WO2021124824A1 - 硬化性パーフルオロポリエーテル粘着剤組成物、その硬化物を用いた粘着剤並びに粘着テープ - Google Patents

硬化性パーフルオロポリエーテル粘着剤組成物、その硬化物を用いた粘着剤並びに粘着テープ Download PDF

Info

Publication number
WO2021124824A1
WO2021124824A1 PCT/JP2020/043943 JP2020043943W WO2021124824A1 WO 2021124824 A1 WO2021124824 A1 WO 2021124824A1 JP 2020043943 W JP2020043943 W JP 2020043943W WO 2021124824 A1 WO2021124824 A1 WO 2021124824A1
Authority
WO
WIPO (PCT)
Prior art keywords
component
perfluoropolyether
group
pressure
sensitive adhesive
Prior art date
Application number
PCT/JP2020/043943
Other languages
English (en)
French (fr)
Inventor
浩之 安田
山口　浩一
Original Assignee
信越化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 信越化学工業株式会社 filed Critical 信越化学工業株式会社
Priority to US17/783,123 priority Critical patent/US20230045921A1/en
Priority to KR1020227019832A priority patent/KR20220116444A/ko
Priority to JP2021565418A priority patent/JP7265038B2/ja
Priority to CN202080086829.1A priority patent/CN114829532A/zh
Publication of WO2021124824A1 publication Critical patent/WO2021124824A1/ja

Abstract

本発明は、硬化性パーフルオロポリエーテル粘着剤組成物であって、下記（Ａ）～（Ｃ）成分：（Ａ）１分子中に少なくとも２個のアルケニル基を有し、かつ主鎖中に－ＣａＦ２ａＯ－で表される繰り返し単位を含むパーフルオロポリエーテル構造を有する直鎖状パーフルオロポリエーテル化合物（ａは１～６の整数）：１００質量部；（Ｂ）１分子中にケイ素原子に結合した水素原子を少なくとも２個有する有機ケイ素化合物：硬化有効量；（Ｃ）ヒドロシリル化反応触媒：触媒量；を含有し、硬化して０．５Ｎ／２５ｍｍ未満の粘着力を有する粘着剤を形成するものである硬化性パーフルオロポリエーテル粘着剤組成物である。これにより、耐熱性、耐候性、撥水性、撥油性等、耐薬品性や耐溶媒性に優れた硬化物であって、特に微粘着性であることを特徴とする硬化物を与える硬化性パーフルオロポリエーテル粘着剤組成物を提供できる。

Description

硬化性パーフルオロポリエーテル粘着剤組成物、その硬化物を用いた粘着剤並びに粘着テープ
　本発明は、耐熱性、耐油性、耐薬品性、耐溶剤性、低温特性、耐湿性、低気体透過性等に優れ、特には微粘着性であることを特徴とする粘着剤（パーフルオロポリエーテルゴム硬化物又はパーフルオロポリエーテルゲル硬化物）を形成するものである硬化性パーフルオロポリエーテル粘着剤組成物（以下、パーフルオロポリエーテル粘着剤組成物という）、並びにその硬化物を用いた粘着剤及び粘着テープに関する。
　従来、１分子中に少なくとも２個のアルケニル基を有し、かつ主鎖中にパーフルオロポリエーテル構造を有する直鎖状パーフルオロポリエーテル化合物、１分子中にＨ－ＳｉＯＳｉＯ構造を２個以上有する有機ケイ素化合物及びヒドロシリル化反応触媒からなる組成物から、耐熱性、耐薬品性、耐溶剤性、撥水性、撥油性、耐候性等の性質がバランスよく優れた硬化物を得ることができることが提案されている（特許文献１、特許文献２）。
　一方、粘着剤は、製品に添付するラベルや粘着テープなどを中心に、様々な場面で使用されている。最近ではディスプレイ保護用の粘着フィルムや製品製造工程中の保護フィルムなど、電子端末関連の技術の進歩に伴い用途が拡大している。また、表面保護だけでなく、材料の透明性を活かし、光学部材にも利用され、Ｏｐｔｉｃａｌ　Ｃｌｅａｒ　Ａｄｈｅｓｉｖｅ　Ｔａｐｅ（ＯＣＡテープ）など、製品部内に使用される用途も展開されている。
　粘着剤の主な分類としては、アクリル系、ゴム系、シリコーン系等があり、それぞれに長所と欠点がある。シリコーン粘着剤は、コスト面でアクリル系やゴム系より不利であるが耐熱性、耐寒性、耐候性、耐薬品性及び電気絶縁性等の特性が他の２種の粘着剤よりも優れている。
　最近では、携帯電話等の端末が広く普及しているが、これらのディスプレイ保護の粘着フィルムはシリコーン粘着剤を用いたものがほとんどである。シリコーンはその特性上、被着体へのぬれ性が良好であるため、貼り合わせる際に気泡を巻き込むことが無く、ひとりでにずれたり剥がれたりすることはないが、リワーク性が良いため貼りなおしも可能である（特許文献３）。また、製品製造工程中に使用する保護フィルムに関しても同様で、更に耐熱性などが必要になるため、シリコーン粘着剤を用いた粘着フィルムが大量に用いられている。
　また、携帯電話の中でもスマートフォンと呼ばれる従来よりも高機能な端末が急速に普及しており、これまでの多くは従来までのボタンの替わりに、タッチパネルと呼ばれるディスプレイに触れることで操作することができる。類似のものにタブレット端末があり、これは持ち運びが容易でタッチパネルを備えるコンピューターである。これらの普及により、ディスプレイの面積が大きくなることに伴い、画面保護用の粘着フィルムの需要は増加傾向にある。
　しかしながら、このようなシリコーン粘着剤は、殆どの用途においてはこれで十分な性能を有しているものの、更なる耐薬品性や耐溶媒性を要求される自動車のエンジン回りや臨床検査、病理検査の工程で使用されるバーコードラベル用途など、耐薬品性や耐溶媒性に優れる粘着剤組成物の出現が強く望まれていた。
　その中で硬化性パーフルオロポリエーテル粘着剤組成物の提案がなされている（特許文献４）。この組成物は耐熱性、耐候性、撥水性、撥油性等に優れている上、耐薬品性や耐溶媒性に優れた硬化物を与えることが示されているが、粘着力が０．５Ｎ／２５ｍｍ以上であるため、被着体の強度が弱く容易に破損することを回避できるような微粘着用途には適していなかった。
特許第２９９０６４６号公報 特開２０００－２４８１６６号公報 特開平０７－１９７００８号公報 特開２０１９－３８９０４号公報
　本発明は、上記事情に鑑みなされたもので、耐熱性、耐候性、撥水性、撥油性等、耐薬品性や耐溶媒性に優れた硬化物であって、特に微粘着性であることを特徴とする硬化物を与える硬化性パーフルオロポリエーテル粘着剤組成物及びその硬化物を含む粘着剤並びに粘着テープを提供することを目的とする。
　上記課題を解決するために、本発明では、硬化性パーフルオロポリエーテル粘着剤組成物であって、下記（Ａ）～（Ｃ）成分、
（Ａ）１分子中に少なくとも２個のアルケニル基を有し、かつ主鎖中に－ＣａＦ２ａＯ－で表される繰り返し単位を含むパーフルオロポリエーテル構造を有する直鎖状パーフルオロポリエーテル化合物（ａは１～６の整数）：１００質量部
（Ｂ）１分子中にケイ素原子に結合した水素原子を少なくとも２個有する有機ケイ素化合物：硬化有効量
（Ｃ）ヒドロシリル化反応触媒：触媒量
を含有し、硬化して０．５Ｎ／２５ｍｍ未満の粘着力（微粘着力）を有する粘着剤を形成するものである硬化性パーフルオロポリエーテル粘着剤組成物を提供する。
　本発明のような（Ａ）～（Ｃ）成分を含有する硬化性パーフルオロポリエーテル粘着剤組成物であれば、耐熱性、耐候性、撥水性、撥油性、耐油性、低温特性、耐湿性、低気体透過性等に優れている上、特に耐薬品性や耐溶媒性に優れるとともに０．５Ｎ／２５ｍｍ未満の粘着力を有する硬化物（粘着剤）を与える硬化性パーフルオロポリエーテル粘着剤組成物となる。０．５Ｎ／２５ｍｍ未満の粘着力を有する硬化物を含む粘着テープは、脆弱な基材に貼った場合にも、基材を傷めずに該基材から剥がすことができる。また、以上のような本発明の（Ａ）～（Ｃ）成分を含有する硬化性パーフルオロポリエーテル粘着剤組成物であれば、ゴム硬化物（パーフルオロポリエーテルゴム硬化物）を与えることができる。
　また本発明では硬化性パーフルオロポリエーテル粘着剤組成物であって、下記（Ａ）～（Ｄ）成分、
（Ａ）１分子中に少なくとも２個のアルケニル基を有し、かつ主鎖中に－ＣａＦ２ａＯ－の繰り返し単位を含むパーフルオロポリエーテル構造を有する直鎖状パーフルオロポリエーテル化合物（ａは１～６の整数）：１００～４０質量部
（Ｄ）１分子中に１個のアルケニル基を有し、かつ主鎖中にパーフルオロポリエーテル構造を有するポリフルオロモノアルケニル化合物：０～６０質量部（但し、（Ａ）、（Ｄ）成分の合計量を１００質量部とする）
（Ｂ）１分子中にケイ素原子に結合した水素原子を少なくとも２ 個有する有機ケイ素化合物：硬化有効量
（Ｃ）ヒドロシリル化反応触媒： 触媒量
を含有し、硬化して０．５Ｎ／２５ｍｍ未満の粘着力を有する粘着剤を形成するものである硬化性パーフルオロポリエーテル粘着剤組成物を提供する。
　本発明のような（Ａ）～（Ｄ）成分を含有する硬化性パーフルオロポリエーテル粘着剤組成物であれば、耐熱性、耐候性、撥水性、撥油性、耐油性、低温特性、耐湿性、低気体透過性等に優れている上、特に耐薬品性や耐溶媒性に優れるとともに０．５Ｎ／２５ｍｍ未満の粘着力を有する硬化物（粘着剤）を与える硬化性パーフルオロポリエーテル粘着剤組成物となる。０．５Ｎ／２５ｍｍ未満の粘着力を有する硬化物を含む粘着テープは、脆弱な基材に貼った場合にも、基材を傷めずに該基材から剥がすことができる。また、以上のような本発明の（Ａ）～（Ｄ）成分を含有する硬化性パーフルオロポリエーテル粘着剤組成物であれば、ゴム又はゲル硬化物（パーフルオロポリエーテルゴム硬化物又はゲル硬化物）を与えることができる。
　この場合、前記（Ｄ）成分が、下記一般式（２）
Ｒｆ１－（Ｘ’）ｐ－ＣＨ＝ＣＨ２（２）
［式中、Ｘ’は－ＣＨ２－、－ＯＣＨ２－、－ＣＨ２ＯＣＨ２－、又は－ＣＯ－ＮＲ２－Ｙ’－（但し、Ｙ’は－ＣＨ２－又は下記構造式（Ｚ’）で示される基であり、
Figure JPOXMLDOC01-appb-C000014
 （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）
Ｒ２は水素原子、メチル基、フェニル基、又はアリル基である。）であり、ｐは０又は１である。Ｒｆ１は、一般式Ｆ－［ＣＦ（ＣＦ３）ＣＦ２Ｏ］ｗ－ＣＦ（ＣＦ３）－（式中、ｗは１～５００の整数で表される。）で示されるパーフルオロポリエーテル構造である。］で表されるポリフルオロモノアルケニル化合物であることが好ましい。
　このような（Ｄ）成分を含む組成物であれば、より耐薬品性や耐溶媒性に優れた硬化物（粘着剤）を与える硬化性パーフルオロポリエーテル粘着剤組成物となる。
　また、前記（Ａ）成分が、下記一般式（１）
Figure JPOXMLDOC01-appb-C000015
 ［式中、Ｘは－ＣＨ２－、－ＣＨ２Ｏ－、－ＣＨ２ＯＣＨ２－、又は－Ｙ－ＮＲ１－ＣＯ－（但し、Ｙは－ＣＨ２－又は下記構造式（Ｚ）で示される基であり、Ｒ１は水素原子、メチル基、フェニル基、又はアリル基である。）である。Ｘ’は－ＣＨ２－、－ＯＣＨ２－、－ＣＨ２ＯＣＨ２－、又は－ＣＯ－ＮＲ２－Ｙ’－（但し、Ｙ’は－ＣＨ２－又は下記構造式（Ｚ’）で示される基であり、Ｒ２は水素原子、メチル基、フェニル基、又はアリル基である。）である。ｐは独立に０又は１、ｒは２～６の整数、ｍ、ｎはそれぞれ０～６００の整数であり、更にｍとｎの和が５０～６００である。
Figure JPOXMLDOC01-appb-C000016
 （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）
Figure JPOXMLDOC01-appb-C000017
 （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）］
で表される直鎖状パーフルオロポリエーテル化合物であることが好ましい。
　このような（Ａ）成分を含む組成物であれば、より耐薬品性や耐溶媒性に優れた硬化物（粘着剤）を与えるとともに、粘着テープに必要な粘着性を与えるのに十分な粘着力を有する硬化性パーフルオロポリエーテル粘着剤組成物となる。
　例えば、（Ａ）成分が上記一般式（１）で表される直鎖状パーフルオロポリエーテル化合物であり、該（Ａ）成分１００～８０質量部に対して（Ｄ）成分を０～２０質量部（但し、（Ａ）成分と（Ｄ）成分の合計は１００質量部）を含み、（Ｂ）成分が環状のシロキサン構造を有する含フッ素オルガノ水素ポリシロキサンであることが好ましい。
　また、（Ａ）成分が上記一般式（１）で表される直鎖状パーフルオロポリエーテル化合物であり、該（Ａ）成分７９～５５質量部に対して（Ｄ）成分を２１～４５質量部（但し、（Ａ）成分と（Ｄ）成分の合計は１００質量部）を含み、（Ｂ）成分が直鎖状及び／又は分岐鎖状のシロキサン構造を有する含フッ素ポリオルガノ水素シロキサンであることも好ましい。
　また、（Ａ）成分が、主鎖に（ＣＦ２Ｏ）単位及び（ＣＦ２ＣＦ２Ｏ）単位の繰り返しからなる二価のパーフルオロポリエーテル構造を含む直鎖状パーフルオロポリエーテル化合物であり、該（Ａ）成分１００～５０質量部に対して（Ｄ）成分を０～５０質量部（但し、（Ａ）成分と（Ｄ）成分の合計は１００質量部）を含み、（Ｂ）成分が直鎖状及び／又は分岐鎖状のシロキサン構造を有する含フッ素オルガノ水素ポリシロキサンであることも好ましい。
　また、（Ａ）成分が、上記一般式（１）で表され、主鎖に（ＣＦ２Ｏ）単位及び（ＣＦ２ＣＦ２Ｏ）単位の繰り返しからなる二価のパーフルオロポリエーテル構造を含む直鎖状パーフルオロポリエーテル化合物であり、該（Ａ）成分１００～５０質量部に対して（Ｄ）成分を０～５０質量部（但し、（Ａ）成分と（Ｄ）成分の合計は１００質量部）を含み、（Ｂ）成分が直鎖状及び／又は分岐鎖状のシロキサン構造を有する含フッ素オルガノ水素ポリシロキサンであることも好ましい。
　これらの例の組成物であれば、より耐薬品性や耐溶媒性に優れた硬化物（粘着剤）を与えることができ、得られた硬化物を含んだ粘着テープは、脆弱な基材に貼った場合にも、基材を傷めずに該基材から剥がすことができる。
　また、前記硬化性パーフルオロポリエーテル粘着剤組成物の硬化物が、体積抵抗率が１×１０９Ω・ｃｍ以上の非導電性粘着剤であることが好ましい。
　本発明の硬化性パーフルオロポリエーテル粘着剤組成物は、このような非導電性粘着剤の材料として好適に用いることができる。
　また、前記硬化性パーフルオロポリエーテル粘着剤組成物の硬化物を含む粘着剤を提供する。
　このように、本発明の硬化性パーフルオロポリエーテル粘着剤組成物は、粘着剤として用いることができる。
　また、本発明では、基材上に、前記硬化性パーフルオロポリエーテル粘着剤組成の硬化物層が積層している粘着テープを提供する。
　このように、本発明の硬化性パーフルオロポリエーテル粘着剤組成物の硬化物層（パーフルオロポリエーテルゴム硬化物又はパーフルオロポリエーテルゲル硬化物からなる粘着剤層）を、基材上に積層することにより非導電性の粘着剤層を有する粘着テープとして用いることができる。
　以上のように、本発明のパーフルオロポリエーテル粘着剤組成物であれば、耐熱性、耐候性、撥水性、撥油性、耐油性、低温特性、耐湿性、低気体透過性等に優れ、特には耐薬品性、耐溶剤性に優れるとともに、０．５Ｎ／２５ｍｍ未満の粘着力（微粘着力）を有するゴム状又はゲル状の硬化物（粘着剤）を与えることができる。０．５Ｎ／２５ｍｍ未満の粘着力を有する硬化物を含む粘着テープ（微粘着テープ）は、脆弱な基材に貼った場合にも、基材を傷めずに該基材から剥がすことができる。
　上記のように、耐熱性、耐候性、撥水性、撥油性等に優れている上、特に耐薬品性や耐溶媒性に優れ、更に被着体の強度が弱い場合にその破損を回避できるような微粘着タイプの硬化物（粘着剤）を与える硬化性パーフルオロポリエーテル粘着剤組成物及びその硬化物を含む粘着剤の開発が求められていた。
　本発明者らは、上記目的を達成するため鋭意検討を行った結果、本発明に係る特定のパーフルオロポリエーテル粘着剤組成物によれば、従来のシリコーン粘着剤より耐薬品性や耐溶媒性に優れたゴム状又はゲル状の硬化物（パーフルオロポリエーテルゴム硬化物又はパーフルオロポリエーテルゲル硬化物）を与える微粘着性の粘着剤組成物が得られることを見出し、本発明をなすに至った。
　従って、本発明は下記の硬化性パーフルオロポリエーテル粘着剤組成物、その硬化物を用いた粘着剤並びに粘着テープを与えるものである。
　［１］
　硬化性パーフルオロポリエーテル粘着剤組成物であって、下記（Ａ）～（Ｃ）成分、
（Ａ）１分子中に少なくとも２個のアルケニル基を有し、かつ主鎖中に－ＣａＦ２ａＯ－で表される繰り返し単位を含むパーフルオロポリエーテル構造を有する直鎖状パーフルオロポリエーテル化合物（ａは１～６の整数）：１００質量部
（Ｂ）１分子中にケイ素原子に結合した水素原子を少なくとも２個有する有機ケイ素化合物：硬化有効量
（Ｃ）ヒドロシリル化反応触媒：触媒量
を含有し、硬化して０．５Ｎ／２５ｍｍ未満の粘着力を有する粘着剤を形成するものである硬化性パーフルオロポリエーテル粘着剤組成物。
　［２］
　硬化性パーフルオロポリエーテル粘着剤組成物であって、下記（Ａ）～（Ｄ）成分、
（Ａ）１分子中に少なくとも２個のアルケニル基を有し、かつ主鎖中に－ＣａＦ２ａＯ－の繰り返し単位を含むパーフルオロポリエーテル構造を有する直鎖状パーフルオロポリエーテル化合物（ａは１～６の整数）：１００～４０質量部
（Ｄ）１分子中に１個のアルケニル基を有し、かつ主鎖中にパーフルオロポリエーテル構造を有するポリフルオロモノアルケニル化合物：０～６０質量部（但し、（Ａ）、（Ｄ）成分の合計量を１００質量部とする）
（Ｂ）１分子中にケイ素原子に結合した水素原子を少なくとも２個有する有機ケイ素化合物：硬化有効量
（Ｃ）ヒドロシリル化反応触媒： 触媒量
を含有し、硬化して０．５Ｎ／２５ｍｍ未満の粘着力を有する粘着剤を形成するものである硬化性パーフルオロポリエーテル粘着剤組成物。
　［３］
　前記（Ｄ）成分が、下記一般式（２）
Ｒｆ１－（Ｘ’）ｐ－ＣＨ＝ＣＨ２（２）
［式中、Ｘ’は－ＣＨ２－、－ＯＣＨ２－、－ＣＨ２ＯＣＨ２－、又は－ＣＯ－ＮＲ２－Ｙ’－（但し、Ｙ’は－ＣＨ２－又は下記構造式（Ｚ’）で示される基であり、
Figure JPOXMLDOC01-appb-C000018
 （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）
Ｒ２は水素原子、メチル基、フェニル基、又はアリル基である。）であり、ｐは０又は１である。Ｒｆ１は、一般式Ｆ－［ＣＦ（ＣＦ３）ＣＦ２Ｏ］ｗ－ＣＦ（ＣＦ３）－（式中、ｗは１～５００の整数で表される。）で示されるパーフルオロポリエーテル構造である。］で表されるポリフルオロモノアルケニル化合物である［２］に記載の硬化性パーフルオロポリエーテル粘着剤組成物。
　［４］
　前記（Ａ）成分が、下記一般式（１）
Figure JPOXMLDOC01-appb-C000019
 ［式中、Ｘは－ＣＨ２－、－ＣＨ２Ｏ－、－ＣＨ２ＯＣＨ２－、又は－Ｙ－ＮＲ１－ＣＯ－（但し、Ｙは－ＣＨ２－又は下記構造式（Ｚ）で示される基であり、Ｒ１は水素原子、メチル基、フェニル基、又はアリル基である。）である。Ｘ’は－ＣＨ２－、－ＯＣＨ２－、－ＣＨ２ＯＣＨ２－、又は－ＣＯ－ＮＲ２－Ｙ’－（但し、Ｙ’は－ＣＨ２－又は下記構造式（Ｚ’）で示される基であり、Ｒ２は水素原子、メチル基、フェニル基、又はアリル基である。）である。ｐは独立に０又は１、ｒは２～６の整数、ｍ、ｎはそれぞれ０～６００の整数であり、更にｍとｎの和が５０～６００である。
Figure JPOXMLDOC01-appb-C000020
 （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）
Figure JPOXMLDOC01-appb-C000021
 （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）］
で表される直鎖状パーフルオロポリエーテル化合物であることを特徴とする［１］～［３］のいずれかに記載の硬化性パーフルオロポリエーテル粘着剤組成物。
　［５］
　（Ａ）成分が上記一般式（１）で表される直鎖状パーフルオロポリエーテル化合物であり、該（Ａ）成分１００～８０質量部に対して（Ｄ）成分を０～２０質量部（但し、（Ａ）成分と（Ｄ）成分の合計は１００質量部）を含み、（Ｂ）成分が環状のシロキサン構造を有する含フッ素オルガノ水素ポリシロキサンである［２］又は［３］に記載の硬化性パーフルオロポリエーテル粘着剤組成物。
　［６］
　（Ａ）成分が上記一般式（１）で表される直鎖状パーフルオロポリエーテル化合物であり、該（Ａ）成分７９～５５質量部に対して（Ｄ）成分を２１～４５質量部（但し、（Ａ）成分と（Ｄ）成分の合計は１００質量部）を含み、（Ｂ）成分が直鎖状及び／又は分岐鎖状のシロキサン構造を有する含フッ素オルガノ水素ポリシロキサンである［２］又は［３］に記載の硬化性パーフルオロポリエーテル粘着剤組成物。
　［７］
　（Ａ）成分が、主鎖に（ＣＦ２Ｏ）単位及び（ＣＦ２ＣＦ２Ｏ）単位の繰り返しからなる二価のパーフルオロポリエーテル構造を含む直鎖状パーフルオロポリエーテル化合物であり、該（Ａ）成分１００～５０質量部に対して（Ｄ）成分を０～５０質量部（但し、（Ａ）成分と（Ｄ）成分の合計は１００質量部）を含み、（Ｂ）成分が直鎖状及び／又は分岐鎖状のシロキサン構造を有する含フッ素オルガノ水素ポリシロキサンである［２］又は［３］に記載の硬化性パーフルオロポリエーテル粘着剤組成物。
　［８］
　（Ａ）成分が上記一般式（１）で表され、主鎖に（ＣＦ２Ｏ）単位及び（ＣＦ２ＣＦ２Ｏ）単位の繰り返しからなる二価のパーフルオロポリエーテル構造を含む直鎖状パーフルオロポリエーテル化合物であり、該（Ａ）成分１００～５０質量部に対して（Ｄ）成分を０～５０質量部（但し、（Ａ）成分と（Ｄ）成分の合計は１００質量部）を含み、（Ｂ）成分が直鎖状及び／又は分岐鎖状のシロキサン構造を有する含フッ素オルガノ水素ポリシロキサンである［２］又は［３］に記載の硬化性パーフルオロポリエーテル粘着剤組成物。
　［９］
　前記硬化性パーフルオロポリエーテル粘着剤組成物の硬化物が、体積抵抗率が１×１０９Ω・ｃｍ以上の非導電性粘着剤である［１］～［８］のいずれかに記載の硬化性パーフルオロポリエーテル粘着剤組成物。
　［１０］
　［１］～［９］のいずれかに記載の硬化性パーフルオロポリエーテル粘着剤組成物の硬化物を含む粘着剤。
　［１１］
　基材上に、［１］～［９］のいずれかに記載の硬化性パーフルオロポリエーテル粘着剤組成物の硬化物層が積層している粘着テープ。
　すなわち、本発明の第一の態様は、ゴム状硬化物（パーフルオロポリエーテルゴム硬化物）を与える硬化性パーフルオロポリエーテル粘着剤組成物であって、下記（Ａ）～（Ｃ）成分、
（Ａ）１分子中に少なくとも２個のアルケニル基を有し、かつ主鎖中に－ＣａＦ２ａＯ－で表される繰り返し単位を含むパーフルオロポリエーテル構造を有する直鎖状パーフルオロポリエーテル化合物（ａは１～６の整数）：１００質量部
（Ｂ）１分子中にケイ素原子に結合した水素原子を少なくとも２個有する有機ケイ素化合物：硬化有効量
（Ｃ）ヒドロシリル化反応触媒：触媒量
を含有し、硬化して０．５Ｎ／２５ｍｍ未満の粘着力を有する粘着剤（パーフルオロポリエーテルゴム硬化物）を形成するものである硬化性パーフルオロポリエーテル粘着剤組成物である。
　以下、本発明の第一の態様について詳細に説明するが、本発明はこれらに限定されるものではない。
　［（Ａ）成分］
　本発明の硬化性パーフルオロポリエーテル粘着剤組成物に含まれる（Ａ）成分は、本発明の硬化性パーフルオロポリエーテル粘着剤組成物の主剤（ベースポリマー）として作用するものであり、１分子中に少なくとも２個のアルケニル基を有し、かつ主鎖中にパーフルオロポリエーテル構造（パーフルオロオキシアルキレン構造）、好ましくは二価のパーフルオロオキシアルキレン構造を有する直鎖状パーフルオロポリエーテル化合物である。
　ここで、パーフルオロオキシアルキレン構造としては、－ＣａＦ２ａＯ－（式中、各単位のａは独立に１～６の整数である。）で示されるオキシアルキレン単位の多数の繰り返し構造を含むもので、例えば下記一般式（５）で示されるものなどが挙げられる。
　　（ＣａＦ２ａＯ）ｑ　　　　　　　　　　　　　　　　　　　　　（５）
（式中、ｑは５０～６００の整数、好ましくは５０～４００の整数、より好ましくは５０～２００の整数である。）
　上記式（５）で示されるパーフルオロオキシアルキレン構造を構成する個々の繰り返し構造－ＣａＦ２ａＯ－（即ち、オキシアルキレン単位）としては、例えば下記の構造等が挙げられる。なお、上記パーフルオロアルキルエーテル構造は、これらの繰り返し構造の１種単独で構成されていてもよいし、２種以上の組み合わせであってもよい。
－ＣＦ２Ｏ－
－ＣＦ２ＣＦ２Ｏ－
－ＣＦ２ＣＦ２ＣＦ２Ｏ－
－ＣＦ（ＣＦ３）ＣＦ２Ｏ－
－ＣＦ２ＣＦ２ＣＦ２ＣＦ２Ｏ－
－ＣＦ２ＣＦ２ＣＦ２ＣＦ２ＣＦ２ＣＦ２Ｏ－
－Ｃ（ＣＦ３）２Ｏ－
　これらの中では、特に下記構造が好適である。
－ＣＦ２Ｏ－
－ＣＦ２ＣＦ２Ｏ－
－ＣＦ２ＣＦ２ＣＦ２Ｏ－
－ＣＦ（ＣＦ３）ＣＦ２Ｏ－
　なお、本発明において「直鎖状」とは、主鎖のパーフルオロポリエーテル構造（パーフルオロオキシアルキレン構造）を構成する個々の繰り返し単位－ＣａＦ２ａＯ－（オキシアルキレン単位）同士が直鎖状に結合していることを意味するものであって、それぞれの繰り返し単位（オキシアルキレン単位）自体は、直鎖状のオキシアルキレン単位であっても分岐状のオキシアルキレン単位（例えば、－ＣＦ（ＣＦ３）ＣＦ２Ｏ－、－Ｃ（ＣＦ３）２Ｏ－等）であってもよい。
　（Ａ）成分は、主鎖に（ＣＦ２Ｏ）単位及び（ＣＦ２ＣＦ２Ｏ）単位の繰り返しからなる二価のパーフルオロポリエーテル構造を含む直鎖状パーフルオロポリエーテル化合物であることが特に好ましい。
　この（Ａ）成分の直鎖状パーフルオロポリエーテル化合物におけるアルケニル基としては、炭素数２～８、特に炭素数２～６で、かつ末端にＣＨ２＝ＣＨ－構造を有するものが好ましく、例えば、ビニル基、アリル基、プロペニル基、イソプロペニル基、ブテニル基、ヘキセニル基等の末端にＣＨ２＝ＣＨ－構造を有する基、特にビニル基、アリル基等が好ましい。このアルケニル基は、直鎖状パーフルオロポリエーテル化合物の主鎖を構成するパーフルオロポリエーテル構造、特には二価のパーフルオロオキシアルキレン構造の両端部に直接結合していてもよいし、二価の連結基、例えば、－ＣＨ２－、－ＣＨ２Ｏ－、－ＣＨ２ＯＣＨ２－、又は－Ｙ－ＮＲ－ＣＯ－［但し、Ｙは－ＣＨ２－又は下記構造式（Ｚ）で示される基
Figure JPOXMLDOC01-appb-C000022
 （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）
であり、Ｒは水素原子、メチル基、フェニル基、又はアリル基である。］等を介して結合していてもよい。また、（Ａ）成分は、アルケニル基を１分子中に少なくとも２個有する。
　（Ａ）成分としては、下記一般式（６）又は（７）で表されるポリフルオロジアルケニル化合物を挙げることができる。
　ＣＨ２＝ＣＨ－（Ｘ）ｐ－Ｒｆ２－（Ｘ’）ｐ－ＣＨ＝ＣＨ２　　　　　　（６）
　ＣＨ２＝ＣＨ－（Ｘ）ｐ－Ｑ－Ｒｆ２－Ｑ－（Ｘ’）ｐ－ＣＨ＝ＣＨ２　　（７）
［式中、Ｘは独立に－ＣＨ２－、－ＣＨ２Ｏ－、－ＣＨ２ＯＣＨ２－、又は－Ｙ－ＮＲ１－ＣＯ－（但し、Ｙは－ＣＨ２－又は下記構造式（Ｚ）で示される基であり、Ｒ１は水素原子、メチル基、フェニル基、又はアリル基である。）であり、Ｘ’は－ＣＨ２－、－ＯＣＨ２－、－ＣＨ２ＯＣＨ２－、又は－ＣＯ－ＮＲ２－Ｙ’－（但し、Ｙ’は－ＣＨ２－又は下記構造式（Ｚ’）で示される基であり、Ｒ２は水素原子、メチル基、フェニル基又はアリル基である。）である。
Figure JPOXMLDOC01-appb-C000023
 （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）
Figure JPOXMLDOC01-appb-C000024
 （オルト、メタ、又はパラ位で示されるジメチルシリルフェニレン基）
　Ｒｆ２は二価のパーフルオロポリエーテル構造（パーフルオロオキシアルキレン構造）であり、上記式（５）、即ち（ＣａＦ２ａＯ）ｑで示されるものが好ましい。Ｑは炭素数１～１５の二価の炭化水素基であり、エーテル結合を含んでいてもよく、具体的にはアルキレン基、エーテル結合を含んでいてもよいアルキレン基である。ｐは独立に０又は１である。］
　このような（Ａ）成分は、主鎖に（ＣＦ２Ｏ）単位及び（ＣＦ２ＣＦ２Ｏ）単位の繰り返しからなる二価のパーフルオロポリエーテル構造を含む直鎖状パーフルオロポリエーテル化合物であることが特に好ましい。
　このような（Ａ）成分の直鎖状パーフルオロポリエーテル化合物としては、特に下記一般式（１）で示されるものが好適である。
Figure JPOXMLDOC01-appb-C000025
 ［式中、Ｘ、Ｘ’及びｐは前記と同じであり、ｒは２～６の整数、ｍ、ｎはそれぞれ０～６００の整数であり、更にｍとｎの和が５０～６００である。］
　上記一般式（１）の直鎖状パーフルオロポリエーテル化合物は、フッ素系溶剤を展開溶媒としたゲルパーミエーションクロマトグラフィー（ＧＰＣ）分析による分子量分布測定におけるポリエチレン換算の重量平均分子量が３，０００～１００，０００、特に４，０００～５０，０００であることが望ましい。重量平均分子量が４，０００以上であれば、ガソリンや各種溶剤に対する膨潤が小さくなる。特に、ガソリンに対する膨潤が６％以下となり、耐ガソリン性が要求される部材として特性を満足することができる。また、重量平均分子量が１００，０００以下であれば、粘度が高すぎず、作業性に優れるため実用的である。なお、上記一般式（１）の直鎖状パーフルオロポリエーテル化合物の重合度（ｍ＋ｎ）の値も同様に、フッ素系溶剤を展開溶媒としたゲルパーミエーションクロマトグラフィー（ＧＰＣ）分析による分子量分布測定におけるポリエチレン換算の数平均重合度又は重量平均重合度等として求めることができる。なお、これらの数平均重合度や数平均分子量は、１９Ｆ－ＮＭＲスペクトルから得られる末端構造と繰り返し単位構造の比率から算出することもできる。
　一般式（１）で表される直鎖状パーフルオロポリエーテル化合物の具体例としては、下記式で表されるものが挙げられる。
Figure JPOXMLDOC01-appb-C000026
Figure JPOXMLDOC01-appb-C000027
Figure JPOXMLDOC01-appb-C000028
 （式中、ｍ及びｎはそれぞれ０～６００の整数、好ましくは０～２００の整数、ｍ＋ｎ＝５０～６００、好ましくはｍ＋ｎ＝５０～２００を満足する整数を示す。）
　更に、本発明では、上記式（１）の直鎖状パーフルオロポリエーテル化合物を目的に応じた所望の重量平均分子量に調節するため、予め上記したような直鎖状パーフルオロポリエーテル化合物を分子内にＳｉＨ基を２個含有する有機ケイ素化合物と通常の方法及び条件でヒドロシリル化反応させ、鎖長延長した生成物を（Ａ）成分として使用することも可能である。なお、（Ａ）成分の直鎖状パーフルオロポリエーテル化合物は１種単独で使用しても２種以上を併用してもよい。
　［（Ｂ）成分］
　（Ｂ）成分は、（Ａ）成分の架橋剤及び／又は鎖長延長剤として作用するものである。この（Ｂ）成分は、１分子中にケイ素原子に結合した水素原子（ＳｉＨで示されるヒドロシリル基）を少なくとも２個、好ましくは３個以上有するオルガノハイドロジエンポリシロキサン等の有機ケイ素化合物である。なお、（Ｂ）成分の有機ケイ素化合物は、（Ａ）成分、あるいは後述する本発明の第二の実施態様においては（Ａ）成分及び後述する（Ｄ）成分との相溶性、分散性、硬化後のゴム又はゲル硬化物（粘着剤）の均一性等の観点から、１分子中に１個以上の一価のパーフルオロアルキル基、一価のパーフルオロオキシアルキル基、二価のパーフルオロアルキレン基及び／又は二価のパーフルオロオキシアルキレン基を有している含フッ素オルガノ水素ポリシロキサンを好適に使用することができる。
　かかる（Ｂ）成分としては、前記特許文献１、特許文献２および特許文献４記載の公知の有機ケイ素化合物が挙げられるが、特に限定されるものではない。
　この一価又は二価の含フッ素有機基としては、例えば下記式で表されるパーフルオロアルキル基、パーフルオロオキシアルキル基、パーフルオロアルキレン基及びパーフルオロオキシアルキレン基等を挙げることができる。
ＣgＦ2g+1－
－ＣgＦ2g－
（式中、ｇは１～２０の整数、好ましくは２～１０の整数である。）
Figure JPOXMLDOC01-appb-C000029
 （式中、ｆは１～２００の整数、好ましくは１～１００の整数、ｈは１～３の整数である。）
Figure JPOXMLDOC01-appb-C000030
 　（式中、ｉ及びｊはそれぞれ１以上の整数、好ましくは１～１００の整数であり、ｉ＋ｊの平均は２～２００、好ましくは２～１００である。）
　－（ＣＦ２Ｏ）ｄ－（ＣＦ２ＣＦ２Ｏ）ｅ－ＣＦ２－
　（式中、ｄ及びｅはそれぞれ１～５０の整数、好ましくは１～４０の整数である。）
　また、これらパーフルオロアルキル基、パーフルオロオキシアルキル基、パーフルオロアルキレン基又はパーフルオロオキシアルキレン基とケイ素原子とは２価の連結基により繋がれていることが好ましく、該２価の連結基としては、アルキレン基、アリーレン基及びそれらの組み合わせ、若しくはこれらの基にエーテル結合酸素原子、アミド結合、カルボニル結合、エステル結合、ジオルガノシリレン基等を介在させたものであってもよく、例えば、以下の炭素数２～１２の２価の連結基等が挙げられるが、これらに限定されない。
－ＣＨ２ＣＨ２－、
－ＣＨ２ＣＨ２ＣＨ２－、
－ＣＨ２ＣＨ２ＣＨ２ＯＣＨ２－、
－ＣＨ２ＣＨ２ＣＨ２－ＮＨ－ＣＯ－、
－ＣＨ２ＣＨ２ＣＨ２－Ｎ（Ｐｈ）－ＣＯ－、
－ＣＨ２ＣＨ２ＣＨ２－Ｎ（ＣＨ３）－ＣＯ－、
－ＣＨ２ＣＨ２ＣＨ２－Ｎ（ＣＨ２ＣＨ３）－ＣＯ－、
－ＣＨ２ＣＨ２－Ｓｉ（ＣＨ３）２－Ｐｈ’－Ｎ（ＣＨ３）－ＣＯ－、
－ＣＨ２ＣＨ２ＣＨ２－Ｓｉ（ＣＨ３）２－Ｐｈ’－Ｎ（ＣＨ３）－ＣＯ－、
－ＣＨ２ＣＨ２ＣＨ２－Ｏ－ＣＯ－
（式中、Ｐｈはフェニル基であり、Ｐｈ’はフェニレン基である。）
　また、この（Ｂ）成分の含フッ素オルガノ水素ポリシロキサンにおける上記１価又は２価の含フッ素有機基及びケイ素原子に結合した水素原子以外のケイ素原子に結合した１価の置換基としては、例えば、メチル基、エチル基、プロピル基、ブチル基、ヘキシル基、シクロヘキシル基、オクチル基、デシル基等のアルキル基；ビニル基、アリル基等のアルケニル基；フェニル基、トリル基、ナフチル基等のアリール基；ベンジル基、フェニルエチル基等のアラルキル基及びこれらの基の水素原子の一部又は全部が塩素原子、シアノ基等で置換された、例えば、クロロメチル基、クロロプロピル基、シアノエチル基等の炭素数１～２０、好ましくは１～１２の非置換又は置換の１価炭化水素基が挙げられる。
　（Ｂ）成分の含フッ素オルガノ水素ポリシロキサン中のシロキサン構造としては、環状、直鎖状、分岐鎖状、三次元網状及びそれらの組み合わせのいずれでもよい。この含フッ素オルガノハイドロジェンポリシロキサンのケイ素原子数は、特に制限されるものではないが、通常２～６０、好ましくは３～３０程度である。（Ｂ）成分の含フッ素オルガノ水素ポリシロキサンとしては、特に、一価のパーフルオロアルキル基又は一価のパーフルオロオキシアルキル基を含有する環状構造の含フッ素オルガノハイドロジェンポリシロキサン、あるいは、二価のパーフルオロアルキレン基又は二価のパーフルオロオキシアルキレン基の両末端に分岐状又は環状のオルガノハイドロジェンポリシロキサン構造を有する含フッ素オルガノハイドロジェンポリシロキサンが好ましい。
　このような１価又は２価の含フッ素有機基及びケイ素原子結合水素原子を有する（Ｂ）成分としては、例えば次の化合物が挙げられる。これらの化合物は、１種単独でも２種以上を併用して用いてもよい。なお、下記式において、Ｍｅはメチル基を示し、Ｐｈはフェニル基を示す。
Figure JPOXMLDOC01-appb-C000031
Figure JPOXMLDOC01-appb-C000032
Figure JPOXMLDOC01-appb-C000033
Figure JPOXMLDOC01-appb-C000034
Figure JPOXMLDOC01-appb-C000035
Figure JPOXMLDOC01-appb-C000036
Figure JPOXMLDOC01-appb-C000037
Figure JPOXMLDOC01-appb-C000038
Figure JPOXMLDOC01-appb-C000039
Figure JPOXMLDOC01-appb-C000040
Figure JPOXMLDOC01-appb-C000041
Figure JPOXMLDOC01-appb-C000042
Figure JPOXMLDOC01-appb-C000043
　上記（Ｂ）成分の配合量は、（Ａ）成分及び後述の（Ｄ）成分を硬化する有効量、すなわち硬化有効量であり、特に本組成物中の上記（Ａ）成分が有するアルケニル基１モルに対し、あるいは後述する本発明の第二の実施態様においては（Ａ）成分及び（Ｄ）成分が有するアルケニル基の合計１モルに対し、（Ｂ）成分中のヒドロシリル基（Ｓｉ－Ｈ）が好ましくは０．２～４モル、より好ましくは０．５～３モルとなる量である。ヒドロシリル基（Ｓｉ－Ｈ）が０．２モル以上となる量であれば、架橋度合が十分であり、硬化物が得られない恐れがない。また、ヒドロシリル基（Ｓｉ－Ｈ）が４モル以下となる量であれば、硬化時に発泡してしまう恐れがない。
　（Ｂ）成分は１種を単独で又は２種以上を組み合わせて使用できる。
　［（Ｃ）成分］
　本発明の（Ｃ）成分のヒドロシリル化反応触媒（付加反応触媒）は、（Ａ）成分中のアルケニル基、あるいは後述する本発明の第二の実施態様においては（Ａ）成分及び後述する（Ｅ）成分中のアルケニル基と、（Ｂ）成分中のヒドロシリル基との付加反応を促進する触媒である。このヒドロシリル化反応触媒は、一般に貴金属（白金族金属）の化合物であり、高価格であることから、比較的入手しやすい白金又は白金化合物がよく用いられる。
　白金化合物としては、例えば塩化白金酸又は塩化白金酸とエチレン等のオレフィンとの錯体、アルコールやビニルシロキサンとの錯体、シリカ、アルミナ、カーボン等を担持した金属白金等を挙げることができる。白金化合物以外の白金族金属触媒として、ロジウム、ルテニウム、イリジウム、パラジウム系化合物も知られており、例えばＲｈＣｌ（ＰＰｈ３）３、ＲｈＣｌ（ＣＯ）（ＰＰｈ３）２、Ｒｕ３（ＣＯ）１２、ＩｒＣｌ（ＣＯ）（ＰＰｈ３）２、Ｐｄ（ＰＰｈ３）４等を例示することができる。
　ヒドロシリル化反応触媒の配合量は、触媒量とすることができるが、通常（Ａ）、（Ｂ）及び（Ｄ）成分の合計質量に対して０．１～５００ｐｐｍ（白金族金属の質量換算）の割合で配合することが好ましく、０．１～１００ｐｐｍの割合で配合することがより好ましい。（Ｃ）成分のヒドロシリル化反応触媒は１種を単独で又は２種以上を組み合わせて使用できる。
　［その他の成分］
　本組成物においては、上記の（Ａ）～（Ｃ）成分以外にも、各種配合剤を添加することは任意である。ヒドロシリル化反応触媒の制御剤として、例えば１－エチニル－１－ヒドロキシシクロヘキサン、３－メチル－１－ブチン－３－オール、３，５－ジメチル－１－ヘキシン－３－オール、３－メチル－１－ペンテン－３－オール、フェニルブチノールなどのアセチレンアルコールや、３－メチル－３－ペンテン－１－イン、３，５－ジメチル－３－ヘキセン－１－イン等、あるいはポリメチルビニルシロキサン環式化合物、有機リン化合物等が挙げられ、その添加により硬化反応性と保存安定性を適度に保つことができる。
　また、接着性を付与するためにエポキシ基、アルコキシ基等を含有する、公知の接着性付与剤（例えば、分子中にエポキシ基とトリアルコキシシリル基とを有する接着性官能性基含有加水分解性オルガノシラン化合物（いわゆるエポキシ基含有シランカップリング剤）、分子中にケイ素原子に結合した水素原子（ＳｉＨ基）を必須に含有し、更に炭素原子又は炭素原子と酸素原子を介してケイ素原子に結合したエポキシ基を含有する（含フッ素）オルガノハイドロジェンポリシロキサン、分子中にケイ素原子に結合した水素原子（ＳｉＨ基）を必須に含有し、更に炭素原子又は炭素原子と酸素原子を介してケイ素原子に結合したトリアルコキシシリル基を含有する（含フッ素）オルガノハイドロジェンポリシロキサン、分子中にケイ素原子に結合した水素原子（ＳｉＨ基）を必須に含有し、更に炭素原子又は炭素原子と酸素原子を介してケイ素原子に結合したエポキシ基及び、炭素原子又は炭素原子と酸素原子を介してケイ素原子に結合したトリアルコキシシリル基とを含有する（含フッ素）オルガノハイドロジェンポリシロキサンなど）を添加することもできる。
　また、本発明の第二の態様は、ゴム状硬化物（パーフルオロポリエーテルゴム硬化物）又はゲル状硬化物（パーフルオロポリエーテルゲル硬化物）を与える硬化性パーフルオロポリエーテル粘着剤組成物であって、下記（Ａ）～（Ｄ）成分、
（Ａ）１分子中に少なくとも２個のアルケニル基を有し、かつ主鎖中に－ＣａＦ２ａＯ－の繰り返し単位を含むパーフルオロポリエーテル構造を有する直鎖状パーフルオロポリエーテル化合物（ａは１～６の整数）：１００～４０質量部
（Ｄ）１分子中に１個のアルケニル基を有し、かつ主鎖中にパーフルオロポリエーテル構造を有するポリフルオロモノアルケニル化合物：０～６０質量部（但し、（Ａ）、（Ｄ）成分の合計量を１００質量部とする）
（Ｂ）１分子中にケイ素原子に結合した水素原子を少なくとも２個有する有機ケイ素化合物：硬化有効量
（Ｃ）ヒドロシリル化反応触媒：触媒量
を含有し、硬化して０．５Ｎ／２５ｍｍ未満の粘着力を有する粘着剤（パーフルオロポリエーテルゴム又はゲル硬化物）を形成するものである硬化性パーフルオロポリエーテル粘着剤組成物も提供する。
　このときの（Ａ）～（Ｃ）成分としては、上述で説明したものと同様のものを使用できる。
　なお、本発明の第二の態様の硬化性パーフルオロポリエーテル粘着剤組成物は、（Ｄ）成分の配合量が０～６０質量部である。そのため、本発明の第二の態様の組成物は、（Ｄ）成分を含んでいても含んでいなくてもよい。つまり、本発明の第二の態様の組成物において、（Ｄ）成分は任意成分であり、本発明の第二の態様の組成物が所定量の（Ｄ）成分を含有する場合には、硬化してゲル状硬化物（パーフルオロポリエーテルゲル硬化物）を与えるものであり、また、本発明の第二の態様の組成物の（Ａ）～（Ｃ）成分は先に説明した第一の態様の組成物の（Ａ）～（Ｃ）成分であるため、本発明の第二の態様の組成物のうち（Ｄ）成分を含まないものは、先に説明した第一の態様の硬化してゴム状硬化物を与える硬化性パーフルオロポリエーテル粘着剤組成物であり得る。すなわち、本発明の第二の態様の硬化性パーフルオロポリエーテル粘着剤組成物は、本発明の第一の態様の硬化性パーフルオロポリエーテル粘着剤組成物を包含する。本発明の第二の態様の硬化性パーフルオロポリエーテル粘着剤組成物は、（Ａ）成分を１００～５５質量部、及び（Ｄ）成分を０～４５質量部（但し、（Ａ）、（Ｄ）成分の合計量を１００質量部とする）を含有することが好ましい。
　［（Ｄ）成分］
　（Ｄ）成分は、本発明の硬化性パーフルオロポリエーテル粘着剤組成物において、上述した本発明の第一の実施態様（即ち、ゴム硬化物を与える組成物）に対して、特定の第二の実施態様（即ち、ゴム硬化物又はゲル硬化物を与える組成物）において用いられる成分であり、１分子中に１個のアルケニル基を有し、かつ主鎖中にパーフルオロポリエーテル構造を有する、ポリフルオロモノアルケニル化合物である。特に、下記式（２）のポリフルオロモノアルケニル化合物が好ましい。
　　Ｒｆ１－（Ｘ’）ｐ－ＣＨ＝ＣＨ２　　　　　　　　　　　　　　　（２）
［式中、Ｘ’及びｐは上記と同じであり、Ｒｆ１は、下記一般式で示される。
　　Ｆ－［ＣＦ（ＣＦ３）ＣＦ２Ｏ］ｗ－ＣＦ（ＣＦ３）－
（式中、ｗは１～５００の整数、好ましくは２～２００の整数で表される。）］
　上記一般式（２）で表されるポリフルオロモノアルケニル化合物の具体例としては、例えば、下記のものが挙げられる。
Figure JPOXMLDOC01-appb-C000044
Figure JPOXMLDOC01-appb-C000045
 （上記式において、ｍは１～２００の整数、特に２～１００の整数である。）
　上記式（２）のポリフルオロモノアルケニル化合物を配合する場合、その配合量は、硬化性パーフルオロポリエーテル粘着剤組成物において、本組成物中の上記（Ａ）成分の直鎖状パーフルオロポリエーテルジアルケニル化合物とこの（Ｄ）成分とが、（Ａ）成分１００～４０質量部、（Ｄ）成分０～６０質量部の割合で、（Ａ）成分と（Ｄ）成分の合計量が１００質量部となるように選定される。
　例えば、本発明の第二の態様のパーフルオロポリエーテル粘着剤組成物は、（Ｄ）成分を、（Ａ）成分８０～４０質量部に対して、２０～６０質量部の割合となるように、且つ（Ａ）成分と（Ｄ）成分との合計量が１００質量部となるように含むことができる。なお、（Ｄ）成分のポリフルオロモノアルケニル化合物は１種単独で使用しても２種以上を併用してもよい。
　［その他の成分］
　本組成物においては、上記の（Ａ）～（Ｄ）成分以外にも、第一態様と同様に、上述で説明したものと同様の各種接着性付与剤などの各種配合剤を添加することは任意である。ヒドロシリル化反応触媒の制御剤としては、上述で説明したものと同様のものを例示できる。
　［硬化物］
　本発明のパーフルオロポリエーテル粘着剤組成物は、上記した組成物を硬化させることにより、０．５Ｎ／２５ｍｍ未満、好ましくは０．００１～０．４５Ｎ／２５ｍｍ、より好ましくは０．００２～０．４Ｎ／２５ｍｍの粘着力（表面微粘着力）を有するパーフルオロポリエーテルゴム又はゲルの硬化物からなる粘着剤を形成するものであり、耐熱性、撥水性、撥油性、耐候性等に優れている上、特に耐薬品性、耐溶剤性、に優れる硬化物（粘着剤）を形成させることができ、各種の用途に使用することができる。
　なお、本発明のパーフルオロポリエーテル粘着剤組成物を硬化させてなる硬化物において、表面粘着力を０．５Ｎ／２５ｍｍ未満のゴム又はゲル状の硬化物を得るためには、（Ａ）成分として上記一般式（１）で示される直鎖状パーフルオロポリエーテル化合物を使用する場合には、
　（ｉ）（Ａ）成分１００～８０質量部に対して（Ｄ）成分０～２０質量部を併用する組成物（（Ａ）成分と（Ｄ）成分の合計は１００質量部）において、（Ｂ）成分の架橋剤として環状のシロキサン構造を有する含フッ素オルガノ水素ポリシロキサンを使用する、若しくは
　（ｉｉ）（Ａ）成分７９～５５質量部に対して（Ｄ）成分２１～４５質量部を併用する組成物（（Ａ）成分と（Ｄ）成分の合計は１００質量部）において、（Ｂ）成分の架橋剤として直鎖状及び／又は分岐鎖状のシロキサン構造を有する含フッ素ポリオルガノ水素シロキサンを使用する、
あるいは、（Ａ）成分として上記一般式（６）又は（７）で表されるポリフルオロジアルケニル化合物において主鎖を構成するＲｆ２の二価のパーフルオロポリエーテルとして
（ＣＦ２Ｏ）単位及び（ＣＦ２ＣＦ２Ｏ）単位の繰り返し構造を含む直鎖状パーフルオロポリエーテル化合物を使用する場合には、
　（ｉｉｉ）（Ａ）成分１００～５０質量部に対して（Ｄ）成分０～５０質量部を併用する組成物（（Ａ）成分と（Ｄ）成分の合計は１００質量部）において、（Ｂ）成分の架橋剤として直鎖状及び／又は分岐鎖状のシロキサン構造を有する含フッ素オルガノ水素ポリシロキサンを使用する、
等の条件を満足するパーフルオロポリエーテル粘着剤組成物を使用することが好ましい。
　例えば、本発明の第一の実施態様において、パーフルオロポリエーテル粘着剤組成物は、（Ａ）成分１００質量部に対して、（Ｂ）成分を（Ａ）成分が有するアルケニル基の合計のモル数１に対して（Ｂ）成分のヒドロシリル基が０．２～３．０モルとなる量、（Ｃ）成分が（Ａ）、（Ｂ）成分の合計量に対して白金換算で０．１～１００ｐｐｍを硬化させることにより形成させることができる。
　また、例えば、本発明の第二の実施態様において、パーフルオロポリエーテル粘着剤組成物は、（Ａ）成分１００～４０質量部に対して、（Ｄ）成分が０～６０質量部で、（Ａ）、（Ｄ）成分の合計が１００質量部であり、（Ｂ）成分が（Ａ）成分及び（Ｄ）成分が有するアルケニル基の合計のモル数１に対して（Ｂ）成分のヒドロシリル基が０．２～３．０モルとなる量、（Ｃ）成分が（Ａ）、（Ｂ）、（Ｄ）成分の合計量に対して白金換算で０．１～１００ｐｐｍを硬化させることにより形成させることができる。
　上記したパーフルオロポリエーテル粘着剤組成物の形成は、本発明のそれぞれの組成物を適当な基板上にコーティングした後に硬化を行う、あるいは貼り合わせ等により従来公知の方法により行われる。硬化は、通常６０～１５０℃の温度で１～３０分程度の加熱処理によって容易に行うことができる。
　本発明のパーフルオロポリエーテル粘着剤組成物を用いた粘着剤は、例えば、自動車用、化学プラント用、半導体製造ライン用、分析・理化学機器用、医療機器用、航空機用、光学用等部材として、使用することができる。
　また、例えば、ポリエチレンテレフタレート（ＰＥＴ）フィルム等の有機樹脂フィルムからなる基材上に本発明の硬化性パーフルオロポリエーテル粘着剤組成物の硬化物（パーフルオロポリエーテルゴム硬化物又はパーフルオロポリエーテルゲル硬化物）層を積層してなる粘着テープは、耐熱性、耐油性、低温特性、耐湿性、低気体透過性等に優れ、特には耐薬品性、耐溶剤性に優れた非導電性の粘着剤層を有する粘着テープとして有用である。
　また、本発明の粘着剤組成物をコーティングする場合、基材との密着性あるいは接着性を向上させるために公知のプライマーを併用することが有用である。プライマーにより、基材界面からの薬品及び溶剤の浸入を防止することができ、部品全体の耐酸性、耐薬品性及び耐溶剤性を向上することができる。
　プライマーとしては、シランカップリング剤を主体とするシラン系プライマー、オルガノハイドロジェンポリシロキサンを主体とするプライマー、合成ゴムを主成分とするプライマーや、アクリル樹脂を主成分とするプライマー、ウレタン樹脂を主成分とするプライマー、エポキシ樹脂を主成分とするプライマー、また本発明のパーフルオロポリエーテルゴム組成物に接着付与剤を添加した組成物もプライマーとして使用できる。
　また、本発明の硬化性パーフルオロポリエーテル粘着剤組成物の硬化物（パーフルオロポリエーテルゴム硬化物又はパーフルオロポリエーテルゲル硬化物）は、体積抵抗率が１×１０９Ω・ｃｍ以上の非導電性の粘着剤であることが好ましい。このような本発明の硬化性パーフルオロポリエーテル粘着剤組成物は、非導電性粘着剤の材料として好適である。本発明の硬化性パーフルオロポリエーテル粘着剤組成物の硬化物の体積抵抗率の上限は特に限定されないが、例えば、１×１０１３Ω・ｃｍとすることができる。
　このような本発明のパーフルオロポリエーテル粘着剤組成物であれば、耐熱性、耐候性、耐油性、低温特性、耐湿性、低気体透過性、撥水性、撥油性等に優れ、特には耐薬品性、耐溶剤性（耐溶媒性）に優れ、微粘着性の硬化物（粘着剤）を与える。微粘着性を有する硬化物を含む粘着テープは、脆弱な基材に貼った場合にも、基材を傷めずに剥がすことができる。
　また、本発明の第三の態様は、先に説明した、本発明の硬化性パーフルオロポリエーテル粘着剤組成物の硬化物（パーフルオロポリエーテルゴム硬化物又はパーフルオロポリエーテルゲル硬化物）を含む粘着剤である。
　先に説明したように、本発明のパーフルオロポリエーテル粘着剤組成物は、耐熱性、耐候性、耐油性、耐薬品性、耐溶剤性（耐溶媒性）、低温特性、耐湿性、低気体透過性、撥水性、撥油性等に優れた硬化物（粘着剤）を与えることができる。そのため、本発明の粘着剤は、耐熱性、耐候性、耐油性、耐薬品性、耐溶剤性（耐溶媒性）、低温特性、耐湿性、低気体透過性、撥水性、撥油性等に優れる。更に、本発明の粘着剤が含む硬化物は、微粘着性を有する。そのため、本発明の粘着剤を用いた粘着テープは、脆弱な基材に貼った場合にも、基材を傷めずに該基材から剥がすことができる。
　更に、本発明の第四の態様は、先に説明した、本発明の硬化性パーフルオロポリエーテル粘着剤組成物の硬化物層が積層している粘着テープである。
　先に説明したように、本発明のパーフルオロポリエーテル粘着剤組成物は、耐熱性、耐候性、耐油性、耐薬品性、耐溶剤性（耐溶媒性）、低温特性、耐湿性、低気体透過性、撥水性、撥油性等に優れた硬化物（粘着剤）を与えることができる。そのため、本発明の粘着テープは、耐熱性、耐候性、耐油性、耐薬品性、耐溶剤性（耐溶媒性）、低温特性、耐湿性、低気体透過性、撥水性、撥油性等に優れる。更に、本発明の粘着テープが含む硬化物は、微粘着性を有する。そのため、本発明の粘着テープは、脆弱な基材に貼った場合にも、基材を傷めずに該基材から剥がすことができる。
　以下、実施例及び比較例を示して本発明を具体的に説明するが、本発明は下記の実施例に制限されるものではない。なお、下記例で％は質量％を示す。
　［実施例１～９、比較例１～３］
　下記原料を使用し、表１に示す硬化性パーフルオロポリエーテル粘着剤組成物を調製した。これらの粘着剤組成物を１３０℃、５分の硬化条件にて硬化し、それぞれの硬化物の表面粘着力を測定すると共に、下記方法によって耐溶剤性試験を行った。結果を表１に併記する。
　原料
　（Ａ）直鎖状パーフルオロポリエーテル化合物
　（Ａ－１）２官能性パーフルオロポリエーテル（パーフルオロポリエーテル１）
Figure JPOXMLDOC01-appb-C000046
　（Ａ－２）２官能性パーフルオロポリエーテル（パーフルオロポリエーテル２）
ＣＨ２＝ＣＨ―ＣＨ２―Ｏ―ＣＨ２―Ｒｆ―ＣＨ２―Ｏ－ＣＨ２―ＣＨ＝ＣＨ２
（Ｒｆ：－ＣＦ２Ｏ（ＣＦ２ＣＦ２Ｏ）２０．８（ＣＦ２Ｏ）２２．1ＣＦ２－）、
ただし繰り返し単位ＣＦ２ＣＦ２ＯとＣＦ２Ｏの配列はランダムである
　（Ｄ）１官能性パーフルオロポリエーテル化合物（パーフルオロポリエーテル３）
Figure JPOXMLDOC01-appb-C000047
　（Ｂ）オルガノハイドロジェンポリシロキサン
（ｂ－１）オルガノハイドロジェンシロキサン１
Figure JPOXMLDOC01-appb-C000048
　（ｂ－２）オルガノハイドロジェンシロキサン２
Figure JPOXMLDOC01-appb-C000049
　（Ｃ）白金－ジビニルテトラメチルジシロキサン錯体／エタノール溶液（白金含有量３．０％）
　（ｅ）硬化制御剤：エチニルシクロヘキサノール／５０％トルエン溶液
　（ｆ）ＫＲ－３７００（信越化学工業株式会社製商品名）ジメチルシリコーンをベースとした付加硬化型シリコーン粘着剤
　粘着力測定
　実施例及び比較例の各組成物を、厚み５０μｍ、幅２５ｍｍのＰＥＴ（ポリエチレンテレフタレート）フィルムに厚みが３０μｍとなるようにアプリケータを用いて塗工した後、１３０℃、５分間の条件で加熱してゴム又はゲル状に硬化させ、厚み５０μｍのＰＥＴフィルム上に厚み３０μｍの粘着剤層（ゴム又はゲル硬化物層）が積層された粘着テープを作成した。この粘着テープを金属板（研磨したステンレス板）に貼りつけ、重さ２ｋｇのゴム層で被覆されたローラーを、該テープ基材上で１往復させることにより該粘着テープを圧着した。室温で２０時間放置した後、２５℃において、引っ張り試験機を用いて、各粘着剤層（ゴム又はゲル硬化物層）の粘着力として、３００ｍｍ／分の引張り速度で１８０°の角度で粘着テープをステンレス板から引き剥がすのに要する力（Ｎ／２５ｍｍ）を測定した。
　耐溶剤性試験（重量変化）
　３２φ×１５ｍｍガラス容器内に実施例及び比較例の組成物を３ｇ充填した後、１３０℃、５分間の条件にて硬化させてサンプルを作成し、キシレン及びＦｕｅｌＣ（トルエン／イソオクタンの５０／５０（ｗｔ％）混合溶液）に２５℃にて７日間浸漬し、浸漬前と後の重量変化率を測定した。
Figure JPOXMLDOC01-appb-T000050
　表１に示されるように、本発明の硬化性パーフルオロポリエーテル粘着剤組成物を用いた実施例１～９のような粘着剤であれば、耐溶剤性の高い粘着剤であった。それに対し、シリコーン粘着剤である比較例１は、粘着力が高か過ぎるとともに、耐溶剤性が低かった。また、本発明の必須成分である（Ｂ）成分または（Ｃ）成分が含まれない比較例２および比較例３は、硬化には至らなかった。
　以上のことから、本発明であれば、耐熱性、耐候性、撥水性、撥油性等に優れている上、特に耐薬品性や耐溶媒性に優れた硬化物（粘着剤）を与える微粘着性の硬化性パーフルオロポリエーテル粘着剤組成物となることがわかった。
　なお、本発明は、上記実施形態に限定されるものではない。上記実施形態は例示であり、本発明の特許請求の範囲に記載された技術的思想と実質的に同一な構成を有し、同様な作用効果を奏するものは、いかなるものであっても本発明の技術的範囲に包含される。

Claims (11)

  1. 　硬化性パーフルオロポリエーテル粘着剤組成物であって、下記（Ａ）～（Ｃ）成分、
    （Ａ）１分子中に少なくとも２個のアルケニル基を有し、かつ主鎖中に－ＣａＦ２ａＯ－で表される繰り返し単位を含むパーフルオロポリエーテル構造を有する直鎖状パーフルオロポリエーテル化合物（ａは１～６の整数）：１００質量部
    （Ｂ）１分子中にケイ素原子に結合した水素原子を少なくとも２個有する有機ケイ素化合物：硬化有効量
    （Ｃ）ヒドロシリル化反応触媒：触媒量
    を含有し、硬化して０．５Ｎ／２５ｍｍ未満の粘着力を有する粘着剤を形成するものである硬化性パーフルオロポリエーテル粘着剤組成物。
  2. 　硬化性パーフルオロポリエーテル粘着剤組成物であって、下記（Ａ）～（Ｄ）成分、
    （Ａ）１分子中に少なくとも２個のアルケニル基を有し、かつ主鎖中に－ＣａＦ２ａＯ－の繰り返し単位を含むパーフルオロポリエーテル構造を有する直鎖状パーフルオロポリエーテル化合物（ａは１～６の整数）：１００～４０質量部
    （Ｄ）１分子中に１個のアルケニル基を有し、かつ主鎖中にパーフルオロポリエーテル構造を有するポリフルオロモノアルケニル化合物：０～６０質量部（但し、（Ａ）、（Ｄ）成分の合計量を１００質量部とする）
    （Ｂ）１分子中にケイ素原子に結合した水素原子を少なくとも２個有する有機ケイ素化合物：硬化有効量
    （Ｃ）ヒドロシリル化反応触媒： 触媒量
    を含有し、硬化して０．５Ｎ／２５ｍｍ未満の粘着力を有する粘着剤を形成するものである硬化性パーフルオロポリエーテル粘着剤組成物。
  3. 　前記（Ｄ）成分が、下記一般式（２）
    Ｒｆ１－（Ｘ’）ｐ－ＣＨ＝ＣＨ２（２）
    ［式中、Ｘ’は－ＣＨ２－、－ＯＣＨ２－、－ＣＨ２ＯＣＨ２－、又は－ＣＯ－ＮＲ２－Ｙ’－（但し、Ｙ’は－ＣＨ２－又は下記構造式（Ｚ’）で示される基であり、
    Figure JPOXMLDOC01-appb-C000001
     （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）
    Ｒ２は水素原子、メチル基、フェニル基、又はアリル基である。）であり、ｐは０又は１である。Ｒｆ１は、一般式Ｆ－［ＣＦ（ＣＦ３）ＣＦ２Ｏ］ｗ－ＣＦ（ＣＦ３）－（式中、ｗは１～５００の整数で表される。）で示されるパーフルオロポリエーテル構造である。］で表されるポリフルオロモノアルケニル化合物である請求項２に記載の硬化性パーフルオロポリエーテル粘着剤組成物。
  4. 　前記（Ａ）成分が、下記一般式（１）
    Figure JPOXMLDOC01-appb-C000002
     ［式中、Ｘは－ＣＨ２－、－ＣＨ２Ｏ－、－ＣＨ２ＯＣＨ２－、又は－Ｙ－ＮＲ１－ＣＯ－（但し、Ｙは－ＣＨ２－又は下記構造式（Ｚ）で示される基であり、Ｒ１は水素原子、メチル基、フェニル基、又はアリル基である。）である。Ｘ’は－ＣＨ２－、－ＯＣＨ２－、－ＣＨ２ＯＣＨ２－、又は－ＣＯ－ＮＲ２－Ｙ’－（但し、Ｙ’は－ＣＨ２－又は下記構造式（Ｚ’）で示される基であり、Ｒ２は水素原子、メチル基、フェニル基、又はアリル基である。）である。ｐは独立に０又は１、ｒは２～６の整数、ｍ、ｎはそれぞれ０～６００の整数であり、更にｍとｎの和が５０～６００である。
    Figure JPOXMLDOC01-appb-C000003
     （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）
    Figure JPOXMLDOC01-appb-C000004
     （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）］
    で表される直鎖状パーフルオロポリエーテル化合物である請求項１～３のいずれか１項に記載の硬化性パーフルオロポリエーテル粘着剤組成物。
  5. 　（Ａ）成分が、下記一般式（１）
    Figure JPOXMLDOC01-appb-C000005
     ［式中、Ｘは－ＣＨ２－、－ＣＨ２Ｏ－、－ＣＨ２ＯＣＨ２－、又は－Ｙ－ＮＲ１－ＣＯ－（但し、Ｙは－ＣＨ２－又は下記構造式（Ｚ）で示される基であり、Ｒ１は水素原子、メチル基、フェニル基、又はアリル基である。）である。Ｘ’は－ＣＨ２－、－ＯＣＨ２－、－ＣＨ２ＯＣＨ２－、又は－ＣＯ－ＮＲ２－Ｙ’－（但し、Ｙ’は－ＣＨ２－又は下記構造式（Ｚ’）で示される基であり、Ｒ２は水素原子、メチル基、フェニル基、又はアリル基である。）である。ｐは独立に０又は１、ｒは２～６の整数、ｍ、ｎはそれぞれ０～６００の整数であり、更にｍとｎの和が５０～６００である。
    Figure JPOXMLDOC01-appb-C000006
     （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）
    Figure JPOXMLDOC01-appb-C000007
     （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）］
    で表される直鎖状パーフルオロポリエーテル化合物であり、該（Ａ）成分１００～８０質量部に対して（Ｄ）成分を０～２０質量部（但し、（Ａ）成分と（Ｄ）成分の合計は１００質量部）を含み、（Ｂ）成分が環状のシロキサン構造を有する含フッ素オルガノ水素ポリシロキサンである請求項２又は３に記載の硬化性パーフルオロポリエーテル粘着剤組成物。
  6. 　（Ａ）成分が下記一般式（１）
    Figure JPOXMLDOC01-appb-C000008
     ［式中、Ｘは－ＣＨ２－、－ＣＨ２Ｏ－、－ＣＨ２ＯＣＨ２－、又は－Ｙ－ＮＲ１－ＣＯ－（但し、Ｙは－ＣＨ２－又は下記構造式（Ｚ）で示される基であり、Ｒ１は水素原子、メチル基、フェニル基、又はアリル基である。）である。Ｘ’は－ＣＨ２－、－ＯＣＨ２－、－ＣＨ２ＯＣＨ２－、又は－ＣＯ－ＮＲ２－Ｙ’－（但し、Ｙ’は－ＣＨ２－又は下記構造式（Ｚ’）で示される基であり、Ｒ２は水素原子、メチル基、フェニル基、又はアリル基である。）である。ｐは独立に０又は１、ｒは２～６の整数、ｍ、ｎはそれぞれ０～６００の整数であり、更にｍとｎの和が５０～６００である。
    Figure JPOXMLDOC01-appb-C000009
     （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）
    Figure JPOXMLDOC01-appb-C000010
     （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）］
    で表される直鎖状パーフルオロポリエーテル化合物であり、該（Ａ）成分７９～５５質量部に対して（Ｄ）成分を２１～４５質量部（但し、（Ａ）成分と（Ｄ）成分の合計は１００質量部）を含み、（Ｂ）成分が直鎖状及び／又は分岐鎖状のシロキサン構造を有する含フッ素ポリオルガノ水素シロキサンである請求項２又は３に記載の硬化性パーフルオロポリエーテル粘着剤組成物。
  7. 　（Ａ）成分が、主鎖に（ＣＦ２Ｏ）単位及び（ＣＦ２ＣＦ２Ｏ）単位の繰り返しからなる二価のパーフルオロポリエーテル構造を含む直鎖状パーフルオロポリエーテル化合物であり、該（Ａ）成分１００～５０質量部に対して（Ｄ）成分を０～５０質量部（但し、（Ａ）成分と（Ｄ）成分の合計は１００質量部）を含み、（Ｂ）成分が直鎖状及び／又は分岐鎖状のシロキサン構造を有する含フッ素オルガノ水素ポリシロキサンである請求項２又は３に記載の硬化性パーフルオロポリエーテル粘着剤組成物。
  8. 　（Ａ）成分が下記一般式（１）
    Figure JPOXMLDOC01-appb-C000011
     ［式中、Ｘは－ＣＨ２－、－ＣＨ２Ｏ－、－ＣＨ２ＯＣＨ２－、又は－Ｙ－ＮＲ１－ＣＯ－（但し、Ｙは－ＣＨ２－又は下記構造式（Ｚ）で示される基であり、Ｒ１は水素原子、メチル基、フェニル基、又はアリル基である。）である。Ｘ’は－ＣＨ２－、－ＯＣＨ２－、－ＣＨ２ＯＣＨ２－、又は－ＣＯ－ＮＲ２－Ｙ’－（但し、Ｙ’は－ＣＨ２－又は下記構造式（Ｚ’）で示される基であり、Ｒ２は水素原子、メチル基、フェニル基、又はアリル基である。）である。ｐは独立に０又は１、ｒは２～６の整数、ｍ、ｎはそれぞれ０～６００の整数であり、更にｍとｎの和が５０～６００である。
    Figure JPOXMLDOC01-appb-C000012
     （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）
    Figure JPOXMLDOC01-appb-C000013
     （オルト、メタ、又はパラ位で示されるジメチルフェニルシリレン基）］
    で表され、主鎖に（ＣＦ２Ｏ）単位及び（ＣＦ２ＣＦ２Ｏ）単位の繰り返しからなる二価のパーフルオロポリエーテル構造を含む直鎖状パーフルオロポリエーテル化合物であり、該（Ａ）成分１００～５０質量部に対して（Ｄ）成分を０～５０質量部（但し、（Ａ）成分と（Ｄ）成分の合計は１００質量部）を含み、（Ｂ）成分が直鎖状及び／又は分岐鎖状のシロキサン構造を有する含フッ素オルガノ水素ポリシロキサンである請求項２又は３に記載の硬化性パーフルオロポリエーテル粘着剤組成物。
  9. 　前記硬化性パーフルオロポリエーテル粘着剤組成物の硬化物が、体積抵抗率が１×１０９Ω・ｃｍ以上の非導電性粘着剤である請求項１～８のいずれか１項に記載の硬化性パーフルオロポリエーテル粘着剤組成物。
  10. 　請求項１～９のいずれか１項に記載の硬化性パーフルオロポリエーテル粘着剤組成物の硬化物を含む粘着剤。
  11. 　基材上に、請求項１～９のいずれか１項に記載の硬化性パーフルオロポリエーテル粘着剤組成物の硬化物層が積層している粘着テープ。
PCT/JP2020/043943 2019-12-17 2020-11-26 硬化性パーフルオロポリエーテル粘着剤組成物、その硬化物を用いた粘着剤並びに粘着テープ WO2021124824A1 (ja)