WO2019187130A1 - Groupe d'électrodes, batterie et bloc-batterie - Google Patents

Groupe d'électrodes, batterie et bloc-batterie Download PDF

Info

Publication number
WO2019187130A1
WO2019187130A1 PCT/JP2018/013922 JP2018013922W WO2019187130A1 WO 2019187130 A1 WO2019187130 A1 WO 2019187130A1 JP 2018013922 W JP2018013922 W JP 2018013922W WO 2019187130 A1 WO2019187130 A1 WO 2019187130A1
Authority
WO
WIPO (PCT)
Prior art keywords
negative electrode
active material
positive electrode
current collector
electrode current
Prior art date
Application number
PCT/JP2018/013922
Other languages
English (en)
Japanese (ja)
Inventor
圭吾 保科
政典 田中
大典 高塚
康宏 原田
高見　則雄
Original Assignee
株式会社 東芝
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社 東芝 filed Critical 株式会社 東芝
Priority to PCT/JP2018/013922 priority Critical patent/WO2019187130A1/fr
Priority to JP2020508895A priority patent/JP6952876B2/ja
Publication of WO2019187130A1 publication Critical patent/WO2019187130A1/fr

Abstract

La présente invention concerne, selon un mode de réalisation, un groupe d'électrodes comprenant un stratifié incluant une électrode positive, une électrode négative et un élément d'isolation électrique. L'électrode positive est dotée : d'un collecteur de courant d'électrode positive de type courroie ; d'une languette de collecteur de courant d'électrode positive disposée sur un bord de celui-ci ; et d'une couche contenant un matériau actif d'électrode positive qui est supportée sur le collecteur de courant d'électrode positive. La couche contenant un matériau actif d'électrode positive comprend une première partie d'extrémité et une deuxième partie d'extrémité qui sont orientées parallèlement à l'un des bords du collecteur de courant d'électrode positive. L'électrode négative est pourvue d'un collecteur de courant d'électrode négative de type courroie, d'une languette de collecteur de courant d'électrode négative disposée sur un bord de celui-ci et d'une couche contenant un matériau actif d'électrode négative , ladite couche étant supportée sur le collecteur de courant d'électrode négative et comprenant un oxyde contenant du titane. La couche contenant un matériau actif d'électrode négative comprend une troisième partie d'extrémité et une quatrième partie d'extrémité qui sont orientées parallèlement à l'un des bords du collecteur de courant d'électrode négative. L'élément d'isolation électrique est interposé entre la couche contenant un matériau actif d'électrode positive et la couche contenant un matériau actif d'électrode négative. Le stratifié est laminé. La languette de collecteur de courant d'électrode positive fait saillie dans une première direction parallèle à l'axe de laminage. La quatrième partie d'extrémité est positionnée à proximité du côté de la languette de collecteur de courant d'électrode positive par rapport à la première partie d'extrémité. La languette de collecteur de courant d'électrode négative fait saillie dans une seconde direction qui est opposée à la première direction. La troisième partie d'extrémité est positionnée plus près du côté de la languette de collecteur de courant d'électrode négative par rapport à la deuxième partie d'extrémité. Une première largeur de déviation entre la première partie d'extrémité et la quatrième partie d'extrémité est plus large qu'une seconde largeur de déviation entre la deuxième partie d'extrémité et la troisième partie d'extrémité.
PCT/JP2018/013922 2018-03-30 2018-03-30 Groupe d'électrodes, batterie et bloc-batterie WO2019187130A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
PCT/JP2018/013922 WO2019187130A1 (fr) 2018-03-30 2018-03-30 Groupe d'électrodes, batterie et bloc-batterie
JP2020508895A JP6952876B2 (ja) 2018-03-30 2018-03-30 電極群、電池、及び電池パック

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2018/013922 WO2019187130A1 (fr) 2018-03-30 2018-03-30 Groupe d'électrodes, batterie et bloc-batterie

Publications (1)

Publication Number Publication Date
WO2019187130A1 true WO2019187130A1 (fr) 2019-10-03

Family

ID=68059776

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/013922 WO2019187130A1 (fr) 2018-03-30 2018-03-30 Groupe d'électrodes, batterie et bloc-batterie

Country Status (2)

Country Link
JP (1) JP6952876B2 (fr)
WO (1) WO2019187130A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112952034A (zh) * 2021-03-03 2021-06-11 珠海冠宇动力电池有限公司 一种锂离子电芯及采用该电芯的锂离子电池
WO2022264419A1 (fr) 2021-06-18 2022-12-22 株式会社 東芝 Groupe d'électrodes, batterie et bloc-batterie

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008266593A (ja) * 2007-03-23 2008-11-06 Sumitomo Chemical Co Ltd 多孔質フィルム
JP2014075335A (ja) * 2012-09-13 2014-04-24 Gs Yuasa Corp 電極体、電極体の製造方法、及び電極体を備えた蓄電素子
JP2016058264A (ja) * 2014-09-10 2016-04-21 株式会社東芝 電極群及び非水電解質電池
JP2017224496A (ja) * 2016-06-15 2017-12-21 株式会社東芝 非水電解質電池、電池モジュール及び車両

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008266593A (ja) * 2007-03-23 2008-11-06 Sumitomo Chemical Co Ltd 多孔質フィルム
JP2014075335A (ja) * 2012-09-13 2014-04-24 Gs Yuasa Corp 電極体、電極体の製造方法、及び電極体を備えた蓄電素子
JP2016058264A (ja) * 2014-09-10 2016-04-21 株式会社東芝 電極群及び非水電解質電池
JP2017224496A (ja) * 2016-06-15 2017-12-21 株式会社東芝 非水電解質電池、電池モジュール及び車両

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112952034A (zh) * 2021-03-03 2021-06-11 珠海冠宇动力电池有限公司 一种锂离子电芯及采用该电芯的锂离子电池
WO2022264419A1 (fr) 2021-06-18 2022-12-22 株式会社 東芝 Groupe d'électrodes, batterie et bloc-batterie

Also Published As

Publication number Publication date
JP6952876B2 (ja) 2021-10-27
JPWO2019187130A1 (ja) 2021-01-07

Similar Documents

Publication Publication Date Title
JP5793442B2 (ja) 電池用活物質、非水電解質電池及び電池パック
KR101646888B1 (ko) 전지용 활물질, 비수전해질 전지 및 전지 팩
KR101789005B1 (ko) 전지용 활물질, 비수전해질 전지 및 전지 팩
JP6096817B2 (ja) 非水電解質二次電池および電池パック
JP6668478B2 (ja) 非水電解質電池及び電池パック
JP6383144B2 (ja) 非水電解液二次電池用活物質、非水電解液二次電池、電池パック、および車
KR101649023B1 (ko) 전지용 활물질, 비수 전해질 전지 및 전지 팩
JP2017059390A (ja) 電極、非水電解質電池及び電池パック
JP6571284B2 (ja) 電極、非水電解質電池及び電池パック
CN111164819B (zh) 非水电解质电池及电池包
JP6965434B2 (ja) 電極複合体、電池、及び電池パック
WO2018020669A1 (fr) Batterie à électrolyte non aqueux et bloc-batterie
JP6952876B2 (ja) 電極群、電池、及び電池パック
JP6325678B2 (ja) 非水電解質二次電池およびそれを備えた電池パック
WO2020194439A1 (fr) Groupe d'électrodes, batterie et bloc-batterie
WO2019187131A1 (fr) Groupe d'électrodes, batterie et bloc-batterie
WO2018020670A1 (fr) Batterie à électrolyte non aqueux et bloc-batterie
WO2019187128A1 (fr) Batterie et bloc-batterie
WO2019187132A1 (fr) Complexe d'électrode, batterie et bloc-batterie
JP6132945B2 (ja) 電池パック及び自動車
WO2023079639A1 (fr) Électrode, batterie et bloc-batterie
WO2023233692A1 (fr) Électrode, batterie secondaire et bloc-batterie
JP2015046400A (ja) 電池用活物質、非水電解質電池及び電池パック

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18911664

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020508895

Country of ref document: JP

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 18911664

Country of ref document: EP

Kind code of ref document: A1