縁膜４ｂ、ゲート電極５ａおよびソース電極５ｂを備える。図１のＭＯＳＦＥＴにおいては、図１から明らかなとおり、ドレイン電極５ｃ上にｎ＋型半導体層３、ｎ－型半導体層（ドリフト層）７、電流遮断層２、チャネル層６およびｎ＋型半導体層（ソース層）１とがこの順に形成されている。ここで、前記ｎ＋型半導体層３、ｎ－型半導体層７、チャネル層６、電流遮断層２およびｎ＋型半導体層１が結晶性酸化物半導体層８を構成している。なお、電流遮断層２は、ドリフト層７上にエピタキシャル成長により形成されている。前記電流遮断層は、前記結晶性酸化物半導体層８の厚み方向からみて前記ソース電極と平面視で重なっており、且つチャネル層の一部と平面視で重なっている。なお、前記電流遮断層は、前記結晶性酸化物半導体層８の厚み方向からみて前記チャネル層の一部とは重ならないような構成となっている。このような構成により、電流遮断効果を維持しつつ、電流経路が確保されている。また、前記電流経路の幅Ｗは、本発明の目的を阻害しない限り、特に限定されない。本発明の実施態様においては、特に、ドリフト層として酸化ガリウム等のバンドギャップの大きな材料を用いる場合、前記電流経路の幅Ｗが、２μｍ以下であるのが好ましい。また、前記電流遮断層の厚さｄも、本発明の目的を阻害しない限り、特に限定されない。本発明の実施態様においては、特に、ドリフト層として酸化ガリウム等のバンドギャップの大きな材料を用いる場合、前記電流遮断層の厚さｄは０．１５μｍ以上であるのが好ましく、０．２μｍ以上であるのがより好ましい。図１のＭＯＳＦＥＴのオン状態では、前記ソース電極５ｂとでドレイン電極５ｃとの間に電圧を印加し、前記ゲート電極５ａに前記ソース電極５ｂに対して正の電圧を与えると、電子（ホール）がチャネル層６に注入され、ターンオンする。オフ状態は、前記ゲート電極の電圧を０Ｖとすることにより、チャネル層６が空乏層で満たされた状態となり、ターンオフする。本発明の実施態様においては、ドリフト層７の主成分としての第１の結晶性酸化物と前記電流遮断層の主成分としての第２の結晶性酸化物とが異なる組成を有するので、前記半導体装置のＭＯＳＦＥＴ動作（ノーマリーオフ動作）を保ちつつ、耐圧性をより向上させることができる。なお、他の好適な実施態様として、図１の半導体装置において、ソース領域（ｎ＋型半導体層）１は、チャネル層６内に少なくとも一部が埋め込まれていてもよい。ソース領域（ｎ＋型半導体層）１がチャネル層６内に埋め込まれている場合の例を図４に示す。図４に示す構造によれば、ゲート絶縁膜にかかる電界の電界集中が生じにくく、ゲート絶縁膜の信頼性をより向上させることができる。
　図５は、本発明の好適な実施態様の一つである金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）の主要部を示す。図５のＭＯＳＦＥＴは、結晶性酸化物半導体層８が少なくともチャネル層６を貫通するトレンチを有しており、且つ、電流遮断層２がチャネル層６の直下に位置している点で図１のＭＯＳＦＥＴと異なる。本発明の実施態様においては、このようなトレンチ型ＭＯＳＦＥＴの場合には、ｓ前記電流遮断層２の厚みが０．２μｍ以下であるのが好ましく、０．１μｍ以下であるのがより好ましい。このような好ましい厚みとすることにより、ＭＯＳＦＥＴの立ち上がり電圧（Ｖｔｈ）への影響を抑えつつ電流遮断効果を奏することができる。
　図１３および図１４は、本発明の好適な実施態様の一つである金属酸化膜半導体電界効果トランジスタ（ＭＯＳＦＥＴ）の主要部を示す。図１３のＭＯＳＦＥＴは、電流遮断層２の底部がゲート絶縁膜４まで延びており、電流遮断層の少なくとも一部がゲート絶縁膜（トレンチ）と接触している点、および電流遮断層２がソース電極５ｂと直接コンタクトしている点で図５のＭＯＳＦＥＴと異なる。これにより、ゲート絶縁膜と接している電流遮断層2端部の電位がソース電極の電位に固定され、ゲート閾値電圧のふらつきがなく確実なスイッチング動作が可能となる。図１３の電流遮断層２のキャリア密度は、１．０×１０１８以下であるのが好ましい。図１３のＭＯＳＦＥＴにおいては、ドレイン電極５ｃ上にｎ＋型半導体層３、ｎ－型半導体層（ドリフト層）７、電流遮断層２、チャネル層６およびｎ＋型半導体層（ソース層）１がこの順に形成されている。また、図１３のＭＯＳＦＥＴは、ｎ＋型半導体層（ソース層）１およびチャネル層６を貫通してｎ－型半導体層（ドリフト層）７に達するトレンチが設けられており、該トレンチ内に、ゲート絶縁膜４を介してゲート電極５ａが設けられている。このような好ましい構成とすることにより、半導体装置のオン抵抗の増加を抑制しつつ、電流遮断層２による効果を良好に発現することができる。なお、図１３のＭＯＳＦＥＴにおいては、チャネル層６が設けられていなくてもよい。また、図１４のＭＯＳＦＥＴは、図１３のＭＯＳＦＥＴの構成に加えて、さらに、トレンチ内に埋め込まれた第２の半導体層（埋込半導体層）１０を備えている。具体的には、図１４のＭＯＳＦＥＴにおいては、ドレイン電極５ｃ上にｎ＋型半導体層３、第１の半導体層（ドリフト層）７、電流遮断層２、チャネル層６およびｎ＋型半導体層（ソース層）１がこの順に形成されている。また、ソース層１およびチャネル層６を貫通して第１の半導体層（ドリフト層）７に達するトレンチが設けられており、該トレンチ内に、ゲート絶縁膜４を介して、ゲート電極５ａが設けられている。また、ゲート絶縁膜４とトレンチ側壁の少なくとも一部との間に、第２の半導体層１０が設けられている。第２の半導体層（埋込半導体層）１０は、ｎ型半導体層であってもよいし、ｐ型半導体層であってもよい。ここで、「ｐ型」の半導体層とは、正孔（ホール）密度が電子密度より大きい半導体層をいい、ホール効果測定によってｐ型であることが確認できるものに限られない。例えば、前記ｐ型半導体層がチャネルとして用いられる場合、電圧印可時にチャネルとして機能するものであれば、前記半導体層は「ｐ型」に含まれる。図１４の半導体装置のように、第２の半導体層（埋込半導体層）１０が設けられている場合には、前記電流遮断層２のキャリア密度は１．０×１０１８以上であってもよい。このような好ましい第２の半導体層１０と電流遮断層２との組合せを用いることにより、オン抵抗をより低減しつつ耐圧性により優れた半導体装置を得ることができる。なお、図１４のＭＯＳＦＥＴにおいては、チャネル層６が設けられていなくてもよい。また、第２の半導体層のキャリア密度は、前記ソース層１よりもキャリア密度が小さい。
　なお、本開示においては、例えば、図１４に示されるように、第１の半導体層（ドリフト層）７、電流遮断層2、チャネル層6およびソース層１がこの順に積層された積層体を含む結晶性酸化物半導体層と、前記ソース層、前記チャネル層および前記電流遮断層を貫通し前記ドリフト層に達するトレンチと、該トレンチ内にゲート絶縁膜４を介して設けられているゲート電極５ａとを少なくとも備える半導体装置であって、前記ゲート絶縁膜４と前記トレンチ側壁の前記チャネル層および前記電流遮断層の少なくとも一部との間に、第２の半導体層１０が設けられており、前記第１の半導体層７が第１の結晶性酸化物半導体を主成分として含み、前記第２の半導体層１０が、第２の結晶性酸化物半導体を主成分として含む半導体装置もまた、新規且つ有用であり、本発明の他の実施形態の一つとして含めることができる。このような構成とすることにより、半導体装置のオン抵抗をより低減しつつ、耐圧性を優れたものとすることができる。なお、この場合、半導体装置は電流遮断層２を含んでいてもよいし、含んでいなくてもよい。前記第１および／または第２の結晶性酸化物半導体は、上記した結晶性酸化物半導体と同様であってよい。また、前記第１の結晶性酸化物半導体と前記第２の結晶性酸化物半導体とは、互いに同じ組成を有してもよいし、互いに異なる組成を有していてもよい。前記第１の半導体層と前記第２の半導体層とは同じドーパントを含んでいてもよいし、異なるドーパントを含んでいてもよい。また第１の結晶性酸化物半導体と第２の結晶性酸化物半導体とが異なる組成を有する場合、第２の結晶性酸化物半導体は、前記電流遮断層の構成材料として例示した材料であるのも好ましい。例えば、第２の結晶性酸化物半導体は、移動度の高いインジウムとガリウムとを含む混晶であっても良いし、p型を形成しやすいイリジウムとガリウムとを含む混晶であっても良い。
　図１、図４、図５、図１３および図１４の各層の形成手段は、本発明の目的を阻害しない限り、特に限定されず、公知の手段であってよい。例えば、真空蒸着法やＣＶＤ法、スパッタ法、各種コーティング技術により成膜した後、フォトリソグラフィー法によりパターニングする手段、または印刷技術などを用いて直接パターニングを行う手段などが挙げられる。
　以下、図１の半導体装置を製造する好適な例を用いて、本発明をより詳細に説明する。図２（ａ）は、基板９上に、ｎ＋型半導体層３、ドリフト層（ｎ－型半導体層）７および電流遮断層（電流遮断領域）２がこの順に積層されている積層構造体を示す。前記電流遮断層２は、公知のパターニング技術を用いてパターン形成されている。図２（ａ）の積層体上に、チャネル層６、ソース領域としてのｎ＋型半導体層１を形成することにより、図２（ｂ）の積層体を得る。なお、前記ｎ＋型半導体層１は、例えばミストＣＶＤ法等のエピタキシャル成長方法を用いて成膜した後、公知のエッチング技術を用いてエッチングすることにより、パターン形成される。ついで、図２（ｂ）の積層体上に、ゲート絶縁膜４ａおよびゲート電極５ａを形成し、さらに層間絶縁膜４ｂおよびコンタクトホールを形成することにより、図２（ｃ）の積層体を得る。前記ゲート絶縁膜４ａおよびゲート電極５ａは、それぞれ公知の成膜方法を用いて成膜した後、公知のエッチング技術を用いてエッチングすることにより、図２（ｃ）に示す形状に加工することができる。
　次に、図２（ｃ）の積層体上に、公知の成膜方法を用いてソース電極５ｂを形成して、図３（ｄ）の積層体を得る。前記ソース電極５ｂの成膜方法としては、上記したドライ法またはウェット法等が挙げられる。ついで、図３（ｄ）の積層体における基板９を除去した後、公知の成膜方法を用いてドレイン電極５ｃを形成することにより、図３（ｅ）の半導体装置を得ることができる。図３（ｅ）の半導体装置は、上述のように、ドリフト層の主成分である第１の結晶性酸化物と、電流遮断層の主成分である第２の結晶性酸化物とが異なる組成を有しているので、ＭＯＳＦＥＴ動作を保ちつつ、耐圧性により優れたものとなる。
　また、本実施例として、前記電流遮断層による耐圧向上効果を確認するために、図６に示す構造の半導体装置を、試作した。実施例の構成は以下に示すとおりである。ｎ－型半導体層３として、スズドープα－Ｇａ２Ｏ３からなるｎ－型半導体層、ｎ＋型半導体層１ａとして、スズドープα－Ｇａ２Ｏ３からなるｎ＋型半導体層を用いた。また、電流遮断層として、ＩｒＧａＯ（Ｉｒ比率１０％）を用いた。また、比較例として、電流遮断層を設けないこと以外は、実施例１と同様にして半導体装置を試作した。実施例１で作製した半導体装置のＩ－Ｖ測定の結果を図７に示す。図７から明らかなように、本発明の実施態様における半導体装置は、耐圧が１４００Ｖを超えており、耐圧性に優れていることがわかる。また、比較例における耐圧は６００Ｖ程度であった。実施例および比較例から明らかなように、本発明の実施態様にかかる半導体装置は、耐圧性が向上されたものであることがわかる。このことは、酸化ガリウム（特にα－Ｇａ２Ｏ３）を用いた半導体装置を試作して初めて得られた新知見である。
　上述した本発明の実施態様にかかる半導体装置は、上記した機能を発揮させるべく、インバータやコンバータなどの電力変換装置に適用することができる。より具体的には、スイッチング素子であるサイリスタ、パワートランジスタ、ＩＧＢＴ（Ｉｎｓｕｌａｔｅｄ　Ｇａｔｅ　Ｂｉｐｏｌａｒ　Ｔｒａｎｓｉｓｔｏｒ）、ＭＯＳＦＥＴ（Ｍｅｔａｌ－Ｏｘｉｄｅ－Ｓｅｍｉｃｏｎｄｕｃｔｏｒ　Ｆｉｅｌｄ　Ｅｆｆｅｃｔ　Ｔｒａｎｓｉｓｔｏｒ）等として適用することができる。図９は、本発明の実施態様に係る半導体装置を用いた制御システムの一例を示すブロック構成図、図１０は同制御システムの回路図であり、特に電気自動車（Ｅｌｅｃｔｒｉｃ　Ｖｅｈｉｃｌｅ）への搭載に適した制御システムである。
　図９に示すように、制御システム５００はバッテリー（電源）５０１、昇圧コンバータ５０２、降圧コンバータ５０３、インバータ５０４、モータ（駆動対象）５０５、駆動制御部５０６を有し、これらは電気自動車に搭載されてなる。バッテリー５０１は例えばニッケル水素電池やリチウムイオン電池などの蓄電池からなり、給電ステーションでの充電あるいは減速時の回生エネルギーなどにより電力を貯蔵するとともに、電気自動車の走行系や電装系の動作に必要となる直流電圧を出力することができる。昇圧コンバータ５０２は例えばチョッパ回路を搭載した電圧変換装置であり、バッテリー５０１から供給される例えば２００Ｖの直流電圧を、チョッパ回路のスイッチング動作により例えば６５０Ｖに昇圧して、モータなどの走行系に出力することができる。降圧コンバータ５０３も同様にチョッパ回路を搭載した電圧変換装置であるが、バッテリー５０１から供給される例えば２００Ｖの直流電圧を、例えば１２Ｖ程度に降圧することで、パワーウインドーやパワーステアリング、あるいは車載の電気機器などを含む電装系に出力することができる。
　インバータ５０４は、昇圧コンバータ５０２から供給される直流電圧をスイッチング動作により三相の交流電圧に変換してモータ５０５に出力する。モータ５０５は電気自動車の走行系を構成する三相交流モータであり、インバータ５０４から出力される三相の交流電圧によって回転駆動され、その回転駆動力を図示しないトランスミッション等を介して電気自動車の車輪に伝達する。
　一方、図示しない各種センサを用いて、走行中の電気自動車から車輪の回転数やトルク、アクセルペダルの踏み込み量（アクセル量）などの実測値が計測され、これらの計測信号が駆動制御部５０６に入力される。また同時に、インバータ５０４の出力電圧値も駆動制御部５０６に入力される。駆動制御部５０６はＣＰＵ（Ｃｅｎｔｒａｌ　Ｐｒｏｃｅｓｓｉｎｇ　Ｕｎｉｔ）などの演算部やメモリなどのデータ保存部を備えたコントローラの機能を有するもので、入力された計測信号を用いて制御信号を生成してインバータ５０４にフィードバック信号として出力することで、スイッチング素子によるスイッチング動作を制御する。これによって、インバータ５０４がモータ５０５に与える交流電圧が瞬時に補正されることで、電気自動車の運転制御を正確に実行させることができ、電気自動車の安全・快適な動作が実現する。なお、駆動制御部５０６からのフィードバック信号を昇圧コンバータ５０２に与えることで、インバータ５０４への出力電圧を制御することも可能である。
　図１０は、図９における降圧コンバータ５０３を除いた回路構成、すなわちモータ５０５を駆動するための構成のみを示した回路構成である。同図に示されるように、本発明の半導体装置は、例えばショットキーバリアダイオードとして昇圧コンバータ５０２およびインバータ５０４に採用されることでスイッチング制御に供される。昇圧コンバータ５０２においてはチョッパ回路に組み込まれてチョッパ制御を行い、またインバータ５０４においてはＩＧＢＴを含むスイッチング回路に組み込まれてスイッチング制御を行う。なお、バッテリー５０１の出力にインダクタ（コイルなど）を介在させることで電流の安定化を図り、またバッテリー５０１、昇圧コンバータ５０２、インバータ５０４のそれぞれの間にキャパシタ（電解コンデンサなど）を介在させることで電圧の安定化を図っている。
　また、図１０中に点線で示すように、駆動制御部５０６内にはＣＰＵ（Ｃｅｎｔｒａｌ　Ｐｒｏｃｅｓｓｉｎｇ　Ｕｎｉｔ）からなる演算部５０７と不揮発性メモリからなる記憶部５０８が設けられている。駆動制御部５０６に入力された信号は演算部５０７に与えられ、必要な演算を行うことで各半導体素子に対するフィードバック信号を生成する。また記憶部５０８は、演算部５０７による演算結果を一時的に保持したり、駆動制御に必要な物理定数や関数などをテーブルの形で蓄積して演算部５０７に適宜出力する。演算部５０７や記憶部５０８は公知の構成を採用することができ、その処理能力等も任意に選定できる。
　図９や図１０に示されるように、制御システム５００においては、昇圧コンバータ５０２、降圧コンバータ５０３、インバータ５０４のスイッチング動作にはダイオードやスイッチング素子であるサイリスタ、パワートランジスタ、ＩＧＢＴ、ＭＯＳＦＥＴ等が用いられる。これらの半導体素子に酸化ガリウム（Ｇａ２Ｏ３）、特にコランダム型酸化ガリウム（α－Ｇａ２Ｏ３）をその材料として用いることでスイッチング特性が大幅に向上する。さらに、本発明に係る半導体装置等を適用することで、極めて良好なスイッチング特性が期待できるとともに、制御システム５００の一層の小型化やコスト低減が実現可能となる。すなわち、昇圧コンバータ５０２、降圧コンバータ５０３、インバータ５０４のそれぞれが本発明による効果を期待できるものとなり、これらのいずれか一つ、もしくは任意の二つ以上の組合せ、あるいは駆動制御部５０６も含めた形態のいずれにおいても本発明の効果を期待することができる。
　なお、上述の制御システム５００は本発明の半導体装置を電気自動車の制御システムに適用できるだけではなく、直流電源からの電力を昇圧・降圧したり、直流から交流へ電力変換するといったあらゆる用途の制御システムに適用することが可能である。また、バッテリーとして太陽電池などの電源を用いることも可能である。
　図１１は、本発明の実施態様に係る半導体装置を採用した制御システムの他の例を示すブロック構成図、図１２は同制御システムの回路図であり、交流電源からの電力で動作するインフラ機器や家電機器等への搭載に適した制御システムである。
　図１１に示すように、制御システム６００は、外部の例えば三相交流電源（電源）６０１から供給される電力を入力するもので、ＡＣ／ＤＣコンバータ６０２、インバータ６０４、モータ（駆動対象）６０５、駆動制御部６０６を有し、これらは様々な機器（後述する）に搭載することができる。三相交流電源６０１は、例えば電力会社の発電施設（火力発電所、水力発電所、地熱発電所、原子力発電所など）であり、その出力は変電所を介して降圧されながら交流電圧として供給される。また、例えば自家発電機等の形態でビル内や近隣施設内に設置されて電力ケーブルで供給される。ＡＣ／ＤＣコンバータ６０２は交流電圧を直流電圧に変換する電圧変換装置であり、三相交流電源６０１から供給される１００Ｖや２００Ｖの交流電圧を所定の直流電圧に変換する。具体的には、電圧変換により３．３Ｖや５Ｖ、あるいは１２Ｖといった、一般的に用いられる所望の直流電圧に変換される。駆動対象がモータである場合には１２Ｖへの変換が行われる。なお、三相交流電源に代えて単相交流電源を採用することも可能であり、その場合にはＡＣ／ＤＣコンバータを単相入力のものとすれば同様のシステム構成とすることができる。
　インバータ６０４は、ＡＣ／ＤＣコンバータ６０２から供給される直流電圧をスイッチング動作により三相の交流電圧に変換してモータ６０５に出力する。モータ６０４は、制御対象によりその形態が異なるが、制御対象が電車の場合には車輪を、工場設備の場合にはポンプや各種動力源を、家電機器の場合にはコンプレッサなどを駆動するための三相交流モータであり、インバータ６０４から出力される三相の交流電圧によって回転駆動され、その回転駆動力を図示しない駆動対象に伝達する。
　なお、例えば家電機器においてはＡＣ／ＤＣコンバータ３０２から出力される直流電圧をそのまま供給することが可能な駆動対象も多く（例えばパソコン、ＬＥＤ照明機器、映像機器、音響機器など）、その場合には制御システム６００にインバータ６０４は不要となり、図１１中に示すように、ＡＣ／ＤＣコンバータ６０２から駆動対象に直流電圧を供給する。この場合、例えばパソコンなどには３．３Ｖの直流電圧が、ＬＥＤ照明機器などには５Ｖの直流電圧が供給される。
　一方、図示しない各種センサを用いて、駆動対象の回転数やトルク、あるいは駆動対象の周辺環境の温度や流量などといった実測値が計測され、これらの計測信号が駆動制御部６０６に入力される。また同時に、インバータ６０４の出力電圧値も駆動制御部６０６に入力される。これらの計測信号をもとに、駆動制御部６０６はインバータ６０４にフィードバック信号を与え、スイッチング素子によるスイッチング動作を制御する。これによって、インバータ６０４がモータ６０５に与える交流電圧が瞬時に補正されることで、駆動対象の運転制御を正確に実行させることができ、駆動対象の安定した動作が実現する。また、上述のように、駆動対象が直流電圧で駆動可能な場合には、インバータへのフィードバックに代えてＡＣ／ＤＣコンバータ６０２をフィードバック制御することも可能である。
　図１２は、図１１の回路構成を示したものである。同図に示されるように、本発明の半導体装置は、例えばショットキーバリアダイオードとしてＡＣ／ＤＣコンバータ６０２およびインバータ６０４に採用されることでスイッチング制御に供される。ＡＣ／ＤＣコンバータ６０２は、例えばショットキーバリアダイオードをブリッジ状に回路構成したものが用いられ、入力電圧の負電圧分を正電圧に変換整流することで直流変換を行う。またインバータ６０４においてはＩＧＢＴにおけるスイッチング回路に組み込まれてスイッチング制御を行う。なお、ＡＣ／ＤＣコンバータ６０２とインバータ６０４の間にキャパシタ（電解コンデンサなど）を介在させることで電圧の安定化を図っている。
　また、図１２中に点線で示すように、駆動制御部６０６内にはＣＰＵからなる演算部６０７と不揮発性メモリからなる記憶部６０８が設けられている。駆動制御部６０６に入力された信号は演算部６０７に与えられ、必要な演算を行うことで各半導体素子に対するフィードバック信号を生成する。また記憶部６０８は、演算部６０７による演算結果を一時的に保持したり、駆動制御に必要な物理定数や関数などをテーブルの形で蓄積して演算部６０７に適宜出力する。演算部６０７や記憶部６０８は公知の構成を採用することができ、その処理能力等も任意に選定できる。
　このような制御システム６００においても、図９や図１０に示した制御システム５００と同様に、ＡＣ／ＤＣコンバータ６０２やインバータ６０４の整流動作やスイッチング動作にはダイオードやスイッチング素子であるサイリスタ、パワートランジスタ、ＩＧＢＴ、ＭＯＳＦＥＴ等が用いられる。これら半導体素子に酸化ガリウム（Ｇａ２Ｏ３）、特にコランダム型酸化ガリウム（α－Ｇａ２Ｏ３）をその材料として用いることでスイッチング特性が向上する。さらに、本発明に係る半導体膜や半導体装置を適用することで、極めて良好なスイッチング特性が期待できるとともに、制御システム６００の一層の小型化やコスト低減が実現可能となる。すなわち、ＡＣ／ＤＣコンバータ６０２、インバータ６０４のそれぞれが本発明による効果を期待できるものとなり、これらのいずれか一つ、もしくは組合せ、あるいは駆動制御部６０６も含めた形態のいずれにおいても本発明の効果を期待することができる。
　なお、図１１および図１２では駆動対象としてモータ６０５を例示したが、駆動対象は必ずしも機械的に動作するものに限られず、交流電圧を必要とする多くの機器を対象とすることができる。制御システム６００においては、交流電源から電力を入力して駆動対象を駆動する限りにおいては適用が可能であり、インフラ機器（例えばビルや工場等の電力設備、通信設備、交通管制機器、上下水処理設備、システム機器、省力機器、電車など）や家電機器（例えば、冷蔵庫、洗濯機、パソコン、ＬＥＤ照明機器、映像機器、音響機器など）といった機器を対象とした駆動制御のために搭載することができる。
　本発明の半導体装置は、半導体（例えば化合物半導体電子デバイス等）、電子部品・電気機器部品、光学・電子写真関連装置、工業部材などあらゆる分野に用いることができるが、とりわけ、パワーデバイスに有用である。
　１　　　　　ソース領域（ｎ＋型半導体層）
　２　　　　　電流遮断層
　３　　　　　ｎ＋型半導体層
　４ａ　　　　ゲート絶縁膜
　４ｂ　　　　層間絶縁膜
　５ａ　　　　ゲート電極
　５ｂ　　　　ソース電極
　５ｃ　　　　ドレイン電極
　６　　　　　チャネル層
　７　　　　　ｎ－型半導体層（ドリフト層／第１の半導体層）
　８　　　　　結晶性酸化物半導体層
　９　　　　　基板
　１０　　　　第２の半導体層（埋込半導体層）
　２１　　　　成膜装置（ミストＣＶＤ装置）
　２２ａ　　　キャリアガス源
　２２ｂ　　　キャリアガス（希釈）源
　２３ａ　　　流量調節弁
　２３ｂ　　　流量調節弁
　２４　　　　ミスト発生源
　２４ａ　　　原料溶液
　２４ｂ　　　原料微粒子
　２５　　　　容器
　２５ａ　　　水
　２６　　　　超音波振動子
　２７　　　　成膜室
　２８　　　　ホットプレート
　２９　　　　供給管
　３０　　　　基板
　１０１ａ　　ｎ－型半導体層
　１０１ｂ　　ｎ＋型半導体層
　１０２　　　電流遮断層
　１０９　　　基板
　１０５ａ　　ショットキー電極
　５００　　　制御システム
　５０１　　　バッテリー（電源）
　５０２　　　昇圧コンバータ
　５０３　　　降圧コンバータ
　５０４　　　インバータ
　５０５　　　モータ（駆動対象）
　５０６　　　駆動制御部
　５０７　　　演算部
　５０８　　　記憶部
　６００　　　制御システム
　６０１　　　三相交流電源（電源）
　６０２　　　ＡＣ／ＤＣコンバータ
　６０４　　　インバータ
　６０５　　　モータ（駆動対象）
　６０６　　　駆動制御部
　６０７　　　演算部
　６０８　　　記憶部

 

Claims (15)

  1. 　チャネル層およびドリフト層を含む結晶性酸化物半導体層と、該チャネル層上にゲート絶縁膜を介して配置されているゲート電極とを少なくとも備え、前記チャネル層と前記ドリフト層との間に電流遮断層を有する半導体装置であって、前記ドリフト層が第１の結晶性酸化物を主成分として含み、前記電流遮断層が、第２の結晶性酸化物を主成分として含み、前記第１の結晶性酸化物と前記第２の結晶性酸化物とが異なる組成を有することを特徴とする半導体装置。
  2. 　前記第１の結晶性酸化物が、アルミニウム、インジウムおよびガリウムから選ばれる少なくとも１種の金属を含有する請求項１記載の半導体装置。
  3. 　前記第１の結晶性酸化物が、コランダム構造を有する請求項１または２に記載の半導体装置。
  4. 　前記第２の結晶性酸化物が、周期律表第６族～第１０族から選ばれる少なくとも１種の金属を含有する請求項１～３のいずれかに記載の半導体装置。
  5. 　前記第２の結晶性酸化物が、周期律表第６族～第１０族から選ばれる少なくとも１種の金属と、周期律表第１３族金属とを少なくとも含む混晶である請求項１～４のいずれかに記載の半導体装置。
  6. 　前記第２の結晶性酸化物が、周期律表第９族金属と周期律表第１３族金属とを少なくとも含む混晶である請求項１～５のいずれかに記載の半導体装置。
  7. 　前記第２の結晶性酸化物のバンドギャップが、３．０ｅＶ以上である請求項１～６のいずれかに記載の半導体装置。
  8. 　前記電流遮断層が、ｐ型の導電型を有する請求項１～７のいずれかに記載の半導体装置。
  9. 　前記チャネル層の少なくとも一部にソース領域を有しており、前記ソース領域上にソース電極を備えている請求項１～８のいずれかに記載の半導体装置。
  10. 　前記ソース電極が、前記電流遮断層と直接コンタクトしている請求項１～９のいずれかに記載の半導体装置。
  11. 　前記結晶性酸化物半導体層が、少なくともチャネル層を貫通するトレンチを有しており、該トレンチ内に前記ゲート電極の少なくとも一部が前記ゲート絶縁膜を介して埋め込まれている請求項１～１０のいずれかに記載の半導体装置。
  12. 　トランジスタである請求項１～１１のいずれかに記載の半導体装置。
  13. 　第１の半導体層としてのドリフト層、チャネル層およびソース層がこの順に積層された積層体を含む結晶酸化物半導体層と、前記ソース層およびチャネル層を貫通し前記第１の半導体層に達するトレンチと、該トレンチ内にゲート絶縁膜を介して設けられているゲート電極とを少なくとも備える半導体装置であって、前記ゲート絶縁膜と前記トレンチ側壁の前記チャネル層に接した部分の少なくとも一部との間に、第２の半導体層が設けられており、前記第１の半導体層が第１の結晶性酸化物半導体を主成分として含み、前記第２の半導体層が、第２の結晶性酸化物半導体を主成分として含むことを特徴とする半導体装置。
  14. 　請求項１～１３のいずれかに記載の半導体装置を用いた電力変換装置。
  15. 　請求項１～１３のいずれかに記載の半導体装置を用いた制御システム。

     
PCT/JP2022/018787 2021-04-26 2022-04-25 半導体装置 WO2022230831A1 (ja)