Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
  • B01J20/20—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising free carbon; comprising carbon obtained by carbonising processes
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
  • B01J20/0203—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising compounds of metals not provided for in B01J20/04
  • B01J20/0233—Compounds of Cu, Ag, Au
  • B01J20/0237—Compounds of Cu
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
  • B01J20/0203—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising compounds of metals not provided for in B01J20/04
  • B01J20/0259—Compounds of N, P, As, Sb, Bi
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
  • B01J20/06—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising oxides or hydroxides of metals not provided for in group B01J20/04
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/30—Processes for preparing, regenerating, or reactivating
  • B01J20/3078—Thermal treatment, e.g. calcining or pyrolizing
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/30—Processes for preparing, regenerating, or reactivating
  • B01J20/3085—Chemical treatments not covered by groups B01J20/3007 - B01J20/3078
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/30—Processes for preparing, regenerating, or reactivating
  • B01J20/32—Impregnating or coating ; Solid sorbent compositions obtained from processes involving impregnating or coating
  • B01J20/3202—Impregnating or coating ; Solid sorbent compositions obtained from processes involving impregnating or coating characterised by the carrier, support or substrate used for impregnation or coating
  • B01J20/3204—Inorganic carriers, supports or substrates
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/30—Processes for preparing, regenerating, or reactivating
  • B01J20/32—Impregnating or coating ; Solid sorbent compositions obtained from processes involving impregnating or coating
  • B01J20/3231—Impregnating or coating ; Solid sorbent compositions obtained from processes involving impregnating or coating characterised by the coating or impregnating layer
  • B01J20/3234—Inorganic material layers
  • B01J20/3236—Inorganic material layers containing metal, other than zeolites, e.g. oxides, hydroxides, sulphides or salts
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/30—Processes for preparing, regenerating, or reactivating
  • B01J20/32—Impregnating or coating ; Solid sorbent compositions obtained from processes involving impregnating or coating
  • B01J20/3231—Impregnating or coating ; Solid sorbent compositions obtained from processes involving impregnating or coating characterised by the coating or impregnating layer
  • B01J20/3234—Inorganic material layers
  • B01J20/324—Inorganic material layers containing free carbon, e.g. activated carbon
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J6/00—Heat treatments such as Calcining; Fusing ; Pyrolysis
  • B01J6/001—Calcining
• • C—CHEMISTRY; METALLURGY
  • C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F1/00—Treatment of water, waste water, or sewage
  • C02F1/28—Treatment of water, waste water, or sewage by sorption
  • C02F1/283—Treatment of water, waste water, or sewage by sorption using coal, charred products, or inorganic mixtures containing them
• • C—CHEMISTRY; METALLURGY
  • C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F1/00—Treatment of water, waste water, or sewage
  • C02F1/28—Treatment of water, waste water, or sewage by sorption
  • C02F1/286—Treatment of water, waste water, or sewage by sorption using natural organic sorbents or derivatives thereof
• • C—CHEMISTRY; METALLURGY
  • C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F1/00—Treatment of water, waste water, or sewage
  • C02F1/28—Treatment of water, waste water, or sewage by sorption
  • C02F1/288—Treatment of water, waste water, or sewage by sorption using composite sorbents, e.g. coated, impregnated, multi-layered
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J2220/00—Aspects relating to sorbent materials
  • B01J2220/40—Aspects relating to the composition of sorbent or filter aid materials
  • B01J2220/48—Sorbents characterised by the starting material used for their preparation
  • B01J2220/4812—Sorbents characterised by the starting material used for their preparation the starting material being of organic character
  • B01J2220/4825—Polysaccharides or cellulose materials, e.g. starch, chitin, sawdust, wood, straw, cotton
• • C—CHEMISTRY; METALLURGY
  • C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F2101/00—Nature of the contaminant
  • C02F2101/10—Inorganic compounds
  • C02F2101/12—Halogens or halogen-containing compounds
• • C—CHEMISTRY; METALLURGY
  • C02—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F—TREATMENT OF WATER, WASTE WATER, SEWAGE, OR SLUDGE
  • C02F2303/00—Specific treatment goals
  • C02F2303/18—Removal of treatment agents after treatment
  • C02F2303/185—The treatment agent being halogen or a halogenated compound

Definitions

• Fluids such as water are routinely disinfected by adding oxidizing compounds, irradiating the water with ultraviolet radiation, or both. While these techniques are effective at disinfecting the water, the disinfected water will often include the oxidizing compounds themselves, products of the oxidizing compounds as they dissolve in the water, or reaction compounds that result from the irradiation of the water that contains various constituent compounds.
• these various compounds include chlorine, chloramines, chloroform, trihalomethanes, haloacetic acids, and hydrogen peroxides. Furthermore, in some situations the above compounds are present in water even when that water has not been disinfected. These compounds are undesired because they alter the smell and taste of the water, cause health problems, and can cause corrosion of mains and service lines. [0003] To remove these compounds, sorbents have been used. The sorbents absorb and adsorb the various compounds. In particular, the pores of sorbents permit the adsorption of the compounds. However, pure sorbents are inefficient and only adsorb a fraction of the compounds that must be removed.
• the sorbents are sometimes treated with compounds to form catalytic sorbent.
• Catalytic species are usually present on the surface of the sorbent particles and function by catalyzing the chemical decomposition of those undesired compounds that adsorb or absorb poorly on the sorbent.
• a catalytic sorbent is significantly more efficient than a pure, untreated sorbent.
• Catalytic sorbents have proven effective for removing chlorine, chloramines, chloroform, trihalomethanes, haloacetic acids, and hydrogen peroxides from water and other fluids.
• a method of manufacturing a sorbent material comprising: providing a carbonaceous material; activating the carbonaceous material to form a precursor activated carbon; doping the precursor activated carbon by contacting the precursor activated carbon with an copper source and a nitrogen source to thereby form a doped precursor activated carbon; calcining the doped precursor activated carbon in a calcining atmosphere that does not cause any substantial oxidation or activation of the doped precursor activated carbon to thereby form a sorbent material.
• the copper source is selected from copper sulfate pentahydrate, CuSO 4 ⁇ 5H 2 O, or copper (II) carbonate hydroxide, CuCO 3 (OH) 2
• the nitrogen source is one or more of urea, CO(NH 2 ) 2, ammonium carbonate, (NH 4 ) 2 CO 3 , or aqueous ammonium hydroxide, NH 4 OH (nominally aq, 28wt.%).
• the copper source is selected from copper sulfate pentahydrate, CuSO 4 ⁇ 5H 2 O, and the nitrogen source is of urea, CO(NH 2 ) 2 .
• the copper source is copper (II) carbonate hydroxide, CuCO 3 (OH) 2
• the nitrogen source is one or more of urea, CO(NH 2 ) 2 , ammonium carbonate, (NH 4 ) 2 CO 3 , or aqueous ammonium hydroxide, NH 4 OH (nominally aq, 28 wt.%).
• calcining is performed at a temperature of about 850°C to about 1050°C in a N 2 atmosphere.
• the oxidizing is required and is performed.
• doping the precursor activated carbon is performed in a single stage process, the single stage process including a single step of contacting the precursor activated carbon with both a copper source and a nitrogen source.
• contacting the precursor activated carbon with the copper source and the nitrogen source is performed with a single aqueous solution that contains both the copper source and the nitrogen source.
• the precursor activated carbon is dried after it is contacted with the single aqueous solution containing the copper source and the nitrogen source.
• calcining is performed at a temperature of about 600°C to about 1000°C in a N 2 atmosphere.
• calcining is performed at a temperature of about 700°C to about 1000°C in a N 2 atmosphere. [0016] In another embodiment, calcining is performed at a temperature of about 850°C to about 1000°C in a N 2 atmosphere. [0017] In another embodiment, the method further comprises oxidizing the precursor activated carbon prior to doping. [0018] In another embodiment, the method further comprises oxidizing the precursor activated carbon prior to doping. [0019] In one embodiment, there is a method of removing chlorine, chloramine, or both chlorine and chloramine from a fluid, the method comprising: providing a sorbent material comprising an activated carbon doped with copper and nitrogen, and contacting the sorbent material with the fluid.
• the fluid is liquid water.
• the water or the sorbent material has previously undergone a disinfecting step.
• the sorbent material is formed from a carbonaceous material that is activated to form a precursor activated carbon, and the sorbent material comprises about 2 wt.% to about 15 wt.% nitrogen as measured on a dry precursor activated carbon basis; about 0.25 wt.% to about 2 wt.% copper as measured on a dry precursor activated carbon basis; and wherein the sorbent material has a chloramine destruction number (CDN) of at least about 6.
• CDN chloramine destruction number
• a sorbent material formed from a carbonaceous material that is activated to form a precursor activated carbon, the sorbent material comprising: about 2 wt.% to about 15 wt.% nitrogen as measured on a dry precursor activated carbon basis; about 0.25 wt.% to about 2 wt.% copper as measured on a dry precursor activated carbon basis; wherein the sorbent material has a chloramine destruction number (CDN) of at least about 6.
• the CDN is about 6 to about 60.
• the sorbent material is formed from a carbonaceous material that is formed from one or more of coal, wood, and coconut.
• FIG.1 depicts a process in accordance with an embodiment.
• FIG.2 depicts a process in accordance with an embodiment.
• FIG.3 depicts selected experimental results according to several embodiments.
• FIG.4 depicts selected process parameters and experimental results according to several embodiments.
• FIG.5 depicts selected process parameters and experimental results according to several embodiments.
• the term “comprising” means “including, but not limited to.”
• the term “about” means plus or minus 10% of the numerical value of the number with which it is being used. Therefore, “about 50” means “in the range of 45-55”.
• the term “sorbent material” means any material that exhibits adsorbent properties, absorbent properties, or a combination of adsorbent properties and absorbent properties. Adsorbent properties mean that atoms, ions, or molecules physically adhere to the surface of the material.
• sorbent properties means that atoms, ions, or molecule enter and are retained by a bulk phase of the material.
• sorbent materials include activated carbon, reactivated carbon, natural and synthetic zeolite, silica, silica gel, alumina, zirconia, and diatomaceous earths.
• sorbent material is a material whose constituent components are substantially adsorbent and/or absorbent, with only minimal components that are not adsorbent and/or absorbent (for example, the minimal amount of binder that is required for activated carbon pellets to maintain their shape).
• sorbent means any composition or composite that includes a sorbent material in a blend, mixture, composite, or compound with one or more additional materials that do not exhibit adsorbent properties.
• sorbent includes an activated carbon sorbent material mixed with a thermally conductive filler.
• carbonaceous material means a material that contains carbon that has not been thermally activated or chemically activated. Carbonaceous material may have been mechanically treated, thermally treated, or chemically treated, and can even have weakly sorbent properties, but carbonaceous material does not adsorb compounds in substantial amounts as would be expected of a material such as activated carbon.
• carbonaceous material examples include but are not limited to bituminous coal, sub-bituminous coal, lignite coal, anthracite coal, wood, wood chips, sawdust, peat, nut shells, pits, coconut shell, babassu nut, macadamia nut, dende nut, peach pit, cherry pit, olive pit, walnut shell, wood, lignin, polymers, nitrogen-containing polymers, resins, petroleum pitches, bagasse, rice hulls, corn husks, wheat hulls and chaff, graphenes, carbon nanotubes, or polymer fibers.
• the term “disinfection byproduct” means a compound that is formed as a result of chemical reactions between organic and inorganic matter found in water and the chemical compounds that are used during the disinfection process, or a compound that is formed as a result of the irradiation of organic and inorganic matter found in water by ultraviolet radiation.
• disinfection byproducts include one or more of chlorine, chloramines, chloroform, trihalomethanes, haloacetic acids, and hydrogen peroxides. It should be noted, however, that it is possible for compounds that are disinfection byproducts to be present in water that has not undergone a disinfection process.
• the term “macropores” means pores within a sorbent that are greater than about 50 nm in diameter.
• the term “mesopores” means pores within a sorbent that have a diameter of about 2 nm to about 50 nm.
• the term “micropores” means pores within a sorbent that have a diameter of less than about 2 nm.
• chloramine means one or more of mono-chloramine (NH 2 Cl), di-chloramine (NHCl 2 ), or tri-chloramine (NCl 3 ).
• the “apparent density” of a sorbent or sorbent material is obtained by the industry standard test ASTM D2854-09 (2019).
• the sorbents or sorbent materials described herein are useful for removing chloroforms and other similar volatile organic chemical compounds (VOC) from fluids such as water.
• the VOC are not limited and include one or more of styrene, alachlor, atrazine, benzene, carbofuran, carbon tetrachloride, chlorobenzene, chloropicrin, 2,4- dichlorophenoxyacetic acid (2,4-D), dibromochloropropane (DBCP), o-dichlorobenzene, p- dichlorobenzene, 1,2-dichloroethane, 1,1-dichloroethylene, cis-1,2-dichloroethylene, trans- 1,2-dichloroethylene, 1,2-dichloropropane, cis-1,3-dichloropropylene, dinoseb, endrin, ethylbenzene, ethylene dibromide (EDB), haloacetonitriles (HAN) including bromochloroacetonitrile, dibromoacetonitrile, dichloroacetonitrile, and trichloroacetonit
• VOC that are relevant in the field of drinking water are known in the industry and are described, for example, in NSF/ANSI 53-2019, which was designated a standard on May 6, 2019 and which is incorporated by reference in its entirety.
• the removal of VOC by sorbents or sorbent materials is measured by the removal of the individual VOC species themselves.
• the removal of VOC by sorbents or sorbent materials is measured by the removal of surrogate compounds.
• Surrogates are compounds that are similar in chemical composition to the analytes of interest and which are present in sample prior to preparation and analysis. For example, chloroform is one example of a surrogate for the compounds of this paragraph.
• the sorbents or sorbent materials described herein are also useful for removing other contaminants from water or other fluids such as perfluoroalkyl and polyfluoroalkyl substances (PFAS).
• PFAS compounds include one or more of perfluorooctanoic acid (PFOA), perfluorooctanesulfonic acid (PFOS), and compounds produced by the GENX process such as 2,3,3,3,-tetrafluoro-2-(heptafluoropropoxy)propanoate and heptafluoropropyl 1,2,2,2-tetrafluoroethyl ether.
• the sorbents or sorbent materials are also useful in removing a wide variety of emerging contaminants from water or other fluids.
• emerging contaminants include one or more of meprobamate, phenytoin, atenolol, carbamazepine, tris(2-chloroethyl) phosphate (TCEP), tris(1-chloro-2-propyl) phosphate (TCPP), N,N-diethyl-meta-toluamide (DEET), metolachlor, trimethoprim, ibuprofen, naproxen, estrone, bisphenol A, linuron, or nonyl phenol.
• TCEP tris(2-chloroethyl) phosphate
• TCPP tris(1-chloro-2-propyl) phosphate
• DEET N,N-diethyl-meta-toluamide
• metolachlor trimethoprim, ibuprofen, naproxen
• FIG.1 One embodiment of the overall process 10 of the disclosure is shown in FIG.1.
• a carbonaceous material is provided 20, followed by activating 30 the carbonaceous material to form a precursor activated carbon.
• the precursor activated carbon is oxidized 40.
• the precursor activated carbon is doped 50 which imparts a quantity of copper dopants and nitrogen dopants to the precursor activated carbon and thereby produce a doped precursor activated carbon.
• the doped precursor activated carbon is then calcined 60 by heating under at specified temperatures and under a specified atmosphere and cooled 70 in an inert atmosphere so as not to substantially alter the pore structure or cause any substantial oxidation or activation of the doped precursor activated carbon.
• the completion of calcination 60 and cooling 70 produces the sorbent material of the disclosure.
• Carbonaceous Material Processing [0049] The disclosure provides one or more carbonaceous materials that are precursors to the final sorbents.
• Carbonaceous material may have been mechanically treated, thermally treated, or chemically treated, and can even have weakly sorbent properties, but carbonaceous material does not adsorb compounds in substantial amounts as would be expected of a material such as activated carbon. Additionally, although the carbonaceous materials may have been mechanically treated, thermally treated, or chemically treated, they have not been treated in ways that activate the carbon.
• carbonaceous material examples include but are not limited to bituminous coal, sub-bituminous coal, lignite coal, anthracite coal, wood, wood chips, sawdust, peat, nut shells, pits, coconut shell, babassu nut, macadamia nut, dende nut, peach pit, cherry pit, olive pit, walnut shell, wood, lignin, polymers, nitrogen-containing polymers, resins, petroleum pitches, bagasse, rice hulls, corn husks, wheat hulls and chaff, graphenes, carbon nanotubes, and polymer fibers.
• the carbonaceous material is coconut shell.
• coconut shell carbonaceous materials are particularly useful because when coconut shell is activated to form activated carbon, it has excellent adsorption of chloroform and other organic compounds.. [0051] After the carbonaceous material is provided, it is activated.
• the activation process is not limited. Any suitable activation process may be used.
• Those processes depend on the kind of the carbonaceous material and also the desired form of the final activated carbon, and the steps include one or more of pyrolysis of the carbonaceous material to form a charcoal, pulverizing the charcoal, mixing a binder with the pulverized charcoal, briquetting the pulverized charcoal and binder, crushing the briquettes, sizing the crushed briquettes, and baking the sized briquettes or the briquettes themselves to carbonize, cure, or remove the binder.
• the carbonaceous material in the form of baked briquettes or sized particles is thermally activated, chemically activated, or thermally and chemically activated.
• Thermal activation is performed by heating the baked briquettes or sized particles in the presence of one or more of water, oxygen, and carbon dioxide. Chemical activation is performed by impregnating the baked briquettes or sized particles in the presence of a strong acid, strong base, or a salt. It should be noted that whether each of the above steps are included in the processing sometimes depends on the provided carbonaceous material. For example, when the carbonaceous material is coconut, process steps do not include “reagglomeration,” which is the steps of mixing a binder with the pulverized charcoal, briquetting the pulverized charcoal and binder, crushing the briquettes, and sizing the crushed briquettes. [0052] The result of processing the carbonaceous material is that activated carbon is formed.
• this activated carbon will be referred to as “precursor activated carbon” as subsequent disclosure describes additional steps that will be applied to the precursor activated carbon to further improve its performance.
• the performance of the precursor activated carbon depends on several factors, including the kind and amount of one or more carbonaceous materials that are included, the type of activation including chemical or thermal activation, and the level of activation that is imparted on the carbonaceous material to thereby form the precursor activated carbon. Performance of the precursor activated carbon is also affected by other processing steps such as the crushing and sizing of reagglomerated carbonaceous material particles, the level of residual binder, and the final size of the precursor activated carbon.
• the precursor activated carbon is not separately treated or oxidized beyond the steps outlined above.
• the sorbent capacity with respect to different disinfection byproducts or other contaminant species is substantial because the adsorptive capacity of the precursor activated carbon itself is maintained and is not particularly dependent on catalytic effects.
• the precursor activated carbon retains substantially all organic compound adsorption capability of species like chloroform because of the internal pore structure of the precursor activated carbon the internal pore structure of the precursor activated carbon.
• Oxidation of Precursor Activated Carbon [0054] The disclosure contemplates optional oxidation of the precursor activated carbon. In certain embodiments, the precursor activated carbon is oxidized after it is activated.
• Oxidation of the precursor activated carbon means that the precursor activated carbon is exposed to oxygen molecules at temperatures sufficient to impart oxygen species or complexes on the surface of the activated carbon. Oxidation does not contemplate substantial modification of the pore structure of the precursor activated carbon.
• oxidation is performed by exposing the feedstock to an oxygen containing environment and heating the feedstock to a temperature of about 150 °C to about 1050°C.
• the temperature of oxidizing can be about 150°C to about 250°C, about 250°C to about 350°C, about 350°C to about 450°C, about 450°C to about 550°C, about 550°C to about 650°C, about 650°C to about 750°C, or about 750°C to about 850°C, or any of those disclosed endpoints, or any range that is made of a combination of any of the above ranges or values within those ranges.
• the oxygen containing environment is one or more of atmospheric air, oxygen gas (O 2 ), oxygen plasma, hydrogen peroxide (H 2 O 2 ), ozone (O 3 ), nitrous oxide (N 2 O), steam (i.e., dissociated O 2 ), or carbon dioxide (CO 2 ).
• the oxygen containing environment is dry, and includes no moisture or substantially no measurable moisture. The selection of the oxidizing temperature and the oxidant and oxidizing process does not substantially modify the pore structure of the precursor activated carbon. Thus, if a more oxidizing oxygen containing environment is selected, temperatures must be lowered to reduce the potential that additional activation will occur.
• Oxidation can also be accomplished electrochemically. It should be noted that carbons slowly oxidize in the presence of air with or without moisture at room temperature and this oxidation, although slow, would be eventually sufficient to produce an oxidized carbon precursor.
• the carbon may be oxidized in a non-thermal process using at least one of nitric acid, potassium peroxymonosulfate, potassium persulfate, ammonium persulfate, sodium persulfate, hydrogen peroxide, peracetic acid, acetic acid, calcium hypochlorite, sodium hypochlorite, hypochlorous acid, benzoyl peroxide, sodium percarbonate, sodium perborate, organic peroxides, organic hydroperoxides, bleaching compounds, peroxide-based bleach, chlorine-based bleach, a mixture of hydrogen peroxide and urea, a mixture of peracetic acid and urea, and combinations of one or more of the above.
• the above compounds that are used for non-thermal oxidation are in the liquid or vapor phase and contact the precursor activated carbon at temperatures less than about 100°C.
• Cu-N Doping [0058] After the precursor activated carbon is prepared and optionally oxidized, the precursor activated carbon is further treated by doping with copper-nitrogen (Cu-N) compounds. Doping with Cu-N imparts Cu-N complexes on the surface of the precursor activated carbon, thereby serving to catalyze disinfection byproducts.
• the source of the copper compounds is copper sulfate pentahydrate, CuSO 4 ⁇ 5H 2 O, or copper (II) carbonate hydroxide, Cu 2 CO 3 (OH) 2 .
• the source of the nitrogen is one or more of urea, CO(NH 2 ) 2 , aqueous ammonium hydroxide, NH 4 OH (nominally aq, 28wt.%), or ammonium carbonate, (NH 4 ) 2 CO 3 .
• the source of nitrogen is provided as part of an aqueous solution.
• the doping process is not limited. In some embodiments, doping is performed in a single stage. In a single stage process, the precursor activated carbon is treated by contacting it with a single solution, and that single solution includes both the copper compounds and the nitrogen compounds.
• the copper compounds are not limited and include copper(II) sulfate pentahydrate, CuSO 4 .5H 2 O, copper (II) carbonate hydroxide, Cu 2 CO 3 (OH) 2 , copper(II) chloride, CuCl 2 , copper(II) chloride dihydrate, CuCl 2 ⁇ 2H 2 O, copper(II) nitrate, Cu(NO 3 ) 2, copper(II) nitrate monohydrate, Cu(NO 3 ) 2.
• the doping is performed in a single stage by contacting the precursor activated carbon with an aqueous solution containing copper sulfate pentahydrate , CuSO 4 ⁇ 5H 2 O, and urea, CO(NH 2 ) 2
• the doping is performed in a single stage by contacting the precursor activated carbon with an aqueous solution containing copper (II) carbonate hydroxide, Cu 2 CO 3 (OH) 2 , and one or more nitrogen source selected from urea, CO(NH 2 ) 2 , aqueous ammonium hydroxide, NH 4 OH (nominally aq, 28wt.%), or ammonium carbonate, (NH 4 ) 2 CO 3 .
• the amount of copper compounds and the amount of nitrogen compounds that are doped can be controlled by one or more of varying the concentration of the copper compound in solution, varying the concentration of nitrogen concentration in solution, varying the amount of time that the solution contacts the precursor activated carbon, or varying the temperature of the solution.
• the precursor activated carbon is dried to remove water or other solvent, with the copper and nitrogen compounds thereby remaining on the precursor activated carbon. The process of drying is not limited and is performed by drying in air at 100-150°C for up to 2 hours.
• the resultant doped and dried precursor activated carbon includes copper and nitrogen in various amounts.
• the amount of copper that is added when measured on a dry carbon basis is about 0.1 wt.%, about 0.2 wt.%, 0.3 wt.%, about 0.4 wt.%, about 0.5 wt.%, about 0.6 wt.%, about 0.7 wt.%, about 0.8 wt.%, about 0.9 wt.%, about 1.0 wt.%, about 1.1 wt.%, about 1.2 wt.%, about 1.3 wt.%, about 1.4 wt.%, about 1.5 wt.%, about 1.6 wt.%, about 1.7 wt.%, about 1.8 wt.%, about 1.9 wt.%, about 2.0 wt.%, or any range that includes one or more of the above values as endpoints.
• the amount of nitrogen when measured on a dry carbon basis is about 1.5 wt.%, about 2.0 wt.%, about 2.2 wt.%, about 2.5 wt.%, about 3.0 wt.%, about 3.5 wt.%, about 4.0 wt.%, about 4.5 wt.%, about 5.0 wt.%, about 5.5 wt.%, about 6.0 wt.%, about 6.5 wt.%, about 7.0 wt.%, about 7.5 wt.%, about 8.0 wt.%, about 8.3 wt.%, about 8.5 wt.%, about 9.0 wt.%, about 9.3 wt.%, about 9.5 wt.%, about 10.0 wt.%, about 10.3 wt.%, about 10.5 wt.%, about 11.0 wt.%, about 11.3 wt.%, about 11.5 wt.%, about 12.0 wt.%, about
• FIG.2 shows one embodiment of the doping process 50 in a single stage configuration.
• the precursor activated carbon is contacted with an aqueous solution containing a copper source and a nitrogen source, shown by box 51.
• the contacted precursor activated carbon is dried 52.
• doped precursor activated carbon is ready for calcining.
• Thermal Processing / Calcination [0064] After the completion of the single-stage Cu-N doping processes, the doped precursor activated carbon is ready for thermal processing, which is also referred to as calcination. During calcination, the doped precursor activated carbon is heated in the presence of a specified atmosphere to achieve additional changes in the doped precursor activated carbon.
• the temperature of calcination of the doped precursor activated carbon is not limited. In some embodiments, calcination takes place at a temperature of about 400°C, about 450°C, about 500°C, about 550°C, about 600°C, about 650°C, about 700°C, about 750°C, about 800°C, about 850°C, about 900°C, about 950°C, about 1000°C, about 1050°C, or any range that includes one or more of the above values as endpoints. [0066] The calcination atmosphere is one that does not cause any substantial oxidation or activation of the doped precursor activated carbon at the specified temperatures so as not to alter the pore structure of the doped precursor activated carbon.
• the atmosphere contains no oxygen, carbon dioxide, or water, or the atmosphere contains amounts of oxygen, carbon dioxide, or water that are so small as to not cause any oxidation or activation.
• atmospheres for calcination include one or more of nitrogen gas (N 2 ), helium, neon, argon, krypton, xenon, and combinations thereof.
• N 2 nitrogen gas
• sorbent material is granular activated carbon (GAC), which is defined as activated carbon particles sized to be retained on a 50-mesh sieve (holes of about 0.300 mm).
• the sorbent material is powdered activated carbon (PAC), which is defined as particles that pass through an 80-mesh sieve (holes of about 0.180 mm). While these particle size ranges are mentioned for activated carbon sorbent materials, it is also contemplated that any of the disclosed sorbent materials may be measured by the above 50-mesh and 80-mesh sieve sizes. In still other embodiments, the sorbent material is pelletized activated carbon. Performance Measurement / Sorbent Characterization [0068] The performance of the sorbent materials of the disclosure is measured in various ways, including the “chloramine destruction number” (CDN) which defined below. The chloramine destruction number quantifies the amount of chloramine that can be removed from a fluid by the sorbent materials of the disclosure.
• CDN chloramine destruction number
• the measurement of the CDN is known in the art, for example in U.S. Patent No.10,702,853 patented on July 7, 2020 and titled “CHLORAMINE AND CHLORINE REMOVAL MATERIAL AND METHODS FOR MAKING THE SAME,” which is incorporated by reference herein in its entirety.
• the CDN is the absolute value of the first order linear kinetic fit, multiplied by 1000, that is applied to a natural log of a concentration of chloramine in water versus time, where the initial concentration of chloramine is decreased over a period of 150 minutes. When ammonia is in equilibrium with chlorine in solution the form of chloramine is pH dependent.
• the chloramine solution comprised ammonium chloride; sodium hypochlorite and deionized water were mixed to obtain a 1 L solution of 300 ppm chloramine at a pH of 9.0. At a pH value of 9.0, the chloramine species that is present at equilibrium is the mono- chloramine form, which is the most difficult to destroy.
• the solution was buffered using sodium carbonate to maintain the solution pH during evaluation.
• the chlorine solution comprised sodium hypochlorite and deionized water to obtain 1 L of a 300 ppm chlorine solution.
• One liter of the 300 ppm respective solution was added to an Erlenmeyer flask that was placed in a water bath controlled to 20°C.
• a constant volume of 2.0 mL activated carbon (sized at 80 ⁇ 325 mesh) was added to the agitated 1 L chloramine or chlorine solution for each sample analysis.
• the volume of the carbon used was determined from the apparent density of the 80x325 carbon as determined by ASTM Method D-2854.
• the concentration of total chlorine in solution was measured at various time points over a 150 min period by taking aliquots and then analyzing using a standard HACH colorimetric EPA accepted method 10070 for total chlorine.
• concentration versus time data for each sorbent material sample is replotted as the natural log of total chlorine concentration versus time to linearize the data according to first order kinetic theory.
• a linear fit is then applied to the data and the slope of the linear fit is determined.
• the slope is always negative because the initial concentration of total chlorine decreases over the 150 min. period.
• the absolute value of the slope multiplied by 1000 is used quantify the rate of chloramine and chlorine destruction (removal). The larger the absolute slope, the more effective the sorbent material is at removing chlorine and chloramine.
• the slope resulting from the linear fit of the first order kinetic experimental data (again multiplied by 1000) is referred to as the “chloramine destruction number” or CDN. In the case of chlorine destruction this rate is referred to as the “chlorine destruction number” of Cl-DN.
• the “peroxide destruction number” which is also referred to as the “peroxide number” is also measured.
• the peroxide number is a volumetric test, which means that performance is measured and normalized to a specified volume of sorbent material.
• the test for the peroxide number is well known in the art, and is described by U.S. Patent No. 5,470,748, which is incorporated by reference herein in its entirety.
• the sorbent material is first pulverized to a fine mesh size fraction where at least 90 wt.%, and in certain tests at least 95 wt.%, of the sorbent material will pass through a 325 mesh U.S. Standard Series sieve (44 ⁇ m opening size).
• a specified amount of the pulverized sorbent material is placed in a vacuum flask (Dewar), and 100 mL of deionized water is added to the vacuum flask.
• the addition of deionized water is performed such that any pulverized sorbent material clinging to the sides of the vacuum flask is carried into the main body of water at the bottom of the vacuum flask.
• a 50 mL aliquot of acqueous buffer solution is added to the vacuum flask.
• the aqueous buffer solution is 0.5 molar in K 2 HPO 4 and 0.5 molar in KH 2 PO 4 .
• a magnetic stir bar is added into the vacuum flask and energized to begin stirring.
• Stirring speed is increased until a vortex greater than about 0.5 inches (1.27 cm) deep is formed in the mixture and the optimum stir bar speed is achieved.
• the optimum stir bar speed is selected so that additional increases in stir bar speed do not significantly affect the peroxide decomposition time.
• the mass of sorbent material in grams that is added to the solution is equal to one half (1/2) of the measured apparent density of the sorbent material, when the apparent density of the sorbent material is reported in g/cm 3 .
• the catalytic properties of the sorbent material cause the peroxide to be catalyzed and thereby destroyed (i.e., the hydrogen peroxide decomposes into water and oxygen gas).
• the catalysis of hydrogen peroxide is exothermic.
• the rated of decomposition by way of the sorbent material can be approximated over time by measuring the temperature of the buffered solution.
• the “peroxide number” is the length of time in minutes that is required for the buffered solution containing the sorbent material sample to reach 75% of the recorded maximum temperature. Faster times and therefore smaller values of the peroxide number indicate more catalytic activity and thus a higher performance sorbent material.
• the peroxide destruction number measured in minutes is about 2.5, about 3.0, about 3.5, about 4.0, about 4.5, about 5.0, about 5.5, about 6.0, about 6.5, about 7.0, or any range that is formed from two or more of the above values as endpoints of the range.
• the peroxide destruction number measured in minutes is about 10, about 15, about 20, about 25, about 30, about 35, about 40, about 45, or any range that is formed from two or more of the above values as endpoints of the range.
• the peroxide number is related to and has some correlation with the CDN and C1-DN, in that each are measures of the catalytic activity of the sorbent material. However, the correlation is not always exact, because each represents a different aspect of the catalytic activity of a sorbent material. Still further, the catalytic activity is useful only for those compounds that are catalyzed, but other compounds must be adsorbed to be effectively removed from a fluid stream.
• a superior sorbent material therefore must have good performance in more than one of the CDN, C1-DN, peroxide number, and adsorption tests so that it is effective at removing a broad range of compounds from fluid streams.
• Fluid Treatment [0077] Further embodiments are directed to methods for purifying fluids such as water by using the chlorine and chloramine destroying sorbent materials described above.
• a fluid is treated by flowing the fluid over a bed of sorbent material, introducing fluid onto a filter including sorbent material, introducing sorbent material into a container for holding fluid, and the like.
• the above steps are combined in parallel or subsequently in series.
• the fluid is water.
• the fluid is water that is for human, plant, animal, or marine life consumption. In some embodiments, the fluid is in liquid form.
• the methods of purifying fluids includes additional steps. For example, in some embodiments, methods for purifying includes the steps of filtering the fluid using, for example, a screen or sand filter before, after, or both before and after contacting with sorbent material to remove particulates. In further embodiments, the methods include a step of disinfecting the water to remove biological contaminants such as bacteria or other microorganisms, and in some embodiments, the methods include the step of introducing a disinfectant into the fluid or irradiating the fluid with ultraviolet radiation.
• the methods include the step of clarifying the fluid, adjusting the pH of the fluid, and the like and combinations thereof.
• the fluid can be water.
• EXAMPLES [0079] The following experimental examples are intended to better illustrate specific embodiments, and they are not intended to limit the disclosure.
• Single Stage Process Examples [0080] Coconut shell carbonaceous material was provided, processed and activated. The resultant coconut shell activated carbon is available from Calgon Carbon Corporation under the product name OLC and is referred to as precursor activated carbon. The coconut shell activated carbon is a granular activated carbon and tested in the sizes of 12 ⁇ 30 and 12 ⁇ 40.
• the activated carbons that are specified numerically such as 12 ⁇ 40 are specified as all particles that pass through a 12 US mesh size (1.7 mm openings) screen, but which are retained by a 30 US mesh (0.6 mm openings) screen. Thus, again using the 12 ⁇ 40 example, the activated carbon would have particle sizes of roughly about 0.6 mm to about 1.7 mm.
• the precursor activated carbon is oxidized for some tests but is not oxidized for other tests. After the provision of the precursor activated carbon and, in some instances, the optional oxidation step, the precursor activated carbon is ready for doping with Cu and N.
• “Precursor activated carbon” referred to throughout this specification and claim refers to either oxidized or unoxidized activated carbon, as appropriate in context.
• CuSO4 ⁇ 5H2O/Urea Doping Process During the Cu and N doping, a single stage doping process is performed. The single stage doping process dopes the oxidized or the unoxidized precursor activated carbon with copper and nitrogen. During the single stage doping process, an aqueous solution containing both copper sulfate pentahydrate and urea contacts the oxidized or unoxidized precursor activated carbon to achieve 0.25-2.0 wt.% Cu and 9.5 wt.% N on the carbon (dry precursor activated carbon basis). [0082] The aqueous solution contacts the precursor activated carbon for up to 30 minutes at ambient temperature.
• the precursor activated carbon is dried for up to two hours at about 100°C to about 150°C to thereby produce a doped precursor activated carbon.
• Table 1 below provides examples.
• the dried, doped precursor activated carbon is then calcined. During calcination, the doped precursor activated carbon is heated under a pure N 2 atmosphere to about 950 °C for about 1 hour. The resultant copper and nitrogen treated activated carbons have excellent sorbent performance when contacted with chloramine.
• Experimental Results [0084] The CDN and the peroxide destruction number, described above, were determined for a representative group of samples and controls, as shown below.
• Copper (II) Carbonate Hydroxide/Ammonium Hydroxide/ Ammonium Carbonate Doping Process During the Cu and N doping, a single stage doping process is performed. The single stage doping process dopes the oxidized or the unoxidized precursor activated carbon with copper from a copper source that is not copper sulfate and nitrogen. For these tests, the source of nitrogen is not limited and can be from multiple sources. [0088] This method avoids the use of copper sulfate which may be beneficial regarding emission controls and reduced corrosion by avoiding acidic SO 3 formation. [0089] Here, the source of copper is copper (II) carbonate hydroxide, Cu 2 CO 3 (OH) 2 .
• the concentration of copper is based on the wt.% of Cu added to the precursor activated carbon (dry carbon basis) before any thermal treatment.
• the nitrogen source may be any or all of: Ammonium hydroxide (NH 4 OH (e.g. aqueous ammonia, 28 wt.%)), ammonium carbonate, (NH 4 ) 2 CO 3 , urea, CO(NH 2 ) 2 .
• the total concentration of nitrogen is based on the wt.% of N added to the precursor activated carbon prior (dry carbon basis) before any thermal treatment. As noted, the nitrogen can come from a combination of these nitrogen sources in various molar percentages.
• FIGS.4-5 show the proportion of elemental nitrogen added to the carbon (again prior to drying, calcination) from each of the nitrogen sources, reported as mol % N.
• Other nitrogen containing precursors with a -3 oxidation state, such as dicyandiamide may be employed.
• the doping operation is performed by first mixing a doping solution by: mixing 1 part 28 wt.% aqueous ammonium hydroxide solution with 1 part water (volumetric basis), adding the desired amount of ammonium carbonate to the solution adding desired amount of urea to the solution adding the desired amount of copper (II) carbonate hydroxide to the solution, and heating the solution gently until all solids are dissolved (nominally 25-100°C).
• the aqueous doping solution then contacts the precursor activated carbon for up to 30 minutes at ambient temperature. After the aqueous solution contacts the precursor activated carbon, the precursor activated carbon is dried for up to two hours at about 100°C to about 150 °C to thereby produce a doped precursor activated carbon.
• the dried, doped precursor activated carbon is then calcined. During calcination, the doped precursor activated carbon is heated under a pure N 2 atmosphere to about 950°C for about 1 hour.
• the resultant copper and nitrogen treated activated carbons have excellent sorbent performance when contacted with chloramine as shown in FIG.4.
• Experimental Results [0094] As shown in FIG 4 , the CDN values reach values as high as 12.9. While the copper (II) carbonate hydroxide-nitrogen doping method produces similar CDN values to the copper sulfate-urea methods (refer to Table 1), it has an added advantage because it avoids emissions and other issues associated with copper sulfate. Thus, in certain embodiments and scenarios, this is an alternative path to achieve good chloramine performance.
• Patent No.5,504,050 are expected to yield superior performance, whether oxidized or not oxidized prior to the doping step.
• U.S. Patent No.5,504,050 is incorporated by reference herein in its entirety.
• copper in any oxidation state is expected to be effective for producing activated carbons with enhanced catalytic properties.
• additional sources of nitrogen such as but not limited to dicyandiamide (DCD) can also be used as a nitrogen instead of urea and/or compounds that contain ammonia or nitrogen in the -3 oxidation state.
• DCD dicyandiamide
• the CuSO 4 /Urea doping method on oxidized OLC is favored by high temperature calcination at about 950°C.
• compositions, methods, and devices are described in terms of “comprising” various components or steps (interpreted as meaning “including, but not limited to”), the compositions, methods, and devices can also “consist essentially of” or “consist of” the various components and steps, and such terminology should be interpreted as defining essentially closed-member groups. It will be further understood by those within the art that if a specific number of an introduced claim recitation is intended, such an intent will be explicitly recited in the claim, and in the absence of such recitation no such intent is present. [0103] For example, as an aid to understanding, the following appended claims may contain usage of the introductory phrases "at least one" and "one or more” to introduce claim recitations.
• each range discussed herein can be readily broken down into a lower third, middle third and upper third, et cetera.
• all language such as “up to,” “at least,” and the like include the number recited and refer to ranges that can be subsequently broken down into subranges as discussed above.
• a range includes each individual member.
• a group having 1-3 components refers to groups having 1, 2, or 3 components.
• a group having 1-5 components refers to groups having 1, 2, 3, 4, or 5 components, and so forth.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Analytical Chemistry (AREA)
• Inorganic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Water Supply & Treatment (AREA)
• Life Sciences & Earth Sciences (AREA)
• Hydrology & Water Resources (AREA)
• Environmental & Geological Engineering (AREA)
• Physics & Mathematics (AREA)
• Thermal Sciences (AREA)
• Materials Engineering (AREA)
• Solid-Sorbent Or Filter-Aiding Compositions (AREA)
• Catalysts (AREA)
• Exhaust Gas Treatment By Means Of Catalyst (AREA)
• Water Treatment By Sorption (AREA)
• Carbon And Carbon Compounds (AREA)

Priority Applications (6)

Applications Claiming Priority (2)

Publications (1)

Family

ID=80354063

Family Applications (1)

Country Status (9)

Families Citing this family (13)

Citations (7)

Family Cites Families (121)

• 2021
  • 2021-08-31 TW TW110132329A patent/TWI921375B/zh active
  • 2021-08-31 US US17/446,532 patent/US11872539B2/en active Active
  • 2021-08-31 CA CA3189498A patent/CA3189498A1/en active Pending
  • 2021-08-31 JP JP2023507221A patent/JP7853949B2/ja active Active
  • 2021-08-31 MX MX2023002244A patent/MX2023002244A/es unknown
  • 2021-08-31 EP EP21863029.1A patent/EP4204123A4/en active Pending
  • 2021-08-31 KR KR1020237010710A patent/KR20230060515A/ko active Pending
  • 2021-08-31 WO PCT/US2021/071324 patent/WO2022047501A1/en not_active Ceased
  • 2021-08-31 CN CN202180053082.4A patent/CN116075354A/zh active Pending
• 2023
  • 2023-11-06 US US18/502,190 patent/US20240075458A1/en active Pending

Patent Citations (7)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events