WO2021095183A1 - Matériau en acier - Google Patents

Matériau en acier Download PDF

Info

Publication number
WO2021095183A1
WO2021095183A1 PCT/JP2019/044609 JP2019044609W WO2021095183A1 WO 2021095183 A1 WO2021095183 A1 WO 2021095183A1 JP 2019044609 W JP2019044609 W JP 2019044609W WO 2021095183 A1 WO2021095183 A1 WO 2021095183A1
Authority
WO
WIPO (PCT)
Prior art keywords
less
content
contained
steel
corrosion resistance
Prior art date
Application number
PCT/JP2019/044609
Other languages
English (en)
Japanese (ja)
Inventor
亜希子 富尾
淳子 今村
Original Assignee
日本製鉄株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本製鉄株式会社 filed Critical 日本製鉄株式会社
Priority to KR1020227013385A priority Critical patent/KR20220066368A/ko
Priority to PCT/JP2019/044609 priority patent/WO2021095183A1/fr
Priority to CN201980101846.5A priority patent/CN114729414B/zh
Priority to JP2020515042A priority patent/JP6787530B1/ja
Publication of WO2021095183A1 publication Critical patent/WO2021095183A1/fr

Abstract

L'invention concerne un matériau en acier ayant une composition chimique, en % en masse, de 0,01 % à 0,10 % de C, de 0,04 % à 0,40 % de Si, de 0,50 % à 1,50 % de Mn, de 0,05 % à 0,50 % de Cu, de 0,01 % à 0,30 % de Sb, de 0,005 % à 0,050 % d'Al, de 0,01 % à 0,30 % de Mo + W, pas plus de 0,020 % de P, de 0,0005 % à 0,015 % de S, pas plus de 0,005 % de N, de 0,0005 % à 0,0035 % d'O, plus de 0 % et pas plus de 0,010 % de Ca, de 0 % à 0,30 % de Ni, de 0 % à 0,50 % de Sn, de 0 % à 0,30 % d'As, de 0 % à 0,30 % de Co, de 0 % à 0,70 % de Cr, de 0 % à 0,050 % de Ti, de 0 % à 0,10 % de Nb, de 0 % à 0,10 % de V, de 0 % à 0,050 % de Zr, de 0 % à 0,050 % de Ta, de 0 % à 0,010 % de B, de 0 % à 0,010 % de Mg et de 0 % à 0,010 % de REM, le reste étant du Fe et des impuretés inévitables. Le matériau en feuille présente de 6,0 à 16,0 de Si/Al, de 0,06 à 0,21 d'Al, de 2,5 à 6,0 d'EI et/ou de 0,10 % à 0,25 % de Cu + Sb et de 0,180 à 0,330 de Ceq. La nombre volumique de MnS dans le matériau en acier est inférieur à 50/mm2.
PCT/JP2019/044609 2019-11-13 2019-11-13 Matériau en acier WO2021095183A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
KR1020227013385A KR20220066368A (ko) 2019-11-13 2019-11-13 강재
PCT/JP2019/044609 WO2021095183A1 (fr) 2019-11-13 2019-11-13 Matériau en acier
CN201980101846.5A CN114729414B (zh) 2019-11-13 2019-11-13 钢材
JP2020515042A JP6787530B1 (ja) 2019-11-13 2019-11-13 鋼材

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2019/044609 WO2021095183A1 (fr) 2019-11-13 2019-11-13 Matériau en acier

Publications (1)

Publication Number Publication Date
WO2021095183A1 true WO2021095183A1 (fr) 2021-05-20

Family

ID=73220017

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/044609 WO2021095183A1 (fr) 2019-11-13 2019-11-13 Matériau en acier

Country Status (4)

Country Link
JP (1) JP6787530B1 (fr)
KR (1) KR20220066368A (fr)
CN (1) CN114729414B (fr)
WO (1) WO2021095183A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003213367A (ja) * 2001-11-19 2003-07-30 Nippon Steel Corp 耐塩酸腐食性および耐硫酸腐食性に優れた低合金鋼およびその溶接継手
JP2007262558A (ja) * 2006-03-30 2007-10-11 Jfe Steel Kk 耐塩酸性に優れる耐硫酸露点腐食鋼
WO2009084747A1 (fr) * 2007-12-27 2009-07-09 Posco Acier ayant une excellente résistance à la corrosion par l'acide chlorhydrique et l'acide sulfurique et son procédé de fabrication
KR20130022874A (ko) * 2011-08-26 2013-03-07 주식회사 포스코 황산 및 염산 복합내식성 및 용접성이 우수한 강판 및 그 제조방법
JP2017014577A (ja) * 2015-07-01 2017-01-19 新日鐵住金株式会社 酸性環境用耐食鋼材及び防食方法
JP2019196535A (ja) * 2018-05-11 2019-11-14 日本製鉄株式会社 鋼材

Family Cites Families (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3153981B2 (ja) 1994-05-23 2001-04-09 新日本製鐵株式会社 硫酸と塩酸を同時に生成する露点環境中で優れた耐食性を示す高合金ステンレス鋼
JP3530439B2 (ja) 1999-12-06 2004-05-24 新日本製鐵株式会社 高加工性・良溶接性耐硫酸露点腐食鋼板
JP5186769B2 (ja) 2006-02-13 2013-04-24 新日鐵住金株式会社 耐硫酸露点腐食鋼
JP5818418B2 (ja) 2010-09-09 2015-11-18 日新製鋼株式会社 耐硫酸及び塩酸露点腐食鋼並びに排ガス流路構成部材
WO2015075771A1 (fr) * 2013-11-19 2015-05-28 新日鐵住金株式会社 Tôle d'acier
WO2015125915A1 (fr) * 2014-02-24 2015-08-27 新日鐵住金株式会社 Matériau en acier pour durcissement par induction
BR112017021206A2 (pt) * 2015-04-15 2018-07-03 Nippon Steel & Sumitomo Metal Corporation chapa de aço laminada a quente e método para produzir a mesma
EP3366800B1 (fr) * 2015-10-19 2020-03-25 Nippon Steel Corporation Acier pour utilisation en structure de machine et composant en acier trempé par induction
JP6245417B1 (ja) * 2016-04-19 2017-12-13 新日鐵住金株式会社 鋼材
EP3447162B1 (fr) * 2016-04-21 2020-12-30 Nippon Steel Corporation Plaque d'acier épaisse
JP6394839B1 (ja) * 2017-12-14 2018-09-26 新日鐵住金株式会社 鋼材

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003213367A (ja) * 2001-11-19 2003-07-30 Nippon Steel Corp 耐塩酸腐食性および耐硫酸腐食性に優れた低合金鋼およびその溶接継手
JP2007262558A (ja) * 2006-03-30 2007-10-11 Jfe Steel Kk 耐塩酸性に優れる耐硫酸露点腐食鋼
WO2009084747A1 (fr) * 2007-12-27 2009-07-09 Posco Acier ayant une excellente résistance à la corrosion par l'acide chlorhydrique et l'acide sulfurique et son procédé de fabrication
KR20130022874A (ko) * 2011-08-26 2013-03-07 주식회사 포스코 황산 및 염산 복합내식성 및 용접성이 우수한 강판 및 그 제조방법
JP2017014577A (ja) * 2015-07-01 2017-01-19 新日鐵住金株式会社 酸性環境用耐食鋼材及び防食方法
JP2019196535A (ja) * 2018-05-11 2019-11-14 日本製鉄株式会社 鋼材

Also Published As

Publication number Publication date
KR20220066368A (ko) 2022-05-24
CN114729414A (zh) 2022-07-08
JP6787530B1 (ja) 2020-11-18
CN114729414B (zh) 2024-03-29
JPWO2021095183A1 (ja) 2021-11-25

Similar Documents

Publication Publication Date Title
JP7348463B2 (ja) 鋼材
JP7099041B2 (ja) 鋼材
JP6813127B1 (ja) 鋼材
JP7385106B2 (ja) 鋼材
JP7127355B2 (ja) 鋼材
JP7127354B2 (ja) 鋼材
JP7124432B2 (ja) 鋼材
JP2022044093A (ja) 鋼材
JP6787530B1 (ja) 鋼材
JP6813128B1 (ja) 鋼材
JP6743996B1 (ja) 鋼材
JP7252497B2 (ja) 熱間圧延鋼材
JP2020045539A (ja) 鋼材
JP7415140B2 (ja) 鋼材
JP7091968B2 (ja) 鋼材
JP2022044092A (ja) 鋼材
JP2021017637A (ja) 鋼材
JP2021085047A (ja) 鋼材
JP2023066027A (ja) 鋼材
JP2023066026A (ja) 鋼材
JP2023140621A (ja) 熱間圧延鋼材

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2020515042

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19952151

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20227013385

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19952151

Country of ref document: EP

Kind code of ref document: A1