WO2022097476A1 - Produit cosmétique - Google Patents
Produit cosmétique Download PDFInfo
- Publication number
- WO2022097476A1 WO2022097476A1 PCT/JP2021/038745 JP2021038745W WO2022097476A1 WO 2022097476 A1 WO2022097476 A1 WO 2022097476A1 JP 2021038745 W JP2021038745 W JP 2021038745W WO 2022097476 A1 WO2022097476 A1 WO 2022097476A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- component
- powder
- iron
- preferable
- cosmetic
- Prior art date
Abstract
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN202180073212.0A CN116782874A (zh) | 2020-11-04 | 2021-10-20 | 化妆品 |
JP2022560706A JPWO2022097476A1 (fr) | 2020-11-04 | 2021-10-20 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2020184059 | 2020-11-04 | ||
JP2020-184059 | 2020-11-04 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2022097476A1 true WO2022097476A1 (fr) | 2022-05-12 |
Family
ID=81457233
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2021/038745 WO2022097476A1 (fr) | 2020-11-04 | 2021-10-20 | Produit cosmétique |
Country Status (4)
Country | Link |
---|---|
JP (1) | JPWO2022097476A1 (fr) |
CN (1) | CN116782874A (fr) |
TW (1) | TW202233157A (fr) |
WO (1) | WO2022097476A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2024085115A1 (fr) * | 2022-10-17 | 2024-04-25 | 株式会社コーセー | Produit cosmétique en poudre solide |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH11279432A (ja) * | 1998-03-30 | 1999-10-12 | Shiseido Co Ltd | 合成フッ素金雲母粉末を用いた着色剤、およびそれを配合した化粧料 |
JP2000290526A (ja) * | 1999-04-02 | 2000-10-17 | Topy Ind Ltd | パール光沢顔料及び該顔料を含有する塗料組成物、化粧料、インキ並びにプラスチック |
JP2006348007A (ja) * | 2005-06-13 | 2006-12-28 | Milott:Kk | 化粧料 |
JP2008088317A (ja) * | 2006-10-03 | 2008-04-17 | Kose Corp | 白色複合粉体及びそれを配合した化粧料 |
JP2011063560A (ja) * | 2009-09-18 | 2011-03-31 | Nippon Menaade Keshohin Kk | 固形粉末化粧料 |
JP2016037497A (ja) * | 2014-08-08 | 2016-03-22 | 株式会社 資生堂 | 固形粉末化粧料 |
-
2021
- 2021-10-20 JP JP2022560706A patent/JPWO2022097476A1/ja active Pending
- 2021-10-20 WO PCT/JP2021/038745 patent/WO2022097476A1/fr active Application Filing
- 2021-10-20 CN CN202180073212.0A patent/CN116782874A/zh active Pending
- 2021-10-29 TW TW110140211A patent/TW202233157A/zh unknown
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH11279432A (ja) * | 1998-03-30 | 1999-10-12 | Shiseido Co Ltd | 合成フッ素金雲母粉末を用いた着色剤、およびそれを配合した化粧料 |
JP2000290526A (ja) * | 1999-04-02 | 2000-10-17 | Topy Ind Ltd | パール光沢顔料及び該顔料を含有する塗料組成物、化粧料、インキ並びにプラスチック |
JP2006348007A (ja) * | 2005-06-13 | 2006-12-28 | Milott:Kk | 化粧料 |
JP2008088317A (ja) * | 2006-10-03 | 2008-04-17 | Kose Corp | 白色複合粉体及びそれを配合した化粧料 |
JP2011063560A (ja) * | 2009-09-18 | 2011-03-31 | Nippon Menaade Keshohin Kk | 固形粉末化粧料 |
JP2016037497A (ja) * | 2014-08-08 | 2016-03-22 | 株式会社 資生堂 | 固形粉末化粧料 |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2024085115A1 (fr) * | 2022-10-17 | 2024-04-25 | 株式会社コーセー | Produit cosmétique en poudre solide |
Also Published As
Publication number | Publication date |
---|---|
TW202233157A (zh) | 2022-09-01 |
JPWO2022097476A1 (fr) | 2022-05-12 |
CN116782874A (zh) | 2023-09-19 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2015166459A1 (fr) | Composition comportant des microcapsules contenant des particules ayant un point élevé à l'état humide | |
CN107921291B (zh) | 用于对角蛋白材料进行护理和/或化妆的包含包封至少一种反射剂的油性分散体的微胶囊的水包油乳液 | |
US20180116947A1 (en) | Water in oil emulsion providing skin mattity and true color | |
WO2019225491A1 (fr) | Nouvelle poudre d'oxyde de titane et produit cosmétique formulé avec cette poudre | |
EP3362034A1 (fr) | Composition comprenant une charge à effet de flou et un pigment composite à base d'alumine non sphérique et d'un oxyde métallique | |
JP5491540B2 (ja) | 化粧料の製造方法 | |
WO2018100065A1 (fr) | Composition cosmétique comprenant de la cellulose nanocristalline, procédé et utilisation associés | |
JP6514859B2 (ja) | メイクアップ化粧料 | |
JP6815098B2 (ja) | 油中水型乳化化粧料 | |
JP2021501192A (ja) | セルロース、窒化ホウ素及びサテン光沢を呈する真珠光沢剤の粒子を含む、明るさを与えるサテン光沢効果を有する組成物 | |
JP6629962B2 (ja) | 少なくとも1つの反射剤の油性分散体を封入するマイクロカプセルを含む、ケラチン物質をケアし、および/またはメイクアップするための水性組成物 | |
WO2022097476A1 (fr) | Produit cosmétique | |
ES2768686T3 (es) | Emulsión de agua en aceite para el cuidado y/o el maquillaje de materiales queratínicos que comprende microcápsulas que encapsulan una dispersión oleosa de al menos un agente reflectante | |
JP2010235489A (ja) | 含水化粧料 | |
JP6228484B2 (ja) | 多層型油性化粧料 | |
JP5754866B2 (ja) | 化粧料 | |
JP6462583B2 (ja) | テアニンを用いた表面処理粉体及びそれを含有する化粧料 | |
JP6170312B2 (ja) | 含水粉末化粧料 | |
JP2013082649A (ja) | スイゼンジノリ由来糖誘導体被覆処理粉体およびその製造方法並びに化粧料 | |
JP6064192B2 (ja) | 粉体化粧料 | |
WO2021200781A1 (fr) | Produit cosmétique contenant de la poudre | |
JP7227917B2 (ja) | 固形粉末化粧料 | |
JP4733917B2 (ja) | 化粧料 | |
JP2023097497A (ja) | 化粧料 | |
JP5580148B2 (ja) | 表面処理粉体及びその製造方法並びにそれを含有する化粧料 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 21889029 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 2022560706 Country of ref document: JP Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 202180073212.0 Country of ref document: CN |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 21889029 Country of ref document: EP Kind code of ref document: A1 |