WO2022054870A1 - ポリ（３－ヒドロキシアルカノエート）系発泡粒子又はポリ（３－ヒドロキシアルカノエート）系発泡成形体の製造方法 - Google Patents

ポリ（３－ヒドロキシアルカノエート）系発泡粒子又はポリ（３－ヒドロキシアルカノエート）系発泡成形体の製造方法 Download PDF

Info

Publication number
WO2022054870A1
WO2022054870A1 PCT/JP2021/033161 JP2021033161W WO2022054870A1 WO 2022054870 A1 WO2022054870 A1 WO 2022054870A1 JP 2021033161 W JP2021033161 W JP 2021033161W WO 2022054870 A1 WO2022054870 A1 WO 2022054870A1
Authority
WO
WIPO (PCT)
Prior art keywords
poly
p3ha
foamed particles
pressure
hydroxyalkanoate
Prior art date
Application number
PCT/JP2021/033161
Other languages
English (en)
French (fr)
Inventor
徹也 南
Original Assignee
株式会社カネカ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社カネカ filed Critical 株式会社カネカ
Priority to CN202180062026.7A priority Critical patent/CN116075546B/zh
Priority to US18/044,625 priority patent/US20230331950A1/en
Priority to JP2022547648A priority patent/JPWO2022054870A1/ja
Publication of WO2022054870A1 publication Critical patent/WO2022054870A1/ja

Abstract

耐圧容器内で、ポリ（３－ヒドロキシアルカノエート）を含む樹脂粒子、及び、架橋剤を含む水分散体に、発泡剤を導入し、前記耐圧容器の内容物を、１３０～１５０℃の範囲内にある所定温度まで加熱し、該所定温度で５～５５分間保持し、前記耐圧容器の一端を開放し、前記耐圧容器の内容物を低圧の雰囲気下に放出することにより前記樹脂粒子を発泡させて、ポリ（３－ヒドロキシアルカノエート）系発泡粒子を得る。前記ポリ（３－ヒドロキシアルカノエート）は、ポリ（３－ヒドロキシアルカノエート）共重合体とポリ（３－ヒドロキシブチレート）単独重合体を、重量比９９：１～８０：２０で含む混合物であり、前記架橋剤は、パーカーボネート類の有機過酸化物である。

Description

ポリ（３－ヒドロキシアルカノエート）系発泡粒子又はポリ（３－ヒドロキシアルカノエート）系発泡成形体の製造方法
　本発明は、ポリ（３－ヒドロキシアルカノエート）系組成物から構成される樹脂粒子を発泡することによるポリ（３－ヒドロキシアルカノエート）系発泡粒子の製造方法、及び、該発泡粒子を成形することによるポリ（３－ヒドロキシアルカノエート）系発泡成形体の製造方法に関する。
　石油由来プラスチックは毎年大量に廃棄されており、これらの大量廃棄物による埋立て処分場の不足や環境汚染が深刻な問題として取り上げられている。また近年、マイクロプラスチックが、海洋環境において大きな問題になっている。このため海や土等の環境中や埋立て処分場、コンポスト中で微生物の作用によって分解される生分解性プラスチックが注目されている。生分解性プラスチックは、環境中で利用される農林水産業用資材、使用後の回収・再利用が困難な食品容器、包装材料、衛生用品、ゴミ袋等への幅広い応用を目指して、開発が進められている。更に生分解性プラスチックから構成される発泡体は、包装用緩衝材、農産箱、魚箱、自動車部材、建築材料、土木材料等での使用が期待されている。
　前記生分解性プラスチックの中でも、優れた生分解性およびカーボンニュートラルの観点から、植物由来のプラスチックとしてポリ（３－ヒドロキシアルカノエート）（以下、Ｐ３ＨＡと称する場合がある）が注目されている。その中でも、ポリ（３－ヒドロキシブチレート）（以下、Ｐ３ＨＢと称する場合がある）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシバレレート）（以下、Ｐ３ＨＢ３ＨＶと称する場合がある）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシヘキサノエート）（以下、Ｐ３ＨＢ３ＨＨと称する場合がある）、ポリ（３－ヒドロキシブチレート－コ－４－ヒドロキシブチレート）（以下、Ｐ３ＨＢ４ＨＢと称する場合がある）等が注目されている。
　上述の生分解性プラスチックを発泡体用途に展開することが検討されている。例えば、特許文献１には、ゲル分率と融解熱量を特定の範囲としたポリ（３－ヒドロキシアルカノエート）系発泡粒子およびポリ（３－ヒドロキシアルカノエート）系発泡成形体が開示されている。
　また、特許文献２には、ポリ（３－ヒドロキシアルカノエート）とイソシアネート化合物を含み特定値以上の溶融粘度を持つ樹脂組成物からなるポリ（３－ヒドロキシアルカノエート）樹脂発泡粒子が開示されている。
国際公開第２０１９／１４６５５５号 国際公開第２００７／０４９６９４号
　特許文献１では、ポリ（３－ヒドロキシアルカノエート）系発泡粒子のゲル分率と融解熱量を特定の範囲とすることで、表面性が良好、かつ、成形収縮率が小さいポリ（３－ヒドロキシアルカノエート）系発泡成形体が得られることが報告されている。しかしながら、該文献に記載の発泡粒子は、架橋剤として過酸化ベンゾイルを使用して製造されるため、ベンゼン等の芳香族化合物由来の臭気が残る場合があることが、本発明者により確認された。
　特許文献２では、ポリ（３－ヒドロキシアルカノエート）とイソシアネート化合物を押出機等で溶融混練し、特定値以上の溶融粘度を持つ樹脂組成物を得た後、発泡剤を用いて該樹脂組成物を発泡させることで、成形時の加工条件幅が広く、また成形後の後収縮が見られないポリ（３－ヒドロキシアルカノエート）樹脂発泡粒子が得られることが報告されている。しかしながら、イソシアネート化合物は毒性があり、得られる発泡粒子が黄色くなる場合がある。また、該文献の実施例では、発泡剤を導入した後、高温・高圧状態で１時間も保持しており、発泡粒子の生産性が低い。
　以上に鑑み、本発明の目的は、生産性が高く、かつ、臭気が抑制されたポリ（３－ヒドロキシアルカノエート）系発泡粒子を得ることができる製造方法、及び、該発泡粒子を用いたポリ（３－ヒドロキシアルカノエート）系発泡成形体の製造方法を提供することにある。
　本発明者は前記課題を解決するために鋭意研究を重ねた結果、ポリ（３－ヒドロキシアルカノエート）として特定の混合物を使用し、かつ、架橋剤として特定の化合物を使用することに加えて、発泡剤を導入してから特定の温度で特定時間保持することで、生産性は高く、かつ臭気が抑制されたポリ（３－ヒドロキシアルカノエート）系発泡粒子が得られることを見出し、本発明を完成させた。
　第一の本発明は、ポリ（３－ヒドロキシアルカノエート）系発泡粒子の製造方法であって、耐圧容器内で、ポリ（３－ヒドロキシアルカノエート）を含む樹脂粒子、及び、架橋剤を含む水分散体に、発泡剤を導入する工程、前記耐圧容器の内容物を、１３０～１５０℃の範囲内にある所定温度まで加熱し、該所定温度で５～５５分間保持する工程、及び、前記耐圧容器の一端を開放し、前記耐圧容器の内容物を低圧の雰囲気下に放出することにより前記樹脂粒子を発泡させる工程を含み、前記ポリ（３－ヒドロキシアルカノエート）が、ポリ（３－ヒドロキシアルカノエート）共重合体とポリ（３－ヒドロキシブチレート）単独重合体を、重量比９９：１～８０：２０で含む混合物であり、前記架橋剤が、パーカーボネート類の有機過酸化物である、製造方法に関する。
　好ましくは、前記発泡剤が、二酸化炭素である。
　好ましくは、前記ポリ（３－ヒドロキシアルカノエート）共重合体が、３－ヒドロキシブチレートとコモノマーの共重合体であり、該共重合体中のモノマー比率が、３－ヒドロキシブチレート／コモノマー＝９９／１～８９／１１（モル％／モル％）である。
　好ましくは、前記パーカーボネート類の有機過酸化物が、１分間半減期温度が１５０～１７０℃であり、かつ常温で液体である。
　好ましくは、前記パーカーボネート類の有機過酸化物が、カーボネート基を１つ有する化合物である。
　前記製造方法は、好ましくは、前記樹脂粒子を発泡させる工程の後、得られた発泡粒子に無機ガスを含浸させて該発泡粒子内の圧力を高めた後、該発泡粒子を加熱して膨張させる工程をさらに含む。
　また本発明は、前記製造方法によってポリ（３－ヒドロキシアルカノエート）系発泡粒子を製造する工程、及び、該発泡粒子を型内で加熱して成形する工程を含む、ポリ（３－ヒドロキシアルカノエート）系発泡成形体の製造方法にも関する。
　本発明によると、生産性が高く、かつ、臭気が抑制されたポリ（３－ヒドロキシアルカノエート）系発泡粒子を得ることができる製造方法、及び、該発泡粒子を用いたポリ（３－ヒドロキシアルカノエート）系発泡成形体の製造方法を提供することができる。
Ｐ３ＨＡ系組成物から構成される樹脂粒子について測定されるＤＳＣ曲線およびそれから測定される融点等を示す図である。
　以下に、本発明の実施形態について説明するが、本発明は以下の実施形態に限定されるものではない。
　本実施形態に係るＰ３ＨＡ系発泡粒子は、Ｐ３ＨＡ系組成物から構成される樹脂粒子を発泡剤を用いて発泡させることで得ることができる。また、Ｐ３ＨＡ系発泡成形体は、Ｐ３ＨＡ系発泡粒子を型内で加熱して成形することにより、具体的には、型内発泡成形することにより得ることができる。
　［Ｐ３ＨＡ］
　Ｐ３ＨＡは、３－ヒドロキシアルカノエート繰り返し単位を必須の構成単位（モノマー単位）として有する重合体であり、具体的には、下記一般式（１）で示される繰り返し単位を含む重合体が好ましい。
　　　　　[－ＣＨＲ－ＣＨ２－ＣＯ－Ｏ－]　　　（１）
　一般式（１）中、ＲはＣｐＨ２ｐ＋１で表されるアルキル基を示し、ｐは１～１５の整数を示す。Ｒとしては、例えば、メチル基、エチル基、プロピル基、メチルプロピル基、ブチル基、イソブチル基、ｔ－ブチル基、ペンチル基、ヘキシル基等の直鎖または分岐鎖状のアルキル基が挙げられる。ｐとしては、１～１０が好ましく、１～８がより好ましい。
　Ｐ３ＨＡとしては、特に微生物から産生されるＰ３ＨＡが好ましい。微生物から産生されるＰ３ＨＡは、３－ヒドロキシアルカノエート繰り返し単位が、全て（Ｒ）－３－ヒドロキシアルカノエートであるポリ［（Ｒ）－３－ヒドロキシアルカノエート］である。
　本実施形態では、Ｐ３ＨＡとして、ポリ（３－ヒドロキシアルカノエート）共重合体とポリ（３－ヒドロキシブチレート）単独重合体を含む混合物を用いる。以下では、Ｐ３ＨＡは当該混合物のことを指す。
　ポリ（３－ヒドロキシアルカノエート）共重合体は、少なくとも２種類の３－ヒドロキシアルカノエート単位を含む共重合体、又は、少なくとも１種類の３－ヒドロキシアルカノエート単位と、３－ヒドロキシアルカノエート単位以外のコモノマー単位を含む共重合体である。ポリ（３－ヒドロキシアルカノエート）共重合体は、少なくとも３－ヒドロキシブチレート単位を含む共重合体であることが好ましい。
　ポリ（３－ヒドロキシアルカノエート）共重合体の具体例としては、例えば、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシプロピオネート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシバレレート）（略称：Ｐ３ＨＢ３ＨＶ）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシバレレート－３－ヒドロキシヘキサノエート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシヘキサノエート）（略称：Ｐ３ＨＢ３ＨＨ）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシヘプタノエート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシオクタノエート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシノナノエート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシデカノエート）、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシウンデカノエート）、ポリ（３－ヒドロキシブチレート－コ－４－ヒドロキシブチレート）（略称：Ｐ３ＨＢ４ＨＢ）等が挙げられる。ポリ（３－ヒドロキシアルカノエート）共重合体としては１種類を単独で用いてもよいし、２種以上を併用してもよい。特に、加工性及び発泡成形体の物性等の観点から、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシヘキサノエート）、及び／又は、ポリ（３－ヒドロキシブチレート－コ－４－ヒドロキシブチレート）が好ましく、ポリ（３－ヒドロキシブチレート－コ－３－ヒドロキシヘキサノエート）が特に好ましい。
　ポリ（３－ヒドロキシアルカノエート）共重合体が、３－ヒドロキシブチレートとコモノマーの共重合体である場合、３－ヒドロキシブチレートと、コモノマー［例えば、３－ヒドロキシヘキサノエート（以下、３ＨＨと称する場合がある）や４－ヒドロキシブチレート（以下、４ＨＢと称する場合がある）］との構成比、即ち共重合体中のモノマー比率としては、３－ヒドロキシブチレート／コモノマー＝９９／１～８９／１１（モル％／モル％）が好ましく、９７／３～９１／９（モル％／モル％）がより好ましく、９５／５～９３／７（モル％／モル％）がさらに好ましい。共重合体中のコモノマー比率が１モル％以上であると、Ｐ３ＨＡの溶融加工温度域と熱分解温度域が離れることで、加工性が良好になる傾向がある。一方、共重合体中のコモノマー比率が１１モル％以下であると、溶融加工時の結晶化が速く、生産性がより良好になる傾向がある。
　なお、各モノマー比率は、当業者に公知の方法、例えば国際公開２０１３／１４７１３９号に記載の方法により求めることができる。
　前述したポリ（３－ヒドロキシブチレート）単独重合体とは、実質的に３－ヒドロキシブチレート単位のみからなる単独重合体（略称：Ｐ３ＨＢ）である。但し、コモノマーを微量（具体的には、モノマー比率として１モル％未満）含む共重合体も、前記単独重合体に含まれるものとする。ポリ（３－ヒドロキシアルカノエート）共重合体とポリ（３－ヒドロキシブチレート）単独重合体を含む混合物であれば、発泡温度が高温であってもポリ（３－ヒドロキシブチレート）単独重合体由来の成分が完全に融解し難く、かつ、結晶成長し易いので、発泡粒子の生産性を高めることができる。
　ポリ（３－ヒドロキシアルカノエート）共重合体とポリ（３－ヒドロキシブチレート）単独重合体を含む混合物において、両重合体の重量比（共重合体：単独重合体）は、高温での発泡温度にて発泡粒子が好適に得られ、発泡粒子の生産性を高めることができるように、９９：１～８０：２０であることが好ましく、９８：２～８４：１６がより好ましく、９７：３～８８：１２がさらに好ましく、９６：４～９０：１０が特に好ましい。
　Ｐ３ＨＡの融点は、特に限定されないが、１１０～１７０℃が好ましく、より好ましくは１２０～１６５℃である。融点が１１０℃未満では、得られるＰ３ＨＡ系発泡成形体の加熱寸法変化が大きくなる傾向がある。一方、融点が１７０℃を超えると、発泡工程中に加水分解が起こり易くなる傾向がある。なお、Ｐ３ＨＡの融点は、示差走査熱量計（日立ハイテクサイエンス社製ＤＳＣ７０２０）を用いて、Ｐ３ＨＡを約５ｍｇ計量し、１０℃／分の昇温速度にて１０℃から１９０℃まで昇温した時に得られるＤＳＣ曲線において、最も高温の融解ピークの温度として測定される。
　Ｐ３ＨＡの重量平均分子量は、特に限定されないが、２０万～２００万が好ましく、より好ましくは２５万～１５０万、更に好ましくは３０万～１００万である。重量平均分子量が２０万以上であると、得られるＰ３ＨＡ系発泡粒子の独立気泡率が高くなる傾向がある。一方、重量平均分子量が２００万以下であると、樹脂粒子作製などの溶融加工時の機械への負荷が低く、生産性が高くなる傾向がある。なお、Ｐ３ＨＡの重量平均分子量は、クロロホルム溶液を用いたゲルパーミエーションクロマトグラフィー（島津製作所社製ＨＰＬＣ　ＧＰＣ　ｓｙｓｔｅｍ）を用い、ポリスチレン換算分子量分布より測定することができる。該ゲルパーミエーションクロマトグラフィーにおけるカラムとしては、重量平均分子量を測定するのに適切なカラムを使用すればよい。
　Ｐ３ＨＡの製造方法は特に限定されず、化学合成による製造方法であってもよいし、微生物による製造方法であってもよい。中でも、上述のように微生物による製造方法が好ましい。微生物による製造方法については、公知乃至慣用の方法を適用できる。
　例えば、３－ヒドロキシブチレートと、その他のヒドロキシアルカノエートとのコポリマー生産菌としては、Ｐ３ＨＢ３ＨＶおよびＰ３ＨＢ３ＨＨ生産菌であるアエロモナス・キヤビエ（Ａｅｒｏｍｏｎａｓ　ｃａｖｉａｅ）、Ｐ３ＨＢ４ＨＢ生産菌であるアルカリゲネス・ユートロファス（Ａｌｃａｌｉｇｅｎｅｓ　ｅｕｔｒｏｐｈｕｓ）等が知られている。特に、Ｐ３ＨＢ３ＨＨに関し、Ｐ３ＨＢ３ＨＨの生産性を上げるために、Ｐ３ＨＡ合成酵素群の遺伝子を導入したアルカリゲネス・ユートロファス　ＡＣ３２株（Ａｌｃａｌｉｇｅｎｅｓ　ｅｕｔｒｏｐｈｕｓ　ＡＣ３２，　ＦＥＲＭ　ＢＰ－６０３８）（Ｔ．Ｆｕｋｕｉ，Ｙ．Ｄｏｉ，Ｊ．Ｂａｔｅｒｉｏｌ．，１７９，ｐ４８２１－４８３０（１９９７））等がより好ましく、これらの微生物を適切な条件で培養して菌体内にＰ３ＨＢ３ＨＨを蓄積させた微生物菌体が用いられる。また前記以外にも、生産したいＰ３ＨＡに合わせて、各種Ｐ３ＨＡ合成関連遺伝子を導入した遺伝子組み換え微生物を用いても良いし、基質の種類を含む培養条件を最適化すればよい。
　ポリ（３－ヒドロキシアルカノエート）共重合体とポリ（３－ヒドロキシブチレート）単独重合体の混合物を得る方法は特に限定されず、微生物産生により混合物を直接得る方法であってよいし、化学合成により混合物を直接得る方法であってもよい。また、押出機、ニーダー、バンバリーミキサー、ロール等を用いて２種以上の樹脂を溶融混練して混合物を得てもよいし、２種以上の樹脂を溶媒に溶解して混合・乾燥して混合物を得ても良い。中でも、上述のように微生物により混合物を直接得る方法が好ましい。微生物による製造方法については、例えば国際公開２０１５／１４６１９５号に記載の方法を適用できる。
　［Ｐ３ＨＡ系組成物から構成される樹脂粒子］
　Ｐ３ＨＡ系組成物から構成される樹脂粒子は、Ｐ３ＨＡを必須成分として含む組成物（Ｐ３ＨＡ系組成物）で構成される粒子である。当該組成物は、通常、Ｐ３ＨＡと必要に応じて添加剤とを含む。なお、本開示において、樹脂粒子とは、発泡工程に付す前の、いまだ発泡していない粒子のことを指す。
　Ｐ３ＨＡ系組成物から構成される樹脂粒子におけるＰ３ＨＡの含有量は、特に限定されないが、得られる発泡粒子や発泡成形体の生分解性等の観点で、７０重量％以上が好ましく、より好ましくは８０重量％以上である。
　Ｐ３ＨＡ系組成物から構成される樹脂粒子の融点（以下、Ｔｍｐと称する場合がある）は、特に限定されないが、１１０～１７０℃が好ましく、より好ましくは１２０～１６５℃である。融点が１１０℃未満では、得られるＰ３ＨＡ系発泡成形体の加熱寸法変化が大きくなる傾向がある。一方、融点が１７０℃を超えると、発泡工程中にＰ３ＨＡの加水分解が起こり易い傾向がある。なお、Ｐ３ＨＡ系組成物から構成される樹脂粒子の融点は、示差走査熱量計（日立ハイテクサイエンス社製ＤＳＣ７０２０）を用いて、Ｐ３ＨＡ系組成物から構成される樹脂粒子を約５ｍｇ計量し、１０℃／分の昇温速度にて１０℃から１９０℃まで昇温した時に得られるＤＳＣ曲線において、最も高温の融解ピークの温度として測定される。
　Ｐ３ＨＡ系組成物から構成される樹脂粒子のメルトフローレート（以下、ＭＦＲと称する場合がある）は、特に限定されないが、１～３０ｇ／１０ｍｉｎ（分）が好ましく、より好ましくは１～２５ｇ／１０ｍｉｎ、更に好ましくは１～２０ｇ／１０ｍｉｎである。ＭＦＲが１ｇ／１０ｍｉｎ未満では、１回の発泡だけでは見掛け密度の低い発泡粒子を得ることが難しくなる傾向がある。一方、ＭＦＲが３０ｇ／１０ｍｉｎを超えると、得られる発泡粒子の独立気泡率が低くなる傾向がある。なお、Ｐ３ＨＡ系組成物から構成される樹脂粒子のＭＦＲは、メルトフローインデックステスター（安田精機製作所社製）を用いて、ＪＩＳ　Ｋ７２１０に準じて、荷重５ｋｇ、測定温度は、「Ｐ３ＨＡ系組成物から構成される樹脂粒子の融点の測定」で得られるＤＳＣ曲線から読み取った融解終了温度＋１～１０℃の条件で測定することにより求められる。
　Ｐ３ＨＡ系組成物から構成される樹脂粒子の１粒当たりの重量は、０．３～１０ｍｇが好ましく、より好ましくは０．４～７．５ｍｇであり、更に好ましくは０．５～５ｍｇである。１粒当たりの重量が０．３ｍｇ以上であると、Ｐ３ＨＡ系組成物から構成される樹脂粒子を高い生産性で安定して製造することができる。一方、１粒当たりの重量が１０ｍｇ以下であると、Ｐ３ＨＡ系発泡成形体の薄肉化を容易に実現することができる。
　Ｐ３ＨＡ系組成物から構成される樹脂粒子の形状が円柱状である場合、前記樹脂粒子の長さ／直径は０．５～３が好ましく、より好ましくは０．７～２．７、更に好ましくは１～２．５である。長さ／直径が０．５未満では、得られる発泡粒子の形状が偏平となる傾向がある。一方、長さ／直径が３を超えると、発泡粒子の形状が縦長となる傾向がある。
　Ｐ３ＨＡ系組成物から構成される樹脂粒子は、発明の効果を阻害しない範囲において、添加剤を含有していてもよい。添加剤としては、例えば、気泡調整剤、結晶化核剤、滑剤、可塑剤、帯電防止剤、難燃剤、導電剤、断熱剤、架橋剤、酸化防止剤、紫外線吸収剤、着色剤、無機充填剤、有機充填剤、加水分解抑制剤等を目的に応じて使用できる。特に生分解性を有する添加剤が好ましい。
　気泡調整剤としては、例えば、タルク、シリカ、ケイ酸カルシウム、炭酸カルシウム、酸化アルミニウム、酸化チタン、珪藻土、クレイ、重曹、アルミナ、硫酸バリウム、酸化アルミニウム、ベントナイト等が挙げられる。中でも、Ｐ３ＨＡへの分散性が特に優れている点で、タルクが好ましい。気泡調整剤の使用量は、特に限定されないが、Ｐ３ＨＡ１００重量部に対して、０．０１～１重量部が好ましく、より好ましくは０．０３～０．５重量部、更に好ましくは０．０５～０．３重量部である。また、気泡調整剤は、１種のみならず２種以上混合してもよく、目的に応じて、混合比率を適宜調整することができる。
　結晶化核剤としては、例えば、ペンタエリスリトール、オロチン酸、アスパルテーム、シアヌル酸、グリシン、フェニルホスホン酸亜鉛、窒化ホウ素等が挙げられる。中でも、Ｐ３ＨＡの結晶化促進効果が特に優れている点で、ペンタエリスリトールが好ましい。結晶化核剤の使用量は、特に限定されないが、Ｐ３ＨＡ１００重量部に対して、０．１～５重量部が好ましく、より好ましくは０．５～３重量部、更に好ましくは０．７～１．５重量部である。また、結晶化核剤は、１種のみならず２種以上混合してもよく、目的に応じて、混合比率を適宜調整することができる。
　滑剤としては、例えば、ベヘン酸アミド、オレイン酸アミド、エルカ酸アミド、ステアリン酸アミド、パルミチン酸アミド、Ｎ－ステアリルベヘン酸アミド、Ｎ－ステアリルエルカ酸アミド、エチレンビスステアリン酸アミド、エチレンビスオレイン酸アミド、エチレンビスエルカ酸アミド、エチレンビスラウリル酸アミド、エチレンビスカプリン酸アミド、ｐ－フェニレンビスステアリン酸アミド、エチレンジアミンとステアリン酸とセバシン酸の重縮合物等が挙げられる。中でも、Ｐ３ＨＡへの滑剤効果が特に優れている点で、ベヘン酸アミド又はエルカ酸アミドが好ましい。滑剤の使用量は、特に限定されないが、Ｐ３ＨＡ１００重量部に対して、０．０１～５重量部が好ましく、より好ましくは０．０５～３重量部、更に好ましくは０．１～１．５重量部である。また、滑剤は、１種のみならず２種以上混合してもよく、目的に応じて、混合比率を適宜調整することができる。
　可塑剤としては、例えば、グリセリンエステル系化合物、クエン酸エステル系化合物、セバシン酸エステル系化合物、アジピン酸エステル系化合物、ポリエーテルエステル系化合物、安息香酸エステル系化合物、フタル酸エステル系化合物、イソソルバイドエステル系化合物、ポリカプロラクトン系化合物、二塩基酸エステル系化合物等が挙げられる。中でも、Ｐ３ＨＡへの可塑化効果が特に優れている点で、グリセリンエステル系化合物、クエン酸エステル系化合物、セバシン酸エステル系化合物、二塩基酸エステル系化合物が好ましい。グリセリンエステル系化合物としては、例えば、グリセリンジアセトモノラウレート等が挙げられる。クエン酸エステル系化合物としては、例えば、アセチルクエン酸トリブチル等が挙げられる。セバシン酸エステル系化合物としては、例えば、セバシン酸ジブチル等が挙げられる。二塩基酸エステル系化合物としては、例えば、ベンジルメチルジエチレングリコールアジペート等が挙げられる。可塑剤の使用量は、特に限定されないが、Ｐ３ＨＡ１００重量部に対して、１～２０重量部が好ましく、より好ましくは２～１５重量部、更に好ましくは３～１０重量部である。また、可塑剤は、１種のみならず２種以上混合してもよく、目的に応じて、混合比率を適宜調整することができる。
　着色剤としては、例えば、アゾ系、ポリ縮合アゾ系、アゾメチン基を含むアゾ系、アゾメチン系、アンスラキノン系、フタロシアニン系、ペリノン・ペリレン系、インジゴ・チオインジゴ系、ジオキサジン系、キナクリドン系、イソインドリノン系、ジケトピロロピロール系、キノフタロン系等の有機顔料、および、酸化鉄系顔料、水酸化鉄系顔料、紺青系顔料、カーボンブラック系顔料、酸化チタン系顔料、複合酸化物系顔料等の無機顔料等が挙げられる。着色剤の使用量は、特に限定されないが、Ｐ３ＨＡ１００重量部に対して、０．００１～５重量部が好ましく、より好ましくは０．０５～５重量部、更に好ましくは０．１～２重量部である。また、着色剤は、１種のみならず２種以上混合してもよく、目的に応じて、混合比率を適宜調整することができる。
　Ｐ３ＨＡ系組成物から構成される樹脂粒子を製造する際に、イソシアネート基を有する化合物（以下、イソシアネート化合物という）を用いることも可能である。但し、イソシアネート化合物は毒性を持つ場合がある。また、得られるＰ３ＨＡ系発泡粒子や発泡成形体が黄色くなる場合がある。したがって、イソシアネート化合物の使用量としては、Ｐ３ＨＡ１００重量部に対して、３重量部未満が好ましく、より好ましくは１重量部未満、更に好ましくは０．１重量部未満である。最も好ましいのは、樹脂粒子がイソシアネート化合物を含有しないことである。
　前記イソシアネート化合物としては、例えば、１分子中にイソシアネート基を２個以上有するポリイソシアネート化合物を用いることができる。具体的な種類としては芳香族、脂環族、脂肪族系のイソシアネート等がある。例えば、芳香族イソシアネートとしてはトリレン、ジフェニルメタン、ナフチレン、トリジン、キシレン、トリフェニルメタンを骨格とするイソシアネート化合物、脂環族イソシアネートとしてはイソホロン、水素化ジフェニルメタンを骨格とするイソシアネート化合物、脂肪族イソシアネートとしてはヘキサメチレン、リジンを骨格とするイソシアネート化合物等がある。更に、これらイソシアネート化合物を２種類以上組み合わせたものも使用可能であるが、汎用性、取扱い性、耐候性等からトリレン、ジフェニルメタン、特にジフェニルメタンのポリイソシアネートの使用が好ましい。
　Ｐ３ＨＡ系組成物から構成される樹脂粒子（Ｐ３ＨＡ系発泡粒子も同様）は、更に、Ｐ３ＨＡ以外の樹脂成分（「その他の樹脂成分」と称する場合がある）を実質的に含まなくともよいし、含んでいてもよい。その他の樹脂成分としては、例えば、ポリ乳酸、ポリブチレンサクシネート、ポリブチレンサクシネートアジペート、ポリブチレンアジペートテレフタレート、ポリブチレンサクシネートテレフタレート、ポリカプロラクトン等の脂肪族ポリエステルや脂肪族芳香族ポリエステル等が挙げられる。なお、その他の樹脂成分は、一種を単独で使用することもできるし、二種以上を組み合わせて使用することもできる。Ｐ３ＨＡ系組成物から構成される樹脂粒子（Ｐ３ＨＡ系発泡粒子も同様）におけるその他の樹脂成分の含有量は特に限定されないが、例えば、Ｐ３ＨＡ１００重量部に対して、１０～４００重量部が好ましく、より好ましくは５０～１５０重量部である。
　Ｐ３ＨＡ系組成物から構成される樹脂粒子の製造方法は特に限定されず、公知乃至慣用の方法を適用することで製造できる。例えば、まず、Ｐ３ＨＡと必要に応じて前記添加剤とを、押出機、ニーダー、バンバリーミキサー、ロール等を用いて溶融混練し、溶融したＰ３ＨＡ系組成物をダイスのノズルから吐出し、冷却した後、カットすることで、円柱状、楕円柱状、球状、立方体状、直方体状等の、発泡に利用しやすい形状の樹脂粒子を得ることができる。製造装置としては、生産性と利便性の観点から二軸押出機が好ましい。
　前記Ｐ３ＨＡ系組成物から構成される樹脂粒子の製造方法において、Ｐ３ＨＡと必要に応じて前記添加剤とを溶融混練する温度は、Ｐ３ＨＡの融点、重量平均分子量等や、使用する添加剤にもよるため一概には規定できないが、例えば、ダイスのノズルから吐出される溶融したＰ３ＨＡ系組成物の温度を１５０～２００℃とすることが好ましく、より好ましくは１６０～１９５℃、更に好ましくは１７０～１９０℃である。溶融したＰ３ＨＡ系組成物の温度が１５０℃未満では、Ｐ３ＨＡ系組成物が溶融混練不足となる傾向がある。一方、溶融したＰ３ＨＡ系組成物の温度が２００℃を超えると、Ｐ３ＨＡが熱分解し易くなる傾向がある。
　前記Ｐ３ＨＡ系組成物から構成される樹脂粒子の製造方法において、ダイスのノズルから吐出される溶融したＰ３ＨＡ系組成物を冷却する温度は、特に限定されないが、２０～８０℃が好ましく、より好ましくは３０～７０℃、更に好ましくは４０～６０℃である。冷却する温度が２０℃以上であると、溶融したＰ３ＨＡ系組成物の結晶化が速くなり、Ｐ３ＨＡ系組成物から構成される樹脂粒子の生産性がより良好になる傾向がある。一方、冷却する温度が８０℃以下であると、溶融したＰ３ＨＡ系組成物の結晶化が速くなり、Ｐ３ＨＡ系組成物から構成される樹脂粒子の生産性がより良好になる傾向がある。
　［Ｐ３ＨＡ系発泡粒子］
　本実施形態に係るＰ３ＨＡ系発泡粒子は、上述のＰ３ＨＡ系組成物から構成される樹脂粒子を発泡剤を用いて発泡させることにより得ることができる。
　Ｐ３ＨＡ系発泡粒子が示すゲル分率は、該発泡粒子中のＰ３ＨＡの架橋度を示す指標である。当該ゲル分率は、特に限定されないが、２０～９０重量％の範囲にあることが好ましい。また、ゲル分率は７５重量％を超えても良く、例えば７６重量％以上であってもよい。更に、８０重量％を超えても良く、例えば８１重量％以上であってもよい。Ｐ３ＨＡ系発泡粒子のゲル分率は、後述する架橋剤の種類やその使用量等によって制御することができる。
　Ｐ３ＨＡ系発泡粒子のゲル分率の測定方法は次の通りである。１００ｍｌのフラスコに、０．５ｇの発泡粒子と５０ｍｌのクロロホルムを入れ、大気圧下、６２℃で８時間加熱還流した後、得られた加熱処理物を１００メッシュの金網を有する吸引濾過装置を用いて濾過処理する。得られた金網上の濾過処理物を、８０℃のオーブン中で真空条件下にて８時間乾燥する。この際、得られた乾燥物重量Ｗｇｗ（ｇ）を測定する。ゲル分率は、Ｗｇｗ／０．５×１００（重量％）として算出される。
　Ｐ３ＨＡ系発泡粒子の１粒当たりの重量は、０．３～１０ｍｇが好ましく、より好ましくは０．４～７．５ｍｇであり、更に好ましくは０．５～５ｍｇである。１粒当たりの重量が０．３ｍｇ以上であると、Ｐ３ＨＡ系組成物から構成される樹脂粒子を高い生産性で安定して製造することができるため、得られるＰ３ＨＡ系発泡粒子の均一性が高まる傾向がある。一方、１粒当たりの重量が１０ｍｇ以下であると、Ｐ３ＨＡ系発泡成形体の薄肉化を容易に実現することができる。
　Ｐ３ＨＡ系発泡粒子の形状が円柱状である場合、前記発泡粒子の長さ／直径は０．５～２．５が好ましく、より好ましくは０．７～１．５であり、更に好ましくは０．８～１．２である。長さ／直径が０．５未満では、発泡成形体の表面性が悪くなる傾向がある。長さ／直径が２．５を超えると、型内発泡成形時の充填性が悪くなる傾向がある。
　Ｐ３ＨＡ系発泡粒子の見掛け密度は、特に限定されないが、２０～１５０ｇ／Ｌが好ましく、より好ましくは２３～１４０ｇ／Ｌ、更に好ましくは２５～１３０ｇ／Ｌである。１回の発泡だけでは所望の見掛け密度のＰ３ＨＡ系発泡粒子が得られない場合、１回発泡した発泡粒子を、２回目以降の発泡工程に付してもよい。なお、Ｐ３ＨＡ系発泡粒子の見掛け密度は、エタノールが入ったメスシリンダーを用意し、該メスシリンダーに重量Ｗｄ（ｇ）の発泡粒子群を、金網等を使用して沈め、エタノール水位上昇分より読みとられる発泡粒子群の容積をＶｄ（Ｌ）とする。発泡粒子の見掛け密度は、Ｗｄ／Ｖｄ（ｇ／Ｌ）である。
　Ｐ３ＨＡ系発泡粒子の独立気泡率は、特に限定されないが、８８％以上が好ましく、より好ましくは９０％以上、更に好ましくは９３％以上である。独立気泡率が８８％未満では、得られる発泡成形体の成形収縮率が大きくなる傾向がある。なお、Ｐ３ＨＡ系発泡粒子の独立気泡率の測定方法は次の通りである。Ｐ３ＨＡ系発泡粒子に対して、ＡＳＴＭ　Ｄ２８５６－８７の手順Ｃ（ＰＲＯＳＥＤＵＲＥ　Ｃ）に記載の方法に準拠して、空気比較式比重計（東京サイエンス社製モデル１０００）を用いて、体積Ｖｃ（ｃｍ３）を測定する。次に、Ｖｃを測定後の発泡粒子の全量を、エタノールの入ったメスシリンダー中に沈め、メスシリンダーの水位上昇分（水没法）から、発泡粒子の見掛け上の体積Ｖａ（ｃｍ３）を求める。発泡粒子の独立気泡率は、１００－（Ｖａ－Ｖｃ）×１００／Ｖａ（％）である。
　Ｐ３ＨＡ系発泡粒子の平均気泡径は、特に限定されないが、５０～５００μｍが好ましく、より好ましくは１００～４００μｍである。なお、Ｐ３ＨＡ系発泡粒子の平均気泡径の測定方法は次の通りである。発泡粒子を、カミソリ（フェザー社製ハイステンレス両刃）を用いて、該発泡粒子の中央で切断する。該切断面を、光学顕微鏡（キーエンス社製ＶＨＸ－１００）を用いて、倍率５０倍にて観察して得られた画像において、該発泡粒子のほぼ中心を通る直線を引き、該直線が貫通している気泡数ｎ、および、該直線と該発泡粒子表面との交点から定まる発泡粒子径Ｌ（μｍ）を読み取る。発泡粒子の平均気泡径は、Ｌ／ｎ（μｍ）である。
　Ｐ３ＨＡ系発泡粒子は、以下に説明する方法によって製造することができる。
　まず、Ｐ３ＨＡ系組成物から構成される樹脂粒子、水、および架橋剤と、必要に応じて分散剤、分散助剤、架橋助剤、及び／又は可塑剤とを含む水分散体を含む耐圧容器内に、発泡剤を導入する。より具体的には、Ｐ３ＨＡ系組成物から構成される樹脂粒子、水、および架橋剤と、必要に応じて分散剤、分散助剤、架橋助剤、及び／又は可塑剤とを攪拌下で耐圧容器内に仕込み、これらを十分に分散させて、水分散体を形成した後、発泡剤を耐圧容器内に導入すればよい。あるいは、別容器内でＰ３ＨＡ系組成物から構成される樹脂粒子、水、および架橋剤と、必要に応じて分散剤、分散助剤、架橋助剤、及び／又は可塑剤とを十分に分散させた後、得られた分散体と発泡剤を順次、耐圧容器内に導入すればよい。
　次いで、耐圧容器の内容物を、１３０～１５０℃の範囲内にある所定温度（発泡温度）まで加熱し、該所定温度で５～５５分間保持する。これによって、樹脂粒子を軟化させつつ、樹脂粒子に発泡剤を含浸させ、また樹脂粒子に架橋剤を含浸および反応させることができる。本実施形態では、Ｐ３ＨＡとしてポリ（３－ヒドロキシアルカノエート）共重合体とポリ（３－ヒドロキシブチレート）単独重合体の混合物を用いるため、高い発泡温度を採用することができ、それに応じて保持時間を短く設定することで、発泡粒子の生産性を高めることができる。加えて、保持時間が短いにも関わらず、架橋剤としてパーカーボネート類の有機過酸化物を用いることで発泡粒子の臭気を抑制することが可能である。
　前記所定温度での保持の後、耐圧容器の一端を解放し、樹脂粒子や水を含む耐圧容器の内容物を、耐圧容器内の圧力よりも低圧の雰囲気下に放出することにより、該樹脂粒子を発泡させてＰ３ＨＡ系発泡粒子を得る（この一連の操作を、以下では除圧発泡と称する場合がある）。なお、低圧の雰囲気下に放出する際の耐圧容器内の温度を発泡温度とし、低圧の雰囲気下に放出する際の耐圧容器内の圧力を発泡圧力とする。
　前記水としては、Ｐ３ＨＡ系組成物から構成される樹脂粒子、分散剤、分散助剤、架橋剤、発泡剤等を均一に分散できるものであればよく、特に限定されない。例えば、ＲＯ水（逆浸透膜法により精製された水）、蒸留水、脱イオン水（イオン交換樹脂により精製された水）等の純水および超純水等を用いることができる。水の使用量は、特に限定されないが、Ｐ３ＨＡ系組成物から構成される樹脂粒子１００重量部に対して、１００～１０００重量部が好ましい。
　前記分散剤としては、例えば、第三リン酸カルシウム、第三リン酸マグネシウム、塩基性炭酸マグネシウム、炭酸カルシウム、硫酸バリウム、カオリン、タルク、クレイ、酸化アルミニウム、酸化チタン、水酸化アルミニウム等の無機物が挙げられる。分散剤の使用量は、特に限定されないが、Ｐ３ＨＡ系組成物から構成される樹脂粒子１００重量部に対して、０．１～３．０重量部が好ましい。
　前記分散助剤としては、例えば、ドデシルベンゼンスルホン酸ソーダ、α－オレフィンスルホン酸ソーダ、ノルマルパラフィンスルホン酸ソーダ等のアニオン界面活性剤が挙げられる。分散助剤の使用量は、特に限定されないが、Ｐ３ＨＡ系組成物から構成される樹脂粒子１００重量部に対して、０．００１～０．５重量部が好ましく、より好ましくは０．０１～０．２重量部である。
　前記架橋剤としては、パーカーボネート類の有機過酸化物を用いる。有機過酸化物は、溶融混練によりＰ３ＨＡと混合して反応させる必要がなく、上述したように樹脂粒子を作製した後に該樹脂粒子に含浸、反応させることができるため、プロセス上好ましい架橋剤である。架橋剤として有機過酸化物を使用することで、Ｐ３ＨＡの分子鎖同士が、架橋剤に由来する構造を介在することなく、直接結合することで架橋構造が形成される。更に、パーカーボネート類の有機過酸化物を用いることで、発泡粒子の臭気を抑制することができる。
　架橋剤は、樹脂粒子の軟化温度付近で架橋反応が進行すること、Ｐ３ＨＡとの相溶性が良好であること、樹脂粒子の内部まで含浸しやすいこと、といった特性を有することが望ましい。この観点から、前記パーカーボネート類の有機過酸化物は、１分間半減期温度が１５０～１７０℃であり、かつ常温で液体である有機過酸化物が好ましい。中でも、前記１分間半減期温度を満足し得ることから、カーボネート基を１つ有する有機過酸化物が好ましい。また、芳香族化合物由来の臭気を回避するため、前記パーカーボネート類の有機過酸化物は、芳香環を有しない化合物であることが好ましい。具体的には、ｔ－ブチルパーオキシ－２－エチルへキシルモノカーボネート（１分間半減期温度：１６１℃）、ｔ－ブチルパーオキシイソプロピルモノカーボネート（１分間半減期温度：１５９℃）、ｔ－アミルパーオキシ－２－エチルへキシルモノカーボネート（１分間半減期温度：１５５℃）、ｔ－アミルパーオキシイソプロピルモノカーボネート（１分間半減期温度：１５３℃）等が挙げられる。これら架橋剤は１種類を単独で使用してもよいし、二種以上を併用してもよい。
　架橋剤の使用量は、特に限定されないが、Ｐ３ＨＡ系組成物から構成される樹脂粒子１００重量部に対して、１．２～５重量部が好ましく、より好ましくは１．３～４重量部、更に好ましくは１．４～３．５重量部であり、特に好ましくは１．５～３重量部である。架橋剤の使用量が１．２重量部未満では、Ｐ３ＨＡ系発泡粒子が示すゲル分率が十分に高くならず、発泡粒子から発泡成形体に型内発泡成形することが困難であったり、また、成形可能であっても、発泡成形体に型内発泡成形する時に採用できる成形加工条件の幅が狭くなる。一方、架橋剤の使用量が５重量部を超えると、添加しただけの効果を得られるものでもなく、経済的に無駄となる傾向がある。架橋剤の使用量はＰ３ＨＡ系発泡粒子のゲル分率と相関関係があり、当該ゲル分率の値に影響するため、得られるゲル分率の値を考慮して架橋剤の使用量を設定することが望ましい。
　前記架橋助剤としては、例えば、分子内に少なくとも１個の不飽和結合を有する化合物が挙げられる。中でも、特にアリルエステル、アクリル酸エステル、メタクリル酸エステル、ジビニル化合物等が好ましい。架橋助剤の使用量は特に限定されないが、Ｐ３ＨＡ系組成物から構成される樹脂粒子１００重量部に対して、０．０１～３重量部が好ましく、より好ましくは０．０３～１．５重量部、さらに好ましくは０．０５～１重量部である。但し、架橋助剤は使用しなくともよい。
　前記可塑剤としては、例えば、グリセリンエステル系化合物、クエン酸エステル系化合物、セバシン酸エステル系化合物、アジピン酸エステル系化合物、ポリエーテルエステル系化合物、安息香酸エステル系化合物、フタル酸エステル系化合物、イソソルバイドエステル系化合物、ポリカプロラクトン系化合物、二塩基酸エステル系化合物等が挙げられる。この中でもＰ３ＨＡの可塑化効果が優れている点で、グリセリンエステル系化合物、クエン酸エステル系化合物、セバシン酸エステル系化合物、二塩基酸エステル系化合物が好ましい。グリセリンエステル系化合物としては、グリセリンジアセトモノラウレート等が挙げられる。クエン酸エステル系化合物としては、アセチルクエン酸トリブチル等が挙げられる。セバシン酸エステル系化合物としては、セバシン酸ジブチル等が挙げられる。二塩基酸エステル系化合物としては、ベンジルメチルジエチレングリコールアジペート等が挙げられる。可塑剤の使用量は特に限定されないが、Ｐ３ＨＡ系組成物から構成される樹脂粒子１００重量部に対して、１～２０重量部が好ましく、より好ましくは２～１５重量部、さらに好ましくは３～１０重量部である。但し、可塑剤は使用しなくともよい。また、可塑剤は、１種のみならず２種以上混合してもよく、目的に応じて、混合比率を適宜調整することができる。
　前記発泡剤としては、二酸化炭素、窒素、空気等の無機ガス；プロパン、ノルマルブタン、イソブタン、ノルマルペンタン、イソペンタン、ネオペンタン等の炭素数３～５の飽和炭化水素；ジメチルエーテル、ジエチルエーテル、およびメチルエチルエーテル等のエーテル；モノクロルメタン、ジクロロメタン、ジクロロジフルオロエタン等のハロゲン化炭化水素；水等が挙げられ、これらの群より選ばれる少なくとも１種を用いることができる。中でも、環境負荷や発泡力の観点から二酸化炭素を用いることが好ましい。発泡剤の添加量は、特に限定されないが、Ｐ３ＨＡ系組成物から構成される樹脂粒子１００重量部に対して、２～１００００重量部が好ましく、５～５０００重量部がより好ましく、１０～１０００重量部が更に好ましい。発泡剤の添加量が２重量部未満であると、見掛け密度の低い発泡粒子が得られ難い傾向がある。一方、発泡剤の添加量が１００００重量部を超えると、添加しただけの効果を得られるものでもなく、経済的に無駄となる傾向がある。
　前記除圧発泡において、Ｐ３ＨＡ系組成物から構成される樹脂粒子に架橋剤および必要に応じて架橋助剤を含浸、反応させる際、架橋効率を上げるために耐圧容器内の酸素濃度および水の溶存酸素量を低くすることが好ましい。その方法としては、二酸化炭素や窒素等の無機ガスで置換したり、真空引きすることが挙げられる。
　前記除圧発泡において、所望の発泡温度まで昇温する際の速度（以下、昇温速度と称する場合がある）としては１～３℃／分が好ましく、１．５～３℃／分がより好ましい。昇温速度が１℃／分以上であると、生産性が良好となる傾向がある。一方、昇温速度が３℃／分以下であると、昇温時に、Ｐ３ＨＡ系組成物から構成される樹脂粒子への発泡剤の含浸および架橋剤の含浸、反応を十分に進行させることができる。
　前記除圧発泡において、前記所定温度（発泡温度）は、上述のように１３０～１５０℃の範囲内にある。前記所定温度が１３０℃未満であると、ポリ（３－ヒドロキシアルカノエート）共重合体とポリ（３－ヒドロキシブチレート）単独重合体を含むＰ３ＨＡ系組成物から構成される樹脂粒子に対して発泡剤の含浸が不十分となり、該樹脂粒子が発泡せず、発泡粒子が得られ難い場合がある。一方、前記所定温度が１５０℃を超えると、Ｐ３ＨＡの加水分解が進行してしまう場合がある。前記所定温度は１３２～１４８℃が好ましく、１３４～１４６℃がより好ましく、１３６～１４４℃がさらに好ましい。また、前記所定温度は１４０℃を超えてもよく、例えば１４１℃以上であってもよい。
　前記除圧発泡において、発泡圧力（即ち耐圧容器内の圧力）は、１～１０ＭＰａ（ゲージ圧）が好ましく、より好ましくは２～５ＭＰａ（ゲージ圧）である。発泡圧力が１ＭＰａ（ゲージ圧）未満では、見掛け密度の低い発泡粒子が得られ難い傾向がある。
　前記除圧発泡において、耐圧容器の内容物を前記所定温度で保持する時間は、上述のように５～５５分間である。保持時間が５分間未満であると、樹脂粒子中に未反応の架橋剤が残留する場合がある。一方、５５分間を超えると、発泡粒子の生産性が不十分となる。前記保持時間は１０～５０分間が好ましく、１５～４０分間がより好ましく、２０～３５分間がさらに好ましい。
　前記除圧発泡において、耐圧容器内の内容物を低圧雰囲気下に放出する際、流量調整や、発泡倍率バラツキ低減等の目的で、直径１～５ｍｍの開口オリフィスを通して放出することもできる。また、比較的融点の高いＰ３ＨＡ系組成物から構成される樹脂粒子については、発泡性を向上させる目的で、前記低圧雰囲気を飽和水蒸気で満たしても良い。
　前記除圧発泡を一回実施するだけでは所望の見掛け密度のＰ３ＨＡ系発泡粒子が得られない場合がある。その場合、前記除圧発泡で得られたＰ３ＨＡ系発泡粒子を耐圧容器内に入れて空気、二酸化炭素等の無機ガスを含浸させる加圧処理により該Ｐ３ＨＡ系発泡粒子内の圧力（以下、発泡粒子内圧と称する場合がある）を常圧よりも高くした後、該Ｐ３ＨＡ系発泡粒子を過熱水蒸気等で加熱して更に膨張させ、所望の見掛け密度のＰ３ＨＡ系二段発泡粒子としても良い（以下、この一連の操作を二段発泡と称する場合がある）。
　前記二段発泡を行う際の発泡粒子内圧は、０．１５～０．６０ＭＰａ（絶対圧）が好ましく、より好ましくは０．２０～０．５０ＭＰａ（絶対圧）である。
　前記二段発泡において、Ｐ３ＨＡ系発泡粒子に無機ガスを含浸させる際の耐圧容器内の温度としては、１０～９０℃が好ましく、より好ましくは４０～９０℃である。
　前記二段発泡において、Ｐ３ＨＡ系発泡粒子を加熱する過熱水蒸気等の圧力（以下、二段発泡圧力と称する場合がある）は、用いる発泡粒子の特性、所望の見掛け密度によって異なり、一概には規定できないが、０．０１～０．１７ＭＰａ（ゲージ圧）が好ましく、より好ましくは０．０１～０．１０ＭＰａ（ゲージ圧）である。
　Ｐ３ＨＡ系二段発泡粒子は、上述のＰ３ＨＡ系発泡粒子の見掛け密度、独立気泡率、平均気泡径を充足することが好ましい。
　［Ｐ３ＨＡ系発泡成形体］
　Ｐ３ＨＡ系発泡成形体の製造方法は特に限定されず、前記Ｐ３ＨＡ系発泡粒子（上述のＰ３ＨＡ系二段発泡粒子を含む、以下同じ）を型内で加熱して成形すればよく、公知乃至慣用の方法を適用することができる。例えば、次の（Ａ）～（Ｄ）の型内発泡成形の方法等が挙げられるが、特に限定されない。
　（Ａ）Ｐ３ＨＡ系発泡粒子を無機ガスで加圧処理して、該発泡粒子内に無機ガスを含浸させ、所定の発泡粒子内圧を付与した後、該発泡粒子を金型に充填し、過熱水蒸気で加熱する方法
　（Ｂ）Ｐ３ＨＡ系発泡粒子を金型に充填した後、該金型内の体積を１０～７５％減ずるように圧縮し、過熱水蒸気で加熱する方法
　（Ｃ）Ｐ３ＨＡ系発泡粒子をガス圧力で圧縮して金型に充填し、該発泡粒子の回復力を利用して、過熱水蒸気で加熱する方法
　（Ｄ）特に前処理することなく、Ｐ３ＨＡ系発泡粒子を金型に充填し、過熱水蒸気で加熱する方法
　Ｐ３ＨＡ系発泡成形体の製造において、Ｐ３ＨＡ系発泡粒子を加熱する過熱水蒸気の圧力（以下、成形圧力と称する場合がある）は、用いる発泡粒子の特性等によって異なり、一概には規定できないが、０．０５～０．３０ＭＰａ（ゲージ圧）が好ましく、より好ましくは０．０８～０．２５ＭＰａ（ゲージ圧）である。
　Ｐ３ＨＡ系発泡成形体の製造方法のうち前記（Ａ）法での無機ガスとしては、空気、窒素、酸素、二酸化炭素、ヘリウム、ネオン、アルゴン等が使用でき、これらの群より選ばれる少なくとも１種を使用できる。これらの中でも、空気または二酸化炭素が好ましい。
　Ｐ３ＨＡ系発泡成形体の製造方法のうち前記（Ａ）法での発泡粒子内圧は０．１０～０．３０ＭＰａ（絶対圧）が好ましく、より好ましくは０．１１～０．２５ＭＰａ（絶対圧）である。
　Ｐ３ＨＡ系発泡成形体の製造方法のうち（Ａ）法での無機ガスを発泡粒子に含浸させる際の耐圧容器内の温度としては、１０～９０℃が好ましく、より好ましくは４０～９０℃である。
　Ｐ３ＨＡ系発泡成形体は、各種用途に使用することができ、例えば、包装用緩衝材、農産箱、魚箱、自動車部材、建築材料、土木材料等の用途に用いることができる。
　以下、実施例により本発明を具体的に説明するが、本発明は、これらの実施例によりその技術的範囲を限定されるものではない。
　実施例および比較例で使用した物質を以下に示す。
　［ポリ（３－ヒドロキシアルカノエート）］
　Ｐ３ＨＡ－１：Ｐ３ＨＢ３ＨＨとＰ３ＨＢ（重量比９２：８）の混合物（Ｐ３ＨＢ３ＨＨ中のモノマー比率は３ＨＢ／３ＨＨ＝９５／５（モル％／モル％））
　Ｐ３ＨＡ－２：Ｐ３ＨＢ３ＨＨとＰ３ＨＢ（重量比９６：４）の混合物（Ｐ３ＨＢ３ＨＨ中のモノマー比率は３ＨＢ／３ＨＨ＝９５／５（モル％／モル％））
　Ｐ３ＨＡ－３：Ｐ３ＨＢ３ＨＨ　１００重量％（Ｐ３ＨＢ３ＨＨ中のモノマー比率は３ＨＢ／３ＨＨ＝９５／５（モル％／モル％））
　［気泡調整剤］
　気泡調整剤：タルク（林化成社製タルカンパウダーＰＫ－Ｓ）
　［分散剤］
　分散剤：第三リン酸カルシウム（太平化学産業社製）
　［分散助剤］
　分散助剤：アルキルスルホン酸ソーダ（花王社製ラテムルＰＳ）
　［架橋剤］
　架橋剤－１：ｔ－ブチルパーオキシ－２－エチルヘキシルカーボネート（含有量　９７％）（日油社製パーブチルＥ）
　架橋剤－２：過酸化ベンゾイル（含有量　７５％）（日油社製ナイパーＢＷ）
　実施例および比較例において実施した評価方法に関して以下に説明する。
　［Ｐ３ＨＡ系組成物から構成される樹脂粒子の融点の測定］
　示差走査熱量計（日立ハイテクサイエンス社製ＤＳＣ７０２０）を用いて、Ｐ３ＨＡ系組成物から構成される樹脂粒子を約５ｍｇ計量し、１０℃／分の昇温速度にて１０℃から１９０℃まで昇温した時に得られるＤＳＣ曲線において、最も高温の融解ピークの温度を融点とした（図１を参照）。
　［Ｐ３ＨＡ系組成物から構成される樹脂粒子のＭＦＲの測定］
　メルトフローインデックステスター（安田精機製作所社製）を用いて、ＪＩＳ　Ｋ７２１０に準じて、荷重５ｋｇ、測定温度は「Ｐ３ＨＡ系組成物から構成される樹脂粒子の融点の測定」で得られるＤＳＣ曲線から読み取った融解終了温度＋１～１０℃の条件で測定した。
　［Ｐ３ＨＡ系発泡粒子の生産性の評価］
　Ｐ３ＨＡ系発泡粒子の生産性を、以下の基準にて評価した。
　◎：Ｐ３ＨＡ系発泡粒子の製造において、昇温開始から発泡開始までの時間が５５分以内であり、生産性が非常に高い。
　○：Ｐ３ＨＡ系発泡粒子の製造において、昇温開始から発泡開始までの時間が５６分から７０分の間であり、生産性が高い。
　×：Ｐ３ＨＡ系発泡粒子の製造において、昇温開始から発泡開始までの時間が７１分から１００分の間であり、生産性が悪い。
　××：Ｐ３ＨＡ系発泡粒子の製造において、昇温開始から発泡開始までの時間が１００分を超え、生産性が非常に悪い、又は、発泡粒子が得られない。
　［Ｐ３ＨＡ系発泡粒子の臭気の評価］
　架橋剤の取り扱いに従事している者１０名により官能試験を行い、Ｐ３ＨＡ系発泡粒子が発し得る、架橋剤又はその分解生成物由来の臭気について、以下の基準にて評価した。
○：官能試験員１０名全員がＰ３ＨＡ系発泡粒子に臭気が無いと判定した。
△：官能試験員のうち１名以上９名以下がＰ３ＨＡ系発泡粒子に臭気が有ると判定した。
×：官能試験員１０名全員がＰ３ＨＡ系発泡粒子に臭気が有ると判定した。
××：官能試験員１０名全員がＰ３ＨＡ系発泡粒子に芳香族化合物由来の臭気が有ると判定した。
　［Ｐ３ＨＡ系発泡粒子のゲル分率の測定］
　１００ｍｌのフラスコに、０．５ｇのＰ３ＨＡ系発泡粒子と５０ｍｌのクロロホルムを入れ、大気圧下、６２℃で８時間加熱還流した後、得られた加熱処理物を１００メッシュの金網を有する吸引濾過装置を用いて濾過処理した。得られた金網上の濾過処理物を、８０℃のオーブン中で真空条件下にて８時間乾燥した。この際、得られた乾燥物重量Ｗｇｗ（ｇ）を測定した。ゲル分率は、Ｗｇｗ／０．５×１００（重量％）より求めた。
　［Ｐ３ＨＡ系発泡粒子またはＰ３ＨＡ系二段発泡粒子の見掛け密度の測定］
　エタノールが入ったメスシリンダーを用意し、該メスシリンダーにＰ３ＨＡ系発泡粒子またはＰ３ＨＡ系二段発泡粒子（該発泡粒子の重量Ｗｄ（ｇ））を、金網等を使用して沈め、エタノール水位上昇分より読みとられる発泡粒子の容積をＶｄ（Ｌ）とした。該発泡粒子の見掛け密度は、Ｗｄ／Ｖｄ（ｇ／Ｌ）より求めた。
　［Ｐ３ＨＡ系発泡成形体の密度の測定］
　Ｐ３ＨＡ系発泡成形体の縦、横、および厚みをデジタルノギスで測定し、該発泡成形体の体積を求めた。該発泡成形体の重量を該発泡成形体の体積で割った値を、発泡成形体の密度とした。
　＜実施例１＞
　［Ｐ３ＨＡ系組成物から構成される樹脂粒子の製造］
　Ｐ３ＨＡとしてＰ３ＨＡ－１を用い、Ｐ３ＨＡ－１が１００重量部、気泡調整剤が０．１重量部となるように計量し、ドライブレンドした。ドライブレンドした混合物を、二軸押出機（東芝機械社製ＴＥＭ－２６ＳＸ）を用いて、シリンダー設定温度１４０～１７０℃で溶融混練し、押出機の先端に取り付けたダイスのノズルから吐出された１８５℃の溶融したＰ３ＨＡ系組成物を４３℃で水冷後、切断して、１粒当たりの重量が２．０ｍｇの樹脂粒子を得た。得られた樹脂粒子は、融点が１６３℃であり、１７０℃で測定したＭＦＲが２．５ｇ／１０ｍｉｎであった。
　［Ｐ３ＨＡ系発泡粒子の製造］
　得られた樹脂粒子１００重量部、純水２００重量部、分散剤１．０重量部、分散助剤０．１重量部、および架橋剤２重量部を、攪拌下で耐圧容器内に仕込んだ後、真空引きを行い耐圧容器内の酸素を除去した。次に、耐圧容器内に発泡剤として二酸化炭素を導入した。その後、耐圧容器内容物を１４２．０℃の発泡温度まで４０分かけて昇温した。その後、二酸化炭素を追加導入して３．３ＭＰａ（ゲージ圧）の発泡圧力まで昇圧し、該発泡温度付近、該発泡圧力付近で３０分間保持した。その後、耐圧容器下部のバルブを開き、直径３．６ｍｍの開口オリフィスを通して、耐圧容器の内容物を大気圧下に放出し、発泡粒子を得た。昇温開始から発泡開始までの時間は７０分であり、発泡粒子の生産性が高かった。該発泡粒子の表面に付着した分散剤を洗浄した後、９０℃で乾燥した。得られた発泡粒子から発する臭気は官能試験員１０名全員が無いと判定した。その他の発泡粒子の特性を表１にまとめた。
Figure JPOXMLDOC01-appb-T000001
　[Ｐ３ＨＡ系発泡成形体の製造]
　得られた発泡粒子を８０℃に加温した耐圧容器に仕込み、空気で加圧処理することで発泡粒子内圧を０．１８ＭＰａ（絶対圧）とした。該発泡粒子を成形機（ＤＡＩＳＥＮ社製ＥＰ－９００Ｌ－Ｍ５）の縦３７０ｍｍ×横３２０ｍｍ×厚み６０ｍｍの金型内に充填した。次に、圧力０．１５ＭＰａ（ゲージ圧）の過熱水蒸気で加熱して発泡成形体を得た後、７５℃で乾燥した。得られた発泡成形体の密度は４８ｇ／Ｌであった。
　＜実施例２、３、比較例１～５＞
　配合や発泡条件を表１に示すように変更したこと以外は実施例１と同様にして、樹脂粒子、発泡粒子および発泡成形体を作製し、実施例１と同様の評価を実施した。結果を表１にまとめた。
　表１に示すように、ポリ（３－ヒドロキシアルカノエート）として、ポリ（３－ヒドロキシアルカノエート）共重合体とポリ（３－ヒドロキシブチレート）単独重合体を、重量比９９：１～８０：２０で含む混合物を使用し、架橋剤としてパーカーボネート類の有機過酸化物を使用し、発泡温度が１３０～１５０℃の範囲にある実施例１～３では、Ｐ３ＨＡ系発泡粒子の生産性が高く、かつ、得られた発泡粒子が発する臭気は抑制されていた。
　一方、ポリ（３－ヒドロキシアルカノエート）として、ポリ（３－ヒドロキシアルカノエート）共重合体のみを使用し、発泡温度が１３０～１５０℃の範囲にはない比較例１及び２では、発泡粒子は得られたものの、発泡粒子の生産性と、発泡粒子が発する臭気の抑制を両立することは困難であった。即ち、比較例１では臭気は抑制されたが、生産性が悪く、保持時間を短くした比較例２では生産性は高いものの、臭気があった。
　比較例３では発泡温度を１３０～１５０℃の範囲としたが、ポリ（３－ヒドロキシアルカノエート）として、ポリ（３－ヒドロキシアルカノエート）共重合体のみを使用したため、耐圧容器内でポリ（３－ヒドロキシアルカノエート）共重合体からなる樹脂粒子が塊となってしまい、発泡すら出来なかった。
　比較例４ではポリ（３－ヒドロキシアルカノエート）として、ポリ（３－ヒドロキシアルカノエート）共重合体とポリ（３－ヒドロキシブチレート）単独重合体を含む混合物を使用したが、発泡温度が１３０～１５０℃の範囲にはないため、発泡粒子を得ることすら出来なかった。
　比較例５ではポリ（３－ヒドロキシアルカノエート）として、ポリ（３－ヒドロキシアルカノエート）共重合体とポリ（３－ヒドロキシブチレート）単独重合体を含む混合物を使用したが、架橋剤としてパーカーボネート類ではなく、過酸化ベンゾイルを使用しているため、得られた発泡粒子に芳香族化合物由来の臭気があった。
　＜実施例４＞
　［Ｐ３ＨＡ系二段発泡粒子および発泡成形体の製造］
　実施例１で得られた発泡粒子を８０℃に加温した耐圧容器に仕込み、空気で加圧処理することで発泡粒子内圧を０．３０ＭＰａ（絶対圧）とした。その後、圧力０．０４ＭＰａ（ゲージ圧）の過熱水蒸気で加熱して、二段発泡粒子を得た後、７５℃で乾燥した。得られた二段発泡粒子が発する臭気は官能試験員１０名全員が無いと判定した。
　得られた二段発泡粒子を８０℃に加温した耐圧容器に仕込み、空気で加圧処理することで発泡粒子内圧を０．１８ＭＰａ（絶対圧）とした。該発泡粒子を成形機（ＤＡＩＳＥＮ社製ＥＰ－９００）の縦３７０ｍｍ×横３２０ｍｍ×厚み６０ｍｍの金型内に充填した。次に、圧力０．１５ＭＰａ（ゲージ圧）の過熱水蒸気で加熱して発泡成形体を得た後、７５℃で乾燥した。得られた発泡成形体の密度は２５ｇ／Ｌであった。
　以上のように、本発明の製造方法によると、生産性が高く、かつ、臭気が抑制されたポリ（３－ヒドロキシアルカノエート）系発泡粒子及び発泡成形体を製造できることが確認された。
 

Claims (7)

  1. 　ポリ（３－ヒドロキシアルカノエート）系発泡粒子の製造方法であって、
    　耐圧容器内で、ポリ（３－ヒドロキシアルカノエート）を含む樹脂粒子、及び、架橋剤を含む水分散体に、発泡剤を導入する工程、
    　前記耐圧容器の内容物を、１３０～１５０℃の範囲内にある所定温度まで加熱し、該所定温度で５～５５分間保持する工程、及び、
    　前記耐圧容器の一端を開放し、前記耐圧容器の内容物を低圧の雰囲気下に放出することにより前記樹脂粒子を発泡させる工程を含み、
    　前記ポリ（３－ヒドロキシアルカノエート）が、ポリ（３－ヒドロキシアルカノエート）共重合体とポリ（３－ヒドロキシブチレート）単独重合体を、重量比９９：１～８０：２０で含む混合物であり、
    　前記架橋剤が、パーカーボネート類の有機過酸化物である、製造方法。
  2. 　前記発泡剤が、二酸化炭素である、請求項１に記載のポリ（３－ヒドロキシアルカノエート）系発泡粒子の製造方法。
  3. 　前記ポリ（３－ヒドロキシアルカノエート）共重合体が、３－ヒドロキシブチレートとコモノマーの共重合体であり、該共重合体中のモノマー比率が、３－ヒドロキシブチレート／コモノマー＝９９／１～８９／１１（モル％／モル％）である、請求項１又は２に記載のポリ（３－ヒドロキシアルカノエート）系発泡粒子の製造方法。
  4. 　前記パーカーボネート類の有機過酸化物が、１分間半減期温度が１５０～１７０℃であり、かつ常温で液体である、請求項１～３のいずれか１項に記載のポリ（３－ヒドロキシアルカノエート）系発泡粒子の製造方法。
  5. 　前記パーカーボネート類の有機過酸化物が、カーボネート基を１つ有する化合物である、請求項４に記載のポリ（３－ヒドロキシアルカノエート）系発泡粒子の製造方法。
  6. 　前記樹脂粒子を発泡させる工程の後、得られた発泡粒子に無機ガスを含浸させて該発泡粒子内の圧力を高めた後、該発泡粒子を加熱して膨張させる工程をさらに含む、請求項１～５のいずれか１項に記載のポリ（３－ヒドロキシアルカノエート）系発泡粒子の製造方法。
  7. 　請求項１～６のいずれか１項に記載の製造方法によってポリ（３－ヒドロキシアルカノエート）系発泡粒子を製造する工程、及び、
    　該発泡粒子を型内で加熱して成形する工程を含む、ポリ（３－ヒドロキシアルカノエート）系発泡成形体の製造方法。
     
PCT/JP2021/033161 2020-09-11 2021-09-09 ポリ（３－ヒドロキシアルカノエート）系発泡粒子又はポリ（３－ヒドロキシアルカノエート）系発泡成形体の製造方法 WO2022054870A1 (ja)