WO2019039450A1 - Procédé de production de résine contenant des groupes uretdione, résine contenant des groupes uretdione, procédé de production de résine contenant des isocyanates, et stratifié - Google Patents

Procédé de production de résine contenant des groupes uretdione, résine contenant des groupes uretdione, procédé de production de résine contenant des isocyanates, et stratifié Download PDF

Info

Publication number
WO2019039450A1
WO2019039450A1 PCT/JP2018/030756 JP2018030756W WO2019039450A1 WO 2019039450 A1 WO2019039450 A1 WO 2019039450A1 JP 2018030756 W JP2018030756 W JP 2018030756W WO 2019039450 A1 WO2019039450 A1 WO 2019039450A1
Authority
WO
WIPO (PCT)
Prior art keywords
isocyanate
containing resin
uretdione
compound
resin
Prior art date
Application number
PCT/JP2018/030756
Other languages
English (en)
Japanese (ja)
Inventor
常行 手島
松木　光一郎
武田　博之
Original Assignee
Dic株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dic株式会社 filed Critical Dic株式会社
Publication of WO2019039450A1 publication Critical patent/WO2019039450A1/fr

Abstract

L'invention concerne un procédé de production d'une résine contenant des groupes uretdione A, qui comprend une étape consistant à faire réagir un composé isocyanate et un composé alcool l'un avec l'autre, et qui est caractérisé en ce que le composé isocyanate contient un composé isocyanate ayant un squelette uretdione et en ce que le composé alcool contient un composé polyol. L'invention concerne également le procédé de production d'une résine contenant des groupes uretdione A, le rapport molaire des groupes isocyanate contenus dans le composé isocyanate aux groupes hydroxyle alcooliques dans le composé alcool étant de 1,0:0,8 à 1,0:2,0.
PCT/JP2018/030756 2017-08-25 2018-08-21 Procédé de production de résine contenant des groupes uretdione, résine contenant des groupes uretdione, procédé de production de résine contenant des isocyanates, et stratifié WO2019039450A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017162297 2017-08-25
JP2017-162297 2017-08-25

Publications (1)

Publication Number Publication Date
WO2019039450A1 true WO2019039450A1 (fr) 2019-02-28

Family

ID=65439322

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/030756 WO2019039450A1 (fr) 2017-08-25 2018-08-21 Procédé de production de résine contenant des groupes uretdione, résine contenant des groupes uretdione, procédé de production de résine contenant des isocyanates, et stratifié

Country Status (1)

Country Link
WO (1) WO2019039450A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111040101A (zh) * 2019-12-23 2020-04-21 万华化学集团股份有限公司 色值稳定的含有脲二酮基团的多异氰酸酯及其制备方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS50149793A (fr) * 1974-04-27 1975-12-01
JPH0532759A (ja) * 1991-01-14 1993-02-09 Nippon Polyurethane Ind Co Ltd ポリイソシアネート硬化剤、これを使用した塗料組成物および接着剤組成物
JPH0797423A (ja) * 1993-09-29 1995-04-11 Nippon Polyurethane Ind Co Ltd ポリイソシアネート硬化剤、これを用いた塗料組成物および接着剤組成物
JPH08134164A (ja) * 1994-11-15 1996-05-28 Inoac Corp 一成分系加熱速硬化型ポリウレタンエラストマー組成物、及びその成形加工方法

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS50149793A (fr) * 1974-04-27 1975-12-01
JPH0532759A (ja) * 1991-01-14 1993-02-09 Nippon Polyurethane Ind Co Ltd ポリイソシアネート硬化剤、これを使用した塗料組成物および接着剤組成物
JPH0797423A (ja) * 1993-09-29 1995-04-11 Nippon Polyurethane Ind Co Ltd ポリイソシアネート硬化剤、これを用いた塗料組成物および接着剤組成物
JPH08134164A (ja) * 1994-11-15 1996-05-28 Inoac Corp 一成分系加熱速硬化型ポリウレタンエラストマー組成物、及びその成形加工方法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111040101A (zh) * 2019-12-23 2020-04-21 万华化学集团股份有限公司 色值稳定的含有脲二酮基团的多异氰酸酯及其制备方法

Similar Documents

Publication Publication Date Title
JP6317428B2 (ja) ラミネート接着剤、ラミネートフィルムの製造方法、ラミネートフィルムおよびレトルトパウチ材料
JP5765510B1 (ja) ガスバリア性接着剤用樹脂組成物、及び接着剤
TWI507434B (zh) 聚酯樹脂組成物、接著劑、及薄膜
US9951259B2 (en) Adhesive composition and laminate
EP3418343B2 (fr) Adhésif à deux constituants durcissable sans solvant destiné à des stratifiés et produit durci en résine
US9676976B2 (en) Oxygen-barrier film and adhesive
JP2008516026A (ja) ウレトジオン基を含有する高反応性ポリウレタン組成物
JP6980234B2 (ja) 樹脂組成物、成形体、積層体、ガスバリア材、コーティング材及び接着剤
WO2015088037A1 (fr) Adhésif pour films d'emballage alimentaires
JP5821826B2 (ja) 接着剤
JP4660677B2 (ja) 無溶剤２液硬化型接着剤組成物
WO2015104867A1 (fr) Composition adhésive pour stratifié sans solvant à ouverture facile et film stratifié utilisant ladite composition adhésive
WO2019039450A1 (fr) Procédé de production de résine contenant des groupes uretdione, résine contenant des groupes uretdione, procédé de production de résine contenant des isocyanates, et stratifié
WO2019167638A1 (fr) Procédé de production de film d'emballage souple
EP2546274B1 (fr) Additif de flux pour système uréthane
JP2016098323A (ja) 接着剤、及び該接着層を有する多層フィルム
JP6303595B2 (ja) 二液型無溶剤ラミネート用接着剤、及び該接着剤を用いたラミネートフィルム
JP6929805B2 (ja) コーティング組成物および太陽電池バックシート
JP6178541B1 (ja) 二液硬化型無溶剤系ラミネート用接着剤および樹脂硬化物
JP5589691B2 (ja) 接着剤及びそれを使用した酸素バリア性フィルム
EP4353797A1 (fr) Adhésif et stratifié
JPWO2019167638A1 (ja) 軟包装用フィルムの製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18848471

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

NENP Non-entry into the national phase

Ref country code: JP

122 Ep: pct application non-entry in european phase

Ref document number: 18848471

Country of ref document: EP

Kind code of ref document: A1