WO2021065767A1 - Composition de résine d'élément de lampe, élément de lampe et procédé de production de composition de résine d'élément de lampe - Google Patents

Composition de résine d'élément de lampe, élément de lampe et procédé de production de composition de résine d'élément de lampe Download PDF

Info

Publication number
WO2021065767A1
WO2021065767A1 PCT/JP2020/036535 JP2020036535W WO2021065767A1 WO 2021065767 A1 WO2021065767 A1 WO 2021065767A1 JP 2020036535 W JP2020036535 W JP 2020036535W WO 2021065767 A1 WO2021065767 A1 WO 2021065767A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin composition
lamp
lamp member
component
group
Prior art date
Application number
PCT/JP2020/036535
Other languages
English (en)
Japanese (ja)
Inventor
啓介 山西
光男 前田
Original Assignee
住友化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社 filed Critical 住友化学株式会社
Priority to JP2021551222A priority Critical patent/JPWO2021065767A1/ja
Publication of WO2021065767A1 publication Critical patent/WO2021065767A1/fr

Abstract

Une composition de résine d'élément de lampe selon la présente invention comprend : en tant que constituant (P), une polysulfone aromatique; et, en tant que constituant (M), au moins un type de substance choisi dans le groupe constitué par les oxydes, les peroxydes, les oxydes multiples et les carbonates de métaux appartenant aux groupes 1 et 2 du tableau périodique détaillé. La présente invention concerne également un élément de lampe moulé à partir de la composition de résine d'élément de lampe.
PCT/JP2020/036535 2019-10-02 2020-09-28 Composition de résine d'élément de lampe, élément de lampe et procédé de production de composition de résine d'élément de lampe WO2021065767A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2021551222A JPWO2021065767A1 (fr) 2019-10-02 2020-09-28

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019-182112 2019-10-02
JP2019182112 2019-10-02

Publications (1)

Publication Number Publication Date
WO2021065767A1 true WO2021065767A1 (fr) 2021-04-08

Family

ID=75338244

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/036535 WO2021065767A1 (fr) 2019-10-02 2020-09-28 Composition de résine d'élément de lampe, élément de lampe et procédé de production de composition de résine d'élément de lampe

Country Status (2)

Country Link
JP (1) JPWO2021065767A1 (fr)
WO (1) WO2021065767A1 (fr)

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH02281502A (ja) * 1989-03-22 1990-11-19 Basf Ag 照明工学用途のためのポリアリールエーテルスルホン
JPH0834853A (ja) * 1994-03-18 1996-02-06 Sekisui Chem Co Ltd 光学材料
JPH1196817A (ja) * 1997-09-19 1999-04-09 Sumitomo Chem Co Ltd ランプリフレクター
JP2003301107A (ja) * 2002-04-11 2003-10-21 Toray Ind Inc 樹脂組成物
JP2009138149A (ja) * 2007-12-10 2009-06-25 Sumitomo Chemical Co Ltd ポリエーテルスルホン系樹脂組成物及びその成形体
JP2010530914A (ja) * 2007-06-22 2010-09-16 ビーエーエスエフ ソシエタス・ヨーロピア 改善された表面品質を有するポリアリールエーテルを含有する成形材料
WO2013080566A1 (fr) * 2011-12-01 2013-06-06 東レ株式会社 Composition de résine de sulfure de polyphénylène, procédé pour la production de ladite composition, et plaque réfléchissante
WO2014017274A1 (fr) * 2012-07-24 2014-01-30 出光ライオンコンポジット株式会社 Phare de véhicule
CN106810804A (zh) * 2016-12-09 2017-06-09 芜湖天鸿汽车零部件有限公司 一种汽车灯罩成型材料及其制备方法
JP2018517045A (ja) * 2015-06-10 2018-06-28 ソルベイ スペシャルティ ポリマーズ ユーエスエー， エルエルシー ポリマー組成物およびそれから得ることができる滅菌可能な物品

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH02281502A (ja) * 1989-03-22 1990-11-19 Basf Ag 照明工学用途のためのポリアリールエーテルスルホン
JPH0834853A (ja) * 1994-03-18 1996-02-06 Sekisui Chem Co Ltd 光学材料
JPH1196817A (ja) * 1997-09-19 1999-04-09 Sumitomo Chem Co Ltd ランプリフレクター
JP2003301107A (ja) * 2002-04-11 2003-10-21 Toray Ind Inc 樹脂組成物
JP2010530914A (ja) * 2007-06-22 2010-09-16 ビーエーエスエフ ソシエタス・ヨーロピア 改善された表面品質を有するポリアリールエーテルを含有する成形材料
JP2009138149A (ja) * 2007-12-10 2009-06-25 Sumitomo Chemical Co Ltd ポリエーテルスルホン系樹脂組成物及びその成形体
WO2013080566A1 (fr) * 2011-12-01 2013-06-06 東レ株式会社 Composition de résine de sulfure de polyphénylène, procédé pour la production de ladite composition, et plaque réfléchissante
WO2014017274A1 (fr) * 2012-07-24 2014-01-30 出光ライオンコンポジット株式会社 Phare de véhicule
JP2018517045A (ja) * 2015-06-10 2018-06-28 ソルベイ スペシャルティ ポリマーズ ユーエスエー， エルエルシー ポリマー組成物およびそれから得ることができる滅菌可能な物品
CN106810804A (zh) * 2016-12-09 2017-06-09 芜湖天鸿汽车零部件有限公司 一种汽车灯罩成型材料及其制备方法

Also Published As

Publication number Publication date
JPWO2021065767A1 (fr) 2021-04-08

Similar Documents

Publication Publication Date Title
JP6211602B2 (ja) 耐光性樹脂組成物およびその成形体
JP6048833B2 (ja) 表面実装型ｌｅｄ用反射板に使用するポリエステル樹脂組成物
JP6260085B2 (ja) Ｌｅｄ反射板用ポリエステル樹脂組成物
KR102158764B1 (ko) 폴리에스테르 수지 및 그것을 사용한 표면 실장형 led 반사판용 폴리에스테르 수지 조성물
TW200836912A (en) Polyphenylene sulfide resin molded article
KR101831097B1 (ko) 반사재용 수지 조성물 및 그것을 포함하는 반사판
JP6321754B2 (ja) 芳香族ポリスルホンの製造方法
WO2009125556A1 (fr) Composition de résine de sulfure de polyarylène et moulages à base de résine de sulfure de polyarylène destinés à être mis en contact avec un solvant organique
WO2021065767A1 (fr) Composition de résine d'élément de lampe, élément de lampe et procédé de production de composition de résine d'élément de lampe
WO2021065770A1 (fr) Composition de polysulfone aromatique, objet moulé et procédé de production de composition de polysulfone aromatique
JP2012131968A (ja) 金属膜を形成した反射板
JP2001354855A (ja) ポリアリーレンスルフィド樹脂組成物及びその成形体
WO2016002193A1 (fr) Composition de résine polyester pour matériaux réfléchissants et plaque de réflexion les contenant
JP6172586B2 (ja) 芳香族ポリスルホン樹脂及びその製造方法
JP2000265060A (ja) ポリアリーレンスルフィド樹脂組成物
JP2014065842A (ja) ポリフェニレンスルフィド樹脂組成物および成形品
JP6042271B2 (ja) 反射材用ポリエステル樹脂組成物および反射板
JP2020019914A (ja) 反射材用ポリエステル樹脂組成物および反射材
TWI701274B (zh) 樹脂組成物及成形體
JP2019127545A (ja) 反射材用ポリエステル樹脂組成物および反射材
JPWO2007046451A1 (ja) ポリアリーレンサルファイド樹脂組成物及び有機溶剤に接するポリアリーレンサルファイド樹脂成形品
JP6221662B2 (ja) Ｌｅｄ反射板用ポリエステル樹脂組成物
KR101238474B1 (ko) 폴리에스테르로 이루어진 조명 소자
JP2019142986A (ja) 反射材用ポリエステル樹脂組成物および反射材
JP7286217B2 (ja) リフレクター形成用樹脂組成物

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20871682

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2021551222

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20871682

Country of ref document: EP

Kind code of ref document: A1