WO2020188867A1 - 断熱シートの製造方法 - Google Patents

断熱シートの製造方法 Download PDF

Info

Publication number
WO2020188867A1
WO2020188867A1 PCT/JP2019/039947 JP2019039947W WO2020188867A1 WO 2020188867 A1 WO2020188867 A1 WO 2020188867A1 JP 2019039947 W JP2019039947 W JP 2019039947W WO 2020188867 A1 WO2020188867 A1 WO 2020188867A1
Authority
WO
WIPO (PCT)
Prior art keywords
silica gel
heat insulating
sheet
temperature
fiber sheet
Prior art date
Application number
PCT/JP2019/039947
Other languages
English (en)
French (fr)
Inventor
康隆 花城
臼井　良輔
佐藤　千尋
裕司 山岸
Original Assignee
パナソニックＩｐマネジメント株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by パナソニックＩｐマネジメント株式会社 filed Critical パナソニックＩｐマネジメント株式会社
Priority to CN201980088774.5A priority Critical patent/CN113286773A/zh
Priority to JP2021506141A priority patent/JP7369914B2/ja
Priority to US17/413,928 priority patent/US20220090313A1/en
Publication of WO2020188867A1 publication Critical patent/WO2020188867A1/ja

Abstract

内部に空間を有して、互いに反対側の第１面と第２面とを有する繊維シートを準備する。水ガラスとエチレンカーボネートとを含むシリカゾル溶液を繊維シートの空間に含浸させる。繊維シートの第１面と第２面とで５０℃以上の温度差をつけた状態でシリカゾル溶液をゲル化させてシリカゲルを形成する。シリカゲルを疎水化する。これにより断熱シートを得る。以上のようにして得られた断熱シートは、第１面と第２面とで所定の圧力に対する圧縮率を異ならせることができる。この断熱シートを２つの電池セル間に配置した場合には、一方の電池セルが膨張しても他方の電池セルに影響を与えることを防止することができる。

Description

断熱シートの製造方法
　本発明は、断熱対策として用いられる断熱シートの製造方法に関する。
　近年省エネルギー化の要求が増加しているが、その実現方法として機器の保温によりエネルギー効率を向上させるものがある。また複数個の電池セルを組み合わせた二次電池等では、ひとつの電池セルが高温になった場合に隣の電池セルに影響を与えないため、電池セル間を断熱したいという要望もある。これらの対策として電池セルの間に、断熱効果に優れた断熱シートを用いることがある。
　このような断熱シートは、例えば、特許文献１に開示されている。
特開２０１１－１３６８５９号公報
　内部に空間を有して、互いに反対側の第１面と第２面とを有する繊維シートを準備する。水ガラスとエチレンカーボネートとを含むシリカゾル溶液を繊維シートの空間に含浸させる。繊維シートの第１面と第２面とで５０℃以上の温度差をつけた状態でシリカゾル溶液をゲル化させてシリカゲルを形成する。シリカゲルを疎水化する。これにより断熱シートを得る。
　以上のようにして得られた断熱シートは、第１面と第２面とで所定の圧力に対する圧縮率を異ならせることができる。この断熱シートを２つの電池セル間に配置した場合には、一方の電池セルが膨張しても他方の電池セルに影響を与えることを防止することができる。
図１は実施の形態における断熱シートの断面図である。 図２は実施の形態における断熱シートの製造方法を示す断面図である。 図３は実施の形態における断熱シートを用いた二次電池の断面図である。
　図１は実施の形態における断熱シート１０１の断面図である。断熱シート１０１は、内部に空間２１ｑを有する繊維シート２１と、繊維シート２１の空間２１ｑに含浸させたシリカゲル３１とを備える。
　以下に断熱シート１０１の製造方法を説明する。図２は断熱シート１０１の製造方法を示す断面図である。まず、内部に空間２１ｑを有する繊維シート２１を準備する。繊維シート２１は、約１ｍｍの厚みを有し、大きさ約８０ｍｍ×１５０ｍｍの矩形状を有する。繊維シート２１は平均繊維太さ約２μｍのガラス繊維よりなる繊維２１ｐからなる。繊維２１ｐは空間２１ｑが形成されるように互いに絡みあっている。実施の形態では、繊維シート２１の厚さ１ｍｍ当たりの目付量は約１３０ｇ／ｍ２である。繊維シート２１は、互いに反対側の面１１１、２１１を有する。
　次に、シリカキセロゲルであるシリカゲル３１を繊維シート２１の内部の空間２１ｑに含浸するための準備を行う。シリカゲル３１の材料として、約２０％の水ガラスに触媒として約６％のエチレンカーボネートを添加してシリカゾル溶液４１を調整する。シリカゾル溶液４１に繊維シート２１を浸漬して繊維シート２１の空間２１ｑにシリカゾル溶液４１を含浸させることで、材料シート２０１を得る。
　次に、シリカゾル溶液４１を含浸した材料シート２０１をプレスして厚みを均一にする。厚みの整え方は、ロールプレス等の方法を用いてもよい。厚みを整えた材料シート２０１をフィルム２０２に挟んだ状態で養生してゲル骨格を強化するためにシリカゾル溶液４１をゲル化してシリカキセロゲルであるシリカゲル３１を形成する。この養生により、材料シート２０１は一定の温度に保ったまま放置され、繊維シート２１の空間２１ｑ内にシリカゾル溶液４１を保持した状態でシリカゾル溶液４１がゲル化され、さらにゲルが成長する。また、材料シート２０１をフィルムで挟むことにより、シリカゾル溶液４１の蒸発を防ぐことができる。ゲル化の際には、繊維シート２１の面１１１が鉛直方向の上方を向き、面２１１が鉛直方向の下方を向きすなわち重力の方向を向き、かつ面１１１を約９０℃に保ち、面２１１を約２０℃に保ちながら約１０分間だけ材料シート２０１を放置する。水ガラス原料に触媒としてエチレンカーボネートが添加されているので、温度が８５℃を超えると急激に加水分解反応が進み、シリカの一部が溶出しながらシリカゾル溶液４１のゲル化が進む。そのため、シリカゾル溶液４１の高温の部分では低温の部分に比べてシリカゲルの含有量が減り、シリカゲル３１の加えられた圧力に対する圧縮率が大きくなる。逆にシリカゾル溶液４１の温度が低い部分では、高い部分に比べて脱水縮合が進みシリカゾル溶液４１がそのままゲル化され、シリカゲル３１の圧縮率は低くなる。
　次にシリカゲル３１を以下の方法で疎水化する。シリカゲル３１を含浸した繊維シート２１を６Ｎの塩酸に約３０分浸漬し、シリカゲル３１に塩酸を反応させる。そのあと、シリル化剤とアルコールの混合溶液からなるシリル化液にシリカゲル３１を含浸した繊維シート２１を浸漬させた後、約５５℃の恒温槽にて約２時間保管する。この際に、シリル化剤とアルコールの混合溶液がシリカゲル３１に浸透する。反応が進行し、トリメチルシロキサン結合が形成し始めるとシリカゲル３１を含有した繊維シート２１から塩酸水が外部に排出される。シリル化処理が終了したら、約１５０℃の恒温槽にてシリカゲル３１を約２時間乾燥して、断熱シート１０１を得る。
　繊維シート２１すなわち材料シート２０１の面１１１、２１１で温度を互いに異ならせるには、例えば、面２１１を下方にすなわち重力の方向に向けて低温に保った冷却板の上にシリカゾル溶液４１を含浸した材料シート２０１の面２１１を配置し、高温に保った加熱板を面１１１に当接させて所定時間維持する。あるいは面１１１に赤外線を照射して面１１１を加熱しても良い。
　以上のようにして、面１１１と面２１１とで５０℃以上の温度差をつけた状態でシリカゾル溶液４１をゲル化してゲル骨格を強化することにより、面１１１付近と面２１１付近とで圧縮率を大きく異ならせることができる。
　また鉛直方向の上側に面１１１を向け、面１１１の温度を面２１１の温度よりも高くして材料シート２０１を養生することが望ましい。面１１１の温度を面２１１より高くすることで、面２１１に比べて面１１１付近で加水分解反応がより進み、シリカの一部が溶出し、重力によって面２１１に向かって移動する。そのため断熱シート１０１の面１１１付近と面２１１付近とで圧縮率をより大きく互いに異ならせることができる。
　また、ゲル化の際に面１１１の温度を８５℃以上で１３５℃以下とすることが望ましい。面１１１の温度が８５℃より低いと加水分解反応が進みにくくなり、１３５℃を超えると反応速度が上がり過ぎばらつきが大きくなりやすくなる。
　以上のようにして得られた断熱シート１０１では、高温に維持された面１１１付近の部分は高圧縮率を有し、低温で維持された面２１１付近の部分は低圧縮率を有する。
　図３は実施の形態における二次電池３０１の断面図である。二次電池３０１は、複数の電池セル３０２と、複数の電池セル３０２の間に設けられた２つの断熱シート１０１とを備える。２つの断熱シート１０１は面２１１が互いに対向して電池セル３０２間に配置される。断熱シート１０１の面１１１は電池セル３０２にそれぞれ対向する。断熱シート１０１の面１１１は高圧縮率を有するので、一つの電池セル３０２が発熱して膨張した場合に、断熱シート１０１の高圧縮率を有する面１１１の付近の領域で膨張を吸収し、低圧縮率を有する面２１１の付近の領域で断熱性を保てるので、隣の他方の電池セル３０２に与える熱の影響を防いで熱暴走を防ぐことができる。なお、実施の形態における二次電池３０１では２つの断熱シート１０１が電池セル３０２間に配置されているが、２つの断熱シート１０１の代わりに、面２１１が互いに対向するように折り曲げられた１つの断熱シート１０１が配置されていてもよい。
　二次電池の寿命末期には、電池セル内部に発生したガス等によりにセルの中央部分が膨張する。均一な密度でシリカキセロゲルを繊維シートに担持させた従来の断熱シートは、硬すぎるとセルの膨張を十分に吸収できない。この断熱シートが逆に柔らかすぎると圧縮されることによって断熱性が劣化し、ひとつの電池セルが高温になった場合に隣の電池セルに影響を与えてしまう可能性がある。
　それに対して、実施の形態における断熱シート１０１は二次電池３０１に用いることで、一つの電池セル３０２が発熱して膨張した場合に、隣の他方の電池セル３０２に与える熱の影響を防いで熱暴走を防ぐことができる。
２１　　繊維シート
３１　　シリカゲル
４１　　シリカゾル溶液
１０１　　断熱シート

Claims (3)

  1. 内部に空間を有して、互いに反対側の第１面と第２面とを有する繊維シートを準備するステップと、
    水ガラスとエチレンカーボネートとを含むシリカゾル溶液を前記繊維シートの前記空間に含浸させるステップと、
    前記繊維シートの前記第１面と前記第２面とで５０℃以上の温度差をつけた状態で前記含浸されたシリカゾル溶液をゲル化させてシリカゲルを形成するステップと、
    前記シリカゲルを疎水化するステップと、
    を含む、断熱シートの製造方法。
  2. 前記シリカゲルを形成する前記ステップは、前記第２面を重力の方向に向け、かつ前記第１面の温度を前記第２面の温度よりも高くした状態で前記含浸されたシリカゾル溶液をゲル化させて前記シリカゲルを形成するステップを含む、請求項１に記載の断熱シートの製造方法。
  3. 前記シリカゲルを形成する前記ステップは、前記第２面を重力の方向に向け、かつ前記第１面の温度を前記第２面の温度よりも高くし、かつ前記第１面の温度を８５℃以上で１３５℃以下とした状態で前記含浸されたシリカゾル溶液をゲル化させて前記シリカゲルを形成するステップを含む、請求項２に記載の断熱シートの製造方法。
PCT/JP2019/039947 2019-03-19 2019-10-10 断熱シートの製造方法 WO2020188867A1 (ja)